Electrodegradation of Acid Mixture Dye through the Employment of Cu/Fe Macro-Corrosion Galvanic Cell in Na2SO4 Synthetic Wastewater

Traditional wastewater purification processes are based on a combination of physical, chemical, and biological methods; however, typical electrochemical techniques for removing pollutants require large amounts of electrical energy. In this study, we report on a process of wastewater purification, through continuous anodic dissolution of iron anode for aerated Cu/Fe galvanic cell in synthetic Na2SO4 wastewater solution. Electrochemical experiments were conducted by means of a laboratory size electrolyzer, where electrocoagulation along with electrooxidation phenomena were examined for wastewater containing Acid Mixture dye. The above was visualized through the employment of electrochemical (cyclic voltammetry and ac impedance spectroscopy techniques) along with instrumental spectroscopy analyses.


Introduction
Large amounts of different dyes that are present in industrial wastewaters are responsible for serious environmental and health problems [1,2]. Globally, many industries discharge up to 15% of the total dyes used in effluents directly into water bodies. Among various groups of textile dyes, particular attention should be paid to the so-called azo dyes. This specific group of coloring agents is characterized with the presence of one or more azo groups (-N=N-) [3][4][5]. Large concentrations of azo-type dyes in water have a direct impact on the conditions of all organisms living in a biosystem, which, most importantly, are then transferred to human populations. Various studies conducted in recent years have confirmed serious toxicity, as well as mutagenic and carcinogenic effects of some azo dyes, including their metabolites [6][7][8][9][10]. The above, combined with severe environmental pollutions, have led scientists to consider the development of novel, more efficient treatment methods for the dye-based industrial wastewaters.
Dc-powered electrochemical methods have widely been examined and utilized for the remediation of dye-polluted wastewaters. These methods are of significant interest as they combine three parallel processes, namely electrocoagulation, electrooxidation and electroflotation [11][12][13]. Numerous scientific studies have reported total decolorization of Molecules 2021, 26, 4580 2 of 15 wastewaters containing azo dyes by electrochemical means, in the order of 71-99% [14][15][16][17][18][19][20][21][22]. However, despite the high efficiency of such dc-powered systems, they still suffer from excessive power consumption. Nevertheless, this deficiency could be successfully overcome by an electrochemical method based on the galvanic series theory through the application of an appropriately designed galvanic cell (cathode/anode) reactor. This receptacle generates spontaneous current based on sacrificial anode oxidation, along with reduction reaction proceeding on the cathode surface. As compared with formerly described dc-powered methods, the latter design eliminates the presence of expensive dc. infrastructure and electronic control systems, and also radically reduces total consumption of electricity upon wastewater purification (see recently published work by Łuba et al. from this laboratory on Cu/Al alloy galvanic cell-based dye purification in [23]).
During the electrolysis process that occurs inside the Cu/Fe reactor, an iron-made anode undergoes oxidation reaction, which releases soluble ferrous (Fe 2+ ) ions that rapidly form iron hydroxide species through the reaction with OHions (and highly reactive short-lived • OH radicals that may lead to the cleavage of the dye molecule) generated on the surface of the cathode [24][25][26][27][28][29][30]. During the electrolysis process, the electrolyte's pH increases. The mechanism of the anodic and cathodic reactions for the Cu/Fe galvanic cell is described by Equations (1)-(3) as follows: Anodic reaction: Cathodic reaction: Formation of ferrous hydroxide and ferric oxide: Hence, Fe dissolution leads initially to the formation of ferrous hydroxide species Equation (3) during the spontaneous reaction of Fe 2+ , cations emerge in the supporting solution during the anodic dissolution process Equation (1) with hydroxyl (OH − ) anions generated on the cathode surface Equation (2). Then, in the presence of dissolved oxygen, ferrous hydroxide is converted to ferric oxide (Fe 2 O 3 ), according to Equation (3).
The aim of this study was to evaluate the effectiveness of a Cu/Fe mild steel galvanic cell in the electrochemical treatment of synthetic wastewater, comprising small, but significant amounts of Acid Mixture (Acid Violet 90 and Acid Red 357 constituents, Figure 1) dye. The examination of the dye's removal was made by means of the combined effect of the electrocoagulation and surface-electrooxidation processes.
Molecules 2021, 26, x FOR PEER REVIEW 2 of 16 electroflotation [11][12][13]. Numerous scientific studies have reported total decolorization of wastewaters containing azo dyes by electrochemical means, in the order of 71-99% [14][15][16][17][18][19][20][21][22]. However, despite the high efficiency of such dc-powered systems, they still suffer from excessive power consumption. Nevertheless, this deficiency could be successfully overcome by an electrochemical method based on the galvanic series theory through the application of an appropriately designed galvanic cell (cathode/anode) reactor. This receptacle generates spontaneous current based on sacrificial anode oxidation, along with reduction reaction proceeding on the cathode surface. As compared with formerly described dc-powered methods, the latter design eliminates the presence of expensive dc. infrastructure and electronic control systems, and also radically reduces total consumption of electricity upon wastewater purification (see recently published work by Łuba et al. from this laboratory on Cu/Al alloy galvanic cell-based dye purification in [23]). During the electrolysis process that occurs inside the Cu/Fe reactor, an iron-made anode undergoes oxidation reaction, which releases soluble ferrous (Fe 2+ ) ions that rapidly form iron hydroxide species through the reaction with OHions (and highly reactive short-lived • OH radicals that may lead to the cleavage of the dye molecule) generated on the surface of the cathode [24][25][26][27][28][29][30]. During the electrolysis process, the electrolyte's pH increases. The mechanism of the anodic and cathodic reactions for the Cu/Fe galvanic cell is described by Equations (1)-(3) as follows: Anodic reaction: Cathodic reaction: Formation of ferrous hydroxide and ferric oxide: Hence, Fe dissolution leads initially to the formation of ferrous hydroxide species Equation (3) during the spontaneous reaction of Fe 2+ , cations emerge in the supporting solution during the anodic dissolution process Equation (1) with hydroxyl (OH − ) anions generated on the cathode surface Equation (2). Then, in the presence of dissolved oxygen, ferrous hydroxide is converted to ferric oxide (Fe2O3), according to Equation (3).
The aim of this study was to evaluate the effectiveness of a Cu/Fe mild steel galvanic cell in the electrochemical treatment of synthetic wastewater, comprising small, but significant amounts of Acid Mixture (Acid Violet 90 and Acid Red 357 constituents, Figure  1) dye. The examination of the dye's removal was made by means of the combined effect of the electrocoagulation and surface-electrooxidation processes.

Characterization of Galvanic Cell's Operation
The electrochemical characterization of the Cu/Fe galvanic reactor was examined in Na 2 SO 4 supporting electrolyte containing AM (50 mg dm −3 , pH = 3.05, κ = 15 mS cm −1 ,  The electrochemical performance of the Cu/Fe mild steel galvanic cell was examined by measuring the galvanic coupling current (Igc) intensity. Hence, after 1 h of continuous Cu/Fe cell's operation, the recorded Igc value reached 8.55 mA or 0.29 mA cm −2 ( Figure 2b). As previously mentioned, this current resulted from the formation of ferrous hydroxide species during the spontaneous reaction of Fe 2+ , cations evolved into the electrolyte during the anodic dissolution process with hydroxyl OHanions generated on the cathode, according to Equations (1) and (2) above. Moreover, the Fe 2+ ions could react with The electrochemical performance of the Cu/Fe mild steel galvanic cell was examined by measuring the galvanic coupling current (I gc ) intensity. Hence, after 1 h of continuous Cu/Fe cell's operation, the recorded I gc value reached 8.55 mA or 0.29 mA cm −2 ( Figure 2b). As previously mentioned, this current resulted from the formation of ferrous hydroxide species during the spontaneous reaction of Fe 2+ , cations evolved into the electrolyte during the anodic dissolution process with hydroxyl OHanions generated on the cathode, according to Equations (1) and (2) above. Moreover, the Fe 2+ ions could react with electrolyte-dissolved molecular oxygen to form Fe(OH) 3 species, according to Equation (4) below: Then, freshly formed metal hydroxide species attract oppositely charged dye molecules, leading to their neutralization, destabilization, and formation of larger agglomerates that eventually sediment on the bottom of the reaction tank [31][32][33].

Cyclic Voltammetry Electrochemical Behavior of AM Dye
Initially, the electrochemical behavior of Fe mild steel electrode in 0.054 M Na 2 SO 4 supporting solution was examined by means of the cyclic voltammetry (CV) technique, over the potential range from −1.1 to 0.0 V vs. SCE. Figure 3a shows the third cycle of the CV response for Fe working electrode of the Cu/Fe galvanic cell, carried out in pure and AM-modified 0.054 M Na 2 SO 4 electrolyte, obtained at 293 K with a sweep-rate of 50 mV s −1 .
For the cyclic voltammogram recorded in the absence of the AM dye, two irreversible anodic peaks could clearly be observed, namely a low potential and very broad feature, centered at about −0.85 V, and another one positioned at ca. −0.35 V vs. SCE. Thus, the former peak is related to the process of Fe(II) formation, whereas the latter one could be allotted to its further oxidation to form Fe 3 O 4 or Fe(OH) 3 surface layers [34][35][36].
Then, having introduced 50 mg dm −3 of AM dye into the electrolyte, two well-pronounced oxidation features (centered at ca. −0.56 and −0.42 V) appeared upon cycling towards more positive potentials. It is strongly believed that these anodic patterns correspond to consecutive surface oxidation (commencing with nitrogen-to-nitrogen bond cleavage) of the examined dye's constituents [37][38][39][40]. Afterwards, as the cycling becomes reversed towards less anodic potentials, a broad cathodic feature is observed over the potential range from −0.8 to −1.0 V (Figure 3a). This feature is most likely related to reduction of the surface-oxidized AM or its intermediates, upon preceding anodic cycle. Most importantly, as the cycling continues, the above-described pattern exhibits a significant shift towards more negative potentials (see Figure 3b). However, as the CV sweep is then limited to the potential range from −0.75 to −1.1 V vs. SCE, formation of the surface-oxidized intermediates is stopped, and the previously observed reduction peak completely disappears from the cyclic voltammogram after only several cycles (see Figure 3c).

Electrochemical ac Impedance Characterization
The ac impedance characterization of iron electrode in the presence of 50 mg dm −3 of AM dye in the supporting 0.054 M Na 2 SO 4 solution is shown in Table 1 and Figure 4a,b. Hence, in the presence of the AM dye, the Nyquist impedance plots exhibited two "depressed" and partial semicircles over the examined potential range from −950 to −380 mV vs. SCE. Thus, for the most negative potentials (i.e., −950 and −900 mV), the highfrequency semicircle was associated with oxidative formation of Fe 2+ cations, whereas the low-frequency arc observed in the Nyquist impedance plots corresponded to the surface formation of iron II hydroxide layer (see Figure 4a along with its Bode plot inset). Thus, for the first, −0.95 V oxidation peak (Figure 3a), the recorded charge transfer resistance (R ct ) parameter for iron oxidation came to 67.4 Ω cm 2 , whereas the recorded adsorption, i.e., Fe(OH) 2 charge transfer resistance (R Ads ) value, reached 1980 Ω cm 2 . Moreover, the corresponding interfacial capacitance (C dl ) and pseudocapacitance (C Ads ) parameters reached 536 and 5181 µF cm −2 , respectively (see equivalent circuit used to fit the recorded data in Figure 5). It should be noted that these results are in line with those recently reported on a similar experimental azo dye purification system in [41].

Cyclic Voltammetry Electrochemical Behavior of AM Dye
Initially, the electrochemical behavior of Fe mild steel electrode in 0.054 M Na2SO4 supporting solution was examined by means of the cyclic voltammetry (CV) technique, over the potential range from −1.1 to 0.0 V vs. SCE. Figure 3a shows the third cycle of the CV response for Fe working electrode of the Cu/Fe galvanic cell, carried out in pure and AM-modified 0.054 M Na2SO4 electrolyte, obtained at 293 K with a sweep-rate of 50 mV s −1 . For the cyclic voltammogram recorded in the absence of the AM dye, two irreversible anodic peaks could clearly be observed, namely a low potential and very broad feature, centered at about −0.85 V, and another one positioned at ca. −0.35 V vs. SCE. Thus, the former peak is related to the process of Fe(II) formation, whereas the latter one could be allotted to its further oxidation to form Fe3O4 or Fe(OH)3 surface layers [34][35][36].  Table 1. Parameters for the processes of Fe electrode oxidation and azo dye electrodegradation (at a total concentration of AM at 50 mg dm −3 ) on the surface of the Fe mild steel anode in contact with 0.054 M Na 2 SO 4 , achieved by fitting equivalent circuit models presented in Figure 5 to the experimentally obtained impedance data (dimensionless ϕ parameter, which determines the constant phase angle in the complex-plane plot (0 ≤ ϕ ≤ 1) of the CPEs circuit, varied between 0.79 and 0.86, and 0.50 and 0.96 for ϕ 1 and ϕ 2 , respectively). The potential range from −630 to −380 mV ( Table 1) is characteristic of further iron oxidation to form Fe 3 O 4 or Fe(OH) 3 species along with consecutive surface electrooxidation of the dye's components (see Figure 3a). Hence, the high frequency arcs, observed in the Nyquist plots of Figure 4b, correspond to the former process, whereas intermediate/low frequency semicircles refer to the latter, i.e., dye electrodegradation steps. Thus, for the peak potential points (−570 and −410 mV), the recorded R ct reached 32.8 and 12.8 Ω cm 2 , whereas the C dl parameter reached 672 and 510 µF cm −2 , respectively. Interestingly, the recorded charge-transfer resistance (R ox ) values, corresponding to the successive, oxidative electrodegradation of the dye components were radically diminished (6.64 and 2.06 Ω cm 2 , correspondingly). The above comes in line with major augmentation of the recorded pseudocapacitance, C p parameter (see Table 1 for details).

E/mV
Alternatively, for the pure Na 2 SO 4 solution at positive potentials to −800 mV, only one somewhat depressed semicircle was noticed in relation to a single-step charge transfer reaction associated with further electrode surface oxidation process, resulting in the formation of Fe(III) species [36] (see examples of this behavior in Figure S1 in Supplementary Materials).    The potential range from −630 to −380 mV ( Table 1) is characteristic of further iron oxidation to form Fe3O4 or Fe(OH)3 species along with consecutive surface electrooxidation of the dye's components (see Figure 3a). Hence, the high frequency arcs, observed in the Nyquist plots of Figure 4b, correspond to the former process, whereas intermediate/low frequency semicircles refer to the latter, i.e., dye electrodegradation steps. Thus, for the peak potential points (−570 and −410 mV), the recorded Rct reached 32.8 and 12.8 Ω cm 2 , whereas the Cdl parameter reached 672 and 510 µF cm −2 , respectively. Interestingly, the recorded charge-transfer resistance (Rox) values, corresponding to the successive, oxidative electrodegradation of the dye components were radically diminished (6.64 and 2.06 Ω cm 2 , correspondingly). The above comes in line with major augmentation of the recorded pseudocapacitance, Cp parameter (see Table 1 for details).
Alternatively, for the pure Na2SO4 solution at positive potentials to −800 mV, only one somewhat depressed semicircle was noticed in relation to a single-step charge transfer reaction associated with further electrode surface oxidation process, resulting in the formation of Fe(III) species [36] (see examples of this behavior in Figure S1 in Supplementary Materials).

UV-Vis Spectrophotometry Analysis
The process of Fe surface electrooxidation and -degradation of the examined AM azo dye upon operation of the Cu/Fe galvanic macro-corrosion cell was primarily monitored by utilizing the UV-Vis spectrophotometry technique, where the process's optimization was carried out by recording absorption spectra over a 230-800 nm wavelength range (see Figure 6a).
The effect of an initial dye decomposition stage recorded at a wavelength of 500 nm is illustrated in Figure 6b. Here, the recorded, gradually diminishing absorbance, is directly linked to the concentration reduction of the pigment. During the stage of decolorization, the azo (-N=N-) bond, which is a chromogenic entity, becomes an acceptor for electrons released during the anodic oxidation process. Thus, the molecule breaks down into aromatic/phenol and aromatic amine derivatives, which are structurally similar to 3amino-2-hydroxy-5-nitorbenzenesulfonic acid or 2-chloro-4-nitrobenzamine [37][38][39]. With respect to the aromatic ring degradation stage (λ = 280 nm), over the initial 900 s of the electrolysis process, the recorded changes in the absorbance intensity at the where R s is solution resistance; C dl is double-layer capacitance; R ct is charge-transfer resistance parameter for electrooxidation of Fe anode surface; R Ads and C Ads are adsorption resistance and capacitance parameters for Fe(OH) 2 film, respectively; and R ox and C p are azo dyes electrooxidation resistance and pseudocapacitance parameters, respectively, connected with oxidative degradation of AM dye molecule. The circuits include constant phase elements (CPEs) to account for distributed capacitance.

UV-Vis Spectrophotometry Analysis
The process of Fe surface electrooxidation and -degradation of the examined AM azo dye upon operation of the Cu/Fe galvanic macro-corrosion cell was primarily monitored by utilizing the UV-Vis spectrophotometry technique, where the process's optimization was carried out by recording absorption spectra over a 230-800 nm wavelength range (see Figure 6a).
The effect of an initial dye decomposition stage recorded at a wavelength of 500 nm is illustrated in Figure 6b. Here, the recorded, gradually diminishing absorbance, is directly linked to the concentration reduction of the pigment. During the stage of decolorization, the azo (-N=N-) bond, which is a chromogenic entity, becomes an acceptor for electrons released during the anodic oxidation process. Thus, the molecule breaks down into aromatic/phenol and aromatic amine derivatives, which are structurally similar to 3-amino-2-hydroxy-5-nitorbenzenesulfonic acid or 2-chloro-4-nitrobenzamine [37][38][39]. With respect to the aromatic ring degradation stage (λ = 280 nm), over the initial 900 s of the electrolysis process, the recorded changes in the absorbance intensity at the wavelength of 280 nm (Figure 6c) indicate that total concentration of the aromatic type substances/molecules containing aromatic ring in their structures has increased. These results are in good agreement with the above-depicted AM degradation pathway. As it comes to the last step of the AM mineralization process (monitored at λ = 240 nm, Figure 6d), a vast number of relatively simple (e.g., maleic, formic, and acetic acids; aldehydes; ammonia; nitrogen oxides; and finally, carbon dioxide molecule) or more complex chemical compounds (e.g., pentanoic acid) could be produced. Finally, the total quantitative removal of the AM dye through the electrooxidation and electrocoagulation processes yielded 21 and 37%, after 900 and 3600 s of continuous electrolysis, respectively (see Figure 6e).
Furthermore, Table 2 presents the total quantitative removal of various azo dyes, obtained through other novel degradation methods described in the literature [17,18,20,22,[40][41][42]. On the one hand, the estimated total quantitative removal of azo dyes for yeast-and algaebased were inferior as compared with the method presented in this study. On the other hand, the literature-based electrochemical methods powered with external power supply turned out to be significantly superior in dye degradation process as compared with both biological and galvanic-driven methods. Nevertheless, they have their own disadvantages, for example, high energy consumption (high operational current densities), as well as use of scarce and rare materials and generation of harmful by-products during the electrolysis process. However, employment of Cu/Fe macro-corrosion galvanic cell excludes the use of an

Chromatography
The successive removal of the AM dye from synthetic wastewater solution was also evidenced by ultra-performance liquid chromatography, coupled with double quadrupole tandem mass spectrometry (UPLC-MS/MS) system analysis. The above showed that, just after 900 s of continuous electrolysis, the total removal of the dye's constituents reached 60 and 71% for AV90 and AR357, respectively. Then, after one hour of the test, the removal of the AV90 and AR357 dye components came to 86 and 91%, respectively (see Table 3 and Figure 7 for details). As compared with the UV-Vis technique, there were significant differences in the recorded data, which resulted from selectivity variation between these two analytical methods. Figure 6. UV-Vis absorption spectra changes in time for AM dye's electrodegradation, carriedout by means of Cu/Fe galvanic cell, where: (a) Representation of the three segments of AM dye's electrooxidation process on the surface of Fe anode in Na 2 SO 4 solution (for an initial dye concentration of 50 mg dm −3 ); (b) evolution of decolorization process, recorded for a wavelength of 500 nm; (c) progress of aromatic ring degradation, recorded for a wavelength of 280 nm; (d) evolution of mineralization process, recorded for a wavelength of 240 nm; (e) quantitative dye assay after sedimentation process, recorded for a wavelength of 500 nm.

Chromatography
The successive removal of the AM dye from synthetic wastewater solution was also evidenced by ultra-performance liquid chromatography, coupled with double quadrupole tandem mass spectrometry (UPLC-MS/MS) system analysis. The above showed that, just after 900 s of continuous electrolysis, the total removal of the dye's constituents reached 60 and 71% for AV90 and AR357, respectively. Then, after one hour of the test, the removal of the AV90 and AR357 dye components came to 86 and 91%, respectively (see Table 3 and Figure 7 for details). As compared with the UV-Vis technique, there were significant differences in the recorded data, which resulted from selectivity variation between these two analytical methods. Figure S2 in the Supplementary Materials presents the UPLC-MS/MS chromatogram with the scan showing a number of high molecular mass (MM), unidentifiable electrodegradation products. As the electrolysis process causes the formation of small amounts, but high MM compounds, it could be concluded that after initial breaking of the -N=N-azo bond, some of the reactive fragments of an initial dye could react with each other, thus, forming such species.

Materials and Methods
Construction of Galvanic Cell Reactor, Chemicals, and Solutions Experimental Methodologies.
In this study, the wastewater electrocoagulation/electrooxidation unit was composed of ca. 300 mL glass-made electrochemical reactor (see Figure 9 in [23]) and electrodes, which were arranged in a single Fe sacrificial anode placed between two Cu cathodes. A cylindrically shaped Fe mild steel was used as a sacrificial anode with an effective surface area of 29.3 cm 2 (diameter Φ = 3.5 cm, thickness: d = 1 cm) (DIN C15 (1.0401), ArcelorMittal, Dąbrowa Górnicza, Poland) and cathodes were made of cylindrically shaped copper with a total effective electrode area of 84 cm 2 (two plates 4 × 5 × 0.1 cm). An anode-to-cathode interelectrode gap was about 15 mm.
All procedures for the preparation of Cu and Fe electrodes, as well as electrochemical cell and working solutions' preparation, employed electrochemical instrumentation and methodologies (cyclic voltammetry and ac impedance spectroscopy), and the UV-Vis spectroscopy analyses were as those recently reported in [23,43] from this laboratory. The electrolyte pH, dissolved oxygen concentration, and conductivity evaluations were performed with pHenomenal ® pH 1100 L, pHenomenal ® OX 4100 L, and pHenomenal ® CO 3100 L meters from VWR, correspondingly. The chromatographic quantitation of AR357 and AV90 levels was achieved in reversed-phase liquid chromatography ACQUITY UPLC (ultra-performance liquid chromatography) system with I-Class Plus coupled with a Xevo TQ-XS Triple Quadrupole Mass Spectrometry (Waters, Milford, CT, USA). Chromatographic separation of AR357 and AV90 dye components was performed by means of ACQUITY UPLC BEH C18 column (1.7 µm, 2.1 × 50 mm, Waters) maintained at 50 • C. The mobile phase consisted of phase A (0.005% ammonium acetate for AR357 and AV90) and phase B (acetonitrile for AR357 and AV90) in the gradient elution. Each sample analysis was carried out for 5 min, at a flow rate of 400 µL min −1 . An injection volume was 1 µL and temperature of the autosampler was maintained at 15 • C. Detection was performed with a double quadrupole tandem mass spectrometer in the negative ion mode for both AR357 and AV90 pigments. The setting parameters of the detector are illustrated in Table 4 below. Equipment was set up in a multiple reaction monitoring (MRM) mode and transitions of 447.5 and 442.5 m/z were used for determination of the AR357 and AV90 parts, respectively. Samples collected from electrolysis (100 µL of AM) were dissolved in water to achieve final volume of 500 µL and transferred into total recovery vials (Waters). Finally, an aliquot was injected for UPLC-MS/MS analysis.  Poland). In order to provide the required high effectiveness of surface electrooxidation processes, conductivity of the working solutions was settled at about 15 mS, the working solution was under additional aeration to obtain ca. 10.5 ppm of dissolved oxygen content, whereas their pH was adjusted to the set value of 3.05.

Conclusions
The electrochemical method, based on the operation of a macro-corrosion, Cu/Fe galvanic cell, for wastewater purification from AM dye pollutant, referred to in this work, gave very encouraging results. Surface electrooxidation (degradation) of the dye components seems to be a key and necessary step to initiate the process of the dye removal from synthetically made wastewater.
The surface electrooxidation reactions were strongly supported by the recorded ac impedance spectroscopy and cyclic voltammetry results. In addition, the UV-Vis and UPLC-MS/MS characterizations implied a very complex and unpredictable mechanism of AM electrodecomposition, most likely leading to the formation of numerous, though extremely hard to identify, products.
In summary, in this study, the proposed wastewater treatment method, based on the operation of commonly available macro-corrosion galvanic cell, may be considered to be a suitable replacement for the generally used, multi-step wastewater treatment methods. However, further work is necessary in order to adapt this technology to real industrial conditions.
Supplementary Materials: Figure S1: The recorded complex plane Nyquist impedance plots for low carbon steel electrode in Na 2 SO 4 solution, derived for the potential value of −390 vs. SCE. The solid lines correspond to the representation of the data according to the equivalent circuit model presented in Figure 5 of the main manuscript., Figure S2

Data Availability Statement:
The data presented in this study are available on request from the corresponding author.