Rare Earth Extraction from Phosphogypsum by Aspergillus niger Culture Broth

The extraction of rare earth elements (REEs) from phosphogypsum (PG) is of great significance for the effective utilization of rare earth resources and enhancing the resource value of PG waste residues. This study used Aspergillus niger (A. niger) fungal culture filtrate as a leaching agent to investigate the behavior of extracting REEs from PG through direct and indirect contact methods. According to the ICP-MS results, direct leaching at a temperature of 30 °C, shaking speed of 150 rpm, and a solid–liquid ratio of 2:1, achieved an extraction rate of 74% for REEs, with the main elements being yttrium (Y), lanthanum (La), cerium (Ce), and neodymium (Nd). Under the same conditions, the extraction rate of REEs from phosphogypsum using an A. niger culture filtrate was 63.3% higher than that using the simulated organic acid-mixed solution prepared with the main organic acid components in the A. niger leachate. Moreover, the morphological changes observed in A. niger before and after leaching further suggest the direct involvement of A. niger’s metabolic process in the extraction of REEs. When compared to using organic acids, A. niger culture filtrate exhibits higher leaching efficiency for extracting REEs from PG. Additionally, using A. niger culture filtrate is a more environmentally friendly method with the potential for industrial-scale applications than using inorganic acids for the leaching of REEs from PG.


Introduction
Phosphogypsum (PG) is a kind of industrial solid waste produced in the manufacturing of phosphate fertilizer and phosphoric acid and is generally gray or yellow.At a global level, the massive accumulation of PG has led to significant environmental issues, the occupation of large areas, and negative impacts on water, soil, the atmosphere, and organisms [1].According to a previous study, 4-5 tons of PG are produced for every 1 ton of phosphoric acid (calculated by 100% P 2 O 5 ) [2].
China is the world's largest producer of PG, with a current stockpile of nearly 400 million tons, which is increasing at the rate of 50 million tons/a.In the Earth's crust, rare earth elements (REEs) mainly occur in rare earth minerals and eluvial minerals of the weathering crust [3].Because the ionic radius of RREs (0.848-0.106 nm) is close to that of Ca 2+ (0.106 nm), a considerable portion of REEs exist in the crystal structure of apatite in an isomorphic form [4]. Globally, the reserves of phosphate rock amount to 100 billion tons, of which about 50 million tons are associated with rare earth elements, with an average of 0.05% [5].With the increasing shortage of rare earth resources, the trace rare earth associated with phosphate rock as a potential rare earth resource has attracted considerable attention.Approximately 90% of the world's phosphoric acid is produced by a wet process using sulfuric acid to decompose phosphate rock; the most common dihydrate phosphoric acid process results in 70-85% of the REEs in phosphate rock being transferred to PG, whereas semi-hydrate phosphoric acid can transfer 95% of the REEs into PG [6].
It is estimated that each year, 250 million tons of phosphate ore are used in the production of phosphoric acid, and about 100,000 tons of REEs end up in PG [4].In this sense, the recovery of rare earth from PG is a potential solution to dwindling global rare earth resources [5].The extraction of REEs from PG generally uses inorganic acid leaching [7][8][9], applying sulfuric acid, hydrochloric acid, and nitric acid.Although the rare earth recovery rate is 80-90% and above, the acidity of PG is largely increased, resulting in higher disposal costs and environmental issues.
Biological hydrometallurgy is generally considered an environmentally friendly alternative to traditional chemical leaching methods for the extraction of low-grade rare earth minerals, with low investment and low energy consumption [10].Bioleaching can recover some valuable elements, using microorganisms to reduce waste toxicity.Studies have shown that the microbial leaching of rare earth resources creates favorable conditions for the migration of rare earth elements from solid into solution.This approach can save costs [11], reduce environmental pollution, and largely diminish resource waste.
The use of fungi in the bioleaching of REEs has, so far, scarcely been investigated.It has been reported that A. niger has been used to leach metallic elements, such as copper, zinc, uranium, manganese, and aluminum, from various substances for more than 40 years [12][13][14].In this context, this paper used A. niger under different conditions and invested its leaching efficiency for rare earth elements from PG.In this process, the fungal spores, acidity, and metal complexing are supposed to be the main factors.The biomass and pH of A. niger in a pure culture were measured before bioleaching, and A. niger morphology was investigated before and after bioleaching, using a scanning electron microscope (SEM).The internal structure of A. niger cells and the distribution of rare earth elements before and after bioleaching were studied by transmission electron microscopy (TEM).

An Overview of the Phosphogypsum Sample
According to the XRF analysis, the main components of PG were oxides, with the following mass percentage concentrations (±3%): SO 3 (50.73wt %), CaO (37.73 wt %), SiO 2 (4.97 wt %), P 2 O 5 (0.91 wt %), Al 2 O 3 (0.75 wt %), and Fe 2 O 3 (0.5 wt %); F accounted for 3.96 wt %.The most abundant metals were Ca, Ba, Cr, Cu, Fe, K, and Mg.The gypsum (calcium sulfate) in phosphogypsum exists in the form of dihydrate calcium sulfate (CaSO 4 •2H 2 O) crystals.According to the analysis results of the ICP-MS, the following REEs (ppm) were recovered with an error of ±5%: Y (25.24 wt %), Ce (13.55 wt %), Nd (6.45 wt %), La (6.34 wt %), Gd (4.31 wt %), Sm (3.52 wt %), and Dy (3.49 wt %).The total rare earth element content of PG in the Xifeng phosphate mining area studied reached 70.04 ppm.It is the result of the low rare earth content in this phosphate rock.Due to the low content of rare earth elements, it is speculated that rare earth elements exist in a homologous form within the dihydrate calcium sulfate crystals.

Pure Biological Culture
Prior to microbial leaching, the activity of A. niger was investigated.According to the different microbial properties and culture conditions, the growth state of A. niger has a certain impact on the overall process.To reduce errors, it is therefore necessary to culture pure A. niger under the same conditions as those of the biological leaching and to determine the fungal biomass and pH value of the culture medium within 7 days.A. niger spores are then dispersed in the medium on a shaking table, forming one macro agglomerated ball [15].In previous studies, there was little or no explanation of how the A. niger used for metal ion leaching exerts its metabolic and morphological effects.As seen in Figure 1, the growth of A. niger pellets changed over time, and its biomass grew to 1.15 g/L on day 3, followed by a decrease in biomass, which may be due to the influence of metabolites produced by the microorganisms (organic acid, ferricarriers, and extracellular enzymes, among others), which, to some extent, inhibited the growth of A. niger.During culturing, the pH value of the medium decreased from 5.48 to 3.81 on the second day; the logarithmic growth period of A. niger was 2-4 days [16].On the third day, the pH value further decreased to 2.55, when A. niger produced the highest amounts of organic acids [17].After that, the pH value increased continuously, indicating the end of the active growth period of A. niger.The increase in the pH value in the culture medium might be the result of the lysis of cell walls and the release of intracellular metabolites and alkaline buffering properties.
spores are then dispersed in the medium on a shaking table, forming one macro agglomerated ball [15].In previous studies, there was little or no explanation of how the A. niger used for metal ion leaching exerts its metabolic and morphological effects.As seen in Figure 1, the growth of A. niger pellets changed over time, and its biomass grew to 1.15 g/L on day 3, followed by a decrease in biomass, which may be due to the influence of metabolites produced by the microorganisms (organic acid, ferricarriers, and extracellular enzymes, among others), which, to some extent, inhibited the growth of A. niger.During culturing, the pH value of the medium decreased from 5.48 to 3.81 on the second day; the logarithmic growth period of A. niger was 2-4 days [16].On the third day, the pH value further decreased to 2.55, when A. niger produced the highest amounts of organic acids [17].After that, the pH value increased continuously, indicating the end of the active growth period of A. niger.The increase in the pH value in the culture medium might be the result of the lysis of cell walls and the release of intracellular metabolites and alkaline buffering properties.

Effects of Direct and Indirect Methods on REEs and pH Value in A. niger Leaching Process
The leaching of REEs by A. niger by direct and indirect contact methods and their pH changes in fermentation broth were showed in Figure 2. As shown in Figure 2a, the leaching rate of rare earth elements under the two methods reached the highest value on the third day.The leaching rate of rare earth elements under the indirect contact method was as high as 44.24%, which was 13.52% higher than that under direct contact method.As can be seen from Figure 2b, there is a negative correlation between the leaching rate of rare earth elements and pH value in the whole leaching process, that is, the higher the leaching rate of rare earth elements, the lower the pH value of the fermentation liquid, which is consistent with the previous report [18].This may be because microorganisms consume nutrients in the culture medium and produce metabolites in the growth process.Organic acids are the main reason affecting the decrease in pH value of the fermentation liquid, and low acidity can promote the chemical bond of PG to be weaker and easier to break.As shown in Figure 2b, the control experiment used pure-culture A. niger fermentation liquid, therefore no rare earth element leaching occurred.

Effects of Direct and Indirect Methods on REEs and pH Value in A. niger Leaching Process
The leaching of REEs by A. niger by direct and indirect contact methods and their pH changes in fermentation broth were showed in Figure 2. As shown in Figure 2a, the leaching rate of rare earth elements under the two methods reached the highest value on the third day.The leaching rate of rare earth elements under the indirect contact method was as high as 44.24%, which was 13.52% higher than that under direct contact method.As can be seen from Figure 2b, there is a negative correlation between the leaching rate of rare earth elements and pH value in the whole leaching process, that is, the higher the leaching rate of rare earth elements, the lower the pH value of the fermentation liquid, which is consistent with the previous report [18].This may be because microorganisms consume nutrients in the culture medium and produce metabolites in the growth process.Organic acids are the main reason affecting the decrease in pH value of the fermentation liquid, and low acidity can promote the chemical bond of PG to be weaker and easier to break.As shown in Figure 2b, the control experiment used pure-culture A. niger fermentation liquid, therefore no rare earth element leaching occurred.
In the direct contact method, the distribution of REEs consists of two parts, the total leaching rate of the REEs in the fermentation liquid and A. niger strain adsorption of rare earth elements.The leached A. niger strain (2 g, dry weight) was ashified in a hightemperature furnace (550 • C, 3 h), and then high-grade pure nitric acid (5 mL) was added to the ashes for digestion; with a constant volume of 50 mL, the REEs were detected by ICP-MS.The results showed that the mycelia of A. niger were enriched by 43.69% REEs.Combined with the REEs leached into the fermentation liquid, the total leaching rate of rare earth elements was up to 74%, obviously about two times higher than that in the indirect contact method.According to previous studies, as A. niger strains are directly involved in leaching in the direct contact method, rare earth elements will be adsorbed to A. niger cells or adhere to their surfaces, forming stable complexes with carboxyl or phosphoric functional groups on the surface [19,20].A. niger strains and their metabolites both play an important role in the leaching process of REEs. Figure 3 shows the different forms of the two methods in the leaching process.Therefore, the direct method is a better method for extracting trace rare earth elements from phosphogypsum with an A. niger culture solution.In the direct contact method, the distribution of REEs consists of two parts, the total leaching rate of the REEs in the fermentation liquid and A. niger strain adsorption of rare earth elements.The leached A. niger strain (2 g, dry weight) was ashified in a high-temperature furnace (550 °C, 3 h), and then high-grade pure nitric acid (5 mL) was added to the ashes for digestion; with a constant volume of 50 mL, the REEs were detected by ICP-MS.The results showed that the mycelia of A. niger were enriched by 43.69% REEs.Combined with the REEs leached into the fermentation liquid, the total leaching rate of rare earth elements was up to 74%, obviously about two times higher than that in the indirect contact method.According to previous studies, as A. niger strains are directly involved in leaching in the direct contact method, rare earth elements will be adsorbed to A. niger cells or adhere to their surfaces, forming stable complexes with carboxyl or phosphoric functional groups on the surface [19,20].A. niger strains and their metabolites both play an important role in the leaching process of REEs. Figure 3 shows the different forms of the two methods in the leaching process.Therefore, the direct method is a better method for extracting trace rare earth elements from phosphogypsum with an A. niger culture solution.

Organic Acid Detection and Leaching Mechanism
The presence of organic acids was an important feature of metal leaching.The types and contents of organic acids produced by different microorganisms varied and changed with the culture conditions.Table 1 lists the different acids in the pure culture of A. niger  In the direct contact method, the distribution of REEs consists of two parts, the total leaching rate of the REEs in the fermentation liquid and A. niger strain adsorption of rare earth elements.The leached A. niger strain (2 g, dry weight) was ashified in a high-temperature furnace (550 °C, 3 h), and then high-grade pure nitric acid (5 mL) was added to the ashes for digestion; with a constant volume of 50 mL, the REEs were detected by ICP-MS.The results showed that the mycelia of A. niger were enriched by 43.69% REEs.Combined with the REEs leached into the fermentation liquid, the total leaching rate of rare earth elements was up to 74%, obviously about two times higher than that in the indirect contact method.According to previous studies, as A. niger strains are directly involved in leaching in the direct contact method, rare earth elements will be adsorbed to A. niger cells or adhere to their surfaces, forming stable complexes with carboxyl or phosphoric functional groups on the surface [19,20].A. niger strains and their metabolites both play an important role in the leaching process of REEs. Figure 3 shows the different forms of the two methods in the leaching process.Therefore, the direct method is a better method for extracting trace rare earth elements from phosphogypsum with an A. niger culture solution.

Organic Acid Detection and Leaching Mechanism
The presence of organic acids was an important feature of metal leaching.The types and contents of organic acids produced by different microorganisms varied and changed with the culture conditions.Table 1 lists the different acids in the pure culture of A. niger in this study and the organic acid content in the triangle flask after leaching.According to

Organic Acid Detection and Leaching Mechanism
The presence of organic acids was an important feature of metal leaching.The types and contents of organic acids produced by different microorganisms varied and changed with the culture conditions.Table 1 lists the different acids in the pure culture of A. niger in this study and the organic acid content in the triangle flask after leaching.According to these findings, A. niger mainly produced citrate, gluconic acid, oxalate, tartaric acid, and ketoglutaric acid during growth, with concentrations (error of ±5%) of 983.089 mg/L, 134.140 mg/L, 130.471 mg/L, 56.865 mg/L, and 32.787 mg/L, respectively.To prove the biological role of fungi, not just organic acids, and to determine whether the bioleaching of metal ions occurs through dissolution and chelation of organic acids, the mixed acids prepared from commercial organic acids were compared to a biological fermentation liquid.The mixed acid solution had the following composition: 1000 mg/L of citric acid, 150 mg/L of tartaric acid, 100 mg/L of ketoglutaric acid, 100 mg/L of gluconic acid, 200 mg/L of mixed acids; the bio-fermentation liquid was added at the same amount as for the PG solid samples at a solid-liquid ratio of 2:1, a temperature of 30 • C, and an oscillation rate of 150 rpm on a shaking table.The contents of rare earth elements in the supernatant of the leaching solution were determined by ICP-MS after 10 days of co-culturing.As shown in Table 2, the total amount of REEs leaching by biological method is 5735.7 µg/L more than that by organic acid method 63.3%, in which heavy REEs are increased by 33.14% and light REEs are increased by 44.59%, indicating that A. niger promotes the leaching of REEs from PG.As shown in Figure 4, the leaching of rare earth elements in the A. niger fermentation liquid was more pronounced than that of the mixed acid liquid.The rare earth elements are usually divided into two types: ceric rare earth elements, La-Eu, also known as light rare earth elements (LREEs), and yttrium rare earth elements, Gd-Lu+Y+Sc, also known as heavy rare earth elements (HREEs) [21].In addition, in the mixed acid, the amount of heavy REEs was higher than that of light REEs, whereas in the A. niger fermentation liquid, the opposite pattern was observed.This indicates a certain selectivity of the A. niger fermentation liquid.

Morphological Changes in the A. niger Mycelium
In the microbial leaching of PG, various mechanisms were at play, such as acid solution, surface complexation, ion exchange, and redox reactions [22], resulting in the accumulation of refractory material in the acid solution [23].Surface complexation was mainly related to the composition of the microbial surface, which was largely composed of protein polysaccharides and lipids.There were various functional groups on the surface, such as hydroxyl amino and carboxyl groups, as well as some inorganic elements, such as O,  In the microbial leaching of PG, various mechanisms were at play, such as acid solution, surface complexation, ion exchange, and redox reactions [22], resulting in the accumu-lation of refractory material in the acid solution [23].Surface complexation was mainly related to the composition of the microbial surface, which was largely composed of protein polysaccharides and lipids.There were various functional groups on the surface, such as hydroxyl amino and carboxyl groups, as well as some inorganic elements, such as O, N, P, and S, which could coordinate with metal ions as coordination atoms.In A. niger, in the production of organic acid, siderophores also participated in the leaching process [24], and existing studies showed that iron carriers, generally divided into hydroxyl oxime acid and catechins, usually formed complexes with octahedral.During leaching, the complex coordination depended on the amounts of organic acids in solution, the stability of the chelate, and the functional groups on the microbial surface.
In order to study the morphology of A. niger and the distribution of REEs adsorbed before and after leaching, the morphology of A. niger bodies in the direct contact method was scanned.As seen in Figure 5a,b, prior to the leaching experiment, the mycelium surface was smooth.Although the shape of the mycelia was not changed after leaching (Figure 5c), granular substances could be observed on the surface.As seen in Figure 5d, the PG and A. niger mycelium were intertwined, and the mycelium surface was severely eroded.Figure 6 shows that a large number of REEs are enriched on the surface of A. niger bodies.

Changes in A. niger Cells
As shown in Figure 7a, before extraction, the A. niger cell structure was intact and clear, with an obvious cell wall, nucleus, nucleolus, mitochondria, and vacuoles, etc.As shown in Figure 7b, after extraction, although the black mold cells of A. niger remained intact and the cell wall was clearly visible, the organelles aggregated together.This was indicative of cell apoptosis, and similar findings had also been reported by other researchers [25].One possible reason was that toxic substances in phosphogypsum may have damaged A. niger cells, leading to a decrease in cell activity and a reduction in acid production.Another possible reason was that cells maintained their metabolism by changing their morphology and specific surface area to resist the erosion of rare earth elements or heavy metals until cell apoptosis [26,27].As shown in Figure 7a, before extraction, the A. niger cell structure was intact and clear, with an obvious cell wall, nucleus, nucleolus, mitochondria, and vacuoles, etc.As shown in Figure 7b, after extraction, although the black mold cells of A. niger remained intact and the cell wall was clearly visible, the organelles aggregated together.This was indicative of cell apoptosis, and similar findings had also been reported by other researchers [25].One possible reason was that toxic substances in phosphogypsum may have damaged A. niger cells, leading to a decrease in cell activity and a reduction in acid production.Another possible reason was that cells maintained their metabolism by changing their morphology and specific surface area to resist the erosion of rare earth elements or heavy metals until cell apoptosis [26,27].

Phosphogypsum Collection
The PG samples were collected from the Xifeng phosphate mining area, China.To avoid the uneven distribution of minerals, the samples were dried and ground with an agate mortar to obtain PG particles with a particle size of less than 150 µm.In order to measure the pH value of PG, 1 g of the PG sample was weighed in a 250 mL conical flask, and 50 mL of ultrapure water was added into it, followed by shaking on a shaking table for 24 h at 250 rpm; the obtained pH was 4.55.To quantify REEs in PG, 0.5 g of PG was placed in a Teflon beaker with 2 mL of ultrapure water.Subsequently, 10 mL of high-grade pure nitric acid was added, and the mixture was slowly heated on a heating plate to evaporate the acid until it was nearly dry.After cooling slightly, 10 mL of nitric acid solution (1 + 1) was added and dissolved by heating.After cooling to room temperature, ultrapure water was used to reach a volume of 50 mL, and the mixture was filtered and set aside.For the analysis of REEs, a rare earth multi-element calibration standard solution was used to generate external standard curves, and the same method was used to prepare standard controls to evaluate the accuracy of the analysis data [28].The concentrations of total REEs were determined by inductively coupled plasma mass spectrometry (ICP-MS, Perki-nElmer, Waltham, MA, USA, NexION2000; RSD < 3%).The settings of the ICP-MS were as follows: power, 1.5 kW; plasma gas flow, 20.0 L/min; auxiliary gas flow, 2 L/min; pump speed, 35 rpm; cleaning time, 25 s.An X-ray fluorescence analyzer (XRF) was used to detect the major elements in PG.

Microorganisms and Growth Conditions
The Aspergillus strain was provided by Nantong Kaiheng Biotechnology Develop-

Phosphogypsum Collection
The PG samples were collected from the Xifeng phosphate mining area, China.To avoid the uneven distribution of minerals, the samples were dried and ground with an agate mortar to obtain PG particles with a particle size of less than 150 µm.In order to measure the pH value of PG, 1 g of the PG sample was weighed in a 250 mL conical flask, and 50 mL of ultrapure water was added into it, followed by shaking on a shaking table for 24 h at 250 rpm; the obtained pH was 4.55.To quantify REEs in PG, 0.5 g of PG was placed in a Teflon beaker with 2 mL of ultrapure water.Subsequently, 10 mL of highgrade pure nitric acid was added, and the mixture was slowly heated on a heating plate to evaporate the acid until it was nearly dry.After cooling slightly, 10 mL of nitric acid solution (1 + 1) was added and dissolved by heating.After cooling to room temperature, ultrapure water was used to reach a volume of 50 mL, and the mixture was filtered and set aside.For the analysis of REEs, a rare earth multi-element calibration standard solution was used to generate external standard curves, and the same method was used to prepare standard controls to evaluate the accuracy of the analysis data [28].The concentrations of total REEs were determined by inductively coupled plasma mass spectrometry (ICP-MS, PerkinElmer, Waltham, MA, USA, NexION2000; RSD < 3%).The settings of the ICP-MS were as follows: power, 1.5 kW; plasma gas flow, 20.0 L/min; auxiliary gas flow, 2 L/min; pump speed, (1) The fungus A. niger exists widely in nature and is easy to culture.Although glucose is used as the substrate for A. niger culture in this study, cheap organic matter can also be used for culture to reduce the output cost.(2) In the direct contact method, the maximum leaching rate under the optimum leaching condition is 74%, The amount of leached light rare earth elements was higher than that of heavy rare earth elements.(3) Several organic acids were found in the A. niger fermentation broth, such as citric acid, gluconic acid, oxalic acid, etc., which achieved the leaching of rare earth elements through dissolution and chelation.The metabolic process of A. niger cells significantly improved the leaching rate of rare earth elements.(4) Based on the SEM-EDS and TEM-EDS results, the surface and lumen of the A. niger cells contained large amounts of rare earth elements after leaching.
REEs leaching using A. niger is an environmentally friendly approach and a viable alternative to the use of mixed acid solutions.This approach can be used in the large-scale extraction of rare earth elements from PG and, perhaps, other waste products.

Figure 1 .
Figure 1.Changes in biomass concentration and pH value of A. niger in pure culture.

Figure 1 .
Figure 1.Changes in biomass concentration and pH value of A. niger in pure culture.

12 Figure 2 .
Figure 2. Bioleaching under different pulp concentrations: (a) recovery of leached REEs; (b) changes in the pH value of the leaching solution.

Figure 3 .
Figure 3. Different forms of the two methods in the leaching process: (a) direct method; (b) indirect method.

Figure 2 .
Figure 2. Bioleaching under different pulp concentrations: (a) recovery of leached REEs; (b) changes in the pH value of the leaching solution.

Figure 2 .
Figure 2. Bioleaching under different pulp concentrations: (a) recovery of leached REEs; (b) changes in the pH value of the leaching solution.

Figure 3 .
Figure 3. Different forms of the two methods in the leaching process: (a) direct method; (b) indirect method.

Figure 3 .
Figure 3. Different forms of the two methods in the leaching process: (a) direct method; (b) indirect method.

Figure 4 .
Figure 4.The rare earth elements in PG were extracted by mixed acid and fermentation liquid.

Figure 4 .
Figure 4.The rare earth elements in PG were extracted by mixed acid and fermentation liquid.

Figure 5 .
Figure 5. SEM images of (a,b) A. niger mycelium before leaching, (c) A. niger mycelium after 15 days of leaching, and (d) details of precipitation on A. niger fungal biomass after leaching.Figure 5. SEM images of (a,b) A. niger mycelium before leaching, (c) A. niger mycelium after 15 days of leaching, and (d) details of precipitation on A. niger fungal biomass after leaching.

Figure 5 .Figure 5 .
Figure 5. SEM images of (a,b) A. niger mycelium before leaching, (c) A. niger mycelium after 15 days of leaching, and (d) details of precipitation on A. niger fungal biomass after leaching.Figure 5. SEM images of (a,b) A. niger mycelium before leaching, (c) A. niger mycelium after 15 days of leaching, and (d) details of precipitation on A. niger fungal biomass after leaching.

Figure 6 .
Figure 6.(a) SEM image of PG attached to A. niger mycelium; (b) EDS figure; Y, Ce, and Sm are enriched on the surface.

Figure 6 .
Figure 6.(a) SEM image of PG attached to A. niger mycelium; (b) EDS figure; Y, Ce, and Sm are enriched on the surface.

Figure 8
Figure 8 showed the distribution of elements in A. niger cells before extraction.The cells were oval-shaped.The main elements in the cells were C, K, and O, with no rare earth elements detected.After the extraction experiment, the cells underwent deformation (Figure8b), and a large amount of Ce, Gd, La, Nd, Pr, Sm, and Y aggregated within the cells.This indicated that the rare earth elements extracted from the PG accumulated inside the cells.Both Figures7 and 8reflected the shrinkage of A. niger cells after rare earth extraction, which could have served as a method for enriching rare earths using A. niger bio-

Figure 8 12 Figure 8 .
Figure 8 showed the distribution of elements in A. niger cells before extraction.The cells were oval-shaped.The main elements in the cells were C, K, and O, with no rare

Figure 8 .
Figure 8. Images of A. niger cells and accumulated elements: (a) before leaching; (b) after leaching.

Table 1 .
Changes in organic acids before and after leaching (error of ±5%).

Table 2 .
The concentration of rare earth elements leached by bioleaching and organic acid leaching methods (error of ±5%).