Heavy Metal-Based Nanoparticles as High-Performance X-ray Computed Tomography Contrast Agents

X-ray computed tomography (CT) contrast agents offer extremely valuable tools and techniques in diagnostics via contrast enhancements. Heavy metal-based nanoparticles (NPs) can provide high contrast in CT images due to the high density of heavy metal atoms with high X-ray attenuation coefficients that exceed that of iodine (I), which is currently used in hydrophilic organic CT contrast agents. Nontoxicity and colloidal stability are vital characteristics in designing heavy metal-based NPs as CT contrast agents. In addition, a small particle size is desirable for in vivo renal excretion. In vitro phantom imaging studies have been performed to obtain X-ray attenuation efficiency, which is a critical parameter for CT contrast agents, and the imaging performance of CT contrast agents has been demonstrated via in vivo experiments. In this review, we focus on the in vitro and in vivo studies of various heavy metal-based NPs in pure metallic or chemical forms, including Au, Pt, Pd, Ag, Ce, Gd, Dy, Ho, Yb, Ta, W, and Bi, and provide an outlook on their use as high-performance CT contrast agents.


Introduction
Heavy metal-based nanoparticles (NPs) are extremely valuable materials in various applications due to their high surface-to-volume ratios and optical, magnetic, antibacterial, and mechanical properties [1][2][3].Surface modification can endow them with biocompatibility and colloidal stability for various biomedical applications, such as imaging, cancer therapy, and targeted drug delivery.In particular, they can strongly attenuate X-rays because X-ray attenuation is proportional to atomic number (Z) [4].Therefore, heavy metal-based NPs can serve as contrast agents in X-ray computed tomography (CT) [5][6][7][8][9][10][11].
Contrast agents play a key role in CT as they enable the accurate diagnosis and monitoring of diseases via contrast enhancements [5].In addition, they allow for the detection of small lesions by increasing contrast.Heavy metal-based NPs have emerged as a promising class of powerful CT contrast agents as they possess a high density of heavy metal atoms with high X-ray attenuation coefficients.
Conventional iodine (I, Z = 53)-based CT contrast agents, which are organic compounds with three iodines per molecule or six iodines per dimeric molecule [12], have shown limitations such as short blood circulation times and high injection doses (>1 mmol/kg) due to their low imaging sensitivity.High injection doses can cause renal toxicity or side effects [13].In addition, iodine-based CT contrast agents are randomly dispersed in the intravascular and extravascular regions, resulting in confounding CT images [14].Heavy metal-based NPs can be used to overcome the limitations of iodine-based CT contrast agents due to their higher X-ray attenuation and longer blood circulation times.Furthermore, heavy metal-based NPs can easily be surface-modified with targeting molecules to enhance the discernibility of specific diseases, organs, and tissues, making them excellent candidates for highly sensitive and specific CT contrast agents [15,16].
Biocompatibility, colloidal stability, and renal excretion must be carefully designed to develop heavy metal-based NPs as CT contrast agents [17][18][19].Surface modification can be used to improve biocompatibility and colloidal stability.In particular, polyethylene glycol (PEG) can be used to improve blood circulation times [20][21][22].The elimination of NPs via the renal system is essential because most heavy metals are toxic [23].This can be achieved via reducing the particle diameter (d) and hydrodynamic diameter (HD) (<3 nm) [18,19].

Basic Principles of CT Contrast Agents
CT is a medical imaging technique that provides detailed cross-sectional images of the body using the distinct X-ray attenuation properties of tissues, bones, organs, and blood vessels [89].In particular, CT is useful for imaging bones and hardened diseases because soft tissues made of light elements (C, H, O, N, etc.) weakly attenuate X-rays.As shown in Figure 1a,b, the linear X-ray attenuation coefficients of heavy metal atoms are higher than that of iodine [4], making their NPs more effective CT contrast agents than iodine-based CT contrast agents.

Basic Principles of CT Contrast Agents
CT is a medical imaging technique that provides detailed cross-sectional images of the body using the distinct X-ray attenuation properties of tissues, bones, organs, and blood vessels [89].In particular, CT is useful for imaging bones and hardened diseases because soft tissues made of light elements (C, H, O, N, etc.) weakly attenuate X-rays.As shown in Figure 1a,b, the linear X-ray attenuation coefficients of heavy metal atoms are higher than that of iodine [4], making their NPs more effective CT contrast agents than iodine-based CT contrast agents.CT and magnetic resonance imaging (MRI) are the most widely used clinical imaging techniques which provide high-spatial-resolution (~1 mm) and three-dimensional anatomical images with high penetration depths suitable for whole body imaging [90].In addition, they can be used to diagnose various conditions, including tumors, fractures, and internal bleeding.CT offers faster scanning than MRI, but its sensitivity to the imaging probe is less than that of MRI [90], requiring approximately ten times higher injection doses for iodine contrast agents compared with gadolinium contrast agents in MRI.This high injection dose of iodine-based CT contrast agents may be a burden to patients [91], which can be overcome using heavy metal-based NPs with increased imaging sensitivity.

Noble Metal-Based NPs
Noble metal-based NPs can exist in pure metallic forms (Pt, Pd, Ag, and Au) or, occasionally, in chemical forms.They also exhibit photothermal properties useful for cancer therapy [92].

Pd (Z = 46)-NPs
Pd-based NPs also possess high photothermal conversion efficiency and high photothermal stability, making them promising for applications in nanomedicine, such as cancer imaging and treatment.
Lyu et al. synthesized cysteamine-coated FePd bimetallic nanodots (d = 3.4 nm) (Figure 2a) as trimodal CT-MRI-photoacoustic (PA) imaging agents [24].FePd bimetallic nanodots were synthesized using NaBH4 as a reducing agent in a nitrogen atmosphere and then coated with cysteamine for colloidal stability and biocompatibility via soni- CT and magnetic resonance imaging (MRI) are the most widely used clinical imaging techniques which provide high-spatial-resolution (~1 mm) and three-dimensional anatomical images with high penetration depths suitable for whole body imaging [90].In addition, they can be used to diagnose various conditions, including tumors, fractures, and internal bleeding.CT offers faster scanning than MRI, but its sensitivity to the imaging probe is less than that of MRI [90], requiring approximately ten times higher injection doses for iodine contrast agents compared with gadolinium contrast agents in MRI.This high injection dose of iodine-based CT contrast agents may be a burden to patients [91], which can be overcome using heavy metal-based NPs with increased imaging sensitivity.

Noble Metal-Based NPs
Noble metal-based NPs can exist in pure metallic forms (Pt, Pd, Ag, and Au) or, occasionally, in chemical forms.They also exhibit photothermal properties useful for cancer therapy [92].

Pd (Z = 46)-NPs
Pd-based NPs also possess high photothermal conversion efficiency and high photothermal stability, making them promising for applications in nanomedicine, such as cancer imaging and treatment.
Lyu et al. synthesized cysteamine-coated FePd bimetallic nanodots (d = 3.4 nm) (Figure 2a) as trimodal CT-MRI-photoacoustic (PA) imaging agents [24].FePd bimetallic nanodots were synthesized using NaBH 4 as a reducing agent in a nitrogen atmosphere and then coated with cysteamine for colloidal stability and biocompatibility via sonication in ethanol.They obtained an X-ray attenuation efficiency of 2.6 HU/mM, higher than that of the commercial iodine contrast agent Iopromide (2.0 HU/mM).In addition, high contrast enhancement was observed in the in vivo CT images of BALB/c mice at the tumor site (red circles in Figure 2b) 12 h after intravenous injection (dose = 50 µL, 10 mg Pd/mL) (Figure 2b).The nanodots offered excellent CT signal augmentation and showed exceptional stability and biocompatibility.In addition, they were applied to in vivo thermoradiotherapy (photothermal therapy combined with radiation therapy).
Pharmaceuticals 2023, 16, x FOR PEER REVIEW 10 of 30 cation in ethanol.They obtained an X-ray attenuation efficiency of 2.6 HU/mM, higher than that of the commercial iodine contrast agent Iopromide (2.0 HU/mM).In addition, high contrast enhancement was observed in the in vivo CT images of BALB/c mice at the tumor site (red circles in Figure 2b) 12 h after intravenous injection (dose = 50 µL, 10 mg Pd/mL) (Figure 2b).The nanodots offered excellent CT signal augmentation and showed exceptional stability and biocompatibility.In addition, they were applied to in vivo thermoradiotherapy (photothermal therapy combined with radiation therapy).3.1.2.Ag (Z = 47)-NPs Among noble metal NPs, Ag-NPs have attracted interest due to their novel optical (i.e., surface plasmon resonance), photothermal, and antimicrobial properties.In addition, Ag-NPs have received considerable interest in medical imaging as potential CT contrast agents due to their high X-ray attenuation properties.
Zhang et al. synthesized spherical and monodispersed hyaluronic acid-coated Ag-NPs (HA-Ag-NPs) (d = ~10 nm, HD = 13.5 nm) through one-pot NaBH4 reduction (Figure 3a) [26].The HA-Ag-NPs exhibited excellent long-term stability in water and low cytotoxicity.The in vitro phantom images demonstrated the strong X-ray attenuation of HA-Ag-NPs, which increased with increasing Ag concentrations (Figure 3b,c).The NPs exhibited an X-ray attenuation coefficient of 3.5 kHU/mM.3.1.2.Ag (Z = 47)-NPs Among noble metal NPs, Ag-NPs have attracted interest due to their novel optical (i.e., surface plasmon resonance), photothermal, and antimicrobial properties.In addition, Ag-NPs have received considerable interest in medical imaging as potential CT contrast agents due to their high X-ray attenuation properties.
Zhang et al. synthesized spherical and monodispersed hyaluronic acid-coated Ag-NPs (HA-Ag-NPs) (d = ~10 nm, HD = 13.5 nm) through one-pot NaBH 4 reduction (Figure 3a) [26].The HA-Ag-NPs exhibited excellent long-term stability in water and low cytotoxicity.The in vitro phantom images demonstrated the strong X-ray attenuation of HA-Ag-NPs, which increased with increasing Ag concentrations (Figure 3b,c).The NPs exhibited an X-ray attenuation coefficient of 3.5 kHU/mM.Hsu et al. synthesized glutathione-conjugated Ag 2 S NPs using a viscosity-mediated, thermal decomposition method at 165 • C in a nitrogen atmosphere with size control (d = 2.3, 3.1, 4.1, and 5.1 nm) based on the reaction time [27].Because the NPs were ultrasmall, they were renally excretable.For example, 85% of the injected 3.1 nm glutathione-conjugated Ag 2 S NPs were excreted via the renal system with urine.The X-ray attenuation efficiency was nearly independent of the particle diameter and decreased with increasing X-ray tube voltages so that 80 kVp (~3.5 HU/mM) > 100 kVp (~2.7 HU/mM) > 120 kVp (~2.3 HU/mM) > 140 kVp (~1.9 HU/mM).In addition, the X-ray attenuation efficiency was lower than that of the commercial iodine contrast agent Iopamidol (~5.1 HU/mM at 80 kVp, ~4.3 HU/mM at 100 kVp, ~3.4 HU/mM at 120 kVp, and ~3.0 HU/mM at 140 kVp).The potential of Ag 2 S NPs as CT contrast agents was demonstrated in vivo by observing contrast enhancements at the bladder, heart, and kidneys after intravenous injection (dose = 250 mg Ag/kg).In vivo CT imaging indicated NP excretion with urine with minor accumulation in the liver and spleen.Therefore, the ultrasmall Ag 2 S NPs with efficient renal excretion exhibited great potential for clinical translation.Hsu et al. synthesized glutathione-conjugated Ag2S NPs using a viscosity-mediated, thermal decomposition method at 165 °C in a nitrogen atmosphere with size control (d = 2.3, 3.1, 4.1, and 5.1 nm) based on the reaction time [27].Because the NPs were ultrasmall, they were renally excretable.For example, 85% of the injected 3.1 nm glutathione-conjugated Ag2S NPs were excreted via the renal system with urine.The X-ray attenuation efficiency was nearly independent of the particle diameter and decreased with increasing X-ray tube voltages so that 80 kVp (~3.5 HU/mM) > 100 kVp (~2.7 HU/mM) > 120 kVp (~2.3 HU/mM) > 140 kVp (~1.9 HU/mM).In addition, the X-ray attenuation efficiency was lower than that of the commercial iodine contrast agent Iopamidol (~5.1 HU/mM at 80 kVp, ~4.3 HU/mM at 100 kVp, ~3.4 HU/mM at 120 kVp, and ~3.0 HU/mM at 140 kVp).The potential of Ag2S NPs as CT contrast agents was demonstrated in vivo by observing contrast enhancements at the bladder, heart, and kidneys after intravenous injection (dose = 250 mg Ag/kg).In vivo CT imaging indicated NP excretion with urine with minor accumulation in the liver and spleen.Therefore, the ultrasmall Ag2S NPs with efficient renal excretion exhibited great potential for clinical translation.
Cui et al. synthesized bovine serum albumin (BSA)-stabilized Ag nanodots (d = 5.8 nm) using biomineralization, in which a mixture of BSA and AgNO3 in a basic aqueous solution was stirred.The BSA-stabilized Ag nanodots exhibited an X-ray attenuation efficiency of 5.7 HU/mM, higher than that of the commercial iodine contrast agent Iopromide (4.3 HU/mM) [28].The NPs were intratumorally injected (injection dose = 10 mg/mL, 20 µL), and contrast enhancements at the mice tumor site were observed after injection and then decreased with time, demonstrating their potential as a CT contrast agent.In addition, the signal intensities of the bladder and the tumor gradually decreased, proving that the BSA-stabilized Ag nanodots were renally excretable.Furthermore, the authors demonstrated the efficiency of the BSA-stabilized Ag nanodots in photothermal therapy of tumors in vivo using an 808 nm near infrared laser after intratumoral injection.

Pt (Z = 78)-NPs
Pt with a high atomic number (Z = 78) possesses a high X-ray attenuation coefficient that is useful for CT imaging [4].In addition, it has the PA effect, which can be used in PA imaging, and a high photothermal conversion efficiency, which is useful for photothermal and radiation based on cancer therapies.
Wang et al. developed an albumin-mediated one-pot synthesis method to generate ultrasmall Pt@BSA NPs for CT imaging by reducing H2PtCl6 using BSA as the biotemplate and NaBH4 as the reducing agent in an aqueous solution [56].The Pt@BSA NPs with a core size of 2.1 nm showed excellent colloidal stability, hemocompatibility, and Cui et al. synthesized bovine serum albumin (BSA)-stabilized Ag nanodots (d = 5.8 nm) using biomineralization, in which a mixture of BSA and AgNO 3 in a basic aqueous solution was stirred.The BSA-stabilized Ag nanodots exhibited an X-ray attenuation efficiency of 5.7 HU/mM, higher than that of the commercial iodine contrast agent Iopromide (4.3 HU/mM) [28].The NPs were intratumorally injected (injection dose = 10 mg/mL, 20 µL), and contrast enhancements at the mice tumor site were observed after injection and then decreased with time, demonstrating their potential as a CT contrast agent.In addition, the signal intensities of the bladder and the tumor gradually decreased, proving that the BSA-stabilized Ag nanodots were renally excretable.Furthermore, the authors demonstrated the efficiency of the BSA-stabilized Ag nanodots in photothermal therapy of tumors in vivo using an 808 nm near infrared laser after intratumoral injection.

Pt (Z = 78)-NPs
Pt with a high atomic number (Z = 78) possesses a high X-ray attenuation coefficient that is useful for CT imaging [4].In addition, it has the PA effect, which can be used in PA imaging, and a high photothermal conversion efficiency, which is useful for photothermal and radiation based on cancer therapies.
Wang et al. developed an albumin-mediated one-pot synthesis method to generate ultrasmall Pt@BSA NPs for CT imaging by reducing H 2 PtCl 6 using BSA as the biotemplate and NaBH 4 as the reducing agent in an aqueous solution [56].The Pt@BSA NPs with a core size of 2.1 nm showed excellent colloidal stability, hemocompatibility, and biocompatibility.The X-ray attenuation efficiency of the Pt@BSA NPs (16.8 HU/mM) at 120 kVp was approximately 2.4 times higher than that of the commercial iodine contrast agent Ultravist (~6.3 HU/mM).The contrast enhancement of the heart was observed 5 min after the intravenous injection of the Pt@BSA NPs, whereas no contrast enhancement was observed at the heart after the intravenous injection of Ultravist, indicating the enhanced CT imaging capabilities of the Pt@BSA NPs compared to those of iodine-based CT contrast agents.In addition, the contrast of the heart, which plays an important role in vascular imaging, gradually decreased over 4 h before stabilizing to usual levels, indicating the extended angiographic capabilities of the Pt@BSA NPs in vivo.
CT contrast agents.In addition, the contrast of the heart, which plays an important role in vascular imaging, gradually decreased over 4 h before stabilizing to usual levels, indicating the extended angiographic capabilities of the Pt@BSA NPs in vivo.
Recently, Saidi et al. designed Pt-NPs coated with hydrophilic and biocompatible polymers, namely poly(acrylic acid) (PAA), poly(acrylic acid-co-maleic acid) (PAAMA), and poly(methyl vinyl ether-alt-maleic acid) (PMVEMA) (d = 2.0 nm, Figure 4a), using a one-pot polyol method.The polymer-coated Pt NPs exhibited approximately four times higher X-ray attenuation efficiencies (i.e., 16.4 HU/mM at 50 kVp and 18.4 HU/mM at 70 kVp) at the same atomic concentration (Figure 4b,c) [57], and approximately 500 times higher X-ray attenuation efficiency at the same density compared to Ultravist (Figure 4c).Zhang et al. synthesized Ce6-PEG-coated mesoporous Pt (mPt) nanoplatforms (Pt@PEG-Ce6) (Ce6 = photosensitizer chlorin e6, d = 70 nm, and pore diameter = 11 nm) [58].The mPt nanomaterials were synthesized by reducing the Pt precursor in an aqueous solution, followed by Ce6 coating for colloidal stability, biocompatibility, and photosensitization.Pt@PEG-Ce6 exhibited an X-ray attenuation efficiency of 3.1 HU/mM at 120 kVp.In addition, the contrast at the tumor site significantly increased after intravenously injecting 100 mL of Pt@PEG-Ce6 (1 mg/mL) into the mice, indicating that the NPs can be used as a CT contrast agent.In addition, further studies were conducted on the biosafety of Pt@PEG-Ce6 in vivo.The biochemical parameters of blood were assessed 24 h after the intravenous injection of Pt@PEG-Ce6 (1 mg/mL) into BALB/c mice.The results showed that Pt@PEG-Ce6 had no visible toxicity as the blood biochemical indicators of the injected mice were not significantly different from those of healthy mice.In addition, Pt@PEG-Ce6 was applied to CT/PA imaging-guided photodynamic therapy (PT) of cancer in vivo.
Fu et al. synthesized mesoporous Pt-NPs (mesoPt-NPs) using Pluronic F127 as a structure-directing agent without seeds or organic reagents [59].The synthesized mes-oPt-NPs showed a spherical structure and uniform diameter (94 nm).The surface of the mesoPt-NPs was modified with PEG, and the prepared mesoPt-PEG NPs showed excellent biocompatibility and an X-ray attenuation efficiency of 5.547 HU/mM at 120 kVp.In Zhang et al. synthesized Ce6-PEG-coated mesoporous Pt (mPt) nanoplatforms (Pt@PEG -Ce6) (Ce6 = photosensitizer chlorin e6, d = 70 nm, and pore diameter = 11 nm) [58].The mPt nanomaterials were synthesized by reducing the Pt precursor in an aqueous solution, followed by Ce6 coating for colloidal stability, biocompatibility, and photosensitization.Pt@PEG-Ce6 exhibited an X-ray attenuation efficiency of 3.1 HU/mM at 120 kVp.In addition, the contrast at the tumor site significantly increased after intravenously injecting 100 mL of Pt@PEG-Ce6 (1 mg/mL) into the mice, indicating that the NPs can be used as a CT contrast agent.In addition, further studies were conducted on the biosafety of Pt@PEG-Ce6 in vivo.The biochemical parameters of blood were assessed 24 h after the intravenous injection of Pt@PEG-Ce6 (1 mg/mL) into BALB/c mice.The results showed that Pt@PEG-Ce6 had no visible toxicity as the blood biochemical indicators of the injected mice were not significantly different from those of healthy mice.In addition, Pt@PEG-Ce6 was applied to CT/PA imaging-guided photodynamic therapy (PT) of cancer in vivo.
Fu et al. synthesized mesoporous Pt-NPs (mesoPt-NPs) using Pluronic F127 as a structure-directing agent without seeds or organic reagents [59].The synthesized mesoPt-NPs showed a spherical structure and uniform diameter (94 nm).The surface of the mesoPt-NPs was modified with PEG, and the prepared mesoPt-PEG NPs showed excellent biocompatibility and an X-ray attenuation efficiency of 5.547 HU/mM at 120 kVp.In addition, the authors loaded the mesoPt-PEG NPs with doxorubicin (Dox; anticancer drug) and performed chemo-photothermal therapy of cancer cells in vitro, where 84% of cancer cells were killed.
Ma et al. synthesized poly(maleic anhydride-alt-1-octadecene)-PEG-coated (or simply PEGylated) Pt nanoworms (HD = ~100 nm) [60].The Pt nanoworms were synthesized using thermal decomposition in a nitrogen atmosphere and then coated with C18PMH-PEG for colloidal stability and biocompatibility.The Pt-PEG nanoworms exhibited an X-ray attenuation efficiency of 3.9 HU/mM.In addition, they observed contrast enhancements at the tumor site after subcutaneous injection (dose = 16 mg/kg).In addition, the Pt-PEG nanoworms exhibited extensive blood circulation due to their PEG chains [20][21][22], demonstrating that they passively targeted tumors via the enhanced permeability and retention (EPR) effect.The authors also applied the Pt-PEG nanoworms to CT/PA imagingguided photothermal/radiation therapy of cancers in vivo.
Jameel et al. synthesized highly stable, biocompatible, and ultrasmall Pt-NPs with a mean diameter of 3.8 nm using a one-step, one-pot, eco-friendly, and simple process [61].They used an extract from Prosopis farcta fruits as a reducing agent and stabilizer and obtained an X-ray attenuation efficiency of 6.6 HU/mM at 80 kVp, higher than that of the commercial iodine contrast agent Omnipaque (3.1 HU/mM).
Tang et al. synthesized human serum albumin (HSA)-coordinated monodisperse 6.7 nm Pt-NPs by reducing the Pt precursor with NaBH 4 in an aqueous solution, followed by reaction with HSA [62].The synthesized HSA-coordinated Pt-NPs exhibited an X-ray attenuation efficiency of ~5.6 HU/mM, which was higher than that of Iopromide (~5.2 HU/mM).The HSA-coordinated Pt-NPs were intratumorally injected at 250.0 µmol Pt/kg to evaluate their potential for in vivo CT imaging, and they demonstrated higher contrast enhancements at the tumor site than those obtained with Iopromide due to the higher X-ray attenuation coefficient of Pt compared to that of iodine and the excellent tumor retention of the NPs.In addition, the authors successfully applied the HSA-coordinated Pt-NPs to CT/PA dual imaging and photothermal cancer therapy in vivo.
Wang et al. synthesized hollow Pt cubes (or spirals) with an average size of 30 nm via the selective etching of Pd@Pt core-shell nanostructures using HCl, followed by modification with PEG-SH for biocompatibility [63].With an X-ray attenuation efficiency of 5.39 HU/mM, Pt spirals offered higher contrast than that of Omnipaque (4.76 HU/mM).Their superiority as a CT contrast agent was demonstrated via in vivo imaging, which showed significant contrast enhancement at the tumor site 24 h after intravenous injection (a 1.45-fold increase against preinjection).The enhanced contrast at the tumor was attributed to the EPR effect of the NPs due to the long blood circulation time (the measured circulation halftime = 2.91 h).In addition, the Pt spirals exhibited outstanding photothermal properties that exceeded those of Pt NPs, making them useful for in vivo photothermal cancer therapy.

Au (Z = 79)-NPs
Au-NPs are noble metal-based NPs that have been intensively investigated as CT contrast agents due to the superior X-ray attenuation ability [4] and biocompatibility of Au.In addition, Au-NPs possess photothermal properties applicable to cancer therapy [92,93].Owing to their high affinity to thiol derivatives, Au-NPs can be easily surface modified to improve their biocompatibility, colloidal stability, and durability.
Dong et al. generated six PEGylated Au-NPs with various particle diameters (4, 15, 50, 79, 100, and 152 nm; HD = 24.1,40.7, 69.9, 96.9, 104.8, and 140.6 nm, respectively).For the synthesis of 4 and 15 nm Au-NPs, the gold precursor was reduced using NaBH 4 , and for the larger Au-NPs, a seed growth method was used.The authors found that X-ray attenuation did not depend on the Au-NP size (4.0-4.2HU/mM at 80 kVp) [78].After intravenous injection (injection dose = 500 mg Au/kg), they observed that the smaller Au-NPs (4 nm and 15 nm) provided CT contrasts with a longer circulation time compared to the larger Au-NPs because mononuclear phagocytic systems find it more difficult to remove them as they pass through the liver and kidneys, leading to the accumulation of a large number of small Au-NPs in the blood.On the other hand, large Au-NPs (>50 nm) accumulated in the liver and spleen, providing excellent CT contrast in those areas.This particle size-dependent NP biodistribution suggests that NPs with appropriate particle sizes must be used to achieve the intended diagnostic and therapeutic applications.
Tsvirkun et al. coated Au-NPs with diameters of 10, 30, and 100 nm (Cytodianostic Inc., Burlington, ON, Canada) with PEG-COOH and then GB111-NH 2 via the amide bond [79].Then, targeting ligand cathepsin was conjugated with GB111-PEG-Au-NPs.The cathepsin-labeled Au-NPs exhibited an X-ray attenuation efficiency of 25.2 HU/mM at 35 kVp and 22.0 HU/mM at 85 kVp, slightly higher than those of the iodine contrast agent (5.4 and 4.0 HU/mM, respectively).In addition, enhanced in vivo CT imaging signals were observed at the tumor site using 10 and 30 nm Au-NPs rather than 100 nm Au-NPs due to the more efficient diffusion of smaller NPs after intravenous injection.For tumor targeting, they used the enzyme targeting method.In addition, the authors observed that tumor-targeted imaging exhibited higher contrast enhancements than nontargeted (or passive) imaging for all particle sizes and that the targeted imaging contrast decreased with increasing particle size, indicating that smaller NPs (10-100 nm) can provide better contrast in targeted imaging.
Sun et al. synthesized the heparin-amino acid 3,4-dihydroxyphenylalanine (DOPA)conjugated Au-NPs (HEPA-Au-NPs) (d = 24.0nm; HD = 54.6 nm).They coated Au-NPs (British Biocell International, Salisbury, UK) with HEPA in an aqueous solution, leading to low toxicity and sustained stability [80].They employed the HEPA-Au-NPs as a liverspecific CT imaging agent.The average size of the heparin coating layers on the surface was approximately 20 nm, almost the size of the bare Au-NPs, as can be observed using TEM (Figure 5a).The HEPA-Au-NPs provided 21.9 HU/mM at 70 kVp, whereas the commercial iodine contrast agent eXIA 160 provided 4.2 HU/mM.In vivo micro-CT images revealed that the HEPA-Au-NPs produced enhanced liver-specific CT images compared with iodinebased contrast agents (Figure 5b).Approximately 2 h after injection, HEPA-Au-NPs showed highest contrast in the liver, which was 12.6 and 3.2 times higher than that of saline and eXIA 160, respectively.In addition, the efficient liver targeting of the HEPA-Au-NPs was confirmed from the liver-specific contrast, which persisted for up to 24 h.This nanoplatform has potential as a molecular imaging probe and liver-specific CT imaging agent for the monitoring of liver cancer.
bond [79].Then, targeting ligand cathepsin was conjugated with GB111-PEG-Au-NPs.The cathepsin-labeled Au-NPs exhibited an X-ray attenuation efficiency of 25.2 HU/mM at 35 kVp and 22.0 HU/mM at 85 kVp, slightly higher than those of the iodine contrast agent (5.4 and 4.0 HU/mM, respectively).In addition, enhanced in vivo CT imaging signals were observed at the tumor site using 10 and 30 nm Au-NPs rather than 100 nm Au-NPs due to the more efficient diffusion of smaller NPs after intravenous injection.For tumor targeting, they used the enzyme targeting method.In addition, the authors observed that tumor-targeted imaging exhibited higher contrast enhancements than nontargeted (or passive) imaging for all particle sizes and that the targeted imaging contrast decreased with increasing particle size, indicating that smaller NPs (10-100 nm) can provide better contrast in targeted imaging.
Sun et al. synthesized the heparin-amino acid 3,4-dihydroxyphenylalanine (DOPA)conjugated Au-NPs (HEPA-Au-NPs) (d = 24.0nm; HD = 54.6 nm).They coated Au-NPs (British Biocell International, Salisbury, UK) with HEPA in an aqueous solution, leading to low toxicity and sustained stability [80].They employed the HEPA-Au-NPs as a liver-specific CT imaging agent.The average size of the heparin coating layers on the surface was approximately 20 nm, almost the size of the bare Au-NPs, as can be observed using TEM (Figure 5a).The HEPA-Au-NPs provided 21.9 HU/mM at 70 kVp, whereas the commercial iodine contrast agent eXIA 160 provided 4.2 HU/mM.In vivo micro-CT images revealed that the HEPA-Au-NPs produced enhanced liver-specific CT images compared with iodine-based contrast agents (Figure 5b).Approximately 2 h after injection, HEPA-Au-NPs showed highest contrast in the liver, which was 12.6 and 3.2 times higher than that of saline and eXIA 160, respectively.In addition, the efficient liver targeting of the HEPA-Au-NPs was confirmed from the liver-specific contrast, which persisted for up to 24 h.This nanoplatform has potential as a molecular imaging probe and liver-specific CT imaging agent for the monitoring of liver cancer.Hainfeld et al. used 1.9 nm Au-NPs (Nanoprobes, Inc., preparation # 1101, Yaphank, NY, USA) for in vivo mice experiments [81].The injection dose of the Au-NPs suspended in phosphate-buffer saline (PBS) at pH 7.4 was 0.01 mL/g for the Au-NP solution (concentration = 270 mg Au/mL).After intravenous injection via mice tails, high-resolution CT images of blood vessels (<100 µm) were obtained, whereas they were not obtained using the iodine contrast agent Omnipaque.In addition, kidneys and tumors were observed via high-spatial-resolution images.No evidence of toxicity was observed from Hainfeld et al. used 1.9 nm Au-NPs (Nanoprobes, Inc., preparation # 1101, Yaphank, NY, USA) for in vivo mice experiments [81].The injection dose of the Au-NPs suspended in phosphate-buffer saline (PBS) at pH 7.4 was 0.01 mL/g for the Au-NP solution (concentration = 270 mg Au/mL).After intravenous injection via mice tails, high-resolution CT images of blood vessels (<100 µm) were obtained, whereas they were not obtained using the iodine contrast agent Omnipaque.In addition, kidneys and tumors were observed via high-spatial-resolution images.No evidence of toxicity was observed from blood plasma analytes and organ histology at both 11 days and 30 days after intravenous injection.

Lanthanide (Ln)-Based NPs
Ln has a higher X-ray attenuation coefficient than iodine (I) [4]; thus, it can be used in CT contrast agents.In addition, Ln exhibits optical and magnetic properties, enabling the development of multimodal imaging agents.

Ce (Z = 58)-Based NPs
Ce-based NPs possess various properties useful for biomedical applications, such as high X-ray attenuation [4] and antioxidant properties [94].Therefore, Ce-based NPs can be employed in the imaging of anatomical features with enhanced contrast and protection against X-ray radiation damage during CT because Ce can effectively remove reactive oxygen species formed during a CT scan.
Naha et al. used a precipitation method to synthesize dextran-coated CeO 2 NPs (Dex-Ce-NPs) (i.e., precipitation of cerium salts after addition to ammonium hydroxide in the presence of dextran) (d = 4.8 nm and HD = 17.5 nm) (Figure 6a) as CT contrast agents for gastrointestinal tract (GIT) imaging [29].The Dex-Ce-NPs exhibited X-ray attenuation efficiencies of ~6.3 HU/mM (80 kVp), ~4.8 HU/mM (100 kVp), ~3.8 HU/mM (120 kVp), and ~3.2 HU/mM (140 kVp).The Dex-Ce-NPs exhibited no contrast in the large intestines of healthy mice, whereas they exhibited contrast in the colitis-affected region (Figure 6b).The dextran coating on the NP surfaces provided stability in aqueous media, biocompatibility, and specificity toward colitis.More than 97% of the oral doses were cleared from the body within 24 h.In addition, the Dex-Ce-NPs helped to reduce oxidative damage induced by CT scans by scavenging free radicals generated due to the ionization of X-ray radiation, implying that Dex-Ce-NPs can be used as a potential CT contrast agent for imaging GIT with colitis.
Ce-based NPs possess various properties useful for biomedical applications, such as high X-ray attenuation [4] and antioxidant properties [94].Therefore, Ce-based NPs can be employed in the imaging of anatomical features with enhanced contrast and protection against X-ray radiation damage during CT because Ce can effectively remove reactive oxygen species formed during a CT scan.
Naha et al. used a precipitation method to synthesize dextran-coated CeO2 NPs (Dex-Ce-NPs) (i.e., precipitation of cerium salts after addition to ammonium hydroxide in the presence of dextran) (d = 4.8 nm and HD = 17.5 nm) (Figure 6a) as CT contrast agents for gastrointestinal tract (GIT) imaging [29].The Dex-Ce-NPs exhibited X-ray attenuation efficiencies of ~6.3 HU/mM (80 kVp), ~4.8 HU/mM (100 kVp), ~3.8 HU/mM (120 kVp), and ~3.2 HU/mM (140 kVp).The Dex-Ce-NPs exhibited no contrast in the large intestines of healthy mice, whereas they exhibited contrast in the colitis-affected region (Figure 6b).The dextran coating on the NP surfaces provided stability in aqueous media, biocompatibility, and specificity toward colitis.More than 97% of the oral doses were cleared from the body within 24 h.In addition, the Dex-Ce-NPs helped to reduce oxidative damage induced by CT scans by scavenging free radicals generated due to the ionization of X-ray radiation, implying that Dex-Ce-NPs can be used as a potential CT contrast agent for imaging GIT with colitis.García et al. synthesized albumin-stabilized 5.1 nm CeO2 NPs via the chemical precipitation of a Ce 3+ precursor in a basic aqueous solution using tetramethylammonium hydroxide, followed by the dropwise addition of a CeO2 NP solution to the albumin solution [30].The NPs exhibited contrast enhancements in the liver, whereas the commercial iodine contrast agent Iopamidol-370 exhibited fast accumulation in the kidneys, followed by renal excretion.A tenfold contrast enhancement was obtained compared to those of commercial contrast agents.Efficient uptake by the liver and spleen was observed up to 7 days after intravenous tail injection, and 85% of the injected dose was recovered.In addition, the intratumoral injection of the albumin-stabilized CeO2 NPs led to contrast enhancements at the tumor site for up to 7 days after injection, and 99% of the injected dose remained at the tumor site, allowing for the monitoring of tumor growth and dynamics.García et al. synthesized albumin-stabilized 5.1 nm CeO 2 NPs via the chemical precipitation of a Ce 3+ precursor in a basic aqueous solution using tetramethylammonium hydroxide, followed by the dropwise addition of a CeO 2 NP solution to the albumin solution [30].The NPs exhibited contrast enhancements in the liver, whereas the commercial iodine contrast agent Iopamidol-370 exhibited fast accumulation in the kidneys, followed by renal excretion.A tenfold contrast enhancement was obtained compared to those of commercial contrast agents.Efficient uptake by the liver and spleen was observed up to 7 days after intravenous tail injection, and 85% of the injected dose was recovered.In addition, the intratumoral injection of the albumin-stabilized CeO 2 NPs led to contrast enhancements at the tumor site for up to 7 days after injection, and 99% of the injected dose remained at the tumor site, allowing for the monitoring of tumor growth and dynamics.

Gd (Z = 64)-Based NPs
Trivalent Gd(III) possesses the highest spin magnetic moment (s = 7/2) among the elements in the periodic table.Therefore, Gd(III)-chelates have been commercially developed as positive (T 1 ) MRI contrast agents [91].In addition, the X-ray attenuation coefficient of Gd is higher than that of iodine [4], implying that Gd-based NPs are potential candidates for MRI-CT dual imaging agents.
Ahmad et al. [31] developed iodine compound (i.e., C 8 H 4 I 3 NO 4 )-coated ultrasmall Gd 2 O 3 NPs with a mean diameter of ~2 nm using a one-pot polyol method (Figure 7a).The iodine compound was used as a surface-coating ligand as it is hydrophilic, biocompatible, and can boost X-ray contrast via the use of iodine.They observed an X-ray attenuation efficiency of 11.8 HU/mM at 70 kVp.Following intravenous tail injection (injection dose = ~0.53mmol Gd/kg), brighter contrast enhancements were observed for the mouse bladder (indicated by B in Figure 7b).The contrast at the region-of-interest (ROI) of the bladder, denoted by the small dotted circle in Figure 7b, peaked at approximately 30 min after injection and then gradually reduced over time (Figure 7c), indicating that the sample solution was expelled through the bladder as urine.As a result, the potential of iodine compound-coated Gd 2 O 3 NPs as a CT contrast agent was demonstrated.In addition, they observed high positive contrasts in MR images in vivo, demonstrating the T 1 MRI-CT dual imaging ability of the NPs.
mouse bladder (indicated by B in Figure 7b).The contrast at the region-of-interest (ROI) of the bladder, denoted by the small dotted circle in Figure 7b, peaked at approximately 30 min after injection and then gradually reduced over time (Figure 7c), indicating that the sample solution was expelled through the bladder as urine.As a result, the potential of iodine compound-coated Gd2O3 NPs as a CT contrast agent was demonstrated.In addition, they observed high positive contrasts in MR images in vivo, demonstrating the T1 MRI-CT dual imaging ability of the NPs.Ghazanfari et al. examined the X-ray attenuation characteristics of PAA-coated ultrasmall Gd2O3 NPs with an average particle diameter of 1.9 nm, which were synthesized using the one-pot polyol method [32].The hydrophilic and biocompatible PAA was used for surface coating to ensure good colloidal stability and nontoxicity.The samples showed excellent biocompatibility and colloidal stability.The PAA-coated Gd2O3 NPs demonstrated higher X-ray attenuation (5.9 HU/mM) than Ultravist (4.40 HU/mM) at 70 kVp.
Zheng et al. synthesized PAA-capped GdF3 NSs (10.6 × 7.0 × 4.2 nm) as bimodal MRI-CT contrast agents [35].In this study, GdF3 nanoplates were synthesized using the thermolysis of Gd 3+ precursors in high-boiling-point nonpolar solvents in a nitrogen atmosphere and then coated with PAA via the ligand exchange method.The NSs exhibited ~7.9 HU/mM at 60 kVp, which was higher than that of the commercial iodine contrast agent Iohexol (~4.8 HU/mM).

Dy (Z = 66)-Based NPs
Dy possesses a high X-ray attenuation coefficient [4].Therefore, Dy-based NPs can strongly attenuate X-rays, leading to high contrast in CT images.In addition, Dy exhibits Ghazanfari et al. examined the X-ray attenuation characteristics of PAA-coated ultrasmall Gd 2 O 3 NPs with an average particle diameter of 1.9 nm, which were synthesized using the one-pot polyol method [32].The hydrophilic and biocompatible PAA was used for surface coating to ensure good colloidal stability and nontoxicity.The samples showed excellent biocompatibility and colloidal stability.The PAA-coated Gd 2 O 3 NPs demonstrated higher X-ray attenuation (5.9 HU/mM) than Ultravist (4.40 HU/mM) at 70 kVp.
Zheng et al. synthesized PAA-capped GdF 3 NSs (10.6 × 7.0 × 4.2 nm) as bimodal MRI-CT contrast agents [35].In this study, GdF 3 nanoplates were synthesized using the thermolysis of Gd 3+ precursors in high-boiling-point nonpolar solvents in a nitrogen atmosphere and then coated with PAA via the ligand exchange method.The NSs exhibited ~7.9 HU/mM at 60 kVp, which was higher than that of the commercial iodine contrast agent Iohexol (~4.8 HU/mM).

Dy (Z = 66)-Based NPs
Dy possesses a high X-ray attenuation coefficient [4].Therefore, Dy-based NPs can strongly attenuate X-rays, leading to high contrast in CT images.In addition, Dy exhibits a high magnetic moment (10.4-10.6Bohr magneton) at room temperature; thus, Dy-based NPs can be used as negative (T 2 ) MRI-CT dual imaging agents.
Recently, Ghazanfari et al. synthesized PAA-coated ultrasmall Dy 2 O 3 NPs with an average particle diameter of 1.8 nm using the one-pot polyol method and characterized their X-ray attenuation properties [32].The NPs exhibited excellent colloidal stability in aqueous media and nontoxicity in vitro due to the PAA coating.They observed an X-ray attenuation efficiency of 6.1 HU/mM at 70 kVp for the Dy 2 O 3 NP suspension, greater than that of Ultravist (4.4 HU/mM).
Olifirenko et al. synthesized polyethyleneimine (PEI)-coated Dy 2 O 3 NPs (d = 79-102 nm) in aqueous media [36].They prepared Dy 2 O 3 NPs via calcination; subsequently, the NPs were coated with PEI in an aqueous solution.The PEI-coated Dy 2 O 3 NPs precipitated in 6 h, but could be redispersed via shaking; they exhibited low cellular toxicity up to 100 µg/mL due to the PEI coating.The authors observed an X-ray attenuation efficiency of ~5 HU/mM at 120 kVp.

Ho (Z = 67)-Based NPs
Similar to Dy, Ho possesses a high X-ray attenuation coefficient [4]; thus, Ho-based NPs can be used as CT contrast agents.In addition, the high magnetic moment of Ho Zhang et al. synthesized PEG-modified HoF 3 NPs using a one-pot solvothermal technique [38].The PEG-HoF 3 NPs exhibited size uniformity and exhibited excellent dispersibility in an aqueous solution due to the PEG coating (d = 38 nm and HD = ~100 nm) (Figure 8a).The X-ray attenuation efficiency was 19.0 HU/mM at 120 kVp, which was higher than that of Iohexol (3.0 HU/mM).The PEG-HoF 3 NPs demonstrated good biocompatibility and low toxicity in histological studies and a cytotoxicity evaluation.For in vivo CT images, the PEG-HoF 3 NP solution was injected into tumor-model Kunming mice tail veins (dose = 100 µL, 2 mg/mL).The distribution of the PEG-HoF 3 NPs was monitored using CT at different time points.An enhanced brightness of the tumor site and liver was observed for 24 h after injection (Figure 8b).However, the kidneys did not show obvious contrast enhancements because the large NP size blocked renal filtration.This may reduce kidney side effects.

Ho (Z = 67)-Based NPs
Similar to Dy, Ho possesses a high X-ray attenuation coefficient [4]; thus, Ho-based NPs can be used as CT contrast agents.In addition, the high magnetic moment of Ho (10.4-10.7 Bohr magneton) at room temperature enables the development of Ho-based NPs as T2 MRI-CT dual imaging agents.
Zhang et al. synthesized PEG-modified HoF3 NPs using a one-pot solvothermal technique [38].The PEG-HoF3 NPs exhibited size uniformity and exhibited excellent dispersibility in an aqueous solution due to the PEG coating (d = 38 nm and HD = ~100 nm) (Figure 8a).The X-ray attenuation efficiency was 19.0 HU/mM at 120 kVp, which was higher than that of Iohexol (3.0 HU/mM).The PEG-HoF3 NPs demonstrated good biocompatibility and low toxicity in histological studies and a cytotoxicity evaluation.For in vivo CT images, the PEG-HoF3 NP solution was injected into tumor-model Kunming mice tail veins (dose = 100 µL, 2 mg/mL).The distribution of the PEG-HoF3 NPs was monitored using CT at different time points.An enhanced brightness of the tumor site and liver was observed for 24 h after injection (Figure 8b).However, the kidneys did not show obvious contrast enhancements because the large NP size blocked renal filtration.This may reduce kidney side effects.Ni et al. synthesized PEGylated NaHoF4 NPs with various particle diameters (d = 3.2, 7.4, and 13.2 nm; HD = 12.9, 19.0, 22.7 nm) and NRs (28.9 × 16.7 nm) by controlling the ligand concentration, temperature, and time [40].They obtained an X-ray attenuation Ni et al. synthesized PEGylated NaHoF 4 NPs with various particle diameters (d = 3.2, 7.4, and 13.2 nm; HD = 12.9, 19.0, 22.7 nm) and NRs (28.9 × 16.7 nm) by controlling the ligand concentration, temperature, and time [40].They obtained an X-ray attenuation efficiency of 6.9 HU/mM at 120 kVp for 3.2 nm PEGylated NaHoF 4 NPs, higher than that of the commercial iodine contrast agent Iobitridol (2.1 HU/mM).They observed enhanced contrast at the thighs of the Kunming mice after directly injecting the 3.2 nm PEGylated NaHoF 4 NPs into the thigh (injection dose = ~120 µg Ho).In addition, the NPs exhibited a five-fold contrast increase at the tumor after injection compared with that before injection (injection dose = ~80 µg Ho).

Yb (Z = 70)-Based NPs
Yb has a higher Z value and thus a higher X-ray attenuation coefficient than iodine (Z = 53) [4], making Yb-based NPs promising CT contrast agents.
Ghazanfari et al. investigated the X-ray attenuation properties of PAA-coated ultrasmall Yb 2 O 3 NPs with an average particle diameter of 1.7 nm synthesized using a one-pot polyol method [32].The PAA-coated ultrasmall Yb 2 O 3 NPs showed good colloidal stability in aqueous media and nontoxicity in cellular cytotoxicity tests due to the PAA coating.The X-ray attenuation efficiency of the Yb 2 O 3 NP suspension (6.8 HU/mM) was higher than that of Ultravist (4.4 HU/mM).
To measure CT contrast enhancement, the Yb(OH)CO 3 NPs and Iobitridol were dispersed in PBS buffer containing 1% agarose with different Yb and I concentrations in a concentration range of 0-25 mg/mL.The Yb(OH)CO 3 NPs exhibited an X-ray attenuation efficiency of ~9.0 HU/mM at 120 kVp, which was higher than that of Iobitridol (~3.6 HU/mM).In in vivo CT studies, the Yb(OH)CO 3 NPs (injection dose: 1.0 mL of 50 mg Yb/mL) provided higher CT contrast in the liver (bottom, right) than Iobitridol (bottom, left) (injection dose: 0.3 mL of 350 mg I/mL) after intravenous injection at 120 kVp (Figure 9b), demonstrating the potential of the Yb(OH)CO 3 NPs as CT contrast agents.On the contrary, Iobitridol exhibited contrasts at the kidneys (top, left) and bladder (bottom, left), whereas the Yb(OH)CO 3 NPs did not (top and bottom, right).This is due to the primary accumulation of the Yb(OH)CO 3 NPs in the liver due to their large particle size, whereas Iobitridol was quickly excreted through the kidneys and bladder as urine due to its molecular size.
trasmall Yb2O3 NPs with an average particle diameter of 1.7 nm synthesized using a one-pot polyol method [32].The PAA-coated ultrasmall Yb2O3 NPs showed good colloidal stability in aqueous media and nontoxicity in cellular cytotoxicity tests due to the PAA coating.The X-ray attenuation efficiency of the Yb2O3 NP suspension (6.8 HU/mM) was higher than that of Ultravist (4.4 HU/mM).
Liu et al. synthesized Yb(OH)CO3 NPs (d = 170 nm) using a one-pot urea-based homogeneous precipitation method without using surface-coating ligands (Figure 9b) [44].To measure CT contrast enhancement, the Yb(OH)CO3 NPs and Iobitridol were dispersed in PBS buffer containing 1% agarose with different Yb and I concentrations in a concentration range of 0-25 mg/mL.The Yb(OH)CO3 NPs exhibited an X-ray attenuation efficiency of ~9.0 HU/mM at 120 kVp, which was higher than that of Iobitridol (~3.6 HU/mM).In in vivo CT studies, the Yb(OH)CO3 NPs (injection dose: 1.0 mL of 50 mg Yb/mL) provided higher CT contrast in the liver (bottom, right) than Iobitridol (bottom, left) (injection dose: 0.3 mL of 350 mg I/mL) after intravenous injection at 120 kVp (Figure 9b), demonstrating the potential of the Yb(OH)CO3 NPs as CT contrast agents.On the contrary, Iobitridol exhibited contrasts at the kidneys (top, left) and bladder (bottom, left), whereas the Yb(OH)CO3 NPs did not (top and bottom, right).This is due to the primary accumulation of the Yb(OH)CO3 NPs in the liver due to their large particle size, whereas Iobitridol was quickly excreted through the kidneys and bladder as urine due to its molecular size.[45].The PEG-UCNPs exhibited an X-ray attenuation efficiency of ~9.9 HU/mM at 120 kVp, which was higher than that of Iobitridol (~3.4 HU/mM).In addition, the PEG-UCNPs exhibited high contrast in the heart, liver, spleen, and kidneys after intravenous injection at 120 kVp, whereas Iobitridol mostly accumulated in the urinary organs (kidney and bladder), and no contrast was detected in the heart, vessels, and other organs, indicating the short circulation time and rapid vascular permeation of Iobitridol.
Liu et al. synthesized PEGylated Er 3+ -doped (5 mol%) Yb 2 O 3 upconversion NPs (PEG-UCNPs) (d = 170 nm) for use as high-performance contrast agents using a one-pot urea-based homogeneous precipitation process [46].The potential of the PEG-UCNPs in upconversion fluorescence imaging and CT was investigated in vitro and in vivo.The NPs exhibited a long blood circulation time due to the PEG coating [20][21][22] and an X-ray attenuation efficiency of 10.0 HU/mM at 120 kVp, which was higher than that of Iobitridol (3.0 HU/mM).In vivo CT studies showed that after intravenous injection, the contrast enhancements for the liver were higher for the NP samples compared with that of Iobitridol.The PEG-UCNPs also showed contrast enhancements for the heart and spleen but not the kidneys due to their large particle size, whereas Iobitridol exhibited high contrast enhancement only for the kidneys due to its quick renal excretion due to its molecular size.

Other Heavy Metal-Based NPs (Ta, W, and Bi)
Other heavy metal-based NPs, such as Ta, W, and Bi, have been investigated as CT contrast agents because they possess atomic numbers higher than I, providing higher X-ray attenuation compared with commercial iodine contrast agents.In particular, Bi possesses the highest Z value among nonradioactive elements, thereby exhibiting very strong X-ray attenuation.

Ta (Z = 73)-Based NPs
Ta is a highly biocompatible transition metal with negligible side effects in all redox states compared with other transition metals [95].Thus, Ta has been extensively used in clinical implants, prosthetic joints, stents, and vascular clips for nearly 50 years.Ta has recently been used as a CT contrast agent because of its high X-ray attenuation coefficient [4].
Tantalum oxide (TaOx) NPs of uniform size were synthesized by Oh et al. using a simple microemulsion approach and surface-modified with V [47].The particle diameter was controlled (6, 9, 13, and 15 nm) by varying the volume of ethanol in the synthesis.The X-ray attenuation efficiency of the TaOx NPs (~5.1 HU/mM at 100 keV) was obtained.The TaOx NPs (840 mg/kg) were injected intravenously into the tails of mice to observe the contrast enhancements for the liver, heart, kidneys, and spleen after injection.The contrast enhancements lasted for more than 3 h, indicating the prolonged circulation of the NPs in the bloodstream (attributable to the PEG coating) [20][21][22].
Bonitatibus et al. synthesized (2-diethylphosphato-ethyl)triethoxysilane-coated Ta 2 O 5 NPs (d = ~6 nm and HD = 6 nm) with high stability in water [48].The Ta 2 O 5 NPs were synthesized via the controlled hydrolysis of tantalum ethoxide and then coated with (2diethylphosphato-ethyl)triethoxysilane.At equal molar concentrations of tantalum and iodine, the NPs provided greater image contrast than Iopromide across the diagnostic X-ray spectrum between 80 and 140 kVp in in vitro phantom images.In addition, in vivo studies showed high contrast at the arterial system after intravenous injection into mice tails (1 mL of 0.92 M [Ta]) at 120 kVp.The same group improved their performance by synthesizing a zwitterionic siloxane polymer coating, which reduced the viscosity of the concentrated NP solutions by a factor of five, decreased the tissue retention of injected NPs by a factor of ten, and prevented pathological responses in the kidneys [49].
Liu et al. synthesized 1,2-distearoyl-sn-glycero-3-phosphoethanolamine-N-methoxy (polyethylene glycol)-3000 (DSPE-PEG)-coated TaS 2 NSs (PEG-TaS 2 NSs) (d = 50-100 nm and HD = ~110 nm) for safe and efficient cancer treatment (Figure 10a) [50].The TaS 2 NSs were synthesized using the combinatorial grinding of bulk TaS 2 and sonication processes and then coated with DSPE-PEG in aqueous media.The PEG-TaS 2 NSs demonstrated high X-ray attenuation (6.3 HU/mM) at 120 kVp (similar to that of Iobitridol).After intravenous injection (4.5 mg Ta/kg), contrast enhancements at the liver (Figure 10b) were observed, demonstrating the potential of the NSs as CT contrast agents.The PEG-TaS 2 NSs showed extended circulation times due to the PEG coating [20][21][22], making them useful for in vivo imaging and drug delivery, as well as cancer theranosis through the EPR effect.10a) [50].The TaS2 NSs were synthesized using the combinatorial grinding of bulk TaS2 and sonication processes and then coated with DSPE-PEG in aqueous media.The PEG-TaS2 NSs demonstrated high X-ray attenuation (6.3 HU/mM) at 120 kVp (similar to that of Iobitridol).After intravenous injection (4.5 mg Ta/kg), contrast enhancements at the liver (Figure 10b) were observed, demonstrating the potential of the NSs as CT contrast agents.The PEG-TaS2 NSs showed extended circulation times due to the PEG coating [20][21][22], making them useful for in vivo imaging and drug delivery, as well as cancer theranosis through the EPR effect.Owing to the high Z value of W, W-based NPs have emerged as promising CT contrast agents due to their high X-ray attenuation properties [4].Various W-based NPs and NRs have been investigated as X-ray contrast agents.
Kim et al. studied the use of D -glucuronic acid-coated Na 2 WO 4 NPs as CT contrast agents [51].The D -glucuronic acid-coated Na 2 WO 4 NPs were synthesized through using a one-pot polyol method.The average particle diameter of the NPs was 3.2 nm (Figure 11a).In vitro phantom images showed stronger X-ray attenuation than that obtained using Ultravist at 70 kVp (Figure 11b); the X-ray attenuation efficiency of the NPs was ~10 HU/mM, whereas that of Ultravist was ~4.5 HU/mM.In addition, in vivo CT images showed contrast enhancements at the kidneys after intravenous injection (0.1 mmol W/kg) at 70 kVp (Figure 11c).This dose is much lower than that of the iodine contrast agents (2-6.4 mmol I/kg), indicating that the D -glucuronic acid-coated Na 2 WO 4 NPs can be used as CT contrast agents.

W (Z = 74)-Based NPs
Owing to the high Z value of W, W-based NPs have emerged as promising CT contrast agents due to their high X-ray attenuation properties [4].Various W-based NPs and NRs have been investigated as X-ray contrast agents.
Kim et al. studied the use of D-glucuronic acid-coated Na2WO4 NPs as CT contrast agents [51].The D-glucuronic acid-coated Na2WO4 NPs were synthesized through using a one-pot polyol method.The average particle diameter of the NPs was 3.2 nm (Figure 11a).In vitro phantom images showed stronger X-ray attenuation than that obtained using Ultravist at 70 kVp (Figure 11b); the X-ray attenuation efficiency of the NPs was ~10 HU/mM, whereas that of Ultravist was ~4.5 HU/mM.In addition, in vivo CT images showed contrast enhancements at the kidneys after intravenous injection (0.1 mmol W/kg) at 70 kVp (Figure 11c).This dose is much lower than that of the iodine contrast agents (2-6.4 mmol I/kg), indicating that the D-glucuronic acid-coated Na2WO4 NPs can be used as CT contrast agents.[52].The Rb x WO 3 NRs were synthesized using a hydrothermal method.The WO 3 precursor Rb 2 SO 4 was mixed with polyvinyl pyrrolidone in ethylene glycol at 180 • C for 16 h.The NRs showed excellent contrast efficacy for CT imaging, as evidenced by an X-ray attenuation efficiency of ~7.1 HU/mM at 70 kVp, which was much higher than that of Ultravist (1.7 HU/mM).The CT signal at the tumor site was apparent immediately after intratumoral injection (3 mg/mL, 20 µL) at 70 kVp, indicating that the Rb x WO 3 NRs can be used as contrast agents for in vivo CT imaging.
Zhou et al. produced tungsten oxide (WO 2.9 ) NRs (length × diameter = 13.1 × 4.4 nm) via a facile thermal decomposition method [53].The NRs modified with PEG exhibited water solubility and biocompatibility, as well as a higher X-ray attenuation efficiency (1.9 HU/mM) than Iohexol (0.5 HU/mM) at 80 kVp.They used the PEGylated WO 2.9 NRs for in vivo tumor imaging and photothermal therapy by intratumorally injecting the sample solution into nude mice with HeLa tumors (20 mg W/kg).After injection, high-contrast enhancements at the tumor site were observed at 60 kVp.In addition, tumor ablation was achieved by employing photothermal therapy at 980 nm irradiation, implying that the NRs can be used as a theranostic agent in the treatment of tumors (i.WO 3 NPs had an X-ray attenuation efficiency of ~15 HU/mM at 49 kVp, which was nearly four times greater than that of the commercial iodine contrast agent Fenestra VC.After intravenous injection (0.73 mmol W/kg mice), contrast enhancements were observed at the heart, liver, spleen, and kidneys at 50 kVp and then decayed with time, finally reaching the initial contrasts ~10 h after the injection.The PCL/PEG-coated WO 3 NPs had extended blood circulation times due to the PEG coating [20][21][22], making them ideal for angiography, but were rapidly excreted from the body, minimizing long-term toxicity.
Dong et al. synthesized biocompatible and high-performance amino acid-capped MnWO 4 NRs (d = 20 nm × = 50 nm) using a hydrothermal method [55].The NRs exhibited an X-ray attenuation efficiency of 4.5 HU/mM at 120 kVp, which was higher than that of Iobitridol (3.0 HU/mM).In in vivo experiments, contrast enhancements at the liver and kidneys were observed after intravenous injection (1 mL of 0.42 M [W]) at 120 kVp.The amino acid-capped MnWO 4 NRs showed sustained contrast enhancement at the liver owing to their accumulation, making them useful for the detection of liver diseases.In addition, the NRs functioned as a T 1 MRI contrast agent owing to Mn, demonstrating their potential as a T 1 MRI-CT dual imaging agent.

Bi (Z = 83)-Based NPs
Among nonradioactive elements, Bi possesses the highest atomic number and thus the highest X-ray attenuation coefficient [4], making Bi-based NPs extremely useful as a CT contrast agent.From polonium (Po) (Z = 84) onward, all elements are radioactive and therefore not suitable for biomedical applications.In addition, Bi is a relatively inexpensive heavy metal with low toxicity.
Ghazanfari et al. synthesized PAA-coated ultrasmall Bi 2 O 3 NPs (d = 2.3 nm) (Figure 12a) using a one-pot polyol method and examined their X-ray attenuation properties [32].The NPs exhibited good colloidal stability and nontoxicity in in vitro cellular assays due to the PAA coating.The X-ray attenuation efficiency of the Bi 2 O 3 NP suspension (11.7 HU/mM) at 70 kVp was greater than that of Ultravist (4.4 HU/mM).To demonstrate their effectiveness as a CT contrast agent, the suspension of the PAA-coated ultrasmall Bi 2 O 3 NPs was injected into the mouse tail vein (dose = ~0.1 mmol/kg), which is significantly smaller than the average injection dose used for iodine contrast agents (1.5 mmol/kg).CT images were taken before and after the injection, and positive contrasts were observed for the mouse kidney and bladder after injection, as illustrated in Figure 12b.The contrast enhancement at the liver was minimal because of the low injection dose.However, contrast enhancements at the kidney and bladder were achieved even at the low injection dose due to the excretion of the NPs through the renal system.The results suggested the need for ultrasmall CT contrast agents for practical applications.The same group synthesized D-glucuronic acid-coated BiOI NPs using a one-pot polyol method [82].The particle diameter was controlled by varying the solvent volume so that 1.9-and 6.1 nm BiOI NPs were produced using 20 and 10 mL of triethylene glycol, respectively.A D-glucuronic acid-coated BiOI NP (d = 1.9 nm) solution was used to determine their X-ray attenuation efficiency using in vitro phantom imaging.The sample solution exhibited exceptionally high X-ray attenuation owing to the combined effects of Bi and I.It exhibited ~21 HU/mM, which was 4.4 times higher than that of Ultravist (~4.8 HU/mM) and ~127 times higher at the same number density, highlighting the potential of D-glucuronic acid-coated BiOI NPs as CT contrast agents.
BiOI NPs were produced using 20 and 10 mL of triethylene glycol, respectively.A D-glucuronic acid-coated BiOI NP (d = 1.9 nm) solution was used to determine their X-ray attenuation efficiency using in vitro phantom imaging.The sample solution exhibited exceptionally high X-ray attenuation owing to the combined effects of Bi and I.It exhibited ~21 HU/mM, which was 4.4 times higher than that of Ultravist (~4.8 HU/mM) and ~127 times higher at the same number density, highlighting the potential of D-glucuronic acid-coated BiOI NPs as CT contrast agents.Rabin et al. synthesized bismuth sulfide (Bi 2 S 3 ) NSs (d × w = 10-50 nm × 3-4 nm) via precipitation in the presence of 3-mercaptopropionic acid [84].The NSs were coated with polyvinylpyrrolidone (PVP) for stability in aqueous media and biocompatibility.This formulation showed a longer in vivo circulation time (140 min), higher stability, and a five-fold increase in the X-ray attenuation coefficient (~9.7 HU/mM), compared to that of Iopromide at 50 kVp.The lymph nodes of mice were visible after intravenous injection (dose = 11.4 µmol Bi) into Balb/c mice, demonstrating that the Bi 2 S 3 NSs could be an excellent CT contrast agent for disease diagnosis.In addition, the PVP-coated Bi 2 S 3 NSs exhibited a long blood circulation time, making them suitable for obtaining CT scans for extended periods.
Wei et al. developed oligosaccharide-modified Bi-NPs (OS-Bi-NPs) (d = 22 nm) as a CT contrast agent for GIT imaging [87].The Bi-NPs were synthesized in 1-dodecanethiol under argon flow at 178 • C to avoid air oxidation and coated with sweet OS to make OS-Bi-NPs that were nontoxic and stable in aqueous media and facilitate their oral administration.The X-ray attenuation efficiency of the OS-Bi-NPs (i.e., 8.5 HU/mM at 80 kVp and 6.4 HU/mM at 120 kVp) was 1.5 times greater than that of the conventional clinical CT contrast agent BaSO 4 used for GIT imaging.In addition, the OS-Bi-NPs were employed in GIT imaging in vivo (dose = 400 µL of 14 mg Bi/mL) at 80 kVp.Small intestinal loops were observed, implying the feasibility of the diagnosis of inflammatory, neoplastic intestinal lesions and incidental extra-intestinal pathological changes.
Because of their chemical stability, dual chalcogenides are frequently used as CT contrast agents.Mao et al. obtained ultrasmall Bi 2 Se 3 nanodots (2.7 nm) stabilized with BSA (BSA-Bi 2 Se 3 nanodots), which were synthesized via the reaction of hydroxyethylthioselenide with bismuth chloride in an aqueous solution under ambient conditions [88].BSA was used to stabilize the Bi 2 Se 3 nanodots in aqueous media, which were further conjugated with radioactive 99m Tc for the single-photon-emission CT of cancer.They found that the X-ray absorption coefficient was approximately 7.06 HU/mM at 55 kVp, higher than that of Iopromide (3.9 HU/mM).The BSA-Bi 2 Se 3 nanodots exhibited contrast enhancements at the 4T1 tumor of mice after intratumoral injection (dose = 50 µL, 0.078 mg Bi 2 Se 3 ) at 55 kVp.The CT value at the tumor was significantly enhanced from 51 HU to 467 HU after injection.
In addition, the high potential of the BSA-stabilized Bi 2 Se 3 nanodots as theranostic agents was demonstrated due to their excellent performance in PA imaging, photothermal therapy, and radiation therapy for tumors.

Cytotoxicity
For applications as CT contrast agents, surface-modified heavy metal-based NPs in pure metallic or chemical forms (metal = Pd, Ag, Ce, Gd, Dy, Ho, Yb, Ta, W, Pt, Au, and Bi) must be nontoxic.In addition, metal or metal ion leaking must be avoided as heavy metals and heavy metal ions are generally toxic depending on the type of metal and metal ion species [95][96][97][98][99][100][101][102][103][104][105].Au and Ta are used in tooth crown and dental implants, respectively, and are less toxic than other metals.Gd(III) ions are toxic and can cause nephrogenic systemic fibrosis (NSF), a fibrosis of the skin and internal organs [100].Therefore, heavy metal-based NPs must be completely coated with hydrophilic and biocompatible ligands to avoid metal and metal ion leaking.
Surface-modified heavy metal-based NPs must be nontoxic for in vitro and in vivo applications.To demonstrate this, the in vitro cell viabilities of heavy metal-based NPs that exhibit very low cellular toxicities are provided in Figure 13a-h [28,29,32,38,55,56,68,106].The PEG-coated porous Pd NPs that correspond to Figure 13a were incubated in human lung carcinoma cells (A549) for 24 h and exhibited nontoxicity up to 90 µg/mL [106].The albumin-stabilized Ag nanodots that correspond to Figure 13b exhibited little cytotoxicity in human oral epithelial cells (KB) after incubation for 24 h; a cell viability above 85% was maintained for nanodot concentrations up to 500 µg Ag/mL [28].The dextran-coated CeO 2 NPs that correspond to Figure 13c showed little cytotoxicity in human liver cancer cells (HepG2) after incubation for 1 and 24 h; no substantial toxicity was observed for concentrations up to 1 mg NP/mL [29].After incubation for 24 h, PAA-coated ultrasmall Gd 2 O 3 , Yb 2 O 3 , Dy 2 O 3 , Bi 2 O 3 , and NaTaO 3 NPs exhibited very low cytotoxicity in human prostate cancer cells (DU145) for up to 500 µM [X] (X = Gd, Yb, Dy, Bi, and Ta) (Figure 13d) [32].PEG-coated HoF 3 NPs exhibited very low cytotoxicity in mouse fibroblast cells (L929) after incubation for 24 h; the cell viability was above 85% for up to 300 µg/mL of the NPs (Figure 13e) [38].Amino acid-coated MnWO 4 NRs exhibited almost no toxicity in 293 human embryonic kidney (HEK) cells after incubation for 24 h even up to a high concentration of 1000 µg/mL; the cell viability remained above 90% (Figure 13f) [55].BSAloaded Pt (Pt@BSA) nanocrystals exhibited low cytotoxicity in A549 cells up to 2.5 mM Pt after incubation for 24 and 48 h; the cell viability was above 80% up to 2.5 mM Pt, and the cell viability slightly increased after 48 h of incubation due to BSA, which promoted cell growth (Figure 13g) [56].PEG-PEI-coated Au NPs exhibited very low cytotoxicity in KB cells for up to 300 µg/mL after 24 h of incubation (Figure 13h) [68].Therefore, all surface-modified heavy metal-based NPs are nontoxic and suitable for in vitro and in vivo CT imaging applications.

Conclusions and Perspectives
Heavy metal-based NPs exhibit comparable or higher X-ray attenuation efficiencies compared with their commercial iodine-based counterparts [5][6][7][8][9][10][11]. Side effects such as acute kidney disease resulting from the high injection doses (1-2 mmol/kg) of commercial iodine-based CT contrast agents [13] may be mitigated using heavy metal-based NPs that possess X-ray attenuation efficiencies higher than those of iodine contrast agents.In this review, the applications of Pd-, Ag-, Ce-, Gd-, Dy-, Ho-, Yb-, Ta-, W-, Pt-, Au-, and Bi-based NPs as CT contrast agents were discussed, as demonstrated via in vitro phantom and in vivo CT images.
Heavy metals can strongly attenuate X-rays as X-ray attenuation is proportional to atomic number (Z) [4], making them more desirable than molecular iodine contrast agents, which possess only three iodines per molecule.In addition, they exhibit longer blood circu-

Figure 1 .
Figure 1.Linear X-ray attenuation coefficients [4] of heavy metal atoms and I versus X-ray photon energy between (a) 1 keV and 10 MeV and (b) 10 and 100 keV (clinical energy area).

Figure 1 .
Figure 1.Linear X-ray attenuation coefficients [4] of heavy metal atoms and I versus X-ray photon energy between (a) 1 keV and 10 MeV and (b) 10 and 100 keV (clinical energy area).

Figure 2 .
Figure 2. (a) TEM image of cysteamine-coated FePd bimetallic nanodots.(b) In vivo CT images at the tumor site (red circles) of mice before (labeled as "pre") and 12 h after intravenous injection [24].

Figure 2 .
Figure 2. (a) TEM image of cysteamine-coated FePd bimetallic nanodots.(b) In vivo CT images at the tumor site (red circles) of mice before (labeled as "pre") and 12 h after intravenous injection [24].

Pharmaceuticals 2023 , 30 Figure 3 .
Figure 3. (a) Histogram of the hydrodynamic diameter (HD) distribution of HA-Ag-NPs based on dynamic light scattering (DLS) and cryo-TEM (inset).(b) Phantom images as a function of Ag concentration.(c) CT values (i.e., X-ray attenuation) of HA-Ag-NPs as a function of Ag concentration [26].

Figure 3 .
Figure 3. (a) Histogram of the hydrodynamic diameter (HD) distribution of HA-Ag-NPs based on dynamic light scattering (DLS) and cryo-TEM (inset).(b) Phantom images as a function of Ag concentration.(c) CT values (i.e., X-ray attenuation) of HA-Ag-NPs as a function of Ag concentration [26].

Figure 4 .
Figure 4. (a) TEM images of (i) PAA-, (ii) PAAMA-, and (iii) PMVEMA-coated Pt-NPs.The arrows indicate NPs.(b) Phantom images at 50 and 70 kVp.(c) Histogram of X-ray attenuation efficiency.*: p < 0.05, the significance of the results was confirmed using a t-test.The commercial iodine contrast agent Ultravist was used as a reference [57].

Figure 4 .
Figure 4. (a) TEM images of (i) PAA-, (ii) PAAMA-, and (iii) PMVEMA-coated Pt-NPs.The arrows indicate NPs.(b) Phantom images at 50 and 70 kVp.(c) Histogram of X-ray attenuation efficiency.*:p < 0.05, the significance of the results was confirmed using a t-test.The commercial iodine contrast agent Ultravist was used as a reference[57].

Figure 6 .
Figure 6.(a) TEM images of Dex-Ce-NPs (inset: 5 nm scale).(b) CT images of healthy (left) and colitis (right) mice obtained before (labeled as "pre") and 24 h after the oral administration of Dex-Ce-NPs.The yellow dashed circle indicates CT contrast as Dex-Ce-NPs accumulated in the colitis-affected region 24 h after injection [29].

Figure 6 .
Figure 6.(a) TEM images of Dex-Ce-NPs (inset: 5 nm scale).(b) CT images of healthy (left) and colitis (right) mice obtained before (labeled as "pre") and 24 h after the oral administration of Dex-Ce-NPs.The yellow dashed circle indicates CT contrast as Dex-Ce-NPs accumulated in the colitis-affected region 24 h after injection [29].

Figure 7 .
Figure 7. (a) HRTEM image of ultrasmall Gd2O3 NPs coated with the iodine compound (i.e., C8H4I3NO4) (indicated by the arrows).(b) In vivo CT images of a mouse bladder (marked B) at 70 kVp.The red circle indicates region of interest (ROI).(c) X-ray absorption of the ROI of the bladder (indicated by the small dotted circle) (B) before and after the intravenous injection of an aqueous NP sample into the mouse's tail [31].

Figure 7 .
Figure 7. (a) HRTEM image of ultrasmall Gd 2 O 3 NPs coated with the iodine compound (i.e., C 8 H 4 I 3 NO 4 ) (indicated by the arrows).(b) In vivo CT images of a mouse bladder (marked B) at 70 kVp.The red circle indicates region of interest (ROI).(c) X-ray absorption of the ROI of the bladder (indicated by the small dotted circle) (B) before and after the intravenous injection of an aqueous NP sample into the mouse's tail [31].
4-10.7  Bohr magneton) at room temperature enables the development of Ho-based NPs as T 2 MRI-CT dual imaging agents.

Figure 8 .
Figure 8.(a) TEM image of PEG-HoF3 NPs.(b) In vivo CT images of tumor-bearing Kunming mice showing bright contrast enhancements at the tumor site (top) and liver (bottom) for 24 h after intravenous tail injection [38].The dotted circles indicate the tumor (top) and the liver (bottom).

Figure 8 .
Figure 8.(a) TEM image of PEG-HoF 3 NPs.(b) In vivo CT images of tumor-bearing Kunming mice showing bright contrast enhancements at the tumor site (top) and liver (bottom) for 24 h after intravenous tail injection [38].The dotted circles indicate the tumor (top) and the liver (bottom).

Figure 9 .
Figure 9. (a) TEM images of Yb(OH)CO 3 NPs.(b) In vivo CT images of rats before and after the injection of Yb(OH)CO 3 NPs (right) and Iobitridol (left) at 120 kVp [44].Liu et al. synthesized oleic acid-coated NaYbF 4 :Er NPs (2.0%Er) (OA-UCNPs) (d = 40 nm) and modified them with phospholipid-polyethylene glycol terminated with carboxylic acid (PL-PEG-COOH) (or simply DSPE-PEG 2000) to obtain PEG-UCNPs for dispersibility in water[45].The PEG-UCNPs exhibited an X-ray attenuation efficiency of ~9.9 HU/mM at 120 kVp, which was higher than that of Iobitridol (~3.4 HU/mM).In addition, the PEG-UCNPs exhibited high contrast in the heart, liver, spleen, and kidneys after intravenous injection at 120 kVp, whereas Iobitridol mostly accumulated in the urinary organs (kidney and bladder), and no contrast was detected in the heart, vessels, and other organs, indicating the short circulation time and rapid vascular permeation of Iobitridol.Liu et al. synthesized PEGylated Er 3+ -doped (5 mol%) Yb 2 O 3 upconversion NPs (PEG-UCNPs) (d = 170 nm) for use as high-performance contrast agents using a one-pot urea-based homogeneous precipitation process[46].The potential of the PEG-UCNPs in upconversion fluorescence imaging and CT was investigated in vitro and in vivo.The NPs exhibited a long blood circulation time due to the PEG coating[20][21][22] and an X-ray attenuation efficiency of 10.0 HU/mM at 120 kVp, which was higher than that of Iobitridol (3.0 HU/mM).In vivo CT studies showed that after intravenous injection, the contrast enhancements for the liver were higher for the NP samples compared with that of Iobitridol.The PEG-UCNPs also showed contrast enhancements for the heart and spleen but not the kidneys due to their large particle size, whereas Iobitridol exhibited high contrast enhancement only for the kidneys due to its quick renal excretion due to its molecular size.

Figure 10 .Figure 10 .
Figure 10.(a) TEM image of PEG-TaS2 NSs (the inset shows a magnified image showing the lattice fringe).(b) Time-dependent whole-body CT imaging of a mouse after the intravenous injection of PEG-TaS2 NSs at 120 kVp showing contrast enhancements at the liver [50].3.3.2.W (Z = 74)-Based NPs Owing to the high Z value of W, W-based NPs have emerged as promising CT contrast agents due to their high X-ray attenuation properties [4].Various W-based NPs and NRs have been investigated as X-ray contrast agents.Kim et al. studied the use of D-glucuronic acid-coated Na2WO4 NPs as CT contrast

Figure 10 .
Figure 10.(a) TEM image of PEG-TaS2 NSs (the inset shows a magnified image showing the lattice fringe).(b) Time-dependent whole-body CT imaging of a mouse after the intravenous injection of PEG-TaS2 NSs at 120 kVp showing contrast enhancements at the liver [50].

Figure 11 .
Figure 11.(a) HRTEM image of D-glucuronic acid-coated Na2WO4 NPs.(b) X-ray attenuation phantom images of the D-glucuronic acid-coated Na2WO4 NP solution at 70 kVp and Ultravist as a Figure 11.(a) HRTEM image of D-glucuronic acid-coated Na 2 WO 4 NPs.(b) X-ray attenuation phantom images of the D-glucuronic acid-coated Na 2 WO 4 NP solution at 70 kVp and Ultravist as a function of [I] and [W].(c) Axial and coronal in vivo CT images of a mouse before and after the intravenous injection of D-glucuronic acid-coated Na 2 WO 4 NPs into its tail.The arrows and circles serve to identify the kidney [51].Tian et al. synthesized polyvinyl pyrrolidone (PVP)-coated rubidium tungsten bronze (Rb x WO 3 ) NRs (d × = 5 × 20-40 nm) for CT imaging[52].The Rb x WO 3 NRs were synthesized using a hydrothermal method.The WO 3 precursor Rb 2 SO 4 was mixed with polyvinyl pyrrolidone in ethylene glycol at 180 • C for 16 h.The NRs showed excellent contrast efficacy for CT imaging, as evidenced by an X-ray attenuation efficiency of ~7.1 HU/mM at 70 kVp, which was much higher than that of Ultravist (1.7 HU/mM).The CT signal at the tumor site was apparent immediately after intratumoral injection (3 mg/mL, 20 µL) at 70 kVp, indicating that the Rb x WO 3 NRs can be used as contrast agents for in vivo CT imaging.Zhou et al. produced tungsten oxide (WO 2.9 ) NRs (length × diameter = 13.1 × 4.4 nm) via a facile thermal decomposition method[53].The NRs modified with PEG exhibited water solubility and biocompatibility, as well as a higher X-ray attenuation efficiency (1.9 HU/mM) than Iohexol (0.5 HU/mM) at 80 kVp.They used the PEGylated WO 2.9 NRs for in vivo tumor imaging and photothermal therapy by intratumorally injecting the sample solution into nude mice with HeLa tumors (20 mg W/kg).After injection, high-contrast enhancements at the tumor site were observed at 60 kVp.In addition, tumor ablation was achieved by employing photothermal therapy at 980 nm irradiation, implying that the NRs can be used as a theranostic agent in the treatment of tumors (i.e., CT diagnosis and photothermal tumor therapy).Jakhmola et al. synthesized WO 3 NPs as a CT contrast agent by stirring WCl 6 in benzyl alcohol at 100 • C for 2 days.The biodegradable polymer poly-caprolactone (PCL) and PEG were used to coat the WO 3 NPs (thickness w = 5-10 nm × d = 30-100 nm and HD = ~100-200 nm)[54].Because the PCL layer prevents particle aggregation, the PCL/PEG-coated WO 3 NPs showed good stability and nontoxicity.The PCL/PEG-coated e., CT diagnosis and photothermal tumor therapy).Jakhmola et al. synthesized WO 3 NPs as a CT contrast agent by stirring WCl 6 in benzyl alcohol at 100 • C for 2 days.The biodegradable polymer poly-caprolactone (PCL) and PEG were used to coat the WO 3 NPs (thickness w = 5-10 nm × d = 30-100 nm and HD = ~100-200 nm) [54].Because the PCL layer prevents particle aggregation, the PCL/PEG-coated WO 3 NPs showed good stability and nontoxicity.The PCL/PEG-coated Pharmaceuticals 2023, 16, 1463 20 of 29

Figure 12 .Figure 12 .
Figure 12.(a) HRTEM image of PAA-coated ultrasmall Bi2O3 NPs (the arrows indicate NPs).(b) In vivo CT images of a mouse kidney and bladder before and 20 min after the intravenous injection of the suspension of PAA-coated ultrasmall Bi2O3 NPs into the mouse's tail (indicated by the dotted squares) [32].Rabin et al. synthesized bismuth sulfide (Bi2S3) NSs (d × w = 10-50 nm × 3-4 nm) via precipitation in the presence of 3-mercaptopropionic acid[84].The NSs were coated with polyvinylpyrrolidone (PVP) for stability in aqueous media and biocompatibility.This formulation showed a longer in vivo circulation time (140 min), higher stability, and a five-fold increase in the X-ray attenuation coefficient (~9.7 HU/mM), compared to that of Iopromide at 50 kVp.The lymph nodes of mice were visible after intravenous injection (dose = 11.4 µmol Bi) into Balb/c mice, demonstrating that the Bi2S3 NSs could be an excellent CT contrast agent for disease diagnosis.In addition, the PVP-coated Bi2S3 NSs exhibited a long blood circulation time, making them suitable for obtaining CT scans for extended periods.Swy et al. synthesized 38 nm bismuth(0) NPs encapsulated within 120 nm poly(DL-lactic-co-glycolic acid) (PLGA) NPs using an oil-in-water emulsion methodology[86].The PLGA-coated Bi NPs exhibited an X-ray attenuation coefficient of 10.2 HU/mM at 80 kVp in aqueous media.Wei et al. developed oligosaccharide-modified Bi-NPs (OS-Bi-NPs) (d = 22 nm) as a CT contrast agent for GIT imaging[87].The Bi-NPs were synthesized in 1-dodecanethiol Figure 12.(a) HRTEM image of PAA-coated ultrasmall Bi 2 O 3 NPs (the arrows indicate NPs).(b) In vivo CT images of a mouse kidney and bladder before and 20 min after the intravenous injection of the suspension of PAA-coated ultrasmall Bi 2 O 3 NPs into the mouse's tail (indicated by the dotted squares) [32].