Porphyrin Photosensitizers Grafted in Cellulose Supports: A Review

Cellulose is the most abundant natural biopolymer and owing to its compatibility with biological tissues, it is considered a versatile starting material for developing new and sustainable materials from renewable resources. With the advent of drug-resistance among pathogenic microorganisms, recent strategies have focused on the development of novel treatment options and alternative antimicrobial therapies, such as antimicrobial photodynamic therapy (aPDT). This approach encompasses the combination of photoactive dyes and harmless visible light, in the presence of dioxygen, to produce reactive oxygen species that can selectively kill microorganisms. Photosensitizers for aPDT can be adsorbed, entrapped, or linked to cellulose-like supports, providing an increase in the surface area, with improved mechanical strength, barrier, and antimicrobial properties, paving the way to new applications, such as wound disinfection, sterilization of medical materials and surfaces in different contexts (industrial, household and hospital), or prevention of microbial contamination in packaged food. This review will report the development of porphyrinic photosensitizers supported on cellulose/cellulose derivative materials to achieve effective photoinactivation. A brief overview of the efficiency of cellulose based photoactive dyes for cancer, using photodynamic therapy (PDT), will be also discussed. Particular attention will be devoted to the synthetic routes behind the preparation of the photosensitizer-cellulose functional materials.


Introduction
Functionalized cellulose-based materials have attracted special attention from the scientific community, mainly in the field of biological and medical sciences [1][2][3]. As cellulose demonstrates a carbohydrate nature, it has inherent compatibility with biological tissues and, consequently, possesses unique applicability with respect to its bioavailability, biocompatibility, and biodegradability considerations [3,4].
Cellulose is the most abundant natural biopolymer, considered a valuable starting material for developing new materials from renewable resources [5][6][7], with an estimated annual production of 7.5 × 10 10 tons [8]. Cellulose is available from several natural sources, mainly from trees and green plant cell walls, but also from some types of algae and tunicates or bacteria [9].
Cellulose in higher vascular plants consists of the xylem tissues, which are known as wood, where cellulosic microfibrils are embedded in a matrix of hemicellulose (an amorphous and complex mixture of linear and branched polysaccharides) and lignin, an unstructured phenolic polymer, randomly branched and crosslinked with cellulose. In nature, this β-O-(1 → 4) homopolymer does not occur as a single chain but as multiple The ribbon-like character observed for cellulose biopolymer chains, are tightly bu dled by van der Waals and hydrogen bonds, allowing adjacent cellulose chains to closely together ( Figure 1B), assembling three-dimensional networks known as micro brillated cellulose (MFC) [12]. In these cellulose fibrils, some regions can be found w highly ordered chains (crystalline domain) and others with chains randomly and high disordered (amorphous domain) ( Figure 1B) [13]. The separation or extraction of the cry talline regions from amorphous segments is usually performed by treating the cellulo fibres with an acid (e.g., sulfuric, nitric, or hydrochloric acids), leading principally to t disruption of amorphous regions while leaving the crystalline segments intact. From th disintegration, either cellulose nanofibers (CNF) or nanocrystalline cellulose (NCC) c be obtained, the latter also known as cellulose nanocrystals (CNCs). These CNCs posse unique properties, such as high surface area, high mechanical strength, and a liquid cry talline nature [14][15][16][17] with applications in several fields, such as biomedicine [18,1 wastewater treatment [20,21], biobased adsorbents of metals [22][23][24], energy [25,26], a photonic platforms [27,28].
As mentioned before, bacteria, are also able to synthesize cellulose in aqueous cultu media. Bacterial cellulose (BC), firstly identified in 1886 by A.J. Brown [29] appears a The ribbon-like character observed for cellulose biopolymer chains, are tightly bundled by van der Waals and hydrogen bonds, allowing adjacent cellulose chains to fit closely together ( Figure 1B), assembling three-dimensional networks known as microfibrillated cellulose (MFC) [12]. In these cellulose fibrils, some regions can be found with highly ordered chains (crystalline domain) and others with chains randomly and highly disordered (amorphous domain) ( Figure 1B) [13]. The separation or extraction of the crystalline regions from amorphous segments is usually performed by treating the cellulose fibres with an acid (e.g., sulfuric, nitric, or hydrochloric acids), leading principally to the disruption of amorphous regions while leaving the crystalline segments intact. From this disintegration, either cellulose nanofibers (CNF) or nanocrystalline cellulose (NCC) can be obtained, the latter also known as cellulose nanocrystals (CNCs). These CNCs possess unique properties, such as high surface area, high mechanical strength, and a liquid crystalline nature [14][15][16][17] with applications in several fields, such as biomedicine [18,19], wastewater treatment [20,21], biobased adsorbents of metals [22][23][24], energy [25,26], and photonic platforms [27,28].
As mentioned before, bacteria, are also able to synthesize cellulose in aqueous culture media. Bacterial cellulose (BC), firstly identified in 1886 by A.J. Brown [29] appears as a jelly-like translucent polymer of excellent chemical purity. Under special culturing conditions, BC can be produced extracellularly, in the form of nanofibers, through fermentation mediated by Gram-(−) bacterial cultures of Gluconacetobacter, Acetobacter, Agrobacterium, Achromobacter, Aerobacter, Sarcina, Azobacter, Rhizobium, Pseudomonas, Salmonella and Alcaligenes. The most efficient bacterial strain for BC production belongs to the Gluconacetobacter Bacterial cellulose has the same molecular formula as plant cellulose, but it is characterized by peculiar three-dimensional porous net-work structures with a high degree of polymerization (up to 8000), high crystallinity (70-80%), high water content (up to 99%), and high mechanical stability, [33]. Depending on the BC biofabrication approach (i.e., fermentation process, type of strain, carbon source, and additives), BC shape and supramolecular structure can give rise to different film forms, sizes or thicknesses, being precisely tailored for diverse applications [31]. The inclusion of additives in the nutrient media components during biosynthesis can influence the assembly and microstructure of BC, including the crystallinity, crystalline polymorphism, crystal size, and ribbon width [34]. The BC feature properties, such as controlled porosity, biocompatibility biodegradability, flexibility, ease of production, and absence of contaminants (e.g., lignin and hemicellulose), have raised the interest of academic and pharmaceutical industry communities for its utilization as a competitive product. The high biocompatibility of this hydrogel material has a high impact on its ubiquitous applications in the medical field [3,35]. In fact, this natural polymer is being successfully utilized in the reconstruction and regeneration of tissues as artificial skin ( Figure 2B,C) [35], in vivo implants [36], artificial blood vessels [37], wound healing scaffolds [38], hemostatic materials [39], energy storage [40], and in electronic devices [41]. In addition to CNC and BC, cellulose fibres, as fabrics or as paper sheets present unique mechanical and physical properties to be applied as functional materials for medical applications. According to the literature, cellulose fibres are among the most interesting basic materials for functionalization with antimicrobial agents [4]. The grafting of antimicrobials, as photosensitisers or biocides, would confer exclusive features for medical applications, such as wound healing patches to treat infected diabetic foot/leg ulcers or regeneration of damaged tissue in burn wounds [7,42,43]. The functionalization/immobilization of cellulose fibres with photoactive compounds can be an advantage in the mitigation of nosocomial pathogenic microorganisms. Furthermore, functionalized cellulose fibres with photoactive antimicrobials have also been considered for protective clothing (e.g., surgical masks, caps, gowns) and hospital linen, providing the mitigation of harmful microorganism transmission and spreading of secondary infections. All this can minimize risks for developing a serious illness, to prolong the healing of patients, and consequently reduce economic losses and extra costs to the health. Bacterial cellulose has the same molecular formula as plant cellulose, but it is characterized by peculiar three-dimensional porous net-work structures with a high degree of polymerization (up to 8000), high crystallinity (70-80%), high water content (up to 99%), and high mechanical stability, [33]. Depending on the BC biofabrication approach (i.e., fermentation process, type of strain, carbon source, and additives), BC shape and supramolecular structure can give rise to different film forms, sizes or thicknesses, being precisely tailored for diverse applications [31]. The inclusion of additives in the nutrient media components during biosynthesis can influence the assembly and microstructure of BC, including the crystallinity, crystalline polymorphism, crystal size, and ribbon width [34]. The BC feature properties, such as controlled porosity, biocompatibility biodegradability, flexibility, ease of production, and absence of contaminants (e.g., lignin and hemicellulose), have raised the interest of academic and pharmaceutical industry communities for its utilization as a competitive product. The high biocompatibility of this hydrogel material has a high impact on its ubiquitous applications in the medical field [3,35]. In fact, this natural polymer is being successfully utilized in the reconstruction and regeneration of tissues as artificial skin ( Figure 2B,C) [35], in vivo implants [36], artificial blood vessels [37], wound healing scaffolds [38], hemostatic materials [39], energy storage [40], and in electronic devices [41]. In addition to CNC and BC, cellulose fibres, as fabrics or as paper sheets present unique mechanical and physical properties to be applied as functional materials for medical applications. According to the literature, cellulose fibres are among the most interesting basic materials for functionalization with antimicrobial agents [4]. The grafting of antimicrobials, as photosensitisers or biocides, would confer exclusive features for medical applications, such as wound healing patches to treat infected diabetic foot/leg ulcers or regeneration of damaged tissue in burn wounds [7,42,43]. The functionalization/immobilization of cellulose fibres with photoactive compounds can be an advantage in the mitigation of nosocomial pathogenic microorganisms. Furthermore, functionalized cellulose fibres with photoactive antimicrobials have also been considered for protective clothing (e.g., surgical masks, caps, gowns) and hospital linen, providing the mitigation of harmful microorganism transmission and spreading of secondary infections. All this can minimize risks for developing a serious illness, to prolong the healing of patients, and consequently reduce economic losses and extra costs to the health.
Antimicrobial drugs have had a tremendous impact on modern medicine and have been viewed as a panacea for several infectious diseases, over the last 80 years [44,45].
Sulfonamides or sulfa drugs were the first effective synthetic drugs used systematically against a broad bacterial spectrum [46,47]. Since their discovery in 1935 [48,49], that microbial resistance to antibiotics is a major concern. The widespread, excessive dispensing porphyrin and analogues of natural origin and then the synthetic counterparts according to their charges.
Most of these applications are strongly dependent on specific transformations of the cellulose backbone. Many hydroxyl groups present in the cellulose structure can be chemically modified, providing a platform with functional features suitable for a plethora of applications. The most common modifications are: (i) grafting of new active units for further functionalization via covalent linkages; or (ii) modification of the surface charge density for electrostatic/noncovalent interactions with surfactants, polymers, and counter ion salts. Figure 3 displays the cellulose chemical modifications that will be discussed in the following sections of the current review. ment outcomes using cellulose as PDT photosensitizer carriers will also be described and discussed. Particular attention will be devoted to the synthetic routes behind the preparation of the photosensitizer-cellulose functional materials.
So, after a brief discussion concerning the chemical modifications of cellulose to allow the mobilization of the photoactive dye, this review is organized considering first the porphyrin and analogues of natural origin and then the synthetic counterparts according to their charges.
Most of these applications are strongly dependent on specific transformations of the cellulose backbone. Many hydroxyl groups present in the cellulose structure can be chemically modified, providing a platform with functional features suitable for a plethora of applications. The most common modifications are: (i) grafting of new active units for further functionalization via covalent linkages; or (ii) modification of the surface charge density for electrostatic/noncovalent interactions with surfactants, polymers, and counter ion salts. Figure 3 displays the cellulose chemical modifications that will be discussed in the following sections of the current review. One of the most common approaches used to obtain highly negative charged cellulose sulphate is through cellulose degradation mediated by sulphuric acid, affording CNCs decorated with sulphate esters (Figure 3, path b) [108]. Although the presence of sulphate esters (obtained by esterification of some hydroxyl groups) compromises the CNCs thermal stability, they are useful for the formation of stable colloidal suspensions by electrostatic interaction between charged surfactants, such as cetyltrimethylammonium bromide (CTAB) [5,6].
The phosphorylation of cellulose conducts to the formation of phosphate esters and consequently to negatively charged cellulose ( Figure 3, path i), accountable for important applications [109,110]. For instance, the extraordinary binding ability of phosphate groups to calcium ions or growth factors is being explored in different biological applications [111]. In addition, these functional materials can be used to make materials with flame-resistant and flame-proof properties [112], to be used as supercapacitors [95] or in environmental applications [93,94].
Periodate-mediated oxidation of cellulose is a different approach to make carbonylmodified cellulose derivatives. Unlike TEMPO, the reaction of cellulose with periodate leads to the cleavage of C 2 and C 3 bond of glucose monomer units affording 2,3-dialdehyde cellulose (DAC) (Figure 3, path c) [117]. These aldehyde functionalities in DAC can be further converted into sulfonic acids, carboxylic acids, and imines [107,118]. Moreover, the treatment of cellulose with periodate makes cellulose more flexible, with an improvement in dispersibility.
Organosilyl units have also been used to decorate cellulose surface [119,120]. In general, these entities are introduced by making use of silicon reactants bearing hydrolysable groups (typically alkoxy, acyloxy, amine, or chlorine) that can react with hydroxyl groups on cellulose ( Figure 3, path g). The non-hydrolysable unit typically holds a moiety that can react with a biologically active molecule [121,122].
The reaction with 2,4,6-trichloro-1,3,5-triazine (also known as cyanuric chloride) is a good approach to deliver a very flexible platform to covalently couple active molecules to cellulosic substrates ( Figure 3, path h) [73,[123][124][125]. The stepwise substitution of chlorine atoms with nucleophiles (such as amines, phenols, and thiols) is facile, proceeds under smooth reaction conditions, and can be controlled by temperature since the reactivity decreases with the increase in the number of substituents linked to the cellulose framework [126,127].
Cu(I)-catalyzed Huisgen 1,3-dipolar cycloaddition (Click-Chemistry reaction) was also considered an attractive approach to covalently conjugate functional molecules onto the cellulose surface. In this click reaction, the coupling of an azide moiety, previously introduced ( Figure 3, path d) with a terminal alkyne, leads to the formation of a stable 1,2,3-triazole ring ( Figure 3, path e) [128,129]. In this approach, cellulose primary hydroxyl groups are first converted into tosylate (-OTs) leaving groups, followed by their nucleophilic substitution with sodium azide (NaN 3 ) in dimethylformamide (DMF), affording cellulose displaying azide functionalities (Figure 3, path d). A click reaction involving a molecule bearing a propargylic unit can then produce cellulose bearing triazole moieties (Figure 3, path e). However, this strategy can proceed in a different way i.e., the cellulose support can be first functionalized with the alkynyl unit via propargyl bromide and then the molecule to be appended can contain the azide functionality [130].
The acylation of hydroxyl groups present at cellulose surface is another widely used modification [131]. This functionalization can occur through the reaction with acids or with succinic, maleic, or phthalic anhydrides ( Figure 3, path f) [132]. With these cyclic anhydrides, the functionalization results in a pendant carboxylic moiety attached to the cellulose via a covalent ester bond, providing reactive moieties for further functionalization [133]. Tetrapyrrolic macrocycles, e.g., protoporphyrin IX (PPIX), play a key role in life [134,135]. PPIX can chelate transition metals, affording metalloporphyrins, which accomplish a variety of biological functions. For instance, the complexation of PPIX with Fe(II) forms Heme, a constituent of hemoproteins with significant roles in dioxygen transportation, cellular oxidations and reductions, electron transportation, and drug metabolism. PPIX has some biological functions of its own, and PPIX-based compounds have been used as PS for cancer and aPDT [136].

Synthetic Access to Cellulose-Based Photosensitizers
Considering the photobiological features of PPIX, the development of cellulose based photoactive hybrid materials has attracted the attention of several research groups.
In 2006, Krausz and co-workers [137] developed photobactericidal films 2 obtained by "one-pot, two-steps" esterification of cellulose with PPIX and lauric acid ( Figure 4). The first step comprises the esterification of cellulose with PPIX using tosyl chloride (TsCl) plus pyridine to activate the primary hydroxyl groups, followed by a second step, under similar conditions, concerning the esterification of the remaining OH groups present on the cellulose-appended PPIX with the lauric acid.  . Synthetic approach for preparation of photobactericidal films 2 by "one-pot, two-step" esterification of cellulose with PPIX and lauric acid (adapted from Ref. [137]).
Oxidation of BC was mediated by sodium periodate (NaIO4) in an aqueous solution and then treated with 1,2-ethanediol overnight to remove the excess of periodate, giving material 3 ( Figure 5). The incorporation of amines on 3 was carried out by the "one pot, two steps" method, consisting of the cellulose membrane immersion in a solution of the respective diamine (ethylenediamine, 1,2-bis(2-aminoethoxy)ethane and 1,4-bis(3-aminopropoxy)butane) for 12 h, followed by the addition of the reducing agent sodium cyanoborohydride. The reaction continued for additional 24 h. Finally, after washing steps, the material functionalized with NH2 groups 4 was coupled with the PPIX derivative 5 previously activated with carbonyldiimidazole (CDI), ( Figure 5) giving the photoactive . Synthetic approach for preparation of photobactericidal films 2 by "one-pot, two-step" esterification of cellulose with PPIX and lauric acid (adapted from Ref. [137]).
The biological results on the inactivation of Escherichia coli and Staphylococcus aureus strains revealed that the observed antibacterial activity, upon 24 h of light irradiation (irradiance of 1.7 mW cm −2 ) of the prepared plastic films 2, was reliant on the porphyrin grafting percentage, attaining sterile areas (no bacteria growth) under the plastic film disks 2. In the absence of PPIX, the films did not hamper a massive growth of bacteria. The authors stated that these photoactive materials could be applied in industrial, household, and medical environments, and more generally in areas that would benefit from permanent and efficient surface disinfection.
Oxidation of BC was mediated by sodium periodate (NaIO 4 ) in an aqueous solution and then treated with 1,2-ethanediol overnight to remove the excess of periodate, giving material 3 ( Figure 5). The incorporation of amines on 3 was carried out by the "one pot, two steps" method, consisting of the cellulose membrane immersion in a solution of the respective diamine (ethylenediamine, 1,2-bis(2-aminoethoxy)ethane and 1,4-bis(3aminopropoxy)butane) for 12 h, followed by the addition of the reducing agent sodium cyanoborohydride. The reaction continued for additional 24 h. Finally, after washing steps, the material functionalized with NH 2 groups 4 was coupled with the PPIX derivative 5 previously activated with carbonyldiimidazole (CDI), ( Figure 5) giving the photoactive material PPIX@BC. After 24 h, the remaining free PPIX was thoroughly washed, and the resulting membrane dried under vacuum.
Int. J. Mol. Sci. 2023, 24, x FOR PEER REVIEW 9 of lead to a stronger interaction of E. coli to the surface, bringing it in closer proximity to th PS molecules and to the site of 1 O2 formation, leading to higher photodynamic inactiv tion. The reusability of PPIX@BC membranes was explored through the repetition aPDT assays. A gradual decreasing of the antibacterial efficacy was observed for E. co with aPDT efficiency reduced from the original 99.999% (5 log of reduction, 1st cycle) approximately 45% for the 4th cycle. In spite of the need to improve the reusability materials, the aforementioned work provides a powerful strategy for efficient Gram-( bacteria photodynamic inactivation. The promising results of aPDT accomplished by Wei and co-authors motivated th same authors to extend the strategy to the preparation of an improved photoactive mat rial [139] with enhanced mechanical properties, high efficacy under low light condition and robustness towards photobleaching and reusability. The synthetic route employe was slightly different from the previous one: cellulose acetate (CelAc) was electrospun produce nanofibers, thermally treated to enhance mechanical strength, and finally hydr lyzed to produce regenerated cellulose (RC) nanofibers that possessed a high surface are and nanofibrous structure. Covalent grafting of the activated PPIX 5 on epichloroh drin/triethylenetetramine (TETA) functionalized cellulose 6, followed by zinc(II) com plexation of porphyrinic macrocycle, afforded material 7 with a loading of 412 nm Zn(II)PPIX/mg material ( Figure 6). Antibacterial efficacy was evaluated against S. aureu (ATCC 6538) and E. coli (ATCC 8099), with results achieving detection limit inactivatio (99.999%, >5 log of reduction) for both bacteria after 20 min of white light illumination (X lamp, 500 W, λ > 420 nm, 10 cm distance between lamp and sample). No statistically si nificant loss in antibacterial activity was observed when using nanofibers that had bee photo-aged with 5 h of pre-illumination to simulate the effects of photobleaching. Take together, the results suggest that such systems may employ cost-effective neutral P paired with a wide range of polymeric scaffolds for the development of robust and dur ble self-sterilizing materials based on a photodynamic mode of action. Antibacterial efficacy was evaluated under white light irradiation (Xenon lamp, 30 min, λ > 420 nm) against both S. aureus and E. coli strains as a function of the diamine spacer unit. The best inactivation results were obtained for the PPIX@BC membranes with diamine spacers with backbone chain lengths of 10 atoms [1,2-bis(2-aminoethoxy)ethane], attaining 99.999% (5 log of reduction in CFU mL −1 ) of photoinactivation efficiency against E. coli meanwhile S. aureus was inactivated by 98.5% (~1.5 log reduction in CFU mL −1 ) by the same photosensitizing material. The results obtained are very interesting since the photodynamic effect of PPIX immobilized on BC is higher for the Gram-(−) bacterium E. coli than that of the non-immobilized PPIX under similar experimental conditions. The authors explained these results due to the incomplete grafting of PPIX onto the aminated BC surface, leading to the pronation (in buffer) of free primary amine groups on BC-spacer -NH 2 , giving -NH 3 + , that would result in a positively charged surface. As a consequence, negatively charged bacteria would adhere onto the supported surface. Therefore, it would lead to a stronger interaction of E. coli to the surface, bringing it in closer proximity to the PS molecules and to the site of 1 O 2 formation, leading to higher photodynamic inactivation.
The reusability of PPIX@BC membranes was explored through the repetition of aPDT assays. A gradual decreasing of the antibacterial efficacy was observed for E. coli, with aPDT efficiency reduced from the original 99.999% (5 log of reduction, 1st cycle) to approximately 45% for the 4th cycle. In spite of the need to improve the reusability of materials, the aforementioned work provides a powerful strategy for efficient Gram-(−) bacteria photodynamic inactivation.
The promising results of aPDT accomplished by Wei and co-authors motivated the same authors to extend the strategy to the preparation of an improved photoactive material [139] with enhanced mechanical properties, high efficacy under low light conditions, and robustness towards photobleaching and reusability. The synthetic route employed was slightly different from the previous one: cellulose acetate (CelAc) was electrospun to produce nanofibers, thermally treated to enhance mechanical strength, and finally hydrolyzed to produce regenerated cellulose (RC) nanofibers that possessed a high surface area and nanofibrous structure. Covalent grafting of the activated PPIX 5 on epichlorohydrin/triethylenetetramine (TETA) functionalized cellulose 6, followed by zinc(II) complexation of porphyrinic macrocycle, afforded material 7 with a loading of 412 nmol Zn(II)PPIX/mg material ( Figure 6). Antibacterial efficacy was evaluated against S. aureus (ATCC 6538) and E. coli (ATCC 8099), with results achieving detection limit inactivation (99.999%, >5 log of reduction) for both bacteria after 20 min of white light illumination (Xe lamp, 500 W, λ > 420 nm, 10 cm distance between lamp and sample). No statistically significant loss in antibacterial activity was observed when using nanofibers that had been photo-aged with 5 h of pre-illumination to simulate the effects of photobleaching. Taken together, the results suggest that such systems may employ cost-effective neutral PS paired with a wide range of polymeric scaffolds for the development of robust and durable self-sterilizing materials based on a photodynamic mode of action. . Covalent grafting of activated PPIX 5 using epichlorohydrin functionalized cellulose nanofibers 6 (adapted from Ref. [139]).
In 2018, the Sol research group [140] developed a new antimicrobial material consisting of PPIX 9 bearing aminoethyleneglycol spacer arms immobilized in cotton/polymethacrylic support 10 ( Figure 7). The authors polymerized methacrylic acid on cotton material, mediated by Ce(IV) as a redox radical polymerization system, affording the support 10. Aminoethyleneglycol spacer arms were appended on PPIX to facilitate its grafting to the carboxylic acid groups present at the polymethacrylic acid polymerized /cotton fabric. The first step involved the functionalization of PPIX with 1,2-bis(2-aminoethoxy)ethane monoprotected with tert-butyloxycarbonyl (Boc) in the presence of dicyclohexylcarbodiimide (DCC)/1-hydroxybenzotriazole (HOBt) giving 8. After acid deprotection of the amino groups, the desired PPIX amino derivative 9, obtained in quantitative yield, was successfully attached to 10 using classical peptide linkage conditions, yielding the material 11 (Figure 7). The photodynamic activity of photoactive cotton was evaluated against S. aureus and E. coli. Experimental data show that this cotton textile 11 bearing the PPIX derivative exerts only a photo-antibacterial effect against S. aureus, with inactivation of 99.9% (3 log reduction in CFU mL −1 ) after 24 h of white light irradiation (total light dose 9.5 J cm −2 ). Concerning Gram-(-) bacterium E. coli, the photosensitizing material did not show any photoactivity. In 2018, Sol research group [140] developed a new antimicrobial material consisting of PPIX amino derivative, 9 bearing aminoethyleneglycol spacer arms immobilized in cotton/polymethacrylic support 10 ( Figure 7). The authors polymerized methacrylic acid on cotton material, mediated by Ce(IV) as a redox radical polymerization system, affording the support 10. Aminoethyleneglycol spacer arms were appended on PPIX to facilitate its grafting to the carboxylic acid groups present at the polymethacrylic acid polymerized /cotton fabric. The first step involved the functionalization of PPIX with 1,2bis(2-aminoethoxy)ethane monoprotected with tert-butyloxycarbonyl (Boc) in the presence of dicyclohexylcarbodiimide (DCC)/1-hydroxybenzotriazole (HOBt) giving 8. After acid deprotection of the amino groups, the desired PPIX amino derivative 9, obtained in quantitative yield, was successfully attached to 10 using classical peptide linkage conditions, yielding the material 11 ( Figure 7). The photodynamic activity of photoactive cotton was evaluated against S. aureus and E. coli. Experimental data show that this cotton textile 11 bearing the PPIX derivative exerts only a photo-antibacterial effect against S. aureus, with inactivation of 99.9% (3 log reduction in CFU mL −1 ) after 24 h of white light irradiation (total light dose 9.5 J cm −2 ). Concerning Gram-(−) bacterium E. coli, the photosensitizing material did not show any photoactivity.  Figure 7. Synthetic strategy adopted by Sol: aminoethyleneglycol spacer arms modified PPIX 9 in cotton/polymethacrylic supports 10 (adapted form Ref. [140]).
The Zhang research group [69] prepared a water-soluble hybrid photoactive material introducing PPIX and quaternary ammonium salt (QAS) groups onto a cellulose backbone by means of an esterification reaction.
The introduction of positively charged quaternary amines led to a synergistic effect, increasing water-solubility and electrostatic repulsion between quaternary positive charge groups, which effectively inhibits the π-π stacking of immobilized PPIX, thus enhancing ROS yield ( Figure 8). Zhang research group [69] prepared a water-soluble hybrid photoactive material introducing PPIX and quaternary ammonium salt (QAS) groups onto a cellulose backbone by means of an esterification reaction.
The introduction of positively charged quaternary amines led to a synergistic effect, increasing water-solubility and electrostatic repulsion between quaternary positive charge groups, which effectively inhibits the π-π stacking of immobilized PPIX, thus enhancing ROS yield ( Figure 8).
The inhibition efficiencies of material 12 toward the drug-resistant E. coli and S. aureus were respectively 84% (~0.79 log of reduction) and 98% (~1.70 log of reduction) upon 1 min of white light irradiation at an irradiance of 40 mW cm −2 . After 2 min of white light irradiation, the inhibition efficiencies toward E. coli and S. aureus increased to 93% (~1.15 log of reduction) and >99% (>2 log of reduction), respectively.
The applicability and broad use of the photoactive cellulose-PPIX material 12 were proved in different substrates (e.g., slide glass, scissors, tweezers, gauze, and paper) and in personal bioprotective equipment, e.g., face masks, protective suits, and gloves ( Figure 9).
In these assays, two areas on a face mask, a protective suit, and a glove, were chosen and one of these areas was coated with the photoactive cellulose-PPIX material 12. The selected areas were inoculated with a bacterial suspension and irradiated with white light and sunlight. Then, bacteria survival rates were assessed in these areas. There were almost no colony forming units of E. coli and S. aureus on the coated areas of the face mask, protective suit, and glove after 15 min of white light and sunlight irradiation, corresponding to around 3-4 log of bacterial inactivation. Indeed, the water-soluble and nontoxic cellulose-based PPIX material 12 exhibited excellent antibacterial activity to drug-resistant bacterial strains with promising applications as wearable and robust sunlight-driven antibacterial coatings.  Figure 8. Strategy for preparation of water-soluble hybrid photoactive material 12 containing PPIX and QAS groups onto a cellulose support (adapted from Ref. [69]).
The inhibition efficiencies of material 12 toward the drug-resistant E. coli and S. aureus were respectively 84% (~0.79 log of reduction) and 98% (~1.70 log of reduction) upon 1 min of white light irradiation at an irradiance of 40 mW cm −2 . After 2 min of white light irradiation, the inhibition efficiencies toward E. coli and S. aureus increased to 93% (~1.15 log of reduction) and >99% (> 2 log of reduction), respectively.
In these assays, two areas on a face mask, a protective suit, and a glove, were chosen and one of these areas was coated with the photoactive cellulose-PPIX material 12. The selected areas were inoculated with a bacterial suspension and irradiated with white light and sunlight. Then, bacteria survival rates were assessed in these areas. There were almost and QAS groups onto a cellulose support (adapted from Ref. [69]).
The inhibition efficiencies of material 12 toward the drug-resistant E. coli and S reus were respectively 84% (~0.79 log of reduction) and 98% (~1.70 log of reduction) u 1 min of white light irradiation at an irradiance of 40 mW cm −2 . After 2 min of white irradiation, the inhibition efficiencies toward E. coli and S. aureus increased to 93% (~ log of reduction) and >99% (> 2 log of reduction), respectively.
The applicability and broad use of the photoactive cellulose-PPIX material 12 w proved in different substrates (e.g., slide glass, scissors, tweezers, gauze, and paper) in personal bioprotective equipment, e.g., face masks, protective suits, and gloves (Fi 9). In these assays, two areas on a face mask, a protective suit, and a glove, were ch and one of these areas was coated with the photoactive cellulose-PPIX material 12. selected areas were inoculated with a bacterial suspension and irradiated with white and sunlight. Then, bacteria survival rates were assessed in these areas. There were alm Recently, Ghiladi, Wang and co-workers [141], developed a porous photoactive material based on PPIX-embedded cellulose diacetate (PPIX@CA) microfibers ( Figure 10). The photodynamic antimicrobial membrane was prepared by an electrospinning method with two different PPIX loadings: 5 and 10 wt.% PPIX with respect to CA (85 and 170 nmol PPIX/mg membrane, respectively). The antibacterial activity of the new material was evaluated towards Gram-(+) and Gram-(−) bacterial models. Despite the good efficacy of PPIX@CA porous microfibers against S. aureus after 30 min of white light irradiation (Xe lamp, λ ≥ 420 nm at an irradiance of 65 ± 5 mW cm −2 ), accomplishing 99.8% (~2.7 log) of bacterial reduction, the bacterial reduction observed for E. coli was lower (86.6%,~0.87 log of reduction) using the same experimental protocol. The combined use of KI with the PPIX@CA porous microfibers showed to be beneficial since it further enhances the antimicrobial efficacy of the PPIX@CA microfiber membrane, achieving up to 99.9999% (6 log of reduction) photoinactivation of both S. aureus and E. coli strains in the presence of 25 and 100 mM KI, respectively. PPIX/mg membrane, respectively). The antibacterial activity of the new material was eval-uated towards Gram-(+) and Gram-(−) bacterial models. Despite the good efficacy of PPIX@CA porous microfibers against S. aureus after 30 min of white light irradiation (Xe lamp, λ ≥ 420 nm at an irradiance of 65 ± 5 mW cm −2 ), accomplishing 99.8% (~2.7 log) of bacterial reduction, the bacterial reduction observed for E. coli was lower (86.6%, ~0.87 log of reduction) using the same experimental protocol. The combined use of KI with the PPIX@CA porous microfibers showed to be beneficial since it further enhances the antimicrobial efficacy of the PPIX@CA microfiber membrane, achieving up to 99.9999% (6 log of reduction) photoinactivation of both S. aureus and E. coli strains in the presence of 25 and 100 mM KI, respectively.  [141]. 2021, Elsevier.
Naturally occurring chlorophylls and bacteriochlorophylls are essential constituents of plants and bacteria, often called the "pigments of life" [134,135] owing to their important role in photosynthetic processes. Nowadays, their synthetic counterparts also present multiple applications essentially due to their absorbance of light in a broad range of the spectrum, particularly in the red (chlorins) and near infra-red region, NIR (bacteriochlorins) [65,[143][144][145][146]. Intense red and NIR photons absorption is a desirable feature for biomedical applications (Imaging, PDT, aPDT), since the phototherapeutic window (650-900 nm) for electromagnetic radiation is the most penetrating and least harmful to human tissues [147,148]. Despite the interesting biological applications of natural semi-synthetic or synthetic hydroporphyrins, they are not naturally water-soluble and may aggregate in aqueous media [149,150]. Thus, several studies have been carried out to improve water Figure 10. Scheme for the preparation of the porous PPIX-cellulose diacetate (PPIX@CA) membrane by electrospinning. Reprinted with permission from Ref. [141]. 2021, Elsevier.
Naturally occurring chlorophylls and bacteriochlorophylls are essential constituents of plants and bacteria, often called the "pigments of life" [134,135] owing to their important role in photosynthetic processes. Nowadays, their synthetic counterparts also present multiple applications essentially due to their absorbance of light in a broad range of the spectrum, particularly in the red (chlorins) and near infra-red region, NIR (bacteriochlorins) [65,[143][144][145][146]. Intense red and NIR photons absorption is a desirable feature for biomedical applications (Imaging, PDT, aPDT), since the phototherapeutic window (650-900 nm) for electromagnetic radiation is the most penetrating and least harmful to human tissues [147,148]. Despite the interesting biological applications of natural semisynthetic or synthetic hydroporphyrins, they are not naturally water-soluble and may aggregate in aqueous media [149,150]. Thus, several studies have been carried out to improve water solubility or dispersibility of hydroporphyrins and cellulose or cellulose-like supports have been employed as suitable carrier systems.
Despite not being used in microorganism inactivation, it is worthwhile to mention the seminal works of Roman and co-workers, where a hydroporphyrin, pheophorbidea 13, was recognized to have the potential to be combined with cellulose [151]. Solid samples of 13 ( Figure 11) adsorbed on microcrystalline cellulose were prepared by adding weighed masses of cellulose to ethanol stock solutions of 13 (pheophorbide-a concentrations from 7.1 nmol to 8.9 µmol). After solvent evaporation by vacuum drying, the samples were studied and the absorption and luminescence properties of 13 adsorbed on cellulose support were investigated as a function of the dye concentration.
As an extension of the previous work, the same authors [152] investigated the behavior of cellulose particles loaded with 13 in aqueous media.
The previously prepared samples of pheophorbide-a, 13, adsorbed on microcrystalline cellulose (characterized in the solid state in previous work) were washed with water, leading to stable suspensions of micrometric particles (d < 2 µm) carrying photoactive and monomeric dye molecules. Suspensions were fluorescent and generated 1 O 2 efficiently. A similar effect has been observed on washing samples containing hematoporphyrin IX (HP) adsorbed on the same support. With this study, the authors conclude that, using cellulose as a heterogeneous carrier, it is possible to introduce hydrophobic PS into the aqueous medium while avoiding aggregation, thus preserving their photophysical properties. Results denote that cellulose can be employed as a suitable carrier system for 13. It was also demonstrated that the same principle can be applied to carry HP into the water in its monomeric form. This fact opens the possibility of applying the same strategy to different hydrophobic PS.
solubility or dispersibility of hydroporphyrins and cellulose or cellulose-like supports have been employed as suitable carrier systems.
Despite not being used in microorganism inactivation, it is worthwhile to mention the seminal works of Roman and co-workers, where a hydroporphyrin, pheophorbide-a 13, was recognized to have the potential to be combined with cellulose [151]. Solid samples of 13 ( Figure 11) adsorbed on microcrystalline cellulose were prepared by adding weighed masses of cellulose to ethanol stock solutions of 13 (pheophorbide-a concentrations from 7.1 nmol to 8.9 μmol). After solvent evaporation by vacuum drying, the samples were studied and the absorption and luminescence properties of 13 adsorbed on cellulose support were investigated as a function of the dye concentration. As an extension of the previous work, the same authors [152] investigated the behavior of cellulose particles loaded with 13 in aqueous media.
The previously prepared samples of pheophorbide-a, 13, adsorbed on microcrystalline cellulose (characterized in the solid state in previous work) were washed with water, leading to stable suspensions of micrometric particles (d < 2 μm) carrying photoactive and monomeric dye molecules. Suspensions were fluorescent and generated 1 O2 efficiently. A similar effect has been observed on washing samples containing hematoporphyrin IX (HP) adsorbed on the same support. With this study, the authors conclude that, using cellulose as a heterogeneous carrier, it is possible to introduce hydrophobic PS into the aqueous medium while avoiding aggregation, thus preserving their photophysical properties. Results denote that cellulose can be employed as a suitable carrier system for 13. It was also demonstrated that the same principle can be applied to carry HP into the water in its monomeric form. This fact opens the possibility of applying the same strategy to different hydrophobic PS. In 2017, Sol and collaborators [67] developed a new strategy to devise photoactive material with effectiveness against infections caused by Gram-(−) multidrug resistant bacterial strains. A combination of two well-known concepts to eradicate microbes, aPDT and antibiotic prophylaxis, has been developed based on the fabrication of photobactericidal organic material, consisting of cellulose nanocrystals to which the purpurin 18 (16, see Figure 11) and the polypeptide polymyxin B (PMB) were covalently attached. The photoactive nanocrystals were prepared in three steps: (i) cellulose nanocrystals (CNC) were first obtained by oxidation of commercial cotton (with TEMPO as oxidant) to enable after hydrolysis CNCs ox , ( Figure 12); (ii) purpurin 18 (16) was selected as PS and the reaction of cyclic anhydride with the free amine of spermine linker yielded a chlorin e 6 (14) bearing a linker able to form amide grafting group with nanocrystaline cellulose support CNCse 6 ( Figure 12); (iii) the antimicrobial PMB was covalently attached to the same cellulose support, yielding the photobactericidal organic material, CNCsc 6 -PMB , (Figure 12). In parallel, cellulose nanocrystals functionalized only with polymyxin B (CNCs PMB ) were also synthesized, for comparison with the hybrid material bearing chlorin e 6 CNCsc 6 -PMB ( Figure 12).
trations (0.191 mg mL −1 and 0.019 mg mL −1 ). Similar results of bacterial growth inhibition (>6 log of reduction in CFU/mL) were obtained for P. aeruginosa when the concentrations 0.191 mg mL −1 and 0.080 mg mL −1 of CNCsc6-PMB were used under light irradiation.
An amplifying and synergistic effect of chlorin e6 has been highlighted against these Gram-(-) strains, based on membrane weakening and a potential docking effect from the polymyxin B moiety. Such results confirm the importance of using an antimicrobial peptide to broaden the spectrum of aPDT.  An amplifying and synergistic effect of chlorin e 6 has been highlighted against these Gram-(−) strains, based on membrane weakening and a potential docking effect from the polymyxin B moiety. Such results confirm the importance of using an antimicrobial peptide to broaden the spectrum of aPDT.
Later on, Gavara and coworkers [90] reported the possibility of utilizing copper(II) and magnesium(II) metal complexes of chlorin e 6 (14a, 14b in Figure 11) incorporated in (hydroxypropyl)methyl cellulose (HPMC) for applications as photoactive coatings in polyethylene terephthalate (PET) packages. The antimicrobial properties of 14a and 14b in HPMC as coatings in PET packages were analyzed against Listeria monocytogenes and E. coli. The antimicrobial results indicated that 14b [M = Mg(II)] was more active than 14a [M = Cu(II)]) and that it was more effective against Gram-(+) bacterium L. monocytogenes (7 log reduction) than against E. coli where no significant growth reduction was observed.

Neutral Porphyrins
Synthetic meso-tetraarylporphyrins (tArPs) are versatile compounds (Figure 13), readily accessible by facile and straightforward condensation reactions using pyrrole and aldehydes or dipyrromethanes/tripyrranes as starting materials [153,154]. Their chemical stability, photophysical features, and ability to fine-tune the electronic properties, makes tArPs a multipurpose platform for the preparation of materials with light-harvesting properties capable to generate ROS, namely 1 O 2 [76,155].
One of the seminal works reporting a functionalized tArP derivative immobilized on cellulose support was reported by Krausz and co-workers [156], who developed photobactericidal plastic films by appending porphyrins through the acylation approach ( Figure 14). Two series of porphyrinic cellulose laurate esters (18a and 18b), with PS covalently linked to the cellulosic polymer, were prepared in "one-pot, two-steps" esterification reactions: (i) the tri-tolylporphyrin derivative was first covalently bounded to the cellulosic polymer and (ii) the porphyrin containing plastic films were then obtained by the second esterification with lauric acid (Figure 14). The antimicrobial properties of new photoactive cellulosic polymers were assessed against Gram-(+) and Gram-(−) bacterial strains (S. aureus and E. coli, respectively) under white light conditions (24 h irradiation at an irradiance of 1.7 mW cm −2 ) and the qualitative preliminary results are presented. The porphyrinic cellulose laurate esters 18a and 18b were found effective towards S. aureus and E. coli (no bacterial growth was observed under the films) when the grafting percentage of porphyrin was higher than 0.16% whereas the non-porphyrinic film control allowed full growth of bacteria. The biological data showed that the bacterial inactivation of the immobilized PS was mostly mediated by 1 O 2 which ultimately damages the cell wall since there is no penetration of the PS into the bacterial cell. and magnesium(II) metal complexes of chlorin e6 (14a, 14b in Figure 11) incorporated in (hydroxypropyl)methyl cellulose (HPMC) for applications as photoactive coatings in polyethylene terephthalate (PET) packages. The antimicrobial properties of 14a and 14b in HPMC as coatings in PET packages were analyzed against Listeria monocytogenes and E. coli. The antimicrobial results indicated that 14b [M = Mg(II)] was more active than 14a [M = Cu(II)]) and that it was more effective against Gram-(+) bacterium L. monocytogenes (7 log reduction) than against E. coli where no significant growth reduction was observed.

Neutral Porphyrins
Synthetic meso-tetraarylporphyrins (tArPs) are versatile compounds (Figure 13), readily accessible by facile and straightforward condensation reactions using pyrrole and aldehydes or dipyrromethanes/tripyrranes as starting materials [153,154]. Their chemical stability, photophysical features, and ability to fine-tune the electronic properties, makes tArPs a multipurpose platform for the preparation of materials with light-harvesting properties capable to generate ROS, namely 1 O2 [76,155]. One of the seminal works reporting a functionalized tArP derivative immobilized on cellulose support was reported by Krausz and co-workers [156], who developed photobactericidal plastic films by appending porphyrins through the acylation approach (Figure 14). Two series of porphyrinic cellulose laurate esters (18a and 18b), with PS covalently linked to the cellulosic polymer, were prepared in "one-pot, two-steps" esterification reactions: (i) the tri-tolylporphyrin derivative was first covalently bounded to the cellulosic polymer and (ii) the porphyrin containing plastic films were then obtained by the second esterification with lauric acid (Figure 14). The antimicrobial properties of new photoactive cellulosic polymers were assessed against Gram-(+) and Gram-(-) bacterial strains (S. aureus and E. coli, respectively) under white light conditions (24 h irradiation at an irradiance of 1.7 mW cm −2 ) and the qualitative preliminary results are presented. The porphyrinic cellulose laurate esters 18a and 18b were found effective towards S. aureus and E. coli (no bacterial growth was observed under the films) when the grafting percentage of porphyrin was higher than 0.16% whereas the non-porphyrinic film control allowed full growth of bacteria. The biological data showed that the bacterial inactivation of the immobilized PS was mostly mediated by 1 O2 which ultimately damages the cell wall since there is no penetration of the PS into the bacterial cell. 2008, Elsevier.
Later on, Krausz, Sol and co-workers [157] explored the "Click-Chemistry" synthetic approach to immobilize the Zn(II) complex 19 bearing a propynyloxy substituent on a cellulose cotton fabric functionalized with azide units (Figure 15). The new photoactive material 20 was characterized by ATR-FTIR and the antibacterial properties were evaluated. The authors showed for the fabric a similar antibacterial activity upon visible light irradiation against E. coli and S. aureus (reductions of ~5 log units). Later on, Krausz, Sol and co-workers [157] explored the "Click-Chemistry" synthetic approach to immobilize the Zn(II) complex 19 bearing a propynyloxy substituent on a cellulose cotton fabric functionalized with azide units (Figure 15). The new photoactive material 20 was characterized by ATR-FTIR and the antibacterial properties were evaluated. The authors showed for the fabric a similar antibacterial activity upon visible light irradiation against E. coli and S. aureus (reductions of~5 log units).
Later on, Krausz, Sol and co-workers [157] explored the "Click-Chemistry" synthe approach to immobilize the Zn(II) complex 19 bearing a propynyloxy substituent on cellulose cotton fabric functionalized with azide units (Figure 15). The new photoacti material 20 was characterized by ATR-FTIR and the antibacterial properties were eva ated. The authors showed for the fabric a similar antibacterial activity upon visible lig irradiation against E. coli and S. aureus (reductions of ~5 log units).  [157]).
Based on the versatility, reactivity, and availability for stepwise substitution of ch rine atoms by different nucleophiles, Sol and collaborators [158] used cyanuric chlori (2,4,6-trichloro-1,3,5-triazine), as a grafting agent between porphyrins and cellulose fa rics. The unsymmetric 5-(4-aminophenyl)-10,15,20-triphenylporphyrin derivative 21 w linked to triazine in the presence of a base, N,N-diisopropylethylamine (DIPEA) at 0 ( Figure 16). Then, porphyrin-triazine 22 was grafted onto cellulose square fabrics, in t case using DIPEA plus piperidine, and was tested in vitro against S. aureus. Based on the versatility, reactivity, and availability for stepwise substitution of chlorine atoms by different nucleophiles, Sol and collaborators [158] used cyanuric chloride (2,4,6trichloro-1,3,5-triazine), as a grafting agent between porphyrins and cellulose fabrics. The unsymmetric 5-(4-aminophenyl)-10,15,20-triphenylporphyrin derivative 21 was linked to triazine in the presence of a base, N,N-diisopropylethylamine (DIPEA) at 0 • C ( Figure 16). Then, porphyrin-triazine 22 was grafted onto cellulose square fabrics, in this case using DIPEA plus piperidine, and was tested in vitro against S. aureus. Experimental data showed that the cotton-PS material 23 produced a photobactericidal effect at quantity as low as ~0.8 μmol cm −2 of PS on the fabric sample. After 24 h exposure to white light and a total light dose of 9.5 J cm −2 , a reduction of 93.7% (~1.2 log reduction) of bacterial abundance was achieved when compared with the initial bacterial concentration.
During the experiment, the bacterial growth increased by 4 logs for all the untreated (without PS) cotton samples either in the dark or under light irradiation. The same bacterial growth profile was observed for the cotton-PS material 23 in the dark (used as control). These controls demonstrated that either chemical modification of cotton alone or light exposure alone had no influence on bacterial reduction. In 2022, Chen and collaborators [159] reported the development of the porous fiber CEL-THPP@Zn with promising antibacterial features ( Figure 17). The authors used microcrystalline cellulose (MCC) to obtain, via oxidation with sodium periodate, the oxidized cellulose containing aldehyde groups (DAC), which was used to immobilize through imine bonds the porphyrin 5,10,15,20-tetrakis(4-hydrazinecarbonylphenyl)porphyrin (THPP). Then, the self-assembly of the resulting hybrid CEL-THPP in the presence Zn(II) ions afforded the desired composite CEL-THPP@Zn as a rod-shaped crystalline fiber loaded with porous porphyrin-zinc nanospheres. The antibacterial activity of the new prepared material was assessed against Gram-(+) S. aureus and Gram-(-) E. coli selected as bacterial models. A time-dependent correlation of bacterial inhibition as well as a correlation with antibacterial material concentration were found. The viability of E. coli incubated with 5 or 20 μg mL −1 concentrations of CEL-THPP@Zn decreases from 82% to 1%. In the case of S. aureus, a higher CEL-THPP@Zn concentration (200 μg mL −1 ) was needed to achieve total bacteria inactivation. The antibacterial behavior was justified considering the destruction of the bacterial membrane through the porphyrin zinc nanospheres. The ability of these porous fibers to adsorb both bacteria was also evaluated, opening the possi- Synthetic methodology used to covalently graft 5-(4-aminophenyl)-10,15,20triphenylporphyrin 21 on cellulose fabrics (cotton) via cyanuric chloride as grafting agent (Adapted from reference [158]).
Experimental data showed that the cotton-PS material 23 produced a photobactericidal effect at quantity as low as~0.8 µmol cm −2 of PS on the fabric sample. After 24 h exposure to white light and a total light dose of 9.5 J cm −2 , a reduction of 93.7% (~1.2 log reduction) of bacterial abundance was achieved when compared with the initial bacterial concentration.
During the experiment, the bacterial growth increased by 4 logs for all the untreated (without PS) cotton samples either in the dark or under light irradiation. The same bacterial growth profile was observed for the cotton-PS material 23 in the dark (used as control). These controls demonstrated that either chemical modification of cotton alone or light exposure alone had no influence on bacterial reduction.
In 2022, Chen and collaborators [159] reported the development of the porous fiber CEL-THPP@Zn with promising antibacterial features ( Figure 17). The authors used microcrystalline cellulose (MCC) to obtain, via oxidation with sodium periodate, the oxidized cellulose containing aldehyde groups (DAC), which was used to immobilize through imine bonds the porphyrin 5,10,15,20-tetrakis(4-hydrazinecarbonylphenyl)porphyrin (THPP). Then, the self-assembly of the resulting hybrid CEL-THPP in the presence Zn(II) ions afforded the desired composite CEL-THPP@Zn as a rod-shaped crystalline fiber loaded with porous porphyrin-zinc nanospheres. The antibacterial activity of the new prepared material was assessed against Gram-(+) S. aureus and Gram-(−) E. coli selected as bacterial models. A time-dependent correlation of bacterial inhibition as well as a correlation with antibacterial material concentration were found. The viability of E. coli incubated with 5 or 20 µg mL −1 concentrations of CEL-THPP@Zn decreases from 82% to 1%. In the case of S. aureus, a higher CEL-THPP@Zn concentration (200 µg mL −1 ) was needed to achieve total bacteria inactivation. The antibacterial behavior was justified considering the destruction of the bacterial membrane through the porphyrin zinc nanospheres. The ability of these porous fibers to adsorb both bacteria was also evaluated, opening the possibility of these composites to be used not only on bacterial inhibition, but also in filtration processes. Reprinted with permission from Ref. [159]. 2009., Springer Nature.

Cationic Porphyrins
Meso-substituted porphyrins, bearing positively charged groups have shown remarkable photodynamic activity against both, Gram-(-) and Gram-(+) bacteria [66,81,160]. Positive charges are able to induce a strong electrostatic interaction with the external negatively charged structures of the bacterial cells, thus facilitating their interaction with the bacteria [161,162]. However, other PS properties, such as amphiphilicity, cell membrane interaction, and internalization, can also play a role to account for the therapeutic effect [161,163].

Cationic Porphyrins
Meso-substituted porphyrins, bearing positively charged groups have shown remarkable photodynamic activity against both, Gram-(−) and Gram-(+) bacteria [66,81,160]. Positive charges are able to induce a strong electrostatic interaction with the external negatively charged structures of the bacterial cells, thus facilitating their interaction with the bacteria [161,162]. However, other PS properties, such as amphiphilicity, cell membrane interaction, and internalization, can also play a role to account for the therapeutic effect [161,163].
Commercially available cellophane sheets of 50 μm thickness were kept in contact with the porphyrin solutions of water or water/methanol at 50 °C. The uptake of positively Similar photobactericidal results were reported with the 25 cellophane films only towards S. aureus. The authors highlighted that the attempts to impregnate the cellophane films with anionic porphyrins were not successful.
Later on, Krausz and co-workers [165] prepared and characterized photobactericidal materials 26 through the immobilization of 5-(pyridin-4-yl)-10,15,20-tris(p-tolyl)porphyrin in chloroacetyl cellulose esters ( Figure 19A). Similar photobactericidal results were reported with the 25 cellophane films only towards S. aureus. The authors highlighted that the attempts to impregnate the cellophane films with anionic porphyrins were not successful.
First, cellulose was dissolved in dimethylacetamide (DMAc)/LiCl and was reacted with chloroacetyl chloride leading to a functionalized plastic film with 2-chloroacetoxy units. The modified polymer was isolated by precipitation with water. Purification was carried out by successive dissolution-precipitation cycles and plastic films were then obtained by casting. The grafting of 5-(pyridin-4-yl)-10,15,20-tris(p-tolyl)porphyrin on chloroacetyl cellulose esters was achieved by a reaction of the plastic film previously synthesized, dissolved in anhydrous DMF, with the porphyrin derivative, at room temperature. The plastics films obtained after quaternization of the pyridine units were obtained by casting in a Petri dish after the adequate work-up ( Figure 19B).
The photoactive material 26 was tested against E. coli and S. aureus and the results showed that the high photobactericidal activity of the plastic films 26 prepared (no bacterial growth) was attributed to 1 O2 generation and was dependent on the amount of porphyrin grafting (≥0.2 porphyrin content). In the absence of porphyrinic PS, the films allowed the full growth of bacteria. In 2010, the same group [158] reported the covalent grafting of a cationic amino porphyrin 27a on cotton fabrics via a 1,3,5-triazine linker 28a without any preliminary chemical modification of the cellulosic material ( Figure 20). In fact, several research groups have explored 1,3,5-triazine linkers for the fabrication of covalently linked porphyrin-cellulose antimicrobial materials. The resulting porphyrin-triazine derivative grafted on cotton fabrics 29a was tested in vitro against S. aureus. When the prepared cationic material 29a was exposed to a white light for 24 h with a total light dose of 9.5 J cm 2 , a very high First, cellulose was dissolved in dimethylacetamide (DMAc)/LiCl and was reacted with chloroacetyl chloride leading to a functionalized plastic film with 2-chloroacetoxy units. The modified polymer was isolated by precipitation with water. Purification was carried out by successive dissolution-precipitation cycles and plastic films were then obtained by casting. The grafting of 5-(pyridin-4-yl)-10,15,20-tris(p-tolyl)porphyrin on chloroacetyl cellulose esters was achieved by a reaction of the plastic film previously synthesized, dissolved in anhydrous DMF, with the porphyrin derivative, at room temperature. The plastics films obtained after quaternization of the pyridine units were obtained by casting in a Petri dish after the adequate work-up ( Figure 19B).
The photoactive material 26 was tested against E. coli and S. aureus and the results showed that the high photobactericidal activity of the plastic films 26 prepared (no bacterial growth) was attributed to 1 O 2 generation and was dependent on the amount of porphyrin grafting (≥0.2 porphyrin content). In the absence of porphyrinic PS, the films allowed the full growth of bacteria.
In 2010, the same group [158] reported the covalent grafting of a cationic amino porphyrin 27a on cotton fabrics via a 1,3,5-triazine linker 28a without any preliminary chemical modification of the cellulosic material ( Figure 20). In fact, several research groups have explored 1,3,5-triazine linkers for the fabrication of covalently linked porphyrincellulose antimicrobial materials. The resulting porphyrin-triazine derivative grafted on cotton fabrics 29a was tested in vitro against S. aureus. When the prepared cationic material 29a was exposed to a white light for 24 h with a total light dose of 9.5 J cm 2 , a very high photoinactivation performance against S. aureus was achieved, with the limit detection of the method attained (>6 log of reduction).  . Synthetic methodology used to prepare the cellulose fabrics 29a-c from cationic amino porphyrins using cyanuric chloride to introduce the grafting unit (Adapted from references [158,166]).
The authors also assessed the efficacy of the photomaterial 29a towards the gram-(−) bacterial strain E. coli [166]. After 24 h of exposure to white light (a total light dose of 9.5 J cm −2 ) of binomium photomaterial 29a and E. coli, no photoactivity was found. However, in the same photodynamic conditions, high growth inhibition rates of S. aureus (>4 log reduction) were reached. Despite the good results achieved for light activated PS, the material 29a showed toxicity in the dark (80%) towards S. aureus. The authors attribute this fact to the presence of positively charged groups in the porphyrin macrocycle, known for their membrane disruption action on bacteria, even without light activation [166].
An extension of the previous studies was reported by the same research group [167]. The authors used the same approach (cyanuric chloride as a grafting agent) to immobilize 27b in filter paper ( Figure 21) and evaluated the antimicrobial efficacy of this bactericidal paper 29b against S. aureus and E. coli bacterial strains. The authors showed that the untreated paper in the dark, or under white light irradiation, as well as the treated paper in the dark, allowed a bacterial growth of 4 and 2 log units for S. aureus and E. coli, respectively, when compared with the initial bacterial concentration. However, no survival of either type of bacteria was detected on the paper bearing the porphyrin 27b after white light exposure for 24 h with a total light dose of 9.5 J cm −2 (inhibition of ~4 and 2 log units for S. aureus and E. coli, respectively). The authors also assessed the efficacy of the photomaterial 29a towards the gram-(−) bacterial strain E. coli [166]. After 24 h of exposure to white light (a total light dose of 9.5 J cm −2 ) of photomaterial 29a and E. coli, no photoactivity was found. However, in the same photodynamic conditions, high growth inhibition rates of S. aureus (>4 log reduction) were reached. Despite the good results achieved for light activated PS, the material 29a showed toxicity in the dark (80%) towards S. aureus. The authors attribute this fact to the presence of positively charged groups in the porphyrin macrocycle, known for their membrane disruption action on bacteria, even without light activation [166].
An extension of the previous studies was reported by the same research group [167]. The authors used the same approach (cyanuric chloride as a grafting agent) to immobilize 27b in filter paper ( Figure 21) and evaluated the antimicrobial efficacy of this bactericidal paper 29b against S. aureus and E. coli bacterial strains. The authors showed that the untreated paper in the dark, or under white light irradiation, as well as the treated paper in the dark, allowed a bacterial growth of 4 and 2 log units for S. aureus and E. coli, respectively, when compared with the initial bacterial concentration. However, no survival of either type of bacteria was detected on the paper bearing the porphyrin 27b after white light exposure for 24 h with a total light dose of 9.5 J cm −2 (inhibition of~4 and 2 log units for S. aureus and E. coli, respectively).  Figure 21. Photographs of (A) filter paper; (B) filter paper after reaction with 28b giving 29b. Reprinted with permission from Ref. [167]. 2012, Elsevier.
Studies conducted by Ghiladi group [125], reported the development of self-disinfecting materials through the covalent attachment of 27b to nano-fibrillated cellulose (NFC) and paper (Pap) (Figure 22). The grafting strategy was centered on an environmentally sustainable method where the treatment of cellulose supports was mediated by an aqueous solution of cyanuric chloride, avoiding the use of organic solvents. Then, the 27b and its Zn(II) complex 27c were covalently attached by means of 1,3,5-triazine linkage to NFC or paper giving the materials 29b@NFC, 29c@NFC, 29b@Pap, and 29c@Pap ( Figure  20). Reprinted with permission from Ref. [125]. © The Royal Society of Chemistry 2019.
In vitro aPDT assays employing the PS-cellulose conjugated materials (29b@NFC, 29c@NFC, 29b@Pap, and 29c@Pap) ( Figure 22) were performed under fixed illumination conditions (1 h, white light (400-700 nm) at an irradiance of 65 ± 5 mW cm −2 towards four Studies conducted by Ghiladi group [125], reported the development of self-disinfecting materials through the covalent attachment of 27b to nano-fibrillated cellulose (NFC) and paper (Pap) (Figure 22). The grafting strategy was centered on an environmentally sustainable method where the treatment of cellulose supports was mediated by an aqueous solution of cyanuric chloride, avoiding the use of organic solvents. Then, the 27b and its Zn(II) complex 27c were covalently attached by means of 1,3,5-triazine linkage to NFC or paper giving the materials 29b@NFC, 29c@NFC, 29b@Pap, and 29c@Pap ( Figure 20).  Figure 21. Photographs of (A) filter paper; (B) filter paper after reaction with 28b giving 29b. Reprinted with permission from Ref. [167]. 2012, Elsevier.
Studies conducted by Ghiladi group [125], reported the development of self-disinfecting materials through the covalent attachment of 27b to nano-fibrillated cellulose (NFC) and paper (Pap) (Figure 22). The grafting strategy was centered on an environmentally sustainable method where the treatment of cellulose supports was mediated by an aqueous solution of cyanuric chloride, avoiding the use of organic solvents. Then, the 27b and its Zn(II) complex 27c were covalently attached by means of 1,3,5-triazine linkage to NFC or paper giving the materials 29b@NFC, 29c@NFC, 29b@Pap, and 29c@Pap ( Figure  20). Reprinted with permission from Ref. [125]. © The Royal Society of Chemistry 2019.
In vitro aPDT assays employing the PS-cellulose conjugated materials (29b@NFC, 29c@NFC, 29b@Pap, and 29c@Pap) ( Figure 22) were performed under fixed illumination conditions (1 h, white light (400-700 nm) at an irradiance of 65 ± 5 mW cm −2 towards four In vitro aPDT assays employing the PS-cellulose conjugated materials (29b@NFC, 29c@NFC, 29b@Pap, and 29c@Pap) ( Figure 22) were performed under fixed illumination conditions (1 h, white light (400-700 nm) at an irradiance of 65 ± 5 mW cm −2 towards four multiresistant bacteria strains (S. aureus; Enterococcus faecium, Acinetobacter baumannii and Klebsiella pneumoniae) and two enveloped viruses (Dengue-1 and vesicular stomatitis virus (VSV)). Table 1 summarizes the efficacy of prepared materials against the bacterial strains and viruses tested. It was observed that against Gram-(+) bacteria, methicillin-resistant S. aureus (MRSA), and E. faecium, all photoactive materials achieved the detection limit of the inactivation method (99.9999%, 6 log unit reduction in CFU mL −1 ). In terms of killing Gram-(−) bacterium A. baumannii, most of the materials achieved the method detection limit (99.9999%, 6 log of abundance reduction) with exception of 29b@NFC which was able to inhibit 4.5 log units (99.994% of reduction). For 29b@NFC, no antibacterial activity was found against K. pneumoniae whereas photoinactivation with 29c@NFC reached~82% (0.73 log of reduction in CFU mL −1 ). On the other hand, when paper supports have been employed against K. pneumoniae photoinactivations of 99.9994% (~5.3 log of reduction) in the presence of 29b@Pap and 99.47% (~2.3 log of reduction) for 29c@Pap have been achieved.
The antiviral photodynamic inactivation studies employing 29b@NFC and 29c@NFC were conducted towards the two model enveloped viruses, (VSV and dengue-1), using similar photodynamic conditions to those of the antibacterial studies. Impressively, both materials 29b@NFC and 29c@NFC exhibited photoinactivation of the viral particles: dengue-1 by 99.99% (4 log reduction in PFU mL −1 ), and VSV by 99.9999% (6 log reduction in PFU mL −1 ). However, a dark viral inactivation of~90% (~1 log of reduction in PFU mL −1 ) was also revealed in the dark controls.
Ghiladi research group [168,169] also employed the "Click Chemistry" approach [Cu(I)catalyzed Huisgen 1,3-dipolar cycloaddition] to immobilize covalently the tricationic porphyrin 30 bearing an alkynyl function to cellulose nanocrystals bearing azide moieties, giving material 31 ( Figure 23). The authors prepared the cellulose nanocrystals by hydrolysis of Whatman #1 filter paper (98% α-cellulose, 80% crystallinity) previously blended using aqueous HBr. After removing the excess of acid, water-soluble fragments and ultrafine particles were obtained with an average length of 100-400 nm. These nanocrystals were then functionalized with the azide moieties for further reaction with the alkynylporphyrin 30. It was demonstrated that a suspension of material 31 showed an excellent photodynamic inactivation efficacy toward Mycobacterium smegmatis and S. aureus. However, only slight activity against E. coli was attained.
In the first aPDT assays, the bacterial cultures were irradiated with white light (400-700 nm at an irradiance of 60 mW cm −2 ) for 30 min (total light dose 108 J cm −2 ) in PBS with 20 µM of 31 after a dark incubation period and the results showed a 6 log reduction in viable cells against S. aureus (5 min incubation), 3.5 log for M. smegmatis (45 min incubation), and 2 log for E. coli (60 min incubation) [168].
In the first aPDT assays, the bacterial cultures were irradiated with white light (400-700 nm at an irradiance of 60 mW cm −2 ) for 30 min (total light dose 108 J cm −2 ) in PBS with 20 µ M of 31 after a dark incubation period and the results showed a 6 log reduction in viable cells against S. aureus (5 min incubation), 3.5 log for M. smegmatis (45 min incubation), and 2 log for E. coli (60 min incubation) [168].
As an extension of the previous work, in order to gain insight into the photodynamic action mechanism , the same group used the same photoactive material against different bacterial strains [169]. In that view, photoactive material 31 (20 µ M) was used in the inactivation of multidrug resistant A. baumannii, S. aureus and Pseudomonas aeruginosa (≈10 8 CFU mL −1 ) with visible light at an irradiance of 65 mW cm −2 [169]. A decrease of 6 log in viable cells was observed for S. aureus (5 min incubation), 5-6 log units for sensitive A. baumannii (30 min incubation) and multidrug resistant A. baumannii (15 min incubation) and 2.5 log units for P. aeruginosa (60 min incubation) after receiving a total light dose of 118 J cm −2 (30 min of irradiation). Confocal laser scanning microscopy analysis of samples of A. baumannii or S. aureus incubated with the photoactive material 31 suggested a lack of PS internalization by the bacteria. Considering both studies, the authors commented that material 31 was able to mediate the photodynamic inactivation of all the tested bacterial strains studied. Confocal microscopy demonstrated that the mode of action for 31 did not proceed through a PS-binding or uptake mechanism. The cytotoxic species (e.g., 1 O2 and other ROS) generated by the photodynamic process damaged the bacteria wall, leading to cell inactivation. These results corroborate other studies that highlight the inactivation efficiency of porphyrins towards bacteria without PS internalization requirement [161].
Considering the promising results, and having in mind scalability for the production of anti-infective or self-sterilizing materials, Ghiladi and co-authors [170] also employed cellulose paper activated with azide moieties to graft other porphyrin derivatives (neutral and negatively charged) and BODIPYs bearing an alkynyl unit via the "Click-Chemistry" approach. The bactericidal papers obtained with a dye load of ca. 8 mg g −1 (12.4 nmol mg −1 ) were fully characterized and their antibacterial efficacy was evaluated against "ESKAPE" pathogens, e.g., S. aureus, vancomycin-resistant E. faecium, A. baumannii, P. aeruginosa, and K. pneumoniae. However, from all the bactericidal papers prepared, the best results were Figure 23. Ghiladi grafting method to prepare material 31 by covalently grafting the tricationic porphyrin 30 bearing an alkynyl function to cellulose nanocrystals or cellulose fibers (Whatman #1 filter paper) bearing azide moieties (Adapted from Refs. [168][169][170]).
As an extension of the previous work, in order to gain insight into the photodynamic action mechanism, the same group used the same photoactive material against different bacterial strains [169]. In that view, photoactive material 31 (20 µM) was used in the inactivation of multidrug resistant A. baumannii, S. aureus and Pseudomonas aeruginosa (≈10 8 CFU mL −1 ) with visible light at an irradiance of 65 mW cm −2 [169]. A decrease of 6 log in viable cells was observed for S. aureus (5 min incubation), 5-6 log units for sensitive A. baumannii (30 min incubation) and multidrug resistant A. baumannii (15 min incubation) and 2.5 log units for P. aeruginosa (60 min incubation) after receiving a total light dose of 118 J cm −2 (30 min of irradiation). Confocal laser scanning microscopy analysis of samples of A. baumannii or S. aureus incubated with the photoactive material 31 suggested a lack of PS internalization by the bacteria. Considering both studies, the authors commented that material 31 was able to mediate the photodynamic inactivation of all the tested bacterial strains studied. Confocal microscopy demonstrated that the mode of action for 31 did not proceed through a PS-binding or uptake mechanism. The cytotoxic species (e.g., 1 O 2 and other ROS) generated by the photodynamic process damaged the bacteria wall, leading to cell inactivation. These results corroborate other studies that highlight the inactivation efficiency of porphyrins towards bacteria without PS internalization requirement [161].
Considering the promising results, and having in mind scalability for the production of anti-infective or self-sterilizing materials, Ghiladi and co-authors [170] also employed cellulose paper activated with azide moieties to graft other porphyrin derivatives (neutral and negatively charged) and BODIPYs bearing an alkynyl unit via the "Click-Chemistry" approach. The bactericidal papers obtained with a dye load of ca. 8 mg g −1 (12.4 nmol mg −1 ) were fully characterized and their antibacterial efficacy was evaluated against "ESKAPE" pathogens, e.g., S. aureus, vancomycin-resistant E. faecium, A. baumannii, P. aeruginosa, and K. pneumoniae. However, from all the bactericidal papers prepared, the best results were obtained with the material 31 (positive charged porphyrin derivative) that was able to photoinactivate >4 log (99.99%) of all bacterial strains studied upon illumination for 30 min with white light (400−700 nm) at an irradiance of 65 mW cm −2 . The same material 31 was also able to photoinactivate dengue-1 virus by >4 log, influenza A virus by~2.5 log (~99.5%), and human adenovirus-5 by~2 log (~99%). Zerrouk research groups [171] also used the concept of "click chemistry", as a strategy for grafting propargylated cationic porphyrins in azide modified cellulose materials. Zerrouk considered Kraft Pulp (KrP) as cellulose raw-material for the preparation of antimicrobial photoactive material. The material was first functionalized, via hydroxyl group tosylation, following by the azide group insertion in the presence of sodium azide, yielding 6-azido-6-deoxycellulose ( Figure 24). Then, the treatment 5,10,15,20-tetra(pyridin-4-yl)porphyrin 32 with an excess of propargyl bromide at room temperature afforded the propargylated porphyrin derivative 33 in quantitative yield that after coordination with Zn(II) afforded the corresponding metalloporphyrin 34.
din-4-yl)porphyrin 32 with an excess of propargyl bromide at room temperature afforded the propargylated porphyrin derivative 33 in quantitative yield that after coordination with Zn(II) afforded the corresponding metalloporphyrin 34.
The covalent linkage between the azide kraft pulp and the propargylated cationic metalloporphyrin 34 was carried out using Cu(I)-catalyzed alkyne-azide cycloaddition (CuAAC) approach. The photodynamic antimicrobial activity of new cellulose material 35 was evaluated against the S. aureus, E. coli, and P. aeruginosa bacterial strains under white light irradiation (400-800 nm) at an irradiance of 0.16 mW cm −2 and a total light dose of 13.8 J cm −2 . The functionalized kraft pulp precursors, untreated, tosylated, and azidated were used as control materials and no dark or light antibacterial activity was achieved for all controls. Furthermore, material 35 did not show activity against Gram-(-) bacteria E. coli and P. aeruginosa under dark and light conditions. However, bacteriostatic activity against Gram-(+) bacterium S. aureus was observed (99% of abundance reduction, 2 log reduction in CFU mL −1 ) after dark exposure to the material 35, which changed to a bactericidal effect of (>99.9% of abundance reduction; 3 log reduction) under light conditions. Figure 24. Synthetic strategy adopted by Zerrouk and co-workers to obtain the propargylated cationic porphyrin 34 and to graft it into the azide kraft pulp (adapted form [171]). Figure 24. Synthetic strategy adopted by Zerrouk and co-workers to obtain the propargylated cationic porphyrin 34 and to graft it into the azide kraft pulp (adapted form [171]).
The covalent linkage between the azide kraft pulp and the propargylated cationic metalloporphyrin 34 was carried out using Cu(I)-catalyzed alkyne-azide cycloaddition (CuAAC) approach. The photodynamic antimicrobial activity of new cellulose material 35 was evaluated against the S. aureus, E. coli, and P. aeruginosa bacterial strains under white light irradiation (400-800 nm) at an irradiance of 0.16 mW cm −2 and a total light dose of 13.8 J cm −2 . The functionalized kraft pulp precursors, untreated, tosylated, and azidated were used as control materials and no dark or light antibacterial activity was achieved for all controls. Furthermore, material 35 did not show activity against Gram-(−) bacteria E. coli and P. aeruginosa under dark and light conditions. However, bacteriostatic activity against Gram-(+) bacterium S. aureus was observed (99% of abundance reduction, 2 log reduction in CFU mL −1 ) after dark exposure to the material 35, which changed to a bactericidal effect of (>99.9% of abundance reduction; 3 log reduction) under light conditions.
A similar approach was used by Guesmi to obtain material 37 from the monopropargylated cationic fluoroporphyrin 36 and cellulose functionalized with azide units (Figure 25) [172]. The catalytic coupling reaction was performed in water and in the presence of copper nanoparticles (CuNP).
A similar approach was used by Guesmi to obtain material 37 from the mono-propargylated cationic fluoroporphyrin 36 and cellulose functionalized with azide units (Figure 25) [172]. The catalytic coupling reaction was performed in water and in the presence of copper nanoparticles (CuNP). Figure 25. Synthesis of cellulose fluoro triazole-porphyrin conjugate 37 by "click chemistry" approach (Adapted from Ref. [172]).
Although photodynamic inactivation was not accessed in this study, the antimicrobial activity of the newly porphyrin-cellulose material 37 was evaluated in the dark after incubation with E. coli and S. aureus, along with the non-functionalized textiles as a comparison, at different times. The results showed that the bactericidal efficacy was time dependent: after 20 min of bacterial strain incubation with material 37, a 3 log (99.9%) reduction on bacterial growth was noticed, whereas a 6 log (99.9999%) reduction was obtained after 80 min of photodynamic treatment.
In addition, in 2016, Rahimi, Rassa and Fayyaz [104,173] reported the antimicrobial properties of 5,10,15,20-tetrakis(N,N,N-trimethylanilinium-4-yl)porphyrin, 25 and of its Zn(II) complex 25a after being just embedded in cellulosic fabrics. The process involved the soaking of a 100% cellulosic fabric, pre-treated with an aqueous solution of Na2CO3, with solutions of porphyrins 25 and 25a in PBS for 30 min at 50 °C. After this period, the unbound porphyrin was thoroughly washed, and the molar embedding ratio was calculated by UV-Vis. The authors reported that the embedding yield was dependent on the initial concentration of the PS and its presence in the cellulosic fabrics was confirmed by spectroscopic techniques. The antimicrobial activity of the new materials was tested under visible light irradiation (100 W tungsten lamp with an average irradiance of ~0.36 mW.cm −2 ) towards S. aureus, P. aeruginosa, and E. coli. The results showed that the irradiation period and the PS concentration were important factors to be taken into account. S. aureus was full inactivated (>3 log reduction) with both prepared cellulose fabrics at PS concentration of 100 μM after 30 min of irradiation while for P. aeruginosa (20% of reduction), at the same PS concentration, the full inactivation (>3 log reduction, >99.9%) was only attained in the presence of Zn(II) complex 25a after 90 min of irradiation. The worse efficiency of these materials was observed towards E. coli (58.5% for 25 and 30% for 25a, <0.4 log reduction) at the same concentration and after 90 min of irradiation.

Anionic Porphyrins
The above-mentioned section clearly demonstrates that aPDT research efforts have been focused on the development of cationic complexes, as their biocide efficacy arises from the possibility of interaction of these compounds with the bacterial cell membrane. The development of anionic porphyrins, regardless of their high efficiency to produce ROS, does not receive great attention because of their low interaction on the membrane. Anionic porphyrins carry typically sulfonated [174][175][176][177], carboxylic acid/carboxylate Figure 25. Synthesis of cellulose fluoro triazole-porphyrin conjugate 37 by "click chemistry" approach (Adapted from Ref. [172]).
Although photodynamic inactivation was not accessed in this study, the antimicrobial activity of the newly porphyrin-cellulose material 37 was evaluated in the dark after incubation with E. coli and S. aureus, along with the non-functionalized textiles as a comparison, at different times. The results showed that the bactericidal efficacy was time dependent: after 20 min of bacterial strain incubation with material 37, a 3 log (99.9%) reduction on bacterial growth was noticed, whereas a 6 log (99.9999%) reduction was obtained after 80 min of photodynamic treatment.
In addition, in 2016, Rahimi, Rassa and Fayyaz [104,173] reported the antimicrobial properties of 5,10,15,20-tetrakis(N,N,N-trimethylanilinium-4-yl)porphyrin, 25 and of its Zn(II) complex 25a after being just embedded in cellulosic fabrics. The process involved the soaking of a 100% cellulosic fabric, pre-treated with an aqueous solution of Na 2 CO 3 , with solutions of porphyrins 25 and 25a in PBS for 30 min at 50 • C. After this period, the unbound porphyrin was thoroughly washed, and the molar embedding ratio was calculated by UV-Vis. The authors reported that the embedding yield was dependent on the initial concentration of the PS and its presence in the cellulosic fabrics was confirmed by spectroscopic techniques. The antimicrobial activity of the new materials was tested under visible light irradiation (100 W tungsten lamp with an average irradiance of~0.36 mW.cm −2 ) towards S. aureus, P. aeruginosa, and E. coli. The results showed that the irradiation period and the PS concentration were important factors to be taken into account. S. aureus was full inactivated (>3 log reduction) with both prepared cellulose fabrics at PS concentration of 100 µM after 30 min of irradiation while for P. aeruginosa (20% of reduction), at the same PS concentration, the full inactivation (>3 log reduction, >99.9%) was only attained in the presence of Zn(II) complex 25a after 90 min of irradiation. The worse efficiency of these materials was observed towards E. coli (58.5% for 25 and 30% for 25a, <0.4 log reduction) at the same concentration and after 90 min of irradiation.

Anionic Porphyrins
The above-mentioned section clearly demonstrates that aPDT research efforts have been focused on the development of cationic complexes, as their biocide efficacy arises from the possibility of interaction of these compounds with the bacterial cell membrane. The development of anionic porphyrins, regardless of their high efficiency to produce ROS, does not receive great attention because of their low interaction on the membrane. Anionic porphyrins carry typically sulfonated [174][175][176][177], carboxylic acid/carboxylate [178,179] or phosphonate/phosphinate groups [180][181][182]. These negatively charged functional groups induce an inherent solubility of the porphyrins in aqueous media, which would greatly benefit their application in biological or environmental contexts.
Although there are several reports dealing with the immobilization of cationic and neutral porphyrins onto cellulosic materials, to date, there have been only two studies that describe the covalent linking of an anionic porphyrin derivative onto a cellulose scaffold and its use in light-promoted inactivation of bacteria.
The photodynamic efficacy of anionic porphyrin-grafted in cotton 40 was tested in vitro, against S. aureus. When functional cellulose-based material 40 (~10 μmol of PS) was incubated for 24 h and exposed to white light with a total light dose of 9.5 J/cm 2 , the bacterial reductions were 37% (~0.2 log reduction), 94.7% (~1.3 log reduction), and >99.99% (>4 log reduction) for anionic, neutral, and cationic materials, respectively. The experimental data suggest that results are dependent on the PS charge. It was highlighted that the cationic material 29a showed the highest antimicrobial effect against S. aureus, probably due to the presence of a positive charge, responsible for disrupting cell walls. Figure 26. Synthetic methodology used to covalently graft the anionic amino porphyrin 38 on cellulose fabrics via cyanuric chloride approach (Adapted from reference [158]).
Later on, Carofiglio and co-workers [183] explored the features and properties of the photoactive material obtained by conjugating the anionic and water-soluble amino porphyrin 38 with nanocrystalline cellulose (NCC).
The NCC support selected was produced by sulfuric acid treatment of commercial microcrystalline cellulose (66% of crystallinity). The oxidation with TEMPO in the presence of NaOCl-NaBr selectively converted some primary hydroxyl groups on the NCC surface to carboxylic functionalities. The conjugation of 38 to the obtained NCC-COOH via amide linkage ( Figure 27) was performed using carbodiimide crosslinker chemistry in an acidic aqueous solution of 2-(N-morpholino)ethanesulfonic acid (MES, 50 mM, pH = 4) in the presence of N-(3-dimethylaminopropyl)-N-ethylcarbodiimide hydrochloride (EDC.HCl) and N-hydroxysuccinimide (NHS). The 38@NCC material was isolated after three days under stirring, followed by the usual centrifugation, and washing work-up. Additionally, the authors evaluated the potential of this photoactive material as PS by evaluating the 1 O2 generation. However, no photoinactivaton studies against bacteria have been presented until now. The photodynamic efficacy of anionic porphyrin-grafted in cotton 40 was tested in vitro, against S. aureus. When functional cellulose-based material 40 (~10 µmol of PS) was incubated for 24 h and exposed to white light with a total light dose of 9.5 J/cm 2 , the bacterial reductions were 37% (~0.2 log reduction), 94.7% (~1.3 log reduction), and >99.99% (>4 log reduction) for anionic, neutral, and cationic materials, respectively. The experimental data suggest that results are dependent on the PS charge. It was highlighted that the cationic material 29a showed the highest antimicrobial effect against S. aureus, probably due to the presence of a positive charge, responsible for disrupting cell walls.
Later on, Carofiglio and co-workers [183] explored the features and properties of the photoactive material obtained by conjugating the anionic and water-soluble amino porphyrin 38 with nanocrystalline cellulose (NCC).
The NCC support selected was produced by sulfuric acid treatment of commercial microcrystalline cellulose (66% of crystallinity). The oxidation with TEMPO in the presence of NaOCl-NaBr selectively converted some primary hydroxyl groups on the NCC surface to carboxylic functionalities. The conjugation of 38 to the obtained NCC-COOH via amide linkage ( Figure 27) was performed using carbodiimide crosslinker chemistry in an acidic aqueous solution of 2-(N-morpholino)ethanesulfonic acid (MES, 50 mM, pH = 4) in the presence of N-(3-dimethylaminopropyl)-N-ethylcarbodiimide hydrochloride (EDC.HCl) and N-hydroxysuccinimide (NHS). The 38@NCC material was isolated after three days under stirring, followed by centrifugation, and washing work-up. Additionally, the authors evaluated the potential of this photoactive material as PS by evaluating the 1 O 2 generation. However, no photoinactivaton studies against bacteria have been presented until now.

Other Cellulose Based Biopolymer and Other Cellulose-like Fibres as Supports
In addition to cellulose, other non-toxic and biodegradable supports, such as chitosan, chitin, xylan or lignin biomaterials (Figure 28), and organic synthetic polymers as supports for PS to be used in aPDT, deserve to be discussed since they have an impact in this research field [184,185]. In the grafting of PS to synthetic polymers, different approaches could be considered: (i) covalent or non-covalent linking of the macrocycle with polymers, or (ii) the copolymerization of PS with polymerizable moieties with monomers or electrospinning techniques.
The quest for affordable and industrially robust fabrication technologies of antimicrobial surfaces and biomaterials led Ghiladi and co-workers [186] to employ electrospinning in the preparation of a non-woven textile comprised of polyacrylonitrile nanofibers (PAN) embedded with a porphyrin-based cationic photosensitizer 39, termed PAN-39 ( Figure 29). Antibacterial efficacy of PAN-39 material (PS loading 34.8 nmol mg −1 of ma-

Other Cellulose Based Biopolymer and Other Cellulose-like Fibres as Supports
In addition to cellulose, other non-toxic and biodegradable supports, such as chitosan, chitin, xylan or lignin biomaterials (Figure 28), and organic synthetic polymers as supports for PS to be used in aPDT, deserve to be discussed since they have an impact in this research field [184,185].

Other Cellulose Based Biopolymer and Other Cellulose-like Fibres as Supports
In addition to cellulose, other non-toxic and biodegradable supports, such as chitosan, chitin, xylan or lignin biomaterials (Figure 28), and organic synthetic polymers as supports for PS to be used in aPDT, deserve to be discussed since they have an impact in this research field [184,185]. In the grafting of PS to synthetic polymers, different approaches could be considered: (i) covalent or non-covalent linking of the macrocycle with polymers, or (ii) the copolymerization of PS with polymerizable moieties with monomers or electrospinning techniques.
The quest for affordable and industrially robust fabrication technologies of antimicrobial surfaces and biomaterials led Ghiladi and co-workers [186] to employ electrospinning in the preparation of a non-woven textile comprised of polyacrylonitrile nanofibers (PAN) embedded with a porphyrin-based cationic photosensitizer 39, termed PAN-39 ( Figure 29). Antibacterial efficacy of PAN-39 material (PS loading 34.8 nmol mg −1 of ma- In the grafting of PS to synthetic polymers, different approaches could be considered: (i) covalent or non-covalent linking of the macrocycle with polymers, or (ii) the co-polymerization of PS with polymerizable moieties with monomers or electrospinning techniques.
The quest for affordable and industrially robust fabrication technologies of antimicrobial surfaces and biomaterials led Ghiladi and co-workers [186] to employ electrospinning in the preparation of a non-woven textile comprised of polyacrylonitrile nanofibers (PAN) embedded with a porphyrin-based cationic photosensitizer 39, termed PAN-39 ( Figure 29). Antibacterial efficacy of PAN-39 material (PS loading 34.8 nmol mg −1 of material) was evaluated against multiresistant bacterial models: S. aureus; vancomycin-resistant E. faecium; A. baumannii; K. pneumonia, as well as E. coli. The results obtained showed a broad photodynamic inactivation of all multiresistant bacterial strains studied upon white light exposure (400-700 nm, 30 min of exposure at an irradiance of 65 ± 5 mW cm −2 ) by a minimum of 99.9996% (>5.8 log of abundance reduction) regardless of taxonomic classification. PAN-39 also inactivated human adenovirus-5 (~99.8% reduction in PFU/mL,~3 log reduction) and VSV particles (>7 log reduction in PFU mL −1 ). When compared to previous studies with cellulose-based materials employing this same PS (porphyrin 30) [168][169][170], the higher photodynamic inactivation performance achieved here with PAN-39 is likely due to the combined effects of higher PS loading and a greater surface area imparted by the use of nanofibers. terial) was evaluated against multiresistant bacterial models: S. aureus; vancomycin-resistant E. faecium; A. baumannii; K. pneumonia, as well as E. coli. The results obtained showed a broad photodynamic inactivation of all multiresistant bacterial strains studied upon white light exposure (400-700 nm, 30 min of exposure at an irradiance of 65 ± 5 mW cm −2 ) by a minimum of 99.9996% (>5.8 log of abundance reduction) regardless of taxonomic classification. PAN-39 also inactivated human adenovirus-5 (~99.8% reduction in PFU/mL, ~3 log reduction) and VSV particles (>7 log reduction in PFU mL −1 ). When compared to previous studies with cellulose-based materials employing this same PS (porphyrin 30) [168][169][170], the higher photodynamic inactivation performance achieved here with PAN-39 is likely due to the combined effects of higher PS loading and a greater surface area imparted by the use of nanofibers. The work of Rodgers and collaborators [187] consisted in the immobilization of 5,10,15,20-tetrakis(4-carboxyphenyl)porphyrin 40 on a chitin support (the second most abundant natural polysaccharide, after cellulose, a linear polymer composed of repeating β(14)-N-acetylglucosamine units) using ionic liquids (ILs) as solvent. In this study, the Ils were used for chitin extraction and partial deacetylation, as well as a medium for grafting 40 on chitin support. Chitin was first extracted from shrimp shells using the 1-ethyl-3-methylimidazolium acetate ([C2mim][OAc]), coagulated in water, and then deacetylated. The deacetylated-chitin (DA-chitin) was dissolved in [C2mim][OAc] and the covalent attachment between the amino groups of DA-chitin and the carboxyl groups of 40 was performed in the presence of the activators EDC and N-hydroxy-succinimide (NHS) ( Figure 30). The resulting polymeric composites were cast as a film and coagulated with water to remove the IL and the excess of reagents, resulting in homogeneous 40@DAchitin films. Further modifications of the optical properties were achieved by the incorporation of metal ions (Cu 2+ , Zn 2+ , Gd 3+ , and Fe 3+ ) into the 40@DA-chitin films. In addition, the 40@DA-chitin films, with and without chelating metal ions, exhibited efficient 1 O2 production under light irradiation.
Since these films showed interesting optical and photophysical properties (good 1 O2 generation and tunable optical properties), the authors anticipated that such films have a great potential to be used in aPDT. The work of Rodgers and collaborators [187] consisted in the immobilization of 5,10,15,20-tetrakis(4-carboxyphenyl)porphyrin 40 on a chitin support (the second most abundant natural polysaccharide, after cellulose, a linear polymer composed of repeating β(1→4)-N-acetylglucosamine units) using ionic liquids (ILs) as solvent. In this study, the Ils were used for chitin extraction and partial deacetylation, as well as a medium for grafting 40 on chitin support. Chitin was first extracted from shrimp shells using the 1-ethyl-3-methylimidazolium acetate ([C 2 mim][OAc]), coagulated in water, and then deacetylated. The deacetylated-chitin (DA-chitin) was dissolved in [C 2 mim][OAc] and the covalent attachment between the amino groups of DA-chitin and the carboxyl groups of 40 was performed in the presence of the activators EDC and N-hydroxy-succinimide (NHS) ( Figure 30). The resulting polymeric composites were cast as a film and coagulated with water to remove the IL and the excess of reagents, resulting in homogeneous 40@DA-chitin films. Further modifications of the optical properties were achieved by the incorporation of metal ions (Cu 2+ , Zn 2+ , Gd 3+ , and Fe 3+ ) into the 40@DA-chitin films. In addition, the 40@DA-chitin films, with and without chelating metal ions, exhibited efficient 1 O 2 production under light irradiation.
Since these films showed interesting optical and photophysical properties (good 1 O 2 generation and tunable optical properties), the authors anticipated that such films have a great potential to be used in aPDT.
Hetteger and co-workers [121] selected a cellulose-based fiber, namely Lyocell, to support porphyrins according to the azide-alkyne "click" concept ( Figure 31). First, azidomodified Lyocell fibers 41 and alkynylated PPIX 42 building blocks were prepared through alkoxysilane chemistry and Steglich esterification (DCC/4-dimethylaminopyridine), respectively. Lyocell fibers were pre-activated by swelling in organic solvents to increase the accessibility of hydroxyl groups in the subsequent silanization process. Then, both building blocks were combined under the "Click Chemistry" approach affording photoactive Lyocell fibers 43 (Figure 31) which after a full characterization, by FTIR, NMR, UV/Vis spectroscopy, and elemental analysis, was biologically screened. The photobactericidal activity of the photoactive Lyocell fibers 43 against S. aureus and B. subtilis was confirmed by the diminishing bacterial growth rate of both Gram-(+) strains. These achievements corroborated the potential envisaged for these fibers as antimicrobial textiles to be applicable at home, hospitals, and health care facilities. Hetteger and co-workers [121] selected a cellulose-based fiber, namely Lyocell, to support porphyrins according to the azide-alkyne "click" concept ( Figure 31). First, azidomodified Lyocell fibers 41 and alkynylated PPIX 42 building blocks were prepared through alkoxysilane chemistry and Steglich esterification (DCC/4-dimethylaminopyridine), respectively. Lyocell fibers were pre-activated by swelling in organic solvents to increase the accessibility of hydroxyl groups in the subsequent silanization process. Then, both building blocks were combined under the "Click Chemistry" approach affording photoactive Lyocell fibers 43 ( Figure 31) which after a full characterization, by FTIR, NMR, UV/Vis spectroscopy, and elemental analysis, was biologically screened. The photobactericidal activity of the photoactive Lyocell fibers 43 against S. aureus and B. subtilis was confirmed by the diminishing bacterial growth rate of both Gram-(+) strains. These achievements corroborated the potential envisaged for these fibers as antimicrobial textiles to be applicable at home, hospitals, and health care facilities.   Hetteger and co-workers [121] selected a cellulose-based fiber, namely Lyocell, to support porphyrins according to the azide-alkyne "click" concept ( Figure 31). First, azidomodified Lyocell fibers 41 and alkynylated PPIX 42 building blocks were prepared through alkoxysilane chemistry and Steglich esterification (DCC/4-dimethylaminopyridine), respectively. Lyocell fibers were pre-activated by swelling in organic solvents to increase the accessibility of hydroxyl groups in the subsequent silanization process. Then, both building blocks were combined under the "Click Chemistry" approach affording photoactive Lyocell fibers 43 ( Figure 31) which after a full characterization, by FTIR, NMR, UV/Vis spectroscopy, and elemental analysis, was biologically screened. The photobactericidal activity of the photoactive Lyocell fibers 43 against S. aureus and B. subtilis was confirmed by the diminishing bacterial growth rate of both Gram-(+) strains. These achievements corroborated the potential envisaged for these fibers as antimicrobial textiles to be applicable at home, hospitals, and health care facilities.  Following the same "Click Chemistry" approach, Zerrouki and co-workers [130] grafted the Zn(II) complex of 5-(4-azidophenyl)-10,15,20-triphenylporphyrin 45a onto Kraft pulp fibers. The Kraft pulp material was modified with propargyl bromide giving propargylated pulp fibers 46 ( Figure 32). The functionalized support 46 was characterized by FTIR to evaluate the presence of C-C triple bond and by XPS to determine the degree of substitution. The 5-(4-azidophenyl)-10,15,20-triphenylporphyrinatozinc(II) 45a was prepared in four sequential steps: (i) condensation of pyrrole with nitrobenzaldehyde and benzaldehyde, giving 5-(4-nitrophenyl)-10,15,20-triphenylporphyrin 44; (ii) reduction of nitro group with Sn(II) chloride in acidic media, affording the 5-(4-aminophenyl)-10,15,20-triphenylporphyrin 21; (iii) diazotization of the aminoporphyrin 21 in the presence of NaN 3 affording the azidoporphyrin 5-(4-azidophenyl)-10,15,20-triphenylporphyrin 45, and, finally, (iv) metalation with Zn(II) acetate in THF. The Zn(II) metalloporphyrin complex 45a was grafted by the azide moiety on the propargylated Kraft pulp fibers 46 using a copper(I)-catalyzed coupling reaction, giving the photoactive Kraft fiber material 47.
The antimicrobial activity of material 47 was tested under visible light irradiation against S. aureus and P. aeruginosa used as Gram-(+) and Gram-(-) bacterial models, respectively. The two bacterial strains deposited on the photosensitizing Kraft pulp material 47 were efficiently killed (no surviving bacteria were detected, against to 4.5 log in the controls) after 24 h exposure to white light (total light dose of 9.5 J cm −2 ).  The antimicrobial activity of material 47 was tested under visible light irradiation against S. aureus and P. aeruginosa used as Gram-(+) and Gram-(−) bacterial models, respectively. The two bacterial strains deposited on the photosensitizing Kraft pulp material 47 were efficiently killed (no surviving bacteria were detected, against to 4.5 log in the controls) after 24 h exposure to white light (total light dose of 9.5 J cm −2 ).
On the other hand, when 635 nm (red light) was chosen to irradiate 3-THPP@EC/Chs (15 min at 5 mW), the microbial survival rates of C. albicans, P. aeruginosa, and S. aureus was lower than in the presence of free 3-THPP.
Although all these porphyrin derivatives were successfully encapsulated, the resu ing acetylated lignin nanoparticles disclosed a limited photodynamic bactericide eff under blue-LED light, 450-460 nm, 15 J cm −2 on S. aureus and E. coli. Despite the significant photodynamic action against Gram-(+) bacteria, the newly prepared material 4-THPP@AcLi has not shown any antimicrobial activity against, Gram-(−) bacteria (E. coli and P. aeruginosa). The authors also proved by TEM, once again, that nanoparticles did not penetrate inside the bacterial cell, suggesting that the inactivation effect was elicited on the outside of bacterial wall.
Although all these porphyrin derivatives were successfully encapsulated, the resulting acetylated lignin nanoparticles disclosed a limited photodynamic bactericide effect under blue-LED light, 450-460 nm, 15 J cm −2 on S. aureus and E. coli.
Having in mind the possibility of using the aPDT approach to prevent food spoilage and deterioration or to be used in a clinical context, Castro and collaborators [61,179] considered and developed photoactive materials using porphyrin derivatives incorporated into chitosan films in view of having a high degree of reusability, without any great loss of photodynamic efficacy.
Aiming to prepare new materials for preventing the development of bacterial biofilm in the food industry, the authors prepared a set of photoactive antimicrobial films obtained by the grafting of 5,10,15,20-tetraarylporphyrins in chitosan with different functionalities, e.g., phenyl units bearing carboxyl groups or pentafluorophenyl units without or with 3-or 4-mercaptobenzoic acid groups, as shown in Figure 34 [61]. The efficiency of these antimicrobial films was assessed on the prevention of Listeria innocua attachment and consequent biofilm formation under different irradiation protocols. L. innocua biofilm growth was nearly completely inhibited in two of the porphyrin-chitosan films, one containing the 5,10,15,20-tetrakis(pentafluorophenyl)porphyrin 48 and the other the thio-carboxylate porphyrin 50 after being exposed to white light (at an irradiance of 10 mW cm −2 ) for 24 h followed by incubation in the dark for 48 h.
tained by the grafting of 5,10,15,20-tetraarylporphyrins in chitosan with different functionalities, e.g., phenyl units bearing carboxyl groups or pentafluorophenyl units without or with 3-or 4-mercaptobenzoic acid groups, as shown in Figure 34 [61]. The efficiency of these antimicrobial films was assessed on the prevention of Listeria innocua attachment and consequent biofilm formation under different irradiation protocols. L. innocua biofilm growth was nearly completely inhibited in two of the porphyrin-chitosan films, one containing the 5,10,15,20-tetrakis(pentafluorophenyl)porphyrin 48 and the other the thio-carboxylate porphyrin 50 after being exposed to white light (at an irradiance of 10 mW cm −2 ) for 24 h followed by incubation in the dark for 48 h. Later on, the same research group functionalized 5,10,15-tris(1-methylpyridinium-4yl)-20-(pentafluorophenyl)porphyrin tri-iodide 51 with 3-or 4-mercaptobenzoic acid, yielding two new tricationic porphyrins, 52 and 53, with suitable carboxylic pending groups to be incorporated on chitosan ( Figure 35).
The cationic porphyrins 51, 52 and 53 were immobilized on chitosan by adding each porphyrin dissolved in THF to a solution of chitosan in an aqueous acetic acid solution.
The new materials 51@chitosan, 52@chitosan, and 53@chitosan were evaluated under white light towards the recombinant bioluminescent E. coli (3.0 µ M under 3.0 mW cm −2 of white light irradiation) The most effective material against E. Coli was 51@chitosan, which showed a bacterial inactivation of 4.1 log reduction in CFU/mL (>99.99% of reduction) after 90 min of irradiation. In comparison, when the bacteria were exposed to 52@chitosan and 53@chitosan, the bacterial reduction was almost negligible (decrease of 0.63 (76%) and 0.31 log (~50%) reduction in CFU/mL, respectively). The authors concluded that these porphyrins, in general, have lost their capacity to produce 1 O2 when entrapped on a chitosan material.

Cellulose Based Photoactive Materials for Application in Cancer Therapy
As mentioned above, in addition to bacterial infections, the photodynamic approach can be applied with success to treat other diseases or to improve health conditions. In fact, photodynamic therapy (PDT) is a clinically approved treatment for oncologic, non-oncologic diseases, and tumor diagnoses [191]. Similarly to aPDT, it is based on the interaction of a photosensitizing dye (PS), light, or dioxygen, and involves the production of cytotoxic The cationic porphyrins 51, 52 and 53 were immobilized on chitosan by adding each porphyrin dissolved in THF to a solution of chitosan in an aqueous acetic acid solution.
The new materials 51@chitosan, 52@chitosan, and 53@chitosan were evaluated under white light towards the recombinant bioluminescent E. coli (3.0 µM under 3.0 mW cm −2 of white light irradiation) The most effective material against E. Coli was 51@chitosan, which showed a bacterial inactivation of 4.1 log reduction in CFU/mL (>99.99% of reduction) after 90 min of irradiation. In comparison, when the bacteria were exposed to 52@chitosan and 53@chitosan, the bacterial reduction was almost negligible (decrease of 0.63 (76%) and 0.31 log (~50%) reduction in CFU/mL, respectively). The authors concluded that these porphyrins, in general, have lost their capacity to produce 1 O 2 when entrapped on a chitosan material.

Cellulose Based Photoactive Materials for Application in Cancer Therapy
As mentioned above, in addition to bacterial infections, the photodynamic approach can be applied with success to treat other diseases or to improve health conditions. In fact, photodynamic therapy (PDT) is a clinically approved treatment for oncologic, nononcologic diseases, and tumor diagnoses [191]. Similarly to aPDT, it is based on the interaction of a photosensitizing dye (PS), light, or dioxygen, and involves the production of cytotoxic ROS, which trigger a cascade of reactions, leading to the destruction of abnormal cells [192]. The main advantages of PDT compared with traditional oncological therapies are due to its spatio-temporal nature, relatively non-invasive nature, lower systemic toxicity, relatively selective destruction of undesired cells, good cosmetic outcome, and its ability to stimulate the immune system, as well as its good tolerability profile [77,193].
However, PDT has also some limitations, e.g., the poor solubility of PS agents in biological media, which led the scientific community to search for better delivery systems. PS for PDT can become more efficacious when adsorbed, entrapped, or linked to celluloselike supports which are characterized by biocompatibility and biodegradability [194]. In addition, these cellulose-based systems provide an increased surface area, a very interesting feature for a platform targeted drug delivery [195].
In parallel, nanocrystalline cellulose material was obtained by the hydrolysis of cellulose (cotton) with sulfuric acid/sodium periodate treatment, to covalently attach the amino groups of 54 to the resulting carbonyl groups under reductive conditions ( Figure 36).
The cytotoxicity potential of the new photoactive materials 55 600-25,000 was evaluated in the dark on a human keratinocyte cell line (HaCat) and compared with Photofrin II ® used as control. The results showed that the photoactive material 55 600 (PEI 600 Da) displayed the lowest dark cytotoxicity, close to that of Photofrin II ® . Photocytotoxicity studies revealed the best IC 50 (7.4 nM) for photoactive material 55 600 towards HaCat cell line when compared with the 23 nM for Photofrin II ® , showing that material 55 600 is a very active PS in a nanomolar concentration range. Further studies demonstrated that the photodynamic action of 55 600 induced apoptosis in a large fraction of treated HaCat. This cell death pathway is considered an advantage because apoptosis allows tumor cell destruction and subsequent elimination by phagocytosis.
Moreover, nanoparticles (NP) have been used as drug carriers, demonstrating an outstanding ability to improve PS drug delivery [196]. The encapsulation in NP of PSs with low solubility in water can enhance the overall delivery to targeted sites, improving biological properties such as tissue distribution and absorption rates. used as control. The results showed that the photoactive material 55600 (PEI 600 Da) displayed the lowest dark cytotoxicity, close to that of Photofrin II ® . Photocytotoxicity studies revealed the best IC50 (7.4 nM) for photoactive material 55600 towards HaCat cell line when compared with the 23 nM for Photofrin II ® , showing that material 55600 is a very active PS in a nanomolar concentration range. Further studies demonstrated that the photodynamic action of 55600 induced apoptosis in a large fraction of treated HaCat. This cell death pathway is considered an advantage because apoptosis allows tumor cell destruction and subsequent elimination by phagocytosis. Figure 36. Synthetic methodology adopted by Sol and co-workers to fabricate new cellulose nanocrystals materials (55600-25,000), bearing purpurin 18 (16), conjugated with polyethyleneimine scaffolds (adapted from Ref. [68]).
Moreover, nanoparticles (NP) have been used as drug carriers, demonstrating an outstanding ability to improve PS drug delivery [196]. The encapsulation in NP of PSs with low solubility in water can enhance the overall delivery to targeted sites, improving biological properties such as tissue distribution and absorption rates.
Under this context, Epple and co-workers [197] prepared a positively charged hybrid NP consisting of a calcium phosphate core and an organic shell. The calcium phosphate hybrid NP was prepared by precipitation from water and then functionalized with a mixture of 5,10,15,20-tetrakis(3-hydroxyphenyl)porphyrin (3-THPP) and the biocompatible anionic polymer carboxymethyl cellulose (CMC). The negative charge of the inner shell Figure 36. Synthetic methodology adopted by Sol and co-workers to fabricate new cellulose nanocrystals materials (55 600-25,000 ), bearing purpurin 18 (16), conjugated with polyethyleneimine scaffolds (adapted from Ref. [68]).
Under this context, Epple and co-workers [197] prepared a positively charged hybrid NP consisting of a calcium phosphate core and an organic shell. The calcium phosphate hybrid NP was prepared by precipitation from water and then functionalized with a mixture of 5,10,15,20-tetrakis(3-hydroxyphenyl)porphyrin (3-THPP) and the biocompatible anionic polymer carboxymethyl cellulose (CMC). The negative charge of the inner shell was then reversed by adding an outer shell of the positively charged polymer, polyethyleneimine (PEI) encapsulating the photoactive dye 3-THPP ( Figure 37). The hybrid NP, carrying the photoactive dye, was dispersed in water and the photodynamic activity against HT29 cells (human colon adenocarcinoma cells), HIG-82 cells (rabbit synoviocytes), and J774A.1 cells (murine macrophages) was accessed. A high photodynamic activity together with a very low dark toxicity was observed for both cell lines HIG-82 and J774A.1 at a concentration of 2.0 µM of 3-THPP. This killing efficiency was equivalent to the non-immobilized 3-THPP. The authors ascribed the high efficacy observed for the new materials to the positive charge of the NP surface (facilitating the transport through the negatively charged cell membrane) and to the high loading of 3-THPP into the NP.
The enhancement of PS solubility and the improvement of photodynamic activity observed using a core-shell hybrid NP formed by a silica core and xylan NP was corroborated by Chaleix and co-workers in 2019 [198]. To afford drug delivery control and to increase the drug bioavailability on blood circulation, 5-(4-hydroxyphenyl)-10,15,20-triphenylporphyrin 56 was functionalized with ethyl 4-bromobutyrate through nucleophilic substitution giving 57. After ester hydrolysis, in a basic medium, the resulting compound 58 was then covalently attached to xylan by esterification using 1 1'-carbonyldiimidazole (CDI) as a coupling reagent to afford the material 59 ( Figure 38). Finally, 59 was used to coat the silica NP (SNP) affording 59@SNP (Figure 38). The obtained nanomaterials were characterized and their therapeutic potential for PDT was evaluated against colorectal cancer cell lines (HCT116 and HT-29 cell lines). In vitro studies showed that 59@SNP was 40-fold and 10-fold more effective against HCT116 cells and HT-29 cells, respectively, compared to free porphyrin 56. The authors stated that, at a cellular level, the conjugation of 56 to SNPs (59@SNP) significantly enhanced its solubility and, consequently, the uptake by cancer cells. was then reversed by adding an outer shell of the positively charged polymer, polyethyleneimine (PEI) encapsulating the photoactive dye 3-THPP ( Figure 37). The hybrid NP, carrying the photoactive dye, was dispersed in water and the photodynamic activity against HT29 cells (human colon adenocarcinoma cells), HIG-82 cells (rabbit synoviocytes), and J774A.1 cells (murine macrophages) was accessed. A high photodynamic activity together with a very low dark toxicity was observed for both cell lines HIG-82 and J774A.1 at a concentration of 2.0 μM of 3-THPP. This killing efficiency was equivalent to the non-immobilized 3-THPP. The authors ascribed the high efficacy observed for the new materials to the positive charge of the NP surface (facilitating the transport through the negatively charged cell membrane) and to the high loading of 3-THPP into the NP. Figure 37. Schematic representation of NP containing calcium phosphate core with shells of carboxymethyl cellulose (CMC, anionic), poly(ethyleneimine) (PEI, cationic) and 5,10,15,20-tetrakis(3-hydroxyphenyl)porphyrin (3-THPP). Reprinted with permission from Ref. [197]. 2009, Springer Nature.
The enhancement of PS solubility and the improvement of photodynamic activity observed using a core-shell hybrid NP formed by a silica core and xylan NP was corroborated by Chaleix and co-workers in 2019 [198]. To afford drug delivery control and to increase the drug bioavailability on blood circulation, 5-(4-hydroxyphenyl)-10,15,20-triphenylporphyrin 56 was functionalized with ethyl 4-bromobutyrate through nucleophilic substitution giving 57. After ester hydrolysis, in a basic medium, the resulting compound 58 was then covalently attached to xylan by esterification using 1′1'-carbonyldiimidazole (CDI) as a coupling reagent to afford the material 59 ( Figure 38). Finally, 59 was used to coat the silica NP (SNP) affording 59@SNP (Figure 38). The obtained nanomaterials were characterized and their therapeutic potential for PDT was evaluated against colorectal cancer cell lines (HCT116 and HT-29 cell lines). In vitro studies showed that 59@SNP was 40-fold and 10-fold more effective against HCT116 cells and HT-29 cells, respectively, compared to free porphyrin 56. The authors stated that, at a cellular level, the conjugation of 56 to SNPs (59@SNP) significantly enhanced its solubility and, consequently, the uptake by cancer cells. from Ref. [198]. 2008, Elsevier. (B) Synthetic route used to immobilize 5-(4-hydroxyphenyl)-10,15,20-triphenylporphyrin 56 on Xylan (adapted from Ref. [198]).

Conclusions
This review intends to cover the literature data regarding the immobilization of porphyrin-like molecules on cellulose-based supports. We discussed the typical methods employed for: cellulose modification, functionalization of porphyrins by inserting groups allowing immobilization, as well as the synthetic routes to prepare the photosensitizer-cellulose functional materials. The new photoactive hybrid materials reported herein demonstrate unique properties, including improved mechanical strength and rheological features. These characteristics are excellent for medical applications, such as wound healing photoactive patches to treat diabetic feet, pressure ulcers, or burn wounds, but also for the Reprinted with permission from Ref. [198]. 2008, Elsevier. (B) Synthetic route used to immobilize 5-(4-hydroxyphenyl)-10,15,20triphenylporphyrin 56 on Xylan (adapted from Ref. [198]).

Conclusions
This review intends to cover the literature data regarding the immobilization of porphyrin-like molecules on cellulose-based supports. We discussed the typical methods employed for: cellulose modification, functionalization of porphyrins by inserting groups allowing immobilization, as well as the synthetic routes to prepare the photosensitizercellulose functional materials. The new photoactive hybrid materials reported herein demonstrate unique properties, including improved mechanical strength and rheological features. These characteristics are excellent for medical applications, such as wound healing photoactive patches to treat diabetic feet, pressure ulcers, or burn wounds, but also for the antimicrobial photoinactivation of multiresistant bacteria in vast clinical contexts (surfaces, gloves, catheters, fabrics). The technological approach discussed herein for photosensitizercellulose functional materials offers the possibility to recover and reuse the photosensitizing system in a sustainable manner.
Concerning the application of photoactive cellulose as material in the field of aPDT, its effectiveness has clearly been proven in several contexts. Nonetheless, there still is room for new improvements, maximizing the full potential for translational research and forefront development.
Infections perpetrated by multiresistant bacteria are a current major concern. Improving the PS properties in terms of amphiphilicity, cell membrane interaction, and internalization are indeed important features to exert an effective therapeutical effect. These issues might be addressed by the development of new PS structures, but also through the development of new formulations and site-directed drug delivery cellulose.
We hope that this review might contribute towards providing new insights regarding PS-graphed cellulose and motivate medical and scientific communities to devote further efforts to this topic.