Development and Long-Term Stability of a Novel Microbial Fuel Cell BOD Sensor with MnO2 Catalyst

A novel microbial fuel cell (MFC)-based biosensor was designed for continuous monitoring of biochemical oxygen demand (BOD) in real wastewater. To lower the material cost, manganese dioxide (MnO2) was tested as an innovative cathode catalyst for oxygen reduction in a single chamber air-cathode MFC, and two different crystalline structures obtained during synthesis of MnO2 (namely β- and γ-MnO2) were compared. The BOD sensor was studied in a comprehensive way, using both sodium acetate solution and real domestic wastewater (DWW). The optimal performance of the sensor was obtained with a β-MnO2 catalyst, with R2 values of 0.99 and 0.98 using sodium acetate solution and DWW, respectively. The BOD values predicted by the β-MnO2 biosensor for DWW were in agreement with the BOD5 values, determined according to standard methods, with slight variations in the range from 3% to 12%. Finally, the long-term stability of the BOD biosensor was evaluated over 1.5 years. To the best of our knowledge, this is the first report of an MFC BOD sensor using an MnO2 catalyst at the cathode; the feasibility of using a low-cost catalyst in an MFC for online measurement of BOD in real wastewater broadens the scope of applications for such devices.


Introduction
To ensure efficient operation of wastewater treatment processes, the continuous monitoring of the biochemical oxygen demand (BOD) of the treated effluent is essential. However, the conventional 5-day BOD (BOD 5 ) test is laborious, sometimes poorly reproducible and inaccurate, particularly at low concentrations of organic compounds [1]. Moreover, membrane fouling of the dissolved oxygen probe can become a serious problem with wastewater, and frequent maintenance is therefore needed to maintain high sensitivity [2]. These issues supported the development of microbial biosensors for BOD measurement, based on respirometry [3,4], bioluminescence [5,6], bioreactor/chemostat technology [7,8], and structure-based biodegradation estimation [9]. Biosensors provide the additional benefit of automation; however, they usually make use of single microbial strains, which may not be able to oxidize a broad range of substrates. Consequently, dissolved oxygen consumption in such sensors may not be directly proportional to the total concentration of biodegradable organics present in solution [10]. In addition, the intrinsic limitation of oxygen solubility in aqueous solutions, the short-term stability of probes, and the lysis of immobilized microbial strains challenge the viability of such sensors [11,12].
In recent years, microbial fuel cells (MFCs) have been examined as an alternative BOD sensing device [1,2,[13][14][15][16][17]. MFC BOD sensors are quick and portable, and contain a mixed population of microorganisms (by using environmental inoculum from a wastewater reclamation plant in Singapore) able to oxidize a wide range of substrates [1,18]. Yet the design and operation conditions as reported in the literature are suboptimal, consisting of two-chambered MFC systems [13,14] functioning in batch mode [15][16][17]. For the operator of a wastewater treatment plant to continuously monitor the evolution of BOD in effluent samples, a continuous "online" system is needed. Furthermore, the use of single-chambered air cathode MFCs should be preferred, as these are easier and cheaper to operate than their two-chambered counterparts, mostly because the cathode can be directly exposed to ambient air as a free and sustainable source of oxygen.
Another area of improvement for MFC sensors is the choice of an affordable and sustainable cathode catalyst. So far, most sensors reported in the literature have made use of expensive platinum [19][20][21]. However, considering the high cost and low durability of platinum due to corrosion and degradation of catalytic activity over time [22], alternative metal catalysts such as indium/tin [23], cobalt [24], titanium [25], tungsten [26], or manganese [27] should be sought. In our previous work, we explored the efficacy of manganese oxide (MnO 2 ) as a catalyst for the oxygen reduction reaction [27]. Specifically, three types of MnO 2 catalysts (i.e., α-, β-, and γ-MnO 2 ), based on different preparation methods and crystalline structure, were incorporated individually into three air-cathode MFCs. The performance of the MFCs were characterized and investigated by cyclic voltammetry in neutral medium. The performance of the MFCs based on their electrical performance showed the superior catalytic activity of βand γ-MnO 2 over α-MnO 2 ; yet, the efficacy and long-term stability of such catalyst in a sensor device remains to be assessed.
In this study, a compact single-chambered MFC, with an air cathode and MnO 2 as a cathode catalyst, was tested as a BOD sensor in a continuous mode. With the aim of implementing this MFC BOD sensor in wastewater treatment plants, the performance stability of the sensor must be evaluated over a long time period in order, for example, to address the repeatability of results and the need to re-calibrate the sensor over time. Therefore, unlike previous studies, the performance of the BOD sensor was evaluated over 1.5 years in this study using both a synthetic substrate and real domestic wastewater (DWW). The performance of the MFC BOD sensor was assessed holistically in terms of the linear relationship between signal output and organic concentration, sensor stability, and the compliance of predicted BOD values using the MFC biosensor with BOD 5 , obtained according to standard methods [28].

Optimization of Hydraulic Retention Time (HRT)
A good sensor should measure "true" BOD 5 concentrations, provide a strong signal (in this case, voltage output), and have a quick response time. For this purpose, the HRT of the MFC-based BOD sensor was optimized. A sodium acetate solution at a fixed BOD 5 concentration of 386 ± 10 mg/L was used to avoid the variability of DWW and study the reproducibility of the MFC-based BOD sensor. Figure 1 shows that the BOD 5 removal rate decreased with decreasing HRT from 30 to 2 min. It was observed that an HRT of 30 min removed 85% of BOD 5 in the influent feed, while an HRT of 2 min decreased the BOD 5 removal efficiency down to 6% for both βand γ-MnO 2 -type BOD sensors. Only 6% of BOD 5 removal efficiency at the HRT of 2 min ensured that the MFC BOD sensor would measure BOD values substantially similar to the BOD 5 concentration present in the influent feed. The response time of the BOD sensors was calculated at the HRT of 2 min by alternating the phases of feeding and starvation periods and monitoring the time taken for the voltage output to reach a maximum stable voltage value. The shortest response time of the MFC BOD sensors was measured in the range of 2-3 h at a 2 min HRT for both βand γ-MnO 2 -type BOD biosensors.

Calibration with Sodium Acetate Solution
After three months of operation, the sensors were calibrated with the sodium acetate solution at different BOD5 concentrations ranging from 44 to 483 mg/L (Figure 2A,B). A linear relationship was obtained between the BOD5 and the maximum steady-state voltage as long as the BOD5 remained in the range of 44-343 mg/L. The R 2 value was high at 0.99 and 0.97 for the β-and γ-MnO2, respectively. The reproducibility of the sensor response was found to be better with β-MnO2 (standard deviation of 0.05%) than with γ-MnO2 (standard deviation of 0.22%). As shown in Table 1, the F-values were 511 and 236 for the β-and γ-MnO2 type MFC BOD biosensor, respectively, implying that the linear model was significant. Additionally, the value of "Prob > F" (probability that null hypothesis is correct) remained below 0.05, indicating that the model terms were significant at a 95% level of confidence. In both types of sensor, a good relationship was obtained between the voltage output and the BOD5, indicating reliable performance and calibration.
The performance of the sensors was determined again under the same conditions after one year of operation of the MFC BOD sensor ( Figure 2C,D). Again, a good linear relationship was obtained for a BOD range of 44-343 mg/L with an R 2 value of 0.97 (F-value of 173) and an R 2 value of 0.96 (F-value of 145) for the β-and γ-MnO2-type BOD sensors, respectively. All the experiments were conducted in duplicate, and the standard deviation equaled 0.075% and 0.16%, for the β-and γ-MnO2-type MFC BOD sensors, respectively.

Calibration with Sodium Acetate Solution
After three months of operation, the sensors were calibrated with the sodium acetate solution at different BOD 5 concentrations ranging from 44 to 483 mg/L (Figure 2A,B). A linear relationship was obtained between the BOD 5 and the maximum steady-state voltage as long as the BOD 5 remained in the range of 44-343 mg/L. The R 2 value was high at 0.99 and 0.97 for the βand γ-MnO 2 , respectively. The reproducibility of the sensor response was found to be better with β-MnO 2 (standard deviation of 0.05%) than with γ-MnO 2 (standard deviation of 0.22%). As shown in Table 1, the F-values were 511 and 236 for the βand γ-MnO 2 type MFC BOD biosensor, respectively, implying that the linear model was significant. Additionally, the value of "Prob > F" (probability that null hypothesis is correct) remained below 0.05, indicating that the model terms were significant at a 95% level of confidence. In both types of sensor, a good relationship was obtained between the voltage output and the BOD 5 , indicating reliable performance and calibration.
The performance of the sensors was determined again under the same conditions after one year of operation of the MFC BOD sensor ( Figure 2C,D). Again, a good linear relationship was obtained for a BOD range of 44-343 mg/L with an R 2 value of 0.97 (F-value of 173) and an R 2 value of 0.96 (F-value of 145) for the βand γ-MnO 2 -type BOD sensors, respectively. All the experiments were conducted in duplicate, and the standard deviation equaled 0.075% and 0.16%, for the βand γ-MnO 2 -type MFC BOD sensors, respectively.

Calibration with Sodium Acetate Solution
After three months of operation, the sensors were calibrated with the sodium acetate solution at different BOD5 concentrations ranging from 44 to 483 mg/L (Figure 2A,B). A linear relationship was obtained between the BOD5 and the maximum steady-state voltage as long as the BOD5 remained in the range of 44-343 mg/L. The R 2 value was high at 0.99 and 0.97 for the β-and γ-MnO2, respectively. The reproducibility of the sensor response was found to be better with β-MnO2 (standard deviation of 0.05%) than with γ-MnO2 (standard deviation of 0.22%). As shown in Table 1, the F-values were 511 and 236 for the β-and γ-MnO2 type MFC BOD biosensor, respectively, implying that the linear model was significant. Additionally, the value of "Prob > F" (probability that null hypothesis is correct) remained below 0.05, indicating that the model terms were significant at a 95% level of confidence. In both types of sensor, a good relationship was obtained between the voltage output and the BOD5, indicating reliable performance and calibration.
The performance of the sensors was determined again under the same conditions after one year of operation of the MFC BOD sensor ( Figure 2C,D). Again, a good linear relationship was obtained for a BOD range of 44-343 mg/L with an R 2 value of 0.97 (F-value of 173) and an R 2 value of 0.96 (F-value of 145) for the β-and γ-MnO2-type BOD sensors, respectively. All the experiments were conducted in duplicate, and the standard deviation equaled 0.075% and 0.16%, for the β-and γ-MnO2-type MFC BOD sensors, respectively.   For practical applications, the MFC BOD sensors must be able to work with DWW; therefore, this was tested both with βand γ-MnO 2 after six months of operation. In those conditions, a linear relationship between the voltage output and the BOD 5 concentration was again obtained, confirming the results obtained with synthetic substrate. Figure 3A,B show a linear relationship between the BOD 5 (ranging from 36 to 178 mg/L) and the maximum steady-state voltage with R 2 values of 0.98 and 0.96, and F-values of 360 and 209, with βand γ-MnO 2 , respectively. Additionally, the very low value of model parameter, "Prob > F" indicated that the model was statistically significant. To complete a comprehensive examination of the long-term stability of the MFC BOD sensors, they were finally tested again with DWW after 1.5 years ( Figure 3C,D). When measuring their performance with respect to BOD 5 , which ranged from 33 to 160 mg/L, the regression coefficient, R 2 , was 0.93 and 0.90, and the F-value was 114 and 77, for the βand γ-MnO 2 -type MFC BOD sensors, respectively. Table 1 summarizes the overall performance of both types of MFC BOD sensors and shows that the performances in terms of regression coefficient and F-value were slightly decreased after 1.5 years. Nonetheless, the MFC BOD sensors were still able to measure the BOD of water samples with good accuracy, confirming the longevity of MFC BOD sensors. For practical applications, the MFC BOD sensors must be able to work with DWW; therefore, this was tested both with β-and γ-MnO2 after six months of operation. In those conditions, a linear relationship between the voltage output and the BOD5 concentration was again obtained, confirming the results obtained with synthetic substrate. Figure 3A,B show a linear relationship between the BOD5 (ranging from 36 to 178 mg/L) and the maximum steady-state voltage with R 2 values of 0.98 and 0.96, and F-values of 360 and 209, with β-and γ-MnO2, respectively. Additionally, the very low value of model parameter, "Prob > F" indicated that the model was statistically significant. To complete a comprehensive examination of the long-term stability of the MFC BOD sensors, they were finally tested again with DWW after 1.5 years ( Figure 3C,D). When measuring their performance with respect to BOD5, which ranged from 33 to 160 mg/L, the regression coefficient, R 2 , was 0.93 and 0.90, and the F-value was 114 and 77, for the β-and γ-MnO2-type MFC BOD sensors, respectively. Table 1 summarizes the overall performance of both types of MFC BOD sensors and shows that the performances in terms of regression coefficient and F-value were slightly decreased after 1.5 years. Nonetheless, the MFC BOD sensors were still able to measure the BOD of water samples with good accuracy, confirming the longevity of MFC BOD sensors.

Compliance of Predicted BOD Values (BOD p ) with BOD 5
The compliance of the BOD values as predicted by the MFC sensors (BOD p ) with BOD 5 was determined using five random samples of DWW after 1.5 years of operation, using the calibration curves obtained at that time. Figure 4 plots the BOD p values measured with βand γ-MnO 2 MFC BOD sensors against the BOD 5 for all five samples. The BOD 5 of the five samples ranged from 56 to 155 mg/L, with a standard deviation comprised between 14%-27%. For both types of catalysts, a good correlation was obtained between BOD 5 and BOD p ; yet the standard deviation obtained with β-MnO 2 (3%-12%) was lower than that of γ-MnO 2 (8-21%). Nevertheless, these standard deviations remained lower than that of BOD 5 , therefore showing the improved reliability of the sensors over the conventional BOD 5 method, especially when β-MnO 2 was used as the catalyst.

Compliance of Predicted BOD Values (BODp) with BOD5
The compliance of the BOD values as predicted by the MFC sensors (BODp) with BOD5 was determined using five random samples of DWW after 1.5 years of operation, using the calibration curves obtained at that time. Figure 4 plots the BODp values measured with β-and γ-MnO2 MFC BOD sensors against the BOD5 for all five samples. The BOD5 of the five samples ranged from 56 to 155 mg/L, with a standard deviation comprised between 14%-27%. For both types of catalysts, a good correlation was obtained between BOD5 and BODp; yet the standard deviation obtained with β-MnO2 (3%-12%) was lower than that of γ-MnO2 (8-21%). Nevertheless, these standard deviations remained lower than that of BOD5, therefore showing the improved reliability of the sensors over the conventional BOD5 method, especially when β-MnO2 was used as the catalyst.

Impact of Operating Parameters
For achieving reliable performance of any BOD sensor, the "true" concentration of BOD5 must be measured; the concentration of BOD5 is almost the same in both the influent and effluent wastewater feed. In other words, a lower BOD5 removal rate indicates the measurement of the "true" influent BOD5 concentration, which is the desired BOD5 measurement. The observation of a decreasing BOD5 removal rate with a decreasing HRT illustrates how a lower HRT may help to measure nearly an equal organic concentration, which is present in the influent feed. Moreover, a lower HRT increases the electrochemical activity of the biofilm by increasing mass transfer rate and subsequently helps in decreasing the response time of the MFC BOD sensor. These results are in accordance with the findings of Di Lorenzo et al. [19], who reported that the dynamic response of MFC sensors became faster at lower HRTs (experiments were conducted at HRTs ranging from 89.3 to 417.0 min).

Impact of Catalysts
In the previous study, β-MnO2 was reported as yielding the best performance, as assessed by cyclic voltammetry and confirmed by actual MFC experiments [27]. Nevertheless, the performance of γ-MnO2 was good enough to be assessed for its efficacy as an MFC BOD sensor. The present study confirms the superiority of β-MnO2 MFC sensors over γ-MnO2 sensors in terms of sensitivity and stability. This can be explained by different crystallographic structures of β-and γ-MnO2 catalysts.

Impact of Operating Parameters
For achieving reliable performance of any BOD sensor, the "true" concentration of BOD 5 must be measured; the concentration of BOD 5 is almost the same in both the influent and effluent wastewater feed. In other words, a lower BOD 5 removal rate indicates the measurement of the "true" influent BOD 5 concentration, which is the desired BOD 5 measurement. The observation of a decreasing BOD 5 removal rate with a decreasing HRT illustrates how a lower HRT may help to measure nearly an equal organic concentration, which is present in the influent feed. Moreover, a lower HRT increases the electrochemical activity of the biofilm by increasing mass transfer rate and subsequently helps in decreasing the response time of the MFC BOD sensor. These results are in accordance with the findings of Di Lorenzo et al. [19], who reported that the dynamic response of MFC sensors became faster at lower HRTs (experiments were conducted at HRTs ranging from 89.3 to 417.0 min).

Impact of Catalysts
In the previous study, β-MnO 2 was reported as yielding the best performance, as assessed by cyclic voltammetry and confirmed by actual MFC experiments [27]. Nevertheless, the performance of γ-MnO 2 was good enough to be assessed for its efficacy as an MFC BOD sensor. The present study confirms the superiority of β-MnO 2 MFC sensors over γ-MnO 2 sensors in terms of sensitivity and stability. This can be explained by different crystallographic structures of βand γ-MnO 2 catalysts. Indeed, β-MnO 2 presents a homogeneous nano-rod structure, while γ-MnO 2 forms fine needles, dispersed in clusters around carbon nanotubes [27]. The improved structure of the former is likely to allow for better adsorption of O 2 on its surface and achieve overall higher catalytic activity. In our MFC BOD sensor, this translated into a stronger and more stable signal. This is in accordance with other studies that have correlated the higher catalytic activity of β-MnO 2 with its higher average oxidation state, as compared to γ-MnO 2 [29].

Impact of the Substrate
One of the main goals of this study is to provide the operators of wastewater treatment plants with an efficient and sustainable BOD sensor; for this purpose, it is essential to assess the sensor performance not only with synthetic feed but also with real DWW. It is a well-known fact that simple substrates like acetate are more readily assimilable at the anode of an MFC than complex effluents, leading to higher coulombic recoveries [30]. Additionally, a complex substrate such as DWW helps more in the development of electrochemically active biofilms; meanwhile, as an easily consumable feed, a simple substrate improves voltage generation [31]. Indeed, in an MFC BOD sensor, lower assimilable rates of complex organics in DWW lead to slightly reduced sensitivity; nevertheless, a good linear relationship was established with DWW too, at a BOD 5 ranging between 33 and 172 mg/L, even after 1.5 years, making the MFC BOD sensor applicable for practical use.

Long-Term Stability
Over a long time period of 1.5 years, the voltage generated by both the βand γ-MnO 2 MFC BOD sensors eventually decreased, probably due to changes in biofilm composition, bio-fouling on the proton exchange membrane [32], and decreased catalyst activity [33]. Kim et al. [18] reported that their MFC BOD sensor remained stable for five years, but provided little evidence to support their claim. In particular, re-calibration was not addressed. In this study, we noticed that re-calibration is one of the critical factors that affected the performance of the MFC BOD sensor and that it was definitely needed after a year; however, the exact frequency of re-calibration should be evaluated in future works in order to maintain a good proportionality between BOD 5 and the recorded voltage at all times.

BOD p vs. BOD 5
The β-MnO 2 -type sensor showed a close compliance of BOD p with BOD 5 , while both MFC BOD sensors exhibited low standard deviation in the repetition of measuring BOD p . Results indicated that, for higher BOD values (>150 mg/L), the MFC BOD sensors had a tendency to slightly overestimate the BOD. Yet, the compliance was extremely good in a lower BOD range (between 50 and 100 mg/L), which corresponds to the typical BOD of treated effluents from wastewater treatment plants. This, along with good accuracy, result reproducibility, a fast response time, and an ability to measure BOD, continuously emphasizes the suitability of the MFC BOD sensor developed in this study for application in wastewater treatment plants.

MFC Construction and Operation
The MFCs used in this study were designed and constructed as acrylic single-chambered air-cathode cylindrical reactors, with a diameter of 6 cm and a width of 1 cm (i.e., a total volume of 28.3 mL) ( Figure 5). MnO 2 nanoparticles were mixed with carbon nanotubes as the conductive material and polyvinylidene fluoride as the binder. Both the anode and cathode consisted of carbon cloth (E-Tek, Woburn, MA, USA), with the cathode coated on one side with MnO 2 ink (either β or γ) at a catalyst loading of 3 mg·cm −2 following the procedure of Lu et al. [27]. The cathode was then hot-pressed together with Nafion, a proton exchange membrane (PEM). All MFCs were duplicated. The MFCs were inoculated and operated initially with real DWW collected from the primary clarifier of a wastewater treatment plant in Singapore. DWW was used as-is, except for preliminary screening, used with a 0.45 mm pore-sized filter cloth to remove big particles from accumulating inside the MFCs. DWW had a COD of 355.0 ± 75.0 mg/L, total suspended solids of 218.5 ± 105.0 mg/L, total dissolved solids of 110.2 ± 62.3 mg/L, a pH of 7. ± 0.4, and a conductivity of 0.855 ± 0.085 ms/cm. In some instances, a sodium acetate solution was used, prepared according to methodology described by Lefebvre et al. [24]. Influent feeding was done using peristaltic pumps (Masterflex 07523-70, Spectra-Teknik Pte Ltd., Singapore) in an upflow mode. A 10 Ω resistor was connected externally to each MFC, following recommendations by Di Lorenzo et al. [19] that low external resistance can shorten the response time, and the voltage over the resistor was recorded at fixed intervals of 1 h using a digital multimeter connected to a computer via a data acquisition system (M3500A, Array Electronic, Taipei, Taiwan).

Synthesis of MnO2 Catalysts
The β-MnO2 catalyst was prepared by dissolving MnSO4·H2O (1.6 mmol) and (NH4)2S2O8 (1.6 mmol) in 20 mL of water at ambient temperature (~25 °C) to form a homogeneous solution, which was then transferred to a Teflon-lined stainless steel autoclave, sealed, and maintained at 125 °C for 14 h. After the solution was cooled down to ambient temperature, the resulting dark-gray solid product was filtered, washed, and dried. γ-MnO2 was prepared by dissolving MnSO4·H2O (16 mmol) and (NH4)2S2O8 (16 mmol) in 200 mL of water. After that, the mixture was heated up to 9 °C in an oil bath and maintained for 24 h with magnetic stirring. The resulting black precipitate was filtered, washed, and dried [27].

Calibration Procedure
The BOD sensor was calibrated by plotting the steady-state voltage (the signal) against BOD5 in a linear relationship. Since a fixed external load of 10 Ω was used in all experiments, the relationship between current and voltage was proportional and followed Ohm's law. For calibration with the sodium acetate solution, the MFC BOD sensors were fed with a specific BOD5 until the maximum steady voltage was generated and recorded. Between two sets of experiments, a period of starvation allowed the voltage to drop to 1.5 ± 0.5 mV. The MFC BOD sensor was fed with acetate solutions with different BOD5 concentrations, and each concentration was tested twice to ensure reproducibility. For calibration with DWW, a similar methodology was used with several dilutions of feed prepared using deionized water. The MFCs were inoculated and operated initially with real DWW collected from the primary clarifier of a wastewater treatment plant in Singapore. DWW was used as-is, except for preliminary screening, used with a 0.45 mm pore-sized filter cloth to remove big particles from accumulating inside the MFCs. DWW had a COD of 355.0 ± 75.0 mg/L, total suspended solids of 218.5 ± 105.0 mg/L, total dissolved solids of 110.2 ± 62.3 mg/L, a pH of 7. ± 0.4, and a conductivity of 0.855 ± 0.085 ms/cm. In some instances, a sodium acetate solution was used, prepared according to methodology described by Lefebvre et al. [24]. Influent feeding was done using peristaltic pumps (Masterflex 07523-70, Spectra-Teknik Pte Ltd., Singapore) in an upflow mode. A 10 Ω resistor was connected externally to each MFC, following recommendations by Di Lorenzo et al. [19] that low external resistance can shorten the response time, and the voltage over the resistor was recorded at fixed intervals of 1 h using a digital multimeter connected to a computer via a data acquisition system (M3500A, Array Electronic, Taipei, Taiwan).

Synthesis of MnO 2 Catalysts
The β-MnO 2 catalyst was prepared by dissolving MnSO 4 ·H 2 O (1.6 mmol) and (NH4) 2 S 2 O 8 (1.6 mmol) in 20 mL of water at ambient temperature (~25 • C) to form a homogeneous solution, which was then transferred to a Teflon-lined stainless steel autoclave, sealed, and maintained at 125 • C for 14 h. After the solution was cooled down to ambient temperature, the resulting dark-gray solid product was filtered, washed, and dried. γ-MnO 2 was prepared by dissolving MnSO 4 ·H 2 O (16 mmol) and (NH 4 ) 2 S 2 O 8 (16 mmol) in 200 mL of water. After that, the mixture was heated up to 9 • C in an oil bath and maintained for 24 h with magnetic stirring. The resulting black precipitate was filtered, washed, and dried [27].

Calibration Procedure
The BOD sensor was calibrated by plotting the steady-state voltage (the signal) against BOD 5 in a linear relationship. Since a fixed external load of 10 Ω was used in all experiments, the relationship between current and voltage was proportional and followed Ohm's law. For calibration with the sodium acetate solution, the MFC BOD sensors were fed with a specific BOD 5 until the maximum steady voltage was generated and recorded. Between two sets of experiments, a period of starvation allowed the voltage to drop to 1.5 ± 0.5 mV. The MFC BOD sensor was fed with acetate solutions with different BOD 5 concentrations, and each concentration was tested twice to ensure reproducibility.
For calibration with DWW, a similar methodology was used with several dilutions of feed prepared using deionized water.

Analyzes
BOD 5 and COD tests were performed in accordance with standard methods [28], using the 5-day dilution method and the closed reflux titrimetric method, respectively. The samples were filtered through glass microfiber filters (0.45-µm pore-sized, Whatman, Irvine, UK) prior to analysis. The analysis of variance (ANOVA) was used as a statistical analysis tool to examine and interpret the linear model equations obtained during calibration. ANOVA is a simple regression analysis that uses the Fisher's F-test, and its associated probability to assess the robustness of linear models and overall model significance. A "Prob > F" less than 0.05 and a large F-value indicate that the model terms are significant.

Conclusions
This study is first to use an MnO 2 catalyst (in place of an expensive Pt catalyst) for MFCs applied as online BOD sensors. A good linear relationship between the voltage and BOD 5 in both a sodium acetate solution and DWW, a stable performance in the long term (more than 1.5 years of operation), and close compliance between BOD p and BOD 5 demonstrated the potential of MnO 2 -MFC BOD sensors in substituting the conventional BOD 5 methods, which takes a longer analytical time of five days and suffers from substantial variability.