Phytofabrication of Silver/Silver Chloride Nanoparticles Using Aqueous Leaf Extract of Oedera genistifolia: Characterization and Antibacterial Potential

In this present study, silver nanoparticles (Ag/AgCl NPs) were synthesized using an aqueous leaf extract of Oedera genistifolia as a reducing agent. The biosynthesized Ag/AgCl NPs was characterized by UV-visible spectrophotometry, transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). In addition, sequel to antibacterial assay, the cytotoxic effect of the phytofabricated Ag/AgCl NPs was assessed against the HeLa cell line (human cervix adenocarcinoma). The results of the characterization of the synthesized Ag/AgCl NPs indicate the successful synthesis using plant extract as a reducing agent, with UV-Vis spectra between 290–360 nm. TEM results showed that Ag/AgCl NPs was spherical in shape with an average size of 34.2 nm. EDX analysis revealed that the particles were predominantly composed of carbon, oxygen, chlorine, and silver, while FTIR identified major phytochemical compounds, which could be responsible for bio-reducing and capping potential. XRD analysis showed the crystallinity of Ag/AgCl NPs, with a face-centred cubic structure. The studied Ag/AgCl NPs had no cytotoxic effect on HeLa cells and exhibited antibacterial activity (minimum inhibitory concentration (MIC) 0.25–1 mg/mL; minimum bactericidal concentration (MBC) 2–16 mg/mL) against both the Gram-negative and Gram-positive bacteria investigated. Findings from this study suggest that this plant as a good candidate for producing new antibacterial drugs.


Introduction
Nanotechnology has recently become a subject of active research in materials chemistry. This field deals with the synthesis of particles with structural dimensions on the nanometre scale [1][2][3]. Nanoparticles of metal origin such as silver have been widely used in the synthesis of products such as anti-cancer, antioxidants, and antibacterial agents, as well as in cosmetics, due to their unique superior features [4,5]. The utilization of substrates such as bacteria, plant extracts, biodegradable phytochemicals present in the extracts are responsible for the reduction of metal ions, and efficient stabilization of nanoparticles, with the reduction of Ag + to Ag o ascribed to the presence of these phytochemicals in the aqueous leaf extract of O. genistifolia [22]. Most reports documenting nanoparticle synthesis have highlighted discrepancies in size, synthesis parameters, shape, and stability [31].

UV-Vis Spectroscopy Analysis
Ag/AgCl NPs synthesis via biological means using aqueous leaf extract of O. genistifolia was carried out in this study. Due to its high conductivity and catalytic properties, as well as its chemical stability, silver nitrate was used as a suitable precursor [32]. The gradual addition of the aqueous leaf extract of O. genistifolia (light brown colour) to silver nitrate solution resulted into the instant formation of a dark brown coloration, which could be ascribed to the completion of the reaction. For biological synthesis of nanoparticles to have added advantage over chemical methods, the time for synthesis is also a critical factor to be considered. Subsequently, UV-Vis spectroscopy was used to confirm the formation of the Ag/AgCl NPs, indicated by the appearance of the dark-brown colloidal solution, as a result of excitation of surface plasmon resonance (SPR) between 290-360 nm ( Figure 1). Our findings corroborate with the absorbance value of biosynthesized silver nanoparticles reported from previous studies [33], and contrary to our present study, some biogenic AgNPs synthesized from other plant extracts had SPR between 400 and 500 nm [34][35][36]. The type of biogenic nanoparticles formed depends on the phytochemical compounds in the plant extract. The observed results show that the synthesis of Ag/AgCl NPs through the green approach in this study proved to be efficient with respect to reaction time, as well as having no requirement for the use of toxic chemical reducing or stabilizing agents. Therefore, making it an economical, sustainable, reliable, and an alternative process to chemical or physical methods for the synthesis of silver nanoparticles [12].

FTIR Analysis
Transform infrared spectroscopy (FTIR) is a non-destructive, appropriate, indispensable, and simple method for the determination of the role of plant extracts in the reduction of silver ions to

FTIR Analysis
Transform infrared spectroscopy (FTIR) is a non-destructive, appropriate, indispensable, and simple method for the determination of the role of plant extracts in the reduction of silver ions to silver nanoparticles [37]. In this present study, the FTIR spectra of O. genistifolia extract and Ag/AgCl NPs were analysed, and a comparison of their spectra patterns ( Figure 2). Vibrational frequencies at 1025, 1590, 2933 cm −1 , etc., observed in the spectra of Ag/AgCl NPs and plant extract could be ascribed to the phytochemical compounds in the plant extracts which were not only responsible for the biosynthesis of Ag/AgCl NPs, but also acted as capping and stabilizing agents. This indicated that some of the residual moieties of the phytochemical compounds in the plant extract encapsulated the Ag/AgCl NPs, acting as capping and stabilizing agents [38]. Furthermore, a broad peak at 3454 cm −1 could be attributed to N-H stretching vibration of group NH 2 and OH, in both O. genistifolia leaf extract and the Ag/AgCl NPs. The band at 1657 cm −1 from the plant extract corresponds to amide C=O stretching, which was also observed on the Ag/AgCl NPs at 1697 cm −1 . Similarly, a peak at 1596 cm −1 could be assigned to the C=O group present in amide in the phytochemicals of the plant extract, which was also found on the Ag/AgCl NPs, with a slight shift in the spectra band at 1590 cm −1 . The observed peaks at 1117 cm −1 (plant extract) and 1118 cm −1 (synthesized nanoparticles) denote -C-O-C-linkages, or -C-O-bonds. The detected peaks are mainly attributed to flavonoids and terpenoids present in the plant extract.

TEM, SEM and EDX Analyses
TEM appears to be the most appropriate technique to determine the average size of nanoparticles; nevertheless, other techniques also contribute to understanding the salient features of nanoparticles [31]. The TEM analysis was used to describe the particles based on their shape, size, and particle dispersal. Previous studies have shown that the activity of green Ag/AgCl NPs is sizedependent, with smaller particles showing higher activity as compared to the larger ones [31]. Size distribution studies of the Ag/AgCl NPs synthesized in the present study indicated that the particles were of narrow size distribution, and fall in the acceptable limit range; thus, implying that the silver nanoparticles produced were relatively small. The results depicted in Figure 3A show the Ag/AgCl NPs as poly-disperse, predominantly composed of a well-defined spherical shape with a size range of 10-60 nm, with an average size of 34.2 nm without any agglomeration, and with some irregular rod-like shapes ( Figure 3B). The silver nanoparticles synthesized from Mentha pulegium and Prosopis

TEM, SEM and EDX Analyses
TEM appears to be the most appropriate technique to determine the average size of nanoparticles; nevertheless, other techniques also contribute to understanding the salient features of nanoparticles [31]. The TEM analysis was used to describe the particles based on their shape, size, and particle dispersal. Previous studies have shown that the activity of green Ag/AgCl NPs is size-dependent, with smaller particles showing higher activity as compared to the larger ones [31]. Size distribution studies of the Ag/AgCl NPs synthesized in the present study indicated that the particles were of narrow size distribution, and fall in the acceptable limit range; thus, implying that the silver nanoparticles produced were relatively small. The results depicted in Figure 3A show the Ag/AgCl NPs as poly-disperse, predominantly composed of a well-defined spherical shape with a size range of 10-60 nm, with an average size of 34.2 nm without any agglomeration, and with some irregular rod-like shapes ( Figure 3B). The silver nanoparticles synthesized from Mentha pulegium and Prosopis cineraria were reported to be in the range of 5-50 nm and 20-44 nm, respectively [39,40], which is similar to our result in this study. On the contrary, bigger sizes of silver nanoparticles of 90.87 nm and 74-94 nm have been documented from Gelsemium sempervirens and Rosa damascene, respectively [41,42]. Figure 3B depicts the size distribution image of Ag/AgCl NPs and the size distribution was observed to range from 10 to 60 nm. The calculated average particle size distribution of Ag/AgCl NPs was 34.2 nm. SEM was used to study the surface morphology of AgNPs in this present study. The Ag/AgCl NPs were observed to be uniformly distributed on the surface as illustrated in Figure 3C. The SEM images showed the shape of Ag/AgCl NPs as being non-consistent, with both spherical-shaped and triangular nanoparticles. These observations confirmed the results from the TEM analysis ( Figure 3A) that revealed the spherical and irregular shapes of the Ag/AgCl NPs, which corroborate the previously reported studies [43,44]. The determination of the elemental compositions of the Ag/AgCl NPs was carried out by energy dispersive X-ray spectroscopy (EDX) analysis, to illustrate the surface morphological features of the Ag/AgCl NPs ( Figure 3D). The presence of chloride ions in the O. genistifolia leaf extract was further confirmed by EDX and XRD analyses. The result confirmed the successful formation of Ag/AgCl NPs and revealed its predominant elements to include carbon (8.46%), oxygen (9.57%), chlorine (9.52%), and silver (72.44%). Apart from the intense peak of Ag observed at 3.0 keV, an intense peak of Cl was also noted at 2.7 keV. These intense peaks of Ag and Cl confirmed the formation of Ag/AgCl NPs, and our findings corroborate the reports of Ag/AgCl NPs synthesized from Benincasa hispida and Momordica charantia [45,46]. the O. genistifolia leaf extract was further confirmed by EDX and XRD analyses. The result confirmed the successful formation of Ag/AgCl NPs and revealed its predominant elements to include carbon (8.46%), oxygen (9.57%), chlorine (9.52%), and silver (72.44%). Apart from the intense peak of Ag observed at 3.0 keV, an intense peak of Cl was also noted at 2.7 keV. These intense peaks of Ag and Cl confirmed the formation of Ag/AgCl NPs, and our findings corroborate the reports of Ag/AgCl NPs synthesized from Benincasa hispida and Momordica charantia [45,46].

XRD Analysis
XRD is generally used to elucidate the crystalline nature of Ag/AgCl NPs. It quantifies the firmness of diverse chemical compounds, thus indicating an idea of approximate different chemical groups and particle sizes. In this analysis, a monochromatic beam of X-rays was focused towards crystal samples, which subsequently produced different patterns that were analysed using Bragg's

XRD Analysis
XRD is generally used to elucidate the crystalline nature of Ag/AgCl NPs. It quantifies the firmness of diverse chemical compounds, thus indicating an idea of approximate different chemical groups and particle sizes. In this analysis, a monochromatic beam of X-rays was focused towards crystal samples, which subsequently produced different patterns that were analysed using Bragg's equation in order to reveal the unique features of the crystallinity of the studied Ag/AgCl NPs [31]. In this present study, the crystalline nature of dry powder of the Ag/AgCl NPs was analysed by XRD. The XRD patterns (  [47]. Similarly, our findings agree with the reports documented by other researchers [45,46,[48][49][50]. As emphasized by the report of Davi et al. [46], at the initial stage of the reaction, AgCl formation at room temperature could be due to the reaction between Ag + from AgNO 3 , and Cl − from the phytochemical compounds in the aqueous leaf extract of O. genistifolia. Upon AgCl formation, Ag + ions were reduced to metallic Ag by phytochemical compounds, which act as reducing agents originating from the plant extract. Subsequently, Ag + formed an intermediate complex with OH groups of phenolic compounds from the extract, which later underwent oxidation and reduced Ag + to Ag o NPs. Ag by phytochemical compounds, which act as reducing agents originating from the plant extract. Subsequently, Ag + formed an intermediate complex with OH groups of phenolic compounds from the extract, which later underwent oxidation and reduced Ag + to Ag o NPs.

TGA Analysis
The biosynthesized Ag/AgCl NPs retained more than 70% of their initial weight after heating up to 900 °C ( Figure 5). The initial weight loss between 30-200 °C could be due to the loss of moisture content from the Ag/AgCl NPs, and further decrease in weight loss was observed. The Ag/AgCl NPs retained about 70% of its weight at 900 °C, which indicates its robustness nature. This indicates the stability of the synthesized Ag/AgCl NPs, and in addition, this salient feature makes it a good candidate for pharmaceutical applications and other industrial processes where high temperatures are involved.

TGA Analysis
The biosynthesized Ag/AgCl NPs retained more than 70% of their initial weight after heating up to 900 • C ( Figure 5). The initial weight loss between 30-200 • C could be due to the loss of moisture content from the Ag/AgCl NPs, and further decrease in weight loss was observed. The Ag/AgCl NPs retained about 70% of its weight at 900 • C, which indicates its robustness nature. This indicates the stability of the synthesized Ag/AgCl NPs, and in addition, this salient feature makes it a good candidate for pharmaceutical applications and other industrial processes where high temperatures are involved. up to 900 °C ( Figure 5). The initial weight loss between 30-200 °C could be due to the loss of moisture content from the Ag/AgCl NPs, and further decrease in weight loss was observed. The Ag/AgCl NPs retained about 70% of its weight at 900 °C, which indicates its robustness nature. This indicates the stability of the synthesized Ag/AgCl NPs, and in addition, this salient feature makes it a good candidate for pharmaceutical applications and other industrial processes where high temperatures are involved.   Figure 6 depicts the cytotoxic effect of both the aqueous extract and the biosynthesized Ag/AgCl NPs, as assessed against HeLa cells. Both had no cytotoxic effect on the HeLa cells, since the cells viability was more than 75% in both samples (Figure 6), an indication of its safety for mammalian cells. This finding supports the safe utilization of the synthesized Ag/AgCl NPs as a lead substrate for drug design and development. However, some researchers in previous studies [17,51,52] have reported silver nanoparticles cytotoxic effects when synthesized from different plants. cells. This finding supports the safe utilization of the synthesized Ag/AgCl NPs as a lead substrate for drug design and development. However, some researchers in previous studies [17,51,52] have reported silver nanoparticles cytotoxic effects when synthesized from different plants.

Antibacterial Activity
Owing to the smaller particle size and recent medical advances, the use of silver nanoparticles against deadly diseases has gained significant interest as a means to overcome the limitations of orthodox treatments. The distinctive properties of silver nanoparticles coupled with the high surface area to volume ratio have rendered them potential candidates for biological activities, such as antimicrobial, anti-inflammatory, and anti-cancer activity [31]. In this study, the antibacterial potential of Ag

Antibacterial Activity
Owing to the smaller particle size and recent medical advances, the use of silver nanoparticles against deadly diseases has gained significant interest as a means to overcome the limitations of orthodox treatments. The distinctive properties of silver nanoparticles coupled with the high surface area to volume ratio have rendered them potential candidates for biological activities, such as antimicrobial, anti-inflammatory, and anti-cancer activity [31]. In this study, the antibacterial potential of Ag The minimum inhibitory concentration (MIC) of Ag/AgCl NPs for the tested bacterial strains was 1 mg/mL for L. ivanovic (ATCC 19119), 0.5 mg/mL for E. cloacae (ATCC 13047), S. uberis (ATCC 700407), S. aureus (ATCC 29213), and 0.25 mg/mL for M. smergatis (ATCC 19420) and Vibrio sp., as shown in Table 2. The Ag/AgCl NPs had varying minimum bactericidal concentration (MBC) values for all the bacterial strains tested. Furthermore, the MBC of Ag/AgCl NPs for E. cloacae (ATCC 13047), S. uberis ATCC (700407), S. aureus (ATCC 29213) and Vibrio sp. were 16 mg/mL; whereas, they showed strong bactericidal effect at 8 mg/mL and 2 mg/mL for L. ivanovic (ATCC 19119) and M. smergatis (ATCC 19420), respectively (Table 1). On the other hand, the positive control, ciprofloxacin had a MIC of 0.25 mg/mL for all the tested bacterial strains, and a MBC of 1 mg/mL.
The antibacterial activity of the studied biosynthesized Ag/AgCl NPs was lower compared to the antibacterial activity demonstrated by the positive control, and this could be attributed to the fact that the crude extract of the studied plant was used in the synthesis of Ag/AgCl NPs and not the pure compound. However, the results from this assay showed that the studied Ag/AgCl NPs showed a promising antibacterial effect, and hence, it is highly desirable for future studies to isolate pure compounds from the aqueous extract and carry out further biological assay on them. Nevertheless, findings from previous studies have shown that the shape of nanoparticles influences the efficacy of their biological activity [53]; that is, spherically shaped Ag/AgCl NPs display superior antimicrobial activity compared to rod-like shaped nanoparticles. Therefore, it is noteworthy to observe that the results from the present study corroborate those reported by Moodley et al. [53] and Raja et al. [29], where spherically shaped Ag/AgCl NPs were documented with few rod-like shaped particles.
The mechanism of antibacterial activity of the studied Ag/AgCl NPs on the bacterial strains was not clearly understood. However, previous studies have reported that the bactericidal mechanism could be due to the action of Ag/AgCl NPs on the structural integrity of the cell membrane that often resulted in membrane permeability, and consequently led to cell death [54,55]. The results obtained from this study also indicated that aqueous leaf extract of O. genistifolia could be used for the natural and eco-friendly synthesis of silver nanoparticles, which could be used as a potential candidate species with antibacterial activity, and the mechanism of action would be highly relevant for future studies.

Plant Collection and Extraction
Fresh O. genistifolia leaves were collected around the vicinity (coordinates: 32.7885 • S, 26.8461 • E) of University of Fort Hare, Alice campus, South Africa, in the month of September 2018. The leaves were washed with running tap water to remove debris and other contaminating organic contents, were subsequently rinsed with distilled water, and air-dried at room temperature for 14 days. The dried plant sample was pulverized with an electric grinder, and 100 g of the powder was weighed into 500 mL of distilled water contained in a 1-litre bottle and heated in water-bath at 60 • C for 1 h. Thereafter, the mixture was filtered through Whatman no. 1 filter paper and the extract was stored at 4 • C for further use [12].

Screening for Phytochemical Constituents
The analysis of the phytochemical constituents in the aqueous leaf extract of Oedera genistifolia was carried out as described by Yadav and Agarwala [56] and Karthigaiselvi et al. [57], with slight modifications. The phytochemical compounds screened for included phenolics, tannins, flavonoids, alkaloids, saponins, terpenoids, glycosides, steroids, proteins, carbohydrates, and anthraquinone.

Test for Phenols
We prepared fifty milligrams of Ag/AgCl NPs and added 5 mL of alcohol (50 mg/mL), which was treated separately with a few drops of neutral FeCl 3 (NH 4 OH + FeCl 3 ) solution. The sudden change in colour to blue-green or black coloration indicates the presence of phenols.

Test for Alkaloids
The solution of Ag/AgCl NPs (50 mg/mL) was added to Mayer's reagent (0.68 g of HgCl 2 in 30 mL of distilled water, 2.5 g of KI in 5 mL of distilled water) solution. Formation of whitish yellow (or) cream coloured precipitate indicates the absence of alkaloids.

Test for Tannins
Ag/AgCl NPs (50 mg/mL) was prepared, 1 mL was transferred in test tube, and 2 drops of 5% FeCl 3 solution was added thereafter. Dirty green precipitate indicated the presence of tannin.

Test for Flavonoids
Ag/AgCl NPs at a volume of 1 mL (50 mg/mL) was transferred into a test tube, and 3 mL of Pb(C 2 H 3 O 2 ) 2 solution was added. A bulky white Lead precipitate indicated the test was positive.

Test for Saponins
Ag/AgCl NPs (100 mg) was mixed with 5 mL of distilled water in a test tube, and it was shaken vigorously. The formation of stable foam indicated the presence of saponins.

Test for Glycosides
A volume of 2 mL glacial CH 3 COOH containing one drop of FeCl 3 solution was added to 5 mL of Ag/AgCl NPs (50 mg/mL). A 1 mL volume of concentrated H 2 SO 4 was poured along the sides of the tube. Formation of a brown ring at the interface indicated the presence of glycosides.

Test for Terpenoids
Ag/AgCl NPs (50 mg) was added with chloroform and H 2 SO 4 . Red violet colour indicated the presence of terpenoids.

Test for Protein
Ninhydrin solution (two drops of 10 mg of Ninhydrin in 200 mL of acetone) were added to 2 mL of Ag/AgCl NPs (50 mg/mL). A characteristic purple colour indicated the presence of amino acid.

Test for Carbohydrates
Ag/AgCl NPs (50 mg) was mixed with 2 mL of iodine solution. A dark blue or purple coloration indicated the presence of the carbohydrate.

Test for Anthraquinone
Ag/AgCl NPs (50 mg) was boiled with 10 mL of H 2 SO 4 and filtered while hot. The filtrate was shaken with 5 mL of chloroform. The chloroform layer was transferred into another test tube. The resulting solution was observed for colour changes to violet indicating the presence of anthraquinine.

Test for Steroids
Ag/AgCl NPs (50 mg) was taken in a test tube and dissolved with chloroform (10 mL), then had added an equal volume of concentrated H 2 SO 4 to the test tube by sides. The upper layer in the test tube turned into a red and sulphuric acid layer showing yellow with green fluorescence, showing the presence of steroids.

Biosynthesis of Ag/AgCl NPs
The aqueous extract of O. genistifolia leaves was used to synthesize the green silver nanoparticles. Silver nitrate (A.R.) (99.2%, MW = 169.87) used for the synthesis was purchased from Merck, South Africa. A solution of silver nitrate (450 mL) (AgNO 3 ) at 0.1 mM was prepared in 1 L of distilled water and 50 mL of the plant extract was added drop-wise into the AgNO 3 solution; the mixture was stirred continuously for 1 h at ambient temperature and in a dark chamber to prevent photo-reduction of silver nitrate. The bio-reduction of Ag + to Ag o was confirmed by the physical colour change from colourless solution (silver nitrate solution) to a dark brown (Ag/AgCl NPs). The mixture was centrifuged at 15,000 rpm, 15 • C for 20 min to separate the pellets from the suspension, and 2 mL was withdrawn from the supernatant for UV-Visible spectroscopy analysis. Subsequently, the obtained precipitate was washed three times with distilled water in order to eliminate any other impurity that co-precipitated along with the Ag/AgCl NPs and later oven-dried at 80 • C overnight.

Characterization of Ag/AgCl NPs
The reduction of silver ions to Ag/AgCl NPs was monitored by using a UV-Vis spectrophotometer (Perkin-Elmer Lambda 25, Boston, MA, USA) from 250 to 800 nm. Subsequently, Fourier transform infrared radiation (Perkin-Elmer Universal ATR 100) was employed to identify the characteristic vibrational frequency of Ag/AgCl NPs [14]. Particle size and shape of Ag/AgCl NPs were determined using Transmission electron microscope (JEOL 1210, Austin, TX, USA), operated at an accelerated voltage of 100 kV. The surface morphology of nanoparticles was studied with SEM (JEOL JSM-6390 LVSEM) and the elemental compositions of Ag/AgCl NPs was carried out with Noran Six 200 Energy Dispersive X-ray (JEOL Ltd., Tokyo, Japan) [14]. XRD analysis was carried out by using X-ray Diffractometer to determine the crystalline nature of the biosynthesized Ag/AgCl NPs.

Cytotoxicity Assay-Single Concentration Screening
The cytotoxic effect of Ag/AgCl NPs was evaluated against HeLa cells (Cellonex, South Africa) as described by Larayetan et al. [33]. The sample was incubated at 37 • C for 48 h at a fixed concentration of 50 µg/mL in 96-well plates containing HeLa cells. Emetine was used as positive control drug and the cells that survived Ag/AgCl NPs and extract exposure were quantified by incubation with resazurin and measuring its conversion to resorufin by fluorescence (Exc 560 /Em 590 ). Percentage viability of treated cells was calculated relative to fluorescence readings obtained with untreated control cells.

Antibacterial Activity Assay
Antibacterial activity of Ag/AgCl NPs was evaluated by micro-dilution procedure as described by Larayetan et al. [33] in order to determine the minimum inhibitory concentration (MIC). Mueller Hinton broth (MBH) (250 µL) was transferred into Eppendorf tubes for serial dilution. A stock solution (64 mg/mL) of Ag/AgCl NPs was prepared in dimethyl sulfoxide (DMSO) and subsequently, different concentrations ranging from 0.125-32 mg/mL were prepared by two-fold serial dilutions in MBH. Subsequently, 20 µL of fermented broth of each tested bacteria (0.5 McFarland 1 × 10 8 cfu/mL) was added into the mixture and vortexed followed by incubating at 37 • C for 24 h. The positive and negative controls used were ciprofloxacin and 5% DMSO, respectively. Subsequently, the minimum bactericidal concentration (MBC) was determined by plating out those broths without visible growth on fresh Mueller Hinton agar, and further incubating the plates at 37 • C for 24 h.

Conclusions
The results from this study reveal that the aqueous leaf extract of O. genistifolia aided the synthesis of Ag/AgCl NPs in a one-step process that completely complied with the rules of green synthesis. The biosynthesis of Ag/AgCl NPs was confirmed by UV-Vis spectroscopy analysis and the XRD pattern of the produced nanoparticles revealed their crystalline nature, and the spherical shape of the typical nanoparticles with permissible sizes was revealed by TEM analysis. The studied Ag/AgCl NPs demonstrated good antibacterial potential against both Gram positive and Gram-negative bacteria with no toxic effect on HeLa cells, thus, revealing its safety for human use. The process of synthesis is environmentally compatible, and the synthesized Ag/AgCl NPs could be a promising candidate for development of new antibacterial drugs. Additionally, the findings from this study could serve as a basis for future studies on the mechanism of bactericidal effect of the synthesized Ag/AgCl NPs on the selected pathogens.