Preparation of Microspheres and Monolithic Microporous Carbons from the Pyrolysis of Template-Free Hyper-Crosslinked Oligosaccharides Polymer

Carbon-based materials with different morphologies have special properties suitable for application in adsorption, catalysis, energy storage, and so on. Carbon spheres and carbon monoliths are also nanostructured materials showing promising results. However, the preparation of these materials often require the use of a template, which aggravates their costs, making the operations for their removal complex. In this work, hollow carbon microspheres and carbon monolith were successfully prepared via carbonization of hyper-crosslinked polymer based on either cyclodextrins or amylose, in a template-free way. The carbons obtained are of the microporous type, showing a surface area up to 610 m2/g, and a narrow pore distribution, typically between 5 and 15 Å.


Introduction
Thanks to the ability of carbon to take on different configurations, it has been possible to obtain a wide range of materials with an immensely different variety of structures and morphologies. Carbon materials, in particular porous ones, are generally characterized by their physical characteristics, which allow them to be used in many applications [1], such as food processing [2], chemical and pharma fields [3], petroleum industries [4] in water/air treatment [5], catalysis support [6], and fuel cell [7]. The possibility to use them in this wide range of applications certainly depends on their specific surface areas and porosity, but also on the ability to take the shape required for each specific application. For this reason, porous carbon materials are industrially and conventionally classified in three categories, based on their size and shape: granular carbons, irregular shaped carbons with size ranging from 0.2 to 5 mm [8]; powder carbons, pulverized shaped particles with a predominantly size less than 0.18 mm [9], and carbon fibers [10]. Each type of above-mentioned carbon finds its specific application. For instance, granular carbons are used in liquid and gas phase processes [11]; powder carbons are mainly applied in flue gas treatment [12], and carbon fibers in equipment such as electrodes for electrochemical super-capacitors, hydrogen storage, catalyst support, and so on [13]. Thus, the selection of a proper shape for a specific industrial usage is very important.
Novel carbon structures with specific properties, such as fullerene and carbon nanotubes have been remarkably studied, and their discovery resulted in nanoscience and nanotechnology developments [3].

Preparation of Carbons
Microsphere preparation: 2 g of βNS or LcNS are put in an alumina combustion boat and then pyrolyzed using a Lenton 1200 tubular furnace. Samples are pyrolyzed with a heating ramp of 10 • C min −1 until 800 • C and kept in isotherm for 20 min under a nitrogen flux (65 mL min −1 ). The samples are than cooled to room temperature under nitrogen flux.
Monolith Preparation. The βCD based NS were synthetized dissolving 6.12 g of anhydrous βCD were dissolved in 20 mL of DMSO. After the complete dissolution, 4.50 mL of TEA was added as catalyst. Few minutes later, 4.72 g of pyromellitic dianhydride were mixed and allowed to react at room temperature overnight. Once the reaction was concluded, the block polymer was pulled out. A Soxhlet extractor with acetone was used for the purification. Then the whole block is subjected to the pyrolysis process in the same condition used for the preparation of microsphere. For the LcNS, in a typical procedure, 4.89 g of Lc was solubilized in 20 mL of DMSO in a bottom-rounded flask. Moreover, 3.50 mL of TEA was added and then the 3.76 g of PMDA. After few minutes the cross-linking reaction occurred, and the NS is left to react overnight in order to be considered competed. The LcNS was pulled out and eventually purified in a Soxhlet extractor with acetone for 24 h. The block is then pyrolyzed in a tubular furnace in the same condition used for the preparation of microsphere.

Characterization
Attenuated Total Reflection (ATR) (Perkin-Elmer Spectrum 100) was used for collecting 16 scans for each spectrum of the nanosponges before and after the thermal treatment in the range 4000-650 cm −1 at 4 cm −1 resolution.
Scanning Electron Microscopy (SEM) (Leica Stereoscan 410) was applied to investigate the nanosponges and the carbons morphology. All of the samples were coated with gold by a sputter coater (Baltec SCD 050) for 60 s under vacuum at a current intensity of 40 mA.
Thermal behavior and stability of the nanosponges were studied by thermogravimetric analysis (TGA) (TGA 2950 balance TA Inc.). Moreover, 15 mg of sample were placed in an alumina crucible and heated to 800 • C with a ramp temperature of 10 • C·min −1 under nitrogen flux.
The carbons were characterized by nitrogen adsorption-desorption isotherms at 77 K obtained with an automatic gas-volumetric instrument (ASAP 2010, Micromeritics). The samples were outgassed at 300 • C overnight and analyzed using nitrogen at 77 K. The Langmuir model was applied to evaluate the specific surface area, whereas for the determination of the quantity and dimension of pores, density functional theory (DFT) model were used.
The samples elemental composition was studied using a Thermo Fisher FlashEA 1112 Series elemental analyzer.

Results and Discussion
The βNS and the LcNS are synthesized with the method previously described. The synthesis of both the samples leads to the formation of a solid block that can be ground before being purified in Soxhlet. In our previous works [28,29], it has been reported that from pyrolysis of powdered nanosponges it is possible to obtain microporous carbons with spherical morphology. In order to control the dimension and the formation of carbon sphere, the nanosponges were ground and sieved in four parts with different particle sizes: higher than 100 µm, between 100 and 71 µm, between 71 and 40 µm, and less than 40 µm. These four portions were pyrolyzed in a tubular furnace at 800 • C in inert atmosphere. Figure 1 shows the micrograph collected for the carbons from βNS (C-βNS) and Figure 2 depicts the carbons from Lc-NS (C-LcNS) derived from the different granulometric fractions of βNS and LcNS, respectively. For comparison, the several batches of sieved nanosponges are also reported in Figure 1 and in Figure 2 in order to confirm the granulometric separation and to study the dependence of the spherical shape on the initial particle size.
Regarding the bare βNS (Figure 1a-d), it can be observed that all the particles showed an irregular polyhedral morphology, mainly due to the grinding process, but the dimensional separation successfully occurred. The carbon from βNS ( Figure 1, panel e) displays the ability to produce a spherical morphology for NS particles bigger than 100 µm. Reducing the size of the starting particles (71-100 µm-panel f), the morphology of the carbon particles became more irregular, but the spherical morphology is still predominant. Referring to panel g, which shows the carbons form NS grounded between 71 and 40 µm, it can be notice that the spherical shape has almost disappeared, but there are still some spheres. The sphere morphology disappears pyrolyzing the βNS below 40 µm (Figure 1, panel h).
Molecules 2020, 25, x FOR PEER REVIEW 4 of 12 Figure 2 depicts the carbons from Lc-NS (C-LcNS) derived from the different granulometric fractions of βNS and LcNS, respectively. For comparison, the several batches of sieved nanosponges are also reported in Figure 1 and in Figure 2 in order to confirm the granulometric separation and to study the dependence of the spherical shape on the initial particle size.  Regarding the bare βNS ( Figure 1,a,b,c,d), it can be observed that all the particles showed an irregular polyhedral morphology, mainly due to the grinding process, but the dimensional separation successfully occurred. The carbon from βNS ( Figure 1, panel e) displays the ability to produce a spherical morphology for NS particles bigger than 100 μm. Reducing the size of the starting particles (71-100 μm-panel f), the morphology of the carbon particles became more irregular, but the spherical morphology is still predominant. Referring to panel g, which shows the carbons form NS grounded between 71 and 40 μm, it can be notice that the spherical shape has almost disappeared, but there are still some spheres. The sphere morphology disappears pyrolyzing the βNS below 40 μm ( Figure 1, panel h).
In Figure 2 are reported the SEM image of the NS obtained from Line Caps and the respective carbon particles. The bare LcNS (Figure 2,a,b,c,d) shows particles with polyhedral morphology, but the dimensional separation successfully occurred. As seen for the carbons from βNS, a spherical morphology has been obtained starting form LcNS with particle size wider than 100 μm (panel e). Decreasing the dimension of the particles (71-100 μm-panel f), the morphology of the sample remains mainly spherical. Further decreasing the particles size (40-71 μm-panel g), the presence of spherical shape begins to be no longer the predominant one and it disappears for the carbon from LcNS with particle size of 40 μm (panel h). Thus, the influence of the granulometry on the morphology of the resultant carbons is related with the size of the starting materials. The spheres are obtained when a nanosponge, with size up to 71 μm, is pyrolyzed, and disappears when NS with dimension inferior to 40 μm are used. To see the inner part of the spheres, some of them were broken, and are shown in Figure 3. As can be seen, the spheres are hollow and formed of a carbon shell, whose thickness seems to remain constant despite the variation of the size of the starting precursor particle. In Figure 2 are reported the SEM image of the NS obtained from Line Caps and the respective carbon particles. The bare LcNS (Figure 2a-d) shows particles with polyhedral morphology, but the dimensional separation successfully occurred. As seen for the carbons from βNS, a spherical morphology has been obtained starting form LcNS with particle size wider than 100 µm (panel e). Decreasing the dimension of the particles (71-100 µm-panel f), the morphology of the sample remains mainly spherical. Further decreasing the particles size (40-71 µm-panel g), the presence of spherical shape begins to be no longer the predominant one and it disappears for the carbon from LcNS with particle size of 40 µm (panel h). Thus, the influence of the granulometry on the morphology of the resultant carbons is related with the size of the starting materials. The spheres are obtained when a nanosponge, with size up to 71 µm, is pyrolyzed, and disappears when NS with dimension inferior to 40 µm are used. To see the inner part of the spheres, some of them were broken, and are shown in Figure 3. As can be seen, the spheres are hollow and formed of a carbon shell, whose thickness seems to remain constant despite the variation of the size of the starting precursor particle.
Molecules 2020, 25, x FOR PEER REVIEW 6 of 12 The formation of this morphology can be related with the degradation pathway followed by the hyper-crosslinked polymer during the pyrolysis. During the heat treatment, the nanosponge softens passing through a fluid phase while pyrolysis is taking place. The surface tension of the fluids leads to the formation of spherical particles. Due to the temperature gradient between the outside and inside of the spheres, the carbonization begins on the surface, this causes the formation of a solid carbon shell, while the carbonization continues from the outside towards the inside of the still fluid particle. The particle should be reduced in size since the pyrolysis process causes the volatilization of at least the 60% by weight of the polymer, but this is not possible since the outer shell is solidified. The volume reduction then occurs at the expense of the still fluid internal mass, which withdraws towards the area already carbonized, leaving a vacuum inside the particle. Figure 4 shows a scheme of this process. The carbon shell reaches a thickness of about 3 μm, meaning that there is a limit for the formation of particles with spherical shape. Precursor particles smaller than 40 μm do not allow the creation of a temperature gradient enough to allow this mechanism and below this value; the thickness of the surface coincides with the overall dimension of the particles not allowing to assume the spherical morphology, and so it remains with the same shape of the starting materials. The formation of this morphology can be related with the degradation pathway followed by the hyper-crosslinked polymer during the pyrolysis.
During the heat treatment, the nanosponge softens passing through a fluid phase while pyrolysis is taking place. The surface tension of the fluids leads to the formation of spherical particles. Due to the temperature gradient between the outside and inside of the spheres, the carbonization begins on the surface, this causes the formation of a solid carbon shell, while the carbonization continues from the outside towards the inside of the still fluid particle. The particle should be reduced in size since the pyrolysis process causes the volatilization of at least the 60% by weight of the polymer, but this is not possible since the outer shell is solidified. The volume reduction then occurs at the expense of the still fluid internal mass, which withdraws towards the area already carbonized, leaving a vacuum inside the particle. Figure 4 shows a scheme of this process. The carbon shell reaches a thickness of about 3 µm, meaning that there is a limit for the formation of particles with spherical shape. Precursor particles smaller than 40 µm do not allow the creation of a temperature gradient enough to allow this mechanism and below this value; the thickness of the surface coincides with the overall dimension of the particles not allowing to assume the spherical morphology, and so it remains with the same shape of the starting materials.
The samples of C-βNS and C-LcNS were analyzed with the ASAP 2010 to evaluate their physical properties. The objective of this measure is to the determinate the dependence between the granulometry of the NS and the development of the specific surface area of the resulting carbons. In Figure 5, all of the collected isotherms for C-βNS (a) and C-LCNS (b) are reported, and all of the results are listed in Tables 1 and 2. Figure 4 shows a scheme of this process. The carbon shell reaches a thickness of about 3 μm, meaning that there is a limit for the formation of particles with spherical shape. Precursor particles smaller than 40 μm do not allow the creation of a temperature gradient enough to allow this mechanism and below this value; the thickness of the surface coincides with the overall dimension of the particles not allowing to assume the spherical morphology, and so it remains with the same shape of the starting materials.  The samples of C-βNS and C-LcNS were analyzed with the ASAP 2010 to evaluate their physical properties. The objective of this measure is to the determinate the dependence between the granulometry of the NS and the development of the specific surface area of the resulting carbons. In Figure 5, all of the collected isotherms for C-βNS (a) and C-LCNS (b) are reported, and all of the results are listed in Table 1 and Table 2.  Table 1. Specific surface area, cumulative pore volume and pore width of the C-βNS.

Sample
Specific Surface Area (m 2 /g) Cumulative Pore Volume (cm 3 Table 2. Specific surface area, cumulative pore volume and pore width of the C-LcNS. The trend of the adsorption-desorption isotherms shows that the pyrolysis generates microporous carbons. No capillary condensation phenomena can be observed. Indeed, isotherms recorded are in accordance with Type I isotherm and, following the International Union of Pure and Applied Chemistry (IUPAC) classification, characteristic of microporous samples. The Type 1 isotherm can be described by the Langmuir equation, which was developed assuming the homogeneity and mono-layered adsorption on the surface. From the results listed in Table 1, it can be seen that the specific surface area of the spheres from C-βNS is around 550 m 2 /g and the porosity and the dimension of pores is the same for all the samples having dimensions less than 100 μm. For the C-βCD with dimensions higher than 100 μm, the recorded area is lower than for the other carbons, around 7 m 2 /g. Therefore, below 100 μm, the granulometry of the βNS has no influence on the specific surface area, and in the resulting porosity of the final carbons. Regarding the carbons from LcNS, when the size of the NS decreases, there is a progressive development of the specific surface area. It  Table 1. Specific surface area, cumulative pore volume and pore width of the C-βNS.

Sample
Specific Surface Area (m 2 /g) Cumulative Pore Volume (cm 3 Table 2. Specific surface area, cumulative pore volume and pore width of the C-LcNS.

Sample
Specific Surface Area (m 2 /g) Cumulative Pore Volume (cm 3  The trend of the adsorption-desorption isotherms shows that the pyrolysis generates microporous carbons. No capillary condensation phenomena can be observed. Indeed, isotherms recorded are in accordance with Type I isotherm and, following the International Union of Pure and Applied Chemistry (IUPAC) classification, characteristic of microporous samples. The Type 1 isotherm can be described by the Langmuir equation, which was developed assuming the homogeneity and mono-layered adsorption on the surface. From the results listed in Table 1, it can be seen that the specific surface area of the spheres from C-βNS is around 550 m 2 /g and the porosity and the dimension of pores is the same for all the samples having dimensions less than 100 µm. For the C-βCD with dimensions higher than 100 µm, the recorded area is lower than for the other carbons, around 7 m 2 /g. Therefore, below 100 µm, the granulometry of the βNS has no influence on the specific surface area, and in the resulting porosity of the final carbons. Regarding the carbons from LcNS, when the size of the NS decreases, there is a progressive development of the specific surface area. It passes from 93 m 2 /g for the C-LcNS with dimension higher than 100 µm, to 573 m 2 /g for the carbon from LcNS sieved below 40 µm. The volume of pores also increases as the size of the particles are reduced, whereas their width remains constant. Therefore, for LcNS there is a strong dependence of the granulometry of the starting materials on the physical characteristics of the resulting carbons. The effect of particle size is a complex phenomenon and it is often associated with change in physical properties of samples. It is possible to suppose that the different structure of the native βNS and LcNS have an influence on reorganization reactions that contribute to the specific surface area. Indeed, the building block of the βNS are the β-cyclodextrins that are cyclic oligosaccharides composed by seven glucopyranose units linked by α- (1-4) bonds. The building block of the LcNS are the Linecaps. Similarly to the cyclodextrins, they are a starch derivative, and they are polymeric carbohydrates consisting in anhydroglucose units linked together primarily through α-(1-4)-glucosidic bonds, but they contains two microstructures. The first is amylose, a linear structure of α-1,4 linked glucose units. The second is the amylopectin, a high branched structure composed of short α-1,4 chains linked by α-1,6 bonds. The Linecaps have a helical design with an outer hydrophilic surface, whereas the inner surface is hydrophobic. This different structure of the bare samples could be responsible of the reorganization reactions that occur during the pyrolysis and lead to a diverse evolution of the specific surface area.
Having found out that it is possible to modulate the specific surface area and the morphology of the resulting carbon from βNS and LcNS, tuning the dimension of the particles, the possibility to obtain monolithic carbons was explored. After the cross-linking reaction between the βCD or Lc with the pyromellitic dianhydride, the products obtained are solid blocks (see Supplementary Materials). A part of the two blocks of βNS and LcNS was pyrolyzed in a tubular furnace to obtain carbons with the same morphology of the starting materials. Figure 6 shows a piece of βNS before and after the pyrolysis. Similarly to the cyclodextrins, they are a starch derivative, and they are polymeric carbohydrates consisting in anhydroglucose units linked together primarily through α-(1-4)-glucosidic bonds, but they contains two microstructures. The first is amylose, a linear structure of α-1,4 linked glucose units. The second is the amylopectin, a high branched structure composed of short α-1,4 chains linked by α-1,6 bonds. The Linecaps have a helical design with an outer hydrophilic surface, whereas the inner surface is hydrophobic. This different structure of the bare samples could be responsible of the reorganization reactions that occur during the pyrolysis and lead to a diverse evolution of the specific surface area.
Having found out that it is possible to modulate the specific surface area and the morphology of the resulting carbon from βNS and LcNS, tuning the dimension of the particles, the possibility to obtain monolithic carbons was explored. After the cross-linking reaction between the βCD or Lc with the pyromellitic dianhydride, the products obtained are solid blocks (see Supplementary Materials). A part of the two blocks of βNS and LcNS was pyrolyzed in a tubular furnace to obtain carbons with the same morphology of the starting materials. Figure 6 shows a piece of βNS before and after the pyrolysis. As shown in the Figure 6, the shape of the nanosponge remains unchanged after the pyrolysis process. Thus, it suggests that it is possible to make carbon with different dimensions and shapes.
As a first step, the possibility to obtain monolithic carbons by direct pyrolysis of the whole block of NS was evaluated, without any further purification usually performed after the synthesis. The NS blocks were analyzed using TGA; the thermograms of βNS, LcNS, and of the respective powdered and purified nanosponges are reported in Figure 7. As shown in the Figure 6, the shape of the nanosponge remains unchanged after the pyrolysis process. Thus, it suggests that it is possible to make carbon with different dimensions and shapes.
As a first step, the possibility to obtain monolithic carbons by direct pyrolysis of the whole block of NS was evaluated, without any further purification usually performed after the synthesis. The NS blocks were analyzed using TGA; the thermograms of βNS, LcNS, and of the respective powdered and purified nanosponges are reported in Figure 7.
The thermograms of the βNS (a) shows three steps of weight loss, which occur at the same temperature. The thermal degradation of the βNS purified (solid black line Figure 7a) has a first step of weight loss that occurs before 180 • C with a 7% of weight loss which is related with the moisture adsorbed by the sample. A second step takes place between 220 • C and 350 • C with a 42% of weight loss. The last one goes from 350 • C to 800 • C losing a 14% of its mass. The carbon yield of the pyrolysis is 28%. The thermogram of βNS not purified shows a first step of weight loss until 180 • C, which causes a 51% of weight loss. During this phase, it is possible to suppose that the volatiles released at this temperature are either water adsorbed, but also by-products and solvent (DMSO). Indeed, taking as 100% the weight of the sample at 180 • C, the char yield at 800 • C is 28% as the pyrolysis yield of the βNS purified. Figure 6. Portion of βNS before and after the pyrolysis.
As shown in the Figure 6, the shape of the nanosponge remains unchanged after the pyrolysis process. Thus, it suggests that it is possible to make carbon with different dimensions and shapes.
As a first step, the possibility to obtain monolithic carbons by direct pyrolysis of the whole block of NS was evaluated, without any further purification usually performed after the synthesis. The NS blocks were analyzed using TGA; the thermograms of βNS, LcNS, and of the respective powdered and purified nanosponges are reported in Figure 7. The thermogram of the LcNS purified (solid black line, Figure 7b) show three steps of weight loss as the βNS. The first one occurs before 180 • C; it belongs to the evaporation of the moisture and it corresponds to 5%. The second step goes from 160 • C to 310 • C with a 51% of weight loss. The last stage takes place between 310 • C and 600 • C. The pyrolysis yield in this case is 32%. As for the βNS, it is possible to see that the LcNS not purified (dotted grey line, Figure 7b) shows an initial weight loss of solvent and other by-products before 180 • C.
The presence of DMSO in the monoliths is confirmed by the CHNS analysis (Table 3). In the case of non-purified NS, a huge amount of sulfur, around 20 wt. %, is still present. The physical properties of the not purified NS are listed in Table 4. As can be seen, the monolithic carbon obtained from βNS has a low specific surface area and porosity, while in the case of that obtained from LcNS it was not possible to detect the specific surface area. Table 4. Specific surface area, cumulative pore volume, and pore width of the C-βNS C-LcNS with no purification after the synthesis.

Sample
Specific Surface Area (m 2 /g) Cumulative Pore Volume (cm 3 /g) Pore Width (Å) C-βNS monolith 138 0.010 13-17 C-LcNS monolith / / / In order to improve the physical characteristic of the monolithic carbons, the solid blocks obtained after the synthesis of βNS and LcNS were purified in Soxhlet with acetone. The trend of purification was checked with CHNS analysis. The results are reported in Table 5. The target of the purification is the elimination the residual DMSO and it is possible to see that 18 h of Soxhlet extraction are not enough to completely remove the solvent. The complete elimination of the DMSO was reached after 27 h of Soxhlet extraction. This is confirmed by TGA (Figure 8) where the thermograms of the βNS and LcNS block and βNS and LcNS crushed are perfectly overlapped; hence, the purification step worked successfully. The monolithic NS were then pyrolyzed and the respective monolithic carbons were analyzed for checking the specific surface area and the porosity. All of the data recorded are summarized in Table 6.
Molecules 2020, 25, x FOR PEER REVIEW 10 of 12 The target of the purification is the elimination the residual DMSO and it is possible to see that 18 h of Soxhlet extraction are not enough to completely remove the solvent. The complete elimination of the DMSO was reached after 27 h of Soxhlet extraction. This is confirmed by TGA (Figure 8) where the thermograms of the βNS and LcNS block and βNS and LcNS crushed are perfectly overlapped; hence, the purification step worked successfully. The monolithic NS were then pyrolyzed and the respective monolithic carbons were analyzed for checking the specific surface area and the porosity. All of the data recorded are summarized in Table  6.  Table 6. Specific surface area, cumulative pore volume, and pore width of the C-βNS.

Conclusions
In the present work, hollow carbon microspheres and carbon monolith were successfully prepared via carbonization of hyper-crosslinked polymer based on either cyclodextrins or amylose in a template-free way. In particular, it is possible to obtain microporous carbon monoliths by simply pyrolyzing the nanosponge blocks after the hyper-crosslinked polymer synthesis. The purification steps seem to play an important role in the development of the surface area, up to 610 m 2 /g. Moreover, grinding the nanosponges, it is possible to have carbon microspheres with high specific surface area and a narrow pore size distribution. The possibility to tailor the shape of the carbons makes the nanosponge a suitable precursor for different industrial applications.
Supplementary Materials: The following are available online at www.mdpi.com/xxx/s1, Figure S1: FT-IR Spectra of βNS monolith before and after 18 and 27 h of extraction, Figure S2: FT-IR Spectra of LcNS monolith before and after 18 and 27 h of extraction, Figure S3: a) carbon from a-CD-NS 100 ×; b) the inner part of a-CD-NS carbon 500 ×; c) carbon from g-CD-NS 100 ×; d) the inner part of g-CD-NS carbon 500 ×, Figure S4: SEM image of the carbons form b-CD cross-linked with the pyromellitic dianhydride in molar ratio 1:2.  Table 6. Specific surface area, cumulative pore volume, and pore width of the C-βNS.

Conclusions
In the present work, hollow carbon microspheres and carbon monolith were successfully prepared via carbonization of hyper-crosslinked polymer based on either cyclodextrins or amylose in a template-free way. In particular, it is possible to obtain microporous carbon monoliths by simply pyrolyzing the nanosponge blocks after the hyper-crosslinked polymer synthesis. The purification steps seem to play an important role in the development of the surface area, up to 610 m 2 /g. Moreover, grinding the nanosponges, it is possible to have carbon microspheres with high specific surface area and a narrow pore size distribution. The possibility to tailor the shape of the carbons makes the nanosponge a suitable precursor for different industrial applications.

Supplementary Materials:
The following are available online at http://www.mdpi.com/1420-3049/25/13/3034/s1, Figure S1: FT-IR Spectra of βNS monolith before and after 18 and 27 h of extraction, Figure S2: FT-IR Spectra of LcNS monolith before and after 18 and 27 h of extraction, Figure S3: a) carbon from a-CD-NS 100 ×; b) the inner part of a-CD-NS carbon 500 ×; c) carbon from g-CD-NS 100 ×; d) the inner part of g-CD-NS carbon 500 ×, Figure  S4: SEM image of the carbons form b-CD cross-linked with the pyromellitic dianhydride in molar ratio 1:2.
Author Contributions: All authors contributed equally to this work. All authors have read and agreed to the published version of the manuscript.