Efficient Synthesis of Furfural from Biomass Using SnCl4 as Catalyst in Ionic Liquid

Furfural is a versatile platform molecule for the synthesis of various chemicals and fuels, and it can be produced by acid-catalyzed dehydration of xylose derived from renewable biomass resources. A series of metal salts and ionic liquids were investigated to obtain the best combination of catalyst and solvent for the conversion of xylose into furfural. A furfural yield of 71.1% was obtained at high xylose loading (20 wt%) from the single-phasic reaction system whereby SnCl4 was used as catalyst and ionic liquid 1-ethyl-3-methylimidazolium bromide (EMIMBr) was used as reaction medium. Moreover, the combined catalyst consisting of 5 mol% SnCl4 and 5 mol% MgCl2 also produced a high furfural yield (68.8%), which was comparable to the furfural yield obtained with 10 mol% SnCl4. The water–organic solvent biphasic systems could improve the furfural yield compared with the single aqueous phase. Although these organic solvents could form biphasic systems with ionic liquid EMIMBr, the furfural yield decreased remarkably compared with the single EMIMBr phase. Besides, the EMIMBr/SnCl4 system with appropriate water was also efficient to convert xylan and lignocellulosic biomass corn stalk into furfural, obtaining furfural yields as high as 57.3% and 54.5%, respectively.


Introduction
With the depletion of fossil energy and the deterioration of ecological environments, modern society needs to develop economical, energy-efficient, and environmentally friendly processes to achieve sustainable production of fuels and chemicals [1]. In recent years, considerable attention has been paid to utilizing renewable biomass resources to produce value-added chemicals to relieve the resource and energy crisis [2][3][4]. Both chemical catalysis and biotechnology have been proposed to depolymerize cellulose and hemicellulose into C 5 -C 6 sugar monomers, such as glucose, xylose, and arabinose [5][6][7]. C 6 and C 5 sugar can be further transformed into 5-hydroxymethylfurfural (HMF) and furfural by chemical catalysis routes, respectively [8,9]. Both HMF and furfural could be used as starting materials for the synthesis of important furan derivatives. However, the commercial application of HMF is still not realized due to the high cost of HMF production [10][11][12][13]. In contrast, the large-scale production and commercial application of furfural have already been achieved. Moreover, the important furfural derivatives, such as furfural alcohol, tetrahydrofurfuryl alcohol, furan, tetrahydrofuran (THF), dihydropyran, acetylfuran, furanamine, and furan acid have showed great potential in industry [14][15][16][17]. Among these chemicals, furfural alcohol accounts for 62% of the global furfural market. Furfural can also be converted into green fuels such as methyl furan, methyl tetrahydrofuran, valerate, ethyl furan, and ethyltetrahydro furan ethers [18,19]. The concentration of the acidic species in the reaction medium was determined by the catalyst dosage [45,46]. Consequently, the catalyst dosage had a remarkable effect on the dehydration of xylose into furfural. Figure 2 shows the effect of catalyst dosage on the dehydration of xylose into furfural. When the catalyst dosage increased from 5 mol% to 10 mol%, the furfural yield increased from 52.4% to 71.1%. As the catalyst dosage further increased, the furfural yield gradually decreased. Excessive catalyst not only accelerated the formation of furfural from xylose but also promoted the side reactions, thus leading to the reduced furfural yield [14]. The concentration of the acidic species in the reaction medium was determined by the catalyst dosage [45,46]. Consequently, the catalyst dosage had a remarkable effect on the dehydration of xylose into furfural. Figure 2 shows the effect of catalyst dosage on the dehydration of xylose into furfural. When the catalyst dosage increased from 5 mol% to 10 mol%, the furfural yield increased from 52.4% to 71.1%. As the catalyst dosage further increased, the furfural yield gradually decreased. Excessive catalyst not only accelerated the formation of furfural from xylose but also promoted the side reactions, thus leading to the reduced furfural yield [14].
It has been reported that the combined use of two metal chlorides may improve furfural yield in 1-ethyl-3-methyl-imidazolium chloride (EMIMCl) or a water-organic solvent system [24,47]. For example, Zhang et al. found that the furfural yield from corncob catalyzed by combined catalysts CrCl 3 /AlCl 3 was higher than single CrCl 3 or single AlCl 3 [24]. The effect of the combination of SnCl 4 and another chloride as paired catalysts on the yield of furfural was investigated by Wang et al [47]. They found that the combination of SnCl 4 with monovalent chlorides, such as LiCl, KCl, and NaCl, could improve the furfural yield. Among these monovalent chlorides, LiCl had the best promotion effect. Moreover, similar results were obtained for the preparation of HMF. Su et al. found that a pair of metal chlorides (CuCl 2 and CrCl 2 ) as catalyst was more conducive for the conversion of cellulose into HMF than the single metal chloride [48]. Therefore, paired catalysts were tested for production of furfural from xylose in ionic liquid EMIMBr. As shown in Figure 3, we chose nine kinds of metal chlorides to pair with SnCl 4 as catalyst, but the furfural yields from these paired catalysts were all lower than that from SnCl 4 . When FeCl 3 , AlCl 3 , CuCl 2 , and CrCl 3 were used as co-catalyst, the yield was extremely low (10-20%), and there was a large number of insoluble humins generated during the reaction. In contrast, a furfural yield of more than 60% was obtained by mixing SnCl 4 and other metal chlorides, which possess weak catalytic activity (MgCl 2 , FeCl 2 ) or hardly no catalytic activity (NaCl, LiCl). Although the furfural yield was not improved by the co-catalyst when the total loading of SnCl 4 and metal chloride was kept at 10 mol%, the furfural yields (69.8% and 68.7%, respectively.) obtained with SnCl 4 /MgCl 2 and SnCl 4 /FeCl 2 were almost comparable to that obtained with single SnCl 4 . It has been reported that the combined use of two metal chlorides may improve furfural yield in 1-ethyl-3-methyl-imidazolium chloride (EMIMCl) or a water-organic solvent system [24,47]. For example, Zhang et al. found that the furfural yield from corncob catalyzed by combined catalysts CrCl3/AlCl3 was higher than single CrCl3 or single AlCl3 [24]. The effect of the combination of SnCl4 and another chloride as paired catalysts on the yield of furfural was investigated by Wang et al [47]. They found that the combination of SnCl4 with monovalent chlorides, such as LiCl, KCl, and NaCl, could improve the furfural yield. Among these monovalent chlorides, LiCl had the best promotion effect. Moreover, similar results were obtained for the preparation of HMF. Su et al. found that a pair of metal chlorides (CuCl2 and CrCl2) as catalyst was more conducive for the conversion of cellulose into HMF than the single metal chloride [48]. Therefore, paired catalysts were tested for production of furfural from xylose in ionic liquid EMIMBr. As shown in Figure 3, we chose nine kinds of metal chlorides to pair with SnCl4 as catalyst, but the furfural yields from these paired catalysts were all lower than that from SnCl4. When FeCl3, AlCl3, CuCl2, and CrCl3 were used as co-catalyst, the yield was extremely low (10-20%), and there was a large number of insoluble humins generated during the reaction. In contrast, a furfural yield of more than 60% was obtained by mixing SnCl4 and other metal chlorides, which possess weak catalytic activity (MgCl2, FeCl2) or hardly no catalytic activity (NaCl, LiCl). Although the furfural yield was not improved by the co-catalyst when the total loading of SnCl4 and metal chloride was kept at 10 mol%, the furfural yields (69.8% and 68.7%, respectively.) obtained with SnCl4/MgCl2 and SnCl4/FeCl2 were almost comparable to that obtained with single SnCl4.
Subsequently, we investigated the effect of different dosages of SnCl4 and MgCl2 on the dehydration of xylose into furfural. As show in Table 1, an extremely low furfural yield of 4.5% was obtained using single MgCl2 as catalyst (Entry 6). The furfural yield was 62.0% when 8 mol% SnCl4 was used as catalyst. In contrast, when 2 mol% MgCl2 was added to the reaction system, the furfural yield increased by 12.6% in comparison with the single 8 mol% SnCl4. When 5 mol% MgCl2 was combined with 5 mol% SnCl4 as catalyst, the furfural yield was still as high as 68.8%, which was 31.2% higher than that obtained with 5 mol% SnCl4 and comparable to that obtained with 10 mol% SnCl4. These results showed that MgCl2 could improve the catalytic activity of EMIMBr/SnCl4 when relative low loading of SnCl4 was used. Since magnesium salt was cheaper and safer than tin salts, it was more economical to use the SnCl4/MgCl2 as catalyst instead of single SnCl4. Although several studies have reported that the use of paired catalysts can improve the furfural yield, detailed mechanisms involving the coordination of paired catalysts have not been well studied. We observed that fewer humins were produced in the reaction system with paired catalysts consisting of 5 mol% SnCl4 and 5 mol% MgCl2 than that with single 10 mol% SnCl4. The presence of a higher quantity of Sn 4+ provided abundant Lewis acidity for the isomerization of xylose to xylulose while encouraging the polymerization of furfural with undesired side products [49]. Caes et al. have shown that MgCl2 could promote the conversion of sugars into HMF catalyzed by ortho-carboxyl-substituted phenylboronic acids [50]. Similarly, García-Sancho et al. found that the presence of CaCl2 in a biphasic water-methyl isobutyl ketone (MIBK) system with γ-Al2O3 as catalyst notably improved the catalytic performance [51]. They proposed that the interaction between Ca 2+ and glucose molecules favors the formation of α-d-glucopyranose, thus enhancing glucose conversion to HMF. Likewise, it was inferred that the similar interaction between Mg 2+ and xylose molecules may have promoted the conversion of xylose to furfural, and then MgCl2 and SnCl4 contributed cooperatively to the dehydration process.   Subsequently, we investigated the effect of different dosages of SnCl 4 and MgCl 2 on the dehydration of xylose into furfural. As show in Table 1, an extremely low furfural yield of 4.5% was obtained using single MgCl 2 as catalyst (Entry 6). The furfural yield was 62.0% when 8 mol% SnCl 4 was used as catalyst. In contrast, when 2 mol% MgCl 2 was added to the reaction system, the furfural yield increased by 12.6% in comparison with the single 8 mol% SnCl 4 . When 5 mol% MgCl 2 was combined with 5 mol% SnCl 4 as catalyst, the furfural yield was still as high as 68.8%, which was 31.2% higher than that obtained with 5 mol% SnCl 4 and comparable to that obtained with 10 mol% SnCl 4 . These results showed that MgCl 2 could improve the catalytic activity of EMIMBr/SnCl 4 when relative low loading of SnCl 4 was used. Since magnesium salt was cheaper and safer than tin salts, it was more economical to use the SnCl 4 /MgCl 2 as catalyst instead of single SnCl 4 . Although several studies have reported that the use of paired catalysts can improve the furfural yield, detailed mechanisms involving the coordination of paired catalysts have not been well studied. We observed that fewer humins were produced in the reaction system with paired catalysts consisting of 5 mol% SnCl 4 and 5 mol% MgCl 2 than that with single 10 mol% SnCl 4 . The presence of a higher quantity of Sn 4+ provided abundant Lewis acidity for the isomerization of xylose to xylulose while encouraging the polymerization of furfural with undesired side products [49]. Caes et al. have shown that MgCl 2 could promote the conversion of sugars into HMF catalyzed by ortho-carboxyl-substituted phenylboronic acids [50]. Similarly, García-Sancho et al. found that the presence of CaCl 2 in a biphasic water-methyl isobutyl ketone (MIBK) system with γ-Al 2 O 3 as catalyst notably improved the catalytic performance [51]. They proposed that the interaction between Ca 2+ and glucose molecules favors the formation of α-d-glucopyranose, thus enhancing glucose conversion to HMF. Likewise, it was inferred that the similar interaction between Mg 2+ and xylose molecules may have promoted the conversion of xylose to furfural, and then MgCl 2 and SnCl 4 contributed cooperatively to the dehydration process.  Figure 4 shows the effect of ionic liquids on the dehydration of xylose into furfural using SnCl 4 . As shown in Figure 4, EMIMBr and 1-butyl-3-methylimidazolium bromide (BMIMBr) resulted in higher furfural yields than other ionic liquids. The furfural yield (56.5%) obtained with BMIMBr was slightly lower than that obtained with EMIMBr. When ionic liquid 1,3-dimethylimidazolium iodide (DMIMI) was used as reaction medium, a furfural yield of 46.7% was obtained. The furfural yields from EMIMCl (30.0%) and BMIMCl (33.8%) were much lower than from EMIMBr and BMIMBr. This observation suggested that Brcontaining ionic liquids are more efficient than Cl − containing ionic liquids for the conversion of xylose into furfural catalyzed by SnCl 4 , which may be attributed to the differences in size charge density, and electronegativity of Br − and Cl − [52]. When 1-ethyl-3-methylimidazolium tetrafluoroborate (EMIMBF 4 ) was used as reaction medium, the furfural yield was only 15.1%. The low yield from EMIMBF 4 could be due to their poor ability to dissolve sugar [53]. Besides, the formation of massive brown residues in EMIMBF 4 indicated the severe occurrence of side reactions.

Effect of Solvents on the Dehydration of Xylose into Furfural
Furfural yield can be improved by extracting the produced furfural immediately to inhibit its further degradation [33]. The biphasic systems consisting of water and organic solvents, such as THF [54], toluene [9], MIBK [55], and dimethyl carbonate (DMC) [56] have been widely employed for improving both HMF and furfural yield. In addition, the biphasic systems consisting of ionic liquids and organic solvents have also been demonstrated to successfully improve HMF production efficiency [45]. Therefore, in this study, we examined the effect of these organic solvents on the conversion of xylose to furfural in water and EMIMBr. As expected, toluene, DMC, and MIBK could form two phases with water and partially extract the produced furfural from water to the organic phase during the reaction process. For the water-organic solvent biphasic systems, the use of toluene and MIBK as extracting agents could increase the furfural yield noticeably. The furfural yield (45.7%) from the H 2 O-MIBK system was remarkably higher than that obtained from the single water phase with the same sugar loading (20 wt%). In contrast, the furfural yield slightly decreased when DMC was used as extracting agent. In the EMIMBr-organic solvent biphasic systems, THF, toluene, and DMC exhibited high furfural extracting ability from ionic liquid, while ethylene glycol dimethyl ether (EGDE) and MIBK showed poor extracting ability (Table 2). However, the EMIMBr-organic solvent biphasic systems resulted in an obvious decrease of the furfural yield, compared with the single EMIMBr phase system. These results suggested that the adverse effect of organic solvent on the conversion of xylose into furfural in ionic liquid was more predominant than their inhibition to furfural degradation.
conversion of xylose to furfural in water and EMIMBr. As expected, toluene, DMC, and MIBK could form two phases with water and partially extract the produced furfural from water to the organic phase during the reaction process. For the water-organic solvent biphasic systems, the use of toluene and MIBK as extracting agents could increase the furfural yield noticeably. The furfural yield (45.7%) from the H2O-MIBK system was remarkably higher than that obtained from the single water phase with the same sugar loading (20 wt%). In contrast, the furfural yield slightly decreased when DMC was used as extracting agent. In the EMIMBr-organic solvent biphasic systems, THF, toluene, and DMC exhibited high furfural extracting ability from ionic liquid, while ethylene glycol dimethyl ether (EGDE) and MIBK showed poor extracting ability (Table 2). However, the EMIMBr-organic solvent biphasic systems resulted in an obvious decrease of the furfural yield, compared with the single EMIMBr phase system. These results suggested that the adverse effect of organic solvent on the conversion of xylose into furfural in ionic liquid was more predominant than their inhibition to furfural degradation.  Table 2. Effect of biphasic system on the conversion of xylose into furfural a .  According to previous reports, fructose could be converted into HMF (92%) almost quantitatively by EMIMBr without utilizing any other catalyst [49]. To determine the role of EMIMBr in the conversion of xylose to furfural, the xylose conversion in EMIMBr without catalyst was also studied. As shown in Figure 2, almost no furfural was produced when no catalyst was added into the reaction system. This result suggested that EMIMBr could not directly induce the formation of furfural from xylose. Wrigstedt et al. reported that in the preparation of HMF from glucose, bromine ions could promote the fructose dehydration step in the aqueous phase [57]. The isomer of glucose, fructose, was considered as a predominant intermediate in the process of conversion of glucose to HMF. The reaction pathway for conversion of xylose to furfural is analogous to the reaction pathway of the conversion of glucose to HMF [58]. Accordingly, bromine ions probably could also promote the dehydration of the isomer of xylose, xylulose, into furfural. Based on the above analysis, we speculated that bromide anions were able to catalyze the dehydration of ketose (xylulose) to furans, but not the aldose (xylose). In the presence of Lewis acid, xylose was first isomerized into xylulose, and then the formed xylulose was further dehydrated to furfural by EMIMBr.
It is generally accepted that the conversion of xylose catalyzed by Lewis acid involves two steps: the isomerization of xylose into xylulose and the dehydration of xylulose into furfural [22]. As an isomer of xylose, the dehydration of xylulose to furfural is much easier than the direct conversion of xylose to furfural [39]. In the medium of water, little xylulose or fructose was observed since the hydrolysis of SnCl 4 produced sufficient Bronsted acidity to catalyze the dehydration of the ketose carbohydrates at a rate superior to the isomerization of the aldose carbohydrates [33]. Since the use of ionic liquids could further accelerate the dehydration of ketoses, quantifiable fructose was also not detected in the EMIMBr/SnCl 4 system [30,45] even though the reduced reaction temperature and higher furfural selectivity suggest that the EMIMBr/SnCl 4 system prefers the isomerization pathways rather than the direct dehydration pathways. Figure 5 shows the effect of reaction temperature on the dehydration of xylose into furfural. It was observed that the rates of xylose conversion and furfural production increased with reaction temperature. The furfural yield first increased and then decreased with the increase of reaction temperature. The maximum furfural yields at 120, 130, and 140 • C were 66.5, 71.1, and 70.2%, obtained at 1.5, 1.0, and 0.5 h, respectively. These results indicated that both the xylose conversion rate and the furfural degradation rate increased with the increasing reaction temperature. This was consistent with previous reports. For example, Wang et al. found that the residence time required to reach the maximum furfural yield decreased with increasing temperature when xylose was converted in water-GVL at 120-150 • C using AlCl 3 as catalyst [59]. When the temperature was above 130 • C, the degradation was enhanced because of the stronger molecular thermal motion [60,61]. The xylose conversion, furfural yield, and furfural selectivity in the EMIMBr/SnCl 4 system are shown in Figure 6. The xylose conversion rate reached 95% in 0.5 h. As the reaction time increased from 0.5 h to 1 h, the xylose conversion increased from 95.3% to 98.9% and the furfural selectivity increased from 62.1% to 71.9%. rate and the furfural degradation rate increased with the increasing reaction temperature. This was consistent with previous reports. For example, Wang et al. found that the residence time required to reach the maximum furfural yield decreased with increasing temperature when xylose was converted in water-GVL at 120-150 C using AlCl3 as catalyst [59]. When the temperature was above 130 C, the degradation was enhanced because of the stronger molecular thermal motion [60,61]. The xylose conversion, furfural yield, and furfural selectivity in the EMIMBr/SnCl4 system are shown in Figure  6. The xylose conversion rate reached 95% in 0.5 h. As the reaction time increased from 0.5 h to 1 h, the xylose conversion increased from 95.3% to 98.9% and the furfural selectivity increased from 62.1% to 71.9%.

Effect of Initial Xylose Loading on the Dehydration of Xylose into Furfural
The production of furfural from xylose at a high substrate loading is very important for large scale application [62]. Therefore, the effect of initial xylose loading on the dehydration of xylose into furfural was investigated. As shown in Figure 7, furfural yield was markedly affected by the initial xylose loading. When the xylose loading increased from 10 wt% to 20 wt%, the corresponding furfural yield increased from 60.0% to 71.1%. However, the furfural yield decreased with the further increase of xylose loading. A moderate furfural yield of 54.2% was obtained when the xylose loading was 40 wt%. The furfural yield decreased obviously when the initial xylose loading increased from 40 wt% to 80 wt%. When the initial xylose loading was increased to 80 wt%, only 12.6% furfural yield was obtained. It was also observed that the amount of insoluble humins in the reaction bottle increased with the increase of xylose loading. The decrease in furfural yield at high xylose loading may be related to the increase of the viscosity of reaction mixture. The increased viscosity of the mixture may result in unevenly heating in the oil bath reactor [63] and also inhibit the mass transfer between catalyst and reaction substrate [61]. Moreover, the higher xylose concentration may increase the probability of the condensation between furfural and reaction intermediates, leading to the formation of humins [64]. This is consistent with the trend of conversion of xylose in aqueous acidic solutions [63] and ionic liquid EMIMCl [24].
The catalytic performance of the EMIMBr/SnCl 4 system developed in this work was compared with other representative reaction systems reported recently. As shown in Table 3, unrealistic reaction conditions, including relative high reaction temperature, low xylose loading (lower than 10%), and large amount of organic solvents and electrolytes (such as NaCl) are indispensable to obtain relative high furfural yield from the water-organic solvent biphasic systems [34,65,66]. The furfural yield in the present work was higher than or comparable to previous reports even when the xylose loading (20 wt%, with respect to the mass of reaction medium) was considerably higher than other previous reported catalytic systems. Moreover, the furfural yield still reached 54.2% even at a sugar loading as high as 40 wt%. For the reaction system using SnCl 4 as catalyst, the furfural yield from EMIMBr was higher than that using other single-phasic reaction media, such as water-DMSO [47] or water [33]. Although the furfural yield up to 69.4% was obtained when using high-pressure CO 2 as a catalyst in the water/THF system, the xylose loading was only 1.3% [67]. Therefore, EMIMBr/SnCl 4 is an efficient system for converting carbohydrates to furfural. 40 wt% to 80 wt%. When the initial xylose loading was increased to 80 wt%, only 12.6% furfural yield was obtained. It was also observed that the amount of insoluble humins in the reaction bottle increased with the increase of xylose loading. The decrease in furfural yield at high xylose loading may be related to the increase of the viscosity of reaction mixture. The increased viscosity of the mixture may result in unevenly heating in the oil bath reactor [63] and also inhibit the mass transfer between catalyst and reaction substrate [61]. Moreover, the higher xylose concentration may increase the probability of the condensation between furfural and reaction intermediates, leading to the formation of humins [64]. This is consistent with the trend of conversion of xylose in aqueous acidic solutions [63] and ionic liquid EMIMCl [24]. The catalytic performance of the EMIMBr/SnCl4 system developed in this work was compared with other representative reaction systems reported recently. As shown in Table 3, unrealistic reaction conditions, including relative high reaction temperature, low xylose loading (lower than 10%), and large amount of organic solvents and electrolytes (such as NaCl) are indispensable to obtain relative high furfural yield from the water-organic solvent biphasic systems [34,65,66]. The furfural yield in the present work was higher than or comparable to previous reports even when the xylose loading (20 wt%, with respect to the mass of reaction medium) was considerably higher than other previous reported catalytic systems. Moreover, the furfural yield still reached 54.2% even at a sugar loading as high as 40 wt%. For the reaction system using SnCl4 as catalyst, the furfural yield from EMIMBr was higher than that using other single-phasic reaction media, such as water-DMSO [47] or water [33]. Although the furfural yield up to 69.4% was obtained when using high-pressure CO2 as a catalyst in the water/THF system, the xylose loading was only 1.3% [67]. Therefore, EMIMBr/SnCl4 is an efficient system for converting carbohydrates to furfural.

Effect of Water Content on the Dehydration of Xylose into Furfural
When xylose is completely dehydrated to furfural, every equivalent of xylose releases three equivalents of water [69]. Previous works indicated that water had a negative effect on the dehydration of xylose into furfural [65,69,70]. The effect of water content on xylose dehydration in EMIMBr/SnCl 4 system was studied. As shown in Figure 8, the adverse effect of water on the furfural yield was limited when the water content in the system was less than 10 wt%. However, the furfural yield decreased to 52.7% and 42.1% when the water content increased to 15% and 20%, respectively. When ionic liquids were completely replaced with water, the furfural yield was only 22.1%. It was also observed that the amount of insoluble humins also increased with the increase of water content in the system. It was reported that water could lead to undesirable condensation side products and the rehydration of furfural [60,71]. When there was water in the system, the intermediate products would be more active, which may have led to the accumulation of by-products [65,72]. A similar phenomenon was also observed for the dehydration of glucose to HMF in EMIMCl [73].

Conversion of Xylan into Furfural
Xylan, a polymer of xylose, is the predominant component in hemicellulose. In consequence, the conversion of xylan is critical for utilization of realistic biomass feedstocks [22,24]. Zhang et al. proposed that the (AlCln) (n − 3)− complexes formed from the BMIMCl/AlCl3 system could weaken the glycosidic bonds and then facilitate the hydrolysis of xylan to xylose, which would be further dehydrated into furfural [24]. Likewise, Zhang and Zhao proposed that CrCl3 in BMIMCl could weaken the glycosidic bonds through binding with a glycosidic oxygen atom in a similar manner to protic acid, leading to the hydrolysis of xylan to xylose [74].
We attempted to convert xylan into xylose in the EMIMBr/SnCl4 system at 130 C. As shown in Figure 9, the furfural yield was 41.7% after 30 min reaction. The maximum furfural yield of 50.1% was obtained at 1 h. When the reaction time was prolonged to 4 h, the furfural yield declined to 33.0%. Our results showed that the optimized reaction conditions for xylose were also suitable for the conversion of xylan. Binder et al. investigated the conversion of xylan using CrCl2 in DMA-LiCl into furfural under identical reaction conditions (at 100 C) with xylose [22]. However, only trace yields of furfural were obtained, suggesting that these conditions were too mild to accomplish the depolymerization of xylan into xylose. The furfural yield increased to 7-8% when the reaction temperature increased to 140 C.

Conversion of Xylan into Furfural
Xylan, a polymer of xylose, is the predominant component in hemicellulose. In consequence, the conversion of xylan is critical for utilization of realistic biomass feedstocks [22,24]. Zhang et al. proposed that the (AlCl n ) (n−3)− complexes formed from the BMIMCl/AlCl 3 system could weaken the glycosidic bonds and then facilitate the hydrolysis of xylan to xylose, which would be further dehydrated into furfural [24]. Likewise, Zhang and Zhao proposed that CrCl 3 in BMIMCl could weaken the glycosidic bonds through binding with a glycosidic oxygen atom in a similar manner to protic acid, leading to the hydrolysis of xylan to xylose [74].
We attempted to convert xylan into xylose in the EMIMBr/SnCl 4 system at 130 • C. As shown in Figure 9, the furfural yield was 41.7% after 30 min reaction. The maximum furfural yield of 50.1% was obtained at 1 h. When the reaction time was prolonged to 4 h, the furfural yield declined to 33.0%. Our results showed that the optimized reaction conditions for xylose were also suitable for the conversion of xylan. Binder et al. investigated the conversion of xylan using CrCl 2 in DMA-LiCl into furfural under identical reaction conditions (at 100 • C) with xylose [22]. However, only trace yields of furfural were obtained, suggesting that these conditions were too mild to accomplish the depolymerization of xylan into xylose. The furfural yield increased to 7-8% when the reaction temperature increased to 140 • C.
The hydrolysis of xylan to xylose requires the participation of some water (1 mol water/mol xylose unit in xylan) [19]. When there is not enough water in the reaction medium, dehydration of xylose into furfural is favored but the depolymerization of xylan will be suppressed [75]. Conversely, polymeric carbohydrates will no longer be soluble in ionic liquids and xylose dehydration will be inhibited when water content exceeds a certain level [76]. The effect of water amount on the conversion of xylan into furfural was investigated to improve the catalytic effect of the reaction system. As expected, the yield of furfural increased initially, then decreased gradually with increasing water amount ( Figure 10). The furfural yield reached a maximum of 57.3% when 25 µL water was added to the reaction system. Compared with the reaction systems without additional water, an increase in the furfural yield was observed with water amounts increasing from 15 to 100 µL. When the water amount increased to 150 µL, the furfural yield was lower than that of the reaction system without water. The decreased furfural yield indicated excessive water was adverse to the production of furfural. The hydrolysis of xylan to xylose requires the participation of some water (1 mol water/mol xylose unit in xylan) [19]. When there is not enough water in the reaction medium, dehydration of xylose into furfural is favored but the depolymerization of xylan will be suppressed [75]. Conversely, polymeric carbohydrates will no longer be soluble in ionic liquids and xylose dehydration will be inhibited when water content exceeds a certain level [76]. The effect of water amount on the conversion of xylan into furfural was investigated to improve the catalytic effect of the reaction system. As expected ， the yield of furfural increased initially, then decreased gradually with increasing water amount ( Figure 10). The furfural yield reached a maximum of 57.3% when 25 μL water was added to the reaction system. Compared with the reaction systems without additional water, an increase in the furfural yield was observed with water amounts increasing from 15 to 100 μL. When the water amount increased to 150 μL, the furfural yield was lower than that of the reaction system without water. The decreased furfural yield indicated excessive water was adverse to the production of furfural.  The hydrolysis of xylan to xylose requires the participation of some water (1 mol water/mol xylose unit in xylan) [19]. When there is not enough water in the reaction medium, dehydration of xylose into furfural is favored but the depolymerization of xylan will be suppressed [75]. Conversely, polymeric carbohydrates will no longer be soluble in ionic liquids and xylose dehydration will be inhibited when water content exceeds a certain level [76]. The effect of water amount on the conversion of xylan into furfural was investigated to improve the catalytic effect of the reaction system. As expected ， the yield of furfural increased initially, then decreased gradually with increasing water amount ( Figure 10). The furfural yield reached a maximum of 57.3% when 25 μL water was added to the reaction system. Compared with the reaction systems without additional water, an increase in the furfural yield was observed with water amounts increasing from 15 to 100 μL. When the water amount increased to 150 μL, the furfural yield was lower than that of the reaction system without water. The decreased furfural yield indicated excessive water was adverse to the production of furfural. Binder et al. found that although CrCl 2 and CrCl 3 could afford furfural yields between 30-41%, the furfural yields from xylan were less than 8% in these reaction systems [22]. The highest furfural yield of 18% was obtained when adding HCl to the reaction mixture as a co-catalyst for xylan saccharification and using EMIMCl as the solvent. We attempted to use acid as a co-catalyst for xylan saccharification to improve furfural synthesis. In this study, when 50 µL 0.1mol/L HCl was added to the EMIMBr/SnCl 4 system the furfural yield (54.6%) was almost equal to the furfural yield (54.5%) where 50 µL pure water was used. These results indicated that there was no need to employ additional Bronsted acid to promote the depolymerization of xylan, as was consistent with previous studies. Yu et al. reported that SnCl 4 could generate Bronsted acidity in water to catalyze the hydrolysis of starch into glucose [77]. Enslow et al. demonstrated that the hydrolysis of SnCl 4 provided sufficient Bronsted acidity to catalyze the dehydration of the ketose carbohydrates at a rate higher than the isomerization of the aldose carbohydrates [33]. Although SnCl 4 may hydrolyze in water, leading to the formation of complex Sn species, its catalytic performance can be readily recovered by replenishing appropriate HCl.

Conversion of Corn Stalk into Furfural
The catalytic performance of the EIMIM/SnCl 4 system was also evaluated using corn stalk as representative biomass materials as substrate. The corn stalk used in this study contained 17.9 wt% xylan, and the furfural yield was calculated based on this data. Figure 11 illustrates that a high furfural yield of 54.5% from real raw biomass was obtained at 130 • C after 3 h when a relative low substrate loading (5 wt%) was used. In addition, compared to xylose and xylan, when corn stalk was used as substrate, a longer reaction time was needed to obtain the maximal furfural yield. When the substrate loading increased to 10 wt% and 20 wt%, the furfural yields decreased to 46.4% and 34.7%, respectively, and were lower than that obtained from pure xylose or xylan. This may be due to the complexity and recalcitrance of lignocellulose [78].   The catalytic performance of the EMIMBr/SnCl 4 system developed in this work was compared with other representative homogeneous reaction systems. As shown in Table 4, higher furfural yield could be obtained from the system EMIMBr/SnCl 4 than other systems under mild conditions. Zhang et al. investigated the conversion of lignocellulosic biomass into furfural in system BMIMCl/AlCl 3 under microwave irradiation. The furfural yields from untreated corncob, grass, and pine wood were 19.1%, 31.4%, and 33.6%, respectively, at a low substrate loading of 2.5 wt% [24]. Morais proposed a two-stage furfural production process, where wheat straw was subjected to a high-pressure CO 2 -H 2 O treatment to yield a hemicellulose hydrolysate that was then used as feed in the CO 2 -catalysed dehydration step in a multiphasic CO 2 /water/THF system with MIBK as the extracting solvent [79]. Through this process, a furfural yield of 43 mol% with a selectivity of 44 mol% was obtained with 50 bar of initial CO 2 pressure at 180 • C, 60 min. Compared with previous reports, the EMIMBr/SnCl 4 was more efficient for the production of furfural from raw biomass. To the best of our knowledge, the EMIMBr/SnCl 4 system is the most efficient reaction system for the conversion of high concentration (20 wt%) xylose, and xylan and lignocellulosic biomass. However, more work is necessary to further improve this system in order to achieve large scale application. On the one hand, the use of expensive imidazolium-based ionic liquids as reaction media results in the high cost of converting xylose into furfural. Recently, some concerns have been pointed out regarding the environmental implications and the "greenness" of processes based in ionic liquids [81][82][83]. Therefore, it is very necessary to search for alternative solvents to alleviate the disadvantages of ionic liquids, such as biomass derived ionic liquids and eutectic solvents (DESs). On the other hand, environmentally friendly and efficient extracting agents should be developed to improve the product separation and purification processes, as well as to reduce the associated environmental pollution. Besides, it is also very important to provide more evidence to confirm the proposed reaction pathway, which may promote the development of a more efficient reaction system. using a syringe and needle to evaluate the partition of furfural between the extraction phase and the reaction phase. The sample was filtered with a 0.45 µm polytetrafluoroethylene filter membrane prior to high-performance liquid chromatography (HPLC) analysis. Each experiment was performed at least three times, and the reproducibility of xylose conversion, furfural yield, and selectivity was within 3% standard deviation. The corn stalk used in this study was collected from Lianyungang, China.
All reaction products were analyzed by high performance liquid chromatography (HPLC) and quantified using calibration curves. Furfural was determined at 275 nm and 35 • C by an HPLC system equipped with a diode array detector (DAD) using a methanol/water (v:v = 70%:30%) mobile phase at a flow rate of 1.0 mL/min. Xylose was analyzed by HPLC system equipped with a refractive index detector (refractomax 521 Model) and a Shodex Sugar SH1011 analytical column (8.0 mm × 300 mm). A 5 mM H 2 SO 4 solution was used as the mobile phase at a flow rate of 1.0 mL/min at 65 • C. The catalytic performance of the reaction system was evaluated by xylose conversion, furfural yield, and selectivity. The xylose conversion, furfural yield, and selectivity were calculated as follows: Xylose conversion (from xylose) = moles of xylose reacted moles of initial xylose ×100% Furfural selectivity (from xylose) = moles of xylose produced moles of xylose reacted ×100% (2) Furfural yield (from xylose) = moles of furfural produced moles of initial xylose ×100% Furfural yield (from xylan) = moles of furfural produced moles of initial xylan ×100% (4) Furfural yield (from corn stalk) = moles of furfural produced moles of initial xylan in corn stalk ×100% (5)

Conclusions
This study investigated the catalytic performance of metal chlorides in different solvents for xylose dehydration into furfural. The EMIMBr/SnCl 4 system was screened as the most effective reaction system, obtaining a furfural yield as high as 71.1% when the reaction was carried out at 130 • C for 1 h. In addition, the furfural yield still reached 68.8% when 10 mol% SnCl 4 was replaced by the combined catalyst consisting of 5 mol% MgCl 2 and 5 mol% SnCl 4 . Since the reaction was conducted at relative conditions using high xylose loading (20 wt%), the conversion efficiency of the EMIMBr/SnCl 4 was considerably higher than other catalytic systems. Furthermore, the EMIMBr/SnCl 4 system was also efficient to directly catalyze the conversion of xylan into furfural without the assistance of additional Bronsted acid. The addition of a certain amount of water could promote the conversion of xylan in the EMIMBr/SnCl 4 system, obtaining a furfural yield up to 57.3%. Finally, 54.5% furfural yield from corn stalk could be obtained from the EMIMBr/SnCl 4 reaction system.