Synthesis, Structure and Antibacterial Activity of Two Novel Coordination Polymers Based on N,N′-bis(4-carbozvlbenzvl)-4-aminotoluene and Heterocyclic Ligand against S. aureus

As the use of antibiotics increases, the increasing resistance of bacteria is the main reason for the reduced efficiency of antibacterial drugs, making the research of new antibacterial materials become new hot spot. In this article, two novel coordination polymers (CPs), namely, [Cd2(L)2(bibp)2]n (1) and [Ni(L)(bib)]n (2), where H2L = N,N′-bis(4-carbozvlbenzvl)-4-aminotoluene, bibp = 4,4′-bis(imidazol-1-yl)biphenyl, and bib = 1,3-bis(1-imidazoly)benzene, have been synthesized under solvothermal and hydrothermal condition. Structural clarification was performed through infrared spectrum and single-crystal X-ray diffraction analysis, while thermal analysis and XRD technology were used for the performance assessment of compounds 1 and 2. In addition, antibacterial performance experiments showed that compounds 1 and 2 have certain selectivity in their antibacterial properties and have good antibacterial properties against S. aureus. As the concentration of the compound increases, the inhibitory effect gradually strengthens, and when the concentration of the compound reaches 500 μg/mL and 400 μg/mL, the concentration of the S. aureus solution no longer increases and has been completely inhibited.


Introduction
Infections caused by microorganisms pose a serious threat to human health, and pathogen resistance to antibiotics has been escalating in recent years, resulting in serious health complications [1][2][3].Scientific advances in nanotechnology and materials science have made it possible to produce new substances which have inherent antimicrobial activity, encouraging deeper applications in new technological fields and meeting the challenges of a more modern society [4][5][6].In the last decade, metal-organic skeleton materials have received increasing attention for biomedical applications on account of their high porosity, distinctive biodegradability and outstanding biocompatibility [7][8][9][10].In particular, by means of properly tuning organic linkers or metal clusters, MOFs possess the capability to optimize antimicrobial properties at the molecular level, which gives MOFs a competitive advantage over conventional antimicrobial agents [11,12].Cobalt(II)-, zinc(II)-, copper(II)and silver(I)-based MOFs have been synthesized and show some antimicrobial effects.MOFs and composites containing MOFs have broad prospects in the field of antimicrobial materials [13][14][15].
In order to explore the antibacterial properties of a metal-organic framework, we selected a carboxylic acid ligand H 2 L, synthesized two new Cd(II) and Ni(II) compounds by adjusting the solvent ratio and changing the central metal atom, and discussed their coordination mode and structure.At the same time, PXRD, thermogravimetric, infrared and solid antibacterial properties of the synthesized compounds were tested, which further expanded the application prospect of the coordination polymer.In this paper, we discussed in detail the antibacterial properties of the two coordination polymers against E. coli, S. aureus and C. albicans.The experiments showed that the antibacterial properties of the two complexes were selective and showed good inhibitory properties against S. aureus.When the concentrations of coordination polymer 1 and 2 were 500 µg/mL and 400 µg/mL, respectively, the growth of S. aureus was almost completely inhibited within 24 h.

Structure Description of Compound 1
Single-crystal diffraction analysis indicates that compound 1 crystallizes in the Triclinic crystal system, P1 space group.As shown in Figure 1A, the asymmetric motif in its configuration includes two crystallographically independent Cd(II) ions, two carboxylic acid H 2 L ligands, and two molecules of bibp ligands.In the asymmetric structural unit, both Cd(II) ions are in a hexacoordination mode, with Cd1 coordinating and bonding with O1, O3#1, O4#1 and O7#1 (from the two H 2 L ligands) and N1 and N4#3 (from the same nitrogen-containing ligand), and Cd 2 coordinating and bonding with O2, O5, O6 and O8#1 (from the two H 2 L ligands) and N5 and N8#2 (from the same nitrogen-containing ligands), resulting in an irregular octahedral geometrical configuration, with the four oxygen atoms approximated to be considered co-planar and the nitrogen atoms in the axial position of the octahedron, where the Cd-O bonding distances are 2.222(10)-2.379(9)Å, the Cd-N bonding distances are 2.255(11)-2.371(9)Å, and the angles of N(1)-Cd(1)-N(4)# and N(5)-Cd(2)-N(8)#2 are 170.4• and 172.9 • , respectively (Table S1, ESI †).In the asymmetric structural unit, the two carboxyl groups of the two-molecule carboxylic acid H 2 L ligand adopt different coordination modes, and they are bonded in a bidentate chelating and a monodentate cis-trans bridging sum, respectively.In this complex, the carboxylic acid H 2 L ligand forms a 1D ring structure with a hole of 13.742 Å × 14.890 Å with Cd(II) atoms (Figure 1B), and this 1D ring is then followed by two molecules of nitrogen-containing ligand bibp connected by Cd(II) to form a 2D layer (Figure 1C).
In order to represent its framework composition more simply, we regard the Cd(II) ion as a six-connected node, and the carboxylic acid ligand H 2 L and the nitrogen-containing ligand bibp as two-connected linkers; then, this 2D layer structure can be simplified into the topology shown in Figure 1D.Further software analysis shows that the same 2D layers eventually form a 3D network structure by π-π stacking (Figure 1E).

Structure Description of Compound 2
Single-crystal diffraction analysis indicates that compound 2 crystallizes in the orthorhombic crystal system, Fdd2 space group.As exhibited in Figure 2A, the asymmetric motif in its configuration contains a crystallographically independent Ni(II) ion, a molecule of carboxylic acid H2L ligand, and a molecule of bib ligand.In the asymmetric structural unit, the Ni(II) ion is coordinately bonded to four O atoms from two molecules of the carboxylic acid ligand (O1, O2, O3#3, O4#3) and two N atoms from two molecules of the nitrogen-containing ligand (N2, N5#1), respectively, constituting a deformed octahedral geometrical configuration, with the three oxygen atoms and the one nitrogen atom approximately coplanar and the rest of the ligand atoms in axial positions,.The Ni-O bond distance is 2.045(3)-2.175(4)Å, the Ni-N bond distance is 2.016(5)-2.059(4)Å, the angle of N(2)-Ni(1)-N(5)#1 is 94.81°, and the angle of N(2)-Ni(1)-O(1) is 156.26°(Table S1, ESI †).In the asymmetric structural unit, both carboxyl groups of the carboxylic acid H2L ligand adopt a bidentate chelate coordination mode to participate in bonding.
In this polymer, the carboxylic acid H2L ligand and the nitrogen-containing bib ligand are connected by Ni(II) ions to form two 1D cyclic chains, and the two 1D chains are then connected by unsaturated sites on the Ni(II) ions to form a 2D lattice structure (Figure 2B).Due to the large pores of the constituent lattice, the three identical 2D layers are interspersed with each other, forming a triple-interspersed 2D layer with a pattern of 2D plus 2D to 2D (2D + 2D → 2D) (Figure 2C), which is a relatively common pattern of interspersing.

Structure Description of Compound 2
Single-crystal diffraction analysis indicates that compound 2 crystallizes in the orthorhombic crystal system, Fdd2 space group.As exhibited in Figure 2A, the asymmetric motif in its configuration contains a crystallographically independent Ni(II) ion, a molecule of carboxylic acid H 2 L ligand, and a molecule of bib ligand.In the asymmetric structural unit, the Ni(II) ion is coordinately bonded to four O atoms from two molecules of the carboxylic acid ligand (O1, O2, O3#3, O4#3) and two N atoms from two molecules of the nitrogen-containing ligand (N2, N5#1), respectively, constituting a deformed octahedral geometrical configuration, with the three oxygen atoms and the one nitrogen atom approximately coplanar and the rest of the ligand atoms in axial positions,.The Ni-O bond distance is 2.045(3)-2.175(4)Å, the Ni-N bond distance is 2.016(5)-2.059(4)Å, the angle of N(2)-Ni(1)-N(5)#1 is 94.81 • , and the angle of N(2)-Ni(1)-O(1) is 156.26 • (Table S1, ESI †).In the asymmetric structural unit, both carboxyl groups of the carboxylic acid H 2 L ligand adopt a bidentate chelate coordination mode to participate in bonding.
this compound, we further analyzed and found two helical chains in a separate 2D layer consisting of H2L ligand and bibp ligand with Ni(II) ions in the smallest repeating unit as [-Ni(L)2-Ni(bib)-] with a length of 29.947 Å, which were structurally diagrammed as shown in Figure 2E when viewed from the x-axial and y-axial directions.In this polymer, the carboxylic acid H 2 L ligand and the nitrogen-containing bib ligand are connected by Ni(II) ions to form two 1D cyclic chains, and the two 1D chains are then connected by unsaturated sites on the Ni(II) ions to form a 2D lattice structure (Figure 2B).Due to the large pores of the constituent lattice, the three identical 2D layers are interspersed with each other, forming a triple-interspersed 2D layer with a pattern of 2D plus 2D to 2D (2D + 2D → 2D) (Figure 2C), which is a relatively common pattern of interspersing.
We simplified the Ni(II) ion into a four-connected node, and the carboxylic acid ligand H 2 L and the nitrogen-containing ligand bib into two kinds of two-connected linkers; then, this 2D layer structure can be simplified into a topology as shown in Figure 2C (lower part).Careful analysis reveals that this triply interspersed 2D layer of the composition in turn forms a 3D network structure in an ABAB layer-by-layer stacking fashion (Figure 2D).In this compound, we further analyzed and found two helical chains in a separate 2D layer consisting of H 2 L ligand and bibp ligand with Ni(II) ions in the smallest repeating unit as [-Ni(L) 2 -Ni(bib)-] with a length of 29.947 Å, which were structurally diagrammed as shown in Figure 2E when viewed from the x-axial and y-axial directions.

PXRD and Thermogravimetric Analysis (TGA)
To test the purity of the samples, the PXRD spectra of the samples were tested at room temperature.As can be seen in Figure 3, the locations of the diffraction peaks in the powder XRD spectra of samples 1 and 2 are essentially the same as those of the XRD spectra simulated by single-crystal structure data, which proves that the resulting target product is a pure phase.To test the thermal stability of compounds 1 and 2, TGA experiments were carried out in a nitrogen atmosphere at a ramp rate of 10 • C/min from 20 to 800 • C. 1 was stable up to 340 • C and 2 was stable up to 330 • C (Figure 4).The subsequent processes involved the thermal decomposition of the ligands and the collapse of the frameworks, respectively.

PXRD and Thermogravimetric Analysis (TGA)
To test the purity of the samples, the PXRD spectra of the samples were tested at room temperature.As can be seen in Figure 3, the locations of the diffraction peaks in the powder XRD spectra of samples 1 and 2 are essentially the same as those of the XRD spectra simulated by single-crystal structure data, which proves that the resulting target product is a pure phase.
To test the thermal stability of compounds 1 and 2, TGA experiments were carried out in a nitrogen atmosphere at a ramp rate of 10 °C/min from 20 to 800 °C.Moreover, 1 was stable up to 340 °C and 2 was stable up to 330 °C (Figure 4).The subsequent processes involved the thermal decomposition of the ligands and the collapse of the frameworks, respectively.

Culture of Bacteria and Fungi
In the experiment, the pre-configured PDB medium, LB medium and experimental vessels were autoclaved and transferred to an ultra-clean bench, after which the selected Escherichia coli (E.coli, BNCC 336902), Staphylococcus aureus (S. aureus, BNCC 330041), and Candida albicans (C.albicans, ATCC 10231) were inoculated into the culture solution and placed on the shaking table at 37 °C for overnight incubation.The culture was incubated overnight at 37 °C in a shaker.Finally, the inoculated bacteria were diluted 100-fold with culture medium.

Circle of Inhibition Test
In the circle of inhibition experiment, moderate amounts of S. aureus and E. coli, which use the culture medium diluted to 10 7 CFU/mL, were uniformly applied to the LB medium, and C. albicans was applied to the PDB medium, so that it was completely absorbed.Immediately thereafter, a round paper sheet with a diameter of 6 mm was placed in an aqueous solution of either 1 mg/mL and 5 mg/mL of the compounds.Ultrasonic shaking was performed to make the complexes uniformly attach to the surface of the small paper sheet, and the sheet was then placed on the surface of the culture medium.Blank and carboxylic acid ligand control experiments were conducted using the same method.After that, the samples were put into a constant temperature incubator and incubated at 37 °C for 24 h, during which the inhibition was observed and the diameter of the inhibition

Culture of Bacteria and Fungi
In the experiment, the pre-configured PDB medium, LB medium and experimental vessels were autoclaved and transferred to an ultra-clean bench, after which the selected Escherichia coli (E.coli, BNCC 336902), Staphylococcus aureus (S. aureus, BNCC 330041), and Candida albicans (C.albicans, ATCC 10231) were inoculated into the culture solution and placed on the shaking table at 37 • C for overnight incubation.The culture was incubated overnight at 37 • C in a shaker.Finally, the inoculated bacteria were diluted 100-fold with culture medium.

Circle of Inhibition Test
In the circle of inhibition experiment, moderate amounts of S. aureus and E. coli, which use the culture medium diluted to 10 7 CFU/mL, were uniformly applied to the LB medium, and C. albicans was applied to the PDB medium, so that it was completely absorbed.Immediately thereafter, a round paper sheet with a diameter of 6 mm was placed in an aqueous solution of either 1 mg/mL and 5 mg/mL of the compounds.Ultrasonic shaking was performed to make the complexes uniformly attach to the surface of the small paper sheet, and the sheet was then placed on the surface of the culture medium.Blank and carboxylic acid ligand control experiments were conducted using the same method.After that, the samples were put into a constant temperature incubator and incubated at 37 • C for 24 h, during which the inhibition was observed and the diameter of the inhibition circle was recorded.In order to ensure the rigor of the experiment, we repeated the bacteriostatic zone experiment three times.
Figure 5 shows that compounds 1 and 2 have different inhibitory effects on E. coli, S. aureus and C. albicans.A ratio of 5 mg/mL of compounds 1 and 2 showed a circle of inhibition diameter of 20 mm and 15 mm for S. aureus, and 11 mm and 9 mm for E. coli.For C. albicans, 5 mg/mL of compounds 1 and 2 showed a circle of inhibition of 10 mm and 11 mm.The average data of the three repeated experiments were summarized in the histogram of circle of inhibition diameters for E. coli, S. aureus and C. albicans plotted for each of the different compounds (Figure 6).

Growth Curve Experiment
The number concentration in the bacterial solution was measured with an enzyme marker at intervals.The survival of bacteria in the bacterial solution can be judged by the change in OD value.The growth curve of different concentrations of compounds 1 and 2 against S. aureus was plotted based on the average data of three repeated experiments (Figure 7).
The overnight bacterial solution was diluted into LB and PDB medium with different concentrations of compounds, and 200 μL of it was put into 96-well plates.An enzyme

Growth Curve Experiment
The number concentration in the bacterial solution was measured with an enzyme marker at intervals.The survival of bacteria in the bacterial solution can be judged by the change in OD value.The growth curve of different concentrations of compounds 1 and 2 against S. aureus was plotted based on the average data of three repeated experiments (Figure 7).
The overnight bacterial solution was diluted into LB and PDB medium with different concentrations of compounds, and 200 μL of it was put into 96-well plates.An enzyme

Growth Curve Experiment
The number concentration in the bacterial solution was measured with an enzyme marker at intervals.The survival of bacteria in the bacterial solution can be judged by the change in OD value.The growth curve of different concentrations of compounds 1 and 2 against S. aureus was plotted based on the average data of three repeated experiments (Figure 7).bacterial solution with a high concentration of the compound formed a sharp contrast with the blank bacterial solution; the solution was more clarified, indicating that the concentration of the bacterial solution did not grow, which confirmed that compounds 1 and 2 had good antimicrobial properties against S. aureus.At the same time, comparative experiments were carried out.For compound 1, the growth curves of S. aureus were tested in blank, H2L, bibp, Cd(NO3)2, and compound against S. aureus when the concentration was 500 μg/mL.For compound 2, the growth curves of S. aureus were similarly tested in blank, H2L, bib, Ni(NO3)2 and compound when the concentration was 400 μg/mL.As shown in Figure 9, it was observed that the concentration of the bacterial solution containing carboxylic acid ligands, nitrogen-containing The overnight bacterial solution was diluted into LB and PDB medium with different concentrations of compounds, and 200 µL of it was put into 96-well plates.An enzyme marker was used to determine the initial concentration of the bacterial solution.The bacterial solution was incubated in a shaker at 37 • C, and the absorbance was measured at 600 nm every 3 h with an enzyme labeler to determine the 24 h growth curve of the strain.In order to ensure the rigor of the experiment, we repeated the growth curve experiment three times.
The growth curves in Figure 7 show that the bacterial solution of the blank control group grew exponentially.For compounds 1 and 2, the inhibitory effect was gradually enhanced with the gradient increase of the compound concentration, and when the concentration of the compounds reached 500 µg/mL and 400 µg/mL, respectively, the concentration of S. aureus liquid was no longer growing, and it was determined that it had been completely inhibited.According to the bacterial solution at different moments shown in Figure 8, with the change in time, the bacterial solution without the addition of the compound was gradually turbid; the bacterial solution with a high concentration of the compound formed a sharp contrast with the blank bacterial solution; the solution was more clarified, indicating that the concentration of the bacterial solution did not grow, which confirmed that compounds 1 and 2 had good antimicrobial properties against S. aureus.
Molecules 2024, 29, x FOR PEER REVIEW 7 of 11 marker was used to determine the initial concentration of the bacterial solution.The bacterial solution was incubated in a shaker at 37 °C, and the absorbance was measured at 600 nm every 3 h with an enzyme labeler to determine the 24 h growth curve of the strain.
In order to ensure the rigor of the experiment, we repeated the growth curve experiment three times.The growth curves in Figure 7 show that the bacterial solution of the blank control group grew exponentially.For compounds 1 and 2, the inhibitory effect was gradually enhanced with the gradient increase of the compound concentration, and when the concentration of the compounds reached 500 μg/mL and 400 μg/mL, respectively, the concentration of S. aureus liquid was no longer growing, and it was determined that it had been completely inhibited.According to the bacterial solution at different moments shown in Figure 8, with the change in time, the bacterial solution without the addition of the compound was gradually turbid; the bacterial solution with a high concentration of the compound formed a sharp contrast with the blank bacterial solution; the solution was more clarified, indicating that the concentration of the bacterial solution did not grow, which confirmed that compounds 1 and 2 had good antimicrobial properties against S. aureus.At the same time, comparative experiments were carried out.For compound 1, the growth curves of S. aureus were tested in blank, H2L, bibp, Cd(NO3)2, and compound against S. aureus when the concentration was 500 μg/mL.For compound 2, the growth curves of S. aureus were similarly tested in blank, H2L, bib, Ni(NO3)2 and compound when the concentration was 400 μg/mL.As shown in Figure 9, it was observed that the concentration of the bacterial solution containing carboxylic acid ligands, nitrogen-containing At the same time, comparative experiments were carried out.For compound 1, the growth curves of S. aureus were tested in blank, H 2 L, bibp, Cd(NO 3 ) 2 , and compound against S. aureus when the concentration was 500 µg/mL.For compound 2, the growth curves of S. aureus were similarly tested in blank, H 2 L, bib, Ni(NO 3 ) 2 and compound when the concentration was 400 µg/mL.As shown in Figure 9, it was observed that the concentration of the bacterial solution containing carboxylic acid ligands, nitrogen-containing ligands, and metal salts increased exponentially with increasing time, while the concentration of the bacterial solution containing the compounds remained unchanged, indicating that it was the compounds that inhibited the growth of the bacterial solution.
Molecules 2024, 29, x FOR PEER REVIEW 8 of 11 ligands, and metal salts increased exponentially with increasing time, while the concentration of the bacterial solution containing the compounds remained unchanged, indicating that it was the compounds that inhibited the growth of the bacterial solution.

Materials and Methods
The ligands H2L, bibp, and bib were purchased from Jinan Henghua SCI.& TEC.Co. LTD (Figure 10).(in Jinan, Shandong Province, China).Other raw materials were of analytical level and used without further purification.Powder X-ray diffraction (PXRD) data were collected on a D2 Phaser A26-X1 XRD diffraction meter.IR spectra (4000-400 CM −1 ) were obtained from KBr particles with an FT-IR Nexus spectrometer.Element analysis was performed on a Perkin-Elmer 240 C analyzer.The thermostat analysis (TGA) curve was determined at a heating rate of 10 °C/min on a Perkin-Elmer TG-7 thermal analyzer.A Spectra Max Plus 384 microplate reader was used to determine OD600 of the bacterial liquid.

Materials and Methods
The ligands H 2 L, bibp, and bib were purchased from Jinan Henghua SCI.& TEC.Co., Ltd.(Figure 10) (in Jinan, Shandong Province, China).Other raw materials were of analytical level and used without further purification.Powder X-ray diffraction (PXRD) data were collected on a D2 Phaser A26-X1 XRD diffraction meter.IR spectra (4000-400 CM −1 ) were obtained from KBr particles with an FT-IR Nexus spectrometer.Element analysis was performed on a Perkin-Elmer 240 C analyzer.The thermostat analysis (TGA) curve was determined at a heating rate of 10 • C/min on a Perkin-Elmer TG-7 thermal analyzer.A Spectra Max Plus 384 microplate reader was used to determine OD600 of the bacterial liquid.

Materials and Methods
The ligands H2L, bibp, and bib were purchased from Jinan Henghua SCI.& TEC.Co. LTD (Figure 10).(in Jinan, Shandong Province, China).Other raw materials were of analytical level and used without further purification.Powder X-ray diffraction (PXRD) data were collected on a D2 Phaser A26-X1 XRD diffraction meter.IR spectra (4000-400 CM −1 ) were obtained from KBr particles with an FT-IR Nexus spectrometer.Element analysis was performed on a Perkin-Elmer 240 C analyzer.The thermostat analysis (TGA) curve was determined at a heating rate of 10 °C/min on a Perkin-Elmer TG-7 thermal analyzer.A Spectra Max Plus 384 microplate reader was used to determine OD600 of the bacterial liquid.

X-ray Crystallography
The data on the crystal structure of compounds 1 and 2 were collected at room temperature using a Bruker SMART APEX II CCD X-ray single-crystal diffractometer from Bruker, Germany, with a radiation source of Mo Kα rays (λ = 0.071073 nm).The diffraction data were reduced and refined using the SAINT program, the crystal structure was solved by direct method from the Olex program, the hydrogen atoms were determined by theoretical hydrogenation, and all non-hydrogen atom coordinates and their anisotropic thermal parameters were found using the full-matrix least-squares method.The resulting crystal information for compound 1 and 2 is shown in Table 1.

Conclusions
In this article, two new coordination polymers were synthesized under solvent thermal and hydrothermal conditions, and their antibacterial properties were studied.Antibacterial performance experiments have shown that compounds 1 and 2 have certain selectivity in their antibacterial properties and have good antibacterial properties against S. aureus, but their antibacterial effects on other microorganisms are not as expected.As the concentration of each compound increases, the inhibitory effect gradually strengthens, and when the concentration reaches 500 µg/mL and 400 µg/mL for compound 1 and 2, respectively, the concentration of the S. aureus solution no longer increases and is completely inhibited.Due to the excellent stability of the coordinating polymer itself, it exhibits excellent antibacterial effects within 24 h.The active site of the compound can destroy the cell membrane to a certain extent after binding with S. aureus, thus accelerating the death of the bacteria.

Molecules 2024 , 11 Figure 5
Figure 5 shows that compounds 1 and 2 have different inhibitory effects on E. coli, S. aureus and C. albicans.A ratio of 5 mg/mL of compounds 1 and 2 showed a circle of inhibition diameter of 20 mm and 15 mm for S. aureus, and 11 mm and 9 mm for E. coli.For C. albicans, 5 mg/mL of compounds 1 and 2 showed a circle of inhibition of 10 mm and 11 mm.The average data of the three repeated experiments were summarized in the histogram of circle of inhibition diameters for E. coli, S. aureus and C. albicans plotted for each of the different compounds (Figure 6).

Figure 5 .
Figure 5. Inhibition zone of compound 1 and 2 against S. aureus, E. coli and C. albicans (top to bottom).

Figure 6 .
Figure 6.Histogram of the diameter of the circle of inhibition of compound 1 and 2 against E. coli, S. aureus and C. albicans.

Figure 5 . 11 Figure 5
Figure 5. Inhibition zone of compound 1 and 2 against S. aureus, E. coli and C. albicans (top to bottom).

Figure 5 .
Figure 5. Inhibition zone of compound 1 and 2 against S. aureus, E. coli and C. albicans (top to bottom).

Figure 6 .
Figure 6.Histogram of the diameter of the circle of inhibition of compound 1 and 2 against E. coli, S. aureus and C. albicans.

Figure 6 .
Figure 6.Histogram of the diameter of the circle of inhibition of compound 1 and 2 against E. coli, S. aureus and C. albicans.

Figure 8 .
Figure 8. Changes in the bacteriostatic effect of compound 1 and 2 on S. aureus over 24 h.

Figure 8 .
Figure 8. Changes in the bacteriostatic effect of compound 1 and 2 on S. aureus over 24 h.

Figure 8 .
Figure 8. Changes in the bacteriostatic effect of compound 1 and 2 on S. aureus over 24 h.

Figure 9 .
Figure 9. Growth curves of S. aureus by carboxylic acid ligands, nitrogenous ligands, metal salts, and compounds.

Figure 9 .
Figure 9. Growth curves of S. aureus by carboxylic acid ligands, nitrogenous ligands, metal salts, and compounds.

Molecules 2024 ,
29, x FOR PEER REVIEW 8 of 11 ligands, and metal salts increased exponentially with increasing time, while the concentration of the bacterial solution containing the compounds remained unchanged, indicating that it was the compounds that inhibited the growth of the bacterial solution.

Figure 9 .
Figure 9. Growth curves of S. aureus by carboxylic acid ligands, nitrogenous ligands, metal salts, and compounds.

Table 1 .
Crystal and structure refinement data for compound 1 and 2.