Personalized Anti-Vibration Protection for Telematics Devices in Urban Freight Transport Vehicles

: Vibrations are a major cause of human health disorders, circuit boards and machinery damage. Vibration dampers are considered to be the best option to counter these issues. Three-dimensional printing techniques play an increasingly important role in manufacturing small polymer parts with tailored properties. Thermoplastic elastomers (TPE) constitute a perfect material for manufacturing small-scale series absorber prototypes due to their thermoplastic nature, good elasticity and damping properties. This paper proposes a novel multi-level approach to the design and manufacturing process, e.g., the ﬁrst level—selection of material; second level—decision about the geometry of a damper; third—selection of technological printing parameters; fourth—post-printing treatment. This work primarily aims to overview the design and manufacturing process levels. The impact of each step on the damping capacity of small absorbers is assessed. It was found that thermoplastic elastomers and fused deposition modeling (FDM) have huge potential in shaping the physical properties of small, elastomeric absorbers. It was assessed that at every step of the multilevel design and manufacturing process (MDMP), the designer could tailor the damping to meet the desired criteria of a ﬁnal product: a cylinder-shaped hollow damper that can be made from TPE polymer without post-printing treatment and is characterized by good damping.


Electric Vans in City Logistics
The usefulness of electric vans in city logistics systems has been indisputably demonstrated in numerous publications [1][2][3][4]. Due to the characteristics of the drive system, such as:

•
A high torque, available over the entire speed range; • A low level of noise; • No emissions during stoppages associated with the delivery; • The easy implementation of systems with simultaneous all swivel and all driven wheels (all-wheel steer-all-wheel drive), which increases maneuverability; these vehicles are particularly useful for handling the so-called last mile. As shown in numerous publications, e.g., [5][6][7], trucks and vans are exposed to a number of factors that cause vibrations. In particular, irregularities of roads and their surface condition are indicated as the source of vibrations.
Since the last mile of the supply chain takes place on local and internal roads, often with elements that slow down the traffic, the vehicle is exposed to vibrations and shocks ( Figure 1).
An exemplary course of the components of vibrations of a delivery truck, recorded with the use of accelerometers located in the cargo space, is shown in (Figure 2). An exemplary course of the components of vibrations of a delivery truck, recorded with the use of accelerometers located in the cargo space, is shown in (Figure 2).   An exemplary course of the components of vibrations of a delivery truck, recorded with the use of accelerometers located in the cargo space, is shown in (Figure 2).  As you can see, the handling of last mile shipments, during which vertical accelerations can reach 3 g, is not uncommon. In combination with longitudinal and transverse accelerations of 0.5 g, we obtain conditions in which the elements of the vehicle control electronics are exposed to the harmful influence of vibrations [8][9][10]. The importance of the problem of the reliability of electronic systems in vibration conditions is confirmed by the standardization of test methods, e.g., MIL-STD-750 [11] and MIL-STD-883 [12].
The above facts are important prerequisites for the development of vibration isolation systems for the protection of electronic components in electrically driven vans.

Adverse Effect of Vibrations
Mechanical vibrations cause many adverse phenomena in areas such as human work or activities and machine engineering. The major sources of vibrations include machine part damage, the imbalance of rotating machine parts, structural weakness and ill-designed mechanical systems.
Loosened bolt connections, damaged electrofusion welded connections and construction cracks are often a consequence of vibrations. If the material is subject to vibrations of an ultrasonic frequency range, the result is excessive material hardening or softening. Another adverse phenomenon is material fatigue. For example, turbine wheel parts of a 13K215 electric generator can be damaged by vibrations, resulting in the permanent deflection of the rotor shaft and cracks in the rotor structure [13] (pp. 383-434).
Vibrations can generate the following disorders in the human body: episodes of nervousness, fatigue and insomnia. Additionally, vibrations in the low-frequency range are a serious threat to human body, e.g., elastic natural connections between internal organs can be easily damaged if one is subjected to the vibrations mentioned above (the natural frequency of internal organs is 2-18 Hz). Vibrations also affect the circulatory, nervous and osteoarticular systems, damage and cause pain in the lumbar region of the spine and may be a source of degenerative diseases of the osteoarticular system [14]. Hence, a lot of attention and care is needed to appropriately protect personnel against mechanical vibrations.
Authors of publication [15] point out that the person driving the van under increasing vibration conditions will experience three types of adverse effects. These are the physical, physiological and psychological effects, which include instances of tired eyes, absent-mindedness, irritation, and to a lesser degree, the loss of patience, headache, backache, dizziness and nausea. This issue is significant when driving a delivering van over cobblestone roads, as it has a negative effect on the safety of both the cargo and the driver.

Telematics in Road Transport
In road transport, telematics are classified as follows: In-vehicle and mixed telematics belong to in-vehicle computers, such as a Global Positioning System (GPS) and Radio Frequency Identification (RFID), which are a base of complex freight transport management systems. Out of many telematics systems, one can highlight computerized vehicle routing and scheduling or navigation systems and Traffic Control. For example, computerized vehicle routing and scheduling can result in time savings of 10 to 15%, and the GPS gives the driver more flexibility and increases the speed of deliveries. Telematics have an impact on three major areas: social (a decreasing number of accidents), economic (a fixed and operating costs reduction) and environmental (a demand for energy or lowering pollution emissions, mainly CO 2 and NOx) [16] (pp. [50][51][52][53][54][55]. Without such systems, the efficiency and functioning of urban freight transport would stay at low level.

Damping and Dampers
A damper (or absorber) is a device that reduces vibrations that oscillate the motions of an object by lowering the vibration amplitude. Damper structures vary from one type to another. Dampers can operate in two modes: active-with active electrorheological elements (e.g., magnetorheological fluid and electrical circuit) and passive-without such elements [17,18].
Available on the market are semi-active and active dampers, which have a better ability to adjust damping to a specific use than passive dampers. Passive dampers, however, are cheaper, and their damping performance is sufficient for many everyday applications.
The damping of a system, or material, is characterized by different physical parameters, details of which can be found in these works: [19] (pp. 397, 411-412), [20] (pp. 5-6). Hysteresis [21] (pp. 380-390) and the loss tangent (tan δ) [19] (p. 411) are the most often used. The higher the tan δ value, the more the energy is dissipated in one cycle of deformation in the given temperature-frequency conditions. Likewise, the higher the hysteresis value, the more the energy is dissipated in one loading-unloading cycle.
Active dampers are used in buildings, where, depending on external conditions, such as vibrations of the foundation due to e.g., earthquake, damping characteristics are adjusted in order to obtain the best vibration amplitude decrease. An example of passive dampers with viscous damping media is a buffer (an elastomeric damper used in trains), in which elastomer in a steel cylinder is compressed recurrently. Other examples include: • Sandwich structures that comprise of steel plates and elastomer between the plates, where elastomer is sheared [18]; • Solid of revolution shape dampers, where elastomer is compressed [22]; • Oval Leaf Spring-type structures, where the material of a damper is bent [23].
Although passive dampers have been in use for many years, some issues have not yet been clarified, such as the dependence of damping characteristics on the damper structure and geometry.

Additive Manufacturing (AM) and FDM Method
The terms additive manufacturing and 3D printing are commonly used in literature interchangeably. Additive manufacturing techniques have been widely discussed in the literature:
FDM is a material extrusion technique, where plastic material-filament in the form of a thin wire (approximately 1.75 mm or 3.00 mm in diameter)-is wound on a spool. It is fed mechanically into the extrusion print head by a set of two counter-rotating grooved cylinders or gears. The polymer is heated, melted and extruded onto the previous layer of polymer, or the printing bed, through the nozzle, which is positioned relative to a heated platform using computer software. The polymer layers are fused. The printing bed is lowered by a given value. After printing and removing the raft, the element is instantly ready to use.
The FDM method is widely applied in medicine [31,32], mechanical engineering and construction [33][34][35][36]. For electrical engineering applications [37,38], it seems that the use of the FDM technique in printing soft material parts and their mechanical properties has not been fully explored yet.
In the small-scale production of parts-prototypes using AM methods that are below 100 units, the lead time is comparable to other production techniques. The cost of production of the single part is six times lower than for injection molding [39]. Owing to its low cost, FDM is an available technique for many groups of researchers and entrepreneurs worldwide, who contribute to FDM method development and 3D printing knowledge dissemination. It is also worth pointing out that since the year 2000, FDM has been the most commonly used AM method worldwide. The worldwide thermoplastic elastomers demand is increasingly rising and in 2014 it was estimated to be at 4,200,000 tons [40] (p. 7).
The FDM printing speed is related to the material chemical structure (polymer crystallization speed). The anisotropy of the mechanical properties of the produced items is also an important factor to consider [29,41].
Moreover, the FDM printing method enables the manufacturing of soft [29] or very stiff parts [33]. Despite disadvantages, e.g., high-quality filament extrusion in filament fabrication step, a printing speed that depends on the material and a low-resolution printing technique compared to other AM methods, the FDM printing technique still retains flexibility. It is understood as the method that is susceptible to changes in the different levels of polymer parts manufacturing [41].

Polymers and Thermoplastic Elastomers
Polymers, which are basic engineering materials, have many advantages, such as a low density, good toughness to density ratio, low price per kilogram of material, very good shape mapping capability and good chemical resistance. Common applications of plastics include dampers, which are low hardness polymers/elastomers, household appliances, pipes and small gears, which are medium toughness polymers, sports car bodies and wind turbines external parts, which are very stiff polymer/composites and many more. However, new cutting-edge polymers, with better mechanical and physicochemical properties, are being developed every day.
The market offers many types of polymers that can be used for the fabrication of 3D printing filaments. Many materials that fit for injection molding can be used in the FDM printing process. Prints, as well as injection molded parts, can be further heat-treated or subjected to initial mechanical deformation. This makes adjusting print properties to specific operating conditions possible.
Detailed information about the damping of polymers and tan δ parameter can be found in works [53][54][55]. Attention should be given to the fact that elastomers have the highest damping capacity.
TPEs constitute a group of polymers that can withstand a large strain without breaking (several hundred per cent) and have a high impact resistance. Compared to other engineering polymers, TPEs have a low hardness and very good damping capacity. TPEs are also recyclable and easily processed by injection molding or extrusion [40].
TPEs can be divided into: TPE-S (styrene hard segment), TPE-V or TPV (dynamically vulcanized TPEs), TPE-O (TPEs with polyolefin soft and/or hard segment), TPEs consisting of halogenic derivatives of polyolefins and rubber, TPE-U, TPE-A (amide hard segment), TPE-E and other TPEs [40] (p. 3). The most important of the above mentioned are TPE-S, TPE-U and TPE-E due to their good mechanical properties. There are also other types of thermoplastic polymers that have good mechanical properties, such as EVA. This polymer is worth mentioning at this point but is not addressed in this paper.
However, the present knowledge shows that thermoplastic elastomer filaments have not gained enough popularity among researchers that deal with damping protection [58] (pp. 81-98).

Manufacturing Process Management (MPM)
Designer and printing technologies have to keep to specific algorithms or printing process methodology in order to keep the highest printed part quality.
Layman in printing usually uses a simplified approach to the printing process, which comprises of two steps: the selection of material to print and the selection of geometry of a printed part. Designers and technologists have to be aware of the fact that there are more steps than those mentioned above and that they affect print quality to a high degree [59].
In the work [41], researchers present a "materials and process selection protocol". It is comprised of the following elements: Evaluation-printability and properties; In reference [59], authors present a different approach to the print production process: • Pre-process, encompassing steps such as product development, design, material selection, material composition, slicing and deposition strategy; • In-process: loading of material, liquification, pressure, extrusion, plotting, bonding and support; • Post-process: component cooling, support removal, mechanical finish and chemical finish.
The protocols mentioned above lack an in-depth analysis of each step. They do not explain how each step contributes to the damping of prints made of thermoplastic elastomer material. Therefore, we propose a modified protocol that designers or technologists may use in the design process of prototype fabrication.
With regards to [41] approach, the first step, which was the selection of material, was discussed in more detail. We added the "geometry of a print" as a second step. The third step, "printing", was replaced with "selection of technological parameters". The fourth step, "evaluation-printability and properties", was replaced with "post-printing treatment". We explained how post-printing treatment is related to the properties of a print. The fifth step was "result", which was the quality assessment of a fabricated print ( Figure 3).

Summary-Need of the Study
According to our literature review, there is a lack of works that link additive manufacturing, thermoplastic elastomer filaments, the 3D printing FDM method and the production of small-scale dampers (damping phenomenon). An element of novelty is also the use of additive manufacturing in the quick production of parts designed for urban freight

Summary-Need of the Study
According to our literature review, there is a lack of works that link additive manufacturing, thermoplastic elastomer filaments, the 3D printing FDM method and the production of small-scale dampers (damping phenomenon). An element of novelty is also the use of additive manufacturing in the quick production of parts designed for urban freight transport and telematics. It is also worth noting that technologies presented in this work can eliminate the production of very costly injection molds.
Based on the data and information given above, we can formulate a thesis that in urban freight transport there is a need to provide telemetric devices and appropriate vibration protection for the human body. In order to adjust vibration to a specific application, one can use the multilevel design and manufacturing process protocol presented in this work. Damping absorbers can be readily produced using the FDM method and elastothermoplastic filament (Figure 4).

Summary-Need of the Study
According to our literature review, there is a lack of works that link additive manufacturing, thermoplastic elastomer filaments, the 3D printing FDM method and the production of small-scale dampers (damping phenomenon). An element of novelty is also the use of additive manufacturing in the quick production of parts designed for urban freight transport and telematics. It is also worth noting that technologies presented in this work can eliminate the production of very costly injection molds.
Based on the data and information given above, we can formulate a thesis that in urban freight transport there is a need to provide telemetric devices and appropriate vibration protection for the human body. In order to adjust vibration to a specific application, one can use the multilevel design and manufacturing process protocol presented in this work. Damping absorbers can be readily produced using the FDM method and elastothermoplastic filament (Figure 4). It is essential to adjust the design process to make it more predictive in avoiding sources of vibrations in mechanical systems. The effects of decreased vibrations, i.e., lower amplitudes, in the mechanical system, should translate into producing parts of higher It is essential to adjust the design process to make it more predictive in avoiding sources of vibrations in mechanical systems. The effects of decreased vibrations, i.e., lower amplitudes, in the mechanical system, should translate into producing parts of higher quality, lower machine failure rate and better health and comfort of workers at places exposed to vibrations.
The relationship between the damping and micro-and macrostructure of absorbers produced using additive manufacturing methods needs to be clarified.

Vibration Test
Vibrations caused by roadway failures are measured by accelerometers in vehicle modules or simply in driver's smartphone. That data can then be transferred to vehicle microcontroller and further analysed. Work [60] presents simple approach. Using smartphone or other device, such as iPad, with accelerometers, transversal, longitudinal and vertical components of acceleration were recorded. Values of transversal component of acceleration represent turning or rocking of vehicle body, longitudinal values represent accelerating or slowing down of a vehicle, vertical values represent vertical movements of vehicle body. Using this simplified approach, authors of present publication recorded dataset of three acceleration components, which were analyzed afterwards.
Discussion on the sensors embedded in mobile devices is given in number of publications, including biomechanics in the field of health sciences [61][62][63], geology and geophysics [64,65], which includes a technical description of software intended to make tests in the field of vibroacoustics.
This discussion indicates that accuracy of sensors varies from group to group. In particular, authors of works [64,65] are critical when dealing with stability and accuracy of magnetometers and clinometers. They suggest to compare the reading of device with other analogue devices very often. In turn, publications [61][62][63] point out good correlation of mobile accelerometer readings with those used in clinical research. Robert Bosch GmbH uses mobile devices embedded sensors to vibroacoustic measurements [66].
Authors of present work assumed measuring range of accelerometers in 4th generation iPad to be 2 g, i.e., approximately 20 m/s 2 at 0.1 m/s 2 measurement accuracy. These parameters are in line with data from specialistic websites, e.g., Phyphox [67]. Official data on sensors used in iPad device are not available to general public.
The aim of present publication was to develop simple and initial methodology to test the damping of small vibroisolators. Thus, freely available mobile devices were used. Using the high precision accelerometers in a calibration and testing procedure is intended in the next step of the research. In particular, fragile shipments delivery monitoring 5G telematics and their resistance to vibrations will be researched.
Vibration-inducing device was mechanical sieve shaker Morek Multiserw type LPzE-2e, with excitation frequency 50 Hz. Dampers were glued to the sieve shaker using double-sided 0.2 mm thick tape ( Figure 5). Afterwards, iPad was attached to dampers using the same manner as mentioned above.  Data registration in vibration tests: iPad commercial device with Matlab Mobile, sampling rate 100 Hz, accelerometers work in +/−20 m/s 2 (2 g) acceleration range, 8 bit resolution. For each sample three amplitudes: 0.5 mm, 1 mm and 1.5 mm, were used and three acceleration components were recorded.
Peak-to-peak amplitude for each dataset in experiment (Table 1) was then calculated. Damping was calculated by dividing amplitude peak-to-peak for each sample by amplitude for system without dampers.

Model Symbol
Model Geometry Infill Density, % Remarks C100 Cylinder 100 Infill type-linear Data registration in vibration tests: iPad commercial device with Matlab Mobile, sampling rate 100 Hz, accelerometers work in +/−20 m/s 2 (2 g) acceleration range, 8 bit resolution. For each sample three amplitudes: 0.5 mm, 1 mm and 1.5 mm, were used and three acceleration components were recorded.
Peak-to-peak amplitude for each dataset in experiment (Table 1) was then calculated. Damping was calculated by dividing amplitude peak-to-peak for each sample by amplitude for system without dampers.

Printing Parameters and Conditions
Small-scale absorbers used to determine stress-strain curve and relationship between max compression strain in one cycle and energy dissipated, were fabricated with use of MakerBot Replicator 2X printer. Authors used following filament: 1.75 mm in diameter, 3D UNIVERSAL filament known under the name UNIFLEX 75 ® . This filament had hardness of 75 Shore A and elongation at break 650%. Printing parameters: absorber geometry = cylinder 10 mm high and diameter 12 mm, infill type = linear, infill density = 0%, 50% and 100% (see Table 1), printing temperature = 245 • C, cooling fan speed = 100%, layer height = 0.2 mm and number of shells (walls) = 3. Slicer software was provided by MakerBot Replicator 2X printer manufacturer.
With the use of computer-aided design/computer-aided manufacturing (CAD/CAM) FreeCAD software, vibration dampers were designed. Damper geometries used in analysis are shown in Figure 6. hardness of 75 Shore A and elongation at break 650%. Printing parameters: absorber geometry = cylinder 10 mm high and diameter 12 mm, infill type = linear, infill density = 0%, 50% and 100% (see Table 1), printing temperature = 245 °C, cooling fan speed = 100%, layer height = 0.2 mm and number of shells (walls) = 3. Slicer software was provided by Mak-erBot Replicator 2X printer manufacturer.
With the use of computer-aided design/computer-aided manufacturing (CAD/CAM) FreeCAD software, vibration dampers were designed. Damper geometries used in analysis are shown in Figure 6. Each absorber volume was approximately 1000 mm 3 . This was an optimum value between a load that a single damper can withstand and printing time which needs to be as low as possible. Height of each damper was set to 10 mm. Each absorber volume was approximately 1000 mm 3 . This was an optimum value between a load that a single damper can withstand and printing time which needs to be as low as possible. Height of each damper was set to 10 mm.

Compression Test
The compression tests were carried out on a universal testing machine type AGS-X, Shimadzu, Japan. Traverse speed was set to 5 mm/min. Cyclic tensile test methodology can be found elsewhere in literature [68]. Cyclic compression test is conducted in the same way as tensile test, but sample is compressed instead. Sample was loaded with increasing force to the point where deformation reaches value 0.1, then unloaded to 0 N force. Next cycles were conducted cognately to increasing deformation: 0.2, 0.3, 0.4, 0.5 and 0.6. Hysteresis is taken as integral of load vs compression strain and expressed in units of J/mm 3 ; see work [69].
After comparing the values of hysteresis and maximum compression in a given cycle, diagram was prepared. This was followed by curve fitting with polynomial of degree 3. Equation and R 2 value were added into the chart.

Criterions
For each step of MDMP, one can adjust printing process parameters to meet desired criteria. In FDM technology, one can specify: lowest price criteria, lowest production time, lowest waste, highest quality, the best mechanical properties or performance criteria. Due to thesis of present work, authors decided to maximize damping in each MDMP step.

Selection of Material
Thermoplastic elastomers have a structure that varies depending on such factors as the soft-to-hard segment ratio and soft and hard segment molecular mass. It causes the structure and properties to change even though it is still the same polymer chemically [70] (pp. 3236-3237), [40] (pp. 161-164). For example, the copolymer soft segment length affects the mechanical properties of thermoplastic elastomer poly(trimethylene terephthalate)block-poly(ethylene oxide) (PTT-b-PEO), with a soft segment length of 1130 g/mol and 3130 g/mol, and loss tangent values of 0.24 and 0.14, respectively [71].
Depending on the monomer type and synthesis method, it is possible to obtain various thermoplastic elastomers with different structures and physical and chemical properties [70] (pp. 3236-3237), [72] (pp. [10][11][12][13][14][15][16][17][18][19][20]. Regarding the chemical structure of the macromolecule, the hardness and its other mechanical properties, including the damping characteristic of the polymer, vary. Table 2 shows examples of properties of main thermoplastic elastomer types commonly used in the industry. The most significant factors in the context of damping are tan δ, which is, as mentioned above, the qualitative damping indicator, modulus of elasticity, hardness and low glass transition temperature (T g ). The T g of the polymer is the transition temperature below which the polymer behaves like a very stiff solid, and above which it behaves like a viscoelastic solid. Concerning the processing temperature, the FDM is similar to injection molding/extrusion techniques.
The hardness of general TPE groups is similar and is in the range of 30 ShA ÷ 75 ShD. During the design process of dampers, hardness needs to be selected for a specific application. When mechanical damage is likely to occur, the designer should choose a higher hardness material.
The modulus of elasticity is the stiffness of a material. Given a constant force acting on the printed part, the higher the modulus of elasticity, the less compliant the TPE material is to deformation. Therefore, it is more difficult to reach higher values of hysteresis (Figure 7b). It should be considered that the TPE's modulus of elasticity is not a constant value in the whole range of deformations [40] (p. 166).  The damping data are shown on two bar diagrams ( Figure 8). The upper diagram is the horizontal compression damping, which is the damping measured in the direction transversal of an iPad. The lower diagram is the vertical compression damping, which is the damping measured in the direction longitudinal of the iPad device ( Figure 5). Phase separation due to the complete or limited miscibility of copolymer blocks is a very well-known behavior of plastics [70] (p. 3236). Two-phase polymer materials are of two types: blends of homopolymers (mechanical mixtures) [40] (pp. 181-182) and block copolymers [72] (pp. 51,54). The morphology has a great impact on the overall properties of both groups of polymers mentioned above [40] (p. 182), [75,76]. As a result of the limited miscibility two-phase material, excellent mechanical and damping properties are obtained.
Block copolymers characterized by the size of the domains of 20 nm are compositions with the highest damping capacity, while approximately 100 nm give the material a higher impact resistance [72] (p. 165).
The compounding process leads to a polymer with new properties. In order to improve the mechanical properties and performance of the filament, various additives are used, e.g., antioxidants, nucleating agents, flame retardants, colorants, antistatic agents, slip agents, fillers and plasticizers. Of these, the most important are fillers: TiO 2 , carbon nanofibers, montmorillonite, graphite, graphene [77], chopped fiberglass, copper and bronze powder and carbon black [43]. In general, fillers that are popular in the last two decades, such as carbon black (CB), multiwall carbon nanotubes (MWCNT) or nano clay (NC), decrease damping and reduce shrinkage of TPEs, while additives such as hydrocarbon oils cause plasticizing of the compound (Table 3). Interestingly, the addition of graphite results in increased damping. The compounding of the filament material components results in numerous new applications.

The Geometry of a Printed Part
The results of the compression test are presented in Figure 7a. The stress-strain curve shows that it is characteristic of soft TPE material. The plastic deformation is small when compared to the maximal strain in each cycle.
The damping data are shown on two bar diagrams (Figure 8). The upper diagram is the horizontal compression damping, which is the damping measured in the direction transversal of an iPad. The lower diagram is the vertical compression damping, which is the damping measured in the direction longitudinal of the iPad device ( Figure 5). The damping data are shown on two bar diagrams (Figure 8). The upper diagram is the horizontal compression damping, which is the damping measured in the direction transversal of an iPad. The lower diagram is the vertical compression damping, which is the damping measured in the direction longitudinal of the iPad device ( Figure 5). Values of damping lower than 1.0 mean that damping occurs. The lower the value, the higher the damping.
The mechanical sieve shaker-dampers-iPad system turned out to be very unstable Values of damping lower than 1.0 mean that damping occurs. The lower the value, the higher the damping.
The mechanical sieve shaker-dampers-iPad system turned out to be very unstable in excitation, with amplitudes higher than 1.5 mm. In this case, the dampers detached from the lower surface of the iPad. In amplitudes lower and equal to 1.5 mm, detachment did not occur.
Data gathered show that every damper failed to reduce the amplitude of vibration in the direction perpendicular to the iPad surface. Therefore, data referring to this direction were excluded from further analysis. This also indicated that the dominating deformation type was bending of the samples, rather than compression of the samples. This behavior is explained by the fact that the stiffness is higher in the direction parallel to the damper side wall.
The iPad device used in this study was not heavy enough to move the damper to an area of high damping. Figure 7b shows that the damping rises with the power of three, and thus heavier objects would induce a higher deformation and eventually a higher damping of the damper. Vibroisolators characterized by a higher infill density should be used with heavier loads. For telematics, whose mass is not too high, dampers with a relatively small volume and infill density are more effective.
Another step of the analysis of the vibration test data is to analyze the influence of the deviation of the side walls' direction with respect to the vertical direction on damping. In this case, a general conclusion cannot be drawn, since the results of the damping are ambiguous. For example, in the horizontal direction, KP dampens more than KD in every case. While for the vertical direction, and in case of amplitudes 0.5 mm and 1 mm, KD dampens more. Similar behavior is seen for the pair of samples PP and PD, where PD in the horizontal direction dampens more if the excitation amplitudes are 1 mm and 1.5 mm. If 0.5 mm is used, then PD has worse damping. In case of vertical compression, PD has worse damping than PP in every vibration amplitude.
In general, the highest damping shown is by damper C00, KP and KD. The damping is slightly lower only for the horizontal and 1 mm excitation amplitude. Damper C00 turned out to be the most effective damper type from tested geometries.
In the horizontal direction, and at 1 mm amplitude, damping turns out to be lower for C00, KP and KD. To our surprise, the pyramid turned out to be inferior to the cylinder and cube geometry.

The Effect of Printing Parameters on Damper Properties
Printing parameters affecting mechanical properties and damping include deposition temperature, slicing and deposition strategy, single layer height and infill density [59].
Research in the additive manufacturing FDM field lacks works that explain how those parameters relate to the damping capacity of absorbers. Therefore, authors of the present publication could not discuss in detail the relationship between each printing parameter and damping. Some works explicitly show the relationship between energy absorption and damping, while others only concentrate on describing the pure mechanical properties of prints.
Thermoplastic elastomers have been used in FDM as well as in injection molding with success over many years [84]. The modulus of elasticity, loss tangent and hysteresis of the thermoplastic elastomer parts produced by injection molding and FDM are directly related to the process temperature. The higher the processing temperature, the higher the loss tangent, and the lower the modulus of elasticity and hysteresis of the soft block copolymer damper [84]. These are linked to structure. At lower processing temperatures, the polymer morphology is dominated by oriented cylinders. Injection molding and FDM have the same operating principle: a polymer in higher temperatures is melted and extruded through a nozzle and finally cooled down. Therefore, when increasing the printing temperature, a decrease in hysteresis is anticipated. The energy absorption is also dependent on the slicing and deposition strategy, e.g., a cylindrical-shaped polyamide print has the best energy absorption when printed in a circular manner and has the worst when printed horizontally [85]. The influence of layer thickness on the mechanical properties and damping for polyurethane thermoplastic elastomer is vague and beyond the scope of the present publication [86]. The results of our own research show that the lower the infill density, the better the damping of the small damper-iPad system (see Figure 8).
The most significant capability of FDM is printing parts of various infill types and degrees. The infill can range from 0% (print with only the outer wall) to 100% (the part without voids) [87]. The infill of a print is linear [42], lattice or honeycomb [34,88]. The latest research in the AM field shows that using FDM enabled obtaining even more complicated structures of infill, such as gyroid [30] or sea urchin-inspired supportless infill [81]. The impact of infill type on the damping of dampers made from thermoplastic elastomers is vague and not explained in literature as well.

Post-Printing Treatment
The main components of the possible post-printing treatment of a damper material are mechanical treatment, thermal treatment, chemical treatment and machining.
The mechanical properties of a polymer are temperature and strain-dependent, which is referred to as the temperature [89] and mechanical history of the polymer, including Mullins effect [19] (p. 585), [72] (p. 563), [71]. Generally, during thermal treatment, the polymer crystallinity increases, e.g., annealing [90] and mechanical deformation [81] (p. 49). Damper made of TPE material and compressed to a deformation of 50% is characterized by the increase in modulus of elasticity, dissipated energy and the plastic component of deformation (Figure 7a,b). When stiffer TPE is used, an increase in dissipated energy is anticipated [91].
In [92], it is reported that PLA tensile test samples after chemical treatment of the outer surface with dichloromethane vapors are distinguished by a higher tensile strength and lower elongation at break. TPE mechanical properties, as well as damping, should change after chemical treatment with specific solvent vapors. There is a lack of works that explain this phenomenon regarding TPE prints subjected to a compression test.
Chemical treatment is related to the chemical resistance of TPE. In general, the TPE's resistance to various aggressive fluids depends on the chemical composition of the polymer. TPE-S is compliant with several solvents: cyclohexane, toluene, methyl ethyl ketone, diethyl ether and styrene. Mixtures of naphtha and toluene, hexane and toluene and hexane-toluene-ketone are known to be excellent solvents [40] (p. 170). Solvents of TPE-U divide into non-polar and polar. The former does not affect TPE-Us and include hexane and heptane. The latter are excellent solvents and include dimethylformamide, tetrahydrofuran, N-methyl pyrrolidone, dimethylacetamide and dimethyl sulfoxide [40] (p. 223). The TPE-E's chemical compliance is composition and stiffness dependent. Ones with higher stiffness are more resistant to chemical solvents. However, TPE-Es are moderately resistant to acetone [40] (pp. 253-254). TPE-Vs, because of polypropylene (PP), which is a dominant part of this material, are very resistant to various solvents.
Reference [93] presents Computer Numerical Control (CNC) machining of print made from ABS polymer. Tests show that the quality of print surface after the machining operation increases. Besides, the quality of the print surface is cutting-depth dependent. Low hardness TPEs are difficult to machine materials. Machining can deteriorate the printed part surface. Therefore, the importance of soft TPE prints machining in ultimate treatment is marginal.
Reference [46] indicates that the print surface quality can be improved using a hot air jet. Increasing the air jet temperature and decreasing the air flow results in a decrease in surface roughness. The behavior that parts with a notch characterize by lower toughness and impact resistance is a well-known phenomenon. However, such behavior for the compression testing and damping of TPE samples is ambiguous. Therefore, along with CNC machining, it should be treated as insignificant.

Conclusions
Each level of MDMP enables the tailoring of the damping. At level I, a designer can choose one of many TPE groups. These have different physical properties, such as the modulus of elasticity, hardness and tan δ. FDM and TPE jointly create a pair one may use to solve technological or economic issues today; for example, avoiding fabricating very costly injection molds for small-scale production, or the possibility of tailoring the properties of prototypes to a specific use. At level II, geometry is also a significant factor. Using a similar TPE volume, but different geometry, hysteresis and damping may vary. The cylinder (C00) and hollow cube-type (KP, KD) absorber show the highest damping. Dampers, such as the pyramid (PP, PD) and cylinder (C100, C50), turned out to be characterized by the lowest damping. At level III, the optimal printing temperature value, layer height, infill density, slicing and deposition strategy and printing speed have to be selected. Each of the printing parameters influence the damping of a print in a different way. For example, if the printing temperature rises, the damping decreases, and if the infill density is low, the light telematics are dampened better. The layer height turned out to be difficult to characterize. A literature review shows that its influence on mechanical properties and damping is vague. At level IV, the post-processing operation is a final step of MDMP. The thermal and mechanical treatment affects the vibration absorber damping. The machining and air jet treatment are considered marginal for soft thermoplastic elastomers. The surface chemical treatment deserves little attention when compared to the thermal and mechanical treatment. It is worth noting that when the damper is deformed from 0 to 40% strain, damping increases from 0 to over 0.2 mJ/mm 3 (Figure 7b).
An example of MDMP information flow may look as follows: a designer-selected TPE-S polymer used as a base material due to the fairly good hardness and highest tan δ. The geometry of the damper is the cylinder. Optimal printing parameters are the deposition temperature = recommended by filament manufacturer, layer height = 0.2 mm and infill density = 0%. The ultimate step is the mechanical compression post-printing treatment in order to increase hysteresis value.
As the authors of the present publication have shown, these absorbers made from thermoplastic elastomers have a high potential to become a new class of electric vehicles systems elements.
Future research opportunities and research directions. As a result of advanced research using FEM and modal analysis, the influence of geometry and material parameters on vibration damping can be optimized. The fabrication and analysis of simple geometry dampers is of key importance. After acquiring the knowledge of the simple geometry dampers' mechanical behavior, one can design, print and analyze complex geometry dampers.
With regards to the damping-structure relationship of small-scale elastomer dampers, basic research still needs to be carried out. It is still unclear how basic parameters such as printing layer height, print orientation and internal structure, surface quality, chemical and mechanical finish affect vibration absorbers damping under consideration.
The effect identified during tests was the low mass of telematics that were used in this work (lower than 1 kg). In connection with a relatively good stiffness of small dampers, in order to obtain desired damping, vibroisolators should have an infill density close to 0% and a low cross-section area. However, the long-lasting use of dampers with such an area is vulnerable to fatigue cracking. Therefore, future research should involve the development of new solutions in damper macro geometry that allow for the use of composite materials. Moreover, one needs to take into consideration the use of two-nozzle two-component 3D printers in order to fabricate dampers with tough elastic outer walls and a soft core. Producing novel, soft and good damping filament material is also an option to consider. Figure 9 shows a vertically mounted telematic device (here, a smartphone was used as a telematic device model) that will withstand both an impact or vibrations coming from the source located in back of the plate.

Data Availability Statement:
The data presented in this study are available on request from the corresponding author. The data are not publicly available due to novel character of research.