Progress in Promising Semiconductor Materials for Efficient Photoelectrocatalytic Hydrogen Production

Photoelectrocatalytic (PEC) water decomposition provides a promising method for converting solar energy into green hydrogen energy. Indeed, significant advances and improvements have been made in various fundamental aspects for cutting-edge applications, such as water splitting and hydrogen production. However, the fairly low PEC efficiency of water decomposition by a semiconductor photoelectrode and photocorrosion seriously restrict the practical application of photoelectrochemistry. In this review, the mechanisms of PEC water decomposition are first introduced to provide a solid understanding of the PEC process and ensure that this review is accessible to a wide range of readers. Afterwards, notable achievements to date are outlined, and unique approaches involving promising semiconductor materials for efficient PEC hydrogen production, including metal oxide, sulfide, and graphite-phase carbon nitride, are described. Finally, four strategies which can effectively improve the hydrogen production rate—morphological control, doping, heterojunction, and surface modification—are discussed.


Introduction
Hydrogen is known as the 21st century's most promising clean energy due to its status as an efficient energy carrier with a high energy combustion value (142.5 kJ/g), and the end product of its use is water [1,2].To some extent, the development and utilization of hydrogen energy in relation to renewable energy sources has alleviated the fossil energy crisis [3,4].Solar energy is inexhaustible but inconveniently used due to its dispersion.In this case, converting solar energy into hydrogen energy is a very promising energy solution because it can be more easily stored and effectively used [5,6].
Photoelectrocatalytic (PEC) hydrogen evolution using semiconductor photoelectrodes under irradiation has been widely studied as one of the effective ways to convert solar energy into hydrogen energy [7,8].TiO 2 has been one of the most important and frequently studied PEC photoelectrodes since the discovery of the Fujishima-Honda effect [9].After decades of development, PEC photoelectrodes have sufficiently expanded to a variety of TiO 2 -based and other new photoelectrode materials; the influence of these photoelectrodes on PEC hydrogen production has been widely studied, and the related mechanisms have been exhaustively discussed [10][11][12].
The purpose of this review is to consider the progress on photoelectrocatalysis (PECs) for hydrogen generation from water using high-performance photoelectrode materials.In particular, this work considers the key material properties of photoelectrodes and the trends in research focused on the development of photoelectrodes that may bring PEC technology to commercial maturity.We focus on the preparation and modification of semiconductor photoelectrode materials that have been widely investigated by researchers.Various highperformance photoelectrode materials, including metal oxide, sulfide, and graphitic carbon nitride semiconductors, are discussed.Numerous considerations are limited solely to oxide materials, which appear to exhibit superior properties as photoelectrodes in comparison to other types of materials.

Mechanisms
PECs combines the advantages of both photocatalytic and electrocatalytic technologies.PECs can both make use of solar energy and regulate the photocatalytic process by using photoelectrodes with an appropriate external bias.Moreover, photoelectrodes are convenient for recycling in PEC processes, avoiding the dilemma encountered in the photocatalytic process.
When a semiconductor (e.g., photoanode) is irradiated, electrons and holes can be formed in the conduction band and the valence band, respectively.An electric field at the electrode/electrolyte interface is required in order to avoid the recombination of these charge carriers.The electrons generated in the photoanode are transferred over the external circuit to the cathode, resulting in a reduction reaction (for example, hydrogen ions are reduced into gaseous hydrogen).The light-induced holes lead to the splitting of water molecules into gaseous oxygen and hydrogen ions.The overall reaction for the PEC process may be expressed in the following form: Reaction (1) takes place through a high energy barrier with a Gibbs free energy value of 237.2 kJ/mol, and the electrochemical decomposition of water is possible when the electromotive force of the cell is equal to or larger than 1.23 eV [13].
Concerning the mechanisms of the reactions, the principle of PEC water decomposition is highly related to the energy band structure of the photoelectrode semiconductor.Figure 1 shows a schematic diagram of a typical semiconductor energy band structure, illustrating the various band levels of established electrodes and comparing them with the potentials corresponding to H 2 /H + and H 2 O/O 2 redox couples.The bandgap of the photoelectrode semiconductor should be greater than 1.23 eV for the overall reaction for PEC water decomposition.Meanwhile, the conduction band of the semiconductor should be more negative than the electrode potential of H 2 /H + , while the valence band position should be more positive than the electrode potential of H 2 O/O 2 for the complete decomposition of water.Moreover, the water decomposition voltage is frequently higher than the theoretical value of 1.23 V [14] due to the existence of overpotential in practical PEC systems.It is well known that most semiconductors can satisfy only one of these conditions [15]. Figure 1 shows the band structures of some semiconductors.
Molecules 2024, 29, x FOR PEER REVIEW 2 of 26 of semiconductor photoelectrode materials that have been widely investigated by researchers.Various high-performance photoelectrode materials, including metal oxide, sulfide, and graphitic carbon nitride semiconductors, are discussed.Numerous considerations are limited solely to oxide materials, which appear to exhibit superior properties as photoelectrodes in comparison to other types of materials.

Mechanisms
PECs combines the advantages of both photocatalytic and electrocatalytic technologies.PECs can both make use of solar energy and regulate the photocatalytic process by using photoelectrodes with an appropriate external bias.Moreover, photoelectrodes are convenient for recycling in PEC processes, avoiding the dilemma encountered in the photocatalytic process.
When a semiconductor (e.g., photoanode) is irradiated, electrons and holes can be formed in the conduction band and the valence band, respectively.An electric field at the electrode/electrolyte interface is required in order to avoid the recombination of these charge carriers.The electrons generated in the photoanode are transferred over the external circuit to the cathode, resulting in a reduction reaction (for example, hydrogen ions are reduced into gaseous hydrogen).The light-induced holes lead to the splitting of water molecules into gaseous oxygen and hydrogen ions.The overall reaction for the PEC process may be expressed in the following form: Reaction (1) takes place through a high energy barrier with a Gibbs free energy value of 237.2 kJ/mol, and the electrochemical decomposition of water is possible when the electromotive force of the cell is equal to or larger than 1.23 eV [13].
Concerning the mechanisms of the reactions, the principle of PEC water decomposition is highly related to the energy band structure of the photoelectrode semiconductor.Figure 1 shows a schematic diagram of a typical semiconductor energy band structure, illustrating the various band levels of established electrodes and comparing them with the potentials corresponding to H2/H + and H2O/O2 redox couples.The bandgap of the photoelectrode semiconductor should be greater than 1.23 eV for the overall reaction for PEC water decomposition.Meanwhile, the conduction band of the semiconductor should be more negative than the electrode potential of H2/H + , while the valence band position should be more positive than the electrode potential of H2O/O2 for the complete decomposition of water.Moreover, the water decomposition voltage is frequently higher than the theoretical value of 1.23 V [14] due to the existence of overpotential in practical PEC systems.It is well known that most semiconductors can satisfy only one of these conditions [15]. Figure 1 shows the band structures of some semiconductors.In addition, the hydrogen half-reaction involves the transfer of only two electrons, whereas the half-reaction of oxygen production requires the transfer of four electrons and the formation of O-O bonds.Therefore, the generation of hydrogen is thermodynamically favorable, and the oxygenation reaction is the bottleneck of the whole reaction process if one takes into account the slowest process that determines the overall rate [17].

PEC Cell
Generally, the PEC cell is composed of a photoelectrode, counter electrode, reference electrode, and electrolyte solution.The photoelectrode, used as the working electrode, is mainly composed of a conductive substrate and a semiconductor film material.N-and p-type semiconductors are generally used as photoanodes for PEC oxygen production and photocathodes for PEC hydrogen evolution, respectively.
Materials with good charge collection performance and low reaction overpotential, such as platinum counter electrodes, are usually selected to fulfil the role of the counter electrode.
The electrolyte solution is responsible for mass transfer in the PEC cell.Therefore, the electrolyte solution should have a high conductivity.Salt substances such as Na 2 SO 4 and K 2 SO 4 are commonly used in neutral electrolyte solution, while acidic and alkaline solutions, as well as buffer solution, are employed for specific experimental conditions.
PEC cells can be divided into PEC photoanode cells, PEC photocathode cells, and PEC tandem cells, depending on the way that the semiconductor photoelectrodes are arranged.The PEC photoanode cell generally takes a n-type semiconductor as the working electrode and a platinum electrode as the counter electrode.The PEC photocathode cell often uses a p-type semiconductor as the working electrode and a platinum electrode as the counter electrode.The configuration of the PEC tandem cell is depicted in Figure 2, where a n-type and a p-type semiconductor are used as a photoanode and photocathode, respectively.The first two kinds of cells, using a single semiconductor as a working electrode, frequently require an external bias to promote the decomposition of water [16].Fortunately, in a PEC tandem cell, the combination of a photoanode and photocathode is highly possible to ensure the complete photosplitting of water under sunlight without bias.As shown in Figure 2, photoanode and photocathode materials with different light absorption ranges can broaden the spectral range in the PEC tandem cell.The configuration of the PEC tandem cell is helpful for increasing photocurrent density and improving the efficiency of solar water splitting [18,19].In addition, the hydrogen half-reaction involves the transfer of only two electrons, whereas the half-reaction of oxygen production requires the transfer of four electrons and the formation of O-O bonds.Therefore, the generation of hydrogen is thermodynamically favorable, and the oxygenation reaction is the bottleneck of the whole reaction process if one takes into account the slowest process that determines the overall rate [17].

PEC Cell
Generally, the PEC cell is composed of a photoelectrode, counter electrode, reference electrode, and electrolyte solution.The photoelectrode, used as the working electrode, is mainly composed of a conductive substrate and a semiconductor film material.N-and ptype semiconductors are generally used as photoanodes for PEC oxygen production and photocathodes for PEC hydrogen evolution, respectively.
Materials with good charge collection performance and low reaction overpotential, such as platinum counter electrodes, are usually selected to fulfil the role of the counter electrode.
The electrolyte solution is responsible for mass transfer in the PEC cell.Therefore, the electrolyte solution should have a high conductivity.Salt substances such as Na2SO4 and K2SO4 are commonly used in neutral electrolyte solution, while acidic and alkaline solutions, as well as buffer solution, are employed for specific experimental conditions.
PEC cells can be divided into PEC photoanode cells, PEC photocathode cells, and PEC tandem cells, depending on the way that the semiconductor photoelectrodes are arranged.The PEC photoanode cell generally takes a n-type semiconductor as the working electrode and a platinum electrode as the counter electrode.The PEC photocathode cell often uses a p-type semiconductor as the working electrode and a platinum electrode as the counter electrode.The configuration of the PEC tandem cell is depicted in Figure 2, where a n-type and a p-type semiconductor are used as a photoanode and photocathode, respectively.The first two kinds of cells, using a single semiconductor as a working electrode, frequently require an external bias to promote the decomposition of water [16].Fortunately, in a PEC tandem cell, the combination of a photoanode and photocathode is highly possible to ensure the complete photosplitting of water under sunlight without bias.As shown in Figure 2, photoanode and photocathode materials with different light absorption ranges can broaden the spectral range in the PEC tandem cell.The configuration of the PEC tandem cell is helpful for increasing photocurrent density and improving the efficiency of solar water splitting [18,19].

Metal Oxide Materials
Currently, metal oxide semiconductors are considered for their advantages in terms of photochemical stability, their low cost, and their suitability for large-scale preparation [31][32][33].TiO 2 has been widely studied due to its excellent photocatalytic activity, stability, safety, non-toxicity, rich content, and ease of preparation.However, TiO 2 with a wide bandgap of 3.2 eV can only be activated by UV light with a wavelength below 387 nm.Thus, many efforts have been taken to improve the PEC efficiency of TiO 2 .For example, the visible light activity of TiO 2 can be enhanced by modification.In particular, in the late 1980s, researchers devoted their efforts to developing second-generation TiO 2 that could absorb both UV (290-400 nm) and visible (400-700 nm) light and thereby enhance the overall efficiency.N-type BiVO 4 [34] and p-type Cu 2 O [35] are widely regarded as promising semiconductor materials for efficient PEC hydrogen production due to their bandgap widths and suitable band structures.

TiO 2
TiO 2 , possessing excellent photoelectric performance and high photochemical stability, has always been a very promising PEC material.However, as mentioned above, TiO 2 can only absorb UV light, and the photogenerated charges are easy to recombine, resulting in a low PEC efficiency.Fortunately, the PEC efficiency of TiO 2 can be effectively improved by doping and constructing composite structures.
(1) Doping Gong [36] and co-workers reported a tungsten-doped TiO 2 nanotube arrays (W-TiO 2 NTs) photoelectrode with an exclusive anatase phase utilizing a facile and novel anodization process on a Ti sheet.The results showed that W atoms were successfully incorporated into the TiO 2 lattice in the form of W 6+ ions, which did not influence the morphologies of the TiO 2 NTs samples.The samples were evaluated by XPS to analyze the chemical states of W in W-TiO 2 NTs.The peaks of C1s, O1s, Ti3p, Ti2p, and W4f were observed, as shown in Figure 3A. Figure 3B clearly shows that the peak of Ti3p shifted from 35.9 to 36.9 eV because of the presence of W in the TiO 2 lattice.Thus, the W 6+ ions were loaded into the bulk TiO 2 lattice by displacing Ti 4+ ions and forming W-O-Ti bonds.As shown in Figure 4, the highest photocurrent density and hydrogen production rate were observed for the 15 mM W-TiO 2 NTs annealed at 400 • C.Under illumination, the photocurrent density quickly reached a constant value of 0.3 mA/cm 2 , which indicates that the transfer of the photogenerated charge is quite rapid.The photocurrent pattern is highly reproducible for several on-off light cycles.The photogenerated electrons are rapidly transported from the TiO 2 nanotube arrays to the counter electrode to produce the photocurrent [37].
The PEC performance of TiO 2 can also be improved by metal element doping to increase its conductivity.A simple saturated aqueous solution method was used to synthesize a novel rutile Nb-TiO 2 /g-C 3 N 4 photoanode, whose photocurrent was 1.39 times larger than that of its pristine counterparts under UV light [38].In addition, the unoccupied conduction band of TiO 2 comprises Ti3d, 4s, 4p orbitals, whereas the occupied valence band (VB) comprises O2p orbitals.Ti3d orbitals dominate in the lower position of the conduction band [39,40].An impurity level can be induced by doping with other metal ions (cations) in place of Ti.The resultant intermediate energy level promotes visible light absorption by acting as either an electron donor or acceptor.By doping Fe into TiO 2 , the absorption peak of the sample can gradually shift to red with the increase in the amount of Fe 3+ loading, as shown in Figure 5A.The red shift of the absorption edge in Fe/TiO 2 might be attributed to the excitation of 3d electrons of Fe 3+ ions to the TiO 2 conduction band (charge transfer transition) [41].Figure 5B shows that the hydrogen evolution rate reached the maximum in the 1.0 wt% Fe/TiO 2 photocatalyst.Meanwhile, the H 2 evolution rate decreased in the 2.0 wt% Fe/TiO 2 photocatalyst, which might be due to the role of excess Fe 3+ as a recombination site.Compared with the W-TiO 2 NTs mentioned above, the hydrogen production rate was reduced because more energetic ultraviolet light below 400 nm is shielded.However, its response to visible light makes Fe/TiO 2 more widely used.The PEC performance of TiO2 can also be improved by metal element doping to increase its conductivity.A simple saturated aqueous solution method was used to synthesize a novel rutile Nb-TiO2/g-C3N4 photoanode, whose photocurrent was 1.39 times larger than that of its pristine counterparts under UV light [38].In addition, the unoccupied conduction band of TiO2 comprises Ti3d, 4s, 4p orbitals, whereas the occupied valence band (VB) comprises O2p orbitals.Ti3d orbitals dominate in the lower position of the conduction band [39,40].An impurity level can be induced by doping with other metal ions (cations) in place of Ti.The resultant intermediate energy level promotes visible light absorption by acting as either an electron donor or acceptor.By doping Fe into TiO2, the absorption peak of the sample can gradually shift to red with the increase in the amount of Fe 3+ loading, as shown in Figure 5A.The red shift of the absorption edge in Fe/TiO2 might be attributed to the excitation of 3d electrons of Fe 3+ ions to the TiO2 conduction band (charge transfer transition) [41].Figure 5B shows that the hydrogen evolution rate reached the maximum in the 1.0 wt% Fe/TiO2 photocatalyst.Meanwhile, the H2 evolution rate decreased in the 2.0 wt% Fe/TiO2 photocatalyst, which might be due to the role of excess Fe 3+ as a recombination site.Compared with the W-TiO2 NTs mentioned above, the hydrogen production rate was reduced because more energetic ultraviolet light below 400 nm is shielded.However, its response to visible light makes Fe/TiO2 more widely used.The PEC performance of TiO2 can also be improved by metal element doping to increase its conductivity.A simple saturated aqueous solution method was used to synthesize a novel rutile Nb-TiO2/g-C3N4 photoanode, whose photocurrent was 1.39 times larger than that of its pristine counterparts under UV light [38].In addition, the unoccupied conduction band of TiO2 comprises Ti3d, 4s, 4p orbitals, whereas the occupied valence band (VB) comprises O2p orbitals.Ti3d orbitals dominate in the lower position of the conduction band [39,40].An impurity level can be induced by doping with other metal ions (cations) in place of Ti.The resultant intermediate energy level promotes visible light absorption by acting as either an electron donor or acceptor.By doping Fe into TiO2, the absorption peak of the sample can gradually shift to red with the increase in the amount of Fe 3+ loading, as shown in Figure 5A.The red shift of the absorption edge in Fe/TiO2 might be attributed to the excitation of 3d electrons of Fe 3+ ions to the TiO2 conduction band (charge transfer transition) [41].Figure 5B shows that the hydrogen evolution rate reached the maximum in the 1.0 wt% Fe/TiO2 photocatalyst.Meanwhile, the H2 evolution rate decreased in the 2.0 wt% Fe/TiO2 photocatalyst, which might be due to the role of excess Fe 3+ as a recombination site.Compared with the W-TiO2 NTs mentioned above, the hydrogen production rate was reduced because more energetic ultraviolet light below 400 nm is shielded.However, its response to visible light makes Fe/TiO2 more widely used.(2) TiO2-based composites Liu [42] and co-workers reported a TiO2 NTs/Bi2MoO6 type-II heterojunction (a detailed description of type-II heterojunctions is available in Section 3.3) photocatalyst prepared using a simple solvothermal method.Bi2MoO6 nanoparticles (NPs) with nanosheet (2) TiO 2 -based composites Liu [42] and co-workers reported a TiO 2 NTs/Bi 2 MoO 6 type-II heterojunction (a detailed description of type-II heterojunctions is available in Section 3.3) photocatalyst prepared using a simple solvothermal method.Bi 2 MoO 6 nanoparticles (NPs) with nanosheet microstructures were successfully loaded on the surface of TiO 2 NTs through the adjustment of reaction intervals.With increasing reaction time, the amount of Bi 2 MoO 6 deposition increased gradually.The absorption edges of the samples with reaction times of 14, 18, 22, and 26 h were located at 380, 414, 495, and 452 nm, respectively (Figure 6a).Furthermore, the band gaps of the samples could be estimated using transformational Tauc plots, and their band gaps were calculated to be 3.2, 2.9, 2.4, and 2.7 Ev (Figure 6b).Reductions in band gap values were beneficial to solar energy absorption and photoelectric performance.Because the CB and VB position of Bi 2 MoO 6 are more negative than TiO 2 , a type-II heterojunction can be formed at the interface of TiO 2 NTs/Bi 2 MoO 6 .As shown in Figure 7, the electrons in the VB of the composite material are motivated by photon energy and jump to the CB.Then, electrons in the Bi 2 MoO 6 CB transfer to that of TiO 2 , and the holes in the TiO 2 VB transfer to the Bi 2 MoO 6 VB via the assistance of the internal electric field of the type-II heterojunction.This structure greatly suppresses the recombination of photogenerated electron-hole pairs.
(A) (B) (2) TiO2-based composites Liu [42] and co-workers reported a TiO2 NTs/Bi2MoO6 type-II heterojunction (a detailed description of type-II heterojunctions is available in Section 3.3) photocatalyst prepared using a simple solvothermal method.Bi2MoO6 nanoparticles (NPs) with nanosheet microstructures were successfully loaded on the surface of TiO2 NTs through the adjustment of reaction intervals.With increasing reaction time, the amount of Bi2MoO6 deposition increased gradually.The absorption edges of the samples with reaction times of 14, 18, 22, and 26 hours were located at 380, 414, 495, and 452 nm, respectively (Figure 6a).Furthermore, the band gaps of the samples could be estimated using transformational Tauc plots, and their band gaps were calculated to be 3.2, 2.9, 2.4, and 2.7 Ev (Figure 6b).Reductions in band gap values were beneficial to solar energy absorption and photoelectric performance.Because the CB and VB position of Bi2MoO6 are more negative than TiO2, a type-II heterojunction can be formed at the interface of TiO2 NTs/Bi2MoO6.As shown in Figure 7, the electrons in the VB of the composite material are motivated by photon energy and jump to the CB.Then, electrons in the Bi2MoO6 CB transfer to that of TiO2, and the holes in the TiO2 VB transfer to the Bi2MoO6 VB via the assistance of the internal electric field of the type-II heterojunction.This structure greatly suppresses the recombination of photogenerated electron-hole pairs.Adamopoulos [43] and co-workers reported a photoanode which was made by depositing, on FTO electrodes, either a nanoparticulate WO 3 film alone or a bilayer film made of nanoparticulate WO 3 at the bottom, covered with a nanoparticulate TiO 2 film on the top.Due to the scattering of light by the top TiO 2 layer, the photocurrent increased by enhancing the light absorption by WO 3 , as shown in Figure 8.
Adamopoulos [43] and co-workers reported a photoanode which was made by depositing, on FTO electrodes, either a nanoparticulate WO3 film alone or a bilayer film made of nanoparticulate WO3 at the bottom, covered with a nanoparticulate TiO2 film on the top.Due to the scattering of light by the top TiO2 layer, the photocurrent increased by enhancing the light absorption by WO3, as shown in Figure 8.  [48] reported that a TiO2/Cu2O film photoelectrode led to the continuous generation of H2 from water splitting in the dark after UV-vis light irradiation stopped.The following year, we demonstrated that Ti 3+ in a TiO2/Cu2O bilayer film has energy storage ability under visible light irradiation.We observed that H2 evolution was still noticeable after the irradiation stopped until the third hour.We believe that the electrons trapped in Ti 3+ ions as stored energy lead to the evolution of H2 from H2O in the dark [49].As shown in Figure 9, the photoelectrons of Cu2O were captured by Ti 4+ ions in TiO2, resulting in the reduction of Ti 4+ ions to Ti 3+ ions.The electrons trapped in Ti 3+ ions would have been released if suitable electron acceptors existed.Two years later, we [50] also found that the TiO2/Cu2O composite is capable of both organic degradation and photocatalytic H2 evolution under visible light.Different from the two TiO2 Our research group and a few others developed several TiO 2 -based composite systems for energy storage, such as TiO 2 /WO 3 [44,45], TiO 2 /MoO 3 [46], and TiO 2 /Ni(OH) 2 [47].The energy can be stored either in reduced WO 3 , MoO 3 , or in oxidized Ni(OH) 2 under UV-light irradiation.In 2008, Yasomanee et al. [48] reported that a TiO 2 /Cu 2 O film photoelectrode led to the continuous generation of H 2 from water splitting in the dark after UV-vis light irradiation stopped.The following year, we demonstrated that Ti 3+ in a TiO 2 /Cu 2 O bilayer film has energy storage ability under visible light irradiation.We observed that H 2 evolution was still noticeable after the irradiation stopped until the third hour.We believe that the electrons trapped in Ti 3+ ions as stored energy lead to the evolution of H 2 from H 2 O in the dark [49].As shown in Figure 9, the photoelectrons of Cu 2 O were captured by Ti 4+ ions in TiO 2 , resulting in the reduction of Ti 4+ ions to Ti 3+ ions.The electrons trapped in Ti 3+ ions would have been released if suitable electron acceptors existed.Two years later, we [50] also found that the TiO 2 /Cu 2 O composite is capable of both organic degradation and photocatalytic H 2 evolution under visible light.Different from the two TiO 2 composites mentioned above, the TiO 2 layer here also plays a protective role for the Cu 2 O layer.It is well known that Cu 2 O is highly susceptible to photocorrosion.The existence of the TiO 2 protective layer improves the stability of the photocatalyst.

BiVO4
BiVO4 is considered as one of the most promising materials in the field of PEC water decomposition thanks to its visible light response, good stability, safety, and non-toxicity.

BiVO 4
BiVO 4 is considered as one of the most promising materials in the field of PEC water decomposition thanks to its visible light response, good stability, safety, and non-toxicity.In 1998, Kudo et al. [51] first reported that BiVO 4 powder can be used as a photocatalyst to decompose water under visible light.Five years later, Sayama et al. [52] first demonstrated that a BiVO 4 -based photoanode successfully decomposed water into hydrogen and oxygen gas.
(1) Doping At present, BiVO 4 photoanodes are mainly prepared by coating and electrodeposition.Firstly, a precursor solution containing Bi, V, or other impurity elements are prepared for the deposition of BiVO 4 films; secondly, the precursor solution is coated on the conductive substrate (FTO or ITO) by spin-coating, dip-coating, spraying, or scraping technology; finally, BiVO 4 film photoanodes can be obtained by post-annealing [53,54].The preparation process is convenient for regulating the composition of the film, contributing to a suitable way to study the effect of doping on a BiVO 4 film.Luo et al. [55] examined the PEC performance of BiVO 4 photoanodes doped with 11 different kinds of elements through the above process.They found that the PEC performances of the BiVO 4 photoanodes significantly improved after they were doped with W or Mo.Abdi et al. [56] found that the charge separation efficiency values of the BiVO 4 photoelectrodes significantly improved as the content of W in the precursor ranged from 0% to 1%.
Kim [57] and co-workers used dimethyl sulfoxide with low hydrophilicity to dissolve acetylace to phenoxy vanadium as a vanadium source solution before coating it on the surface of BiOI thin film electrodes.The problem regarding the poor infiltration of ammonia solution and the BiOI film was solved by this step.Crucially, Kim et al. subjected nanoporous BiVO 4 to a mild annealing treatment under N 2 flow, which resulted in nitrogen being incorporated into the oxygen sites.The bandgap of the sample was reduced, while the carrier mobility was increased.
(2) BiVO 4 -based composites In addition to doping, the separation of photogenerated electron-hole pairs can be promoted by constructing BiVO 4 heterojunctions to improve PEC performance.Liang et al. [58] reported on highly efficient and reproducible BiVO 4 photoanodes prepared by a new spray pyrolysis method.As shown in Figure 10, the collection and transfer of carrier charge was substantially improved due to the blocking effect induced on holes, attributable to SnO 2 being introduced as a thin interfacial layer between the FTO and BiVO 4 .The strategy of using a thin SnO 2 layer as a hole mirror can benefit other photoanode materials to avoid the recombination of defect states at the FTO/BiVO 4 interface.This provides an effective method for enhancing the hydrogen production efficiency of FTObased photoelectrode materials.
Li et al. [59] synthesized a Bi 2 S 3 /BiVO 4 photoelectrode with a heterojunction structure through a two-step conversion process.As shown in Figure 11a, it is obvious that the hybrid Bi 2 S 3 /BiVO 4 nanostructure exhibited a higher photocurrent density than the bare BiVO 4 .Compared with Figure 4A, the photocurrent density curve has a sharp decrease at the beginning of each cycle.This phenomenon is caused by the recombination of partial photogenerated charges in the composite, which is very common in composites with heterojunction structures [42,43].Meanwhile, the results showed that Bi 2 S 3 /BiVO 4 has a higher carrier concentration relative to the bare BiVO 4 .In addition, the flat band potential had a negative shift for the hybrid Bi 2 S 3 /BiVO 4 compared with the bare BiVO 4 , which was ascribed to the more negative position of the conduction band for Bi 2 S 3 than that of BiVO 4 (Figure 11b).The negative flat band potential shift contributed to the separation of the photogenerated charge.Because the energy band positions of Bi 2 S 3 were both more negative than that of BiVO 4 , the photoelectrons in the conduction band of Bi 2 S 3 transferred to the conduction band of BiVO 4 , and the photogenerated holes transferred from BiVO 4 to Bi 2 S 3 in the same way (Figure 12).The photocharge recombination can be effectively suppressed, which improves the photocurrent density.
In addition to doping, the separation of photogenerated electron-hole pairs can be promoted by constructing BiVO4 heterojunctions to improve PEC performance.Liang et al. [58] reported on highly efficient and reproducible BiVO4 photoanodes prepared by a new spray pyrolysis method.As shown in Figure 10, the collection and transfer of carrier charge was substantially improved due to the blocking effect induced on holes, attributable to SnO2 being introduced as a thin interfacial layer between the FTO and BiVO4.The strategy of using a thin SnO2 layer as a hole mirror can benefit other photoanode materials to avoid the recombination of defect states at the FTO/BiVO4 interface.This provides an effective method for enhancing the hydrogen production efficiency of FTO-based photoelectrode materials.Li et al. [59] synthesized a Bi2S3/BiVO4 photoelectrode with a heterojunction structure through a two-step conversion process.As shown in Figure 11a, it is obvious that the hybrid Bi2S3/BiVO4 nanostructure exhibited a higher photocurrent density than the bare BiVO4.Compared with Figure 4A, the photocurrent density curve has a sharp decrease at the beginning of each cycle.This phenomenon is caused by the recombination of partial photogenerated charges in the composite, which is very common in composites with heterojunction structures [42,43].Meanwhile, the results showed that Bi2S3/BiVO4 has a higher carrier concentration relative to the bare BiVO4.In addition, the flat band potential had a negative shift for the hybrid Bi2S3/BiVO4 compared with the bare BiVO4, which was ascribed to the more negative position of the conduction band for Bi2S3 than that of BiVO4 (Figure 11b).The negative flat band potential shift contributed to the separation of the photogenerated charge.Because the energy band positions of Bi2S3 were both more negative than that of BiVO4, the photoelectrons in the conduction band of Bi2S3 transferred to the conduction band of BiVO4, and the photogenerated holes transferred from BiVO4 to Bi2S3 in the same way (Figure 12).The photocharge recombination can be effectively suppressed, which improves the photocurrent density.Wu et al. [64] reported a MoS 2 /Cu 2 O nanohybrid prepared by a simple wet chemical method.This heterojunction structure effectively promoted the separation of photogenerated electron-hole pairs, resulting in a significant increase in the photocurrent of the nanohybrid.Peerakiatkhajohn et al. [65] originally introduced a Al 2 O 3 thin-film layer between Au@TiO 2 and Cu 2 O. On the one hand, strong inherent electric fields at the interfaces, produced by the introduction of an extremely thin Al 2 O 3 film, suppress the recombination of photogenerated electron-hole pairs.On the other hand, humic acid served as an electron donor to clear holes and suppressed electron hole recombination by capturing the remaining holes.In the presence of humic acid, the hydrogen production efficiency of the PEC device was significantly improved.A bifunctional PEC system with the function of simultaneous hydrogen production and humic degradation was achieved through using the multi-layer Au@TiO 2 /Al 2 O 3 /Cu 2 O photoelectrodes, as shown in Figure 13.improved if a TiO2 protective layer with a thickness of about 100 nm is deposited on the surface of Cu2O by the electron beam method.Wu et al. [64] reported a MoS2/Cu2O nanohybrid prepared by a simple wet chemical method.This heterojunction structure effectively promoted the separation of photogenerated electron-hole pairs, resulting in a significant increase in the photocurrent of the nanohybrid.Peerakiatkhajohn et al. [65] originally introduced a Al2O3 thin-film layer between Au@TiO2 and Cu2O.On the one hand, strong inherent electric fields at the interfaces, produced by the introduction of an extremely thin Al2O3 film, suppress the recombination of photogenerated electron-hole pairs.On the other hand, humic acid served as an electron donor to clear holes and suppressed electron hole recombination by capturing the remaining holes.In the presence of humic acid, the hydrogen production efficiency of the PEC device was significantly improved.A bifunctional PEC system with the function of simultaneous hydrogen production and humic degradation was achieved through using the multi-layer Au@TiO2/Al2O3/Cu2O photoelectrodes, as shown in Figure 13.A schematic visualization of a bifunctional PEC system (hydrogen generation and humic acid degradation) with a direct Z-scheme mechanism of TiO2-1 wt% Au@TiO2/Al2O3/Cu2O photoelectrodes in a H-cell type reactor [65].Reproduced with permission from Peerakiatkhajohn, P., Journal of Hazardous Materials, published by Elsevier, 2021.

Sulfide Materials
Metal sulfides such as cadmium sulfide (CdS), cadmium zinc sulfide solid solution (ZnxCd1−xS), and indium zinc sulfide (ZnIn2S4) have been extensively studied for their wide range of sources, simple preparation methods, appropriate band structures, and good PEC activity.Solid-phase synthesis is one of the important methods for preparing sulfides.Bao et al. [66] prepared CdS nanocrystals via the pyrolysis of a cadmium thiourea complex at high temperature in a N2 atmosphere.However, the crystal produced by this method had a large crystalline grain size and small specific surface area, which is not conducive to the PEC reaction.
With the development of colloidal chemistry, people have gradually developed a variety of liquid-phase synthesis methods to prepare sulfide materials with high PEC performance.In early studies, CdS was often prepared by a chemical precipitation method,

Sulfide Materials
Metal sulfides such as cadmium sulfide (CdS), cadmium zinc sulfide solid solution (Zn x Cd 1−x S), and indium zinc sulfide (ZnIn 2 S 4 ) have been extensively studied for their wide range of sources, simple preparation methods, appropriate band structures, and good PEC activity.Solid-phase synthesis is one of the important methods for preparing sulfides.Bao et al. [66] prepared CdS nanocrystals via the pyrolysis of a cadmium thiourea complex at high temperature in a N 2 atmosphere.However, the crystal produced by this method had a large crystalline grain size and small specific surface area, which is not conducive to the PEC reaction.
With the development of colloidal chemistry, people have gradually developed a variety of liquid-phase synthesis methods to prepare sulfide materials with high PEC performance.In early studies, CdS was often prepared by a chemical precipitation method, and the precursor was usually cadmium brine solution.H 2 S, Na 2 S, thiourea, and other sulfur-containing organic or inorganic compounds are used as precipitants [67].The microwave hydrothermal method is also an important synthesis method for preparing high-quality sulfides.The electromagnetic field in the microwave reactor changes direction at a frequency of tens of thousands of hertz, causing the dipolar vibration of reactant molecules.The entire reaction system is heated rapidly and evenly, which greatly improves the reaction rate [68].

Doping
For sulfide semiconductors, doping is also an effective way to adjust their band structures for improving PEC performance.Tian et al. [69], Zhang et al. [70], and Barpuzary et al. [71], respectively, incorporated Cu, Co, and Mn elements into CdS, which introduces shallow energy levels into its band gap, improving the PEC performance of doped CdS due to the enhancement in carrier separation efficiency and visible light absorption.As shown in Figure 14, compared with the XPS spectrum of the CdS, the two peaks corresponding to Cd3d 5/2 (404.1 eV) and Cd3d 3/2 (411.7 eV) had a slight shift towards to a higher binding energy.The introduction of Cu 2+ changed the crystal structure of CdS due to the introduction of lattice defects.Similarly, the absorption edge of the UV/Vis spectrum shifted to red because of the Cu defect states formed in the forbidden gap (Figure 15).The 7% Cu-CdS exhibited the best hydrogen production ability, with a rate of 1115 µmol h −1 g −1 , which is almost 5.3 times higher than that of undoped CdS of 212 µmol h −1 g −1 (Figure 16A).Furthermore, a Cu-CdS/MoS 2 composite can reach a hydrogen production rate of 10.18 mmol h −1 g −1 , which is about 48 times higher than that of pure CdS (Figure 16B).MoS 2 can provide a lot of active sites at the edge of its sheets, leading to improved hydrogen production.The photoelectric performances of photoelectrodes with composite structures are often better than those based on pure doping.
In addition to doping, the energy band structure of sulfides can also be modified by forming solid solutions with different precursors of sulfides.The energy band structure of solid solutions can be precisely controlled by changing the composition of different precursors.For example, the band gaps of Zn x Cd 1−x S [72] and Cu x Ag 1−x InS 2 [73] can be precisely tuned by adjusting the composition of Zn/Cd and Cu/Ag, respectively.In this case, both of the tuned sulfides can respond to visible light, allowing for the efficient utilization of solar energy.Moreover, such solid solutions show better PEC performances than doped sulfides.In addition to doping, the energy band structure of sulfides can also be modified by forming solid solutions with different precursors of sulfides.The energy band structure of solid solutions can be precisely controlled by changing the composition of different precursors.For example, the band gaps of ZnxCd1−xS [72] and CuxAg1−xInS2 [73] can be precisely tuned by adjusting the composition of Zn/Cd and Cu/Ag, respectively.In this case, both of the tuned sulfides can respond to visible light, allowing for the efficient utilization of solar energy.Moreover, such solid solutions show better PEC performances than doped sulfides.

Sulfide-Based Composites
Like sulfides, sulfide-based composites have also attracted considerable attention [74].Gao et al. [75] prepared ZnIn2S4 nanosheets on flexible graphite felt by using a hydrothermal method.They found that a photoelectrode with a 5 mm-thick graphite felt and ZnIn2S4 coating exhibited the best PEC properties compared to other photoelectrodes.Guo et al. [73] designed a series of CuxAg1−xInS2/ZnS colloidal quantum dots (CQDs) by the defect passivation of a ZnS shell and the incorporation of Cu ions to engineer its band structure.ZnS shell-assisted defect passivation suppressed charge carrier recombination because of the formation of the core/shell heterojunction interface, enhancing the performance of PEC devices with better charge separation and stability.Furthermore, Cu ion doping in AgInS2 CQDs results in a shift in the energy band of the quantum dots, which greatly promote the interface's charge separation and transfer (Figure 17).

Sulfide-Based Composites
Like sulfides, sulfide-based composites have also attracted considerable attention [74].Gao et al. [75] prepared ZnIn 2 S 4 nanosheets on flexible graphite felt by using a hydrothermal method.They found that a photoelectrode with a 5 mm-thick graphite felt and ZnIn 2 S 4 coating exhibited the best PEC properties compared to other photoelectrodes.Guo et al. [73] designed a series of Cu x Ag 1−x InS 2 /ZnS colloidal quantum dots (CQDs) by the defect passivation of a ZnS shell and the incorporation of Cu ions to engineer its band structure.ZnS shell-assisted defect passivation suppressed charge carrier recombination because of the formation of the core/shell heterojunction interface, enhancing the performance of PEC devices with better charge separation and stability.Furthermore, Cu ion doping in AgInS 2 CQDs results in a shift in the energy band of the quantum dots, which greatly promote the interface's charge separation and transfer (Figure 17).
Mollavali [76] reported the composite structures of a variety of sulfides on Co-doped/modified TiO 2 .TiO 2 nanostructures were first sensitized by nitrogen and carbon with a one-step low-cost anodic oxidation process, and then NiS/CdS/ZnS NPs were deposited on the surfaces of TiO 2 nanostructures by successive ionic layer adsorption and using a successive ionic layer adsorption and reaction (SILAR) method at room temperature (Figure 18).These vertically aligned C, N-co-doped TiO 2 nanotube arrays (TNAs) electrode provide a large surface area for the deposition of NPs, and they are also well-defined channels for efficient charge transport (Figure 19a).The NiS nanoparticles have small aggregation rather than large aggregation on the top of the TNAs (Figure 19b).Although some aggregates of the nanoparticles can be observed in the final photoanode due to the dense particle loading, the nanotubes remain predominantly open after all deposition steps, which is an important factor to maximize light absorbance and photoactivity, as well as electrolyte transport (Figure 19c,d).The optical properties of a C, N-TiO 2 /NiS/CdS/ZnS photoanode were enhanced due to a reduction in the recombination of electrons and holes, improving the surface carrier transfer rate and photogenerated carrier separation.
Like sulfides, sulfide-based composites have also attracted considerable atten [74].Gao et al. [75] prepared ZnIn2S4 nanosheets flexible graphite felt by using a drothermal method.They found that a photoelectrode with a 5 mm-thick graphite felt ZnIn2S4 coating exhibited the best PEC properties compared to other photoelectrodes.et al. [73] designed a series of CuxAg1−xInS2/ZnS colloidal quantum dots (CQDs) by defect passivation of a ZnS shell and the incorporation of Cu ions to engineer its b structure.ZnS shell-assisted defect passivation suppressed charge carrier recombina because of the formation of the core/shell heterojunction interface, enhancing the pe mance of PEC devices with better charge separation and stability.Furthermore, Cu doping in AgInS2 CQDs results in a shift in the energy band of the quantum dots, w greatly promote the interface's charge separation and transfer (Figure 17).Mollavali [76] reported the composite structures of a variety of sulfi doped/modified TiO2.TiO2 nanostructures were first sensitized by nitrogen with a one-step low-cost anodic oxidation process, and then NiS/CdS/ZnS N posited on the surfaces of TiO2 nanostructures by successive ionic layer adso using a successive ionic layer adsorption and reaction (SILAR) method at roo ture (Figure 18).These vertically aligned C, N-co-doped TiO2 nanotube arr electrode provide a large surface area for the deposition of NPs, and they ar defined channels for efficient charge transport (Figure 19a).The NiS nanopa small aggregation rather than large aggregation on the top of the TNAs (Figu hough some aggregates of the nanoparticles can be observed in the final phot to the dense particle loading, the nanotubes remain predominantly open after tion steps, which is an important factor to maximize light absorbance and ph as well as electrolyte transport (Figure 19c,d).The optical properties o TiO2/NiS/CdS/ZnS photoanode were enhanced due to a reduction in the recom electrons and holes, improving the surface carrier transfer rate and photogener separation.

Graphite-Phase Carbon Nitride (g-C3N4)
In 2009, Wang [77] first reported that g-C3N4 can photocatalytically d into hydrogen and oxygen with a sacrificial agent under visible light.Th C3N4 is 2.7 eV.Its minimum conduction band and maximum valence ban +1.6 eV, respectively, which makes it possible to decompose water comp ble light.It can be made by calcining common raw materials such as me chloride, and urea at high temperature.The C/N ratio of g-C3N4 varies d calcination temperature [78].

Doping
Wang et al. [79] found that fluorine doping into g-C3N4 can form a C ing its band gap and increasing its optical absorption range.Wu et al. [ phosphorus (P)-doped g-C3N4 synthesized by a simple sintering meth µA/cm 2 of photocurrent at 1.2 V versus Ag/AgCl under near-IR light (>800 The introduction of P into g-C3N4 reduced its bandgap from 2.75 eV to 1. a superior infrared light response.Meanwhile, the doping of P also impr tion and transfer of photogenerated charges.In addition to non-metal do ing has also been extensively used to improve the PEC performance of al. [81] reported on the synthesis of an elongated g-C3N4 nanostructure cated by the direct pyrolysis of a supramolecular melamine precursor.material was used to host specific amounts of bismuth, a doping eleme the band gap of the hosting matrix.XRD measurements confirmed the ab oxide in the photoanode (Figure 20).The bandgap width was reduced

Graphite-Phase Carbon Nitride (g-C 3 N 4 )
In 2009, Wang [77] first reported that g-C 3 N 4 can photocatalytically decompose water into hydrogen and oxygen with a sacrificial agent under visible light.The band gap of g-C 3 N 4 is 2.7 eV.Its minimum conduction band and maximum valence band are −1.1 eV and +1.6 eV, respectively, which makes it possible to decompose water completely under visible light.It can be made by calcining common raw materials such as melamine, cyanuric chloride, and urea at high temperature.The C/N ratio of g-C 3 N 4 varies depending on the calcination temperature [78].

Doping
Wang et al. [79] found that fluorine doping into g-C 3 N 4 can form a C-F bond, narrowing its band gap and increasing its optical absorption range.Wu et al. [80] reported that phosphorus (P)-doped g-C 3 N 4 synthesized by a simple sintering method exhibited 1.4 µA/cm 2 of photocurrent at 1.2 V versus Ag/AgCl under near-IR light (>800 nm) irradiation.The introduction of P into g-C 3 N 4 reduced its bandgap from 2.75 eV to 1.37 eV, in favor of a superior infrared light response.Meanwhile, the doping of P also improved the separation and transfer of photogenerated charges.In addition to non-metal doping, metal doping has also been extensively used to improve the PEC performance of g-C 3 N 4 .Rouby et al. [81] reported on the synthesis of an elongated g-C 3 N 4 nanostructure which was fabricated by the direct pyrolysis of a supramolecular melamine precursor.The asprepared material was used to host specific amounts of bismuth, a doping element used to adjust the band gap of the hosting matrix.XRD measurements confirmed the absence of bismuth oxide in the photoanode (Figure 20).The bandgap width was reduced due to the introduction of Bi in g-C 3 N 4 (Figure 21).The 2.5% Bi-doped g-C 3 N 4 photoelectrode was twice as efficient as pure g-C 3 N 4 in terms of PEC water decomposition.The schematic diagram shown in Figure 22 shows the energy band structure of a typical element-doped and molecularly modified g-C 3 N 4 sample.

g-C3N4 Composites
Semiconductor heterojunctions can effectively promote the separation of photogenerated electron-hole pairs, thus enhancing the PEC activity of semiconductor materials.

g-C3N4 Composites
Semiconductor heterojunctions can effectively promote the separation of photogenerated electron-hole pairs, thus enhancing the PEC activity of semiconductor materials.

g-C3N4 Composites
Semiconductor heterojunctions can effectively promote the separation of photogenerated electron-hole pairs, thus enhancing the PEC activity of semiconductor materials.

g-C 3 N 4 Composites
Semiconductor heterojunctions can effectively promote the separation of photogenerated electron-hole pairs, thus enhancing the PEC activity of semiconductor materials.As a kind of flexible material, g-C 3 N 4 is beneficial for closely compounding with other semiconductors.Available materials include metal oxides (ZnO [83,84], TiO 2 [85,86], WO 3 [87], BiIO [88], Al 2 O 3 [89]), sulfides (CdS [90], MoS 2 [91]), graphene [92], activated carbon [93], and noble metal Au [94].Velusamy et al. [88] prepared a noble metal-free nano-heterostructure of neodymium (Nd)-doped graphitic carbon nitride (g-C 3 N 4 ) and bismuth oxyiodide (BiOI) by using a two-step thermal poly-condensation and hydrothermal method.The doping of Nd reduced the bandgap width of the photoelectrode, thereby increasing its response range to visible light.At the same time, the construction of heterojunctions can improve the transfer and suppress the recombination of photogenerated charges.The combination of the two methods improves the optical and electrical properties of the photoelectrode, leading to an enhancement in PEC performance (Figure 23).As a kind of flexible material, g-C3N4 is beneficial for closely compounding with other semiconductors.Available materials include metal oxides (ZnO [83,84], TiO2 [85,86], WO3 [87], BiIO [88], Al2O3 [89]), sulfides (CdS [90], MoS2 [91]), graphene [92], activated carbon [93], and noble metal Au [94].Velusamy et al. [88] prepared a noble metal-free nano-heterostructure of neodymium (Nd)-doped graphitic carbon nitride (g-C3N4) and bismuth oxyiodide (BiOI) by using a two-step thermal poly-condensation and hydrothermal method.The doping of Nd reduced the bandgap width of the photoelectrode, thereby increasing its response range to visible light.At the same time, the construction of heterojunctions can improve the transfer and suppress the recombination of photogenerated charges.The combination of the two methods improves the optical and electrical properties of the photoelectrode, leading to an enhancement in PEC performance (Figure 23).

Strategies to Improve the Efficiency of PEC Hydrogen Evolution
Based on the present understanding of the principle of PECs, we discussed the promising semiconductor materials and related experimental methods and means currently used in the PEC decomposition of water.PEC hydrogen evolution involves diversiform chemical and physical processes such as the preparation of a photoelectrode material, photon absorption, semiconductor excitation, and the separation and migration of electron-hole pairs.Considering these important chemical and physical processes involved in PECs, this section summarizes strategies that might be useful for improving the efficiency of PEC hydrogen production.

Morphological Control
The morphological properties of semiconductor photoelectrode materials, such as the thickness of film electrodes and the surface microstructure, have a very important influence on PEC efficiency.For example, the morphology of single-crystalline TiO2 NTs is beneficial for directional charge transport due to their nanotube confinement effect [95].In one study, after size-controllable g-C3N4 quantum dots (QDs) were synthesized in situ and grafted onto TiO2 NTs, the unique morphology and structure efficiently inhibited selfgathering and the leaching of g-C3N4 QDs, leading to excellent PEC performance [95].The reactions of oxidation and reduction occur only when the carrier charges migrate from the

Strategies to Improve the Efficiency of PEC Hydrogen Evolution
Based on the present understanding of the principle of PECs, we discussed the promising semiconductor materials and related experimental methods and means currently used in the PEC decomposition of water.PEC hydrogen evolution involves diversiform chemical and physical processes such as the preparation of a photoelectrode material, photon absorption, semiconductor excitation, and the separation and migration of electron-hole pairs.Considering these important chemical and physical processes involved in PECs, this section summarizes strategies that might be useful for improving the efficiency of PEC hydrogen production.

Morphological Control
The morphological properties of semiconductor photoelectrode materials, such as the thickness of film electrodes and the surface microstructure, have a very important influence on PEC efficiency.For example, the morphology of single-crystalline TiO 2 NTs is beneficial for directional charge transport due to their nanotube confinement effect [95].In one study, after size-controllable g-C 3 N 4 quantum dots (QDs) were synthesized in situ and grafted onto TiO 2 NTs, the unique morphology and structure efficiently inhibited self-gathering and the leaching of g-C 3 N 4 QDs, leading to excellent PEC performance [95].The reactions of oxidation and reduction occur only when the carrier charges migrate from the inside to the surface of the semiconductor photoelectrode or counter electrode.Thus, a considerable part of the carrier charges is likely to recombine before they reach the electrode surface due to the low carrier mobility or excessive thickness of the photoelectrode film.In this case, the thinner the photoelectrode film is, the faster the carrier charges can be transferred to the surface of the photoelectrode.However, excessive reduction of the thickness of the photoelectrode film will weaken the light absorption [96,97].Therefore, a balance regarding the light harvest and fast transfer of the carrier charges should be achieved by optimizing the thickness of the photoelectrode film [98].
It is well known that crystal surfaces play an important role in the PEC activity of photoelectrodes.Compared with a stable anatase (101) crystal surface, a metastable (001) crystal surface has more unsaturated coordination surface dangling bonds.Yang [99] was the first to successfully synthesize anatase TiO 2 micro crystals with an exposure ratio of (001) crystal plane up to 47% through the regulation of hydrofluoric acid (HF).This groundbreaking work led to an upsurge in the study of anatase (001) facet synthesis and related PEC properties.However, HF is highly corrosive.Thus, various fluorides have been used as additives to study the effect of stabilizing (001) crystal facets, including ammonium fluoride, ammonium hydrogen fluoride, sodium fluoride, or fluorine-containing surfactants [100].BiVO 4 film photoelectrodes composed of nanoplates with highly reactive exposed facets (001) also exhibit a photocurrent density more than five times higher than that of nanorods grown along the (100) direction.Similarly, WO 3 nanomultilayers with highly exposed (002) facets (60%) exhibited much better PEC performances than WO 3 nanorods with less exposed (002) facets (20%) [31].

Doping
Doping can create defect energy levels in the bandgap of a semiconductor, thus changing its energy band structure.On one hand, the defect energy levels usually offer a narrow sub-bandgap in the semiconductor, contributing to increasing the light absorption; on the other hand, the defect energy levels can form a charge capture center and thus increase the carrier life.In addition, doping can also regulate the electrical properties of semiconductors, such as carrier concentration and carrier mobility, enhance the conductivity and carrier mobility of semiconductors, and improve the efficiency of charge separation and transfer [101][102][103].Therefore an optimal amount of doping should be determined for photoelectrode materials to achieve optimal PEC performance [104].

Heterojunctions
A heterojunction is the interfacial contact region of two different semiconductors; heterojunctions are mainly divided into types I, II, and III.As shown in Figure 24a, in a type-I heterojunction, both the conduction band (CB) and the valence band (VB) of semiconductor A are included in the bandgap of semiconductor B. The photogenerated electrons transfer from CB(B) to CB(A), while the photogenerated holes transfer from VB(B) to VB(A).All photogenerated charges are accumulated in semiconductor A, probably resulting in the recombination problem of charge carriers.In a type-II heterojunction (Figure 24b), both the CB and the VB of semiconductor B are more negative than those of semiconductor A, meanwhile, the VB of semiconductor B is located in the bandgap of semiconductor A. In this case, the photogenerated electrons and holes are likely to accumulate in the CB (A) and VB(B), respectively, improving the efficiency of the separation of carrier charges, thus enhancing the PEC decomposition of water.Numerous composite photoelectrodes mentioned above employ this type-II heterojunction structure.For example, the PEC performance of TiO 2 can be significantly improved when coupled with Cu 2 O [105] and ZnO [106] to form type-II heterojunctions.In a type-III heterojunction (Figure 24c), the whole band position of semiconductor B is further offset to that of semiconductor A. Such arrangements of band positions are also called broken-gap situations.For type-II heterojunctions, despite the fact that they can effectively separate th charge, their oxidation-reduction abilities have not yet been maximized in this system.contrast, Z-scheme heterojunctions can achieve strong oxidation-reduction abilities.A shown in Figure 25 [108], in Z-scheme heterojunctions, the photogenerated electrons semiconductor II are inclined to combine with the photogenerated holes in semiconducto I.In this case, the photogenerated electrons and holes are likely to accumulate in the C of semiconductor I and VB of semiconductor II, respectively.The structures of Z-schem heterojunctions can both enhance the separation of charge carriers and retain the stron reduction and oxidation ability, thus improving the PEC performance of the photoele trode.

Surface Modification
Metals, especially noble metals (such as Pt) with large work functions (i.e., low Ferm levels) can effectively collect electrons and enjoy a low activation energy and overpotenti for the hydrogen production reaction.Therefore, noble metals are often considered suitable cocatalysts for PEC hydrogen production.Pop et al. [109] reported a "PEC Lea photoelectrode consisting of nano titanium dioxide particles as photocatalysts and a com mercial carbon paste enriched with a small quantity of Pt NPs (0.0134 mg/cm 2 ) as electr catalysts.As shown in Figure 26, Pt can effectively enrich photogenerated electrons fro the photoelectrode, greatly improving hydrogen production efficiency with the help of For type-II heterojunctions, despite the fact that they can effectively separate the charge, their oxidation-reduction abilities have not yet been maximized in this system.In contrast, Z-scheme heterojunctions can achieve strong oxidation-reduction abilities.As shown in Figure 25 [108], in Z-scheme heterojunctions, the photogenerated electrons in semiconductor II are inclined to combine with the photogenerated holes in semiconductor I.In this case, the photogenerated electrons and holes are likely to accumulate in the CB of semiconductor I and VB of semiconductor II, respectively.The structures of Z-scheme heterojunctions can both enhance the separation of charge carriers and retain the strong reduction and oxidation ability, thus improving the PEC performance of the photoelectrode.For type-II heterojunctions, despite the fact that they can effectively separate the charge, their oxidation-reduction abilities have not yet been maximized in this system.In contrast, Z-scheme heterojunctions can achieve strong oxidation-reduction abilities.As shown in Figure 25 [108], in Z-scheme heterojunctions, the photogenerated electrons in semiconductor II are inclined to combine with the photogenerated holes in semiconductor I.In this case, the photogenerated electrons and holes are likely to accumulate in the CB of semiconductor I and VB of semiconductor II, respectively.The structures of Z-scheme heterojunctions can both enhance the separation of charge carriers and retain the strong reduction and oxidation ability, thus improving the PEC performance of the photoelectrode.

Surface Modification
Metals, especially noble metals (such as Pt) with large work functions (i.e., low Fermi levels) can effectively collect electrons and enjoy a low activation energy and overpotential for the hydrogen production reaction.Therefore, noble metals are often considered as suitable cocatalysts for PEC hydrogen production.Pop et al. [109] reported a "PEC Leaf" photoelectrode consisting of nano titanium dioxide particles as photocatalysts and a commercial carbon paste enriched with a small quantity of Pt NPs (0.0134 mg/cm 2 ) as electrocatalysts.As shown in Figure 26, Pt can effectively enrich photogenerated electrons from the photoelectrode, greatly improving hydrogen production efficiency with the help of a

Surface Modification
Metals, especially noble metals (such as Pt) with large work functions (i.e., low Fermi levels) can effectively collect electrons and enjoy a low activation energy and overpotential for the hydrogen production reaction.Therefore, noble metals are often considered as suitable cocatalysts for PEC hydrogen production.Pop et al. [109] reported a "PEC Leaf" photoelectrode consisting of nano titanium dioxide particles as photocatalysts and a commercial carbon paste enriched with a small quantity of Pt NPs (0.0134 mg/cm 2 ) as electrocatalysts.As shown in Figure 26, Pt can effectively enrich photogenerated electrons from the photoelectrode, greatly improving hydrogen production efficiency with the help of a sacrificial agent.It is worth noting that the loading amount of Pt directly affects the PEC performance of the sample, and the excessive loading of Pt will lead to a decrease in the PEC performance of the sample [110].In addition, the hydrogen production performance of photoelectrodes can also be affected by the particle size and shape of the noble metal cocatalyst [111].
Molecules 2024, 29, x FOR PEER REVIEW 20 of 26 sacrificial agent.It is worth noting that the loading amount of Pt directly affects the PEC performance of the sample, and the excessive loading of Pt will lead to a decrease in the PEC performance of the sample [110].In addition, the hydrogen production performance of photoelectrodes can also be affected by the particle size and shape of the noble metal cocatalyst [111].However, the high cost of noble metals limits their use on a large scale.So, some transition metals and oxides have been used as low-cost substitutes, such as NiO [112] and CuO [113].Kim et al. [114] reported a ternary hybrid solar desalination process coupled with PEC water treatment and H2 production in a low-cost device with an oxide photoelectrode and transition sulfate cathode.The desalination of brackish water in the desalination cell is initiated via photoinduced charge generation with a thermochemically reduced TiO2 nanorod array photoanode.As shown in Figure 27, a three-cell device was designed to achieve hydrogen production and seawater desalination.The Ni-Mo-S composite catalyst greatly promoted the generation of hydrogen at the cathode, thereby improving the seawater desalination rate of the entire device.However, the high cost of noble metals limits their use on a large scale.So, some transition metals and oxides have been used as low-cost substitutes, such as NiO [112] and CuO [113].Kim et al. [114] reported a ternary hybrid solar desalination process coupled with PEC water treatment and H 2 production in a low-cost device with an oxide photoelectrode and transition sulfate cathode.The desalination of brackish water in the desalination cell is initiated via photoinduced charge generation with a thermochemically reduced TiO 2 nanorod array photoanode.As shown in Figure 27, a three-cell device was designed to achieve hydrogen production and seawater desalination.The Ni-Mo-S composite catalyst greatly promoted the generation of hydrogen at the cathode, thereby improving the seawater desalination rate of the entire device.
Molecules 2024, 29, x FOR PEER REVIEW 20 of 26 sacrificial agent.It is worth noting that the loading amount of Pt directly affects the PEC performance of the sample, and the excessive loading of Pt will lead to a decrease in the PEC performance of the sample [110].In addition, the hydrogen production performance of photoelectrodes can also be affected by the particle size and shape of the noble metal cocatalyst [111].However, the high cost of noble metals limits their use on a large scale.So, some transition metals and oxides have been used as low-cost substitutes, such as NiO [112] and CuO [113].Kim et al. [114] reported a ternary hybrid solar desalination process coupled with PEC water treatment and H2 production in a low-cost device with an oxide photoelectrode and transition sulfate cathode.The desalination of brackish water in the desalination cell is initiated via photoinduced charge generation with a thermochemically reduced TiO2 nanorod array photoanode.As shown in Figure 27, a three-cell device was designed to achieve hydrogen production and seawater desalination.The Ni-Mo-S composite catalyst greatly promoted the generation of hydrogen at the cathode, thereby improving the seawater desalination rate of the entire device.

Concluding Remarks
An overview of promising semiconductor materials for efficient PEC hydrogen production has been given.The general characteristics, preparation methods, and applications of metal oxides, sulfide materials, and g-C 3 N 4 , as well as their modifications and composites, have been covered, as summarized in Table 1.The benefits and drawbacks of the photoelectrode materials and their corresponding remedial schemes have also been discussed.An efficient PEC photoelectrode should possess an appropriate energy band structure, wide wavelength light absorption, effective carrier separation and transport, and high stability.Doping and modification are effective approaches for improving the PEC performance of hydrogen evolution and stability of photoelectrode materials.Particularly, constructing type-II and Z-scheme heterojunctions using multiple materials is also a good way to effectively promote the separation and transport of carrier charges.We hope a comprehensive understanding of the relationship between the structures and properties of semiconductor materials will benefit the precise control of semiconductor materials as photoelectrodes and thus promote the development of PEC hydrogen production.

Figure 1 .
Figure 1.Band structures of typical semiconductors [16].Reproduced with permission from Yang, W., Chemical Society Reviews, published by Royal Society of Chemistry, 2019.

Figure 7 .
Figure 7. Schematic diagram of the degradation of dyes by a TiO 2 NTs/Bi 2 MoO 6 heterojunction photocatalyst under solar irradiation [42].Reproduced with permission from Liu, Z., Journal of Colloid and Interface Science, published by Elsevier, 2019.

Figure 8 .
Figure 8. Graphical representation of the direction of photons in the presently used setup[43].Reproduced with permission from Adamopoulos, P.M., Catalysts, published by MDPI, 2019.Our research group and a few others developed several TiO2-based composite systems for energy storage, such as TiO2/WO3[44,45], TiO2/MoO3[46], and TiO2/Ni(OH)2[47].The energy can be stored either in reduced WO3, MoO3, or in oxidized Ni(OH)2 under UVlight irradiation.In 2008, Yasomanee et al.[48] reported that a TiO2/Cu2O film photoelectrode led to the continuous generation of H2 from water splitting in the dark after UV-vis light irradiation stopped.The following year, we demonstrated that Ti 3+ in a TiO2/Cu2O bilayer film has energy storage ability under visible light irradiation.We observed that H2 evolution was still noticeable after the irradiation stopped until the third hour.We believe that the electrons trapped in Ti 3+ ions as stored energy lead to the evolution of H2 from H2O in the dark[49].As shown in Figure9, the photoelectrons of Cu2O were captured by Ti 4+ ions in TiO2, resulting in the reduction of Ti 4+ ions to Ti 3+ ions.The electrons trapped in Ti 3+ ions would have been released if suitable electron acceptors existed.Two years later, we[50] also found that the TiO2/Cu2O composite is capable of both organic degradation and photocatalytic H2 evolution under visible light.Different from the two TiO2

Figure 8 .
Figure 8. Graphical representation of the direction of photons in the presently used setup [43].Reproduced with permission from Adamopoulos, P.M., Catalysts, published by MDPI, 2019.
Molecules 2024, 29, x FOR PEER REVIEW 8 of 26 composites mentioned above, the TiO2 layer here also plays a protective role for the Cu2O layer.It is well known that Cu2O is highly susceptible to photocorrosion.The existence of the TiO2 protective layer improves the stability of the photocatalyst.

Figure 9 .
Figure 9. Electron migration diagram of a Cu2O/TiO2 composite [50].Reproduced with permission from Xiong, L., Journal of Physics and Chemistry of Solids, published by Elsevier, 2011.

Figure 9 .
Figure 9. Electron migration diagram of a Cu 2 O/TiO 2 composite [50].Reproduced with permission from Xiong, L., Journal of Physics and Chemistry of Solids, published by Elsevier, 2011.

Figure 10 .
Figure 10.Schematic diagrams illustrating the recombination at the defect state present at the FTO/BiVO4 interface and the hole mirror effect of the SnO2 layer, respectively [58].Reproduced with permission from Liang, Y., The Journal of Physical Chemistry C, published by American Chemical Society, 2011.

Figure 10 .Figure 11 .
Figure 10.Schematic diagrams illustrating the recombination at the defect state present at the FTO/BiVO 4 interface and the hole mirror effect of the SnO 2 layer, respectively [58].Reproduced with permission from Liang, Y., The Journal of Physical Chemistry C, published by American Chemical Society, 2011.Molecules 2024, 29, x FOR PEER REVIEW 10 of

Figure 12 .
Figure 12.Energy band structure of a hybrid Bi2S3/BiVO4 photoelectrode and its electron transf pathway in photoelectrocatalytic hydrogen production under solar light irradiation [59].Repr duced with permission from Li, F., Chemical Engineering Science, published by Elsevier, 2020.

Figure 12 .
Figure 12.Energy band structure of a hybrid Bi2S3/BiVO4 photoelectrode and its electron transfer pathway in photoelectrocatalytic hydrogen production under solar light irradiation [59].Reproduced with permission from Li, F., Chemical Engineering Science, published by Elsevier, 2020.3.1.3.Cu2O Cu2O has attracted considerable interest in the field of PECs since Kondo et al. [60].first reported that Cu2O can photocatalytically carry out complete water decomposition in 1998.Cu2O has a narrow band gap of about 2.1 eV and a high absorption coefficient.It shows red, orange, and other different colors due to its different synthesis methods and

Figure 12 .
Figure 12.Energy band structure of a hybrid Bi 2 S 3 /BiVO 4 photoelectrode and its electron transfer pathway in photoelectrocatalytic hydrogen production under solar light irradiation [59].Reproduced with permission from Li, F., Chemical Engineering Science, published by Elsevier, 2020.

3. 1 . 3 .
Cu 2 O Cu 2 O has attracted considerable interest in the field of PECs since Kondo et al. [60].first reported that Cu 2 O can photocatalytically carry out complete water decomposition in 1998.Cu 2 O has a narrow band gap of about 2.1 eV and a high absorption coefficient.It shows red, orange, and other different colors due to its different synthesis methods and particle sizes.Cu 2 O has various advantages, such as its appropriate band gap, excellent photoelectric performance, simple preparation, and low cost.However, Cu 2 O photocathodes are extremely prone to photocorrosion due to their oxidation-reduction potentials located in the band gap of Cu 2 O [61,62].At present, a large number of studies in the literature are devoted to the stability of Cu 2 O as a photocathode in the process of PECs.Siripala et al. [63] first proposed that the stability of a Cu 2 O photocathode can be substantially improved if a TiO 2 protective layer with a thickness of about 100 nm is deposited on the surface of Cu 2 O by the electron beam method.

Figure 13 .
Figure13.A schematic visualization of a bifunctional PEC system (hydrogen generation and humic acid degradation) with a direct Z-scheme mechanism of TiO2-1 wt% Au@TiO2/Al2O3/Cu2O photoelectrodes in a H-cell type reactor[65].Reproduced with permission from Peerakiatkhajohn, P., Journal of Hazardous Materials, published by Elsevier, 2021.

Figure 13 .
Figure 13.A schematic visualization of a bifunctional PEC system (hydrogen generation and humic acid degradation) with a direct Z-scheme mechanism of TiO 2 -1 wt% Au@TiO 2 /Al 2 O 3 /Cu 2 O photoelectrodes in a H-cell type reactor [65].Reproduced with permission from Peerakiatkhajohn, P., Journal of Hazardous Materials, published by Elsevier, 2021.

Figure 17 .Figure 17 .
Figure 17.Manipulating the catalytic activity of photoanodes by modulating the structure of C (a) Schematic diagram for a CQD-based photoanode with a structure compr glass|FTO|TiO2|CQDs.(b) Figure and predictable band alignment of a CQD-based photoa Figure 17.Manipulating the catalytic activity of photoanodes by modulating the structure of CQDs: (a) Schematic diagram for a CQD-based photoanode with a structure comprising glass|FTO|TiO 2 |CQDs.(b) Figure and predictable band alignment of a CQD-based photoanode photoelectrochemical cells.(c) The band structure of type-I CQDs.(d) Schematic illustration for band structure engineering and defect passivation of Cu-doped AgInS 2 /ZnS CQDs [73] (a detailed description of type-I heterojunctions is available in Section 3.3).Reproduced with permission from Guo, H., ACS Omega, published by American Chemical Society, 2022.

Figure 18 .
Figure 18.Schematic diagram illustrating the SILAR process for depositing NiS, CdS, a on a C, N-co-doped TNA substrate [76].Reproduced with permission from Mollavali tional Journal of Hydrogen Energy, published by Elsevier, 2018.

Figure 18 .
Figure 18.Schematic diagram illustrating the SILAR process for depositing NiS, CdS, and ZnS NPs on a C, N-co-doped TNA substrate [76].Reproduced with permission from Mollavali, M., International Journal of Hydrogen Energy, published by Elsevier, 2018.

Figure 21 .
Figure 21.Schematic illustrations for the valence bands and the conduction bands of neat g-C3N4 and 2.5% Bi-g-C3N4 [81].Reproduced with permission from El Rouby, Solar Energy, published by Elsevier, 2020.

Figure 21 .
Figure 21.Schematic illustrations for the valence bands and the conduction bands of neat g-C3N4 and 2.5% Bi-g-C3N4 [81].Reproduced with permission from El Rouby, Solar Energy, published by Elsevier, 2020.

Figure 21 . 26 Figure 20 .
Figure 21.Schematic illustrations for the valence bands and the conduction bands of neat g-C 3 N 4 and 2.5% Bi-g-C 3 N 4 [81].Reproduced with permission from El Rouby, Solar Energy, published by Elsevier, 2020.

Figure 21 .
Figure 21.Schematic illustrations for the valence bands and the conduction bands of neat g-C3N4 and 2.5% Bi-g-C3N4 [81].Reproduced with permission from El Rouby, Solar Energy, published by Elsevier, 2020.

Figure 22 .
Figure 22.Schematic illustration of the band structures of typical g-C 3 N 4 samples in comparison to TiO 2 samples: g-C 3 N 4 , S-g-C 3 N 4 , B-g-C 3 N 4 , O-g-C 3 N 4 , C-g-C 3 N 4 , and BA-g-C 3 N 4 [82].Reproduced with permission from Cao, S., Advanced Materials, published by John Wiley and Sons, 2015.

Figure 25 .
Figure 25.Schematic illustration of charge carrier transfer for (A) type-II and (B) Z-scheme heter junctions [108].Reproduced with permission from Li, J., Carbon Energy, published by John Wil and Sons, 2022.

Figure 25 .
Figure 25.Schematic illustration of charge carrier transfer for (A) type-II and (B) Z-scheme heterojunctions [108].Reproduced with permission from Li, J., Carbon Energy, published by John Wiley and Sons, 2022.

Figure 25 .
Figure 25.Schematic illustration of charge carrier transfer for (A) type-II and (B) Z-scheme heterojunctions [108].Reproduced with permission from Li, J., Carbon Energy, published by John Wiley and Sons, 2022.

Figure 26 .
Figure 26.Illustration of a "PEC Leaf" (A) showing the area covered by the nanoparticulate photocatalyst (p), the area covered by the electrocatalyst (e), and a reactor producing hydrogen by employing a photocatalytic leaf (B) [109].Reproduced with permission from Pop, L., Applied Surface Science, published by Elsevier, 2015.

Figure 27 .
Figure 27.Illustration of a sunlight-driven ternary hybrid desalination device.The device consists of a thermochemically reduced TiO2 nanorod array (r-TNA) photoelectrode in the anode cell, saline water in the (middle) desalination cell, and a Ni-Mo-S (Ni2S3/MoS2) electrocatalyst in the cathode cell.The anode and desalination cells were separated by an anion exchange membrane (AEM), whereas the desalination cell and cathode cell were separated by a cation exchange membrane (CEM) [114].Reproduced with permission from Kim, S., Applied Catalysis B: Environmental, published by Elsevier, 2021.

Figure 26 .
Figure 26.Illustration of a "PEC Leaf" (A) showing the area covered by the nanoparticulate photocatalyst (p), the area covered by the electrocatalyst (e), and a reactor producing hydrogen by employing a photocatalytic leaf (B) [109].Reproduced with permission from Pop, L., Applied Surface Science, published by Elsevier, 2015.

Figure 26 .
Figure 26.Illustration of a "PEC Leaf" (A) showing the area covered by the nanoparticulate photocatalyst (p), the area covered by the electrocatalyst (e), and a reactor producing hydrogen by employing a photocatalytic leaf (B) [109].Reproduced with permission from Pop, L., Applied Surface Science, published by Elsevier, 2015.

Figure 27 .
Figure 27.Illustration of a sunlight-driven ternary hybrid desalination device.The device consists of a thermochemically reduced TiO2 nanorod array (r-TNA) photoelectrode in the anode cell, saline water in the (middle) desalination cell, and a Ni-Mo-S (Ni2S3/MoS2) electrocatalyst in the cathode cell.The anode and desalination cells were separated by an anion exchange membrane (AEM), whereas the desalination cell and cathode cell were separated by a cation exchange membrane (CEM) [114].Reproduced with permission from Kim, S., Applied Catalysis B: Environmental, published by Elsevier, 2021.

Figure 27 .
Figure 27.Illustration of a sunlight-driven ternary hybrid desalination device.The device consists of a thermochemically reduced TiO 2 nanorod array (r-TNA) photoelectrode in the anode cell, saline water in the (middle) desalination cell, and a Ni-Mo-S (Ni 2 S 3 /MoS 2 ) electrocatalyst in the cathode cell.The anode and desalination cells were separated by an anion exchange membrane (AEM), whereas the desalination cell and cathode cell were separated by a cation exchange membrane (CEM) [114].Reproduced with permission from Kim, S., Applied Catalysis B: Environmental, published by Elsevier, 2021.
[16] structures of typical semiconductors[16].Reproduced with permission from Yang, W., Chemical Society Reviews, published by Royal Society of Chemistry, 2019.

Table 1 .
A summary of promising photoelectrocatalysts with improved photoelectric performance for the hydrogen production.Conceptualization, L.X. and H.Y.; original draft preparation, W.F., Y.Z. and X.Z.; writing, W.F.; writing-review and editing, R.X., S.Z. and Y.L.; supervision and funding acquisition, L.X. and H.Y. All authors have read and agreed to the published version of the manuscript.The authors acknowledge the support of the Natural Science Foundation of Guangdong Province (2021A1515012594), Guangdong Province Office of Education (2020ZDZX2028, 2021gs-zlgc01), United Laboratory of College and Enterprise (GSZLGC2023005), Science and Technology Projects of Guangzhou (202201011335, 202201011256), Guangdong Basic and Applied Basic Research Foundation (2022A1515110463, 2021A1515110803), Jiangxi Provincial Natural Science Foundation (GJJ2201422), and the Scientific Research Foundation of Gannan Medical University (QD202115, XN202004).