Removal of Chromium(III) and Cadmium(II) Heavy Metal Ions from Aqueous Solutions Using Treated Date Seeds: An Eco-Friendly Method

The aim of the research was to prepare low-cost adsorbents, including raw date pits and chemically treated date pits, and to apply these materials to investigate the adsorption behavior of Cr(III) and Cd(II) ions from wastewater. The prepared materials were characterized using SEM, FT-IR and BET surface analysis techniques for investigating the surface morphology, particle size, pore size and surface functionalities of the materials. A series of adsorption processes was conducted in a batch system and optimized by investigating various parameters such as solution pH, contact time, initial metal concentrations and adsorbent dosage. The optimum pH for achieving maximum adsorption capacity was found to be approximately 7.8. The determination of metal ions was conducted using atomic adsorption spectrometry. The experimental results were fitted using isotherm Langmuir and Freundlich equations, and maximum monolayer adsorption capacities for Cr(III) and Cd(II) at 323 K were 1428.5 and 1302.0 mg/g (treated majdool date pits adsorbent) and 1228.5 and 1182.0 mg/g (treated sagai date pits adsorbent), respectively. It was found that the adsorption capacity of H2O2-treated date pits was higher than that of untreated DP. Recovery studies showed maximal metal elution with 0.1 M HCl for all the adsorbents. An 83.3–88.2% and 81.8–86.8% drop in Cr(III) and Cd(II) adsorption, respectively, were found after the five regeneration cycles. The results showed that the Langmuir model gave slightly better results than the Freundlich model for the untreated and treated date pits. Hence, the results demonstrated that the prepared materials could be a low-cost and eco-friendly choice for the remediation of Cr(III) and Cd(II) contaminants from an aqueous solution.


Introduction
Over the last decade, the identification of toxic elements, particularly in water, has grown into a key issue of public interest [1]. Among them, heavy metals have received great attention because of their deadly nature [2]. Heavy metals are increasingly worrisome due to their prospective influences on the environment and human health [2][3][4]. Owing to their physical and chemical properties, they have are extensively disseminated into the surroundings and are used in industrial areas including agricultural, medical and domestic [5][6][7]. Industrial effluents are a major source of environmental pollution and exposure to human beings [8]. Heavy metals are frequently present in water bodies, and most of them are regarded as highly lethal even in very small amounts [9,10]. Heavy metals, for instance, lead, cadmium, chromium, cobalt, arsenic, mercury and nickel, are listed as very toxic elements [11]. These metals are assumed to be ubiquitous toxicants, and their deadliness is influenced by many factors, for instance, the amounts of heavy metal doses, types of elements and exposure route [12][13][14]. Heavy metals can be transported into

H2O2 Treatment of Date Powders
Both the prepared MDP and SDP powder samples were treated with H2O2 (200 mL, 30% v/v) for the possible introduction of negative functionalities (-OH) onto the adsorbent surface. It also helps to decompose organic content, reduce the biomass recalcitrance and prevent cellulose degradation of the MDP and SDP powder [32]. This process was carried out by taking 10 g powders of each date type in a 100 mL beaker individually and 100 mL H2O2 solution and adding them into the beakers. Then, for proper mixing, a magnetic bar was placed inside each beaker, and the beakers were kept overnight in a magnetic stirrer at 125 rpm. Finally, the suspension was filtered through Buckner funnel using a vacuum pump and washed several times with DI water to remove any traces of H2O2. Then, the filtered powders were dried overnight with an oven at 90 °C. Then, they were taken out, allowed to cool and stored in clean glass bottles until further testing for metal ions adsorption. The treated materials were named TMDP and TSDP for majdool and sagai date pits, respectively.

Adsorption and Desorption Studies
Removal of heavy metal ions was carried out through batch adsorption studies. To do so, 0.05 g powder of each date's seeds adsorbents were put into a previously cleaned and dry 100 mL Erlenmeyer flask, and 20 ppm (C o ) metal solutions were added individually into the flask. The solutions in the flasks were kept in a shaker overnight with a speed of 100 rpm to allow equilibration. The mixtures were then filtered and stored in a cool and dry place. At equilibrium, the concentration of metal ions, C e, was quantitatively determined by atomic adsorption spectroscopies, AAS (Thermo Scientific Evolution 600, Waltham, MA, USA).
The percentage adsorption (%) and metal ions removal capacity of the adsorbents at equilibration time (q e ) and at arbitrary time t (q t ) were calculated according to Equations (1)-(3) [32]: adsorption capacity at equilibrium q e = (C o − C e ) × V m (2) adsorption capacity at time t (q t ) = ( where C o , C e , and C t are the initial, equilibrium and at-time-t concentrations, respectively (mg/L), of heavy metal solution; V is the volume (L) of heavy metal solution; and m is the mass (g) of adsorbents. The adsorption capacities, both (q e ) and (q t ), were calculated as mg/g. The initial pH (pH i ) of metal solutions of C o , 25 mg/L, was changed from 2 to 10 for the pH investigations. The effects of metal ion starting concentration (C o ) on adsorption were investigated in the range of 20-100 mg/L at temperatures ranging from 293 to 323 K. The contact time (t) experiment for the target analytes adsorption at C o of 25 mg/L were carried out at intervals ranging from 2 min to 24 h.
For desorption experiments, adsorbents (0.05 g) were initially saturated for 24 h with metal ions solutions (50 mL; 25 mg/L) individually. To remove unadsorbed traces of treated metal ions, saturated adsorbents were gently rinsed with DI water. Thereafter, the metal ions from saturated adsorbent samples were eluted using different eluents, including NaOH, HNO 3 , HCl, H 2 SO 4 and CH 3 COOH solutions (50 mL; 0.1 mol/L). The concentration of metal ions in the eluent was quantitatively determined, and the corresponding percentage of desorption (% Desorption) was calculated as: %Desorption = (Concentration of metal ion desorbed/Concentration of metal ions adsorbed on adsorbent) × 100

Thermodynamic Studies of Metal Ions Adsorptions
Thermodynamic parameters are very important for adsorption studies, indicating the spontaneity of the adsorption process. The negative value of Gibb's free energy change (∆G • ) for a given temperature indicates the spontaneity of the adsorption process. Among the parameters, Gibb's free energy change (∆G • ) were calculated using Equation (1) while the change in enthalpy (∆H • ) and change in entropy (∆S • ) were determined using the equation, where R is the gas constant (8.314 J/mol K), T is the temperature in Kelvin (K) and Ka is the Langmuir constant [33]. Surface morphology and physical properties of different as-prepared and treated adsorbents were investigated by SEM. Figure 2 shows the SEM images of MDP, TMDP, SDP and TSDP samples. The SEM image indicates the rough, highly porous and defined structure surface morphologies of the adsorbents suitable for metal adsorption. In addition, the SEM micrographs revealed that the treated date pits (TMDP, TSDP) were of higher porosity compared to the raw material (MDP, SDP). The Energy Dispersive X-ray Spectroscopy Analysis (EDX) was performed to determine the composition of the adsorbents, which confirms that the adsorbents consisted of carbon and negative heteroatoms such as oxygen and nitrogen. Upon H 2 O 2 treatment, the adsorbents show a higher amount of oxygen, as expected (33 to 41%), indicating the conversion of DPs into negatively charged surfaces ( Table 1).

Results and Discussion
The BET surface areas were determined for untreated and H2O2-treated date pit powder. The surface area for treated materials was found to increase from 2.94 to 9.97 m 2 /g in TMDP, while for TSDP, the areas changed from 2.80 to 9.46 m 2 /g. These changes in areas indicate the development of porosity during the H2O2 treatment of the as-prepared materials and enhancing their adsorption properties [32]. The adsorption average pore widths of both H2O2-treated and untreated dates pit powder were found to be in the range of 5-10 nm.   The BET surface areas were determined for untreated and H 2 O 2 -treated date pit powder. The surface area for treated materials was found to increase from 2.94 to 9.97 m 2 /g in TMDP, while for TSDP, the areas changed from 2.80 to 9.46 m 2 /g. These changes in areas indicate the development of porosity during the H 2 O 2 treatment of the as-prepared materials and enhancing their adsorption properties [32]. The adsorption average pore widths of both H 2 O 2 -treated and untreated dates pit powder were found to be in the range of 5-10 nm.

Fourier-Transform Infrared Spectroscopic Analysis (FTIR)
Before and after metal ion adsorption, FTIR was used to better understand the adsorption mechanism for both as-prepared and treated adsorbents. FTIR is a useful tool for identifying the functional groups on the surface of the adsorbent and how they are affected by the experimental circumstances. RDP is a type of lignocellulosic material made up primarily of cellulose, hemicellulose, lignin and protein. Oxygen-rich components such as hydroxyl, ether and carbonyl functional groups are abundant in cellulose and hemicellulose. The ability of RDP to adsorb heavy metals is explained by the presence of these groups on its surface [34]. Figure 3 (upper panel) shows a broad peak in the 3230-3560 cm −1 range, indicating the presence of -OH, -NH or both, which is characteristic of lignocellulosic organic polymers [35]. The two peaks at 2921 and 2843 cm −1 indicate aliphatic C-H stretching vibrations. Peaks at 1739, 1602 and 1039 cm −1 show the presence of C=O (unconjugated carbonyl), C=C and C-O, respectively, with the small peaks between C=C and C-O referring to methyl group bending peaks [34,36]. The phenolic and C-O stretching vibrations of carboxylates produced a band at 1403-1432 cm −1 . The bands between 1200 and 1350 cm −1 and 1000 and 1150 cm −1 were due to carboxylic acid and C-O-C vibrations, respectively. The presence of -OH polysaccharide groups is confirmed by a band at 500-700 cm −1 . A minor shift (to higher wavenumbers) in peak position and increases in peak intensities were observed after Cr(III) and Cd(II) adsorption on adsorbents at peaks 3230-3560 cm −1 ,1739 cm −1 and 1039 cm −1 . A minor shift (to higher wavenumbers) in peak position and increases in peak intensities were observed after Cr(III) and Cd(II) adsorption on adsorbents at peaks 3230-3560 cm −1 , 1739 cm −1 and 1039 cm −1 , which shows the involvement of the corresponding moieties in adsorption of metal ions. From these findings, it can be postulated that -OH or NH C=O and C-O functions were principally responsible for binding Cr(III) and Cd(II) over the surface via electrostatic interactions and lone-pair donation [32]. As a result, electrostatic interactions, as well as coordination-binding, could be the possible mechanism for metal adsorption.

Effect of pH
Adsorptions of Cr(III) and Cd(II) on MDP, TMDP, SDP and TSDP were studied for pHi range: of 2.9 to 11.1, while pH higher than that was excluded to avoid any precipitation of metal ions as hydroxide species [37]. All the metal ions are cationic in solutions, and there is a possibility of competition in adsorption between the metal ions and the proton (H + ) in the initial pH (pHi) range considered in this experiment. The adsorption capacities of Cr(III) ions were initially found to be increased and reached the maximum values of 158 mg/g and 192 mg/g at pH 7.8, while for Cd(II), it reached its highest values of 108 mg/g and 121 mg/g at pH 7.8, which was also true for MDP and TMDP, respectively. Similarly, adsorption capacities of Cr(III) were found to be increased from 56 to 132 mg/g and 86 to 193 mg/g for the pH increments of 2.9 to 6.5, while for Cd(II), the adsorption capacities were found to be maximum 94 mg/g and 148 mg/g at pH 7.8 for SDP and TSDP, respectively. The decrease in adsorption capacities was recorded for a further increase in pH ( Figure 4). The adsorption maxima for both Cr(III) and Cd(II) were observed at pH values of 7.8, which were above the point of zero charges (pHPZC) for MDP, TMDP, SDP and TSDP (Figure 4). At pH 6.3 and 6.5, the pHPZC value becomes zero for Cr(III) and Cd(II), respectively, indicating the neutral surface of the materials. Below and above this pHpzc value, the surfaces become positive and negatively charged, respectively. Both

Effect of pH
Adsorptions of Cr(III) and Cd(II) on MDP, TMDP, SDP and TSDP were studied for pH i range: of 2.9 to 11.1, while pH higher than that was excluded to avoid any precipitation of metal ions as hydroxide species [37]. All the metal ions are cationic in solutions, and there is a possibility of competition in adsorption between the metal ions and the proton (H + ) in the initial pH (pH i ) range considered in this experiment. The adsorption capacities of Cr(III) ions were initially found to be increased and reached the maximum values of 158 mg/g and 192 mg/g at pH 7.8, while for Cd(II), it reached its highest values of 108 mg/g and 121 mg/g at pH 7.8, which was also true for MDP and TMDP, respectively. Similarly, adsorption capacities of Cr(III) were found to be increased from 56 to 132 mg/g and 86 to 193 mg/g for the pH increments of 2.9 to 6.5, while for Cd(II), the adsorption capacities were found to be maximum 94 mg/g and 148 mg/g at pH 7.8 for SDP and TSDP, respectively. The decrease in adsorption capacities was recorded for a further increase in pH ( Figure 4). The adsorption maxima for both Cr(III) and Cd(II) were observed at pH values of 7.8, which were above the point of zero charges (pH PZC ) for MDP, TMDP, SDP and TSDP (Figure 4). At pH 6.3 and 6.5, the pH PZC value becomes zero for Cr(III) and Cd(II), respectively, indicating the neutral surface of the materials. Below and above this pHpzc value, the surfaces become positive and negatively charged, respectively. Both Cr(III) and Cd(II) are cationic; thus, at acidic conditions, it is possible that the surfaces of both TMDP and TSDP become excessively protonated, which inhibits the binding of metal ions on the adsorbent surfaces. The protonation decreases with the increase in pH (7.8), resulting in an increase in Cr(III) and Cd(II) binding over TMDP and TSDP. A drift in the pH graph was obtained above pH 7.8 during the study (Figure 4), suggesting the occurrences of neutralization of the adsorbents surface together with adsorption equilibrium.

Effect of Initial Concentration and Temperature
Adsorption of Cr(III) (at Co: 10, 20, 30, 40 and 50 mg/L) on as-prepared and treate dates pit adsorbents (TMDP and TSDP) were studied at temperatures range of 20 to 50 ° to determine their corresponding equilibrium isotherms and presented in Figure 5. In tially, the vertical slopes of the plots represent a rapid increase in solid-phase concentr tions of both Cr(III) and Cd(II) on the treated date pits with the increment of liquid-pha concentrations. The same trends with lower adsorption capacities were observed for th as-prepared adsorbents (MDP and SDP, not shown in the Figure). The correlation coeff cient (R 2 ) values for the graph Ce vs. qe at different temperatures were found to be in th range of 0.8686 to 0.9955 for Cr(III), while they were in the range of 0.9814 to 0.9975 f Cd(II) adsorption. The increase in their respective concentration gradients might be actin as a driving force to overcome the resistance barrier mass transfer between solution/sol phases. Finally, the slopes of the plots started to decrease and become parallel to Ce ( axis), indicating the saturation of both untreated and treated date pit adsorbent surfac with Cr(III) adsorption. The adsorption of Cr(III) and Cd(II) on both the untreated an treated date pit adsorbents were increased with temperature, confirming the endotherm adsorption process, consistent with previous studies on metal ion adsorption [38]. At 29

Effect of Initial Concentration and Temperature
Adsorption of Cr(III) (at C o : 10, 20, 30, 40 and 50 mg/L) on as-prepared and treated dates pit adsorbents (TMDP and TSDP) were studied at temperatures range of 20 to 50 • C to determine their corresponding equilibrium isotherms and presented in Figure 5. Initially, the vertical slopes of the plots represent a rapid increase in solid-phase concentrations of both Cr(III) and Cd(II) on the treated date pits with the increment of liquid-phase concentrations. The same trends with lower adsorption capacities were observed for the as-prepared adsorbents (MDP and SDP, not shown in the Figure). The correlation coefficient (R 2 ) values for the graph C e vs. q e at different temperatures were found to be in the range of 0.8686 to 0.9955 for Cr(III), while they were in the range of 0.9814 to 0.9975 for Cd(II) adsorption. The increase in their respective concentration gradients might be acting as a driving force to overcome the resistance barrier mass transfer between solution/solid phases. Finally, the slopes of the plots started to decrease and become parallel to C e (x-axis), indicating the saturation of both untreated and treated date pit adsorbent surfaces with Cr(III) adsorption. The adsorption of Cr(III) and Cd(II) on both the untreated and treated date pit adsorbents were increased with temperature, confirming the endothermic adsorption process, consistent with previous studies on metal ion adsorption [38]. At 293 K temperature, the adsorption capacities of Cr(III) and Cd(II) on TMDP were 55.3-217 and 15.3-120.0 mg/g, while on TSDP, the solid-phase concentration ranges (q e ) were 53.2-199.7 and 11.5-115.0 mg/g respectively. The regular increments in the q e values were noticed with increasing temperature. At temperatures 303, 313 and 318 K, the solid phase concentration ranges of Cr(III) on TMDP were 58.3-245.4, 59.9-269.9 and 60.1-278.9, while on TSDP the ranges of q e were 58.

Effects of Contact Time
Adsorption of Cr(III) and Cd(II) on TMDP and TSDP as a function of contact time for different concentrations of the metal ions was tested from 5 to 300 min, and Figure 6 illustrates the effects of contact time on adsorption of both the metal ions. Slow adsorption of both the metal ions was observed on TMDP and TSDP and reached an equilibrium in 300

Effects of Contact Time
Adsorption of Cr(III) and Cd(II) on TMDP and TSDP as a function of contact time for different concentrations of the metal ions was tested from 5 to 300 min, and Figure 6 illustrates the effects of contact time on adsorption of both the metal ions. Slow adsorption of both the metal ions was observed on TMDP and TSDP and reached an equilibrium in 300 min (5 h). The R 2 values for the graph of time (min) vs. Qe (mg/g) at various concentration levels were found to be in the range of 0.7644 to 0.9881 for Cr(III) and 0.8995 to 0.9477 for Cd(II) adsorption. The equilibrium adsorption capacity (Qe) for Cr(III) on TMDP was 190, 281 and 451 mg/g, while for Cd(II) ions, the Qe was 121, 211 and 371 mg/g for the concentrations of 20, 30 and 50 ppm, respectively. Similarly, the adsorption capacity (Qe) for Cr(III) on TSDP was 140, 229 and 359 mg/g, while for Cd(II) ions, the Qe was 109, 198 and 298 mg/g for the concentrations of 20, 30 and 50 ppm, respectively. Lower adsorption capacities were noticed for as-prepared materials, MDP and SDP (not shown in the Figure).

Adsorption Modeling Equilibrium Isotherm
Two-parameter analysis during the study and Langmuir and Freundlich [39] isotherm models in linear form were used.
Langmuir isotherm model in non-linearized and linearized form is expressed as where q m (mg/g) and K L (L/mg) are the constants for maximum monolayer adsorption capacity and a constant related to the heat of adsorption, respectively. Freundlich isotherm in linear and non-linear form is expressed as [39] q e = K F × C e 1/n (8) log q e = log K F + 1 n log C e (9) where K F ((mg/g) (L/mg) (1/n) ) and n are the Freundlich constants related to bonding energy and deviation in adsorption from linearity, respectively. If n = 1 (linear adsorption process), n < 1 (chemical adsorption process), n > 1 (physical adsorption process). The relevant parameters for Cr(III) and Cd(II) adsorption on TMDP and TSDP at various temperatures are shown in Table 2. Regression coefficient (R 2 ) values for Cr(III) and Cd(II) adsorption on both TMDP and TSDP at varied temperatures were comparatively higher for Langmuir isotherm model, agreeing well with previously reported results of metal ion adsorption [32,40]. In addition, the applicability of the Langmuir model hints towards a monolayer metal ions coverage over adsorbents at varied temperatures. Maximum monolayer adsorption capacity (q m ) for Cr(III) increased from 400 (400/51.99 = 7.693 mmol/g) to 1428 mg/g (1428/51.99 = 27.46 mmol/g) for TMDP and 388 mg/g (388/51.99 = 7.463 mmol/g) to 1182 mg/g (1182/51.99 = 27.735 mmol/g) for TSDP materials, while the temperature was increased from 293 K to 323 K. The maximum monolayer adsorption for Cd(II) for Cd(II) increased from 352 mg/g (352/112.4 = 3.132 mmol/g) to 1302 mg/g (1302/112.4 = 11.584 mmol/g) for TMDP and 332 (332/112.4 = 2.954 mmol/g) to 1182 mg/g (1182/112.4 = 10.516 mmol/g) for TSDP materials, with increasing temperature from 293 to 323 K. The increase in temperature may have increased the frequency of collisions between the adsorbents and Cr(III) and Cd(II), resulting in enhanced adsorption. Additionally, the rise in temperature might have ruptured the surface bonds of the materials, exposing the active site and thus enhancing metal ion adsorption. The magnitudes of the separation factor (K L ) for both Cr(III) and Cd(II) adsorption on TMDP and TSDP at the studied temperature ranges were in the range between 0 and 1, indicating a favorable adsorption process. The magnitude of K F increased with temperature, as for the intensification of metal ions and adsorbents interaction with temperature, and the n > 1 values confirm the physical adsorption process (Table 2).

021, 26, x FOR PEER REVIEW 11 of 18
298 mg/g for the concentrations of 20, 30 and 50 ppm, respectively. Lower adsorption capacities were noticed for as-prepared materials, MDP and SDP (not shown in the Figure).

Adsorption Kinetics
Pseudo-first-order [41], and pseudo-second-order [42] models in linear form were used on adsorption kinetic data, and the models in linearized forms are as follows: where, the adsorption capacities for the pseudo-first-order model and pseudo-second-order model at equilibria and at time t are denoted by q e1 , q e2 and q t , respectively, while k 1 and k 2 are the pseudo-first-order and pseudo-second-order rate constants, respectively. For Cr(III) and Cd(II) adsorption on MDP, TMDP, SDP and TSDP, the obtained kinetic parameters are shown in Table 3. Higher R 2 (closer to unity) supports pseudo-second-order kinetic model fitting to both the metal ions (II) adsorption data in all the tested adsorption systems. Similarly, the closeness of the experimental adsorption capacities (q e,exp ) to computed adsorption capacities (q e2,cal. ) validate the applicability of the aforementioned pseudo-second-order model to the data. Ghobadi et al. [43] reported similar results for La(III) and Ce(III)) adsorption on MnFe 2 O 4 -graphene nanoparticles. Table 3. Kinetic parameters for the adsorption of Cr(III) and Cd(II) on various DP adsorbents (initial concentration, C o for Cr(III) and Cd(II) was 20 mg/L).

Adsorption Thermodynamics
Thermodynamic parameters relating to Cr(III) and Cd(II) adsorption on various adsorbents, such as standard changes of entropy (∆S • ), enthalpy (∆H • ) and free energy (∆G • ), are calculated using van Hoff plots [44] and are shown in Table 4. The adsorption of Cr(III) and Cd(II) on MDP, TMDP, SDP and TSDP was endothermic, as evidenced by positive ∆H • values. The ∆S • values for Cr(III) and Cd(II) adsorption on MDP, TMDP, SDP and TSDP were all positive, indicating that the adsorption process was random as a result of energy redistribution between the metal ions and the adsorbent [45]. Furthermore, the increase in the degree of freedom of the adsorbed metal ions is confirmed by positive ∆G • values. For all types of adsorbents, the ∆G • values for both Cr(III) and Cd(II) adsorption were negative, indicating that the adsorption process was spontaneous. With increasing temperature, much higher negative ∆G • values suggest that the adsorption process tended toward spontaneity [32]. Table 4. Thermodynamic parameters for the adsorption of Cr(III) and Cd(II) on various DP adsorbents (initial concentration, C 0 for Cr(III) and Cd(II) was 20 mg/L).

Elution and Regeneration Studies
The number of eluents was used to test the Cr(III)-and Cd(II)-saturated adsorbents for elution investigations. The elution of both metal ions from all saturated adsorbents was found to be minimal (2.7-3.8%) with 0.1 mol/L NaOH; however, with 0.1 M HCl, a sufficiently higher amount of metal ions was desorbed for all adsorbents (83.0-97.2%) (Figure 7). The elution of both Cr(III) and Cd(II) with eluents followed the order: 0.1 mol/L NaOH < 0.1 mol/L CH 3 COOH < 0.1 mol/L H 2 SO 4 < 0.1 mol/L HNO 3 < 0.1 mol/L HCl. Thus, the maximum Cr(III) ions elution achieved with HCl (0.1 mol/L) were (97.2%), while it was 94.0% for Cd(II) ions. The higher desorption of both metal ions with comparatively strong acid indicated an ion-exchange process, which might govern metal ions binding on adsorbents surface. A series of batch experiments was performed to optimize the adsorbent dosage, solution pH, contact time and initial adsorbate concentrations, and the metal ions were determined using atomic adsorption spectrometry (AAS). The maximum adsorption capacity for all the metal ions was noted at pH 7.8. The obtained results were found to be best fitted with the Langmuir isotherm model, where the maximum adsorption capacities (monolayer) at 323 K were 1428.5 mg/g and 1302.0 mg/g (TMDP) and 1228.5 mg/g and 1182.0 mg/g (TSDP) for Cr(III) and Cd(II), respectively. The efficiencies of all the adsorbents-MDP, SDP, TMDP and TSDP-were compared, and it was found that for both Cr and Cd elements, the adsorption capacities of TMDP and TSDP were much higher compared to untreated materials (MDP and SDP). However, a slightly higher adsorption capacity of TMDP was noticed compared to TSDP, and the most efficiently removed metal ion was Cr(III), then Cd(II), for all the adsorbents. This could be attributed to the surface morphology and pore size of the adsorbents. The higher pore size and surface functionality of the H2O2 treated material compared to MDP and SDP were indicated by FTIR, BET, and SEM results.

Conclusions
In conclusion, optimized MDP, TMDP, SDP and TSDP exhibited excellent adsorption potential for Cr(III) and Cd(II) in their respective adsorption systems. The H2O2-treated Following the optimization of HCl (0.1 mol/L) for Cr(III) and Cd(II) from saturated MDP, TMDP, SDP and TSDP, regeneration tests were conducted to determine the reusability efficiency of the adsorbents. A drastic fall in Cr(III) (85.3-88.2%) and Cd(II) (81.8-86.8%) adsorption on MDP, TMDP, SDP and TSDP were observed after the second regeneration steps. The distortion of surface morphology during repeated adsorption and elutions of Cr(III) and Cd(II) was a probable mechanism behind a drop in metal ion adsorption. As a result, MDP, TMDP, SDP and TSDP could be effectively reutilized for Cr(III) and Cd(II) adsorption with no significant adsorption potential loss during initial regeneration.
There is inadequate research using date seed powders as adsorbents for the removal of heavy metals. Few research studies have used date stones, raw date pits and burnt date pits as potential adsorbents rather dates pit powders for the removal of heavy metals [46,47], while, an enhanced adsorption of heavy metals was reported with the burning of the date seeds. Mohamed et al. [48] reported Cu(II) adsorption using ajwa date pits powder, and the carbonized date seeds for the removal of Cu(II) from wastewater was demonstrated by others [49]. Our results for Cr(III) and Cd(II) removal using MDP, SDP, TMDP and TSDP were not significantly different from the reported findings in terms of heavy metal adsorption; only the preparation of the adsorbents was slightly different. However, in the current research, both the untreated and H2O2 treated materials showed excellent adsorption efficiency for Cr(III) and Cd(II) ions.
A series of batch experiments was performed to optimize the adsorbent dosage, solution pH, contact time and initial adsorbate concentrations, and the metal ions were determined using atomic adsorption spectrometry (AAS). The maximum adsorption capacity for all the metal ions was noted at pH 7.8. The obtained results were found to be best fitted with the Langmuir isotherm model, where the maximum adsorption capacities (monolayer) at 323 K were 1428.5 mg/g and 1302.0 mg/g (TMDP) and 1228.5 mg/g and 1182.0 mg/g (TSDP) for Cr(III) and Cd(II), respectively. The efficiencies of all the adsorbents-MDP, SDP, TMDP and TSDP-were compared, and it was found that for both Cr and Cd elements, the adsorption capacities of TMDP and TSDP were much higher compared to untreated materials (MDP and SDP). However, a slightly higher adsorption capacity of TMDP was noticed compared to TSDP, and the most efficiently removed metal ion was Cr(III), then Cd(II), for all the adsorbents. This could be attributed to the surface morphology and pore size of the adsorbents. The higher pore size and surface functionality of the H 2 O 2 treated material compared to MDP and SDP were indicated by FTIR, BET, and SEM results.

Conclusions
In conclusion, optimized MDP, TMDP, SDP and TSDP exhibited excellent adsorption potential for Cr(III) and Cd(II) in their respective adsorption systems. The H 2 O 2 -treated materials showed better adsorption capacities compared to as-prepared materials. However, better adsorptions of Cr(III) metal were noticed compared to Cd(II) in all the tested adsorbents. The obtained R 2 for C e vs. Q e graph at various temperatures was in the range of 0.8686 to 0.9975 for both Cr(III)and Cd(II) adsorption. Similarly, the R 2 for the Time (min) vs. Qe (mg/g) graph was obtained in the range of 0.7644 to 0.9881 for both metal ions at varying concentrations. The adsorptions of both metal ions on MDP, TMDP, SDP and TSDP were endothermic, and a pseudo-second-order kinetics model is better suited in all cases. Langmuir isotherm model showed slightly better results than the Freundlich model for the untreated and treated date pits, indicating monolayer coverage. Elution experiments showed maximum Cr(III) and Cd(II) recovery with 0.1 mol/L HCl. The obtained adsorption and regeneration results indicate that the synthesized adsorbent materials could be useful for the adsorption of heavy metals from the aqueous system. Institutional Review Board Statement: Not applicable.

Informed Consent Statement: Not applicable.
Data Availability Statement: The study did not report any data.