Spectroscopic Investigations of Porphyrin-TiO2 Nanoparticles Complexes

This study presents the spectral characterization of TiO2 nanoparticles (NPs) functionalized with three porphyrin derivatives: 5,10,15,20-(Tetra-4-aminophenyl) porphyrin (TAPP), 5,10,15,20-(Tetra-4-methoxyphenyl) porphyrin (TMPP), and 5,10,15,20-(Tetra-4-carboxyphenyl) porphyrin (TCPP). UV-Vis absorption and Fourier transform infrared spectroscopy–attenuated total reflection (FTIR-ATR) spectroscopic studies of these porphyrins and their complexes with TiO2 NPs were performed. In addition, the efficiency of singlet oxygen generation, the key species in photodynamic therapy, was investigated. UV-Vis absorption spectra of the NPs complexes showed the characteristic bands of porphyrins. These allowed us to determine the loaded porphyrins on TiO2 NPs functionalized with porphyrins. FTIR-ATR revealed the formation of porphyrin-TiO2 complexes, suggesting that porphyrin adsorption on TiO2 may involve the pyrroles in the porphyrin ring, or the radicals of the porphyrin derivative. The quantum yield for singlet oxygen generation by the studied porphyrin complexes with TiO2 was higher compared to bare porphyrins for TAPP and TMPP, while for the TCPP-TiO2 NPs complex, a decrease was observed, but still maintained a good efficiency. The TiO2 NPs conjugates can be promising candidates to be tested in photodynamic therapy in vitro assays.


Introduction
In the last years, photodynamic therapy (PDT) has attracted significant interest for cancer treatment and the inactivation of microorganisms [1]. PDT implies a combination of photophysical and photochemical processes that lead to biological effects. Photosensitizers (PS) are well known for their use in PDT [2] or in Antimicrobial Photodynamic Therapy (APDT) [3]. Visible light irradiated PS have high efficiency in generating very reactive species such as singlet oxygen, which can destroy the cancer cell or kill various pathogens [4].
In subsequent photon absorption, the PS molecules are excited to their singlet state S 1 . Part of the energy is emitted as fluorescence and/or is lost in internal conversion by decaying back on the ground energy state, and the remaining energy directs PS molecules to the excited triplet state [5,6]. PSs can follow two types of mechanisms of photodynamic reaction, both being closely dependent on oxygen molecules inside cells.
For Type I, in the excited triplet state, the PS can transfer energy to the biomolecules from its surroundings. Between the PS in the triplet state and the disease tissue (or substrate), a hydrogen or electron is transferred, which leads to the formation of free radicals and anion radicals of the PS and the substrate. Electrons interact with oxygen molecules, into TiO 2 's conduction band and subsequent formation of˙O 2 − and˙OH with O 2 adsorbed on the surface of TiO 2 [31]. Efficient electron transfer from the excited PS to the TiO 2 conduction band requires good electronic coupling between the lowest unoccupied orbital (LUMO) of the PS and the Ti 3d orbitals. Effective coupling has typically been accomplished with carboxylate or phosphonate groups, which bind tightly to the TiO 2 surface [33].
The PS-TiO 2 complexes that were synthesized via either chemical functionalization or mixed covalent/noncovalent approach in organic solvents and in water [35] showed potential as catalysts for biomedical and environmental applications, as material for dyesensitized solar cells, and as photosensitizers for PDT [24,36,37].

Morphological Characterization of the Porphyrin-TiO 2 Complexes
The SEM images of TiO 2 sample and the complexes of TiO 2 with porphyrins (TAPP, TCPP, TMPP) are depicted in Figure 1a-d. In Figure 1a, the TiO 2 sample shows a surface with nanoparticles with dimensions between 17.1-23.2 nm (Table 1), but for the TiO 2 -TAPP sample (Figure 1b) The results of EDS investigations for TiO 2 and TiO 2 -porphyrin samples, mass percentage, and atomic percentage are presented in Table 1. Regarding the chemical composition of the TiO 2 complexes, analysis showed mostly Ti content, O, C, and N atoms, without other elements. The structural and morphological results revealed that porphyrins were uniformly dispersed on the surface of the TiO 2 and that the synthesis process has an important role in the quality of the TiO 2 -porphyrin complexes.
The mean hydrodynamic size and zeta potential of TiO 2 and the porphyrin-NPs suspensions were measured by DLS. These results are shown in Table 2. The larger values of the sizes could be explained firstly because DLS approximates the aggregates to a theoretical sphere. The size of this sphere is also influenced by the thickness of the solvation shell (electrical double layer) [38]. Secondly, the coalescence and compactization phenomena take place due to centrifugation forces during preparation, and these processes cannot be completely reversed when they were dispersed by ultrasonication [39]. The polydispersity indexes shown in Table 2 indicated a broad size distribution in the samples [40].
The zeta potential of TiO 2 suspensions was −50.3 mV. The formed complexes have zeta potential values in the same range, as follows: TiO 2 -TAPP zeta potential was −46.8 mV, −44.1 mV for TiO 2 -TMPP, and −44.0 mV for TiO 2 -TCPP. The obtained values indicate a fairly good stability. In general, suspensions having zeta potential higher than −30 mV (in absolute value) can be taken into consideration for pharmaceutical applications [41].

UV Vis Absorption Spectroscopy
The absorption spectra of TAPP, TMPP, TCPP, and Protoporphyrin IX (PPIX) solutions in N-N-dimethylformamide (DMF) are shown in Figure 2. All compounds exhibit a Soret band between 400-450 nm as the main absorption feature, which is specific for porphyrins. The maxima of these are placed at 407 nm-PPIX, 419 nm-TCPP, 422 nm-TMPP, and 435 nm-TAPP. All porphyrins also show lower intensity Q absorption bands between 480-700 nm. The absorption spectra of porphyrin-functionalized TiO 2 nanoparticle suspensions in DMF are shown in Figure 3. The characteristic absorption feature of porphyrins, the Soret bands arising at 400-450 nm, as well as lower intensity bands in longer wavelength spectral ranges can be observed. The nanoparticle loading with porphyrins can be determined by evaluating the absorbance of the major peak of the compounds, which is further compared with spectra obtained at known concentrations of the solutions ( Figure 2). Thus, for all suspensions of TiO 2 nanoparticles with a concentration of 0.024 mg/mL of TiO 2 , a concentration of porphyrins of 0.4 × 10 −6 M is obtained. The origin of the UV-Vis spectroscopic feature of TAPP was studied by Giovanelli et al. [42]. They found that several features are clearly due to the amino group of TAPP, whose effect on the UV-Vis spectrum consists of an overall red-shift and remarkable intensity changes within the Q band.
Electron-donor amino functionalization was found to reduce the HOMO-LUMO electronic transport gap and to increase the HOMO to HOMO−1 energy separation in a way that is consistent with an orbital destabilization process [42].

Fourier Transform Infrared Spectroscopy-Attenuated Total Reflection (FTIR-ATR)
The FTIR-ATR spectra of the porphyrin derivatives (TAPP, TMPP, TCPP) of TiO 2 NPs and of TiO 2 NPs loaded with each porphyrin were recorded. The frequencies observed for each porphyrin were compared with the theoretical frequencies, calculated with Gaussian 09 suite [43]. The assignation of the vibrations was conducted with Gauss View 5.0, which shows exactly the chemical bonds that vibrate for each calculated frequency, and was compared with specialized literature [43][44][45][46].
The observed frequencies for TAPP, as well as the ones calculated with Gaussian 09 suite, and the vibrations of the bonds assigned for each frequency, are given in Table 3.
The FTIR-ATR spectrum of TAPP ( Figure 4) presents absorption bands that can be assigned based on calculated frequencies to stretching and deformation vibrations of chemical bonds from porphyrin rings, as well as from the aminophenyl radicals, or from both.
The absorption bands that arise at wavenumbers over 3400 cm −1 can be assigned to stretching vibrations of NH bonds. The domain 3000-3350 cm −1 contains bands that originate in the CH stretching vibrations from the porphyrin ring, as well as from the aminophenyl radicals. NH bending vibrations contribute to the appearance of absorption bands below 1730 cm −1 in the FTIR-ATR spectrum of TAPP. In the range 1250-1670 cm −1 , there is also a contribution of the CC stretching vibrations to the rise of the absorption bands. CN stretching vibrations participate in the appearance of bands with maxima between 960 and 1470 cm −1 . CC bending vibrations give rise to absorption bands with maxima between 960 and 1120 cm −1 . CH bending vibrations contribute to the appearance of the absorption bands in the range of 740-1670 cm −1 . Furthermore, in Figure 4, the recorded IR spectrum of TAPP is compared with the ones recorded for TiO 2 NPs and for TiO 2 NPs loaded with TAPP (TiO 2 -TAPP).
FTIR-ATR spectrum of TiO 2 NPs presents one absorption band with the maximum at 1647 cm −1 , followed by one shoulder at 1580 cm −1 , two lower intensity peaks at 1460 cm −1 and 1384 cm −1 , and one last, also large, band between 850-600 cm −1 . This last band has its maximum at 686 cm −1 and it is preceded by a shoulder at 900 cm −1 . The large absorption band having the maximum at 3275 cm −1 is due to OH stretching vibration along with CH stretching vibrations and overtones of the C=O stretching vibrations. C=O stretching vibrations from the carboxylate groups are responsible for the appearance of the absorption bands with maxima at 1647 cm −1 and 1580 cm −1 . Carboxylate and alkyl groups come from the precursors used in the synthesis of TiO 2 , namely titanium isopropoxide and isopropyl alcohol [47,48]. The absorption bands with maxima at 1460 cm −1 and 1384 cm −1 are due to CH 2 bending vibrations. Vibrational modes of Ti-O-Ti, along with CH out-of-plane deformation vibrations from alkyl groups, may be responsible for the appearance of the large absorption band between 650 and 1000 cm −1 [47,48].  Figure 4 shows the spectral modifications that are occur during the functionalization of TiO 2 NPs with TAPP. One important modification is the increase in intensity of the peak at 1647 cm −1 . To ensure that this increase is not due to a difference in the thickness of the sample, the ratio between the intensities of the TiO 2 -TAPP peak and the TiO 2 peak at 1647 cm −1 was compared with a similar ratio calculated for the intensities at 787 cm −1 , where the maximum of the absorption band was recorded for TiO 2 -TAPP. For this, the ratio R ν , was determined as follows: The ratio calculated for the absorbances recorded at 1647 cm −1 , R 1647 , was 4.05, while R 787 was 1.77, demonstrating that the difference in the maxima of absorbance is not caused by a variation in samples thickness. This shows that in the rise of the peak at the 1647 cm −1 can contribute, along with C=O stretching vibrations and OH bending vibrations from TiO 2 , CC stretching vibrations, and CH bending vibrations from TAPP.
Prior to the peak at 1647 cm −1 , two bands with shoulder appearance are observed in the spectrum of TiO 2 -TAPP at 1730 cm −1 and 1712 cm −1 . The absorption band with the maximum at 1730 cm −1 is present in the TAPP spectrum and can be attributed to NH 2 bending vibrations in the aminophenyl radicals, but its intensity is much lower in the TiO 2 -TAPP spectrum, suggesting a disruption of NH bonds in these radicals. The band at 1712 cm −1 is distinctive from TAPP and TiO 2 absorption bands, and can be attributed to the interaction of C=O stretching vibrations of TiO 2 and C=N stretching vibrations, and CC stretching vibrations of TAPP.
At the same time, the absorption bands of TAPP with maxima 1668 cm −1 and 1617 cm −1 are no longer present in the IR spectrum of TiO 2 -TAPP, suggesting the disruption of NH bonds in the NH 2 group from aminophenyl radicals.
The disappearance of the peaks at 1512 cm −1 and 1468 cm −1 indicates a reduction of CH bending, NH bending, and CC stretching vibrations. This suggests a stiffening of the porphyrin ring, which would appear if TiO 2 binds with the pyrroles from the TAPP ring. A similar binding between NPs and porphyrin derivatives was also proposed in [39,49].
The shoulder arising at 1550 cm −1 in TiO 2 -TAPP IR spectrum is due to NO stretching vibrations [44,45]. The appearance of this type of vibration indicates the formation of chemical bonds between oxygen from TiO 2 and nitrogen, either from TAPP porphyrin rings or from aminophenyl radicals of TAPP molecules.
The increase of the peak at 1433 cm −1 can be attributed to the C=C bond in the porphyrin ring [50], suggesting the presence of the TAPP bound to the TiO 2 surface, but also to the appearance of NO-stretching vibrations [44,45].
The formation of the TiO 2 -TAPP complex is also demonstrated by the rise of a peak at 1258 cm −1 . This absorption band appears due to CC and CN stretching, NH bending and CH bending vibrations, but also OH deformation and CO stretching vibration interactions.
The rise of absorption bands in the range 1175-1300 cm −1 can be assigned to NOstretching vibrations [44,45]. This type of chemical bond would appear by adsorbing TAPP on TiO 2 and bond formation between TiO 2 and pyrroles from porphyrin ring or TiO 2 and aminophenyl radicals.
CH bending vibrations, CN stretching, and CC bending vibrations are responsible for the appearance of the absorption bands with maxima at 1161 cm −1 , 1116 cm −1 , 1066 cm −1 , and 1030 cm −1 in the IR spectrum of TiO 2 -TAPP.
The absorption bands that appear in the FTIR-ATR spectrum of TiO 2 -TAPP between 650-1000 cm −1 are due to association of Ti-O-Ti vibrational modes with NH bending, CH bending, CC bending, and CN stretching vibrations from TAPP. In addition, NO deformation vibrations can contribute to the appearance of absorption bands in the range 840-895 cm −1 [44,45]. Zoltan et al. reported [51] a broadening of the band observed in the range 600-1000 cm −1 in the IR spectrum of TiO 2 functionalized with a porphyrin derivative, suggesting N-O-Ti interactions in the material surface.
The modifications observed in the IR spectrum of TiO 2 -TAPP indicate the formation of N-O-Ti bonds, which demonstrate the functionalization of the NPs with TAPP molecules. The IR spectrum demonstrates the disruption of part of the NH 2 groups indicating that TAPP binds to TiO 2 through aminophenyl radicals. Simultaneously, the comparison between TAPP and TiO 2 -TAPP spectra reveals a stiffening of the porphyrin ring and a decrease of NH bonds, indicating the formation of N-O-Ti bonds between the pyrroles from porphyrin ring and NPs. Table 4 presents the frequencies observed in the FTIR-ATR spectrum of TMPP ( Figure 5) compared with the calculated frequencies, as well as the assignation of the vibrational bands to the responsible chemical bonds.
The range of 3000-3320 cm −1 presents absorption bands that can be attributed to CH stretching vibrations. CC stretching vibrations, from both porphyrin ring and/or methoxyphenyl radicals, contribute to the appearance of bands between 900-1680 cm −1 . The bands observed in the region 900-1680 cm −1 also have origins in the CH bending vibrations. NH bending vibrations give rise to absorption bands with maxima between 900-1605 cm −1 . The presence of absorption bands in the 900-1410 cm −1 region is also due to CN stretching vibrations from the porphyrin ring or from both porphyrin and methoxyphenyl radicals. CO stretching vibrations contribute to the formation of bands at wavenumbers between 1060-1280 cm −1 .
In Figure 5, the FTIR-ATR spectrum of TiO 2 -TMPP shows the absorption bands characteristic to TMPP, as well as modified peaks that show the loading of TiO 2 NPs with TMPP.  The main modifications are represented by the increase in intensity of the peaks between 960 and 1400 cm −1 , as well as the appearance of new absorption bands with maxima at 840 cm −1 , 805 cm −1 , 785 cm −1 , and 737 cm −1 .
The possible increase of CC and CN stretching vibrations and CH bending vibrations from the porphyrin ring is responsible for the rise of the absorption band at 1382 cm −1 . The increase of the peak at 1350 cm −1 suggests an increment in CC stretching and CH bending vibrations. Potential increment of CH and NH bending vibrations, as well as CN and CC stretching vibrations, causes the rise of the peak at 1289 cm −1 . The rise of the absorption band at 1247 cm −1 indicates an ascent in CC and CO stretching vibrations, along with CH bending vibrations from methoxyphenyl radicals, as well as CC and CN stretching vibrations and CH and NH bending vibrations from the porphyrin ring. A rising trend of CH bending vibrations, together with CN and CC stretching vibrations, is accountable for the increment of the absorption band at 1172 cm −1 . Similarly, the increase of CH bending vibrations are responsible for the rise of the peak at 1105 cm −1 . The rise of the band at 1085 cm −1 is due to an increment of CO and CC stretching vibrations along with CH bending vibrations. The increase of CC and CN stretching vibrations from the porphyrin ring, along with CH bending vibrations, are responsible for the upsurge of the absorption bands with maxima at 1036 cm −1 and 965 cm −1 .
The rise of the absorption bands in the region 1150-1360 cm −1 may be attributed to the CO stretching vibrations of TMPP in interaction with the OH deformation vibration of possible bonds that can be formed between TMPP and TiO 2 [44,45]. NO stretching vibrations may also contribute to the appearance of bands in this range, indicating the formation of bonds between the pyrroles in the porphyrin ring and TiO 2 NPs [39,49].
The new absorption bands that appear in the IR spectrum of TiO 2 -TMPP with maxima at 840 cm −1 , 805 cm −1 , 785 cm −1 , and 737 cm −1 are due to the overlay of CC, CN, CH, and NH bending vibrations, as well as NO deformation vibrations, OH deformation, and CO stretching vibration interactions.
The IR spectrum of TiO 2 -TMPP evidences the functionalization of TiO 2 NPs with TMPP. The appearance of new absorption bands attributed to NO vibrations indicates that TMPP can bind to TiO 2 via N-O-Ti interactions between the pyrroles of the porphyrin ring and NPs. The increase of the absorption bands assigned to CO vibrations suggest the possibility to form O-C-O-Ti bonds if TMPP binds to TiO 2 through methoxyphenyl radicals.
The assigned vibrations of TCPP for each observed in the FTIR-ATR spectrum ( Figure 6) and calculated frequency are presented in Table 5, evidencing what parts of the molecules the responsible chemical bonds belong to (porphyrin ring, carboxyphenyl radicals, or both).
The absorption peaks between 3070-3320 cm −1 are due to stretching vibrations of CH chemical bonds from porphyrin ring or from carboxyphenyl radicals.    The modifications induced by adsorption of TCPP on TiO 2 NPs in the IR spectrum, in comparison to the spectra of TCPP and TiO 2 , can be seen in Figure 6.
FTIR-ATR spectrum of TiO 2 -TCPP presents the absorption bands characteristic to TiO 2 NPs, but also important differences that suggest the loading of TCPP on TiO 2 .
The peak at 1647 cm −1 , due to C=O stretching vibrations from carboxylate groups remaining from TiO 2 precursors, is followed by a shoulder with a maximum at 1604 cm −1 . This band is due to CC ring stretching vibrations along with CH and NH bending vibrations of TCPP.
A superposition of bands appears in the region 1350-1560 cm −1 , with maxima at 1541 cm −1 , 1510 cm −1 , 1458 cm −1 , 1407 cm −1 , and 1375 cm −1 . CC stretching vibrations, CN stretching vibrations from porphyrin ring, as well as CH, NH, and CN bending vibrations characteristics to TCPP, which participate in the formations of these absorption bands.
In the region 650-950 cm −1 , one large absorption band may be observed, with the maximum at 765 cm −1 , and another shoulder with the maximum at 901 cm −1 . These bands may appear due to superposition of Ti-O-Ti vibrational modes with NH, CH, CC, CO bending vibrations of TCPP, as well as CC and CN stretching from TCPP porphyrin ring.
A significant element represents the disappearing of some characteristic bands for TCPP, namely the peaks at 1918 cm −1 , 1724 cm −1 , 1686 cm −1 , and 1633 cm −1 , as well as the ones between 1210-1315 cm −1 . These modifications are an indicative of reduction in C=O stretching vibrations and OH bending vibrations, as well as a decrease of the vibrations coming from carboxyphenyl radicals, suggesting that TCPP binds to TiO 2 through these radicals. Similar findings suggest that TCPP is chemisorbed on the surface of TiO 2 , forming Ti-O-C=O bonds [52,53].
The changes observed in the FTIR-ATR spectrum of TiO 2 -TCPP suggest that the loading of TiO 2 NPs with TCPP may be similar to the one presented in [54], where carboxylfunctionalized porphyrins create surface-anchored connecting carboxylates with TiO 2 NPs through the carboxylic acid radical.
Modifications observed in the FTIR-ATR spectra of the complexes formed by TiO 2 loading with porphyrin derivatives TAPP, TMPP, and TCPP, respectively, suggested that the adsorption of porphyrin may involve the pyrroles in the porphyrin ring, as suggested in [39,49], or may implicate the radicals of the porphyrin derivative [54].

Singlet Oxygen Generation
Based on the analysis of the absorption spectra, the concentration of the porphyrin photosensitizer in the nanoparticle suspensions was established to determine their quantum efficiency for the generation of singlet oxygen, a reactive species used in PDT.
The singlet oxygen quantum yield was determined using a standard solution of protoporphyrin IX (PPIX) in DMF as a reference. The time-resolved phosphorescence signal of the generated singlet oxygen (λ = 1270 nm) was recorded under the same conditions for porphyrin solutions, suspensions with porphyrin-functionalized TiO 2 nanoparticles, and the PPIX standard in DMF. The quantum yield was calculated according to the formula: where Φ is the singlet oxygen generation yield, I is the singlet oxygen phosphorescence intensity, A is the sample absorption, τ is the singlet oxygen lifetime, n is the refractive index of the solvent, and the ref index corresponds to the reference sample values. The phosphorescence intensity is obtained by extrapolating the mono-exponential phosphorescence kinetics fitting curve at t = 0. The quantum yield for singlet oxygen generation for PPIX in DMF was determined as 0.85 by measuring its phosphorescence kinetics relative to PPIX in ethanol, which has Φ = 0.92 [55]. Figure 7a-c exhibits the time-resolved phosphorescence signals for singlet oxygen generated by porphyrin solutions and suspensions in DMF containing TiO 2 NPs complexes with TAPP, TMPP, and TCPP, in comparison with PPIX, which was used as standard. TiO 2 suspensions did not present a phosphorescence signal and generation of singlet oxygen when excited with 532 nm radiation. Following the processing and analysis of phosphorescence signals, by using Equation (2), the quantum yield for singlet oxygen generation was obtained for the studied porphyrins and the suspensions of their complexes with TiO 2 . The photophysical data on singlet oxygen generation were summarized below in Table 6.
It can be noticed that the quantum yield for generation of singlet oxygen by the studied porphyrins is smaller compared with their conjugates with TiO 2 for TAPP and TMPP, while for the TCPP-TiO 2 NPs complex, a decrease is observed.
A potentation effect on photodynamic activity can take place by shifting the response of TiO 2 in the visible range [56].
The TiO 2 nanoparticles can be photosensitized and produce ROS by electron transfer from the visible light-excited PS. While photogenerated electrons react with dissolved oxygen molecules to produce •O 2 − , photogenerated holes mostly react with the water in the surroundings to produce OH radicals. Some •O 2 − can form 1 O 2 by reacting with the holes [57]. From these two species, ROS produced by TiO 2 is 1 O 2 rather than•O 2 − [58]. In contrast, the interaction of PS with TiO 2 and the energy transfer is related to the radicals as anchoring groups of the porphyrins [54,59]. The carboxyl groups favorized these interactions in the adsorption of TCPP on TiO 2 surface [59], which was how it was observed from the FTIR spectra as well. These stronger interactions compared with the methyl or amino porphyrin derivatives possibly favorized the formation of OH rather than 1 O 2 radicals. Further investigations should be made to evaluate the contribution of each species in the ROS formed.
The best value of quantum yield was obtained for TiO 2 -TMPP; still, all of the complexes of the studied porphyrins with TiO 2 NPs exhibited a good efficiency in singlet oxygen generation. Due to TiO 2 non-toxicity to living organisms, its stability in water, its photocatalytic activity [36], and its potential as a drug carrier, the studied complexes are good candidates for further photodynamic therapy in vitro assays either on tumoral cell lines or microorganisms such bacteria.
The functionalization of TiO 2 NPs with the selected porphyrins was performed according to the methods detailed in the literature [32,50,60]. Mixtures of TiO 2 and porphyrins were prepared using a 1:3 ratio of 0.1 mg/mL suspensions of TiO 2 in DMF with 2.5 × 10 −5 M porphyrin solutions in DMF. The resulting mixtures were sonicated for 5 h and were then kept at room temperature in the dark for 24 h. In the next step, the suspensions were centrifuged for 10 min at 12,000 rpm, and the supernatant was removed in order to eliminate the number of porphyrins that were not adsorbed on the nanoparticles' surfaces. The solid deposit was then redispersed in the same volume of DMF using the ultrasound bath for 30 min.
The morphology and structural characteristics of the synthesized TiO 2 and TiO 2porphyrin samples were investigated by scanning electron microscopy (SEM) using an Apreo S microscope from FEI (Thermo Fisher Scientific, Waltham, MA, USA) with an energy-dispersive X-ray spectroscopy (EDS) system, fixed silicon detector, and integrated Peltier element as a cooling system. SEM analyses were performed at an acceleration voltage of 15 kV, in the magnification range of 100,000×, at 10 cm working distance, and a spot beam of 3. For EDS, the used beam spot was 6.5-7, the working distance was 10 cm, and the dead time was 30 s. It was also operated at 10 kV acceleration voltage and 6.3 pA electrical current.
The hydrodynamic size and stability of the nanoparticle suspensions, as well as the porphyrin-functionalized TiO 2 NPs suspensions, were analyzed by dynamic light scattering (DLS) using Nanoparticle Analyzer SZ-100V2 (Horiba, Kyoto, Japan). This employs a diodepumped solid-state laser emitting at 532 nm and a scattering angle of 173 • . Hydrodynamic size measurements were performed in triplicate for 1 mL volume of each suspension placed in a quartz cuvette cell. For zeta potential measurements, an electrophoretic cell with carbon electrodes (6 mm) was used with a lower volume of solution.
The porphyrin loading for the functionalized nanoparticles was assessed by absorption spectroscopy. The absorption spectra of porphyrin solutions and their suspensions in quartz cells of 1 cm pathlength were measured in the 300-700 nm spectral range using a spectrophotometer Lambda 950 (Perkin-Elmer, Waltham, MA, USA) with 1 nm spectral resolution.
FTIR-ATR spectroscopy measurements have also been conducted to highlight the emergence of nanocompound complexes with porphyrin derivatives, and to assess the possible modification of their functional groups. The FTIR-ATR spectra of the three porphyrin derivatives, as well as spectra of their complexes with TiO 2 NPs, were recorded. For this purpose, a volume varying between 100 and 200 µL from each sample was dried on polyethylene (PE) FTIR-cards. Individual 5 µL drops of the sample were dried repeatedly in order to obtain a greater thickness of the sample, which was an implicitly higher optical path. IR spectra were registered using the ATR module of the FTIR NicoletTM iSTM50 spectrometer (Thermo Fisher Scientific, Waltham, MA, USA) in the spectral range 4000-650 cm-1, with 4 cm-1 spectral resolution. Each spectrum represents a mediation of 16 recordings. The sample was placed facing the ZnSe crystal (internal reflection at an incidence angle of 42 • , diameter 1.5 mm, refractive index 2.4, and penetration depth 2.03 µm at 1000 cm −1 ).
The theoretical IR spectra were calculated using Gaussian09 software [43]. The molecular structure was subjected to geometry optimization followed by the calculation of vibrational wavenumbers using the density functional theory (DFT). The hybrid functional B3LYP method with 6-311G(d,p) basis set was used.
The attainment of quantum yield for singlet oxygen generation was performed using the experimental system described elsewhere [61] and based on the measurement of the time-resolved phosphorescence of singlet oxygen at 1275 nm. The excitation source was the second harmonic generation of the pulsed Nd:YAG laser (Minilite II, Continuum), which was emitted at 532 nm with 3 mJ excitation energy and 10 Hz frequency. The phosphorescence was measured using an electronically cooled NIR photomultiplier (Hamamatsu H-10330) whose signal was digitized by an oscilloscope (Tektronix DPO 7254). The sample was placed in a photometric cuvette with an optical pathlength of 1 cm. The phosphorescence was collected at a right angle and was filtered to eliminate wavelengths other than 1270 nm by a suitable optical arrangement (aperture lenses and interference filters) placed in the front of the photomultiplier.

Conclusions
The spectral investigations of TiO 2 nanoparticle complexes with TAPP, TMPP, and TCPP porphyrins was performed. The morphological characterization of the samples revealed the formation of porphyrin-TiO 2 complexes.
The UV-Vis absorption spectra of the complexes showed the characteristic bands of porphyrins and these were used to determine the concentration of adsorbed porphyrins on TiO 2 NPs surface.
FTIR-ATR spectra of each porphyrin-TiO 2 complex showed vibrational bands characteristic to TiO 2 NPs together with peaks typical for porphyrins, but also included changes that suggested the loading of TiO 2 with porphyrins. These analyses indicated that the functionalization of NPs with porphyrin derivatives TAPP, TMPP, and TCPP, respectively, involves either the pyrroles in the porphyrin ring, or it implies the bonding of TiO 2 with the radicals of the porphyrin derivative.
In the case of TiO 2 -TAPP, the appearance of absorption bands assigned to NO vibrations suggested that TAPP binds to TiO 2 via N-O-Ti bonds. The binding could take place either through aminophenyl radicals-considering that the IR spectrum shows a decrease in the signal originating from NH 2 groups-or through the pyrroles of the porphyrin ring because a rigidity of the porphyrin ring and a reduction of NH bonds was also observed. Evidence of N-O-Ti bonds also appeared in the IR spectrum of TiO 2 -TMPP, suggesting that TMPP can bind to TiO 2 through the pyrroles of the porphyrin ring. The rise in the absorption bands assigned to CO vibrations indicated the possibility of forming O-C-O-Ti bonds between the methoxyphenyl radicals and NPs. IR spectrum of TiO 2 -TCPP suggested that the binding of TCPP to TiO 2 takes place via carboxyphenyl radicals, forming Ti-O-C=O bonds.
The studied porphyrin complexes with TiO 2 NPs showed good efficiency in singlet oxygen generation. Further investigations will be devoted to the evaluation of the contribution of other reactive oxygen species generated by complexes due to the presence of the TiO 2 photocatalyst.
The complexes analyzed in this study represent promising candidates for further photodynamic therapy in vitro assays either on tumoral cell lines or microorganisms such as bacteria.

Conflicts of Interest:
The authors declare no conflict of interest.
Sample Availability: Not applicable.