Chemical Composition Variations of Altered and Unaffected Coals from the Huaibei Coalﬁeld, China: Implications for Maturity

: The composition characteristics of altered coals in the Huaibei Coalﬁeld, China, was investigated through a comparative analysis between altered and unaffected coals from the Wolonghu, Taoyuan and Renlou coal mines. Results indicated that the altered coals in Wolonghu coal mine are mostly anthracite coals, with a maximum vitrinite reﬂectance of 1.6–3.9% (average of 2.9%). Coals from Wolonghu coal mine were mainly consisted of vitrinite (66.2–97.0%), followed by inertinite (2.0–4.0%) and exinite (0.4–6.9%). Differences in volatile matter content were observed between the altered coals in Wolonghu coal mine and unaffected coals from neighboring coal mines, implying that the chemical composition and maturity of coals were changed after magmatic alteration. In addition, differences in hydrogen element were noted among the coals from Wolonghu, Renlou and Taoyuan coal mines, and the phenomenon of “deﬁcient in hydrogen element” was observed in Wolonghu coals. The aliphatic hydrocarbon structure parameters suggested that the aliphatic chain lengths of Wolonghu coals are shorter than those of coal samples from the Renlou and Taoyuan coal mines. In addition, maturity is positively correlated with hydrogen enrichment degree, but negatively related with aliphatic hydrocarbon structure. Coals from Renlou and Taoyuan coal mines showed great weight loss with various heating rates at temperatures of 0–1000 ◦ C, whereas those from Wolonghu coal mine had less weight loss. at various heating rates. These plots indicate that the pyrolysis rate of sample WL16-17 is lower than that of samples from the Renlou and Taoyuan coal mines in the pyrolysis temperature range of 450–800 ◦ C. The pyrolysis rate decreases and then increases gradually after reaching its maximum value. The pyrolysis rates of these three samples are relatively stable and display similar change tendencies from 0 to 450 ◦ C.

• Detailed comparative analyses of magma altered and unaffected coals were carried out. • Hydrogen exhibits significantly difference between the magma altered and unaffected coals. • Aromatization degree is closely related with maximum vitrinite reflectance. • Mass fraction of coals varies greatly between 450-1000 • C with different heating rates.

Introduction
Altered coals are commonly observed in coal mines (both surface and underground) worldwide. Differences in the geological conditions (temperature, pressure and materials) of magmatic intrusion may usually cause geochemical anomalies in coals. One example is the element exchange in coal during magmatic intrusion [1][2][3]. This stage enriches some harmful elements [2], but the impact on rare earths is not pronounced [4,5]. Vanadium the former, but the latter includes the Shanxi and Upper and Lower Shihezi Formations. Magmatic rocks have generally developed in the mining area and have severely altered the Nos. 6, 7, 8, and 10 coal seams. The magma flow goes from south to north along the fault belts and coal seams. The plutonic rocks of the Wolonghu coal mine are the products of magmatic activity during the Yanshan orogeny of the late Cretaceous. Moreover, the Yanshanian magmatic intrusion can be divided into four stages [6,26]. The first stage is neutral magmatic rock, which is closely related to the E-W structure and distributed near the Subei fault. The coals from the Wolonghu coal mine were altered by magma during this period (>145 Ma) [26]. The fourth stage is basic and ultrabasic magmatic rocks, which are found near the Zhahe syncline and Sunan Syncline in the east of Huaibei Coalfield. Although located in this area, the magma has minimal influence on the coal seams of Taoyuan and Renlou coal mines. Thus, all the selected coals from Wolonghu, Taoyuan and Renlou coal mines can be compared to reveal the influence of magma intrusion on coal seams.

Samples Collection
On the basis of the distribution of magma-altered coal mines, 28 coal samples were collected from Wolonghu coal mines. The sampling sites are shown in Figure 1c. From the perspective of the mining faces, the coal samples collected from the Wolong coal mine are all altered coals. For comparison, eight and 11 unaffected coal samples were gathered from the Taoyuan and Renlou coal mines, respectively. The number of samples collected varied due to the different development conditions of the working face in each coal mine; however, this does not affect the analysis. The selected coals are dominated by bright coal, followed by semi-bright coal. The coals have developed staggered or stepped fracture and occasionally sliding surfaces. All the collected coal samples were analyzed by means of proximate, maceral analyses, and maximum vitrinite reflectance (R max ) test based on the China National Standard GB/T212-2008, GB/T8899-2013, and GB/T6948-1998, respectively. Prior to measurement, the polished flat surfaces of all selected coals were dried, and the desmocollinite was selected as the object. Moreover, the maceral and mineral contents were quantified by means of grid statistics after compositional characterization. All results from the above measurements are listed in Table 1.

Ultimate Analysis
Element content was measured using an elemental analyzer (MACRO Cube, Vario, Frankfurt, Germany) equipped with an infrared detector following the China National Standard GB/T 476-91. Prior to measurement, all the coals were dried and smashed to a diameter of 200 mesh, and each coal sample weighed approximately 1 g. The samples were tested while the instrument increased the set temperature over a short time of <45 min. The measured values were calculated according to the above standard operation guide, and the detection range for the elements was >100 ppm.

Fourier-Transform Infrared Spectroscopy (FTIR) Analysis
The organic matter structure of the coals was studied through Fourier infrared spectrometry using American Society of Testing Materials Standard ASTM C1441-2013. Prior to measurement, all the coals were powered to a diameter of approximately 200 mesh and coal sample of 1-2 g weight each were prepared. The coals and the dried potassium bromide were placed in an agate mortar at a volume ratio of 1:180, and then ground and scanned under the Fourier infrared spectrometer lamp with a spectral range of 400-4000 cm −1 and a resolution of 2 cm −1 . During measurements, each coal sample was scanned 32 times. After scanning, the baseline of the Fourier infrared spectrum was processed, and peaks were fitted using the Origin 9.0 software (OriginLab, Northampton, MA, USA). The area ratios of several special peaks in the infrared spectrum can reflect the differences of each sample. On the basis of the hydrocarbon generation and evolution of functional groups, the parameters of fat structure and hydrogen enrichment degree were computed as follows: where K al is the aliphatic hydrocarbon structure parameter, A(2920 cm −1 ) is the area of the CH stretching vibration peak in the aliphatic chain or alicyclic ring, A(2850 cm −1 ) is the area of the CH 2 stretching vibration peak. It is worth noting that a high K al value implies a long fat chain.
where I HO is the hydrogen enrichment degree parameter that represents the hydrocarbon generation capacity and aliphatic hydrocarbon content; and A(CH 2 ), A(CH 3 ), and A(C = C) are the area of stretching vibration absorption peaks of CH 3 and CH 2 and corresponding to the wavenumbers of 2950, 2920, and 2850 cm −1 , respectively.

Thermogravimetric Analysis
Thermogravimetric experiment was conducted by TG-DSC (Labsys Evo, Lyon, France) following the China National Standard GB/T 27761-2011. This instrument was equipped with a temperature sensor, and the resolution is ±0.1 • C. Its temperature measurement range was 0 to 1200 • C, and the carrier gas was nitrogen with purity of >99.9%. Prior to measurement, a 10 ± 0.1 mg sample of dried coal with a diameter of approximately 200 mesh was prepared. The temperature of each coal sample was increased from room temperature to <1200 • C at heating rates of 2 • C/min, 5 • C/min and 10 • C/min.

Coal Rank and Basic Characteristics of Coals
The coal rank and basic features of coals in the Wolonghu coal mine are listed in Table 1. The R max is in the range of 1.6% to 3.9% with an average value of 2.9%. The selected coal samples with R max values of <2.5% accounted for 21.4% ( Figure 2); of which R max values of >2.5% yield values of 78.6% predominated in the Wolonghu coal mine. By contrast, the R max values of coals from the Renlou and Taoyuan coal mines are 0.5-1.0% (average of 0.8%) and 0.5-0.9% (average of 0.7%), respectively (Table 1). This finding suggests that almost of all the magma-altered coals in the Wolonghu coal mine are anthracite coals, whereas the unaffected coals of the latter two coal mines are low-rank bituminous coals.
where Kal is the aliphatic hydrocarbon structure parameter, A(2920 cm −1 ) is the area of the CH stretching vibration peak in the aliphatic chain or alicyclic ring, A(2850 cm −1 ) is the area of the CH2 stretching vibration peak. It is worth noting that a high Kal value implies a long fat chain. 2 3 =(A(CH )+A(CH ))/A(C=C) HO I (2) where IHO is the hydrogen enrichment degree parameter that represents the hydrocarbon generation capacity and aliphatic hydrocarbon content; and 2 A(CH ) , 3 A(CH ) , and A(C=C) are the area of stretching vibration absorption peaks of CH3 and CH2 and corresponding to the wavenumbers of 2950, 2920, and 2850 cm −1 , respectively.

Thermogravimetric Analysis
Thermogravimetric experiment was conducted by TG-DSC (Labsys Evo, Lyon, France) following the China National Standard GB/T 27761-2011. This instrument was equipped with a temperature sensor, and the resolution is ±0.1 °C. Its temperature measurement range was 0 to 1200 °C, and the carrier gas was nitrogen with purity of >99.9%. Prior to measurement, a 10 ± 0.1 mg sample of dried coal with a diameter of approximately 200 mesh was prepared. The temperature of each coal sample was increased from room temperature to <1200 °C at heating rates of 2 °C/min, 5 °C/min and 10 °C/min.

Coal Rank and Basic Characteristics of Coals
The coal rank and basic features of coals in the Wolonghu coal mine are listed in Table 1. The Rmax is in the range of 1.6% to 3.9% with an average value of 2.9%. The selected coal samples with Rmax values of <2.5% accounted for 21.4% ( Figure 2); of which Rmax values of >2.5% yield values of 78.6% predominated in the Wolonghu coal mine. By contrast, the Rmax values of coals from the Renlou and Taoyuan coal mines are 0.5-1.0% (average of 0.8%) and 0.5-0.9% (average of 0.7%), respectively (Table 1). This finding suggests that almost of all the magma-altered coals in the Wolonghu coal mine are anthracite coals, whereas the unaffected coals of the latter two coal mines are low-rank bituminous coals.   16.9%), volatile matter (4.9-10.7%; average of 8.3%) and moisture (1.6-6.1%; average of 3.0%). The magma-altered coals from the Wolonghu coal mine have lower volatile matter content than the unaffected coals from the Renlou (17.3-39.8%; average of 29.2%) and Taoyuan (14.7-37.1%; average of 31.1%) coal mines, but have higher fixed carbon than the latter two coal mines, with values of 50.1-87.8% and a mean value of 71.9% (Figure 3b). Notably, the volatile matter content in most coals from the Wolonghu coal mine is lower than 10% with several exceptions (Table 1), and these coals are characterized by relatively low ash and fixed carbon contents. The moisture contents of unaffected coals from the Renlou and Taoyuan coal mines are lower than those of almost all coals from the Wolonghu coal mine with values of 0.7-2.8% (average, 2.1%) and 2.2-2.9% (average of 2.5%), respectively.   Figure 3b). Notably, the volatile matter content in most coals from the Wolonghu coal mine is lower than 10% with several exceptions (Table 1), and these coals are characterized by relatively low ash and fixed carbon contents. The moisture contents of unaffected coals from the Renlou and Taoyuan coal mines are lower than those of almost all coals from the Wolonghu coal mine with values of 0.7-2.8% (average, 2.1%) and 2.2-2.9% (average of 2.5%), respectively.

Element Contents of Coals
The elemental contents of the selected coal samples are listed in Table 2. The Wolonghu coals predominately consisted of C, ranging from 53.3% to 86.1% with a mean value of 72.5%. Its N, O and S element contents are 1.1-2.4% (average of 1.8%), 0.2-7.6% (average of 5.1%) and 0.3-0.8% (average of 0.4%), respectively. Notably, the distributions of the aforementioned elements in Wolonghu coals are similar to those in the coals from the Renlou and Taoyuan coal mines ( Figure 4). However, the H element exhibits different intervals for the above three coal mines, that is, coals from Wolonghu, Renlou and Taoyuan coal mines are 1.9-3.5% (average of 2.8%), 4.2-4.8% (average of 5.1%) and 4.8-6.0% (average of 5.5%), respectively ( Figure 4c).

Element Contents of Coals
The elemental contents of the selected coal samples are listed in Table 2. The Wolonghu coals predominately consisted of C, ranging from 53.3% to 86.1% with a mean value of 72.5%. Its N, O and S element contents are 1.1-2.4% (average of 1.8%), 0.2-7.6% (average of 5.1%) and 0.3-0.8% (average of 0.4%), respectively. Notably, the distributions of the aforementioned elements in Wolonghu coals are similar to those in the coals from the Renlou and Taoyuan coal mines ( Figure 4). However, the H element exhibits different intervals for the above three coal mines, that is, coals from Wolonghu, Renlou and Taoyuan coal mines are 1.9-3.5% (average of 2.8%), 4.2-4.8% (average of 5.1%) and 4.8-6.0% (average of 5.5%), respectively ( Figure 4c).

FTIR Characterisitics of Coals
The 47 Fourier infrared spectrograms for the studied coal samples were normalized, baseline-corrected, and smoothed. Typical coal samples from the Wolonghu, Renlou and Taoyuan coal mines are listed and shown in Figure 5. The absorption peaks and trends of coals exhibit substantial differences among the aforementioned coal mines. For alkyl groups, double peaks were observed in the alkyl (C-H) region of the high-wavenumber section of coals from the Wolonghu coal mine and have developed with small absorption intensities in the measured wavenumber interval. However, the absorption intensity at relatively high wavenumber peak (2920 cm −1 ) is greater than that at lower wavenumber peak (2850 cm −1 ). The alkyl bands in the low-wavenumber section have bimodal characteristics and yield higher peak values than those in the high-wavenumber section. In addition, the absorption intensity at 1460 cm −1 (asymmetric bending vibration of CH2

FTIR Characterisitics of Coals
The 47 Fourier infrared spectrograms for the studied coal samples were normalized, baseline-corrected, and smoothed. Typical coal samples from the Wolonghu, Renlou and Taoyuan coal mines are listed and shown in Figure 5. The absorption peaks and trends of coals exhibit substantial differences among the aforementioned coal mines. For alkyl groups, double peaks were observed in the alkyl (C-H) region of the high-wavenumber section of coals from the Wolonghu coal mine and have developed with small absorption intensities in the measured wavenumber interval. However, the absorption intensity at relatively high wavenumber peak (2920 cm −1 ) is greater than that at lower wavenumber peak (2850 cm −1 ). The alkyl bands in the low-wavenumber section have bimodal characteristics and yield higher peak values than those in the high-wavenumber section. In addition, the absorption intensity at 1460 cm −1 (asymmetric bending vibration of CH 2 and CH 3 bases) is greater than that at 1380 cm −1 (symmetrical bending vibration of CH 3 Energies 2021, 14, 3028 8 of 17 base). The alkyl groups of Wolonghu coals have similar characteristics to those from the Renlou and Taoyuan coal mines. In the high-wavenumber section, bimodal patterns and small absorption intensity can be observed. In the low-wavenumber section, the absorption intensity is higher than that in the high-wavenumber section. and CH3 bases) is greater than that at 1380 cm −1 (symmetrical bending vibration of CH3 base). The alkyl groups of Wolonghu coals have similar characteristics to those from the Renlou and Taoyuan coal mines. In the high-wavenumber section, bimodal patterns and small absorption intensity can be observed. In the low-wavenumber section, the absorption intensity is higher than that in the high-wavenumber section. Aromatic hydrocarbons (CH-based stretching vibration) in the high-wavenumber section of Wolonghu coal samples show a unimodal distribution, and the absorption peak is relatively weak. By contrast, the aromatic hydrocarbons (C=C) in the mid-wavenumber section exhibit deformations and vibrations and are characterized by a bimodal pattern with great absorption intensity. This absorption intensity is larger in a higher wavenumber (1600 cm −1 ) than in a low wavenumber (1550 cm −1 ) region. In addition, the absorption intensity of the low-wavenumber section is greater than that of the highwavenumber region. Coal samples from the Renlou and Taoyuan coal mines show single peaks in the high-wavenumber section, but with relatively weak developed absorption Aromatic hydrocarbons (CH-based stretching vibration) in the high-wavenumber section of Wolonghu coal samples show a unimodal distribution, and the absorption peak is relatively weak. By contrast, the aromatic hydrocarbons (C=C) in the mid-wavenumber section exhibit deformations and vibrations and are characterized by a bimodal pattern with great absorption intensity. This absorption intensity is larger in a higher wavenumber (1600 cm −1 ) than in a low wavenumber (1550 cm −1 ) region. In addition, the absorption intensity of the low-wavenumber section is greater than that of the high-wavenumber region. Coal samples from the Renlou and Taoyuan coal mines show single peaks in the high-wavenumber section, but with relatively weak developed absorption intensity. Aromatic hydrocarbons show double peaks in the middle-wavenumber section, and their Energies 2021, 14, 3028 9 of 17 absorption intensities reach a medium degree. Moreover, the absorption intensity of aromatic hydrocarbon base in the low-wavenumber section is greater than that in the high-wavenumber section.
K al and I HO were calculated using Equations (1) and (2), and the results are listed in Table 3. The I HO of coal samples in Wolonghu coal mine ranges from 0.0 to 0.8 (average of 0.1), that in Renlou coal mine ranges from 0.3 to 0.9 (average of 0.5), and that in Taoyuan coal mine it ranges from 0.3-0.6 (average of 0.5) (Figure 6a). These findings show that the aliphatic hydrocarbon content of coal samples from the Wolonghu coal mine is smaller than those of the Renlou and Taoyuan coal mines. The K al of coals from the Wolonghu coal mine is 0.8-3.1 with an average value of 1.9, and those of coals in Renlou and Taoyuan coal mines is 1.0-2.4 (average of 1.6) and 1.1-2.1 (average of 1.1), respectively (Figure 6b). These results show that the aliphatic chains of coals from Wolonghu coal mine are longer than those of samples from the Renlou and Taoyuan coal mines. On the basis of the relatively low proportion of H element and the length of the aliphatic chain of coals in the Wolonghu coal mine, the result indicates that the number of aliphatic chain in Wolonghu coal mine is smaller than in the Renlou and Taoyuan coal mines.  intensity. Aromatic hydrocarbons show double peaks in the middle-wavenumber section, and their absorption intensities reach a medium degree. Moreover, the absorption intensity of aromatic hydrocarbon base in the low-wavenumber section is greater than that in the high-wavenumber section.
Kal and IHO were calculated using Equations (1) and (2), and the results are listed in Table 3. The IHO of coal samples in Wolonghu coal mine ranges from 0.0 to 0.8 (average of 0.1), that in Renlou coal mine ranges from 0.3 to 0.9 (average of 0.5), and that in Taoyuan coal mine it ranges from 0.3-0.6 (average of 0.5) (Figure 6a). These findings show that the aliphatic hydrocarbon content of coal samples from the Wolonghu coal mine is smaller than those of the Renlou and Taoyuan coal mines. The Kal of coals from the Wolonghu coal mine is 0.8-3.1 with an average value of 1.9, and those of coals in Renlou and Taoyuan coal mines is 1.0-2.4 (average of 1.6) and 1.1-2.1 (average of 1.1), respectively (Figure 6b). These results show that the aliphatic chains of coals from Wolonghu coal mine are longer than those of samples from the Renlou and Taoyuan coal mines. On the basis of the relatively low proportion of H element and the length of the aliphatic chain of coals in the Wolonghu coal mine, the result indicates that the number of aliphatic chain in Wolonghu coal mine is smaller than in the Renlou and Taoyuan coal mines.

Pyrolysis Characteristics of Coals
Figure 7a-c show the pyrolysis behavior of coals from the Wolonghu, Renlou and Taoyuan coal mines at a heating rate of 10 °C/min. The temperatures corresponding to the pyrolysis rate values of coal samples from the above three coal mines are 650 °C, 450 °C and 420 °C, respectively. This finding indicates that the coal samples of the latter two coal mines require higher temperature to reach the maximum pyrolysis rate compared with the magma-altered coals from the Wolonghu coalmine. Figure 7d-f reveal substantial differences in the pyrolysis rates of the coals at various heating rates. These plots indicate that the pyrolysis rate of sample WL16-17 is lower than that of samples from the Renlou and Taoyuan coal mines in the pyrolysis temperature range of 450-800 °C. The pyrolysis rate decreases and then increases gradually after reaching its maximum value. The  Taoyuan coal mines at a heating rate of 10 • C/min. The temperatures corresponding to the pyrolysis rate values of coal samples from the above three coal mines are 650 • C, 450 • C and 420 • C, respectively. This finding indicates that the coal samples of the latter two coal mines require higher temperature to reach the maximum pyrolysis rate compared with the magmaaltered coals from the Wolonghu coalmine. Figure 7d-f reveal substantial differences in the pyrolysis rates of the coals at various heating rates. These plots indicate that the pyrolysis rate of sample WL16-17 is lower than that of samples from the Renlou and Taoyuan coal mines in the pyrolysis temperature range of 450-800 • C. The pyrolysis rate decreases and then increases gradually after reaching its maximum value. The pyrolysis rates of these three samples are relatively stable and display similar change tendencies from 0 to 450 • C.

Pyrolysis Characteristics of Coals
In general, a high heating rate leads to a high pyrolysis rate. For instance, the maximum pyrolysis rate is −0.0043 mg/min at heating rate of 2 • C/min, which corresponds to the temperature of 640 • C. The maximum pyrolysis rate is −0.0095 mg/min at 5 • C/min, and the temperature is 514 • C. When the heating rate is 10 k/min, the maximum pyrolysis rate is −0.0187 mg/min and the temperature is 557 • C. The pyrolysis rate of sample RL16-2 has similar variation tendency with WL16-17, but the maximum pyrolysis rates are −0.0347 mg/min (429 • C), −0.09388 mg/min (447 • C), −0.168546 mg/min (461 • C), −0.326496 mg/min (476 • C).   Figure 8 shows the plots of the relationship between weight loss and temperature in coal samples from the above three coal mines. Figure 8a-c suggest that the selected coals show varying characteristics at a heating rate of 10 °C/min. Compared with the Wolonghu coals, the mass fraction of the Renlou and Taoyuan coals changed greatly and exhibited a remarkable mass loss. Figure 8d shows that in the pyrolysis temperature interval of 0 to 450 °C, the mass fraction of sample WL16-17 is relatively stable at various heating rates and is within the range of −0.02-0%. At 450 to 1000 °C, the mass fraction changes greatly with different heating rates that follow the order: 2 °C/min > 5 °C/min > 10 °C/min. The mass fraction changed from 0.99 to 0.83 at the heating rate of 2 °C/min and changed from 1.00 to 0.94 at 10 °C/min. At the end of pyrolysis, the weight loss ratios of different heating rates are 16.6%, 13.2%, and 10.5%. For sample RL16-2 from the Renlou coal mine ( Figure   Figure 7. The pyrolysis rates at 10 • C/min (a-c) and various heating rates (d-f) of the selected coal samples from the Wolonghu, Taoyuan and Renlou coal mines in the Huaibei Coalfield. Figure 8 shows the plots of the relationship between weight loss and temperature in coal samples from the above three coal mines. Figure 8a-c suggest that the selected coals show varying characteristics at a heating rate of 10 • C/min. Compared with the Wolonghu coals, the mass fraction of the Renlou and Taoyuan coals changed greatly and exhibited a remarkable mass loss. Figure 8d shows that in the pyrolysis temperature interval of 0 to 450 • C, the mass fraction of sample WL16-17 is relatively stable at various heating rates and is within the range of −0.02-0%. At 450 to 1000 • C, the mass fraction changes greatly with different heating rates that follow the order: 2 • C/min > 5 • C/min > 10 • C/min. The mass fraction changed from 0.99 to 0.83 at the heating rate of 2 • C/min and changed from 1.00 to 0.94 at 10 • C/min. At the end of pyrolysis, the weight loss ratios of different heating rates are 16.6%, 13.2%, and 10.5%. For sample RL16-2 from the Renlou coal mine (Figure 8e), the initial pyrolysis temperature is approximately 300 • C and the weight-loss ratios at different heating rates are 27.8%, 27.0% and 27.1%, respectively. Similarly, the weight loss ratios of sample TY15-6 from the Taoyuan coal mine are 26.5%, 38.4% and 32.9%, respectively (Figure 8f).  (Figure 8f).

Influence of Maturity on the Basic Characteristics and Hydrogen Element Content of Coals
Volatile matter and hydrogen contents constitute a large proportion in exinite [2,27,28], and the thermal weight-loss ratio is the largest among the aforementioned macerals [29,30]. These phenomena explain the low exinite content in altered coals.
By examining coals with different maturities from different mining areas of China, Li et al. [31] pointed out that the average contents of vitrinite, inertinite and exinite for anthracite are 64.41%, 34.59% and 0%, respectively. By contrast, the contents of vitrinite and exinite in coals from the Wolonghu coal mine are higher than those in the above studied areas, but that of inertinite is lower. Figure 9 shows the plots of relationships among Rmax, chemical and maceral components of all the selected coal samples from the Huaibei Coalfield. Rmax is positively correlated with moisture content, but shows a weak and negative correlation with ash content (Figure 9a,b). The fixed carbon shows a weak but positive relationship with Rmax (Figure 9c). However, the Rmax shows no relationship with vitrinite, inertinite and exinite contents (Figure 9d-f), and the variations of maceral compositions may be correlated with depositional environments [11].

Influence of Maturity on the Basic Characteristics and Hydrogen Element Content of Coals
Volatile matter and hydrogen contents constitute a large proportion in exinite [2,27,28], and the thermal weight-loss ratio is the largest among the aforementioned macerals [29,30]. These phenomena explain the low exinite content in altered coals.
By examining coals with different maturities from different mining areas of China, Li et al. [31] pointed out that the average contents of vitrinite, inertinite and exinite for anthracite are 64.41%, 34.59% and 0%, respectively. By contrast, the contents of vitrinite and exinite in coals from the Wolonghu coal mine are higher than those in the above studied areas, but that of inertinite is lower. Figure 9 shows the plots of relationships among R max , chemical and maceral components of all the selected coal samples from the Huaibei Coalfield. R max is positively correlated with moisture content, but shows a weak and negative correlation with ash content (Figure 9a,b). The fixed carbon shows a weak but positive relationship with R max (Figure 9c). However, the R max shows no relationship with vitrinite, inertinite and exinite contents (Figure 9d-f), and the variations of maceral compositions may be correlated with depositional environments [11].  Figure 10 shows the negative correlation between Rmax and volatile matter content and suggests that the volatile matter tends to decreases slowly with the increase in maturity. Remarkable variations existed in the volatile matter of coals from the aforementioned coal mines, indicating that the distribution of volatile content is indicative of maturity and magma alteration in the studied coal mines.  Figure 10 shows the negative correlation between R max and volatile matter content and suggests that the volatile matter tends to decreases slowly with the increase in maturity. Remarkable variations existed in the volatile matter of coals from the aforementioned coal mines, indicating that the distribution of volatile content is indicative of maturity and magma alteration in the studied coal mines.
Persuasive evidence is shown in the plots of correlation between the conventional element contents and R max of the collected coal samples. Figure 11a displays that R max is positively related with C content but is negatively correlated with H element content (Figure 11b). R max shows no linear relationship with N and S elements (Figure 11c,d). These findings indicate that the H element content decreases when R max increases, that is, the H element in unaffected coals is higher than that in magmatically altered coal. Therefore, the phenomenon of "deficiency in H element" existed in the latter one. Persuasive evidence is shown in the plots of correlation between the conventional element contents and Rmax of the collected coal samples. Figure 11a displays that Rmax is positively related with C content but is negatively correlated with H element content (Figure 11b). Rmax shows no linear relationship with N and S elements (Figure 11c,d). These findings indicate that the H element content decreases when Rmax increases, that is, the H element in unaffected coals is higher than that in magmatically altered coal. Therefore, the phenomenon of "deficiency in H element" existed in the latter one.
Water molecules include active molecules and inorganic ions in source rocks, which are active in the hydrocarbon generations of kerogen pyrolysis and soluble organic matter. The latter, such as H3O + , H5O2 + , H7O3 + , H9O4 + , and H11O5 + , usually do not react with stabilized organic matter, kerogen, or other parent materials through hydro-dehydration, hydro-decarboxylation and pyrolysis. With continuous burial depth that includes temperature and pressure changes, the coal is strongly squeezed, and the volume of active molecules is constantly compressed. Therefore, molecules can generate a large number of protonic acid beams (H + ).
In addition, the organic matter changes from an unstable to a stable state or polymerizes and condenses into macromolecular kerogen during diagenesis. These compounds then lose hydrogen to some extent and become partially or severely hydrogen-deficient, thus resulting a negatively charged organic matter. The H/C atomic ratio of humic kerogen is generally less than 1. The secondary kerogen after cracking is an organic molecule with a few aromatic and polycyclic arenes as the skeleton, and methyl, carboxyl, and short chain alkyl as the peripheral structure. During hydrocarbon generation, this kind of kerogen becomes strongly negatively charged, and the phenomenon of "deficiency in H element" occurs [6].

Influence of Maturity on the Structure of Organic Matters and Pyrolysis Characteristics of Coals
On the basis of previous studies [32][33][34][35] and the infrared spectral characteristics of coal samples from the Wolonghu, Renlou and Taoyuan coal mines, the hydrogen enrichment degree and aliphatic hydrocarbon structure parameters were chosen for the following discussions. In spectrograms, the spectral peaks are superimposed at certain positions due to the contributions of absorption bands of functional groups to the infrared spectrum; hence, the positions and boundaries of absorption peaks are difficult to determine. Hydrogen enrichment degree is indicative of aliphatic hydrocarbon and can represent the length of aliphatic chains [36]. The content of aliphatic hydrocarbons can explain the hydrocarbon generation capacity of coal [36]. In this work, the coal generation capacity of Wolonghu coal mine coal is smaller than that of the Renlou and Taoyuan coal mines, and this finding is consistent with the industrial analysis of coals ( Table 2).
As shown in Figures 12 and 13, Rmax is negatively related to IHO in all the selected coals but is merely positively correlated with the Kal in the Wolonghu coals. The above analyses Water molecules include active molecules and inorganic ions in source rocks, which are active in the hydrocarbon generations of kerogen pyrolysis and soluble organic matter. The latter, such as H 3 O + , H 5 O 2 + , H 7 O 3 + , H 9 O 4 + , and H 11 O 5 + , usually do not react with stabilized organic matter, kerogen, or other parent materials through hydro-dehydration, hydro-decarboxylation and pyrolysis. With continuous burial depth that includes temperature and pressure changes, the coal is strongly squeezed, and the volume of active molecules is constantly compressed. Therefore, molecules can generate a large number of protonic acid beams (H + ).
In addition, the organic matter changes from an unstable to a stable state or polymerizes and condenses into macromolecular kerogen during diagenesis. These compounds then lose hydrogen to some extent and become partially or severely hydrogen-deficient, thus resulting a negatively charged organic matter. The H/C atomic ratio of humic kerogen is generally less than 1. The secondary kerogen after cracking is an organic molecule with a few aromatic and polycyclic arenes as the skeleton, and methyl, carboxyl, and short chain alkyl as the peripheral structure. During hydrocarbon generation, this kind of kerogen becomes strongly negatively charged, and the phenomenon of "deficiency in H element" occurs [6].

Influence of Maturity on the Structure of Organic Matters and Pyrolysis Characteristics of Coals
On the basis of previous studies [32][33][34][35] and the infrared spectral characteristics of coal samples from the Wolonghu, Renlou and Taoyuan coal mines, the hydrogen enrichment degree and aliphatic hydrocarbon structure parameters were chosen for the following discussions. In spectrograms, the spectral peaks are superimposed at certain positions due to the contributions of absorption bands of functional groups to the infrared spectrum; hence, the positions and boundaries of absorption peaks are difficult to determine. Hydrogen enrichment degree is indicative of aliphatic hydrocarbon and can represent the length of aliphatic chains [36]. The content of aliphatic hydrocarbons can explain the hydrocarbon generation capacity of coal [36]. In this work, the coal generation capacity of Wolonghu coal mine coal is smaller than that of the Renlou and Taoyuan coal mines, and this finding is consistent with the industrial analysis of coals ( Table 2).
As shown in Figures 12 and 13, R max is negatively related to I HO in all the selected coals but is merely positively correlated with the K al in the Wolonghu coals. The above analyses indicate that magma intrusion reduces the content of aliphatic hydrocarbons in coal and weakens the hydrocarbon generation capacity. However, the length of the aliphatic hydrocarbon chain is characteristically similar to that in the coal samples from the areas that have not been invaded by magma. A positive relationship between the aliphatic hydrocarbon chain length and maturity is observed for the coal samples in the intrusive zone but not for those in the non-invaded zone. In addition, the content of aliphatic hydrocarbons is related to the maturity of the collected coals in the Huaibei Coalfield.
In summary, the following hypotheses for the high initial pyrolysis temperature of coals can be put forth: (1) the inorganic components of Wolonghu coals were changed by magma. Li et al. [31,36] believed that the minerals in coals inhibit the pyrolysis of various components, and the internal minerals can hinder the early ignition of two bituminous coal cokes. However, Wu [37] and Zhao et al. [38,39] pointed out that Fe 2 O 3 and minerals have a catalytic effect on coal reactivity and NH 3 release. On the basis of the aforementioned analyses and the element distributions of coals from the Huaibei Coalfield, the minerals of coals in magmatic intrusion area may hinder their pyrolysis, and the pyrolysis rate of these coals is relatively lower than that of the unaffected coals. (2) Organic components were changed during pyrolysis. The aromatic bonding increased, and the aliphatic bonds showed opposite characteristics compared with the former. The bond energy of aromatic bonds was greater than that of fatty bonds.
Three persuasive reasons for the low weight loss ratio of sample WL16-17 can be assumed. The first factor is maturity. When R max is greater than 2.0, the sample is in a high-over mature stage, indicating that the organic matter of coal has generated hydrocarbons [2,10]. Second, the structure parameter of FTIR suggests that the hydrogen enrichment parameter (average of 0.1) of Wolonghu coals is lower than that of Renlou coals (Table 3). Furthermore, the Wolonghu coals show a relatively low proportion of exinite compared with the Renlou and Taoyuan coal mines.
In summary, the heating rate affects pyrolysis. When the heating rate is high, the change of heat transfer rate from surface to interior of coal is inconsistent with that of heating rate. By contrast, the temperature gradient of each layer is relatively small, and the internal temperature is consistent. Therefore, the pyrolysis time of the inner layer only slightly differ.   In summary, the following hypotheses for the high initial pyrolysis temperature of coals can be put forth: (1) the inorganic components of Wolonghu coals were changed by magma. Li et al. [31,36] believed that the minerals in coals inhibit the pyrolysis of various components, and the internal minerals can hinder the early ignition of two bituminous coal cokes. However, Wu [37] and Zhao et al. [38,39] pointed out that Fe2O3 and minerals have a catalytic effect on coal reactivity and NH3 release. On the basis of the aforementioned analyses and the element distributions of coals from the Huaibei Coalfield, the minerals of coals in magmatic intrusion area may hinder their pyrolysis, and the pyrolysis rate of these coals is relatively lower than that of the unaffected coals.
(2) Organic components were changed during pyrolysis. The aromatic bonding increased, and the aliphatic bonds showed opposite characteristics compared with the former. The bond energy of aromatic bonds was greater than that of fatty bonds.
Three persuasive reasons for the low weight loss ratio of sample WL16-17 can be assumed. The first factor is maturity. When Rmax is greater than 2.0, the sample is in a highover mature stage, indicating that the organic matter of coal has generated hydrocarbons [2,10]. Second, the structure parameter of FTIR suggests that the hydrogen enrichment parameter (average of 0.1) of Wolonghu coals is lower than that of Renlou coals (Table 3). Furthermore, the Wolonghu coals show a relatively low proportion of exinite compared with the Renlou and Taoyuan coal mines.
In summary, the heating rate affects pyrolysis. When the heating rate is high, the change of heat transfer rate from surface to interior of coal is inconsistent with that of heating rate. By contrast, the temperature gradient of each layer is relatively small, and  In summary, the following hypotheses for the high initial pyrolysis temperature of coals can be put forth: (1) the inorganic components of Wolonghu coals were changed by magma. Li et al. [31,36] believed that the minerals in coals inhibit the pyrolysis of various components, and the internal minerals can hinder the early ignition of two bituminous coal cokes. However, Wu [37] and Zhao et al. [38,39] pointed out that Fe2O3 and minerals have a catalytic effect on coal reactivity and NH3 release. On the basis of the aforementioned analyses and the element distributions of coals from the Huaibei Coalfield, the minerals of coals in magmatic intrusion area may hinder their pyrolysis, and the pyrolysis rate of these coals is relatively lower than that of the unaffected coals.
(2) Organic components were changed during pyrolysis. The aromatic bonding increased, and the aliphatic bonds showed opposite characteristics compared with the former. The bond energy of aromatic bonds was greater than that of fatty bonds.
Three persuasive reasons for the low weight loss ratio of sample WL16-17 can be assumed. The first factor is maturity. When Rmax is greater than 2.0, the sample is in a highover mature stage, indicating that the organic matter of coal has generated hydrocarbons [2,10]. Second, the structure parameter of FTIR suggests that the hydrogen enrichment parameter (average of 0.1) of Wolonghu coals is lower than that of Renlou coals (Table 3). Furthermore, the Wolonghu coals show a relatively low proportion of exinite compared with the Renlou and Taoyuan coal mines.
In summary, the heating rate affects pyrolysis. When the heating rate is high, the change of heat transfer rate from surface to interior of coal is inconsistent with that of heating rate. By contrast, the temperature gradient of each layer is relatively small, and

Conclusions
The magma-altered coals in Wolonghu coal mine are mostly anthracite coals with maximum vitrinite reflectance of 1.6-3.9% (average of 2.9%). Differences in volatile matter content were observed between the magma-altered coals and unaffected coals from neighboring coal mines.
The maceral components of magma altered coals from Wolonghu coal mine are consisted of vitrinite group. The vitrinite content of unaffected coals from the Renlou and Taoyuan coal mines is higher than that of coals from the Wolonghu coal mine. In addition, the R max shows no relationship with vitrinite, inertinite and exinite contents, the variations of which may be correlated with the corresponding depositional environments.
H element exhibits different intervals for the studied coal mines. The H element contents of coals from the Wolonghu, Renlou and Taoyuan coal mines are 1.9-3.5% (average of 2.8%), 4.2-4.8% (average of 5.1%) and 4.8-6.0% (average of 5.5%), respectively. The H content in unaffected coal is higher than that in magma-altered coal, and a phenomenon of "deficient in H element" is observed in the latter.
The parameter of aliphatic hydrocarbon structure revealed that the aliphatic chain of the coal samples from Wolonghu coal mine is shorter than that of samples from Renlou and Taoyuan coal mines.
At temperature of 0-450 • C, the mass fraction of coal sample from Wolonghu coal mine is relatively stable at various heating rates. However, the mass fraction at 450-1000 • C changes greatly with different heating rates.