Performance Evaluation of a Direct Absorption Collector for Solar Thermal Energy Conversion

: The solar absorption e ﬃ ciency of water as a base-ﬂuid can be signiﬁcantly improved by suspending nanoparticles of various materials in it. This experimental work presents the photo thermal performance of water-based nano-ﬂuids of graphene oxide (GO), zinc oxide (ZnO), copper oxide (CuO), and their hybrids under natural solar ﬂux for the ﬁrst time. Nanoﬂuid samples were prepared by the two-step method and the photothermal performance of these nanoﬂuid samples was conducted under natural solar ﬂux in a particle concentration range from 0.0004 wt % to 0.0012 wt %. The photothermal e ﬃ ciency of water-based 0.0012 wt % GO nanoﬂuid was 46.6% greater than that of the other nanoﬂuids used. This increased photothermal performance of GO nanoﬂuid was associated with its good stability, high absorptivity, and high thermal conductivity. Thus, pure graphene oxide (GO) based nanoﬂuid is a potential candidate for direct absorption solar collection to be used in di ﬀ erent solar thermal energy conversion applications. time of The maximum mass loss was observed for GO nanofluid and minimum for DI It can be observed during the experimentation the mass loss of all types of nanofluids was enhanced with the enhancement in the concentration of the nanoparticles. Maximum mass loss was achieved in GO nanofluid compared with other nanofluids used in because of the high solar absorptivity. The average mass loss of binary nanofluids increased first and then reduced with the increasing CuO and ZnO concentration, which is higher than that of individual CuO and ZnO nanofluid as in and respectively. The addition of and ZnO nanoparticles in nanoparticles reduced the mixture performance at a CuO and ZnO mass fraction, but greater than that of DI water. Figure shows the mass loss for a specific time duration in the nanofluid of CuO, ZnO, and GO under natural sun over the period of 1800 s of DI water base nanofluids at 0.0004 wt % concentration.


Introduction
Solar energy is the most abundant renewable source, and can be used for space heating [1], electricity generation, desalination, and many other similar applications [2]. Owing to the increase of the population, the depleting trend of non-renewable energy resources must be taken into consideration [3]. Efficient energy use is a difficult task [4]. The existing literature describes different type of collectors that rely upon surface-based solar absorption and heat transfer, which is engaged by collectors to a

Experimental Setup
Nanoparticles of three different materials (CuO, ZnO, and GO) were used in this experimental investigation. The experimental setup consisted of a pyranometer, direct solar absorber, digital scale, K-type thermocouples, and data acquisition system or data logger. The solar radiations were absorbed by the nanofluid present in the sample container. The pyranometer interfaced with the computer through a data logger. As a result of evaporation, weight losses occur, which were measured using a digital scale. K-type thermocouples were used to measure the average temperature of nanofluid. Thermocouples were calibrated using a NIST (National Institute of Standards and Technology) traceable precision glass thermometer with ±0.01 • C and the uncertainty in temperature measurement was ±0.25 • C. The data logger was used to record the data over the time of the experiment. A simplified experimental setup scheme is shown in Figure 1.
Deionized water (IPEX, Inc., Oakville, ON, Canada) was used as a base fluid to prepare nanofluid samples. A petri dish was used as a sample container to hold nanofluid samples. It was so deep that three different thermocouples at three different heights were installed to take the average temperature. It helped in the direct absorption of solar irradiation. It was a cylindrical container with a diameter and height of 7 cm each. Before the start of each experiment, 250 g of water was filled in this petri dish, with different concentrations of nanoparticles.
The petri dish was placed on a digital scale for measuring weight loss in the fluids. Change in bulk fluid temperature was determined by three K-type thermocouples (OEM WRR2-130), which were placed at three typical depths; just at the top surface of the nanofluid, in the middle, and close to the bottom of the petri dish. Ambient temperature was measured with the help of a fourth k-type thermocouple. Light irradiance was measured with a pyranometer (SR30-D1). All data were registered to the computer via a data logger (CX402-XXM).

Experimental Setup
Nanoparticles of three different materials (CuO, ZnO, and GO) were used in this experimental investigation. The experimental setup consisted of a pyranometer, direct solar absorber, digital scale, K-type thermocouples, and data acquisition system or data logger. The solar radiations were absorbed by the nanofluid present in the sample container. The pyranometer interfaced with the computer through a data logger. As a result of evaporation, weight losses occur, which were measured using a digital scale. K-type thermocouples were used to measure the average temperature of nanofluid. Thermocouples were calibrated using a NIST (National Institute of Standards and Technology) traceable precision glass thermometer with ±0.01 °C and the uncertainty in temperature measurement was ±0.25 °C. The data logger was used to record the data over the time of the experiment. A simplified experimental setup scheme is shown in Figure 1.
Deionized water (IPEX, Inc. Oakville ON, Canada) was used as a base fluid to prepare nanofluid samples. A petri dish was used as a sample container to hold nanofluid samples. It was so deep that three different thermocouples at three different heights were installed to take the average temperature. It helped in the direct absorption of solar irradiation. It was a cylindrical container with a diameter and height of 7 cm each. Before the start of each experiment, 250 g of water was filled in this petri dish, with different concentrations of nanoparticles.
The petri dish was placed on a digital scale for measuring weight loss in the fluids. Change in bulk fluid temperature was determined by three K-type thermocouples (OEM WRR2-130), which were placed at three typical depths; just at the top surface of the nanofluid, in the middle, and close to the bottom of the petri dish. Ambient temperature was measured with the help of a fourth k-type thermocouple. Light irradiance was measured with a pyranometer (SR30-D1). All data were registered to the computer via a data logger (CX402-XXM).

Nanofluids' Preparation
Water nanofluids of ZnO, CuO, GO, and their hybrids were prepared by the two-step method. For example, in the preparation of copper oxide nanofluid, sodium hydroxide (NaOH) and copper chloride dehydrate (CuCl 2 :2H 2 O) were used as chemical reagents for synthesis. Copper chloride and sodium hydroxide were used according to a molar ratio (CuCl 2 :NaOH) of 0.5:1 to prepare the solution sample. The amount of CuCl 2 as per the molar ratio was dissolved in 100 ml of deionized water. Precipitating agent (NaOH) was added dropwise in this solution under constant stirring. pH value of 12 was maintained throughout the reaction. NaOH was used as a precipitate agent to control the pH value. NaOH was added dropwise under constant stirring and the solution was mixed with precipitating agent (NaOH) to obtain less chemically dispersed nanoparticles. There is no time limit to control the pH value during the preparations of nanofluids. The precipitate settled down upon the completion of the reaction process. The sample was aged for 10 h afterwards. The precipitate was collected and washed a number of times with deionized water through filter paper to make it free from sodium and chloride ions. These precipitates were dried in an oven at 80 • C for 10 h. The precipitate was ground using a pestle and mortar to a clear black powder. The black powder was sintered at 600 • C in a muffle furnace for 3 h. After the completion of the reaction, the samples were aged for 10 h, because of the nanofluids are settled down on the surface of the beaker and in order to obtain less dispersed nanoparticles. Afterwards, samples were put in the muffle furnace for different times and some changes in the nanofluids were observed, that is, change in the crystal structure, size of the nanofluids, and length of the nanofluid. In this new work, a co-precipitation method was used to prepare nanoparticles, where NaOH was used as the precipitating agent and serves as a terminator for growing the nano-particles because the particles cannot come together easily. Furthermore, it expands during the calcination process, which is why the temperature was 80 • C for 10 h and 600 • C for 3 h. The same procedure was followed for the synthesis of other nanomaterials, that is, GO and ZnO [28].
To make a nanofluid sample in base fluid, a measured amount of nano powder was mixed with a given base fluid volume and the acquired mixture was sonicated for 30 min before starting the photothermal conversion experiment. Three different concentrations (0.0004 wt %, 0.0008 wt %, and 0.0012 wt %) of nanoparticles were used in this research. Nanopowders with a maximum concentration of 0.0012 wt % in the experimental range were suspended in the basefluid using ultrasonication and magnetic stirring. A visual method and absorption spectra were used to evaluate the nanoparticle sedimentation. No sedimentation was observed after suspending the nanoparticles in the base fluid until 30 minutes.
Photothermal conversion experiment of the nanofluids was conducted in a particle concentration range from 0.0004 wt % to 0.0012 wt % for individual water-based nanofluids of GO, ZnO, and CuO. The hybrids (binary nanofluids) GO-CuO and GO-ZnO were analysed at 0.0004 wt % concentration under natural solar flux. Table 1 shows that experiments were carried out on 0.0004 wt % for individual nanofluids of GO, ZnO, and CuO and the hybrid combination of GO-CuO and GO-ZnO. The amount of GO is different, but weight concentrations of hybrid nanofluids are still same by varying the concentration of other nanoparticles used in this study. It was observed that adding a very small amount of nanoparticles in the base fluid enhanced the thermo physical properties of the base fluid and heat transfer rate. Photothermal efficiency was sensitive to concentration mixing ratio in the case of binary nanofluids GO-CuO and GO-ZnO, and extreme addition of an individual nanoparticle component ZnO or CuO lowered performance.

Optical Absorbance
In this study, a UV-vis spectrophotometer (Shimadzu 1800, Japan) was used for evaluating the dispersion stability of the prepared nanofluids. Incident scanning light is thrown on the sample in the wavelength range of 300 to 1000 nm. All data were recorded at room temperature (25 • C). The spectrophotometer works on the principle of Lambert-Beer's law (A = εcl), where A shows absorbance, ε shows the molar absorption coefficient, c shows the molar concentration, and l shows the optical path length. Two cuvettes of weight capacity of 0.0001 g each are used. One cuvette contains the reference base fluid, while other is filled with nanofluid. Incident light of equal intensity is thrown on both the cuvettes and difference in the light is measured by the detectors after passing through the solutions. Hence, a spectrum is obtained between the absorbance and wavelength, which gives the concentration of nanoparticles in nanofluids. After comparing this spectrum trend at a specific wavelength after defined time intervals, the concentration and thus stability of nanoparticles are noted.
In UV-visible regions, different types of nanofluids at 0.0004 wt %, 0.0008 wt %, and 0.0012 wt % concentrations have different absorption peaks. The experimental results showed that different nano-fluids have different peaks of optical absorption over the UV-visible spectrum. The display of copper oxide, zinc oxide, and graphene oxide nanofluids was a broad shoulder around 275 nm, 314 nm and 287 nm, respectively, at three different weight concentrations. The intensity of absorption peaks increased with the rise in the concentration of the nanofluid. The graphene oxide nanofluid absorption peak is higher than that of all the other nanofluids used in this research compared at the same weight particle concentration of 0.0004 wt %, 0.0008 wt %, and 0.0012 wt %, respectively. This is because of the augmented performance of carbon-based nanofluids (GO), which have good stability, high absorptivity, and high thermal conductivity properties, which make them distinct from the others. It can fluoresce over a wide range of wavelengths (from near-infrared to ultraviolet) and effectually reduce the fluorescence of other fluorescent dyes. In contrast, minimum absorbance was observed in the case of deionized (DI) water because, in the visible light spectrum, water is a poor absorber of solar energy. Adding nanoparticles that have good absorptivity in the visible region can significantly enhance the solar absorption of water. Compared with graphene oxide, other nanofluids have their absorption peaks in the UV-visible region. Although nanofluids of ZnO and CuO do not have very strong absorption peaks in the UV region, their absorption is far better than water, which is shown below in Figure 2.
In Figures 3 and 4, the optical properties of composite nanoparticles (GO-ZnO and GO-CuO) are evaluated in UV-vis spectroscopy [45,46]. The spectrum exhibits absorption in the visible and infrared regions, but prominent absorption occurs in the UV region. In both situations of GO-ZnO and GO-CuO composites binary nanoparticles, the absorption peaks of pure GO, pure ZnO, and pure         An increasing linear trend in bulk fluid temperature can be seen by the reading of all three thermocouples at the start of the experiments. However, this increasing trend is not continued later. This is because, at the beginning of the experiment, most of the transferred heat energy results in a linear rise in temperature, and very little heat is wasted to the environment. As the nanofluid temperature increases, the temperature of the nanofluid sample and environment is also increased, which is the reason for the enhanced heat loss and linearity not being observed. The increase in temperature is very little when the value of temperature difference reaches the maximum value, and it is clear that, after 600 s, the linear trend finished and the non-linear trend started somehow during the experiment. Moreover, the temperature rises at a greater rate for TC1 than for that of the other two remaining thermocouples (TC2, and TC3). This is because of the decreasing tendency in solar light irradiance accomplished with the optical length. The highest temperature variation between the top and bottom surfaces of the nanofluid was 3.86 °C.

Change in Fluid Volume Temperature
The environmental temperature remained almost the same during the experiment throughout this study. If the comparison is made between the nanofluids and deionized water temperature, it can be realized that all nanofluids have greater temperature gradients than DI water (see Figure 5. It can also be seen that nanofluids' temperature increased with the increase in nanoparticles' concentration, as presented in Figures 6 and 7 The greatest increase in the average change in temperature (2.51 °C) was achieved in GO nanofluid compared with the other nanofluids used in this study because of high solar absorptivity. The specific capacity of nanofluids was observed to be very close to that of water. Moreover, the difference in the increase in temperature is due to the high  An increasing linear trend in bulk fluid temperature can be seen by the reading of all three thermocouples at the start of the experiments. However, this increasing trend is not continued later. This is because, at the beginning of the experiment, most of the transferred heat energy results in a linear rise in temperature, and very little heat is wasted to the environment. As the nanofluid temperature increases, the temperature of the nanofluid sample and environment is also increased, which is the reason for the enhanced heat loss and linearity not being observed. The increase in temperature is very little when the value of temperature difference reaches the maximum value, and it is clear that, after 600 s, the linear trend finished and the non-linear trend started somehow during the experiment. Moreover, the temperature rises at a greater rate for TC 1 than for that of the other two remaining thermocouples (TC 2 and TC 3 ). This is because of the decreasing tendency in solar light irradiance accomplished with the optical length. The highest temperature variation between the top and bottom surfaces of the nanofluid was 3.86 • C.

Change in Fluid Volume Temperature
Energies 2020, 13, 4956 8 of 16 energy absorption. This increased the average change in temperature, which resulted in the enhancement in photo thermal efficiency as compared with individual nanofluids, except for pure GO nanofluid, because pure GO nanofluid is a carbon-based nanofluid having the highest solar absorptivity compared with other individual nanofluids (ZnO, CuO) and binary nanofluids GO-CuO and GO-ZnO used in this study.  The environmental temperature remained almost the same during the experiment throughout this study. If the comparison is made between the nanofluids and deionized water temperature, it can be realized that all nanofluids have greater temperature gradients than DI water (see Figure 5). It can also be seen that nanofluids' temperature increased with the increase in nanoparticles' concentration, as presented in Figures 6 and 7. The greatest increase in the average change in temperature (2.51 • C) was achieved in GO nanofluid compared with the other nanofluids used in this study because of high solar absorptivity. The specific capacity of nanofluids was observed to be very close to that of water. Moreover, the difference in the increase in temperature is due to the high absorbance of graphene nanofluid (GO) in the visible region. GO is black and carbon-based nanofluid. Thanks to this characteristic, it shows augmented absorptivity of solar irradiation.
The temperature variations for the 0.0004 wt % hybrid nanofluids GO-CuO and GO-ZnO and DI water are displayed in Figures 6 and 7 respectively. The average change in temperature increased initially and then decreased with the increasing copper oxide and zinc oxide concentration, which is still higher than that of individual ZnO and CuO nanofluids. The increase in the wt % of of CuO and ZnO nanoparticles in GO reduced the mixture performances even at lower fractions of of CuO and ZnO nanoparticles, but they were superior to that of DI water. Thus, it can be observed that the addition of GO in metal-oxides nanoparticles, that is, binary nanoparticles, enhanced the overall solar energy absorption. This increased the average change in temperature, which resulted in the enhancement in photo thermal efficiency as compared with individual nanofluids, except for pure GO nanofluid, because pure GO nanofluid is a carbon-based nanofluid having the highest solar absorptivity compared with other individual nanofluids (ZnO, CuO) and binary nanofluids GO-CuO and GO-ZnO used in this study.

Mass Loss of Nanofluids
A digital balance was used to calculate the reduction in mass of the nanofluids because of the evaporation phenomena. The time duration for this measurement was selected as 1800 s under natural sunlight. It is observed that a reduction in the mass of the nanofluids is directly related to the bulk temperature increment. Instead of heating bulk fluid, most of the absorbed energy is used to evaporate fluid. An increment in the temperature of the sample as a whole means that more heat loss occurs to the environment.

Mass Loss of Nanofluids
A digital balance was used to calculate the reduction in mass of the nanofluids because of the evaporation phenomena. The time duration for this measurement was selected as 1800 s under natural sunlight. It is observed that a reduction in the mass of the nanofluids is directly related to the bulk temperature increment. Instead of heating bulk fluid, most of the absorbed energy is used to evaporate fluid. An increment in the temperature of the sample as a whole means that more heat loss occurs to the environment.

Mass Loss of Nanofluids
A digital balance was used to calculate the reduction in mass of the nanofluids because of the evaporation phenomena. The time duration for this measurement was selected as 1800 s under natural sunlight. It is observed that a reduction in the mass of the nanofluids is directly related to the bulk temperature increment. Instead of heating bulk fluid, most of the absorbed energy is used to evaporate fluid. An increment in the temperature of the sample as a whole means that more heat loss occurs to the environment. GO nanofluid and minimum for DI water. It can be observed during the experimentation that the mass loss of all types of nanofluids was enhanced with the enhancement in the concentration of the nanoparticles. Maximum mass loss was achieved in GO nanofluid compared with other nanofluids used in this study because of the high solar absorptivity. The average mass loss of binary nanofluids increased first and then reduced with the increasing CuO and ZnO concentration, which is higher than that of individual CuO and ZnO nanofluid as seen in Figures 9 and 10 respectively. The addition of CuO and ZnO nanoparticles in GO nanoparticles reduced the mixture performance even at a low CuO and ZnO mass fraction, but greater than that of DI water. Figure 8 shows the mass loss for a specific time duration in the nanofluid of CuO, ZnO, and GO under natural sun over the period of 1800 s of DI water base nanofluids at 0.0004 wt % concentration.
Energies 2020, 13, x FOR PEER REVIEW 10 of 17 sun light during the experiment for the time period of 30 min. The maximum mass loss was observed for GO nanofluid and minimum for DI water. It can be observed during the experimentation that the mass loss of all types of nanofluids was enhanced with the enhancement in the concentration of the nanoparticles. Maximum mass loss was achieved in GO nanofluid compared with other nanofluids used in this study because of the high solar absorptivity. The average mass loss of binary nanofluids increased first and then reduced with the increasing CuO and ZnO concentration, which is higher than that of individual CuO and ZnO nanofluid as seen in Figures 9 and 10 respectively. The addition of CuO and ZnO nanoparticles in GO nanoparticles reduced the mixture performance even at a low CuO and ZnO mass fraction, but greater than that of DI water. Figure 8 shows the mass loss for a specific time duration in the nanofluid of CuO, ZnO, and GO under natural sun over the period of 1800 s of DI water base nanofluids at 0.0004 wt % concentration.

Photothermal Efficiency
Photothermal efficiency (PTE) is the ratio between the internal energy increase of fluid to the total incident solar radiation [46].
where CW defines the specific heat capacity of water measured in (J/kgK); Lv is the latent heat of vaporization (J/kg) at a pressure of 1 bar; mloss is the mass loss (mloss = minitial/t) of nanofluid in time

Photothermal Efficiency
Photothermal efficiency (PTE) is the ratio between the internal energy increase of fluid to the total incident solar radiation [46]. where C W defines the specific heat capacity of water measured in (J/kgK); L v is the latent heat of vaporization (J/kg) at a pressure of 1 bar; m loss is the mass loss (mloss = minitial/t) of nanofluid in time t, measured in kg/s; I is the solar irradiance, which is equal to 850 W/m 2 , measured by the pyranometer; m w is the mass of water in (kg); A is the illumination area of the nanofluid sample, measured in m 2 ; and ∆T is the average change in temperature value in time t of three thermocouples. Equation (1) gives this energy analysis, which is translated in the form of photothermal efficiency. Figures 11 and 12 show the photothermal efficiency of water base (GO, ZnO/H 2 O, CuO) nanofluids and their composites (GO-ZnO and GO-CuO) at different wt % concentrations (0.0004 wt %, 0.0008 wt %, and 0.0012 wt %). It can be observed that the photothermal efficiency of all types of nanofluids is directly related to nanoparticle concentration, which is enhanced with the enhancement of the nanoparticle concentration.
Pure GO nanofluid has the highest efficiency relative to other nanofluids used in this research because of its high absorptivity and high thermal conductivity compared with the others. Photothermal efficiency would be higher for nanoparticles of higher thermal conductivity. According to the Fourier law of heat conduction, the heat transfer rate depends on thermal conductivity, which is directly related to temperature. At a higher thermal conductivity, a higher temperature will be achieved, which is the main parameter in calculating the photothermal efficiency.
Pure GO nanofluid has the highest efficiency relative to other nanofluids used in this research because of its high absorptivity and high thermal conductivity compared with the others. Photothermal efficiency would be higher for nanoparticles of higher thermal conductivity. According to the Fourier law of heat conduction, the heat transfer rate depends on thermal conductivity, which is directly related to temperature. At a higher thermal conductivity, a higher temperature will be achieved, which is the main parameter in calculating the photothermal efficiency.

Specific Absorption Rate (SAR)
The specific absorption rate is conventionally defined as energy absorbed per unit mass of nanoparticles. It is an important factor that is also used to calculate the photothermal efficiency of different types of nanofluids. It can be calculated in (kW/g) using Equation (1) [46].
In Equation (2), Cw and mw symbolise the specific heat capacity (J/kgK) and mass (kg) of base fluid (water), respectively. Lv is the latent heat of vaporization (J/kg) at a pressure of 1 bar. ΔTn and ΔTw show the change in nanofluid temperature and base fluid (water) in time Δt, respectively. Figures 13 and 14 show the specific absorption rate (SAR) of binary nanofluids (ZnO-GO and CuO-GO) and individual nanofluids (ZnO, CuO, and GO). Comparing all the nanofluids used, pure GO nanofluid has the maximum specific absorption rate (SAR) at different wt % concentration.

Specific Absorption Rate (SAR)
The specific absorption rate is conventionally defined as energy absorbed per unit mass of nanoparticles. It is an important factor that is also used to calculate the photothermal efficiency of different types of nanofluids. It can be calculated in (kW/g) using Equation (1) [46].
In Equation (2), C w and m w symbolise the specific heat capacity (J/kgK) and mass (kg) of base fluid (water), respectively. L v is the latent heat of vaporization (J/kg) at a pressure of 1 bar. ∆T n and ∆T w show the change in nanofluid temperature and base fluid (water) in time ∆t, respectively. Figures 13  and 14 show the specific absorption rate (SAR) of binary nanofluids (ZnO-GO and CuO-GO) and individual nanofluids (ZnO, CuO, and GO). Comparing all the nanofluids used, pure GO nanofluid has the maximum specific absorption rate (SAR) at different wt % concentration.

Conclusions
The collection of direct solar absorption-based nanofluids is an encouraging technique for solar power generation systems. Many studies on different types of nanoparticles for solar energy state that a comparison for photothermal performance characteristics of various nanofluids at the same experimental conditions is much needed. In direct absorption solar collectors (DASCs), the photothermal conversion efficiency of three nanomaterials (GO, ZnO, and CuO) and their composites (GO-CuO and GO-ZnO) is experimentally examined under natural sun. The contribution of optical absorption, changes in fluid volume temperature, and reduction in the mass of the nanofluids are disclosed in the perspective of their photothermal conversion efficiencies. Experimental outcomes describe that all nanofluids and their composites have higher solar energy absorption, higher temperature gain, and higher mass loss than base fluid (DI water), and GO nanofluid proved to be

Conclusions
The collection of direct solar absorption-based nanofluids is an encouraging technique for solar power generation systems. Many studies on different types of nanoparticles for solar energy state that a comparison for photothermal performance characteristics of various nanofluids at the same experimental conditions is much needed. In direct absorption solar collectors (DASCs), the photothermal conversion efficiency of three nanomaterials (GO, ZnO, and CuO) and their composites (GO-CuO and GO-ZnO) is experimentally examined under natural sun. The contribution of optical absorption, changes in fluid volume temperature, and reduction in the mass of the nanofluids are disclosed in the perspective of their photothermal conversion efficiencies. Experimental outcomes describe that all nanofluids and their composites have higher solar energy absorption, higher temperature gain, and higher mass loss than base fluid (DI water), and GO nanofluid proved to be

Conclusions
The collection of direct solar absorption-based nanofluids is an encouraging technique for solar power generation systems. Many studies on different types of nanoparticles for solar energy state that a comparison for photothermal performance characteristics of various nanofluids at the same experimental conditions is much needed. In direct absorption solar collectors (DASCs), the photothermal conversion efficiency of three nanomaterials (GO, ZnO, and CuO) and their composites (GO-CuO and GO-ZnO) is experimentally examined under natural sun. The contribution of optical absorption, changes in fluid volume temperature, and reduction in the mass of the nanofluids are disclosed in the perspective of their photothermal conversion efficiencies. Experimental outcomes describe that all nanofluids and their composites have higher solar energy absorption, higher temperature gain, and higher mass loss than base fluid (DI water), and GO nanofluid proved to be the best because of its strong solar absorptivity nature. A 46.61% enhancement in photothermal conversion efficiency of GO nanofluids is accomplished within experimental domain at 0.0012 wt % concentration. It is quantitatively observed during experimentation that the addition of a small amount of nanoparticle in the base fluid can significantly increase and improve its photothermal performance. Compared with the base fluid, the growing tendency and order of nanofluids with respect to photothermal performance in this experimentation is GO, GO-ZnO, GO-CuO, ZnO, and CuO.