Magnetic Fluorescent Quantum Dots Nanocomposites in Food Contaminants Analysis: Current Challenges and Opportunities

The presence of food contaminants can cause foodborne illnesses, posing a severe threat to human health. Therefore, a rapid, sensitive, and convenient method for monitoring food contaminants is eagerly needed. The complex matrix interferences of food samples and poor performance of existing sensing probes bring significant challenges to improving detection performances. Nanocomposites with multifunctional features provide a solution to these problems. The combination of the superior characteristics of magnetic nanoparticles (MNPs) and quantum dots (QDs) to fabricate magnetic fluorescent quantum dots (MNPs@QDs) nanocomposites are regarded as an ideal multifunctional probe for food contaminants analysis. The high-efficiency pretreatment and rapid fluorescence detection are concurrently integrated into one sensing platform using MNPs@QDs nanocomposites. In this review, the contemporary synthetic strategies to fabricate MNPs@QDs, including hetero-crystalline growth, template embedding, layer-by-layer assembly, microemulsion technique, and one-pot method, are described in detail, and their advantages and limitations are discussed. The recent advances of MNPs@QDs nanocomposites in detecting metal ions, foodborne pathogens, toxins, pesticides, antibiotics, and illegal additives are comprehensively introduced from the perspectives of modes and detection performances. The review ends with current challenges and opportunities in practical applications and prospects in food contaminants analysis, aiming to promote the enthusiasm for multifunctional sensing platform research.


Introduction
Food is the essential material basis for the survival of human beings, unsafe food seriously damages human health and affects social and economic development. The existence of food contaminants is one of the major factors endangering food safety and human health, and the extension of modern food production and processing industry chain also increases the potential risk of food contamination. Even if trace contaminants enter the food chain, they will also cause severe health risks by the bioaccumulation effect [1][2][3]. Therefore, the analysis methods characterized by simple, low-cost, rapid, and sensitive for food contaminants detection are urgently demanded.
One of the primary goals of modern analytical techniques is to develop sensitive, accurate, reliable, and high-throughput food safety detection and quality assurance methods to identify, monitor, and quantify newly discovered food components and contaminants [3,4]. At present, multiple mature instrument analytical techniques have been employed to detect various food contaminants [5][6][7]. However, the requirements of sophisticated devices, complex pretreatment processes, and professional operators make them unsuitable for rapid

Preparation of MNPs@QDs
Currently, the preparation methods of MNPs@QDs have been reported in numerous pieces of the literature [34,38]. The key point to consider in the reasonable integration of MNPs and QDs into multifunctional MNPs@QDs nanocomposites is whether the two components are firmly combined and interact without causing a loss of magnetic and fluorescent performance. Furthermore, its properties such as dispersibility, stability, biocompatibility, and desirable surface functionalization are also related to its practical applications. Although the compositions and morphologies of these nanocomposites perform differently, most strategies can be divided into five categories: hetero-crystalline growth, template embedding, LBL assembly, microemulsion technique, and the one-pot method.

Preparation of MNPs@QDs
Currently, the preparation methods of MNPs@QDs have been reported in numerous pieces of the literature [34,38]. The key point to consider in the reasonable integration of MNPs and QDs into multifunctional MNPs@QDs nanocomposites is whether the two components are firmly combined and interact without causing a loss of magnetic and fluorescent performance. Furthermore, its properties such as dispersibility, stability, biocompatibility, and desirable surface functionalization are also related to its practical applications. Although the compositions and morphologies of these nanocomposites perform differently, most strategies can be divided into five categories: hetero-crystalline growth, template embedding, LBL assembly, microemulsion technique, and the one-pot method.
Subsequently, S and Cd were successively deposited on the surface of Fe@Pt to form metastable core-shell nanostructures at 100 • C. With the increase of solution temperature to 280 • C, the amorphous CdS on the sphere's surface was transformed into a crystal and formed heterodimers FePt@CdS nanoparticles with an appropriate size of 7 nm and a QY of 3.2% (Figure 3a) The core-shell or heterodimer MNPs@QDs all strongly depend on the lattice mismatch between the MNPs and QDs components, and synthesis conditions such as the reaction temperature, surface capping agents and the addition order of the precursors [44,45]. lattice mismatching and high-temperature decomposition [45]. In the presence of oleylamine and oleic acid, Fe@Pt was firstly formed at high-temperature decomposition. Subsequently, S and Cd were successively deposited on the surface of Fe@Pt to form metastable core-shell nanostructures at 100 °C. With the increase of solution temperature to 280 °C, the amorphous CdS on the sphere's surface was transformed into a crystal and formed heterodimers FePt@CdS nanoparticles with an appropriate size of 7 nm and a QY of 3.2% (Figure 3a) The core-shell or heterodimer MNPs@QDs all strongly depend on the lattice mismatch between the MNPs and QDs components, and synthesis conditions such as the reaction temperature, surface capping agents and the addition order of the precursors [44,45]. Although the hetero-crystalline growth method was first reported for preparing MNP@QDs, the main problems of the method are the inability to optimize the properties of the nanocomposites, undesirable magnetic responsiveness, low QY, and lack of functional groups, which make it challenging to satisfy the diversified requirements of food contaminants analysis. The initial nanocrystals can be prepared under optimal conditions; however, in the preparation of subsequent components, the initial crystals may be subject Although the hetero-crystalline growth method was first reported for preparing MNP@QDs, the main problems of the method are the inability to optimize the properties of the nanocomposites, undesirable magnetic responsiveness, low QY, and lack of functional groups, which make it challenging to satisfy the diversified requirements of food contaminants analysis. The initial nanocrystals can be prepared under optimal conditions; however, in the preparation of subsequent components, the initial crystals may be subject to a series of temperature variations that affect their structure. Moreover, the undesirable interfacial interaction between MNPs and QDs may cause the loss of the dual performances of MNPs@QDs. The inner filter effect (IFE) (non-radioactive quenching) induced by MNPs and the poor crystal quality of QDs lead to the QY of MNPs@QDs usually less than 10%. For example, after passivating the surface layer of Fe 3 O 4 @CdSe by ZnS, the QY was increased from 2-3% to 10-15% [50]. This value was still much lower than that of standard CdSe/ZnS QDs alone [51]. The magnetism of MNPs is relatively easy to maintain, but interfacial doping or instability between two lattices may result in disorder in MNPs structure [52]; it is still a troublesome problem in the currently reported research by hetero-crystalline growth method.
Silica (SiO 2 ) has the advantages of good biological inertia and biocompatibility, facile synthesis, and operable surface functionalization, which offer a favorable carrier for loading MNPs and QDs to form MNPs@QDs nanocomposites. Dong et al. encapsulated both Fe 2 O 3 and CdSe QDs within a silica shell to form SiO 2 /MNPs-QDs. The QY decreased appropriately 4-and 10-fold lower than bare CdSe QDs (QY = 11.4%) at the coating reacting at 8 and 48 h, respectively [59]. The quenching effect of MNPs and multiple chemical reactions still inevitably affects the dual performance of nanocomposites, and seeking better spatial separation is significant for its further application. The silica layer wraps on the surface of the MNPs as a classical strategy to construct an efficient barrier to prevent fluorescence quenching by adjusting the thickness of the silica shell. Easy manipulation of surface functionalization provides plenty of binding sites for QDs and recognition elements conjugation. Furthermore, the silica coating helps to reduce the toxicity of bare MNPs, and improve their stability and dispersity, which is conducive to subsequent biological applications [61,[68][69][70]. Meanwhile, the hollow and mesoporous silica templates can effectively reduce the density of the silica, enhance the transmissivity of irradiation light, and avoid the side effects of absorption and scattering [56,57,62,71]. The general strategy of template embedment is illustrated in Figure 3b.
Template-based embedding techniques utilize biocompatible materials to adjust the performance of the obtained nanocomposites, intending to improve their stability and dispersibility, modify functional groups, and reduce toxicity. The carrier of a huge interior cavity provides opportunities for high payloads of dual components and easy manipulation of desirable properties by changing the proportion of different types of components. High loading with MNPs could enhance magnetic responsiveness intensity and separation speed under an external magnetic field, thereby minimizing the separation time in complicated food matrices. Moreover, the different emission QDs could be embedded into SiO 2 , enabling optical encoding of multiple food contaminants. The template embedding method to fabricate MNPs@QDs nanocomposites provides an ideal strategy for designing matrix tolerance and high-performance sensing probes.

Layer-by-Layer Assembly
LBL assembly integrates performed MNPs and QDs through non-covalent forces and chemical covalent bonds to form MNPs@QDs with a multi-layer self-assembled core-shell structure. The non-covalent interactions mainly involve electrostatic adsorption [79][80][81], hydrophobic [82], coordination [83], and biomolecule-assisted system [84,85]. The polyelectrolyte cationic polymers-mediated electrostatic adsorption is commonly used for preparing core-shell MNPs@QDs, such as the poly (allylamine hydrochloride) [79], poly (dimethyl diallyl ammonium chloride) [86], and polyethyleneimine (PEI) [80]. The negatively charged QDs were wrapped on the surface of positively charged PEI capped MNPs, while the luminescent intensity could be tuned by controlling the number of PEI layers to absorb different amounts of QDs [80,87,88] (Figure 3c). The amphiphilic poly(4-vinylpyrollidone) capped Fe 3 O 4 nanoparticles can bind 1-dodecanethiol modified QDs via hydrophobichydrophobic interactions to form MNPs@QDs [82]. Alternatively, barnase-capped MNPs were tightly conjugated with barstar-capped QDs to form dual-functional MNPs@QDs via this protein-assisted noncovalent binding system [84], and the biotin-functionalized Fe 3 O 4 conjugated with streptavidin-functionalized CdSe/ZnS QDs via the high-affinity streptavidin-biotin system [85]. The non-covalent interactions do not depend on complicated chemical reagents and synthesis, which provides a simple way to construct dualfunctional MNPs@QDs nanocomposites. It is worth noting that the QDs may leak or drop from the linker-connected MNPs under certain conditions, which may affect the stability of the storage, coupling, and practical applications. Moreover, the emission intensity is inevitably affected by MNPs to reduce the PL QY, which may be attributed to non-radiative energy or charge transfer processes during the assembly.
Another approach for LBL assembly is based on covalent binding between MNPs and QDs. The strategy utilizes reactive functional groups such as carboxyl (-COOH), amino (-NH 2 ), thiol, and siloxane groups to realize the connection of two components [89][90][91][92][93] (Figure 3c(ii)). NH 2 -Fe 3 O 4 @SiO 2 is the most commonly used for coupling with COOH-QDs via the carbodiimide chemistry method [94,95]. Fe 3 O 4 is easily modified with amino groups by the silanization treatment, and SiO 2 wrapped on the surface of Fe 3 O 4 minimized the quenching effect and provided functional groups for enabling chemical bonding with QDs while solving the problems of easy aggregation and increasing their stability. The l-cysteinemodified ZnS QDs with rich amino are also applied for coupling with COOH-functionalized Fe 3 O 4 to form MNPs@QDs, but the coupling efficiency may be reduced when recognition elements were used directly conjugating with the outer layer of amino-QDs [90]. The thiol modified Fe 3 O 4 @SiO 2 was used for binding QDs seeds on the surface. The carboxylic groups of the thiol ligands improved the water dispersity and surface functionality for further conjugation of bioactive molecules [96]. The 3-mercaptopropyltrimethoxysilane (APTES) capped ZnS QDs have trimethoxysilane groups, which can be easily connected via Si-O-Si bonds to create a SiO 2 network and conglutinated together with Fe 3 O 4 @SiO 2 in a nanosphere [92]. The covalent interaction provides a solid combination compared with non-covalent interactions. This approach increases the stability of nanocomposites and reduces the possibility of QDs leaking from the surface of the MNPs. The abundant functional groups of the dual components build a robust bridge for the construction of MNPs@QDs nanocomposites, and these active functional groups also provide diverse sites for the conjugation of specific recognition elements for convenient detection of multiple food contaminants. The LBL strategy to prepare MNPs@QDs nanocomposites has become popular due to its high simplicity, operability, and adaptability, satisfying the requirements of constructing rapid, sensitive multifunctional sensors for food contaminants analysis.

Microemulsion Technique
The microemulsion technique is a transparent or translucent, isotropic, thermodynamically stable system formed by water, organic solvents, MNPs, QDs, and surfactants in appropriate proportions. Chen et al. mixed hydrophobic QDs and MNPs with dodecyltrimethylammonium bromide (DTAB) to form an aqueous solution, and the mixture was then quickly poured into a poly(vinylpyrrolidone) (PVP) ethylene glycol (EG) solution. The obtained nanoparticles were 120 nm with a close-packed structure, MNPs preferentially became a magnetic core, QDs formed a fluorescent shell, and dipole-dipole interactions of MNPs and oleophobic interactions generated between MNPs and QDs promoted the structure formation [97]. A sol-gel process was introduced to encapsulate a thin silica shell on the surface of MNPs@QDs for improving biocompatibility and colloidal stability, and the obtained nanocomposites were successfully applied as a live cell tracer and dual-modal imaging probe [98].
Polymer beads for incorporating MNPs and QDs also attract considerable attention due to their simplicity and diversity. Guo et al. used trichloromethane containing octadecylamine-coated QDs (OC-QDs), oleic acid-modified MNPs (OA-MNPs), poly (methyl methacrylate) (PMMA), and poly (maleic anhydride-alt-1-octadecene) (PMAO) composites to form MNPs@QDs through an ultrasonic emulsification solvent evaporation process [99]. The fluorescence intensity was 226 times that of corresponding QDs, and saturation magnetization still retained 45.4% of the compared MNPs. The ultrasonic emulsification introduced herein could conveniently control the size of nanocomposites, rendering them more suitable for point of care testing applications. The amphiphilic (2-hydroxyl-3dodecanoxyl) propylcarboxymethyl chitosan [100], PLGA [101], poly (styrene-co-maleic anhydride) [102] also act as carriers, in which MNPs and QDs dissolved in the organic phase are transferred into the aqueous phase through hydrophobic interaction. The general strategy of template embedment is depicted in Figure 3d. The reaction process involves using more organic solvents or surfactants, and incomplete evaporation and washing to remove these reagents may damage the dual properties of MNPs@QDs. Moreover, the materials yield via this method is low, which is not conducive to its wide applications in food contaminants' rapid detection.
The microfluidic devices are also employed to simplify the process of producing standardized MNPs@QDs with uniform size and a controllable number of QDs within each particle. As depicted by Lan et al., the Fe 3 O 4 and CdSe/ZnS QDs were respectively dispersed in the alginate solution within the corresponding inlet, and then co-flow was formed in the flow-focusing-channel [103]. Under the flow-focusing orifice, the Ca 2+ in the oil phase was mixed with droplets, and many Janus droplets were produced by symmetric shearing, and droplets were solidified in the extension serpentine channel and collected at the outlet. The sodium alginate used herein provided an excellent carrier for cross-linked with Ca 2+ to form a gel structure, and the COOH of the surface could be used for further biofunctionalization. Interestingly, Fe 3 O 4 and QDs stayed in their respective hemispheres within a fairly symmetrical structure, which minimized the fluorescence quenching effect of MNPs and prevented the leakage of QDs. The microfluidic technology as a simple, convenient, and straightforward approach for producing MNPs@QDs with fantastic fluorescence and magnetism is of great potential, the dual properties of nanocomposites could be easily manipulated by adjusting the flow rate of liquid. The microfluidic-based microemulsion technique points the way for the production of standardized MNPs@QDs.

One-Pot Method
The one-pot method is to mix the precursors of MNPs and QDs in a vessel to complete the fabrication of MNPs@QDs in a single step. The hydrothermal method is a bottomup strategy under high temperature and pressure and is frequently used for preparing MNPs@QDs nanocomposites in one step; their scheme illustration is presented in Figure 3e. In one study, Zhou et al. utilized graphite oxide (GO), cadmium chloride, ferric dichloride tetrahydrate, and sodium acetate as precursors and dispersed them in a DMSO solution to form a stable suspension. The mixture was then transferred into a Teflon-lined autoclave for a high-temperature reaction (180 • C for 12 h) to obtain nanocomposites [104]. The individual components were well distributed with no mutual interference. The high specific surface area and abundant negative charge of GO provided more nucleation sites for loading MNPs and QDs. The assembled nanocomposites exhibited favorable magnetism intensity (44.85 emu/g) and high loading efficiency (0.98 mg/mg) for doxorubicin.
In addition to QDs, carbon quantum dots (CQDs) were also employed to fabricate MNPs@QDs nanocomposites. There are two apparent merits of CQDs to prepare nanocomposites: (i) the inherent advantages of CQDs, such as low cost, low toxicity, high surface area, abundant surface groups, favorable optical properties; (ii) the electrostatic repulsion generated by CQDs, which provides excellent colloidal stability for Fe 3 O 4 . Maleki et al. added FeCl 3 ·6H 2 O, ethylenediamine, and citric acid into deionized water and poured it into a Teflon-lined autoclave for heating at 200 • C for 5 h, the MNPs@QDs was synthesized, and its magnetism intensity reached 62.0 emu/g [105]. The CQDs derived from a onefold carbon source suffer a low QY, and heteroatom doping plays a crucial role in regulating the fluorescent intensity of CQD. Nitrogen-doping (N-doping) is a common method to improve QY. In the Liu et al. research, Poly-γ-glutamic acid (γ-PGA) was utilized as both a carbon and nitrogen source at the same time, and the precursors experienced heating and stirring, pH control, aging, and high-temperature forming Fe 3 O 4 @CQDs [106]. The QY and magnetism intensity of resulting nanocomposites were 21.6% and 62 emu/g, respectively. The superior characteristics of high QY, good dispersity, excellent colloidal stability, tunable fluorescence, high QY, and strong magnetism make them an advanced probe for triple-modal tumor imaging. In another study, ferric ammonium citrate acted as an iron precursor and carbon source, and triethylenetetramine (TETA) acted as nitrogen source and reducing agent, followed by high-temperature treatment to obtain Fe 3 O 4 @CQDs in one convenient step [107]. TETA effectively improved the adhesion of CQDs and Fe 3 O 4 and gained better crystallinity. The QY of Fe 3 O 4 @CQDs drastically decreased to 4.6% compared with TETA-CQDs (53%). The static and dynamic fluorescence quenching of CQDs and IFE generated by MNPs conspire to cause this phenomenon. Although the one-pot method provides a rapid, simple, and economic strategy for fabricating bifunctional nanocomposites, the selection of suitable precursors is directly related to the magnetic and fluorescent properties of MNPs@QDs nanocomposites. Impurities are inevitably generated during the reaction period, which affects the separation and purification of products, and cannot achieve precise control of fluorescence and magnetic properties.
Doping transition metal ions or lanthanides into a crystalline lattice of QDs is another strategy for the one-pot preparation of MNPs@QDs. The transition metal ions and lanthanides such as Mn 2+ [108,109], Eu 3+ [110], Gd 3+ [111,112], and Ln 3+ [113] are used for preparing doped MNPs@QDs. The doped materials are mainly concentrated in biomedical applications and are seldom involved in the rapid detection of food safety. The magnetic intensity of doped materials may be insufficient for the separation and enrichment of complex sample matrix.

Applications to Food Contaminants Analysis
Currently, MNPs-based rapid sample separation and QDs-based fluorescent labeling are extensively used in food contaminant analysis [114]. The MNPs@QDs simultaneously integrate the functions of separation and labeling, which can quickly enrich and separate the targets from the complicated food matrices under the action of the external magnetic field and realize the "fluorescence switch" quantitative analysis of the target analytes at the same time, simplifying the sample pretreatment, reducing the loss of the analyte, dramatically shortening the detection time, and improving the detection efficiency. The bifunctional MNPs@QDs with excellent performances have been successfully applied to detect food contaminants, including metal ions, foodborne pathogens, toxins, pesticides, antibiotics, and illegal additives. In this section, we summarize in detail the application of MNPs@QDs-based sensors for the detection of food contaminants in food samples.

Metal Ions
Presently, toxic metal ions (Cu 2+ , Hg 2+ , Pb 2+ ) have attracted attention due to their significant side effect. These metal ions are an essential risk factor causing water and environmental pollution. Even if trace levels of metal ions enter humans through the food chain, the health harm to human reproduction, nerve, and cardiovascular systems will produce [115]. Therefore, a rapid, sensitive, efficient, and low-cost method for detecting metal ions is significant to ensure food safety.
The specific surface and structural properties of chitosan (CS) provide excellent chelating ability for metal ions [116][117][118][119][120]. Li et al. designed an adsorbent-chemosensor based on Fe 3 O 4 @CS@CQDs for selective detection of Hg 2+ in water [121]. The introduction of CS/CQDs significantly increased the absorption capacity with a maximum monolayer adsorption capacity of 110. 62 mg/g, while the surface defect of QDs promoted the migration and coupling with Hg 2+ , resulting in fluorescence quenching, achieving a linear range of 0-4 mM with a limit of detection (LOD) of 12.43 nM. The carboxymethyl chitosan (CMCS) microspheres were used for encapsulating MNPs and QDs to fabricate bifunctional MNPs@QDs. The abundant active functional groups of CMCS and electrostatic interaction promoted the binding of Hg 2+ [122]. The proposed sensor achieved a linear range of 0.3-5 µM with a LOD of 0.091 µM (Figure 4a). The abundant amino, carboxyl, and thiol groups of glutathione (GSH) provided a favorable carrier for highly efficient absorption [123], a GSH modified MNPs@QDs nanosensor for simultaneous detection and removal of Cu 2+ was well developed [124]. The method features a linear relationship varying from 5 to 30 µM with a LOD of 0.2 µM. In another study, the di-2-picolylamine/proline co-modified Fe 3 O 4 @ZnS nanocomposites were used for the removal and detection of Cu 2+ [125]. The maximum adsorption capacity of the nanocomposites reached 517.9 mg/g, and the nanocomposites could quantificationally detect Cu 2+ in the range of 6-20 µM. The biocompatible calcium carbonate (CaCO 3 ) crystals also acted as a carrier for encapsulating AgInS 2 /ZnS ternary QDs and Fe 3 O 4 to prepare CaCO 3 -Fe 3 O 4 @AgInS 2 /ZnS fluorescent sensor for simultaneous detection of three metal ions [126]. The positively charged Co 2+ , Ni 2+ , and Pb 2+ interacted with negatively charged AgInS 2 /ZnS QDs to produce a fluorescence quenching, and LODs were 10 nM for Co 2+ , and 100 nM for both Ni 2+ and Pb 2+ . Although good sensitivity is provided by proposed sensors, the deficiency of selectivity reduces its practicality.
Directly using MNPs@QDs nanocomposites without the assistance of a linker is an attractive option to simplify procedures further and improve the adaptability of MNPs@QDs for metal ion detection. Xie and Co-workers utilized the one-pot method to prepare Fe 3 O 4 @CQDs and simultaneously detect and remove Hg 2+ in contaminated water samples [127]. The Fe 3 O 4 @CQDs exhibited a strong blue fluorescent emission at the band of 435 nm; the QY was calculated to be 58%. The abundant active functional groups of CQDs promoted the interactions with Hg 2+ and accelerated non-radiative recombination by an effective electron transfer process. The method manifested a linear response in the range of 0.003-0.01 µM with a LOD of 0.3 nM (Figure 4b), and their practicality was verified in spiked lake water, tap water, and drinks with average recoveries of 96.5-108.8% with an RSD lower than 6.0%. Dong et al. conjugated CQDs with Fe 3 O 4 @SiO 2 -NH 2 nanocomposites via amine-carbonyl reactions and designed a fluorescent sensor for Cu 2+ detection [89]. The LOD of Cu 2+ was calculated to be 0.16 µM with a linear range of 0-80 µM. The graphene quantum dots (GQDs) with large surface areas, abundant active groups, and π-π conjugated networks have a better affinity toward metal ions [128]. Alvand and Shemirani fabricated Fe 3 O 4 @SiO 2 @GQDs nanocomposites and utilized them for dual functional detection and the removal of Hg 2+ in water samples [129]. The nanocomposites exhibited a fast intake of Hg 2+ within 1.5 min, and the maximum adsorption capacity was 68.03 mg/g. The linear range of the sensor covered 0.1-70 µM, with a LOD of 30 nM. Wang et al. encapsulated the CdTe QDs and Rhodamine 6G (Rh6G) into mesoporous SiO 2 to fabricate multifunctional inorganic-organic nanocomposites for simultaneous removal and detection of Hg 2+ [130]. The maximal adsorption capacity of nanocomposites reached 17.7 mg/g and could be reused 8-time recycling. The proposed sensor for the ratiometric analysis of Hg 2+ ranged from 7-900 nM with a LOD of 2.5 nM and had satisfactory recoveries of 97.6-102.3% in deionized water and tap water. The elements doped MNPs@QDs were also used for metal ions sensing [131,132]. The one-step hydrothermal method for preparing Mn-doped CQDs was simultaneously applied as a biosensing probe for Fe 3+ and magnetic resonance imaging [133]. The Mn-CQDs presented a bright, strong yellow-green fluorescence at the emission band of 464 nm, and QY was 13%. The oxygen-containing functional groups on the surface of MnCQDs promoted the coordination with Fe 3+ and resulted in a fluorescence quenching. The fluorescence intensity was inversely proportional to the concentration of Fe 3+ , with a linear range of 0-1.2 µM and LOD of 0.22 µM. Wu et al. synthesized tetragonal chalcopyrite crystalline structured ternary CuFeS 2 QDs for simultaneous sensing Cu 2+ and Fe 3+ [134]. Both Cu 2+ and Fe 3+ coordinated with CuFeS 2 QDs to produce an aggregation effect and cause obvious fluorescence quenching. The method showed LODs for Cu 2+ and Fe 3+ lower to 1.98 and 2.15 µM, respectively. tional detection and the removal of Hg 2+ in water samples [129]. The nanocomposites exhibited a fast intake of Hg 2+ within 1.5 min, and the maximum adsorption capacity was 68.03 mg/g. The linear range of the sensor covered 0.1-70 μM, with a LOD of 30 nM. Wang et al. encapsulated the CdTe QDs and Rhodamine 6G (Rh6G) into mesoporous SiO2 to fabricate multifunctional inorganic-organic nanocomposites for simultaneous removal and detection of Hg 2+ [130]. The maximal adsorption capacity of nanocomposites reached 17.7 mg/g and could be reused 8-time recycling. The proposed sensor for the ratiometric analysis of Hg 2+ ranged from 7-900 nM with a LOD of 2.5 nM and had satisfactory recoveries of 97.6-102.3% in deionized water and tap water. The elements doped MNPs@QDs were also used for metal ions sensing [131,132]. The one-step hydrothermal method for preparing Mn-doped CQDs was simultaneously applied as a biosensing probe for Fe 3+ and magnetic resonance imaging [133]. The Mn-CQDs presented a bright, strong yellowgreen fluorescence at the emission band of 464 nm, and QY was 13%. The oxygen-containing functional groups on the surface of MnCQDs promoted the coordination with Fe 3+ and resulted in a fluorescence quenching. The fluorescence intensity was inversely proportional to the concentration of Fe 3+ , with a linear range of 0-1.2 μM and LOD of 0.22 μM. Wu et al. synthesized tetragonal chalcopyrite crystalline structured ternary CuFeS2 QDs for simultaneous sensing Cu 2+ and Fe 3+ [134]. Both Cu 2+ and Fe 3+ coordinated with CuFeS2 QDs to produce an aggregation effect and cause obvious fluorescence quenching. The method showed LODs for Cu 2+ and Fe 3+ lower to 1.98 and 2.15 μM, respectively.  The applications of MNPs@QDs-based sensors for detecting metal ions are depicted in Table 1. Sensors for metal ion detection based on MNPs@QDs nanocomposites are rapidly developing and have great potential for metal ion adsorption, detection, and removal, which will provide a simple, rapid, accurate, and reliable tool for tracing metal ions in food safety monitoring.

Foodborne Pathogens
Foodborne pathogens, including Escherichia coli O157:H7 (E. coli O157:H7), Salmonellas, Pseudomonas aeruginosa, etc., are among the leading causes of common foodborne disease outbreaks worldwide [135]. The human consumption of food contaminated with pathogens could result in severe vomiting and diarrhea [136]. Therefore, on-site detection of foodborne pathogens is of greatly signifcant for ensuring food hygiene and promoting public health [137].
Lateral flow immunoassay (LFIA), characterized by the merits of rapid, low-cost, and on-site detection, has been widely used for many samples screening [138]. Huang et al. constructed a sandwich LFIA immunosensor to detect E. coli O157:H7 using a bifunctional MNPs@QDs probe [139]. The monoclonal antibody (mAb) was conjugated with MNPs@QDs to form a detection immunoprobe. The rabbit polyclonal antibody (pAb) was immobilized on the test (T) line to capture free E. coli O157:H7, and the high specific antibody guaranteed the selectivity of the method. The fluorescence intensity was positively correlated with the number of E. coli O157:H7 linear range from 2.5 × 10 2 CFU/mL to 5 × 10 5 CFU/mL, and LOD was 2.39 × 10 2 CFU/mL. The high sensitivity benefit from 6.57-10 times magnetic enrichment and the removal of matrix interference of milk, while the omitted elution and incubation process avoid the loss of target and improve detection efficiency. The separation and enrichment, tripe mode signal output, and two formats of quantitation were integrated into one multimodal assay platform to detect Salmonella typhimurium (S. typhi) [140]. Figure 5a depicts the test principles of the bifunctional nanocompositesbased triple mode sensing platform. The visual LODs (vLODs) of the color and fluorescence signal were 1.88 × 10 4 CFU/mL and 3.75 × 10 3 CFU/mL, respectively. A good linear relationship was achieved in the range of 1.88 × 10 4 -1.88 × 10 7 CFU/mL with a LOD of 3.5 × 10 3 CFU/mL for both fluorescence and magnetic signal. The 2-4 orders of magnitude improvement were observed with gold nanoparticles (AuNPs)-LFIA. Ghasemi et al. conjugated NH 2 -Fe 3 O 4 @SiO 2 with COOH-QDs to form core-shell MNPs@QDs, and high specific mAb was immobilized on the surface of nanocomposites for pre-enrichment of Streptococcus agalactiae (S. agalactiae) from milk [141]. The immune-MNPs@QDs captured with S. agalactiae to form a large-grained immunocomplex and could not pass the 60 nm size pore of filters, and fluorescence intensity was directly proportional to the number of S. agalactiae. The LODs for S. agalactiae detection in PBS and milk were 10 and 100 CFU/mL, respectively. The difference could be attributed to fat, protein, and minerals in milk reduced the capture efficiency.
Aptamers are short-chain oligonucleotides (DNA or RNA) that can recognize and bind targets with excellent affinity with the characteristics of chemical stability, low immunogenicity, and automated synthesis. The aptamer-based sensors have been extensively used for monitoring food safety [142,143]. The aptamer was combined with MNPs@QDs to construct a fluorescent sensor for highly sensitive detection of S. typhi in vegetable samples [144]. The aptamers-modified MNPs@QDs produced an aggregation effect upon the capture of S. typhi cells resulting in fluorescence quenching and were separated and redispersed for fluorescence detection. The LODs of the sensor in the fresh-cut vegetable washing solution and lettuce sample were 1 × 10 2 and 1.38 × 10 2 CFU/mL, respectively, and satisfactory recoveries in these two types of samples were achieved between 94.0% and 107.5%. Lin et al. used APTES, γ-Fe 2 O 3 , and QDs as functional components to assemble MNPs@QDs, and by adjusting the number of MNPs to obtain two MNPs@QDs with various magnetic responsiveness [145]. These two MNPs@QDs respectively conjugated E. coli O157:H7 and S. typhi aptamer with the assistance of the streptavidin-biotin system. The two MNPs@QDs immunocomplexes present differentiated magnetic responsiveness under the same external magnetic field, and the immunocomplexes were respectively separated at different immunoreaction times for fluorescence quantitative analysis. The E. coli O157:H7 detection had a linear range of 40-10 8 CFU/mL with a LOD of 16 CFU/mL, and the S. typhi had a linear range of 63-10 8 CFU/mL with a LOD of 25 CFU/mL. The mean recoveries of E. coli O157:H7 and S. typhi in milk samples were 87.6-97.7% and 84.9-95.9%, respectively, and the RSD of both pathogens were in the range of 1.1-5.9%. The high recoveries of this method could be attributed to the following three points: (i) high affinity and specificity of aptamer-modified nanoprobes for the capture of pathogens; (ii) high luminescent intensity improved the detection sensitivity; (iii) variable magnetic response of nanoprobes effectively separated each pathogen at different time points. The high sensitivity and wide quantitative range achieved in this study could satisfy the requirements of different levels of the same pathogens in various regions.
Several works constructed fluorescent nanoswitch control for pathogens detection based on MNPs@QDs nanocomposites. Ahmadian-Fard-Fini et al. used grapefruit, lemon, and turmeric extracts to prepare the blue emissive CQDs with QY of 20%, and they were also utilized as capping agents to prepare Fe 3 O 4 @CQDs nanocomposite [146]. The fluorescence of Fe 3 O 4 @CQDs presents inversely proportional to the number of E. coli in the range of 0-10 9 CFU/mL. A "turn-off" fluorescence response strategy herein was introduced for pathogens detection. A similar approach was also employed for Pseudomonas aeruginosa detection by using Mg 2+ [132] and Ni 2+ [131] doped MNPs@CQDs. Wang et al. used thiolated MNPs@SiO 2 linked with thioglycolic acid-modified CdTe/CdS QDs to form bifunctional nanocomposites and introduced a "turn-on" strategy for Alicyclobacillus spp. detection [147]. In this study, both synergistic effect and electrostatic interaction promoted the fluorescence enhancement during the process of immuno-MNPs@QDs capture Alicyclobacillus spp. The minimum LOD was 10 4 CFU/mL, and the whole testing process was completed within 90 min. Cui et al. utilized a "turn-off-on" strategy for the detection of S. typhi based on the fluorescence resonance energy transfer (FRET) effect between QDs and AuNPs [148]. The absorption spectrum of AuNPs overlapped with the emission spectrum of QDs, and the distance between AuNPs and QDs was reduced to less than 10 nm; satisfaction with these two factors triggered FRET to quench the fluorescence of QDs. The addition of bacterial cells increased the distance and diminished the FRET effect, the LOD was lower to 1.7× 10 2 CFU/mL, and the assay could be completed within 2 h (Figure 5b).
The performances of the MNPs@QDs-based sensors for foodborne pathogens detection are summarized in Table 2. The LFIA and homogenous fluorescent methods are the most widely used detection forms for foodborne pathogens determination. Combining highaffinity recognition elements with MNPs@QDs makes them a powerful pretreatment tool for capturing target pathogens, while high-performance detection probes are used for constructing a fluorescent nanoswitch for sensing foodborne pathogens. The pretreatment and detection were simultaneously integrated into one sensing platform, which will bring significant improvement in foodborne pathogens detection.

Toxins
Mycotoxins are metabolites produced by fungi such as molds and usually exist in moldy food and feed. Even trace levels of mycotoxins intake by human beings can also cause diseases with kidney disease, liver disease, and cancer, posing a serious health threat to people and animals [149]. Therefore, a rapid, simple, and highly sensitive on-site detection method prioritizes ensuring human health and preventing contamination from related products. Among them, aflatoxin is a naturally occurring, highly-toxic carcinogen classified by the World Health Organization, which mainly exists in grain, oil, and their related products [150]. Guo et al. utilized the microemulsion technique to prepare coreshell bifunctional MNPs@QDs with favorable fluorescence and magnetism [99]. The surface of OA-modified QDs contained an abundant COOH group for coupling with high-affinity aflatoxin B 1 mAb through carbodiimide chemistry. It is noteworthy that the fluorescence intensities were not wholly recovered even after 1000-fold sample dilution in direct detection mode. In enrichment detection mode, the antibody-labeled MNPs@QDs were used for enriching AFB 1 molecules and removing pigments in dark soy sauce under an external magnet; just a 6-fold dilution was enough to eliminate the matrix interference with the 167-fold improvement compared with direct detection mode, which indirectly improved the sensitivity of the method. Under optimal conditions, the proposed method achieved a linear range from 0 to 150 pg/mL (R 2 = 0.9931), with a IC 50 of 27 ± 3 pg/mL. The LODs were 3 and 51 pg/mL in soy sauce extract and real dark sauce, respectively. The mean recoveries of AFB 1 in black soy sauce were all higher than 89%, with a CV lower than 12%. The MNPs@QDs-based LFIA realized sample-to-answer within 45 min, and their test process is shown in Figure 6a. tional nanocomposites and introduced a "turn-on" strategy for Alicyclobacillus spp. detection [147]. In this study, both synergistic effect and electrostatic interaction promoted the fluorescence enhancement during the process of immuno-MNPs@QDs capture Alicyclobacillus spp. The minimum LOD was 10 4 CFU/mL, and the whole testing process was completed within 90 min. Cui et al. utilized a "turn-off-on" strategy for the detection of S. typhi based on the fluorescence resonance energy transfer (FRET) effect between QDs and AuNPs [148]. The absorption spectrum of AuNPs overlapped with the emission spectrum of QDs, and the distance between AuNPs and QDs was reduced to less than 10 nm; satisfaction with these two factors triggered FRET to quench the fluorescence of QDs. The addition of bacterial cells increased the distance and diminished the FRET effect, the LOD was lower to 1.7× 10 2 CFU/mL, and the assay could be completed within 2 h (Figure 5b).   Bacteria secrete a wide variety of protein toxins, such as cholera toxin, botulinum neurotoxins (BoNT), staphylococcal enterotoxins (SE), and Shiga toxin, which can cause serious foodborne diseases and substantial economic losses [151]. Given the extremely low concentration (lower than 1 ng/mL) and wide variety of these toxins, sensitive and multi-channel methods need to be developed to identify them from complex samples. A PEI-mediated Fe 3 O 4 @CdSe/ZnS QDs were well fabricated as a novel advanced bifunctional probe for simultaneous enrichment and detection of BoNT/A and SEB with high sensitivity [152]. The proposed method provides a dual signal readout, and the vLOD of the fluorescence signal for both target toxins was 10 pg/mL and lower than that of the brown color signal (1 ng/mL). The LODs for BoNT/A and SEB were calculated to be 2.52 pg/mL and 2.86 pg/mL, respectively, which achieved a significant improvement of approximately 396-fold for BoNT/A and 349-fold for SEB compared with color results. The MNPs@QDs based two-channel LFIA could complete the entire process in 30 min, including 20 min of magnetic separation pretreatment and 10 min of chromatography (Figure 6b). The milk and juice were employed as actual samples for verifying practicability, and recoveries were in the range of 78.8-98.0%, with an RSD lower than 10.3%.
The existing methods for detection of toxins based on MNPs@QDs are listed in Table 3. The currently reported bifunctional MNPs@QDs-based LFIA for detecting toxins are scarce and mainly focused on the form of LFIA. More applications and forms need to be discovered in subsequent research.

Pesticides, Antibiotics and Illegal Additives
Pesticides, including insecticides, herbicides, etc., are extensively used in agricultural production [153]. Unreasonable use will lead to its gradual accumulation in soil, water, and agricultural products, and the risk of human exposure to pesticides will also increase accordingly. Rapid and accurate analysis of these residues is an essential topic in food safety monitoring, and novel nanomaterials based on MNPs@QDs nanocomposites provide an alternative method for pesticide residue analysis. In the face of complicated food matrices, the MIP with specific recognition is usually selected for preconcentrating and subsequent detection. Embedding MIPs to form MNPs@QDs as trifunctional nanocomposites for rapid separation, specific recognition, and fluorescence detection is an interesting strategy. Li and co-workers designed Fe 3 O 4 @SiO 2 @CdTe QDs-MIPs nanocomposites for extracting and tracing the trichlorfon in vegetable samples with a LOD of 30 µg/kg [154]. Good recoveries were also observed in spiked cucumber and cauliflower samples, with average recoveries from 78.7% to 96.6%. In another study, Zhu et al. utilized alkoxysilane groups of silane-modified CQDs copolymerized with Fe 3 O 4 @SiO 2 and constructed a novel sensor for sensitive detection of 4-nitrophenol (4-NP) [155]. The proposed sensor for 4-NP detection with a good linear range from 0.08-10 µM, and LOD was 23.45 nM. Flesh and head samples from fished recovered from the water ranged from 93.2 to 102.2%, with an RSD lower than 5.0%. The five remove-rebinding cycles remained stable fluorescence response with low RSDs, confirming its practical and inexpensive applications in real samples. Moreover, dual recognition derived from imprinted recognition based on hydrogen bond between 4-NP and APTES and fluorescence identification based on nitro dynamic quenching effect is the primary factor for strengthening specificity and sensitivity. Hu et al. employed Mn-doped ZnS QDs as a fluorescent core, TEOS as a cross-linker, assembly Fe 3 O 4 @SiO 2 to form MIPs modified MNPs@QDs [156]. This nanocomposite presented a good fluorescence response to N-Nitrosodiphenylamine. The linear range was 0-120 µM, and LOD was lowered to 0.69 µM. The inner effect generated by the overlapping of UV-Vs absorption of N-Nitrosodiphenylamine with the fluorescence excitation spectrum of MIPs-modified MNPs@QDs may be the fluorescence quenching mechanism.

Pesticides, Antibiotics and Illegal Additives
Pesticides, including insecticides, herbicides, etc., are extensively used in agricultural production [153]. Unreasonable use will lead to its gradual accumulation in soil, water, and agricultural products, and the risk of human exposure to pesticides will also increase accordingly. Rapid and accurate analysis of these residues is an essential topic in food safety monitoring, and novel nanomaterials based on MNPs@QDs nanocomposites provide an alternative method for pesticide residue analysis. In the face of complicated food Antibiotics have been extensively used for treating bacterial infections in humans and animals and used as feed additives to promote animal growth [157]. Animal-derived foods containing antibiotic residues not only directly produce toxic effects after entering the human body through the food chain but also indirectly increase the risk of bacterial resistance transmission. It is necessary to trace these hazardous substances from the source [158]. The NH 2 -Fe 3 O 4 were conjugated with thiolated QDs via covalent binding to form MNPs@QDs nanocomposites and were used for sensing tetracycline hydrochloride [159]. The fluores-cence intensity gradually decreased with the addition of tetracycline hydrochloride, and the linear range was 10-700 nM with a LOD of 1.2 nM; the quenching mechanism was probable dynamic quenching. Dual functional components combined with mesoporous Fe 3 O 4 @SiO 2 contribute to forming more recognition cavities in MIPs. This will achieve better recognition efficiency. Chen et al. developed a novel room-temperature phosphorescence MNPs@QDs-MIPs probe for tracing norfloxacin residue in milk and fish [160]. The MNPs@QDs-MIPs realized a highly specific fluorescence response to norfloxacin, and linearity ranged from 1 to 90 µg/mL with a LOD of 0.8 µg/mL. Its practicability was verified in the fish and milk samples with recoveries of 90.9-111.5%. The whole detection procedure was finished within 40 min. The efficient recognition of norfloxacin by nanocomposites with a large number of imprinting and binding sites directly improved the assay sensitivity, the dynamic quenching generated by photoinduced electron transfer is the main quenching mechanism. A similar strategy was also employed for detecting ceftazidime in the milk samples with a LOD of 0.05 µg/mL [161]. The binding affinity between target analytes and MNPs@QDs could be improved by introducing high-affinity materials with large specific surface areas into MIPs. Porous graphene, GQDs, and MNPs were integrated with MIPs to form a nanohybrid sensing probe and constructed an optosensor for levofloxacin detection [162]. The porous graphene and GQDs jointly promote the transfer of levofloxacin to recognition sites, inducing a fast response to levofloxacin through hydrogen bonding and π-π interaction. The quantitative linear range from 0.1 to 25 µg/mL with a LOD of 0.03 µg/mL. Cefoperazone has also been identified in another study via this strategy [163]. The metal-organic framework was employed as an affinity material with the merits of having a large surface area, high porosity, and tunable pore size. The GQDs with an emission band of 435 nm and CdTe QDs with an emission band of 572 nm were respectively fabricated MIL-101-MNPs@GQDs and MIL-101-MNPs@CdTe QDs, which could respectively detect mafenide, and sulfisoxazole in one sample [164]. The proposed optosensor showed good linearity for mafenide and sulfisoxazole detection in milk from 0.1-25 µg/mL, and LOD of both was 0.1 µg/mL. The average recoveries of this method in milk were 80.4-97.9% and 82.1-97.4% for mafenide and sulfisoxazole, respectively, with the RSD ranging from 0.3-4.6%. The study firstly realized the simultaneous detection of two analytes based on various MIL-101-MNPs@QDs with the same excitation (Figure 7a).
In the modern food industry, food additives play a crucial role in ensuring flavor, improving quality, and extending the shelf life of food. However, some illegal additives have raised new food safety issues and public concerns regarding food safety. Researchers are devoted to developing new sensors to solve these problems [165]. Clenbuterol, also commonly known as "lean meat powder," has been rigorously banned as a feed additive in China and other countries due to its significant side effects. Huang et al. developed a sensitive and matrix-tolerant LFIA based on MNPs@QDs for on-site detection of clenbuterol [166]. The LBL strategy was used to synthesize Fe 3 O 4 @SiO 2 @CdSe/ZnS QDs with a typical core@shell@satellite structure. The fluorescence characteristics were not altered in the forming of nanocomposites, and the nanospheres could be recycled entirely in 3 min under magnetic separation, demonstrating the superior fluorescence and magnetic properties of Fe 3 O 4 @SiO 2 @CdSe/ZnS QDs. The complex components of urine could seriously interfere with the accuracy of LFIA results. The AuNPs-based LFIA presents a significant difference between urine and PBS, and the bifunctional MNPs@QDs were not affected by the urine matrix. In addition, the LODs of MNPs@QDs-based LFIA were 0.16 and 0.22 ng/mL in PBS and swine urine, respectively, which was four times lower than AuNPsbased LFIA. Recoveries for swine urine samples (0.5-2.0 ng/mL) were between 79.1 and 108.9%, with a CV in the range of 3.4-10.3%. The proposed method innovatively integrated magnetism and fluorescence in one probe to allow simultaneous enrichment and detection. This avoided the loss of analyte and improved sensitivity (Figure 7b). The microemulsion technique was utilized to fabricate CdTe QDs/nano-Fe 3 O 4 @MIPs for sensitive and selective detection of malachite green in fish [167]. The nanocomposites exhibited a fast absorption equilibrium of malachite green within 5 min and achieved a LOD of 0.014 µM. The recov-eries of malachite green in fish samples ranged from 102.7% to 108.6%. In another study, polydopamine-modified Fe 3 O 4 @SiO 2 to dop QDs through self-polymerization to form a chemiluminescent (ECL) probe and applied for the ultrasensitive detection of bisphenol A [168]. Free bisphenol A in the sample entered the recognition cavities and occupied the binding sites of MIPs, the strong ECL emission of QDs was blocked. In accordance with the ECL intensity, the detection performance of the sensor with a wide linear range from 1 nM to 0.1 mM, and LOD was lower to 0.34 nM.   Reproduced with permission from [166]. 2019, Copyright Journal of Agricultural Food Chemistry.
As reviewed thus far, some progress has been achieved in detecting pesticides, antibiotics, and illegal additives based on bifunctional MNPs@QDs nanocomposites, and their detection performances are listed in Table 4. The combination of novel MNPs@QDs nanocomposites with high-affinity recognition elements is an attractive strategy to solve the problems of wide varieties, low concentration levels, and complex samples matrix in the detection of these contaminants.

Conclusions and Perspectives
The development of high-throughput, on-site, and portable analysis techniques has become a research hotspot for identifying food contaminants. The MNPs@QDs-based novel sensors have been extensively applied for food contaminants detection with superior detection performances. This review briefly overviews the preparation methods of MNPs@QDs nanocomposites and their applications in food contaminants detection. Despite great efforts that have been exerted by scientists to develop simple preparation methods to fabricate MNPs@QDs nanocomposites with excellent magnetic/fluorescent performances, the preparation process reported in the existing studies is cumbersome, and their stability and biocompatibility are usually unsatisfactory. The introduction of MNPs will inevitably cause the fluorescence quenching of QDs, which confirm that the development of MNPs@QDs nanocomposites with good adaptability still faces tremendous challenges. The integration of sample pretreatment and rapid detection in one sensing platform is attractive, but the complexity of sample pretreatment is a universal challenge for sensing platforms. The lack of standardized pretreatment protocols of MNPs@QDs nanocomposites for the inherent characteristics of specific food types may limit the development of sensors. More detailed information is required to comprehend the process of targets separation and recovery from the food matrix. Moreover, the analytical modes focused on several limited forms, which could not meet the diverse requirements in the face of various food matrices under different usage scenarios.
Despite these limitations, sensing platforms based on MNPs@QDs nanocomposites have great potential for determining contaminants in complicated food matrices and are rapidly developing. Herein, we propose several vital points for the future development of MNPs@QDs nanocomposites.

1.
Pointing towards requirements of strong matrix tolerance and high QY, a universal method should be developed to simplify the preparation process and obtain a multifunctional MNPs@QDs probe.

2.
In-depth exploration of the adsorption, enrichment, and separation procedures between MNPs@QDs and food contaminants, to provide a theoretical basis for tailoring the appropriate pretreatment protocols with various characteristics of food samples.

3.
Combining high affinity, specific and stable recognition elements (such as MIPs, aptamers, and nanobodies) to construct rapid, sensitive, and high-throughput sensing platforms for food contaminants detections through different analytical forms.

4.
Miniaturized and portable equipment integrated with sensing platforms for immediate on-site detection to confront various food safety incidents. The smartphones and microfluidic technologies that belong to smart manufacturing also provide a future development direction for analysis devices.
Simplifying the pretreatment process, improving the detection efficiency, and enhancing the anti-interference ability of the method are the future development directions in food contaminants analysis. Our goal is to stimulate broader interest in developing MNPs@QDsbased sensing platforms and improve their applications in food safety monitoring. We believe that emerging new insights and solutions generated by the collaborative endeavors of scientists in various fields will greatly accelerate the development of this area.