Green Synthesis and Applications of ZnO and TiO2 Nanostructures

Over the last two decades, oxide nanostructures have been continuously evaluated and used in many technological applications. The advancement of the controlled synthesis approach to design desired morphology is a fundamental key to the discipline of material science and nanotechnology. These nanostructures can be prepared via different physical and chemical methods; however, a green and ecofriendly synthesis approach is a promising way to produce these nanostructures with desired properties with less risk of hazardous chemicals. In this regard, ZnO and TiO2 nanostructures are prominent candidates for various applications. Moreover, they are more efficient, non-toxic, and cost-effective. This review mainly focuses on the recent state-of-the-art advancements in the green synthesis approach for ZnO and TiO2 nanostructures and their applications. The first section summarizes the green synthesis approach to synthesize ZnO and TiO2 nanostructures via different routes such as solvothermal, hydrothermal, co-precipitation, and sol-gel using biological systems that are based on the principles of green chemistry. The second section demonstrates the application of ZnO and TiO2 nanostructures. The review also discusses the problems and future perspectives of green synthesis methods and the related issues posed and overlooked by the scientific community on the green approach to nanostructure oxides.


Introduction
Green technologies have gained enormous attention over the last decade. Natural resources are being depleted daily, and the green approach appears to be a prominent solution without destroying natural resources. This technology deals with the fabrication of nanomaterials and their applications in the medical, sensor, optoelectronics, energy, food industries, etc. [1]. There are many physical and chemical methods of preparing metal nanoparticles (NPs) and metal oxide nanostructures such as sputtering, lithography, and electrospinning. However, they are quite expensive, and involvement with toxic chemicals results in health risks. In this regard, the green synthesis approach does not require any harmful chemicals, high-pressure reactors, or high temperatures. Most importantly, it results in degradable waste with less risk of contamination at the end [2,3]. Over the past few years, researchers have shown interest in green chemistry to synthesize NPs using environmentally benign agents such as plants, fruits, flowers, algae, yeasts, bacteria, fungi. Additionally, extensive research has been carried out using plant extracts for the synthesis of NPs, and it was observed that compared to other means, plants are more suitable for the production of NPs, even at the pilot scale [4][5][6][7][8][9].

Green Synthesis Methods of TiO2 and ZnO Nanostructures
This review summarizes the most widely used green synthesis methods in the fabrication of TiO2 and ZnO nanostructures for technological applications such as photocatalytic, supercapacitor, solar cell, and gas sensors. Our main objective was to shed light on the scope of solvothermal, hydrothermal, co-precipitation, and sol-gel methods and their advantages, drawbacks, and research advancements.

Sol-Gel Synthesis
Sol-gel is a widely used method of synthesizing ceramic oxide nanostructures from solution by transforming liquid precursors to "sol" and ultimately to a network structure called "gel" in wet chemical phases [32]. The composition of the sol is usually achieved by hydrolysis and condensation of metal alkoxide precursors. Still, a sol may generally be called a colloidal suspension involving a more comprehensive range of systems. There are also several different ways to form a gel, which Flory described in 1974. He divided gel

Green Synthesis Methods of TiO 2 and ZnO Nanostructures
This review summarizes the most widely used green synthesis methods in the fabrication of TiO 2 and ZnO nanostructures for technological applications such as photocatalytic, supercapacitor, solar cell, and gas sensors. Our main objective was to shed light on the scope of solvothermal, hydrothermal, co-precipitation, and sol-gel methods and their advantages, drawbacks, and research advancements.

Sol-Gel Synthesis
Sol-gel is a widely used method of synthesizing ceramic oxide nanostructures from solution by transforming liquid precursors to "sol" and ultimately to a network structure called "gel" in wet chemical phases [32]. The composition of the sol is usually achieved by hydrolysis and condensation of metal alkoxide precursors. Still, a sol may generally be called a colloidal suspension involving a more comprehensive range of systems. There are also several different ways to form a gel, which Flory described in 1974. He divided gel into four groups: lamellar gel, ordered gel, disordered particulate gels, and physically aggregated polymers [33]. Later in 1996, Kakihana [34]. Table 1 outlines the five major categories of gel types used in sol-gel chemistry. Since there are many articles on the sol-gel synthesis approach used to fabricate various nanostructures, our goal was to show the green approach using sol-gel chemistry. Table 1. Classification of five different types of "gels" essential to a material's sol-gel synthesis [35].  Table 1. Classification of five different types of "gels" essential to a material's sol-gel synthesis [35].  Table 1. Classification of five different types of "gels" essential to a material's sol-gel synthesis [35].  Table 1. Classification of five different types of "gels" essential to a material's sol-gel synthesis [35].  Table 1. Classification of five different types of "gels" essential to a material's sol-gel synthesis [35]. Recently, researchers have demonstrated a high interest in the development of metal oxide NPs through a greener approach because they are eco-friendly, less toxic, and generate less hazardous waste. In this context, nanostructured oxide semiconductors have generated considerable interest due to the fact of their fundamental importance in addressing some of the main issues in fundamental physics and their possible applications as advanced materials. These nanostructures have been prepared by a variety of different fabrication methods. However, the reproducible and scalable synthesis of these nanostructures is the major difficulty for technological applications. Furthermore, many of these methods require expensive equipment and have little control over the scale, shape, and composition of NPs. In this way, the green approach of sol-gel processes can overcome some of the major limitations.

Green Sol-Gel Synthesis Approach for ZnO Nanostructures
Tu Uyen Doan Thi et al. [36] utilized the green sol-gel method to produce ZnO NPs by orange fruit peel extracts and studied the impact of pH and temperature on the morphology and antibacterial activities. Figure 2a shows a schematic of the ZnO NPs' synthesis in which zinc nitrate and orange extract powder were mixed, followed by annealing at 400 °C for one hour. Figure 2b shows the reaction mechanism between the orange peel extract and zinc precursor, where the orange peel extract acts as a ligand agent. They analyzed the morphology and antibacterial properties by annealing the ZnO NPs at different temperatures ranging from 300-900 °C. Figure 2c shows the X-ray diffraction pattern (XRD) of the ZnO NPs annealed at a different temperature; it can be seen that compared to high-temperature samples, the crystal structure and diffraction peaks were poor at a lower temperature. By increasing the annealing temperature, the crystalline size increased, and NPs became reoriented and reduced the number of defects in grain boundaries. Figure 2d shows the Fourier transform infrared spectra (FTIR) of ZnO NPs under different annealing temperatures; a vibration bonding Zn-O and orange peel extract at 450 and 1640 cm −1 were observed, respectively. Moreover, at low annealing temperatures, residual organic extract vibrations in the NPs were present, which gradually disappeared at higher annealing temperatures. Thermal stability and weight loss of the ZnO samples were evaluated by thermogravimetry Analysis (TGA). Significant weight loss was observed at a lower annealing temperature due to the loss of moisture and organic substances. In contrast, no weight loss was observed at higher annealing temperatures (Figure 2e).
Recently, researchers have demonstrated a high interest in the development of metal oxide NPs through a greener approach because they are eco-friendly, less toxic, and generate less hazardous waste. In this context, nanostructured oxide semiconductors have generated considerable interest due to the fact of their fundamental importance in addressing some of the main issues in fundamental physics and their possible applications as advanced materials. These nanostructures have been prepared by a variety of different fabrication methods. However, the reproducible and scalable synthesis of these nanostructures is the major difficulty for technological applications. Furthermore, many of these methods require expensive equipment and have little control over the scale, shape, and composition of NPs. In this way, the green approach of sol-gel processes can overcome some of the major limitations.

Green Sol-Gel Synthesis Approach for ZnO Nanostructures
Tu Uyen Doan Thi et al. [36] utilized the green sol-gel method to produce ZnO NPs by orange fruit peel extracts and studied the impact of pH and temperature on the morphology and antibacterial activities. Figure 2a shows a schematic of the ZnO NPs' synthesis in which zinc nitrate and orange extract powder were mixed, followed by annealing at 400 • C for one hour. Figure 2b shows the reaction mechanism between the orange peel extract and zinc precursor, where the orange peel extract acts as a ligand agent. They analyzed the morphology and antibacterial properties by annealing the ZnO NPs at different temperatures ranging from 300-900 • C. Figure 2c shows the X-ray diffraction pattern (XRD) of the ZnO NPs annealed at a different temperature; it can be seen that compared to high-temperature samples, the crystal structure and diffraction peaks were poor at a lower temperature. By increasing the annealing temperature, the crystalline size increased, and NPs became reoriented and reduced the number of defects in grain boundaries. Figure 2d shows the Fourier transform infrared spectra (FTIR) of ZnO NPs under different annealing temperatures; a vibration bonding Zn-O and orange peel extract at 450 and 1640 cm −1 were observed, respectively. Moreover, at low annealing temperatures, residual organic extract vibrations in the NPs were present, which gradually disappeared at higher annealing temperatures. Thermal stability and weight loss of the ZnO samples were evaluated by thermogravimetry Analysis (TGA). Significant weight loss was observed at a lower annealing temperature due to the loss of moisture and organic substances. In contrast, no weight loss was observed at higher annealing temperatures (Figure 2e).  Similarly, Sasirekha et al. [37] fabricated the ZnO/C nanocomposite via a cost-effective sol-gel method via a green approach in which they used sucrose as a capping agent. They studied the structural and electrochemical behavior of the prepared ZnO/C. Moreover, they performed electrochemical measurements which revealed a maximum specific capacitance of 820 F g −1 with a current density of 1 A g −1 . Moreover, when they performed charge-discharge up to 400 cycles, a power retention of 92% was observed. In another work by Silva and co-workers [38], it was reported for the first time the facile green solgel synthesis of ZnO NPs using whey as a chelating agent, characterizing the samples using different analytical techniques.
Sahoo and co-workers [39] reported ZnO NPs using acacia concinna fruit extract as a surfactant. They used the acacia concinna powder to prepare the Zinc precursor solution, followed by a mixing and calcination process to achieve pure ZnO NPs. Figure 3a shows the XRD pattern of pure ZnO NPs, which reveals the hexagonal wurtzite phase. The ZnO sample's sharp peak indicates the crystalline nature of the materials, and the Debye-Scherer equation measured the crystalline size (26 nm). Structural analysis of the ZnO sample was confirmed by scanning electron microscopy (SEM), and it can be seen that all the NPs were agglomerated (Figure 3b,c). The UV-Vis spectra of the ZnO NPs were analyzed at 498 nm at different time intervals, and it was found that there was a steady decrease in the intensity of the Congo red (CR) dye over time (Figure 3d). The FTIR analysis was carried out for the ZnO NPs, CR dye, and CR-loaded ZnO NPs (Figure 3e). The peaks observed at 1386 cm −1 and 1681 cm −1 indicate the C=O group's asymmetric stretching vibration. In addition, the peak at 1057 cm −1 was due to the occurrence of m (C-N), and the peaks at 1235 and 1178 cm −1 were due to the aromatic C-N stretching and absorption of CR. Even after loading the CR with ZnO NPs, there were no changes in peak positions and bands. Figure 3f displays the transmission electron microscopy (TEM) images of ZnO NPs. It appears that the particles were irregular with an average particle size of approximately 30 to 50 nm. Similarly, the research group of Guy Van Assche [40] reported the cost-effective green synthetic route "sol-gel injection" to incorporate ZnO NPs onto porous silica matrix. They also confirmed that by enclosing ZnO NPs in the silica matrix, there is a way to monitor the size of the particles, the size distribution, and the NPs' ability to aggregate and open up a new possibility to explore the application for catalysis and optical detection. Similarly, Sasirekha et al. [37] fabricated the ZnO/C nanocomposite via a cost-effective sol-gel method via a green approach in which they used sucrose as a capping agent. They studied the structural and electrochemical behavior of the prepared ZnO/C. Moreover, they performed electrochemical measurements which revealed a maximum specific capacitance of 820 F g −1 with a current density of 1 A g −1 . Moreover, when they performed chargedischarge up to 400 cycles, a power retention of 92% was observed. In another work by Silva and co-workers [38], it was reported for the first time the facile green sol-gel synthesis of ZnO NPs using whey as a chelating agent, characterizing the samples using different analytical techniques.
Sahoo and co-workers [39] reported ZnO NPs using acacia concinna fruit extract as a surfactant. They used the acacia concinna powder to prepare the Zinc precursor solution, followed by a mixing and calcination process to achieve pure ZnO NPs. Figure 3a shows the XRD pattern of pure ZnO NPs, which reveals the hexagonal wurtzite phase. The ZnO sample's sharp peak indicates the crystalline nature of the materials, and the Debye-Scherer equation measured the crystalline size (26 nm). Structural analysis of the ZnO sample was confirmed by scanning electron microscopy (SEM), and it can be seen that all the NPs were agglomerated (Figure 3b,c). The UV-Vis spectra of the ZnO NPs were analyzed at 498 nm at different time intervals, and it was found that there was a steady decrease in the intensity of the Congo red (CR) dye over time (Figure 3d). The FTIR analysis was carried out for the ZnO NPs, CR dye, and CR-loaded ZnO NPs (Figure 3e). The peaks observed at 1386 cm −1 and 1681 cm −1 indicate the C=O group's asymmetric stretching vibration. In addition, the peak at 1057 cm −1 was due to the occurrence of m (C-N), and the peaks at 1235 and 1178 cm −1 were due to the aromatic C-N stretching and absorption of CR. Even after loading the CR with ZnO NPs, there were no changes in peak positions and bands. Figure 3f displays the transmission electron microscopy (TEM) images of ZnO NPs. It appears that the particles were irregular with an average particle size of approximately 30 to 50 nm. Similarly, the research group of Guy Van Assche [40] reported the cost-effective green synthetic route "sol-gel injection" to incorporate ZnO NPs onto porous silica matrix. They also confirmed that by enclosing ZnO NPs in the silica matrix, there is a way to monitor the size of the particles, the size distribution, and the NPs' ability to aggregate and open up a new possibility to explore the application for catalysis and optical detection.  Majid Darroudi et al. [41] studied the temperature effect of zinc oxide NPs prepared using gum tragacanth (GT)-a green, economical, and readily available polysaccharide component. They mixed zinc nitrate as a zinc source and GT in the water and fixed it at 80 °C in an oil bath. The final product was washed, cleaned, and calcined at different temperatures (400-700 °C). Figure 4a displays the powder XRD of the ZnO NPs at different calcination temperatures. It can be seen that all the diffraction peaks with miller indices were indexed to a pure ZnO wurtzite structure with a crystalline size below 50 nm. The UV-Vis spectra of the ZnO NPs showed a 3.3 eV bandgap, and a sharp absorption peak at 370 nm was observed, which can be assigned to the absorption of the intrinsic bandgap because of the transition from the valence band to the conduction band ( Figure 4b). The TEM images (Figure 4c,d) indicate the narrow size distribution of the ZnO NPs in GT media with a mean size of approximately 33 nm confirmed with Image J software. These NPs are expected to find potential applications in various fields such as cosmetics, paints and coatings, sensors, and medicines.
Similarly, Araujo et al. [42] reported a novel approach to preparing ZnO NPs using karaya gum-a polysaccharide extracted from low-cost Sterculia species. The prepared ZnO NPs were characterized by analytical techniques and their photocatalytic performance was studied. Moreover, some biosynthesis approaches for the synthesis of ZnO nanostructures were reported using plant extracts, fruit, and leaves ( Table 2). Majid Darroudi et al. [41] studied the temperature effect of zinc oxide NPs prepared using gum tragacanth (GT)-a green, economical, and readily available polysaccharide component. They mixed zinc nitrate as a zinc source and GT in the water and fixed it at 80 • C in an oil bath. The final product was washed, cleaned, and calcined at different temperatures (400-700 • C). Figure 4a displays the powder XRD of the ZnO NPs at different calcination temperatures. It can be seen that all the diffraction peaks with miller indices were indexed to a pure ZnO wurtzite structure with a crystalline size below 50 nm. The UV-Vis spectra of the ZnO NPs showed a 3.3 eV bandgap, and a sharp absorption peak at 370 nm was observed, which can be assigned to the absorption of the intrinsic bandgap because of the transition from the valence band to the conduction band ( Figure 4b). The TEM images (Figure 4c,d) indicate the narrow size distribution of the ZnO NPs in GT media with a mean size of approximately 33 nm confirmed with Image J software. These NPs are expected to find potential applications in various fields such as cosmetics, paints and coatings, sensors, and medicines.
Similarly, Araujo et al. [42] reported a novel approach to preparing ZnO NPs using karaya gum-a polysaccharide extracted from low-cost Sterculia species. The prepared ZnO NPs were characterized by analytical techniques and their photocatalytic performance was studied. Moreover, some biosynthesis approaches for the synthesis of ZnO nanostructures were reported using plant extracts, fruit, and leaves ( Table 2).

Green Sol-Gel Synthesis Approach for TiO 2 Nanostructures
Several synthetic approaches to the preparation of TiO 2 nanostructures have been developed to date. The sol-gel method's green approach is widely used because of the eco-friendly and cost-effective concept for obtaining TiO 2 nanostructures. Li Yang et al. [89] reported the sol-gel route to synthesize TiO 2 microtubes using Platanus acerifolia seed fibers (SFs). Figure 5a,b show SEM images of the natural seed fibers that display the hollow tubular structures with a diameter of 25-30 µm and a wall thickness of 3-5 µm. Figure 5c,d show the titanium sol-impregnated fibers (TIFs), and Figure 5e shows the titanium fiber hybrid (TFH). The TiO 2 microtubes were obtained with further calcination of the TFH at 500 • C for two hours with an average diameter of 24 µm and a wall thickness of 2 µm (Figure 5f-h). With the high magnification of the image with the TiO 2 microtubes, it can be seen that the wall of the microtubes consisted of two layers, where NPs covered the outer wall with a rough surface, and the inner wall was very smooth and compact ( Figure 5i). Furthermore, Figure 5j shows the enlarged view of the TiO 2 microtubes' inner wall that was composed of a dense structure of TiO 2 nanospheres of a diameter of 25 ± 5 nm. We can further understand the double soaking sol-gel route of the synthesized TiO 2 microtubes based on the morphological changes. Figure 5k shows a schematic of the fabrication process of the TiO 2 microtubes, and the first soaking step was to hydrolyze natural seed fibers with titanium sol to generate the metal alkoxide layer on the fibers' surface. Once the Titanium sol was completely hydrolyzed on the deionized water, they formed the rough external wall that was the second soaking step. The final product was obtained with the calcination step to obtained anatase TiO 2 microtubes. The XRD pattern of the TiO 2 microcubes and the microtubes' internal wall ( Figure 5l) were analyzed and confirmed that all the peaks were indexed to the pure anatase TiO 2 phase. There was a slight shift towards a lower degree in the XRD pattern of the internal wall (TiO 2 microcubes) because of fine TiO 2 NPs, which we had seen in the SEM image. Figure 5m shows the FTIR spectra of the natural SFs and TiO 2 microtubes, TIF, and TFH prepared from natural SFs. The major characteristics peaks of C=O, C=C, and C-OH at 2937, 1735, and 1033 cm −1 from cellulose, hemicelluloses, and lignin, while the enlarged view of flexural vibration of O-H at 1630 cm −1 was attributed due to the existence of the moisture in the Platanus acerifolia seed fibers. Figure 5n shows the surface area obtained by the Brunauer-Emmett-Teller (BET) method and pore distribution of the TiO 2 microtubes. A mesoporous size distribution was observed with a surface area of 128.2 m 2 /g with a pore diameter of 3.553 nm, which is higher than that reported for the commercial P25 TiO 2 . The UV-Vis spectra of synthesized TiO 2 microtubes and commercial P25 TiO 2 were analyzed ( Figure 5o). The sharp absorption edge for TiO 2 microtubes and commercial P25 TiO 2 microtubes were observed at 400 and 390 nm. The bandgaps were measured and were 2.81 eV and 3.17 eV for TiO 2 microtubes and commercial P25 TiO 2 , respectively; this difference was observed due to the carbon in the densely packed TiO 2 NPs. This research demonstrated the use of a novel double soaking sol-gel route to synthesize TiO 2 microtubes that have two advantages: they are environmentally friendly and green and they have excellent properties.
In another work, Muhammad Atif Irshad and co-workers reported a novel sol-gel approach using plant extracts (Trianthema portulacastrum (T2) and Chenopodium quinoa (T3)) to synthesize TiO 2 NPs. They also compared this green method with a chemical process to analyze the antifungal activity and observed that TiO 2 prepared via the green approach showed a better antifungal response against wheat rust. The various green sources have been used for TiO 2 -NPs synthesis via the sol-gel route, as reported in Table 3, which gives a broader view of the sol-gel method's green approach. have been used for TiO2-NPs synthesis via the sol-gel route, as reported in Table 3, which gives a broader view of the sol-gel method's green approach. Despite the beneficial aspects of TiO2 NPs, a few minor drawbacks limit the practicality of its application. The bandgap of anatase TiO2 is 3.23 eV, which can hamper the photocatalyst's efficiency due to the fast recombination rate of the generated charge carriers, combined with a slow transfer rate of electrons to oxygen. Therefore, doping or modification of TiO2 NPs with noble metals, such as gold, silver, platinum, and palladium, is an alternative way to lower the bandgap and to promote and enhance visible light absorption. Hariharan et al. [90] reported the fabrication of Pd@TiO2 NPs using Aloe vera gel, which acts as a capping and reducing agent during fabrication. In another work, Rostami-Vartooni et al. [91] reported a novel sol-gel approach to fabricating Ag-TiO2 nanocomposites using C. acinaciformis leaf and flower extracts to achieve the desired photocatalytic properties. They confirmed that silver-doped-TiO2 nanocomposites showed faster photocatalytic degradation than pure TiO2 NPs. Table 3. Green sol-gel synthesis approach for the preparation of TiO2 nanostructures.

Material Green Synthesis Reactant Reference
TiO2

Acanthophyllum laxiusculum SchimanCzeika roots
Titanium tetraisopropoxide (TTIP), 2-propanol, nitric acid [96] (a) (b) Despite the beneficial aspects of TiO 2 NPs, a few minor drawbacks limit the practicality of its application. The bandgap of anatase TiO 2 is 3.23 eV, which can hamper the photocatalyst's efficiency due to the fast recombination rate of the generated charge carriers, combined with a slow transfer rate of electrons to oxygen. Therefore, doping or modification of TiO 2 NPs with noble metals, such as gold, silver, platinum, and palladium, is an alternative way to lower the bandgap and to promote and enhance visible light absorption. Hariharan et al. [90] reported the fabrication of Pd@TiO 2 NPs using Aloe vera gel, which acts as a capping and reducing agent during fabrication. In another work, Rostami-Vartooni et al. [91] reported a novel sol-gel approach to fabricating Ag-TiO 2 nanocomposites using C. acinaciformis leaf and flower extracts to achieve the desired photocatalytic properties. They confirmed that silver-doped-TiO 2 nanocomposites showed faster photocatalytic degradation than pure TiO 2 NPs.

Co-Precipitation Method
Metal oxides can be synthesized using the co-precipitation method through a twostep process: first, the precipitation of metal hydroxides and, second, a heat treatment to crystallize the oxide. In the homogeneous liquid phase, the nucleation and growth kinetics of the particles are determined by the controlled release of anions and cations in the solution, and the shape and size distribution can be adjusted by controlling parameters such as pH and concentration of reagents/ions [99]. The co-precipitation method has some advantages over other chemical routes such as low cost, low energy and time consumption, and the possibility of large-scale production [100,101]. In addition, green synthesis can be easily adapted to this method including TiO 2 and ZnO nanostructures.
Mainly, green co-precipitation synthesis involves the use of plant extracts (leaf, root, fruit, bark). The biocomponents present in the extract can act as a stabilizing, reducing, capping, or chelating agent, changing both the morphology and the properties of the nanostructures, improving their performance in applications. Other strategies for obtaining nanostructures through green routes include the use of less aggressive solvents, fewer reagents, less energy consumption, the use of renewable feedstocks, reduced derivatives, and production of self-degrading products [102]. In general, the green syntheses of TiO 2 /ZnO nanostructures produced by the plant extract-mediated co-precipitation method follows an approximately similar route: First, a precursor solution is mixed with a solution of the plant extract under agitation. Then, changes in the temperature and/or pH of the mixture (addition of NaOH) initiates the precipitation process and hydroxide formation. The third step consists of the separation (simple or by centrifugation) of the precipitate, washing with deionized water and/or ethanol accompanied or not by a drying process at low temperatures. The last step consists of thermal treatment (calcination) at higher temperatures to crystallize the oxide. The final product can also be ground in a crystal mortar pestle. Figure 6 depicts a schematic diagram containing all these steps for a generic green synthesis using the co-precipitation method.

Co-Precipitation Method
Metal oxides can be synthesized using the co-precipitation method through a twostep process: first, the precipitation of metal hydroxides and, second, a heat treatment to crystallize the oxide. In the homogeneous liquid phase, the nucleation and growth kinetics of the particles are determined by the controlled release of anions and cations in the solution, and the shape and size distribution can be adjusted by controlling parameters such as pH and concentration of reagents/ions [99]. The co-precipitation method has some advantages over other chemical routes such as low cost, low energy and time consumption, and the possibility of large-scale production [100,101]. In addition, green synthesis can be easily adapted to this method including TiO2 and ZnO nanostructures.
Mainly, green co-precipitation synthesis involves the use of plant extracts (leaf, root, fruit, bark). The biocomponents present in the extract can act as a stabilizing, reducing, capping, or chelating agent, changing both the morphology and the properties of the nanostructures, improving their performance in applications. Other strategies for obtaining nanostructures through green routes include the use of less aggressive solvents, fewer reagents, less energy consumption, the use of renewable feedstocks, reduced derivatives, and production of self-degrading products [102]. In general, the green syntheses of TiO2/ZnO nanostructures produced by the plant extract-mediated co-precipitation method follows an approximately similar route: First, a precursor solution is mixed with a solution of the plant extract under agitation. Then, changes in the temperature and/or pH of the mixture (addition of NaOH) initiates the precipitation process and hydroxide formation. The third step consists of the separation (simple or by centrifugation) of the precipitate, washing with deionized water and/or ethanol accompanied or not by a drying process at low temperatures. The last step consists of thermal treatment (calcination) at higher temperatures to crystallize the oxide. The final product can also be ground in a crystal mortar pestle. Figure 6 depicts a schematic diagram containing all these steps for a generic green synthesis using the co-precipitation method.

Green Co-Precipitation Synthesis Approach for TiO2 Nanostructures
In general, reports of the green syntheses of TiO2 nanostructures using the co-precipitation method in the literature are still modest but have shown notable growth in recent years due to the method's ease of use and timesaving qualities. Next, we report on some

Green Co-Precipitation Synthesis Approach for TiO 2 Nanostructures
In general, reports of the green syntheses of TiO 2 nanostructures using the co-precipitation method in the literature are still modest but have shown notable growth in recent years due to the method's ease of use and timesaving qualities. Next, we report on some works in this area. In recent years, Rawat and collaborators have produced different TiO 2 nanostructures using a green co-precipitation method. They synthesized spherical TiO 2 NPs (20-30 nm) using Phyllanthus emblica (Amla) leaf extract and TTIP as a titanium source [103]. In a typical process, the TiO 2 precursor and the leaf extract (1:1 ratio by volume) were mixed and stirred at room temperature for 20 min until the color of the solution changed from transparent to whitish brown. Then, ammonia was added drop by drop to the solution, initiating the formation of the precipitate. Anatase NPs were obtained after filtering the solution and rinsing the precipitate with alcohol, calcining in a muffle furnace (400 • C, 3 h), and grinding in a crystal mortar pestle. This same method was previously used to obtain anatase nanocubes using Tinospora cordifolia leaf extract [104]. In this, it was observed that the control of the morphology provided by the extract's biomolecules proved to be fundamental in the performance of the nanostructures for degradation of the neutral red (NR) dye: cubic TiO 2 was more efficient for dye photodegradation than non-cubic NPs, reaching a percentage of 93.4% against 65.3% after 120 min under UV illumination.
Many other works have reported using plant extract mediating the synthesis of anatase TiO 2 NPs using the co-precipitation method [105][106][107][108]. However, as with traditional syntheses, green syntheses of the rutile phase are scarcer. One of the disadvantages of the co-precipitation method is the rapid nucleation and growth of the nanostructures; the accelerated growth can result in a strong agglomeration of the final product. However, many green syntheses have shown that using plant extracts can improve the dispersion of the synthesized NPs using this method. Goutam et al. [95], for example, synthesized TiO 2 NPs using Jatropha curcas L. leaf extract and showed that the low formation of NP agglomerates was related to the performance of phytochemicals present in the extract as capping agents. A similar effect was observed by Subhapriya and Gomathipriya [109] and by Kaur et al. [94] in the green synthesis of polydisperse TiO 2 NPs from Trigonella foenum leaf extract and Lagenaria siceraria leaf extract, respectively.
In this scenario, we highlight the green co-precipitation synthesis in which no plant extract was used, as reported by Muniandy et al. [110], for the production of mesoporous anatase NPs using TTIP as a titanium source, water as a solvent, and starch as a template. According to the authors, starch plays a key role in the formation of mesoporous structures: the nucleation and initial crystal growth occur when the precursor diffuses and forms complexes with amylose molecules close to the interspaces between the swollen starch microspheres. With the calcination process, these starch granule templates are removed, giving rise to mesoporous structures. The morphology of the synthesized structures in this work was analyzed by Field Emission scanning Electron Microscopy (FESEM) and High-Resolution Transmission Electron Microscopy (HRTEM) and can be seen in Figure 7. The influence of the amount of Ti precursor and the pH of the solution on the morphology and photocatalytic activity of the material was also evaluated in this work.

Green Co-Precipitation Synthesis Approach for ZnO Nanostructures
As for the production of ZnO nanostructures, there is a more abundant number of papers using the co-precipitation method, especially when this process is mediated by plant extract. This is largely due to the work of Singh et al. [56], who reported a simple and efficient method for green synthesis of ZnO NPs using this method. In the mentioned work, zinc oxide NPs were produced using latex from Calotropis procera as an alternative to chemical syntheses. For the synthesis, 0.02 M of aqueous zinc acetate dihydrate solution was mixed with 50 mL of distilled water with vigorous stirring. After 10 min, 0.25, 0.5, and 1.0 mL of latex were added, one part at a time, to the acetate solution. Then, NaOH (2.0 M) was added to the solution until it reached pH 12, then the obtained mixture was placed on a magnetic stirrer for 2 h. The precipitate was collected, rinsed repeatedly with distilled water and ethanol to remove impurities, and left to dry overnight in a vacuum at 60 °C. The final product was spherical NPs (5-40 nm) and granular nanosized with little

Green Co-Precipitation Synthesis Approach for ZnO Nanostructures
As for the production of ZnO nanostructures, there is a more abundant number of papers using the co-precipitation method, especially when this process is mediated by plant extract. This is largely due to the work of Singh et al. [56], who reported a simple and efficient method for green synthesis of ZnO NPs using this method. In the mentioned work, zinc oxide NPs were produced using latex from Calotropis procera as an alternative to chemical syntheses. For the synthesis, 0.02 M of aqueous zinc acetate dihydrate solution was mixed with 50 mL of distilled water with vigorous stirring. After 10 min, 0.25, 0.5, and 1.0 mL of latex were added, one part at a time, to the acetate solution. Then, NaOH (2.0 M) was added to the solution until it reached pH 12, then the obtained mixture was placed on a magnetic stirrer for 2 h. The precipitate was collected, rinsed repeatedly with distilled water and ethanol to remove impurities, and left to dry overnight in a vacuum at 60 • C. The final product was spherical NPs (5-40 nm) and granular nanosized with little agglomeration; it remained stable and without visible changes even one month after synthesis. These characteristics were attributed to the effective role of latex as a stabilizing and reducing agent. From this pioneering work, many other green syntheses mediated by plant extracts have been reported for the production of zinc oxide NPs using the co-precipitation method. Table 4 presents works in the literature reporting the use of this type of green synthesis to produce ZnO nanostructures and the functionality of each of the biocomponents used in its preparation. Regarding the syntheses that do not use plant extract for the synthesis of ZnO nanostructures, we can highlight the work of Akir et al. [125] in which structures with different morphologies were produced from three different protocols for the addition of basic solution in the zinc aqueous solution: spherical NPs, nanosheets, and hexagonal prismatic NPs, indicating that the speed of addition of the basic solution to the zinc precursor is a key factor for the morphology of the structures. Charoenthai and Yomma [126] synthesized ZnO NPs with a hexagonal wurtzite structure using a process similar to that adopted by Akir et al. [125]. In this case, the authors showed that the use of water as a solvent, in comparison with ethanol, methanol, propanol, and butanol solvents, results in the formation of smaller NPs with greater surface area and greater pore volume that caused an increased photodegradation for methylene blue (MB) and methyl orange (MO) dyes.

Hydrothermal Method
Nanoparticle synthesis is widely studied today, and many processing methods have been developed to produce homogeneous structures with high crystalline quality. Among all methods used to synthesize nanostructures, hydrothermal synthesis has been considered one of the most promising methods in this regard. In this method, the stability provided by using a closed system, where temperature and pressure are controlled, allows greater control over the size, nucleation, and degree of crystallinity of the NPs [127,128]. Thus, the hydrothermal method has been used to synthesize several nanostructures, including TiO 2 and ZnO nanostructures (mono-dispersed and highly homogeneous NPs, nano-hybrid materials, and nanocomposites), as part of the framework of green synthesis [99]. In general, green hydrothermal syntheses are synthesized by non-toxic solvents and noncorrosive solutions in their process, which minimizes damage to the environment and reduces the consumption of raw materials. There are still few reports on green synthesized TiO 2 and ZnO nanostructures compared to other methods such as co-precipitation and solgel. However, promising results have been presented in the literature and are summarized as follows.

Green Hydrothermal Synthesis for ZnO Nanostructures
Recently, Chang et al. [129] used a green hydrothermal route for the synthesis of versatile nanostructured zinc oxide particles (nZnOs) from zinc acetate precursors (Figure 8a). The morphological characterization showed that the NPs were shaped like nanorods (Figure 8b), nanoplatelets (Figure 8c), and multibranched flower-like particles (Figure 8d) for growth times of 6, 12, and 24 h, respectively. Figure 8e shows the nZnO nanostructure used in antimicrobial activity testing. The multibranched flower-type ZnO presented more remarkable, reliable, and stable antifungal activity than the other nZnOs, probably because it has a larger surface area.
synthesized ZnO NPs with a hexagonal wurtzite structure using a process similar to that adopted by Akir et al. [125]. In this case, the authors showed that the use of water as a solvent, in comparison with ethanol, methanol, propanol, and butanol solvents, results in the formation of smaller NPs with greater surface area and greater pore volume that caused an increased photodegradation for methylene blue (MB) and methyl orange (MO) dyes.

Hydrothermal Method
Nanoparticle synthesis is widely studied today, and many processing methods have been developed to produce homogeneous structures with high crystalline quality. Among all methods used to synthesize nanostructures, hydrothermal synthesis has been considered one of the most promising methods in this regard. In this method, the stability provided by using a closed system, where temperature and pressure are controlled, allows greater control over the size, nucleation, and degree of crystallinity of the NPs [127,128]. Thus, the hydrothermal method has been used to synthesize several nanostructures, including TiO2 and ZnO nanostructures (mono-dispersed and highly homogeneous NPs, nano-hybrid materials, and nanocomposites), as part of the framework of green synthesis [99]. In general, green hydrothermal syntheses are synthesized by non-toxic solvents and non-corrosive solutions in their process, which minimizes damage to the environment and reduces the consumption of raw materials. There are still few reports on green synthesized TiO2 and ZnO nanostructures compared to other methods such as co-precipitation and sol-gel. However, promising results have been presented in the literature and are summarized as follows.

Green Hydrothermal Synthesis for ZnO Nanostructures
Recently, Chang et al. [129] used a green hydrothermal route for the synthesis of versatile nanostructured zinc oxide particles (nZnOs) from zinc acetate precursors ( Figure  8a). The morphological characterization showed that the NPs were shaped like nanorods (Figure 8b), nanoplatelets (Figure 8c), and multibranched flower-like particles (Figure 8d) for growth times of 6, 12, and 24 h, respectively. Figure 8e shows the nZnO nanostructure used in antimicrobial activity testing. The multibranched flower-type ZnO presented more remarkable, reliable, and stable antifungal activity than the other nZnOs, probably because it has a larger surface area. Guo et al. [130] showed that the reaction temperature and time in the hydrothermal method were also fundamental to defining the crystalline phase of the material and the morphology. Changing the autoclave treatments at 100-120 • C for 6 h (or 170 • C for 0 h) to treatment at 170 • C for 3-6 h, the obtained product changed from cubic ZnO 2 nanocrystals to hexagonal ZnO nanorods. The UV-Vis absorption spectra showed the synthesized ZnO 2 nanocrystals had optical bandgaps around 4.1 eV, and the ZnO nanorods presented at 3.3 eV, which makes both structures good candidates for applications in photocatalysis and optoelectronic devices with a short wavelength. In another work, Lam et al. [77] proposed a green hydrothermal approach for the large-scale synthesis of ZnO nanotubes (NTs) using powder ZnO and aqueous H 2 O 2 solution (volume 30%) as starting materials and performing an autoclave treatment at 130 • C for one day. The ZnO NTs with an average diameter of 10 nm and a wall thickness of 3-5 nm (rolling the nanosheet layer) were applied as photocatalysts for degradation of endocrine chemical disruptor methylparaben under UV irradiation. The degradation of methylparaben has been associated with the unique tubular structure and the large surface area of the NTs of ZnO that give rise to increased separation of electrons and holes and the formation of a large number of reactive radicals in the photocatalytic process. Liu et al. [131] also used the same method with an aqueous solution of H 2 O 2 as a solvent for the production of hollow ZnO NTs and nanospheres (treatment in an autoclave at 120 • C for 6 h). An interesting study was also presented by Patrinoiu et al. [111] regarding control over ZnO nanostructures' morphology; different nanostructures were produced by the variation in concentrations of zinc acetate precursor and starch reagent in the hydrothermal synthesis (autoclave treatment at 180 • C for 24 h). The authors claimed that the key parameter for the morphological alterations was the gelation capacity of amylose released by the starch. The study also showed that all the ZnO nanostructures exhibited antibacterial activity and antibiofilm potential.

Green Hydrothermal Synthesis for TiO 2 Nanostructures
Wang et al. [132] successfully synthesized TiO 2 NPs with different morphologies (i.e., nanorods, nanospheres, and microspheres) and crystalline phases by variating oxalic acid (OA) and TTIP precursor concentrations in a surfactant-free green hydrothermal approach. At first, OA was dissolved into H 2 O and magnetically stirred until a transparent solution was obtained. The TTIP was dropped until a colorless solution was reached. The solution was hydrothermally treated at 180 • C for 12 h. Deposits were collected by vacuum filtration, washed in deionized water and anhydrous ethanol, and calcinated at 80 • C for 12 h in a vacuum box. To reach different TiO 2 phases (i.e., anatase and rutile), several TTIP/OA molar ratios were used, from 2:1 to 1:1, 1:3, 1:6, and 1:9 with the same initial route. Their work also showed that the microspheres with mixed anatase and rutile phases presented better photocatalytic performance.
Similarly, Spada et al. [133] used annealing temperature variations of 400-1000 • C (4 h) to control the crystalline phase and the particle size of TiO 2 NPs. The XRD data show that at temperatures above 600 • C, the anatase phase started a transition to the rutile phase, and at temperatures above 1000 • C pure rutile was found. The size of the crystals increased proportionally with the increase in temperature, ranging from 17 to 57 nm; on the other hand, the bandgap decreased from 3.21 to 2.93 eV. Degeneration tests of the rhodamine B (RhB) dye showed that the NPs obtained at 600 • C, with small fractions of the rutile phase, presented improved photocatalytic performance. Green hydrothermal synthesis mediated by plant extracts were also used for the production of TiO 2 NPs. Recently, Hariharan et al. [134] synthesized TiO 2 NPs using Aloe vera gel and deionized water as starting materials (autoclave treatment at 180 • C for 4 h). Sample characterization showed TiO 2 anatase NPs with good crystalline quality and sizes ranging from 6 to 13 nm. In addition, the use of plant extract resulted in a better performance of NPs for picric acid photodegradation than NPs synthesized by the chemical hydrothermal route. Subsequently, Hariharan et al. [135] used the same method for producing Ag-doped TiO 2 NPs. The Ag-TiO 2 NPs were found to have an improved activity for photodegradation of picric acid under visible light and also showed anticancer activity, decreasing the growth of cancer cells and increasing the reactive oxygen species.

Solvothermal Method
Solvothermal synthesis is a widely used process to synthesize several technological materials such as ferrite [136][137][138], Sn: In 2 O 3 [139,140], CeO 2 [141,142], ZnO [143][144][145][146][147], Metal Organic Frameworks (MOFs) [148][149][150][151][152], TiO 2 [153][154][155][156][157][158]. In this approach, an organic solvent (non-aqueous) is used as reactional media in which a solute is dissolved and, subsequently, crystallized under high-temperature and high-pressure conditions. These conditions are achieved by confining the solution to a special sealed system such as an autoclave. There are several advantages associated with using the solvothermal approach instead of other inorganic synthesis, but by far the most attractive one is the simplicity of the approach. Other significant advantages are the control over shape, size distribution, and crystalline phases. Despite the tremendous success of the solvothermal approach for synthesizing TiO 2 and ZnO nanostructures [143][144][145][146][147][153][154][155][156][157][158], it is still an approach that uses highly corrosive and toxic chemical precursors for human beings. For this reason, it is essential to seek greener approaches to synthesize these metal oxide nanostructures, since they are of high technological interest. In this context, our goal was to present the most recent bibliography on the green solvothermal approach to synthesize TiO 2 and ZnO NPs.

Green Solvothermal Synthesis Approach for ZnO Nanostructures
In this section, the green solvothermal approach is presented in a slightly broader concept by considering papers that use plant extracts and natural templates and references in which authors tried to simplify their methodologies, reducing the quantity of precursors, or substituting hazards solvents or not using surfactants. In general, there are still few reports on the green synthesis of ZnO and TiO 2 nanostructures in which the solvothermal approach was employed. Despite this fact, Zhang et al. [159] successfully synthesized Er-Al co-doped ZnO NPs by using a one-pot and surfactant-free, non-toxic solvothermal approach. The authors characterized the samples' structural features and photocatalytic activity by degrading methyl orange (MO) in water under visible light irradiation. The XRD, energy-dispersive X-ray spectroscopy (EDX), and X-ray photoelectron spectroscopy (XPS) measurements revealed that Er and Al ions doped the ZnO's pristine structure. The UV-Vis measurements revealed that the co-doping caused a widening in the ZnO bandgap from 3.14 eV (i.e., pristine structure) to 2.95 (Er-Al co-doped sample) and, consequently, an increase in the visible light absorption of ZnO. The authors also showed that Er-Al codoped ZnO presented an enhanced photocatalytic activity under visible light illumination with 98.9% MO degradation efficiency. Šutka et al. [160] showed a straightforward and ethanol-based solvothermal synthesis of plasmonic Al-doped ZnO (AZO) NPs using Al and Zn salts as starting materials.
The control of ZnO samples was synthesized by mixing zinc acetate dehydrate (Zn(CH 3 CO 2 ) 2 ·2H 2 O) in ethanol, resulting in a 0.1 M solution be mixed with a second solution prepared with NaOH in ethanol. Previously to their mixing, both solutions were vigorously stirred and heated to 80 • C. After this, the two solutions were mixed and left under stirring at 80 • C for 10 h. The final mixture was then transferred into a 50 mL Teflon-lined, stainless-steel autoclave, sealed, and heated at 150 • C for 24 h. The resulting material was filtered and washed with methanol and dried in air at 60 • C for 5 h. Doped samples were synthesized by substituting an amount of Zn(CH 3 CO 2 ) 2 ·2H 2 O in ethanol by Al(NO 3 ) 3 ·9H 2 O. Structural characterization showed that the Al atoms effectively substituted Zn in the zincite structure. Morphological features of the undoped and doped ZnO samples were studied by SEM and TEM measurements as presented in Figure 9.
lined, stainless-steel autoclave, sealed, and heated at 150 °C for 24 h. The resulting material was filtered and washed with methanol and dried in air at 60 °C for 5 h. Doped samples were synthesized by substituting an amount of Zn(CH3CO2)2•2H2O in ethanol by Al(NO3)3•9H2O. Structural characterization showed that the Al atoms effectively substituted Zn in the zincite structure. Morphological features of the undoped and doped ZnO samples were studied by SEM and TEM measurements as presented in Figure 9.    (Figure 9b,d) causes the aspect ratio to decrease, leading the final products to be NPs and nanorods (lengths below 50 nm and diameters around 10 nm). The authors showed via diffuse reflectance measurements the presence of localized surface plasmon absorption in the NIR region for all doped samples. They demonstrated the doped samples could be used for technological applications such as a hyper-realistic piezoresistive sensor based on a composite material formed by mixing Zn0.925Al0.075O nanocrystals into polydimethylsiloxane. In another work, Liu and co-workers [161] reported the synthesis of an octahedral ZnO/ZnFe2O4 heterostructure through a surfactant-free solvothermal method followed by thermal treatment. At the first step, the precursor to the ZnO/ZnFe2O4 final product was synthesized using the solvothermal method in which ZnCl2 and FeCl3·6H2O were dissolved in ethylene glycol (EG), and to this mixture, it was added CH3COONa. This mixture was then stirred for 30 min and then sealed into a Teflon-lined, stainless-steel autoclave (200 °C for 12 h). The final octahedral ZnO/ZnFe2O4 was achieved after the precursor was annealed in air at 500 °C. The authors showed the water treatment promising character of octahedral ZnO/ZnFe2O4 samples because of their excellent adsorption capacity of malachite green (MG) and selectivity in mixtures of dyes such as in MG/MO and MG/RhB. Mahlaule-Glory et al. [162] synthesized ZnO NPs using an eco-friendly approach to the traditional solvothermal method in which    (Figure 9b,d) causes the aspect ratio to decrease, leading the final products to be NPs and nanorods (lengths below 50 nm and diameters around 10 nm). The authors showed via diffuse reflectance measurements the presence of localized surface plasmon absorption in the NIR region for all doped samples. They demonstrated the doped samples could be used for technological applications such as a hyper-realistic piezoresistive sensor based on a composite material formed by mixing Zn 0.925 Al 0.075 O nanocrystals into polydimethylsiloxane. In another work, Liu and co-workers [161] reported the synthesis of an octahedral ZnO/ZnFe 2 O 4 heterostructure through a surfactant-free solvothermal method followed by thermal treatment. At the first step, the precursor to the ZnO/ZnFe 2 O 4 final product was synthesized using the solvothermal method in which ZnCl 2 and FeCl 3 ·6H 2 O were dissolved in ethylene glycol (EG), and to this mixture, it was added CH 3 COONa. This mixture was then stirred for 30 min and then sealed into a Teflon-lined, stainless-steel autoclave (200 • C for 12 h). The final octahedral ZnO/ZnFe 2 O 4 was achieved after the precursor was annealed in air at 500 • C. The authors showed the water treatment promising character of octahedral ZnO/ZnFe 2 O 4 samples because of their excellent adsorption capacity of malachite green (MG) and selectivity in mixtures of dyes such as in MG/MO and MG/RhB. Mahlaule-Glory et al. [162] synthesized ZnO NPs using an eco-friendly approach to the traditional solvothermal method in which Sutherlandia frutescens extract was used as a reducing and capping agent for the synthesis of ZnO NPs. The plant composite formed by the Sutherlandia frutescens and ZnO NPs showed bactericidal effects against Gram-positive and -negative strains and antiproliferative effects against the A549 human alveolar lung cancer cell line. Although the authors claim that they used the solvothermal approach to synthesize the ZnO nanostructures, the parameters used in the synthesis were not described in the text.

Green Solvothermal Synthesis Approach for TiO 2 Nanostructures
Several authors reported the use of titanium alkoxide as the metal precursor of solvothermal green synthesis of titanium oxide nano-and microstructures [163][164][165][166]. Wang and co-workers [164] reported a successful, single-step, green synthesis of the monoclinic metastable phase of TiO 2 known as TiO 2 (B). The samples' structural characterizations confirmed the crystalline phase, and their composition was mainly formed by titanium and oxide atoms. The HRTEM measurements revealed that the as-synthesized TiO 2 (B) comprised tiny crystallites and nanoporous structures (Figure 10a,b). In Figure 10c,d, the fast Fourier transition (FFT) image revealed the crystalline character of the sample, and the inverse fast Fourier transition (IFFT) image showed the (0 0 1) plane of TiO 2 (B), respectively. Wang et al. [164] also found that green synthesized TiO 2 (B) was highly efficient and stable for the decomposition of MO dye in agreement with previously reported studies in which non-green synthesized TiO 2 (B) was found to be a highly efficient phase for the degradation of this dye.
Sutherlandia frutescens extract was used as a reducing and capping agent for the synthesis of ZnO NPs. The plant composite formed by the Sutherlandia frutescens and ZnO NPs showed bactericidal effects against Gram-positive and -negative strains and antiproliferative effects against the A549 human alveolar lung cancer cell line. Although the authors claim that they used the solvothermal approach to synthesize the ZnO nanostructures, the parameters used in the synthesis were not described in the text.

Green Solvothermal Synthesis Approach for TiO2 Nanostructures
Several authors reported the use of titanium alkoxide as the metal precursor of solvothermal green synthesis of titanium oxide nano-and microstructures [163][164][165][166]. Wang and co-workers [164] reported a successful, single-step, green synthesis of the monoclinic metastable phase of TiO2 known as TiO2 (B). The samples' structural characterizations confirmed the crystalline phase, and their composition was mainly formed by titanium and oxide atoms. The HRTEM measurements revealed that the as-synthesized TiO2 (B) comprised tiny crystallites and nanoporous structures (Figure 10a,b). In Figure 10c,d, the fast Fourier transition (FFT) image revealed the crystalline character of the sample, and the inverse fast Fourier transition (IFFT) image showed the (0 0 1) plane of TiO2 (B), respectively. Wang et al. [164] also found that green synthesized TiO2 (B) was highly efficient and stable for the decomposition of MO dye in agreement with previously reported studies in which non-green synthesized TiO2 (B) was found to be a highly efficient phase for the degradation of this dye. Additionally, TiO2 core-shell microspheres were synthesized by a template-free and hydrofluoric acid-free solvothermal synthesis starting from TTIP, isopropyl alcohol, and organic amine [166]. The photocatalytic activity was also studied under visible irradiation and UV-Vis irradiation. Structural characterization data showed that the TiO2 core-shell was mainly composed of NPs aggregates covered by perpendicular assembled nanosheets with high-energy {116} facets exposed. The XPS measurements revealed that in situ doping with nitrogen at the interstitial sites of TiO2 shells occurred and induced local states above the valence band edge, leading to the narrowing of the bandgap and resulting in a Additionally, TiO 2 core-shell microspheres were synthesized by a template-free and hydrofluoric acid-free solvothermal synthesis starting from TTIP, isopropyl alcohol, and organic amine [166]. The photocatalytic activity was also studied under visible irradiation and UV-Vis irradiation. Structural characterization data showed that the TiO 2 core-shell was mainly composed of NPs aggregates covered by perpendicular assembled nanosheets with high-energy {116} facets exposed. The XPS measurements revealed that in situ doping with nitrogen at the interstitial sites of TiO 2 shells occurred and induced local states above the valence band edge, leading to the narrowing of the bandgap and resulting in a visible light response of the material. Zhao et al. [167] reported the synthesis of spinous hollow pure anatase TiO 2 and ZrO 2 -doped TiO 2 microspheres using a solvothermal green approach in which sunflower pollen acted as bio templates. Shortly, the methodology used for the TiO 2 pure phase was based on the dispersion of sunflower pollen template in absolute ethanol and then the addition of titanium butoxide under continuous magnetic stirring. After 2 h, water was added, and the mixture was submitted to the solvothermal conditions. A calcination process was also conducted after the solvothermal synthesis to ensure the samples' crystalline and stoichiometry. Doped samples were synthesized in a very similar way by mixing titanium butoxide and zirconium n-butoxide instead of titanium butoxide.
In Figure 11a, the sunflower pollen morphology was close to a sphere covered with spines at the surface. Without calcination, ZrO 2 -doped TiO 2 spinous hollow microspheres presented a very similar morphology as depicted in Figure 11b. The micrographs obtained for pure TiO 2 and doped samples synthesized with 4.6%, 8.8%, 12.6%, and 18.2% molar ratio of zirconium n-butoxide in mixed esters can be seen in Figure 11c-f, respectively. These results indicated that all samples retain the spherical shape of the pollen templated besides the different amounts of ZrO 2 introduced in the synthesis. Calcined samples presented smaller diameters due to the removal of the pollen templates (Figure 11g), and the hollow structure is presented in Figure 11h by observation of a broken microsphere in the micrograph. The authors claim that the samples' hollow features probably be originated from the release of CO 2 during the carbonization process of organic matter in pollen. Figure  11i depicts the samples synthesized without templates. Zhou and collaborators [168] reported the synthesis of anatase TiO 2 mesocrystals using a green solvothermal method based on a halide precursor TiCl 3 . The authors showed that the as-synthesized samples were mainly composed of anatase mesocrystals with the Wulff construction in which the facet exposed was {101}.
visible light response of the material. Zhao et al. [167] reported the synthesis of spinous hollow pure anatase TiO2 and ZrO2-doped TiO2 microspheres using a solvothermal green approach in which sunflower pollen acted as bio templates. Shortly, the methodology used for the TiO2 pure phase was based on the dispersion of sunflower pollen template in absolute ethanol and then the addition of titanium butoxide under continuous magnetic stirring. After 2 h, water was added, and the mixture was submitted to the solvothermal conditions. A calcination process was also conducted after the solvothermal synthesis to ensure the samples' crystalline and stoichiometry. Doped samples were synthesized in a very similar way by mixing titanium butoxide and zirconium n-butoxide instead of titanium butoxide.
In Figure 11a, the sunflower pollen morphology was close to a sphere covered with spines at the surface. Without calcination, ZrO2-doped TiO2 spinous hollow microspheres presented a very similar morphology as depicted in Figure 11b. The micrographs obtained for pure TiO2 and doped samples synthesized with 4.6%, 8.8%, 12.6%, and 18.2% molar ratio of zirconium n-butoxide in mixed esters can be seen in Figure 11c-f, respectively. These results indicated that all samples retain the spherical shape of the pollen templated besides the different amounts of ZrO2 introduced in the synthesis. Calcined samples presented smaller diameters due to the removal of the pollen templates (Figure 11g), and the hollow structure is presented in Figure 11h by observation of a broken microsphere in the micrograph. The authors claim that the samples' hollow features probably be originated from the release of CO2 during the carbonization process of organic matter in pollen. Figure 11i depicts the samples synthesized without templates. Zhou and collaborators [168] reported the synthesis of anatase TiO2 mesocrystals using a green solvothermal method based on a halide precursor TiCl3. The authors showed that the as-synthesized samples were mainly composed of anatase mesocrystals with the Wulff construction in which the facet exposed was {101}.

Gas Sensor Applications
The living standards of the human race in the 20th century grew rapidly due to the industrial revolution. Industrialization demands specific gas detection and monitoring for

Gas Sensor Applications
The living standards of the human race in the 20th century grew rapidly due to the industrial revolution. Industrialization demands specific gas detection and monitoring for the benefit of society [16,18,[169][170][171][172][173]. These include hydrocarbons (for the exploration of oil fields), oxygen (for breathable atmospheres and combustion processes, e.g., in boilers and internal combustion engines), and other various gaseous chemicals (for medical applications, manufacturing of different chemicals, etc.). However, extensive industrialization has a negative aspect: the emission of polluting gases into the environment poses a risk to public health. Therefore, gas sensors need to measure pollution in the atmosphere to take adequate control measures [13,17,21,174].
Due to the fact of their unique optical, electrical, and chemical properties, semiconductor metal oxide (SMO) nanomaterials, such as SnO 2 , ZnO, and TiO 2 , have created high expectations as sensitive layers. Moreover, SMO-based resistive gas sensors have been extensively used because of their low cost, compact size, and easy production. The SMO's sensing properties depend on their morphology and the type and concentration of defects generated during the synthesis and doping. As discussed earlier, there are many techniques to fabricate ZnO and TiO 2 nanomaterials to control their morphology. Moreover, recent studies show that various nanostructures, such as nanowires, nanocubes, and nanobelts, have enhanced sensor response to toxic gases because of the high surface-to-volume ratio. However, selectivity and high operation temperature hamper the use of these sensors for commercial purposes. With green synthesis, we can achieve the same morphology as other techniques, since they are eco-friendly, energy efficient, and take less time to process than different approaches. However, reproducibility and mass production of NPs via the green approach still requires more research.
The ZnO NPs prepared from Aloe vera plant extract [26] were tested for gas sensing properties and compared with the chemical method. Those NPs were observed to show maximum sensitivity towards 1000 ppm of liquified petroleum gas (LPG) at 250 • C, and it was concluded that both techniques showed similar responses towards LPG; however, green synthesized nanomaterials are recommended due to the fact of their facile approach. The ZnO nanocubes were synthesized using alginate, a water-soluble polysaccharide and a desirable candidate for aqueous processing; it showed room temperature selective sensing towards ammonia gas [175]. Besides their advantages, one of the most challenging issues for SMO-based gas sensors is to achieve selectivity towards target analytes under controlled humidity. Previous works to improve the specificity of metal oxides include: (i) incorporating suitable additives, (ii) temperature control, and (iii) using appropriate filters. A recent study showed that selectivity and sensitivity could be further enhanced by doping some oxides/2D materials, decorating the surface with noble metals, and using UV-light illumination [13,174,[176][177][178][179][180]. In summary, nanomaterials prepared via a green approach could help to achieve high sensitivity; however, selectivity and operation temperature are still a challenge with metal oxide, and there are still many experiments and discoveries required to overcome this issue.

Photocatalysis Applications
Photocatalysis is usually defined as the process in which a photoinduced reaction is accelerated by a catalyst material. When irradiated with photons, the catalyst produces electron-hole pairs that can interact with other molecules in the reaction medium, giving rise to reactive oxidative species (ROS) that can degrade toxic components in less dangerous species. Traditionally, semiconductor materials have been used as a catalyst due to the fact of their unique electronic structure, the bandgap between the full valence band and the empty conduction band is low enough to allow these materials to be sensitizers for light-induced redox processes. In this category, ZnO and TiO 2 oxides also stand out for their low cost, chemical inertness, thermal stability, and low hazard. [181]. In the particular case of nanostructures produced by green syntheses, the main photocatalytic application of TiO 2 and ZnO oxides is in the treatment of wastewater, with the decolorization of water contaminated by dyes being the primary target. Outstanding works that report the use of these nanostructures for the degradation of dyes are listed in Table 5.  The * in the second column indicates that the green syntheses were aided by plant extracts.
Notably, most of the photodegradation processes in Table 5 are associated with RhB, MB, and MG; this is because they are the primary dyes found in effluents [206]. In green syntheses, in which ZnO and TiO 2 nanostructures are produced by means of plant extract, the degradation of harmful agents can be aided by the oxidizing potential of biocomponents such as quinones, phenols, and flavonoids present in the extracts; reduction potential will depend on the plant species, the type of dye analyzed and the temperature [207]. As highlighted in Table 5, NPs obtained with the aid of plant extracts presented excellent catalytic performances for dye degradation (synthesis marked with an asterisk) comparable to that of NPs obtained by other types of green syntheses and also chemical syntheses. Despite the excellent performances, the phenomenon of reduction and the role of biocomponents in photodegradation have been little discussed and need further investigation. Some studies have suggested that these biocomponents can help to generate more hydroxyl radicals on the semiconductor surface, resulting in an increase in photocatalytic activity [185,188].
More recently, in addition to the usual applications in dye photodegradation, TiO 2 NPs synthesized by green approaches have also been used to remove Cr 6+ ions and chemical oxygen demand of real tannery effluents (efficiency of 82.26% and 76.48% under solar illumination) [95], the photoreduction of Cr 6+ ions (79.6% under UV irradiation) [208], removal of Pb from explosive industrial wastewater (82.53% removal after a 12 h treatment with UV light) [108], removal of total organic carbon and total nitrogen in refinery wastewater (efficiency of 32% and 67% under UV-C lighting, respectively) [209], and also organic compounds such as picric acid (100% under visible light at 120 min) [134], ornidazole antibiotic (67% efficiency under UV illumination after 100 min) [210], and ciprofloxacin (CIP) antibiotic (CIP removal of 90% after 60 min under UV-Vis illumination) [211]. The photodegradation of phenol (80% and 100% under irradiation with visible and UV light, respectively) [212], anthracene (96% efficiency a 4 h treatment with UV illumination) [213], photocatalytic generation of H 2 (360 µmol/g under UV-Vis irradiation) [214], and photocatalytic treatment against Enterococcus faecalis bacteria (99.2% efficiency under visible illumination) [118] was also achieved by using ZnO nanostructures produced by green synthesis. In general, the photocatalysis process can be affected by factors such as surface defects that can both reduce the bandgap, decreasing the energy needed to produce photoexcited carriers [198,212,215], act in the prevention of the recombination of carriers [110], or increase the production of •OH radicals [84,203]; texture effects [53]; morphology, by an increase of surface area and/or active sites; and, in this case of ZnO, to its absorption capacity in a wide range of the solar spectrum [193]. The improvement in these aspects constitutes the best way to tailor the use of nanostructures produced by green routes in photocatalytic processes, and efforts should be made in this regard. Although the biggest challenge in the area is to show a superior performance of the ZnO and TiO 2 catalysts for applications other than the well-established dye photodegradation and to elucidate the role of biocomponents (derived from plant extracts used in most green synthesis) in the photocatalytic process using them in their interest.

Supercapacitor Application
Over the last decades, many researches have focused on developing high-performance supercapacitors with greater storage capacity, faster loading, high-temperature resistance, and low cost. Metal oxides have been widely used as electrode materials in supercapacitors because of their high specific capacitance and low resistance, which allow the construction of high-energy devices. Currently, there has been an increase in the interest in producing oxide nanostructures for the development of new supercapacitors by using green approaches in which the environmental impacts can be reduced without impairing the good properties of the electrodes [216,217]. Recently, Reddy et al. [217] synthesized high surface area TiO 2 NPs from the Ocimum tenuiflorum (OT) extracts, and Calotropis gigantea (CG) plants for the development of electrodes. The synthesized NPs showed a high specific capacitance of 105 F·g −1 for the OT and 224 F·g −1 for the CG compared with conventional TiO 2 -based electrodes, which indicates that green synthesized TiO 2 NPs are efficient for electrochemical energy storage devices. Dhanemozhi and co-authors [218] reported ZnO NPs synthesis using the Camellia sinensis plant extracts (i.e., green tea) and evaluated their capacitance features as potential candidates to the development of supercapacitor applications. The ZnO NPs demonstrated excellent CV characteristics and good electrochemical stability, indicating that the as-prepared material can be used for supercapacitors applications. Similar results were achieved by Anand et al. [219] and Lee et al. [220] on ZnO nanostructures synthesized with the aid of Prunus dulcis and Chlorella vulgaris plant extracts, respectively.
As in traditional synthesis, strategies such as functionalization with metallic NPs and the formation of composites have also been used to improve the capacitance of NPs produced by green approaches. Aravinda et al. [221] showed that ZnO decorated carbon NTs nanocomposite electrodes presented a significant increase in specific capacitance and good stored energy density than pure NTs electrodes. Rajangam et al. [222] observed a similar behavior from Ag decorated TiO 2 NPs synthesized using rose petals. Despite the reported significant advance in this area, many challenges need to be overcome to produce high-quality devices such as durability, electrode stability, high-capacity retention, good cycling stability. Although the use of oxide nanostructures itself has been proving that such challenges can be overcome, improvements are still needed in their synthesis approaches to develop active electrodes in which imbalance at redox sites, degradation, rise in internal resistance, and increase in equivalent series resistance can be minimized. In this scenario, the green synthesis approach can be the solution to these issues with the great advantage of low cost since the precursors are abundant in nature [223,224].

Solar Cell Application
Solar cells are an important way to produce clean and renewable energy, given their abundance and continuous availability. Over the last decades, research in this area has expanded due to the high global energy demand and the effects caused to the environment and climate by using fossil fuels. The ZnO and TiO 2 nanostructures synthesized by green approaches have been used in the manufacture of third-generation solar cells (comprising emerging technologies not yet available on the market), especially of Dye-sensitized Solar Cells (DSSCs), a subclass of thin-film solar cells that has shown to be a promising alternative to silicon solar cells in view of the low cost, efficiency and easy manufacturing. In this device, the process of converting sunlight into electricity is based on the sensitization of a wide bandgap semiconductor used as photoanode material [102,225].
The TiO 2 semiconductor is commonly used in DSSC photoanodes due to the fact of its properties such as its small particle size, high surface area, highly active anatase phase, high bandgap energy, low density, and high electron mobility [102,226], in addition to its non-toxicity, easy availability, and low cost. However, the ZnO semiconductor has also gained attention as a photoanode material. Characteristics, such as a wide bandgap, the high exciton binding energy (60 meV), strong luminescence, high thermal conductivity, and greater electron mobility than TiO 2 , have driven these studies [225,227]. Despite the advantages of combining the use of the TiO 2 and ZnO semiconductors produced by green synthesis with the manufacture of solar cells, studies in this area are still scarce, although promising. Deng et al. [201] recently found a very expressive result when manufacturing a DSSC photoanode depositing mesoporous spheres of rutile TiO 2 produced by green hydrothermal synthesis on FTO substrate coated with a dense layer of TiO 2 anatase NPs and sensitizing them with the dye N719. Due to the greater light capture and the high specific surface area provided by the mesoporous spheres, the device achieved a conversion efficiency of 8.43%, 18% higher than that found for the reference DSSC (single layer of NPs). Ullattil and Periyat et al. [228] reached a slightly lower performance using anatase mesoporous NPs synthesized by a green microwave method as photoanode material in a DSSC (6.58% conversion efficiency). However, in general, the conversion efficiency achieved in DSSCs has been more modest with values changing from 2.79% to 4.33% for DSSC with photoanodes based on anatase NPs biosynthesized [229][230][231], a 3.8% efficiency for a DSSC based on mixed-phase anatase and rutile TiO 2 nanorods synthesized from Phellinus linteus mushroom extract [232], an efficiency between 0.63-2.10% for DSSCs with ZnO NPs-based photoanodes [114,[233][234][235].
Strategies to improve the performance of the DSSCs photoanodes have evolved doping of titania with Zn 2+ ions [236] (efficiency increases from 4.4% to 4.8%), morphology changes [227], use of quantum dots instead of dye as sensibilization agent [237], use of a polymer-based electrolyte instead of the traditional liquid electrolyte in DSSCs (5.2% efficiency, TiO 2 NPs) [226], and quasi-solid DSSCs (5.50-6.46% efficiency, ZnO nanosheets, and building blocks) and formation of composites between ZnO and natural graphite (3.12% efficiency) [238], biosynthesized ZnO, commercial TiO 2 and graphene oxide (4.61-6.18% efficiency) [239]. In addition to DSSCs, other types of solar cells have also been developed using TiO 2 and ZnO nanostructures synthesized by green routes, the records include the manufacture of polymeric solar cells (PSCs) with the addition of TiO 2 NPs coating (25% higher efficiency than is found for uncoated PSCs) [240], the fabrication of hole-conductorfree perovskite solar cells from mesoporous TiO 2 NPs (8.52% efficiency, 21% higher than that found for commercial TiO 2 based devices) [163] and Pitchaiya et al. [241] in the manufacture of perovskite solar cells in bilayer using ZnO nanostructures between a TiO 2 NPs film and the perovskite layer (7.83% efficiency). The challenges in the development of third-generation solar cells based on nanostructures involve not only (i) the improvement of conversion efficiency, well below the limit reached by solar cells based on monocrystalline silicon, through the processing of new materials/components or improvement of existing ones; but also (ii) reliability and lifetime, devices must offer long-term stability and good resistance to moisture, heat, and impact; (iii) large-scale manufacturing, based on the implementation of new production techniques with critical dimensional control resources, structural homogeneity and higher yield that allow taking advantage of the quantum resources of nanostructures; (iv) reduction in manufacturing costs [242][243][244]. The use of TiO 2 and ZnO nanostructures synthesized by green routes, although it may not solve the first three problems, is a good bet for reducing production costs through more environmentally friendly processes with less energy consumption, time, and raw material.

Photocatalytic Water Splitting Application
The conversion of solar energy into electrochemical energy as fuel from water splitting has emerged as an efficient and low-cost strategy for clean and renewable energy production. Hydrogen (H 2 ) produced in this photocatalytic process is considered one of the most promising green fuels for the future due to its high energy-per-mass content, zero CO 2 emission, low-cost, operation facility and capability of separating H 2 and O 2 streams [245][246][247].
In photoelectrochemical cells (PEC), H 2 O can be converted directly to H 2 under solar irradiation, using a simple photocatalytic process as follows: (i) photogeneration of electronhole pairs in the photoanode (in general, semiconductor oxide materials); (ii) separation and transfer of the photogenerated electron-hole pairs to the electrolyte and counter-electrode; (iii) reaction of the evolution of O 2 (water splitting) on the surface of the photoanode by combining the photogenerated and H 2 O holes simultaneously with the evolution of H 2 in the counter electrode from the combination of the H + ions and the photogenerated electrons [248][249][250][251][252]. This water splitting reaction requires a minimum redox potential of 1.23 eV, so the semiconductor used with photoanode material must absorb photons with energy greater than 1.23 eV for the process to be viable and above 2.0 eV for the rate of reaction is satisfactory [253]. More detailed information on the water-splitting process can be found at [254][255][256].
The TiO 2 and ZnO semiconductors obtained by green syntheses are particularly interesting for use as photoanode materials in the H 2 generation process due to the simple, inexpensive and eco-friendly method of producing the material [257]. Also, the robustness, abundance, and non-toxicity contribute to the choice of these semiconductors as photocatalysts [258]. Both ZnO and TiO 2 have been considered promising photocatalysts, both are capable of producing photogenerated holes with high oxidizing power. The efficiency of H 2 generation with the use of these photocatalysts is limited by the wide bandgap and the high presence of electron-hole recombination centers; and, in the case of ZnO, due to the easy dissolution in aqueous solution under UV irradiation. Considering that the photocatalytic activity is strongly affected by the size [259], shape [258], and defects of the photocatalysts [260], the optimization of the morphology and crystalline structure [261,262] has been studied, and several micro-and nanostructures of ZnO and TiO 2 have been presented.
Recently, for example, Hu et al. [263] showed enhanced photocatalytic activity for TiO 2 anatase nanoplates produced by green solid-state synthesis. Nanoplates with exposed facet (001) and with a high degree of crystallinity present a generation rate of H 2 (13 mmol h −1 g −1 ) and current density (0.22 mA cm −2 ), higher than the obtained for other structures reported in the literature from conventional syntheses. In addition, the study shows that the photocatalytic generation of H 2 is strongly dependent on the sample's crystallinity and texture effects. Similar studies have also demonstrated good performance of fibrous hierarchical meso-macroporous N-doped TiO 2 (364.3 µmol/h) [264], TiO 2 /Pt NPs nanocomposites (4.92 mmol h −1 g −1 ) [265] and carbon-modified TiO 2 composite (21 mL h −1 g −1 ) [266], synthesized by green routes for the production of H 2 via water splitting. Archana et al. [214] prepared ZnO nanoparticles by a green combustion method and used them as a photocatalyst for the photocatalytic generation of H 2 . The water-splitting experiments showed smaller nanoparticles have a higher H 2 evolution rate, reaching a maximum of 360 µmol/g under optimized conditions. This enhanced efficiency was associated with an abundance of oxygen vacancies in the sample. Also, the study shows that no photo-corrosion process was observed during the reaction, indicating the excellent photostability of the NPs; it is believed that the residual carbon of the synthesis is responsible for this. Promising photochemical water splitting results have also been achieved using Ag-ZnO NPs biosynthesized as a photocatalyst; under ideal conditions, the evolution rate of H 2 reaches 214 mmol g −1 h −1 [267].
Despite the advantages and promising results obtained for the photocatalytic generation of H 2 by water splitting on PECs, this technology still faces many technical difficulties that limit its insertion in the market: (i) the hydrogen and oxygen generated must be immediately separated for reasons of safety, system complexity and product yield (without reverse reaction), which requires additional energy consumption, reducing the global efficiency of the process; (ii) development of more efficient mechanisms for capture, separation, storage and purity of H 2 gas (highly explosive); (iii) development of high quality photoanodes capable of rapid separation/extraction/transport/injection of carriers with low rate of recombination, ability to effectively absorb visible light and strong ability to capture incident photons in order to increase efficiency of the reaction of H 2 generation (~18% currently); current PEC cells need changes in materials and design to acts as electrochemical reactors and for large-scale production [256,[268][269][270][271][272][273]. Although slowly, efforts by the scientific community have been moving in this direction.

Conclusions and Future Perspective
The green synthesis approach of oxide nanostructures has been the area of focused research for the past few years. Green sources, such as plants, flowers, and bacteria, are acting as stabilizing and reducing agents to control nanomaterials' morphology. This review has provided a review of recent advancements, the challenges in green synthesis routes, and the suitability for TiO 2 and ZnO nanostructures for advanced applications.
Herein, firstly, the types of green approaches to synthesize ZnO and TiO 2 nanostructures based on traditional and widely used synthesis methods, such as hydrothermal, solvothermal, sol-gel, and co-precipitation, are highlighted. The possibility of merging low-cost and control of parameters, such as shape and size, with eco-friendly synthesis is the major justification for the employment of future efforts in developing a sustainable and scalable production of nanostructures. Different green sources, such as plant extract, bacteria, flower, and algae, and their use in these synthesis methods show marked variation in morphologies, surface area, porosity, and properties. The major advantages were discussed regarding green approaches such as the use of bio precursors for the synthesis, low waste of chemicals, reduced toxicity, replacement or suppression of the use of hazard solvents, low-energy waste for synthesis or chemical processes. Moreover, the effect of reaction parameters, such as pH, temperature, and reaction time, were discussed. Secondly, the applications of ZnO and TiO 2 have been widely explored already in previous review articles; therefore, we summarized the most important technological applications with their challenges, strengths, and future perspectives. As in gas sensors, we discussed how we can overcome problems such as operating temperature and selectivity issues. Similarly, we discussed challenges related to efficiency, manufacturing costs, lifetime, and large-scale production of solar cells based on nanostructures. In discussing photocatalysis, we showed the challenges in understanding the role of biocomponents used in syntheses and to optimize the structure and morphology of nanostructures to develop new applications in the area. As for supercapacitors, we presented some of the problems involved in their manufacture, such as durability, electrode stability, high-capacity retention, and toxicity, and how the use of greener nanostructures can solve some of them.
From future perspectives, one of the central challenges starting from now would be the development of new green methods to synthesize ZnO and TiO 2 NPs and the improvement of the already existing methods with the optimization of reactions to, consequently, achieve an improved quality of the as-synthesized products. The extrapolation of laboratory experiments to an industrial scale will be important, too, as new green solutions to synthesize nanomaterials will be developed, especially those based on bio precursors, which have rapid change in their physical and chemical properties. The nanostructured materials prepared via green synthesis have a huge application in biomedicine, pharmaceutical, and food industries and, thus, will become a major research area in the next few years.

Conflicts of Interest:
The authors declare no conflict of interest.