Cost-efficient, Effect of Low-Quality PbI2 Purification to Enhance Performances of Perovskite Quantum Dots and Perovskite Solar Cells

In modern society, high-quality material development and a large stable supply are key to perform frontier research and development. However, there are negative issues to address to utilize high-quality resources with a large stable supply for research, such as economic accessibility, commercialization, and so on. One of the cutting-edge research fields, perovskite-related research, usually requires high-quality chemicals with outstanding purity (>99%). We developed an economically feasible PbI2 precursor with around 1/20 cost-down for perovskite/perovskite quantum dots through recrystallization and/or hydrothermal purification. Following the methodology, the quantum dots from both as-prepared and purified PbI2 demonstrated identical photophysical properties, with a photoluminescence quantum yield (PLQY) of 52.61% using the purified PbI2 vs. 45.83% PLQY using commercial PbI2. The role of hydrothermal energy was also checked against the problematic PbI2, and we checked whether the hydrothermal energy could contribute to the hindrance of undesired particle formation in the precursor solution, which enables them to form enlarged grain size from 179 ± 80 to 255 ± 130 nm for higher photoconversion efficiency of perovskite solar cells from 14.77 ± 1.82% to 15.18 ± 1.92%.


Introduction
In modern research and development (R&D), high-quality products usually require high-quality resources with very low impurity. Current chemical industries successfully developed various strategies to provide high-quality chemicals with high purities up to 99.999% in general, or even higher purities. For example, some modern researchers can purchase high-quality chemicals for their research to elucidate the effect of impurities [1], doping [2], regional deformation [3], or to aim at high performances of various electronic/optoelectronic devices [4]. Limiting impurities in the stage of material synthesis or device fabrication is essential to control experimental factors. This variable control should be performed to reduce negative aspects in numerous R&D fields: byproducts in synthesis, current loss, and/or short circuit current in electronic devices, and non-radiative recombination sites in optoelectronic devices. The market for supplying high-quality chemicals is inevitable for cutting-edge R&D and industrial processes.
Some of the negative aspects of the supply of high-quality chemicals are economic accessibility, production costs, commercialization, and the supply of large amounts for industrial processes. Usually, scientists and engineers need to spend more to obtain PbI 2 with 99.99% purity (purchased from TCI ® ). The hydrothermal also applied to another high purity PbI 2 with 99.9985% (purchased from Alfa Aesar ® ) purity and with undesired dissolution issue at certain reaction batch (LOT:U14E066). Through hydrothermal using the issued PbI 2 , we solved the dissolution issue with enlarged grain and slight improvement of photoconversion efficiency. Our work could provide a practical solution for the researchers to obtain better PbI 2 precursors from economically approachable low-grade sources, which acts like high-quality PbI 2 .

Methods for Lead Iodide Synthesis and Purification
First, 3.793 g lead acetate and 5.29 g potassium iodide were dissolved in 1 L distilled water each. Continuously addition of 3 mL of 4 M Hydrochloric acid to lead acetate solution could prevent its hydrolysis. We mixed the two aqueous solutions gradually with few drops early. As soon as bright yellow lead iodide precipitate was observed in the mixing process. After the precipitate is formed, we heated the remaining solution until the PbI 2 precipitate was dissolved to induce recrystallization. After the observing clean solution, the heat was turned off and then the heated solution was cooled down to room temperature on its own (~2h). Around 2 h later, recrystallized PbI 2 was formed. When the PbI 2 solution's temperature was stabilized, it was placed into a fridge for 3 h to obtain as much PbI 2 from the solution as possible. Recrystallized PbI 2 was consecutively filtered to isolate the PbI 2 . The PbI 2 was dried overnight in a vacuum. Furthermore, hydrothermal was performed after the drying process, according to methods found in the literature [30]. In short, 0.8 g of Lead iodide and 120 mL of DI-water were placed in a 150 mL Teflon-lined Hydrothermal autoclave. We maintained the autoclave at 200 • C for 6 h and then cooled the solution at room temperature; the crystallized PbI 2 was filtered out and dried in a vacuum oven overnight [30].

Synthesis of CsPbI 3 Perovskite Quantum Dots
Cs oleate synthesis: 0.407 g of Cs 2 CO 3 , 1.25 mL of oleic acid (OA) and 20 mL of octadecene (ODE) were placed in a 50 mL three-neck flask and heated to 80 • C for 1 h in a vacuum to remove any water. Then, the temperature was kept at 120 • C for 1 h. The Cs precursor was raised to 140 • C under N 2 until all Cs 2 CO 3 reacted with OA and then naturally cooled to 115 • C.
Pb precursor synthesis: a mixture of ODE (25 mL) and 0.5 g PbI 2 was put in another three-neck flask, and the system was degassed under vacuum at 120 • C for 1 h. In addition, OA 2.5 mL and oleylamine (OLA) 2.5 mL were put in another beaker at 130 • C. After completely removing the water from PbI 2 and ODE, we injected the OA and OLA mixture into another three-neck flask. Afterwards, an injection vacuum was applied to remove the water.
Hot injection: The temperature in the three-neck flask containing ODE, PbI 2 , OA, and OLA was adjusted in a nitrogen environment to 170 • C. When the temperature reached 170 • C, we injected 2 mL of Cs-oleate; we cooled down the temperature by putting an ice bath under the reacting flask. When the temperature reached 60 • C, the supernatant was obtained, and centrifugation at 6000 rpm for 10 min was used to obtain a precipitate of PQDs. The precipitate was obtained, and the PQDs precipitate was dissolved in 10 mL of hexane and N 2 purging for 5 min.

Characterizations of PbI 2 Precursor and CsPbI 3 Perovskite Quantum Dots
TEM images and selective area electron diffraction patterns (SAED) were acquired using a Tecnai G2 F20 S-TWIN (FEI Korea). The XRD was performed using a D8 Advance (Bruker). The X-ray diffractometer was equipped with Cu Kα radiation, 10-80 • with 0.05 deg/step, 0.5 sec/step. UV-Vis absorption and photoluminescence spectrophotometer data were performed using Duetta (HORIBA Scientific). We used excitation light at 435 nm to excite PQDs to prevent overtone up to 800 nm and obtain pristine photoluminescence spectra of the PQDs. The PQDs were compared to the PLQY of riboflavin, as 0.3 [31] for measured PLQY. We used an excitation wavelength of 435 nm to obtain PLQY. X-ray fluorescence spectroscopic analysis (XRF) was characterized through NEX-CG (Rigaku) by fundamental parameter (FP) analysis with Energy-dispersive X-ray fluorescence (ED-XRF) semi-quantitative analytic method.

Perovskite Solar Cell Fabrication and Photoconversion Efficiency Measurement
The patterned Fluorine-doped Tin Oxide (FTO) glass was cleaned by using ultrasonication for 15 min in detergent, deionized (DI) water, acetone, and isopropyl alcohol (IPA). Before use, the cleaned FTO glass was treated with UV/ozone for 20 min. The substrate was then spin-coated with SnO 2 solution (2.75% in DI water) at 3000 rpm for 30 s, annealed at 150 • C for 30 min, and UV/ozone treated for 20 min.
A perovskite precursor solution of MAPbI 3 (1.13 M) was prepared by dissolving PbI 2 and MAI in a mixed solvent of N,N-dimethylformamide (DMF): dimethyl sulfoxide (DMSO) = 4:1 (volume ratio) and heated at 60 • C for 20 min before using. The precursor solution was spin-coated onto SnO 2 at 1000 rpm for 5 s and 5000 rpm for 50 s. In the second step, 600 µL of CB was smoothly dropped on the film when 45 s of the spinning remained. After deposition, the film was annealed at 100 • C for 15 min in an N 2 -filled glove box. The spiro-OMeTAD solution was then prepared by dissolving 91 mg spiro-OMeTAD in 1 mL chlorobenzene after adding 20.9 µL of Li-TFSI in acetonitrile (517 mg/mL) and 35.4 µL of t-BP and spin-coated at 4000 rpm for 30 s. As a counter electrode, 100 nm of Au was deposited by thermal evaporated through a shadow mask under a high vacuum condition (under 10 −5 torr).
Current density-voltage curves (J-V curves) were measured using Keithley 2602A Source Meter under simulated air mass (AM) 1.5 G illumination (100 mW cm −2 ) with a solar simulator (K3000 model, McScience) calibrated using a standard Si reference cell

PbI 2 Synthesis and Purification Using Economical Low-Grade Sources
To obtain economically feasible PbI 2 with affordable quality, by obtaining motivation from "Golden Rain", provided Royal Society of Chemistry, we modified the experiment to synthesize PbI 2 using a precipitation reaction (details in Section 2) [32], as follows: Furthermore, we performed recrystallization and consecutive hydrothermal to obtain bright crystalline PbI 2 crystals with a facet angle. In the Teflon-lined hydrothermal autoclave, an un-crystallized PbI 2 aqueous solution was observed, but we obtained PbI 2 crystals for further work. Table 1 compares the retail prices of PbI 2 and chemicals for PbI 2 synthesis, depending on the purity. Prices of PbI 2 with 98.5%, 99.99%, and 99.9985% purities are 1.47 $/g, 6.42 $/g, and 4.33 $/g, respectively. This comparison shows that a high purity of PbI 2 beyond 99% requires a high expenditure. The price of 99.9985% purity of PbI 2 is three times higher than that of low-grade PbI 2 with 98.5% purity. In contrast, using the mentioned chemicals for PbI 2 synthesis, the retail prices are below 10% of the low-grade PbI 2 with 98.5% purity. Considering reaction (1) and assuming that researchers would experiment crudely so that only 50% yield would be obtained, the price to obtain crystalized PbI 2 could be 0.358 $/g. Comparing the synthesized PbI 2 retail price to low-grade PbI 2 , it is 24% of the price for low-grade PbI 2 . Moreover, comparing the synthesized PbI 2 retail price to high-grade PbI 2 , it is only 8.26% of the high-grade PbI 2 . Even though considering initial costs for the synthesis's tools and systems, the synthesis and purification of PbI 2 can be economically feasible for the long-term view and large-scale production. If photophysical properties (for PQDs) or photoconversion efficiencies (for PSCs) would be similar, the prepared PbI 2 can be an economical alternative instead of commercially available high-cost PbI 2 with high purity. Firstly, to confirm the synthesized and purified PbI 2 as an alternative solution to the high-cost PbI 2 with high purity, X-ray diffraction (XRD) patterns and thermogravimetric analysis (TGA) were obtained and performed, respectively, see Figure 1. Figure 1A shows that the crystallized PbI 2 exhibits identical patterns, the same as commercially available PbI 2 , without additional peaks, which can be either a byproduct or the result of degraded products. Compared to reference (PDF# 01-080-1000), hexagonal PbI 2 with P-3m1 space group was obtained for all PbI 2 chemicals. Even as-synthesized PbI 2 without recrystallization and consecutive hydrothermal, XRD patterns match the pattern from commercial PbI 2 . This result indicates that the crystallized PbI 2 structure was obtained, and identical crystallinity was observed when compared to the commercial PbI 2 .  Figure 1B presents TGA curves for various PbI2 sources. All PbI2 sources do not decrease their weight up to 400 °C, which implies that there is no hydrated form and residual H2O in the powder/crystals. Commercially available PbI2 and as-synthesized PbI2 start to lose their weight around 440 °C and the weight loss is generally expected decomposition of PbI2, to metallic Pb 0 , as follows [33,34]: The broad weight loss profile implies breaking the bond between Pb-I-Pb coordination and sublimation of I2 occurs. Interestingly, all hydrothermal PbI2 from both commercial and as-synthesized ones start to lose their weight around 500 °C, indicating higher thermal stability of PbI2. We speculate that improving crystallinity provides better thermal stability raising decomposition starting temperature up to 60 °C higher than that of PbI2 without hydrothermal. We expect that the enhanced crystallinity could reduce defects. The enhanced crystallinity could provide better stoichiometric coordination between Pb and I, reducing imbalanced charging sites induced by the missing crystal components, which may decrease regional lattice distortion/strain. Thus, incorporating more thermal energy at a higher temperature would need to distort the Pb-I-Pb coordination to induce the thermal decomposition of PbI2 [33]. Table 2 shows the X-ray fluorescence spectroscopic analysis (XRF) and elemental analysis about Pb and I. Other elements were not able to be measured. Interestingly, the hydrothermal process enhances the I/Pb molar ratio to the two PbI2 from both as-synthesized and commercial sources. During the hydrothermal process, the dissolution of PbI2 in the aqueous solution occurred and crystallization occurred while cooling the Teflonlined Hydrothermal autoclave [30]. After the crystallization, improvement of iodide components in the PbI2 implies better crystallinity reduces defects, especially iodide-mediated defects. Furthermore, incorporating a higher amount of iodide in the PbI2 can potentially use the larger amount of iodide to fill the iodide medicated vacancies in the perovskite/PQDs, which acts as non-radiative recombination sites.  Figure 1B presents TGA curves for various PbI 2 sources. All PbI 2 sources do not decrease their weight up to 400 • C, which implies that there is no hydrated form and residual H 2 O in the powder/crystals. Commercially available PbI 2 and as-synthesized PbI 2 start to lose their weight around 440 • C and the weight loss is generally expected decomposition of PbI 2 , to metallic Pb 0 , as follows [33,34]: The broad weight loss profile implies breaking the bond between Pb-I-Pb coordination and sublimation of I 2 occurs. Interestingly, all hydrothermal PbI 2 from both commercial and as-synthesized ones start to lose their weight around 500 • C, indicating higher thermal stability of PbI 2 . We speculate that improving crystallinity provides better thermal stability raising decomposition starting temperature up to 60 • C higher than that of PbI 2 without hydrothermal. We expect that the enhanced crystallinity could reduce defects. The enhanced crystallinity could provide better stoichiometric coordination between Pb and I, reducing imbalanced charging sites induced by the missing crystal components, which may decrease regional lattice distortion/strain. Thus, incorporating more thermal energy at a higher temperature would need to distort the Pb-I-Pb coordination to induce the thermal decomposition of PbI 2 [33]. Table 2 shows the X-ray fluorescence spectroscopic analysis (XRF) and elemental analysis about Pb and I. Other elements were not able to be measured. Interestingly, the hydrothermal process enhances the I/Pb molar ratio to the two PbI 2 from both assynthesized and commercial sources. During the hydrothermal process, the dissolution of PbI 2 in the aqueous solution occurred and crystallization occurred while cooling the Teflon-lined Hydrothermal autoclave [30]. After the crystallization, improvement of iodide components in the PbI 2 implies better crystallinity reduces defects, especially iodidemediated defects. Furthermore, incorporating a higher amount of iodide in the PbI 2 can potentially use the larger amount of iodide to fill the iodide medicated vacancies in the perovskite/PQDs, which acts as non-radiative recombination sites.  Figure 2 demonstrates TEM images and SAED patterns of the CsPbI 3 PQDs using commercially available PbI 2 with 99.99% purity (Figure 2A,C) and crystallized PbI 2 ( Figure 2B,D). Both PQDs show cubic shapes with similar size and size distributions (11.3 ± 2.0 nm PQDs made from the commercial PbI 2 , and 11.04 ± 1.23 nm, another PQDs from hydrothermal PbI 2 , see Figure S1 in supporting information). Note that PQDs made from as-synthesized PbI 2 show a similar cubic shape of PQDs but with a slightly smaller size (9.9 ± 1.4 nm, see Figure S2). Also, observing SAED patterns, the two kinds of PQDs show similar patterns to concentric circles and obtained diffractions from multiple PQDs, which imply the presence of (100), (110), (200) planes in the PQDs. The two insets in Figure 2A,C present identical d-spacing for (100). All of the patterns and d-spacing were matched with XRD patterns obtained from the two kinds of PQDs ( Figure S3). In the XRD patterns from the two PQDs, major peak positions, full width at half maximums (FWHMs), and peak intensity ratios were identical. The two kinds of PQDs made from the crystallized/commercial PbI 2 cannot be distinguished through material characterizations. Therefore, using both commercial/hydrothermal PbI 2 produce the identical material quality of PQDs.  Figure 2 demonstrates TEM images and SAED patterns of the CsPbI3 PQDs usin commercially available PbI2 with 99.99% purity (Figure 2A,C) and crystallized PbI2 (Fig  ure 2B,D). Both PQDs show cubic shapes with similar size and size distributions (11.3 2.0 nm PQDs made from the commercial PbI2, and 11.04 ± 1.23 nm, another PQDs from hydrothermal PbI2, see Figure S1 in supporting information). Note that PQDs made from as-synthesized PbI2 show a similar cubic shape of PQDs but with a slightly smaller siz (9.9 ± 1.4 nm, see Figure S2). Also, observing SAED patterns, the two kinds of PQDs show similar patterns to concentric circles and obtained diffractions from multiple PQDs, whic imply the presence of (100), (110), (200) planes in the PQDs. The two insets in Figure 2A, present identical d-spacing for (100). All of the patterns and d-spacing were matched wit XRD patterns obtained from the two kinds of PQDs ( Figure S3). In the XRD patterns from the two PQDs, major peak positions, full width at half maximums (FWHMs), and pea intensity ratios were identical. The two kinds of PQDs made from the crystallized/com mercial PbI2 cannot be distinguished through material characterizations. Therefore, usin both commercial/hydrothermal PbI2 produce the identical material quality of PQDs.  To compare photophysical properties between the two different PQDs, we performed PLQY measurement of the two PQDs with other PQDs made from as-synthesized PbI 2 . Using as-synthesized, commercial, hydrothermal PbI 2 to the PQD synthetic process, PLQY were obtained as 43.00%, 45.83%, 52.61%, respectively. Enhancement of PLQY can be correlated to using iodide enriched PbI 2 through the hydrothermal process (Table 2). PLQY is described as follows: PLQY of these PQDs consists of two components: radiative decay rate constant (k r ) and non-radiative decay rate constant (k nr ). The k r is the rate constant for radiative recombination such as photoluminescence in these PQDs, and k nr is for non-radiative recombination such as vibration relaxation related processes. The k nr is calculated by considering various aspects in the PQDs, such as various defects (interstitials, charged/neutral vacancies, antisites, surface, etc.) [35] charge transfer medium. In this work, the increment of iodide components can fill the iodide-vacancy mediated defect. This defect-mediate non-radiative recombination process can be hindered so that overall PLQY can be increased. The control of non-radiative radiative recombination is key to reducing the translation of electron energy to vibration energy of lattice atoms, i.e., phonons, which are sources to induce heat generation. Usage of the more efficient radiation process is also an important factor in enhancing contrast in the display devices. Therefore, increasing PLQY with this additional purification process for precursor is essential to solve the major technical issues, such as reducing internal-generated heat and increasing energy efficiency in the display devices.
We also tested the stability of the two kinds of PQDs; compared to the other PQDs made from as-synthesized PbI 2 , the initial emission shapes and intensities were maintained (see Figure 3). In contrast, photoluminescence intensities from the other PQDs (made through as-synthesized PbI 2 ) diminished as time goes by, see Figure S4. These PLQY and stability tests, performed through photoluminescence measurements, photophysical properties between the two kinds of PQDs resembled each other; we found that even using hydrothermal PbI 2 can reduce production cost by 1/20 (6.42 $/g for commercial PbI 2 vs. 0.358 $/g for hydrothermal PbI 2 , see Table 1). electron diffraction (SAED) of CsPbI3 PQDs with using commercial PbI2 with 99.99% purity (c) and with using crystallized PbI2 through hydrothermal (D).
To compare photophysical properties between the two different PQDs, we performed PLQY measurement of the two PQDs with other PQDs made from as-synthesized PbI2. Using as-synthesized, commercial, hydrothermal PbI2 to the PQD synthetic process, PLQY were obtained as 43.00%, 45.83%, 52.61%, respectively. Enhancement of PLQY can be correlated to using iodide enriched PbI2 through the hydrothermal process (Table 2). PLQY is described as follows: PLQY of these PQDs consists of two components: radiative decay rate constant (kr) and non-radiative decay rate constant (knr). The kr is the rate constant for radiative recombination such as photoluminescence in these PQDs, and knr is for non-radiative recombination such as vibration relaxation related processes. The knr is calculated by considering various aspects in the PQDs, such as various defects (interstitials, charged/neutral vacancies, antisites, surface, etc.) [35] charge transfer medium. In this work, the increment of iodide components can fill the iodide-vacancy mediated defect. This defect-mediate nonradiative recombination process can be hindered so that overall PLQY can be increased. The control of non-radiative radiative recombination is key to reducing the translation of electron energy to vibration energy of lattice atoms, i.e., phonons, which are sources to induce heat generation. Usage of the more efficient radiation process is also an important factor in enhancing contrast in the display devices. Therefore, increasing PLQY with this additional purification process for precursor is essential to solve the major technical issues, such as reducing internal-generated heat and increasing energy efficiency in the display devices.
We also tested the stability of the two kinds of PQDs; compared to the other PQDs made from as-synthesized PbI2, the initial emission shapes and intensities were maintained (see Figure 3). In contrast, photoluminescence intensities from the other PQDs (made through as-synthesized PbI2) diminished as time goes by, see Figure S4. These PLQY and stability tests, performed through photoluminescence measurements, photophysical properties between the two kinds of PQDs resembled each other; we found that even using hydrothermal PbI2 can reduce production cost by 1/20 (6.42 $/g for commercial PbI2 vs. 0.358 $/g for hydrothermal PbI2, see Table 1.).

Application of the Hydrothermal Process to Problematic PbI 2 to Make Better Quality of MAPbI 3 Perovskite Film for Enhanced Photoconversion Efficiency of PSCs
To clarify the hydrothermal process's effect to cure the unknown dissolving issue, we used problematic PbI 2 with 99.999% purity to prepare two MAPbI 3 perovskite films, but for one of them, the extra hydrothermal process was applied before using the PbI 2 to make Energies 2021, 14, 201 9 of 12 the perovskite film. As shown in Figure 4, bigger grain sizes were obtained by applying the extra hydrothermal process, even using the identical PbI 2 with the same purity. In Figure S5, grain sizes got bigger from 179 ± 80 to 255 ± 130 nm (for the longest sizes within a grain) and from 64 ± 25 to 111 ± 60 nm (for shortest sizes within a grain). The grain sizes were enlarged around 42-73% with the addition of an extra hydrothermal process. Figure S6a shows that in this PbI 2 with a certain synthetic batch, the PbI 2 did not completely dissolve in the mixed solvent of DMF : DMSO (4:1, volume ratio); we cannot determine the reason. With the addition of the hydrothermal process, we improved the solubility of PbI 2 in the mixed solvent. Note that most PbI 2 dissolve well with MAI by forming lead iodide plumbate complex in the mixed solvent under room temperature, but by applying the hydrothermal process to PbI2, we tried to solve the dissolving issue. Currently, we are doing further investigation to clarify the details of the problematic issue. The presence of the undissolved particles can induce faster crystal film growth at the particle's surface that reacts like a seed, so the particles can cause to skip the necessary process: overcoming an energy barrier to induce the nucleation process. Therefore, relatively smaller grain sizes (~100 nm) were observed in SEM images. In our previous work [36], we obtained larger grains with sizes, about 560 nm). Therefore, the hydrothermal process can obtain a crystallized PbI 2 hexagonal structure and reduce lead halide derivates' unwanted species. This work's concentration makes 350 nm MAPbI 3 layer thickness (see Figure S7), which is the optimized thickness for efficient V oc and fill factor (FF) from our earlier work [36]. Also, note that the UV-Vis. absorption spectra of MAPbI 3 films (see Figure S8) made using commercial PbI 2 or crystallized PbI 2 show an almost similar absorption trend in the visible region, which indicates an almost identical thickness.

Application of the Hydrothermal Process to Problematic PbI2 to Make Better Quality of MAPbI3 Perovskite Film for Enhanced Photoconversion Efficiency of PSCs
To clarify the hydrothermal process's effect to cure the unknown dissolving issue, we used problematic PbI2 with 99.999% purity to prepare two MAPbI3 perovskite films, but for one of them, the extra hydrothermal process was applied before using the PbI2 to make the perovskite film. As shown in Figure 4, bigger grain sizes were obtained by applying the extra hydrothermal process, even using the identical PbI2 with the same purity. In Figure S5, grain sizes got bigger from 179 ± 80 to 255 ± 130 nm (for the longest sizes within a grain) and from 64 ± 25 to 111 ± 60 nm (for shortest sizes within a grain). The grain sizes were enlarged around 42-73% with the addition of an extra hydrothermal process. Figure  S6a shows that in this PbI2 with a certain synthetic batch, the PbI2 did not completely dissolve in the mixed solvent of DMF : DMSO (4:1, volume ratio); we cannot determine the reason. With the addition of the hydrothermal process, we improved the solubility of PbI2 in the mixed solvent. Note that most PbI2 dissolve well with MAI by forming lead iodide plumbate complex in the mixed solvent under room temperature, but by applying the hydrothermal process to PbI2, we tried to solve the dissolving issue. Currently, we are doing further investigation to clarify the details of the problematic issue. The presence of the undissolved particles can induce faster crystal film growth at the particle's surface that reacts like a seed, so the particles can cause to skip the necessary process: overcoming an energy barrier to induce the nucleation process. Therefore, relatively smaller grain sizes (⁓100 nm) were observed in SEM images. In our previous work [36], we obtained larger grains with sizes, about 560 nm). Therefore, the hydrothermal process can obtain a crystallized PbI2 hexagonal structure and reduce lead halide derivates' unwanted species. This work's concentration makes 350 nm MAPbI3 layer thickness (see Figure S7), which is the optimized thickness for efficient Voc and fill factor (FF) from our earlier work [36]. Also, note that the UV-Vis. absorption spectra of MAPbI3 films (see Figure S8) made using commercial PbI2 or crystallized PbI2 show an almost similar absorption trend in the visible region, which indicates an almost identical thickness.  In Figure 5 and Table 3, photovoltaic performances of MAPbI3 PSCs are shown with J-V curves. In addition to the hydrothermal process, overall photovoltaic performances increase. By comparing the two best cells in the two cases, we see that hydrothermal addition enhances FF from 72.31 to 75.88. This increment mainly contributes to improving the photoconversion efficiency of PSCs by incorporating the hydrothermal process. From Figure 4, we speculate that enlarged grain size contributes to reducing the series resistance (Rs) and increasing shunt resistance (Rsh) in the PSCs. Even though the average photoconversion efficiencies between the two cases are in the standard deviation, seeing the distribution of the performances carefully in Figure 5A, we observed the positive contribution In Figure 5 and Table 3, photovoltaic performances of MAPbI 3 PSCs are shown with J-V curves. In addition to the hydrothermal process, overall photovoltaic performances increase. By comparing the two best cells in the two cases, we see that hydrothermal addition enhances FF from 72.31 to 75.88. This increment mainly contributes to improving the photoconversion efficiency of PSCs by incorporating the hydrothermal process. From Figure 4, we speculate that enlarged grain size contributes to reducing the series resistance (R s ) and increasing shunt resistance (R sh ) in the PSCs. Even though the average photoconversion efficiencies between the two cases are in the standard deviation, seeing the distribution of the performances carefully in Figure 5A, we observed the positive contribution of the hydrothermal process to enhance the performance of PSCs. We are also conducting research further to improve the overall purification to obtain enhanced performances significantly. However, so far, it is possible to expect similar performances about PQDs and PSCs, by using the synthesized and crystallized PbI 2 from low-quality sources instead of commercially available high-purity PbI 2 .

Conclusions
In conclusion, we aimed to develop a strategy to utilize the economically feasible low-grade precursors to obtain a comparable quality of material for the cutting-edge research field, perovskite solar cells, and study the photophysical properties of perovskite quantum dots. Through recrystallization and hydrothermal, from low-grade resources, we obtained similar PbI2 with 99.99% purity, and conducted analyses using XRD, TGA, and XRF. We observed that similar structural but heat-resistible PbI2 was obtained through the purification processes, and the iodide component increases after the purification, which can act by increasing photoluminescence quantum yield filling the iodide defect mediated non-radiative recombination sites. Furthermore, the hydrothermal process can promote solubility of PbI2 into the DMF/DMSO mixed solvent with MAI, so hindering undissolved particle formation helps to grow grain bigger and improve photoconversion efficiencies of perovskite solar cells. This work can provide the strategy to enhance the quality of PbI2 precursor for the fabrication of high-quality perovskite/perovskite quantum dots. Also, this work can contribute to the commercialization of perovskite-based applications.
Supplementary Materials: The following are available online at www.mdpi.com/xxx/s1, Figure S1: Histograms about sizes of PQDs, Figure S2: TEM images of PQDs made through as-synthesized PbI2 without further recrystallization/hydrothermal and their histogram, Figure S3: XRD patterns

Conclusions
In conclusion, we aimed to develop a strategy to utilize the economically feasible low-grade precursors to obtain a comparable quality of material for the cutting-edge research field, perovskite solar cells, and study the photophysical properties of perovskite quantum dots. Through recrystallization and hydrothermal, from low-grade resources, we obtained similar PbI 2 with 99.99% purity, and conducted analyses using XRD, TGA, and XRF. We observed that similar structural but heat-resistible PbI 2 was obtained through the purification processes, and the iodide component increases after the purification, which can act by increasing photoluminescence quantum yield filling the iodide defect mediated non-radiative recombination sites. Furthermore, the hydrothermal process can promote solubility of PbI 2 into the DMF/DMSO mixed solvent with MAI, so hindering undissolved particle formation helps to grow grain bigger and improve photoconversion efficiencies of perovskite solar cells. This work can provide the strategy to enhance the quality of PbI 2 precursor for the fabrication of high-quality perovskite/perovskite quantum dots. Also, this work can contribute to the commercialization of perovskite-based applications.