Green Synthesis of Silver Nanoparticles through Reduction with Solanum xanthocarpum L. Berry Extract: Characterization, Antimicrobial and Urease Inhibitory Activities against Helicobacter pylori

A green synthesis route for the production of silver nanoparticles using methanol extract from Solanum xanthocarpum berry (SXE) is reported in the present investigation. Silver nanoparticles (AgNps), having a surface plasmon resonance (SPR) band centered at 406 nm, were synthesized by reacting SXE (as capping as well as reducing agent) with AgNO3 during a 25 min process at 45 °C. The synthesized AgNps were characterized using UV–Visible spectrophotometry, powdered X-ray diffraction, and transmission electron microscopy (TEM). The results showed that the time of reaction, temperature and volume ratio of SXE to AgNO3 could accelerate the reduction rate of Ag+ and affect the AgNps size and shape. The nanoparticles were found to be about 10 nm in size, mono-dispersed in nature, and spherical in shape. In vitro anti-Helicobacter pylori activity of synthesized AgNps was tested against 34 clinical isolates and two reference strains of Helicobacter pylori by the agar dilution method and compared with AgNO3 and four standard drugs, namely amoxicillin (AMX), clarithromycin (CLA), metronidazole (MNZ) and tetracycline (TET), being used in anti-H. pylori therapy. Typical AgNps sample (S1) effectively inhibited the growth of H. pylori, indicating a stronger anti-H. pylori activity than that of AgNO3 or MNZ, being almost equally potent to TET and less potent than AMX and CLA. AgNps under study were found to be equally efficient against the antibiotic-resistant and antibiotic-susceptible strains of H. pylori. Besides, in the H. pylori urease inhibitory assay, S1 also exhibited a significant inhibition. Lineweaver-Burk plots revealed that the mechanism of inhibition was noncompetitive.


Introduction
Preparation of nano-sized silver based materials, usually ranging in size from 1 to 100 nanometers (nm), is amongst the most emerging areas in the field of nanotechnology. Currently, the applications of nano materials is becoming increasingly important in order to address the problems associated with material sciences, including solar energy conversion, photonics [1], catalysis [2], microelectronics [3], antimicrobial functionalities [4], and water treatment [5] .
A number of synthetic methods have been employed for the synthesis of silver-based nanoparticles involving physical, chemical [6] and biochemical techniques [7]. Chemical-based synthesis techniques are often discouraged as they involve the use of noxious reducing and/or stabilizing agents like sodium borohydride [8] and N,N-dimethylformamide [9] and toxic solvents [10].
Solanum xanthocarpum, commonly known as yellow-berried nightshade, is a prickly plant, which grows wild in different regions of the Indo-Pakistan subcontinent. It has been reported that this plant contains several steroidal alkaloids like solanacarpine, solanacarpidine, solancarpine, solasonine, solamargine and other constituents, such as caffeic acid, coumarins (aesculetin and aesculin), steroids (carpesterol, diosgenin, campesterol, daucosterol) and triterpenes (cycloartanol and cycloartenol) [29]. The fruit from S. xanthocarpum has flavonoids quercitrin and apigenin glycosides as the major chemical constituents [29]. Various medicinal properties have been ascribed to different parts of this multipurpose herb. For example, the root is an expectorant, and is employed in folk medicine systems for the treatment of cough, asthma and chest pain as well as wound healing [29][30][31][32][33]. Fruits are edible, act as an anthelmintic, and are used as a remedy for the treatment of different ailments [32]. A recent study appraises the antihyperglycemic and antioxidant activities of leaf extracts from S. xanthocarpum on alloxan-induced diabetic rats [34].
It is now firmly established that gastric and duodenal ulcers are generally caused by H. pylori which survives and grows in acidic environments [35]. Triple therapy, including a proton pump inhibitor and any of the two antibiotics, such as AMX, CLA, MNZ and TET is frequently conducted for treating H. pylori-related infections [36]. Although an eradication rate of more than 80% has been reported by the use of relevant therapy, different side-effects including the emergence of antibiotic-resistant in H. pylori due to overuse of antibiotics are still to be addressed.
Therefore, there is a need to develop antimicrobial agents possessing enhanced efficacy against microorganisms and reduced toxicity for human cells. In this regard, many metals and their salts have been reported for possessing antibacterial activities against H. pylori [37,38]. The possible mechanism of action of metallic agents is the inactivation of H. pylori urease [39,40]. In this context, the appliance of silver nanoparticles (AgNps) in the field of medicine including wound dressings and medical devices, etc. is in practice [41]. However, an adequate assessment of the long-term effects of AgNps exposure on human physiology and their release into the environment is debatable. Most of the scientific literature on the toxicology of AgNPs has only been published in the past decade [42]. Many of these studies have revealed AgNPs to have mild toxicity against several cell lines as well as a number of aquatic organisms [43], and the mechanistic basis of these toxic effects is now an area of active research [44][45][46].
To the best of our knowledge, metal nanoparticles have not yet been tested against H. pylori. As a potential exists for the use of medicinal plant extracts as reducing and capping agents to prepare nanoparticles through green synthesis, so in the present work very stable silver nanoparticles (AgNps) were synthesized using S. xanthocarpum berry extract (SXE). SXE acted both as a reducing as well as a capping agent. Anti-Helicobacter pylori activities of synthesized AgNps were evaluated against 34 local isolates and two reference strains of H. pylori by the agar dilution method.

Results and Discussion
In the present work, AgNps have been synthesized by the reduction of aqueous silver ions using S. xanthocarpum berry extract. The effect of concentration of reacting substances, temperature, time and pH on synthesis rate, size and shape of the nanoparticles was studied.

UV-Visible Analysis of AgNps
The optical properties of AgNps were calculated by UV-Vis absorption spectroscopy, an important and most commonly used technique, to ascertain the formation stability of metal nanoparticles. Due to surface plasmon resonance (SPR), a strong absorption of electromagnetic waves is exhibited by metal nanoparticles in the visible range. The SPR phenomenon arises when nanoparticles are irradiated with visible light, because of the collective oscillations of the conduction electrons. It is well known that AgNps exhibit a yellowish-brown color in aqueous solution due to the excitation in UV-visible spectrum depending upon the particle size [47].
The SPR bands in the UV-Vis spectra of AgNps colloidal suspension S1, S2, S3, S4 and S5 appeared at 406, 412, 428, 425 and 433 nm, respectively, Figure 1(a). For colloid S5 the SPR at 433 nm was broad. By increasing the concentration of SXE, the SPR bands for colloids S4, S3, S2 and S1 became sharper and for the typical sample S1 SPR appeared at 406 nm. The broad SPR at lower quantities of the SXE was due mainly to the formation of large anisotropic particles. This perhaps may occur because by lowering the quantity of SXE, the concentration of groups/molecules such as phenolics, alkaloids and sugars, etc. responsible for capping and stabilizing of nanoparticle reduces. Similar results have already been reported in the case of the stabilization effect of biological extracts on the formation of metal nanoparticles [14][15]22]. The increased bandwidth of colloid S5 is due to the fact that beyond a limit the bio-molecules in an extract cease to act as a capping agent. The fairly sharp and symmetrical SPR band observed for colloid S1 at 406 nm is indicative of small spherical nanoparticles. (d) (e) Figure 1(b) shows the effect of temperature on the synthesis of typical sample S1. A broad peak of less intensity was observed at 433 nm for the colloidal suspension obtained after heating the reaction mixture at 25 °C for 2-3 h. With increase in temperature from 25 °C to 45 °C, the SPR peaks became sharper and sharper and for the yellowish brown solution, obtained after 30 min of stirring at 45 °C, an absorption band at 406 nm was obtained which suggested the formation of silver nanoparticles. It can be observed that an optimum temperature is required for the completion of reaction due to the instability of formed silver nanoparticles. The optimum temperature required for the completion of reaction was investigated to be 45 °C. Upon a further increase in temperature (up to 50 °C), a red-shift appeared from 406 nm to 450 nm due to increase in AgNps size. Further increase in temperature caused the broadening of the peak revealing the increased size of nanoparticles. This temperature dependent increase in the peak intensity showed the dependence of the silver ion reduction on the reaction temperature. It was observed that reduction rate of silver ions increased by increasing temperature. Similar results were reported by Pastoriza-Santos and Liz-Marzan [9]. This sharpness in absorbance peak depends on the size of the synthesized nanoparticle, as with higher temperature particle size may be smaller, which results in sharpness of the plasmon resonance band of AgNPs [48]. Initially, the size was reduced due to the reduction in aggregation of the growing nanoparticles. Increasing the temperature beyond 45 °C aids the growth of the crystal around the nucleus resulting in a decrease in absorption.
Effect of time on the completion of reaction was studied by UV-Vis spectroscopy for colloidal suspension S1 . An absorption band of very low intensity appeared at 406 nm for the colloid after 10 min of stirring, Figure1(c), which changed into a clearly visible peak after 30 min at the same absorbance, indicating the presence of spherical AgNps. The absorption peak intensity increased rapidly with increase in reaction time from 10 to 30 min due to the continuous formation of AgNps in the reaction system. It was, therefore, observed that an optimum time is required for the completion of reaction due to the instability of formed silver nanoparticles. The optimum time required for the completion of reaction was recorded to be 30 min.
pH is another important factor affecting the reduction of silver ions. The effect of pH on the reduction of silver ions was studied by UV-Vis spectroscopy and is shown in Figure 1(d,e). At pH 4.0, no absorption peak was observed in the range of 400-450 nm for the colloidal suspension of all samples even after 24 h of the reaction. However, an absorption band appeared at about 440 nm when pH increased from 4 to 5 indicating the formation of AgNps, Figure 1(d). It was observed that the absorption peak intensity increased gradually with an increase in pH, suggesting that the reduction rate of silver ions increases with an increase in pH. The formation of AgNps was suppressed by acidic conditions and enhanced by basic conditions. At lower pH (pH 5), larger nanoparticles were formed, whereas, at higher pH (pH 9), smaller and highly dispersed nanoparticles formed, Figure 1(e).

PXRD and TEM Studies
The XRD pattern of dried silver nanoparticles S1 is shown in Figure 2 [50]. This indicates that the prepared silver nanoparticles may be enriched in (111) facets and thus the (111) plane seems to be preferentially oriented parallel to the surface of the supporting substrate. The average particle size of AgNps was calculated by the use of full width at half maximum (FWHM) of face-centered cubic (111) using the Debye-Scherrer equation, / , where K is the Scherrer constant with value from 0.9 to 1, λ is the wavelength of the X-ray, β is the full width at half maximum and θ is the Bragg angle in radians. From the Scherrer equation the average crystallite size of silver nanoparticles S1 and S2 was found to be about 10 nm and 15 nm, respectively. (c) Typical TEM images of colloid S1 and S2 with size distribution histograms are shown in Figure 2(c,d), respectively. It is evident from the Figure 2(c) that the morphology of S1 is almost spherical, which is in agreement with the shape of the SPR band in the UV-Vis spectra. The average particle size calculated for S1 was 10 nm with size ranging from 4 to 18 nm. Whereas the average particle size for sample S2 was calculated as 14 nm with an average size ranging from 7 to 18 nm. These results are in accordance with the shape of the SPR band and with the particle size calculated from XRD analysis.

Urease Inhibitory Assay
Urease inhibitory activity of silver nanoparticles S1 has been studied by the phenol red method. The results are shown in Table 2 in the form of percent inhibition. It was found that urease inhibitory activity increased linearly with increased concentration of S1. Under the conditions used in the present investigation, H. pylori urease inhibition by S1 followed Michaelis-Menten kinetics. Kinetic studies of the enzyme in the presence of S1 were presented by Lineweaver-Burk plots in which a reciprocal of enzyme activity was taken on the Y-axis and a reciprocal of substrate concentration on the X-axis. The trend of lines of different concentrations of the inhibitor gave the idea about inhibition. The values are mean ± SD of triplicate measurements.
Line weaver-Burk plots indicated that S1 is a non-competitive type of inhibitor. The plot of 1/V o vs. 1/[s] (Figure 3) consisted of a family of straight lines that intersected each other on the same point on X-axis depicting the same K m values with varying values of V max with the concentration of the inhibitor. Furthermore, it was also clear from the graphs that inhibition increased almost linearly. Therefore, it may be suggested that the mechanism was non-competitive in which the inhibitor and substrate were both attached to the enzyme non-competitively [51]. Metal based nano-preparations have gained importance due to a variety of their applications in various fields [1][2][3][4][5][6][7][8][9][10]. The synthesis techniques involve the reduction of the corresponding metallic ion by a reducing agent. The newly synthesized nanoparticles are highly unstable and become aggregated in the absence of a suitable capping agent. Chemical techniques involving the use of chemicals and solvents are described as toxic and carcinogens, and have been suggested to be eliminated by the Conferences on Harmonization [10]. It is, therefore, necessary that the nanoparticles must be synthesized using such techniques which being benign to the environment must be cost-effective. The present investigation explored the use of fruit from an important medicinal plant S. xanthocarpum [31][32][33][34]

1/v (abs/min) 1/[s] (mM)
template for the synthesis of AgNps by acting both as a reducing and a capping agent. The methanolic extract was found as an efficient capping as well as a stabilizing agent, whereas aqueous and acetone extracts did not exhibit good results (data not shown). The possible reason for this may be the dissolved phyto-chemicals present in the methanolic extract. During synthesis, it was found that an increase in concentration of S. xanthocarpum berry extract affected the morphology of the silver nanoparticles and the conditions were maintained such that finally 10 mL of the extract added to 20 mL of 1 mM silver nitrate solution resulted in a color change to golden brown, which is indicative of the formation of silver nanoparticles [16]. It has been established [52] that the optical absorption spectra of metal nanoparticles are dominated by SPR, which shift to longer wavelengths with increasing particle size. Therefore, a SPR band shift from 406 nm to 433nm (S1-S5) is indicative of the fact that an optimum concentration (10 mL) of extract is required for the synthesis of AgNps. Also, the shape of the SPR band of AgNps is strongly dependent on the particle size [53,54]. It has already been demonstrated [22] that only a single SPR band is expected in the absorption spectra of spherical nanoparticles, whereas anisotropic particles could give rise to two or more SPR bands depending on the shape of the particles. Furthermore, the number of SPR peaks increases as the symmetry of the nanoparticle decreases [54]. Therefore, the single symmetrical SPR band at 406 nm confirms the spherical morphology of the typical sample S1. S. xanthocarpum berries have been reported to contain several steroidal alkaloids like solanacarpine, solanacarpidine, solancarpine, solasonine, solamargine and other constituents like caffeic acid, coumarins like aesculetin and aesculin, steroids carpesterol, diosgenin, campesterol, daucosterol and triterpenes like cycloartanol and cycloartenol [55]. The flavonoids quercitrin and apigenin glycosides are the major chemical constituents present in S. xanthocarpum fruit [30]. Carbohydrates, flavonoids, terpenoids and certain proteins present in SXE may have a reducing and stabilizing effect in the nanoparticle synthesis. The synthesized AgNps were tested for their anti-H. pylori activity by the use of agar dilution method and their MICs were compared with silver nitrate and some of the standard drugs being used in anti-H. pylori therapy. AgNps exhibited more potent bactericidal activity than ionic silver (silver nitrate) and some of the standard drugs. The reason for much lower MICs and stronger antibacterial activities of S 1 than AgNO 3 might be due to smaller size and the presence of (111) lattice plane in the former [56]. Metal atoms in nano size provide a significantly large surface area in contact with the bacterial effluent. Considering a hypothetical case with spherical particles of uniform size, a reduction in the particle size from 10 µm to 10 nm would increase the contact surface area by 10 9 . Such a large contact surface is expected to enhance the extent of bacterial elimination. The size-dependent bactericidal activity of silver nanoparticles against gram-negative bacteria has already been reported [57,58]. Literature reports reveal the bactericidal activity of silver nanoparticles of either a simple or composite nature [59,60]. Multiple investigations have been performed to show the antibacterial activity of metals and metals chelated with some ligands against H. pylori [61].
To the best of our understanding, the present investigation can be considered to be the first of its kind reporting the anti-H. pylori activity of silver nanoparticles and their comparison with silver ions and some standard antibiotics being used in triple and quadruple therapy for the eradication of H. pylori. No standard susceptibility testing methods have yet been recommended for nanoparticles and metallic ions. Although broth dilution test and agar dilution test are both standard in vitro susceptibility tests recommended by the CLSI, due to some advantages, the agar dilution method has been adopted in the present investigation [59].The exact mechanism of anti-H. pylori activity of silver nanoparticles is not clearly understood. However, there may be two possible explanations for this mechanism. In this direction, one theory speculates that a very small quantity of silver ions may enter into the bacteria to inhibit the microorganism's respiratory system, electron transport system and enzymes, whilst another theory believes that silver ions may directly interfere with nickel in H. pylori urease, thereby making the enzyme inactive [59,62,63]. Urease, in H. pylori, converts urea into ammonia, which then counters the stomach acid, thereby creating a neutralizing environment for protecting H. pylori from the acid in the stomach. Gastric infection with H. pylori may lead to the onset of various gastric-related diseases. Most patients specifically with duodenal ulcer can be cured by killing H. pylori with antibiotics and proton pump inhibitors [35]. Several triple-or quadruple-antibiotic therapies with proton pump inhibitors have been shown to be effective in the eradication of H. pylori [36], but no single treatment regime is considered the final treatment of choice. Therefore, the specific inhibition of urease activity has been proposed as a possible strategy to inhibit H. pylori. [37,38].
Hence, there is a dire need for the eradication of H. pylori by single-therapy if possible. Bismuth is the only metal being widely used as antibacterial agent against H. pylori as a part of triple therapy. Due to potential toxic effects of bismuth, some other metals [37,38] including silver, having well defined antimicrobial activities, can be explored as possible treatments for gastrointestinal symptoms and infections. Silver compounds have been reported as anti-ulcer agents in animals and man, and their role in wound healing is well established [64]. Since H. pylori are a major peptic-ulcer causing agent, it raised the possibility that a part of the anti-ulcer activity of silver nanoparticles could be due to its effects on the growth of H. pylori.

Materials/Chemicals/Reagents and Strains
Fully ripened S. xanthocarpum berries were collected from Soon Valley of the Punjab province of Pakistan in the month of June 2010 and brought to the Department of Biological Sciences, University of Sargodha, Sargodha, Pakistan. The specimens were further identified and authenticated by Amin Ullah Shah (Assistant Professor, Department of Biological Sciences, University of Sargodha (UoS), Sargodha, Pakistan). A specimen of the berries was also submitted to the herbarium of the UoS. The berries were dried under shade for 4-5 weeks.
Silver nitrate (AgNO 3 , analytical grade) was purchased from Sigma-Aldrich. A total of 34 clinical isolates of H. pylori have already been isolated and characterized by the same group and published elsewhere [37]. Two reference strains of H. pylori NCTC 11637 and NCTC 11638 were purchased from the Health Protection Agency, London, UK.

Isolation of S. xanthocarpum Berry Extract (SXE)
Dried berries (50 g) were ground using an ordinary coffee grinder and extracted with methanol for 24 h using a conventional Orbital Shaker. After filtration, the residue was re-extracted with fresh solvent; both the extracts were pooled and then concentrated to dryness with a rotary evaporator (45 °C). The crude concentrated extract was quantitatively diluted with methanol and preserved at −4 °C for further experiments.

Synthesis of Silver Nanoparticles
Silver nitrate (20 mL; 1 mM) was added dropwise into SXE (10 mL) while stirring and heated (45 °C) in a water bath at pH 9. The resulting solution became yellowish brown after 30 min of heating, indicating the formation of silver nanoparticles [8]. The colloidal suspension thus obtained was centrifuged at 4000 rpm for 30 min and the pellet obtained after discarding the supernatant was re-dispersed in deionized water. The centrifugation process was repeated 2 to 3 times for the removal of any adsorbed substances on the surface of silver nanoparticles (AgNps). The synthesized nanoparticles were lyophilized and recovered in powdered form using a Heto-Holten A/S, DK-3450 freeze dryer (Allerd, Denmark). Different samples of AgNps were synthesized by varying the concentration of SXE and silver nitrate solution as presented in Table 3. To study the effect of temperature on the synthesis of AgNps, a typical sample, namely S 1 , was synthesized at 25 °C, 35 °C, 40 °C, 45 °C and 50 °C. Electronic absorption spectra of the aqueous colloidal suspensions were recorded at each temperature range.

Time Effect
To study the effect of time on the completion of reaction, the reaction was monitored from 0 to 30 min and aliquots were taken after every 5 min time interval for S 1 . The absorbance of the resulting solutions was recorded.

pH Effect
pH of the reaction mixture was maintained at 4, 7 and 9, respectively, by using 0.1 N HCl and 0.1 N NaOH. The absorbance of the resulting solutions was measured spectrophotometrically.

Effect of Volume of SXE Extracts
Effect of SXE to AgNO 3 volume ratio on the shape and size of AgNps was studied by varying the volume ratio of AgNO 3 and SXE. The AgNps samples thus synthesized are presented in Table 3. The absorbance of the resulting colloids was recorded.

UV-Vis Spectroscopy
The UV-Vis absorption spectra of the AgNps were recorded using Pharmaspec UV-1700 (Shimadzu Corporation, Tokyo, Japan) UV-Visible spectrophotometer at room temperature. The scanning range for the samples was 300-800 nm with a resolution of 1 nm at a scan speed of 300 nm/min.

Transmission Electron Microscopy (TEM)
TEM measurements were performed on JEM-1200EX electron microscope (JEOL, Tokyo, Japan) instrument by operating at an accelerating voltage of 120 kV. The size distribution was obtained by measuring the diameter of more than 135 particles and using Origin 7.5 software (Origen Lab Corporation, Northampton, Massachusetts, USA), and confirmed by making the calculations by the use of Debye-Scherrer equation (D = Kλ/βcosθ) from the highest intensity of XRD pattern.

X-ray Diffraction Analysis
The X-ray diffraction analysis was conducted on Bruker D8 Discover Powder Diffractometer (Berlin, Germany) using monochromatic Cu K α radiation (θ = 1.5406 Å) operating at a voltage of at 40 kV and a current of 30 mA at room temperature. The intensity data for the lyophilized nanosilver powder were collected over a 2θ range of 10°-80°. To obtain information about sub-structure and topography of the nanoparticles, AFM measurements were carried out in a Scanning Probe Microscope SPM-9500 J3 (Shimadzu Corporation, Tokyo, Japan) under normal atmospheric conditions. The sample was observed within an area of 5.0 × 5.0 µm using contact mode. A freshly prepared sample was deposited on fine metal surfaces, air dried in a dust-free environment and the resultant smooth surfaces were subjected to AFM analysis.

In Vitro Anti-Helicobacter pylori Activity
In vitro anti-H. pylori activity of the synthesized AgNps was determined by the agar dilution method in accordance with the guidelines provided by CLSI [65]. The results were recorded as minimum inhibitory concentration (MICs). Different concentrations of the synthesized AgNps were prepared by the sample digestion method. Silver nanoparticles were centrifuged and the pellet thus obtained was washed several times with deionized water in order to remove un-reacted silver ions. The removal of un-reacted silver was further confirmed by treating each filtrate with 1 mM HCl until no silver chloride was precipitated. In order to determine the concentration of AgNps for susceptibility studies, the pellet free from silver ions was divided into two halves. One half was dissolved in aqua-regia and the solution evaporated near to dryness. The process of dilution and dryness was repeated three times. In this way, the AgNps were converted to AgNO 3 . The concentration of silver ions was determined by atomic absorption spectrometry. The other half of the nanoparticles, having a concentration almost equal to the first half, was used for anti-H. pylori activities. Fourteen wells on a 96-wells plate were filled with a two-fold serially diluted colloidal suspension of silver nanoparticles in distilled water having final concentrations of 128 to 0.125 μg mL −1 . The control was filled with distilled water only. The final concentrations of other test compounds (AMX, TET, CLA) were also adjusted from 128 to 0.125 μg mL −1 by dissolving in DMSO. The control was filled with DMSO only. These dilutions were transferred to molten Muller Hinton infusion agar plates.
The frozen clinical isolates were thawed, diluted using the Muller Hinton infusion broth (MHIB), and adjusted to 10 7 CFU mL −1 . Culture (5 μL) was streaked over the agar plates. The plates were incubated under microaerophillic conditions in sealed bags at 37 °C for 72 or 96 h as appropriate. The MIC 90 were determined as per standard procedure. The breakpoints to define a resistant strain according to Megraud et al., [36] were found to be clarithromycin 1 μg mL −1 ; and according to Wu et al., [66] 0.5 μg mL −1 and 16 μg mL −1 for amoxicillin and tetracycline, respectively. Each experiment was performed as triplicate.

Isolation of H. Pylori Urease
H. pylori (NCTC-11638, Health Protection Agency, London) was grown in MHIB, supplemented with 10% fetal bovine serum for 24 h at 37 °C under microaerobic conditions (Campygen Oxford, UK). The Mao method [67] of H. pylori urease isolation has been followed. Briefly, the broth cultures (50 mL, 2.0 × 10 8 CFU mL −1 ) were centrifuged (5000× g, 4 °C) and the collected bacterial mass after being washed twice with phosphate-buffered saline (pH 7.4) was stored at −80 °C. Afterwards, H. pylori was thawed to room temperature, and mixed with 3 mL of distilled water, protease inhibitors and sonicated for 60 s. Following centrifugation (15,000 g, 4 °C), the supernatant was desalted through SephadexG-25 column (Pharmacia Bio-tech, Uppsala, Sweden). The resultant crude urease solution was added to an equal volume of glycerol and stored at −4 °C for further use.

Urease Inhibitory Assay
The reaction mixture consisting of phosphate buffer solution (55 µL, 3 mM, 4.5 pH), 25 µL of urease enzyme solution and test compound (5 µL, of S1) was incubated at 30 °C for 15 min in 96 well plates. The urease activity was determined by measuring the ammonia production using the indophenol method, as described by Weatherburn [68]. Briefly, 45 µL of each phenol reagent (1% (w/v) phenol and 0.005% (w/v) sodium nitroprusside) and 70 µL of alkali reagent (0.5% (w/v) NaOH and 0.1% active chloride, NaOCl) were added to each well. The increasing absorbance at 630 nm was measured after 50 min, using a micro-plate reader. The results were processed using the in-built software of the microplate reader. Percent inhibitions were measured by the formula 100-(OD) test well / (OD) control . Thiourea was used as control. IC 50 values of the concentrations that inhibited the hydrolysis of the substrate were calculated using the EZ-Fit kinetic program (Perrella Scientific Inc., Amherst, Massachusetts, USA). The Lineweaver-Burk plots were drawn and the values of Michaelis-Menten constant K i were calculated from the slopes of each line in the plot. Four concentrations of substrate (urea; 80 mM, 60 mM, 40 mM, 20 mM) were set for each sample. Each experiment was performed as triplicate.

Conclusions
A green method has been reported for the synthesis of silver nanoparticles using S. xanthocarpum berry extract as a reducing and capping agent. It was found that high pH value, temperature and molar ratio of S. xanthocarpum extract (SXE) to AgNO 3 could accelerate the reduction rate of Ag + and affect the Ag nanoparticle size. The adopted method is compatible with green chemistry principles as the SXE serves as a matrix for both reduction and stabilization of the silver nanoparticles synthesized. At a given SXE concentration, the efficiency of nanoparticle synthesis increases with silver nitrate concentration and reaction time, a property attributable to the large reduction capacity of the SXE. The synthesized Ag nanomaterials exhibited anti-H. pylori and urease inhibitory activities. The anti-H. pylori activity of AgNps was compared with silver nitrate. The work suggests that silver nanoparticles may provide potential applications as antibacterial and urease inhibitory agents to eradicate H. pylori-related infections.