Synthesis and Electrocatalytic Performance Study of Sulfur Quantum Dots Modified MoS2

The electrolysis of water for hydrogen production is currently receiving significant attention due to its advantageous features such as non-toxicity, safety, and environmental friendliness. This is especially crucial considering the urgent need for clean energy. However, the current method of electrolyzing water to produce hydrogen largely relies on expensive metal catalysts, significantly increasing the costs associated with its development. Molybdenum disulfide (MoS2) is considered the most promising alternative to platinum for electrocatalyzing the hydrogen evolution reaction (HER) due to its outstanding catalytic efficiency and robust stability. However, the practical application of this material is hindered by its low conductivity and limited exposure of active sites. MoS2/SQDs composite materials were synthesized using a hydrothermal technique to deposit SQDs onto MoS2. These composite materials were subsequently employed as catalysts for the HER. Research findings indicate that incorporating SQDs can enhance electron transfer rates and increase the active surface area of MoS2, which is crucial for achieving outstanding catalytic performance in the HER. The MoS2/SQDs electrocatalyst exhibits outstanding performance in the HER when tested in a 0.5 M H2SO4 solution. It achieves a remarkably low overpotential of 204 mV and a Tafel slope of 65.82 mV dec−1 at a current density of 10 mA cm−2. Moreover, during continuous operation for 24 h, the initial current density experiences only a 17% reduction, indicating high stability. This study aims to develop an efficient and cost-effective electrocatalyst for water electrolysis. Additionally, it proposes a novel design strategy that uses SQDs as co-catalysts to enhance charge transfer in nanocomposites.


Introduction
With the rapid advancement of human civilization, there is an increasing dependence on various forms of energy.Fossil fuels remain a predominant and indispensable energy source in the contemporary world.However, due to the limited availability of fossil fuels and the steadily growing global demand, their scarcity or complete depletion is inevitable [1].Furthermore, the extensive use of fossil fuels has led to significant degradation of the ecological environment [2,3].Therefore, the advancement of clean and sustainable energy sources represents a significant challenge for the international community currently [4,5].Hydrogen has garnered considerable attention as an energy carrier due to its exceptionally high energy density, purity, and renewable characteristics [6].However, current methods for hydrogen production still heavily rely on fossil fuels, thus inadequately addressing this issue at its root.Alternatively, renewable energy sources can be used to produce high-purity hydrogen sustainably via water electrolysis [7].However, the efficiency of water electrolysis is significantly reduced due to slow hydrogen evolution reaction kinetics, resulting in a significant increase in costs [8,9].Noble metal materials, such as platinum-based catalysts, exhibit outstanding electrocatalytic performance for the HER.However, their high cost and limited availability hinder the widespread adoption of these materials.To reduce dependence on platinum-based catalysts, it is crucial to develop novel, cost-effective, and efficient catalysts for the HER that are free from precious metals.
Researchers have thus far concentrated on investigating various transition metalbased materials as potential catalysts for the HER that exhibit exceptional performance [10].Transition metal-based compounds, particularly those in Group VI B like molybdenum and tungsten, serve as substantial alternatives to precious metals for catalyzing the HER process.Molybdenum-based materials have exhibited excellent performance in the HER, attracting considerable research attention in recent years.Molybdenum-containing compounds exhibit exceptional performance, leading to their extensive application across diverse disciplines, including molecular probes [11], electrochemical capacitors [12], catalysts [13,14], and batteries [15,16].The investigation into electrochemical HER materials utilizing molybdenum has been ongoing for several decades.Recently, there has been a surge in research exploring various types of molybdenum-based compounds, including alloys, sulfides, selenides, carbides, phosphides, borides, nitrides, and oxides, as highly efficient catalysts for HER.These compounds exhibit substantial electrocatalytic activity and stability across a wide pH range, encompassing strong acids, strong alkalis, and neutral solutions [17].Transition metal dichalcogenides have become widely recognized as effective electrocatalysts for catalyzing the HER in acidic environments.This is mostly due to their exceptional catalytic efficiency and stability, making them a promising alternative to precious metal catalysts [18,19].MoS 2 , one of the transition metal dichalcogenides (TMDs), is a stable and non-toxic material with a low cost.It shows great promise in the field of electrocatalysis for the HER [20,21].However, MoS 2 , extensively researched as a potential alternative to platinum-based HER electrocatalysts, encounters challenges due to its low electrical conductivity and limited accessibility of active sites, which hinder its practical application [22].Several approaches have been proposed to enhance the reactivity of MoS 2 , such as enhancing the exposure of active sites, combining it with highly conductive materials, and introducing metal atoms to enhance the intrinsic reactivity of its edges [23][24][25].For example, research has documented the utilization of Cr-doped FeNi-P nanoparticles and N-doped CoP nanoarrays, both exhibiting significant improvements in their HER capabilities upon the incorporation of chromium (Cr) or nitrogen (N) into the transition metals [26,27].However, relying solely on elemental doping is insufficient to surpass the performance of Pt and Pt-based materials.Additionally, the presence of a substrate is crucial to offer structural support for transition metal materials [28].Chen et al. found that incorporating carbon quantum dots (CQDs) onto transition metal phosphide surfaces enhances their performance in the HER by increasing the surface area and the number of active sites [27].Typically, small 0D nanometer-sized particles (less than 10 nanometers) offer inherent advantages that facilitate their integration into various material structures.The utilization of nanodots, such as CQDs and graphene quantum dots, can significantly enhance electron mobility.Sulphur quantum dots (SQDs) are attracting attention as a promising area of study in electrochemistry, owing to their distinctive characteristics and versatile applications.Nanoscale semiconductor materials typically range in dimensions from 1 to 10 nanometers and exhibit intriguing electrochemical properties due to their adjustable bandgaps, high surface area-to-volume ratio, and exceptional charge transport capabilities.SQDs, or semiconductor quantum dots, demonstrate significant potential across various areas such as energy storage, catalysis, and sensing within the field of electrochemistry.SQDs exhibit high efficiency in conducting redox processes, making them highly suitable for application in batteries, supercapacitors, and electrocatalysis.To date, there are no documented instances of molybdenum-based catalysts being utilized in conjunction with SQDs for HER.
The objective of this study is to attach sulfur quantum dots onto molybdenum disulfide to enhance its electrocatalytic hydrogen evolution performance.This will be achieved by creating a synergistic catalytic system.The incorporation of sulfur quantum dots has a dual effect: improving the conductivity of molybdenum disulfide and facilitating electron transport.Additionally, it regulates the active sites on the surface of molybdenum disulfide, leading to an enhancement in its electrocatalytic hydrogen evolution capability.Sulfur quantum dots and molybdenum disulfide were synthesized via a hydrothermal process, and composite materials of sulfur quantum dots and molybdenum disulfide were effectively analyzed using various techniques.Subsequently, the electrochemical efficiency of hydrogen production was individually assessed for sulfur quantum dots/molybdenum disulfide, pure molybdenum disulfide, and sulfur quantum dots in an acidic electrolyte.The experimental results demonstrate that the HER performance of the sulfur quantum dots/molybdenum disulfide composite surpasses that of both pure MoS 2 and sulfur quantum dots alone, exhibiting a lower onset potential and Tafel slope.The composite material exhibits exceptional durability during stability tests.These results suggest that combining sulfur quantum dots with molybdenum disulfide is a successful approach to improving the electrocatalytic performance of the hydrogen evolution reaction.

Structure Characterization
To gain a more comprehensive understanding and conduct a detailed analysis of the structure of MoS 2 , both before and after the incorporation of SQDs, scanning electron microscopy was employed to investigate the morphology of MoS 2 .The SEM images of pure MoS 2 and MoS 2 /SQDs are depicted in Figure 1a,b, respectively.These images clearly illustrate the regular and closely arranged structure of MoS 2 , resembling a rose-like formation.The addition of SQDs has enhanced the aggregation of molybdenum disulfide compared to pure MoS 2 , resulting in a loosely structured composition comprising several tiny nanosheets.MoS 2 /SQDs exhibit a greater number of exposed edges compared to pure MoS 2 , potentially leading to an increased number of active sites available for the HER and consequently enhancing the electrocatalytic activity of MoS 2 .The XRD graph (Figure 1c) reveals that the diffraction peaks of MoS 2 closely match those of standard MoS 2 in the PDF card (PDF#37-1492) [28].Specifically, the (002), (100), and (110) crystal plane peaks are observed at angles of 14.3 • , 32.6 • , and 58.6 • , respectively.The displacement of the diffraction peaks in MoS 2 /SQDs, compared to pure MoS 2 , is nearly insignificant.Figure 1d displays the E 1 2g vibration of MoS 2 /SQDs at 377.46 cm −1 , corresponding to in-plane Mo-S vibration, while the E 1g peak at 284.30 cm −1 is associated with octahedrally coordinated Mo atoms.Additionally, peaks J 1 , J 2 , and J 3 at 147.59, 238.73, and 337.97 cm −1 , respectively, correspond to the superlattice distortion of the MoS 2 basal plane [29].
The TEM technique was employed for further characterization.Figure 2a,b present the microstructure of SQDs. Figure 2a illustrates the uniformly distributed and highly spherical crystalline structures of all SQDs.In Figure 2b, a lattice spacing of 0.29 nm in the SQDs is clearly visible, corresponding to the (243) crystal plane.Figure 2c provides the size distribution of SQDs, indicating a size range of 1 nm to 5 nm, directly correlating with the size of the SQDs.TEM images confirm the presence of both MoS 2 and SQDs in the sample (Figure 2d).The lattice spacings of 0.31 nm and 0.66 nm observed in the TEM images correspond to the (002) crystal plane of MoS 2 and the (243) plane of SQDs, respectively.Additionally, the EDS spectra demonstrate the homogeneous dispersion of Mo and S elements (Figure 2e).
The surface composition and valence states of the synthesized MoS 2 /SQDs samples were determined using X-ray photoelectron spectroscopy (XPS).The XPS scans revealed the presence of sulfur (S), molybdenum (Mo), oxygen (O), and carbon (C) components in the samples (Figure 3a).The Mo 3d spectrum (Figure 3b) shows six prominent peaks: the peaks at 228.75 and 232.02 eV are identified as the Mo 3d 3/2 of Mo 4+ , while the peaks at 229.86 and 233.33 eV correspond to the Mo 3d 5/2 of Mo 4+ .The peak at a binding energy of 226.24 eV is attributed to S 2s, and the peak at a binding energy of approximately 235.5 eV is the Mo 3d 3/2 peak of Mo 6+ , consistent with previous research findings [30].From Figure 3c, it can be observed that there are two strong peaks located at 161.7 eV and 162.9 eV in the high-resolution spectra of S 2p 1/2 and S 2p 3/2 , respectively, and the sulfur species exist in the form of S 2− ions [31].Based on the fitting results, the peak observed at 161.5 eV likely indicates the presence of sulfur ions in a condition of low coordination on the surface, while the peak at 163.1 eV is indicative of the molybdenum-sulfur bond in MoS 2 .The peaks observed at 284.8, 286.3, and 288.9 eV in the C 1s spectra (Figure 3d) correspond to the presence of C-C, C-N, and C=O bonds, respectively.The surface composition and valence states of the synthesized MoS2/SQDs samples were determined using X-ray photoelectron spectroscopy (XPS).The XPS scans revealed the presence of sulfur (S), molybdenum (Mo), oxygen (O), and carbon (C) components in the samples (Figure 3a).The Mo 3d spectrum (Figure 3b) shows six prominent peaks: the  The surface composition and valence states of the synthesized MoS2/SQDs samples were determined using X-ray photoelectron spectroscopy (XPS).The XPS scans revealed the presence of sulfur (S), molybdenum (Mo), oxygen (O), and carbon (C) components in the samples (Figure 3a).The Mo 3d spectrum (Figure 3b) shows six prominent peaks: the peaks at 228.75 and 232.02 eV are identified as the Mo 3d3/2 of Mo 4+ , while the peaks at 3c, it can be observed that there are two strong peaks located at 161.7 eV and 162.9 eV in the high-resolution spectra of S 2p1/2 and S 2p3/2, respectively, and the sulfur species exist in the form of S 2− ions [31].Based on the fitting results, the peak observed at 161.5 eV likely indicates the presence of sulfur ions in a condition of low coordination on the surface, while the peak at 163.1 eV is indicative of the molybdenum-sulfur bond in MoS2.The peaks observed at 284.8, 286.3, and 288.9 eV in the C 1s spectra (Figure 3d) correspond to the presence of C-C, C-N, and C=O bonds, respectively.

Electrochemical Performance Analysis
The number of active sites on the catalyst was assessed using double-layer capacitance analysis, while cyclic voltammetry was employed to analyze the electrochemical performance of the synthesized materials.Figure 4a-c depict the CV curves and the linear correlation between current density and scan rate at various scan rates.In comparison to other samples, MoS2/SQDs demonstrate a higher current density in the CV curves, suggesting a higher specific capacitance (Figure 4d).The obtained results indicate that the capacitance values of self-made MoS2 and MoS2/SQDs are 3.26 mF cm −2 and 6.32 mF cm −2 , respectively.The charge carrier density of MoS2/SQDs is approximately double that of pure MoS2, indicating a greater number of active sites.This phenomenon can be attributed to the dispersion of previously clustered MoS2 nanosheets by SQDs, leading to a significant increase in the active surface area of MoS2 and consequently creating additional sites for chemical reactions, thereby enhancing overall reaction rates.
The electrochemical performance of the prepared samples for HER was evaluated in an acidic environment using a three-electrode electrochemical workstation, with a scan rate of 1 mV s −1 .Figure 5a illustrates the linear sweep voltammetry profiles of commercially available 20% Pt/C, MoS2, SQDs, and MoS2/SQDs electrodes.While the Pt/C catalyst exhibits anticipated HER activity with an overpotential almost at zero, SQDs, however, perform poorly within the test potential range, suggesting minimal catalytic action for HER.Remarkably, MoS2/SQDs demonstrate stronger catalytic activity than pure molybdenum disulfide.The overpotential of MoS2 is 340 mV at a current density of 10 mA cm −2 , much higher than that of MoS2/SQDs (204 mV).This suggests that MoS2 is the primary

Electrochemical Performance Analysis
The number of active sites on the catalyst was assessed using double-layer capacitance analysis, while cyclic voltammetry was employed to analyze the electrochemical performance of the synthesized materials.Figure 4a-c depict the CV curves and the linear correlation between current density and scan rate at various scan rates.In comparison to other samples, MoS 2 /SQDs demonstrate a higher current density in the CV curves, suggesting a higher specific capacitance (Figure 4d).The obtained results indicate that the capacitance values of self-made MoS 2 and MoS 2 /SQDs are 3.26 mF cm −2 and 6.32 mF cm −2 , respectively.The charge carrier density of MoS 2 /SQDs is approximately double that of pure MoS 2 , indicating a greater number of active sites.This phenomenon can be attributed to the dispersion of previously clustered MoS 2 nanosheets by SQDs, leading to a significant increase in the active surface area of MoS 2 and consequently creating additional sites for chemical reactions, thereby enhancing overall reaction rates.The electrochemical performance of the prepared samples for HER was evaluated in an acidic environment using a three-electrode electrochemical workstation, with a scan rate of 1 mV s −1 .Figure 5a illustrates the linear sweep voltammetry profiles of commercially available 20% Pt/C, MoS 2 , SQDs, and MoS 2 /SQDs electrodes.While the Pt/C catalyst exhibits anticipated HER activity with an overpotential almost at zero, SQDs, however, perform poorly within the test potential range, suggesting minimal catalytic action for HER.Remarkably, MoS 2 /SQDs demonstrate stronger catalytic activity than pure molybdenum disulfide.The overpotential of MoS 2 is 340 mV at a current density of 10 mA cm −2 , much higher than that of MoS 2 /SQDs (204 mV).This suggests that MoS 2 is the primary active component for HER, as indicated by the lower catalytic activity of SQDs.The combination of MoS 2 and SQDs significantly enhances the catalytic performance of MoS 2 /SQDs in the HER process.The ECSA of catalysts is determined by estimating the catalyst's electrochemical C dl , measured using CV in the non-Faradaic zone with gradually increasing scan rates.Among the MoS 2 /SQDs, MoS 2 , and SQDs samples, the MoS 2 /SQDs sample exhibits the highest C dl value at 6.32 mF cm −2 .The ECSA of the MoS 2 /SQDs catalyst is the greatest among the prepared catalysts, calculated to be 158.13cm 2 (Figure 5c).In comparison, the ECSA values for pure MoS 2 and SQDs are calculated to be 81.51cm 2 and 23.5 cm 2 , respectively.
Figure 5d illustrates the electrochemical impedance spectra of the materials.The Nyquist plot commonly uses the diameter of the semicircle to ascertain the charge transfer resistance.A reduced diameter corresponds to decreased charge transfer resistance and an accelerated charge transfer rate.The inclusion of SQDs decreases the electrical resistance of MoS 2 , as indicated by notably lower semicircle diameters observed in MoS 2 /SQDs compared to MoS 2 and SQDs alone.This reduction in resistance is beneficial for lowering the resistance of the interface reaction and enhancing performance, facilitating quicker electron transfer between the catalyst and electrolyte, thereby increasing charge transport during the HER process.
Stability is a significant criterion for catalysts, in addition to their catalytic activity.To further examine the stability of MoS 2 /SQDs in the electrocatalytic HER, current-time curves under overpotential conditions were measured.As depicted in Figure 5e, the initial current density of the MoS 2 /SQDs catalyst decreased by a mere 17% following a 24 h testing period.The exceptional resistance of MoS 2 /SQDs to electrochemical degradation in acidic environments was confirmed through a 24 h endurance test.The decrease in current density could potentially be explained by gas desorption on the electrode surface or sluggish mass transport of the electrolyte.As shown in Figure 6, after 24 h of stability testing, there were no significant changes in the phase and morphology of MoS 2 /SQDs, and they remained essentially consistent before and after stability testing.The high stability of MoS 2 /SQDs throughout prolonged electrochemical processes is validated by these results.Table 1 below demonstrates the comparison of the performance of MoS 2 /SQDs with other HER electrocatalysts.
step, leading to increased HER kinetics and faster rates of charge transfer.
The ECSA of catalysts is determined by estimating the catalyst's electrochemical Cdl measured using CV in the non-Faradaic zone with gradually increasing scan rates.Among the MoS2/SQDs, MoS2, and SQDs samples, the MoS2/SQDs sample exhibits the highest Cd value at 6.32 mF cm −2 .The ECSA of the MoS2/SQDs catalyst is the greatest among the prepared catalysts, calculated to be 158.13cm 2 (Figure 5c).In comparison, the ECSA val ues for pure MoS2 and SQDs are calculated to be 81.51cm 2 and 23.5 cm 2 , respectively.
Figure 5d illustrates the electrochemical impedance spectra of the materials.The Nyquist plot commonly uses the diameter of the semicircle to ascertain the charge transfer resistance.A reduced diameter corresponds to decreased charge transfer resistance and an accelerated charge transfer rate.The inclusion of SQDs decreases the electrical re sistance of MoS2, as indicated by notably lower semicircle diameters observed in MoS2/SQDs compared to MoS2 and SQDs alone.This reduction in resistance is beneficia for lowering the resistance of the interface reaction and enhancing performance, facilitat ing quicker electron transfer between the catalyst and electrolyte, thereby increasing charge transport during the HER process.
Stability is a significant criterion for catalysts, in addition to their catalytic activity To further examine the stability of MoS2/SQDs in the electrocatalytic HER, current-time curves under overpotential conditions were measured.As depicted in Figure 5e, the initia current density of the MoS2/SQDs catalyst decreased by a mere 17% following a 24 h test ing period.The exceptional resistance of MoS2/SQDs to electrochemical degradation in acidic environments was confirmed through a 24 h endurance test.The decrease in curren density could potentially be explained by gas desorption on the electrode surface or slug gish mass transport of the electrolyte.As shown in Figure 6, after 24 h of stability testing there were no significant changes in the phase and morphology of MoS2/SQDs, and they remained essentially consistent before and after stability testing.The high stability o MoS2/SQDs throughout prolonged electrochemical processes is validated by these results Table 1 below demonstrates the comparison of the performance of MoS2/SQDs with other HER electrocatalysts.

Preparation of SQDs
SQDs were synthesized using a hydrothermal method [40].First, 1.6 g of S, 3 g of PEG, 4 g of NaOH, and 100 mL of deionized water were stirred at 90 • C for 10 h.After cooling to room temperature, impurities were removed using a 0.22 µm pore size membrane.Dialysis was performed, and the SQD solution was collected after the dialysis was complete.

Preparation of MoS 2
Next, 0.3 g of Na 2 MoO 4 •2H 2 O and 0.28 g of C 2 H 5 NS were sequentially added to 25 mL of deionized water.After magnetic stirring for 30 min, the mixture was transferred to a 50 mL high-pressure reaction vessel and subjected to hydrothermal reaction at 200 • C for 18 h.After natural cooling to room temperature, repeated centrifugation with a mixture of deionized water and anhydrous ethanol was performed to remove other impurity ions.Finally, the product was freeze-dried to collect the final product.

Preparation of MoS 2 /SQDs
As shown in Figure 7, MoS 2 /SQDs were synthesized via the hydrothermal method, using Na 2 MoO 4 •2H 2 O as the molybdenum source and C 2 H 5 NS as the sulfur source.Specif- ically, 0.3 g of Na 2 MoO 4 •2H 2 O and 0.28 g of C 2 H 5 NS were sequentially added to 30 mL of deionized water.After magnetic stirring for 20 min, 20 mL of SQD solution was added, followed by transfer to a 100 mL high-pressure reaction vessel for hydrothermal reaction at 200 • C for 18 h.After natural cooling to room temperature, repeated centrifugation with a mixture of deionized water and anhydrous ethanol was performed to remove other impurity ions.Finally, the product was freeze-dried to collect the final product.

Characterization
X-ray diffraction (XRD; MiniFlex-600, Rigaku, Tokyo, Japan) with a CuKα source was used to analyze the crystalline condition of samples.X-ray photoelectron spectroscopy (XPS; K-Alpha, Thermo Scientific, Waltham, MA, USA) was used to analyze the elemental valence of materials.Transmission electron microscopy (TEM; JEM-2100, JEOL Ltd., Tokyo, Japan) was used to test the grain size of the samples.Scanning electron microscopy (SEM; KYKY-EM 6900, KYKY Technology Co., Ltd., Beijing, China) was utilized to observe the morphology of the samples.Fourier-transform infrared (FTIR; FTIR-2000, Perki-nElmer, Waltham, MA, USA) spectrometry was employed to analyze the structure of the samples.

Electrochemical Measurements
Herein, electrochemical measurements were performed in a 0.5 M H2SO4 electrolyte using a standard three-electrode system (CHI 760E Instruments, Chenhua, Shanghai,

Electrochemical Measurements
Herein, electrochemical measurements were performed in a 0.5 M H 2 SO 4 electrolyte using a standard three-electrode system (CHI 760E Instruments, Chenhua, Shanghai, China) with a Ag/AgCl reference electrode (saturated with KCl) as a reference, graphite rod as a counter electrode, and GCE (3 mm, diam.) as a working electrode.Data were corrected to reversible hydrogen electrode (RHE) without current and resistance (IR) modifications by employing the formula E(RHE) = E(Ag/AgCl) + 0.197 + 0.059pH.Cyclic voltammetry (CV) was executed over 200 cycles using a scan rate of 50 mV s −1 within the non-Faraday reaction voltage range, resulting in the acquisition of consistent CV curves.The scanning range of electrochemical double layer capacitance (C dl ) was 0.15 to 0.25 V at various scanning rates (20,40,60,80, and 100 mV s −1 ).Linear scanning voltammetry (LSV) was conducted with a scan rate of 1 mV s −1 over a voltage window from −0.6 to 0.1 V. Electrochemical impedance spectroscopy (EIS) measurements were conducted over a frequency interval from 0.01 Hz to 100 kHz with an amplitude of 5 mV.Electrochemical surface area (ECSA) was calculated based on CV curves using the formula ECSA = C dl /Cs, with Cs denoting the specific capacitance from 0.02 to 0.06 mF cm −2 .A mean value of 0.04 mF cm −2 was adopted in this study.

Conclusions
An introduction was provided on a hydrothermal approach for preparing catalysts such as SQDs, MoS 2 , and MoS 2 /SQDs.The characterization results of the synthesized materials were analyzed in detail using SEM, Raman, XRD, XPS, and TEM, confirming the successful synthesis of MoS 2 /SQD composite samples.Subsequently, the electrocatalytic activity of the MoS 2 /SQD composite material for the HER was investigated and compared to SQDs and self-synthesized MoS 2 .The results revealed the notably superior catalytic activity of the MoS 2 /SQDs composite catalyst compared to the aforementioned catalysts.The addition of SQDs significantly enhances the electrocatalytic performance of the MoS 2 catalyst, as evidenced by the characterization results for morphology, surface characteristics, and valence states of the elements.Molybdenum disulfide has a greater specific surface area and more edges, attributed to the presence of SQDs, leading to an increased number of catalytic active sites for the HER process.The research findings suggest that MoS 2 /SQDs have a reduced Tafel slope of 62.85 mV dec −1 and a decreased overpotential of 204 mV at 10 mA cm −2 .Besides its outstanding catalytic activity, the MoS 2 /SQDs catalyst also exhibits remarkable stability, with only a 17% reduction in initial current density after undergoing 24 h of timed current stability testing at 10 mA cm −2 .This presents a novel methodology for creating high-efficiency catalysts for the HER.

Molecules 2024 ,
29, x FOR PEER REVIEW 6 of 11 active component for HER, as indicated by the lower catalytic activity of SQDs.The combination of MoS2 and SQDs significantly enhances the catalytic performance of MoS2/SQDs in the HER process.

Figure 5 .
Figure 5.The electrochemical characteristics of each sample were evaluated using the following methods: (a) linear scanning voltammetry; (b) Tafel curve analysis; (c) estimation of the

Figure 5 .
Figure 5.The electrochemical characteristics of each sample were evaluated using the following methods: (a) linear scanning voltammetry; (b) Tafel curve analysis; (c) estimation of the electrochemical active area; (d) measurement of the electrochemical impedance spectra; (e) assessment of the stability of the MoS 2 /SQDs samples over a 24 h period.To comprehend the HER mechanism, we determined Tafel slopes by fitting the linear portion of the Tafel plots.Figure 5b depicts that the Tafel slope of the MoS 2 /SQDs catalyst is 65.82 mV dec −1 , lower than that of MoS 2 (132.44 mV dec −1 ) and SQDs (289.14 mV dec −1 ), indicating higher HER rates and faster kinetics for the MoS 2 /SQDs catalyst.A Tafel slope value of 65.82 mV dec −1 suggests the occurrence of the Volmer-Heyrovsky mechanism on MoS 2 /SQDs during the HER process, where the Heyrovsky step dictates the reaction rate.Combining SQDs with MoS 2 improves the separation of water molecules in the Volmer step, leading to increased HER kinetics and faster rates of charge transfer.The ECSA of catalysts is determined by estimating the catalyst's electrochemical C dl , measured using CV in the non-Faradaic zone with gradually increasing scan rates.Among

3. 5
. Characterization X-ray diffraction (XRD; MiniFlex-600, Rigaku, Tokyo, Japan) with a CuKα source was used to analyze the crystalline condition of samples.X-ray photoelectron spectroscopy (XPS; K-Alpha, Thermo Scientific, Waltham, MA, USA) was used to analyze the elemental valence of materials.Transmission electron microscopy (TEM; JEM-2100, JEOL Ltd., Tokyo, Japan) was used to test the grain size of the samples.Scanning electron microscopy (SEM; KYKY-EM 6900, KYKY Technology Co., Ltd., Beijing, China) was utilized to observe the morphology of the samples.Fourier-transform infrared (FTIR; FTIR-2000, PerkinElmer, Waltham, MA, USA) spectrometry was employed to analyze the structure of the samples.Molecules 2024, 29, 2551 9 of 11