Chitooligosaccharide-2,5-anhydro-d-mannonic Acid

Chitooligosaccharide with one 2,5-anhydro-D-mannofuranose unit at the reducing end (COSamf) was prepared by nitrous deamination of fully N-deacetylated chitosan. The oxidation of the amf-unit by chlorite sodium was achieved in high yield. The chemical structure of the targeted chitooligosaccharide-2,5-anhydro-D-mannonic acid with a degree of polymerization ~10 was fully characterized by NMR spectroscopy, MALDI-TOF mass spectrometry and size-exclusion chromatography. The success of this synthesis opens the way to a new generation of end-functionalized COS building blocks. Chitosan is a linear polysaccharide of D-glucosamine (GlcN) and N-acetyl-D-glucosamine (GlcNAc) units linked by β-(1→4) glycosidic bonds. Chitosan is produced industrially by alkaline N-deacetylation of chitin, the second most abundant naturally occurring polymer, mainly present in the exoskeleton of arthropods and in the endoskeleton of cephalopods [ 1, 2]. Chitosan and chitin oligomers, also named chitooligosaccharides (COS), have recently received considerable attention as functional biomolecules with a wide range of applications in food, agriculture, medicine, pharmaceutics and cosmetics. COS take advantage of their various remarkable physico-chemical and biological properties, including water-solubility, biocompatibility, antibacterial, antifungal and antitumoral activities [ 3, 4, 5, 6]. Among various chemical methods described in the literature for the preparation of COS by depolymerisation of chitin or chitosan, the nitrous acid (HNO 2) deamination methodology presents several advantages: (i) the reaction is selective and rapid; (ii) the reaction can be carry out in OPEN ACCESS

Chitosan is a linear polysaccharide of D-glucosamine (GlcN) and N-acetyl-D-glucosamine (GlcNAc) units linked by β-(1→4) glycosidic bonds.Chitosan is produced industrially by alkaline N-deacetylation of chitin, the second most abundant naturally occurring polymer, mainly present in the exoskeleton of arthropods and in the endoskeleton of cephalopods [ 1,2].Chitosan and chitin oligomers, also named chitooligosaccharides (COS), have recently received considerable attention as functional biomolecules with a wide range of applications in food, agriculture, medicine, pharmaceutics and cosmetics.COS take advantage of their various remarkable physico-chemical and biological properties, including water-solubility, biocompatibility, antibacterial, antifungal and antitumoral activities [ 3,4,5,6].
Among various chemical methods described in the literature for the preparation of COS by depolymerisation of chitin or chitosan, the nitrous acid (HNO 2 ) deamination methodology presents several advantages: (i) the reaction is selective and rapid; (ii) the reaction can be carry out in homogeneous aqueous solutions and mild reaction conditions of temperature and pH; (iii) the extent of depolymerisation can be controlled through the stoichiometry of reaction [ 7,8,9].The mechanism has been found to be specific in the sense that HNO 2 attacks the amino group of GlcN-units, with a subsequent cleavage of the following glycosidic linkage and a formation of 2,5-anhydro-Dmannofuranose (amf-unit) at the position corresponding to the reducing end.Because the amf-residue in COS is rather unstable in mild acidic conditions, due to its decomposition to hydroxylmethylfurfural (HMF), the standard procedure has been its reduction to 2,5-anhydro-D-mannitol by NaBH 4 [ 10,11].
In order to develop a new easy access of stable COS from nitrous deamination of chitosan, the oxidation of the aldehyde group of amf-units in COS has been studied.We describe here the synthesis and the characterisation of chitooligosaccharide-2,5-anhydro-D-mannonic acid with a low degree of polymerization (DP) ~10 by reaction of COSamf with sodium chlorite.Furthermore, the acid group of 2,5-anhydro-D-mannonic acid could be available for reactions that could make the obtained COS an interesting precursor in organic synthesis.

Results and Discussion
Chitooligosaccharide-2,5-anhydro-D-mannonic acid with an average GlcN-units number into chains around 10, was efficiently synthesized from chitosan in a one pot two-step procedure involving the aldehyde group oxidation of the intermediate chitooligosaccharide-2,5-anhydro-D-mannofuranose (COSamf 1) with sodium chlorite as illustrated in Scheme 1.Thus, COSamf 1 was produced by nitrous acid deamination of a fully N-deacetylated chitosan as described in a previous study [ 12].Briefly, the depolymerization of chitosan (DA 0%, = 270 kg/mol; = 115 kg/mol, Ð = 2.3) was carried out using sodium nitrite (GlcN/NaNO 2 molar ratio = 4) in aqueous acid solution at room temperature.After 24 h of reaction, COSamf 1 could be isolated and purified in 80% mass yield by both ultrafiltration and precipitation in ethanol.The chemical structure of COSamf 1 was fully confirmed by 1 H and 13 C-NMR spectroscopies, MALDI-TOF mass spectrometry and size-exclusion chromatography (see Supporting Information).Therefore it has been shown COSamf 1 is composed of a mixture of GlcN-unit oligomers, with an average DP around 10.
In a second step, the selective oxidation of the amf-unit aldehyde group by sodium chlorite has been directly carried out after the nitrous deamination step at 10 °C for 12 h, leading to the targeted chitooligosaccharide-2,5-anhydro-D-mannonic acid 2 in a good mass yield (70%) from chitosan, after purification by ultrafiltration and precipitation in ethanol.The chemical structure of the compound 2 was fully characterized by 1 H and 13 C-NMR spectroscopies thanks to two-dimensional NMR analyses, pointing out the loss of the aldehyde group at 5.1 ppm in the 1 H-NMR spectrum and the formation of Mw Mn the carboxylic group at 175.0 ppm in the 13 C-NMR spectrum [ 13].As confirmed by MALDI-TOF mass spectrometry, chitooligosaccharide-2,5-anhydro-D-mannonic acid 2 is composed of a mixture of GlcN-unit oligomers (see Supporting Information).The average number of GlcN units into chains was determined by both 1 H-NMR and SEC and was found to be equal to around 10, as for COSamf 1.Additionally, it has been shown this oxidation procedure can be carried out on COSamf with higher average GlcN-units number into chains, i.e.DP ~20 and ~30, leading to corresponding chitooligosaccharide-2,5-anhydro-D-mannonic acids in high mass yields from chitosan, respectively 80% and 90%.
As expected, chitooligosaccharide-2,5-anhydro-D-mannonic acid 2 has shown a good stability in both aqueous solution and powder form at low to room temperatures over several months.Thus, no decomposition into HMF residues was observed in 1 H-NMR analyses, contrarily to what could be shown for COSamf 1 in same storage conditions.

Experimental
Chitooligosaccharide-2,5-anhydro-D-mannonic acid 2: A fully N-deacetylated chitosan (2.1 g, 13 mmol GlcN unit) was solubilized in 100 mL of water by addition of 1.15 mL HCl (37% w/w).Then, a freshly prepared 5 mL aqueous solution of NaNO 2 (0.66 M) was added and the reaction was allowed to proceed for 24 h at room temperature.For isolation and characterisation of COSamf 1, the solution was neutralised (pH 7-8) by 1M sodium hydroxide, then ultra-filtered (cellulose ester membrane, MWCO 500, Spectrum Labs).COSamf 1 was obtained as a white powder after precipitation in ethanol and drying under vacuum (1.7 g, 80% mass yield).For the oxidation step, a 30 mL aqueous solution of sodium chlorite (0.45 M) was added at 10 °C to the COSamf 1 solution obtained after the nitrous deamination step, and the reaction was stirred for 12 h at RT.The solution was neutralised (pH 7-8) by sodium hydroxide, then ultra-filtered (cellulose ester membrane, MWCO 500 g/mol, Spectrum Labs).The product was precipitated in ethanol and drying under vacuum leading to compound 2 as white powder (1.5 g, 70% total mass yield).