Next Article in Journal
Inverted Organic Solar Cells with Low-Temperature Al-Doped-ZnO Electron Transport Layer Processed from Aqueous Solution
Next Article in Special Issue
The Influence of the Morphology and Mechanical Properties of Polymer Inclusion Membranes (PIMs) on Zinc Ion Separation from Aqueous Solutions
Previous Article in Journal
Effect of Curing Rate on the Microstructure and Macroscopic Properties of Epoxy Fiberglass Composites
Previous Article in Special Issue
Highly Zeolite-Loaded Polyvinyl Alcohol Composite Membranes for Alkaline Fuel-Cell Electrolytes
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation, Characterization, and Performance Evaluation of Polysulfone Hollow Fiber Membrane with PEBAX or PDMS Coating for Oxygen Enhancement Process

1
Lee Kong Chian Faculty of Engineering and Science, Universiti Tunku Abdul Rahman, Jalan Sungai Long, Bandar Sungai Long, Kajang 43300, Malaysia
2
Advanced Membrane Technology Research Centre (AMTEC), Universiti Teknologi Malaysia, Skudai 81310, Johor, Malaysia
*
Authors to whom correspondence should be addressed.
Polymers 2018, 10(2), 126; https://doi.org/10.3390/polym10020126
Submission received: 8 November 2017 / Revised: 16 January 2018 / Accepted: 18 January 2018 / Published: 28 January 2018
(This article belongs to the Special Issue Polymeric Membranes)

Abstract

:
Air pollution is a widely discussed topic amongst the academic and industrial spheres as it can bring adverse effects to human health and economic loss. As humans spend most of their time at the office and at home, good indoor air quality with enriched oxygen concentration is particularly important. In this study, polysulfone (PSF) hollow fiber membranes fabricated by dry-jet wet phase inversion method were coated by a layer of polydimethylsiloxane (PDMS) or poly(ether block amide) (PEBAX) at different concentrations and used to evaluate their performance in gas separation for oxygen enrichment. The surface-coated membranes were characterized using SEM and EDX to determine the coating layer thickness and surface chemical properties, respectively. Results from the gas permeation study revealed that the PSF membrane coated with PDMS offered higher permeance and selectivity compared to the membrane coated with PEBAX. The best performing PDMS-coated membrane demonstrated oxygen and nitrogen gas permeance of 18.31 and 4.01 GPU, respectively with oxygen/nitrogen selectivity of 4.56. Meanwhile, the PEBAX-coated membrane only showed 12.23 and 3.11 GPU for oxygen and nitrogen gas, respectively with a selectivity of 3.94. It can be concluded the PDMS coating is more promising for PSF hollow fiber membrane compared to the PEBAX coating for the oxygen enrichment process.

Graphical Abstract

1. Introduction

Air pollution is a serious environmental issue that is widely discussed around the globe, especially in the developing countries. The article published by the Lancet Respiratory Medicine in 2012 reported that 12.6 million deaths recorded worldwide were related to environmental pollution and, out of that number, 8.2 million were caused by air pollution [1]. The study had also shown that indoor air pollution was the major factor contributing to the adverse health problems of humans [1]. A poor level of indoor air quality is likely to cause sick building syndrome that affects both productivity and personal health. One of the effective ways to improve indoor air quality is to supply oxygen-enriched air to enhance air freshness [2]. Additionally, oxygen-enriched air is highly sought after in medical applications for hypoxemic patients and internal combustion engines to reduce the environment pollution that arises from unburned hydrocarbons [3,4].
Currently, two conventional techniques that are commonly used in oxygen gas production are pressure swing absorption (PSA) and cryogenic distillation. These two techniques are commercially utilized in industrial applications to produce large volumes of high purity gases. Membrane technology, on other hand, is an emerging technology which is able to produce gases in relatively good purity at a moderate production volume. The main advantages of membrane technology compared to conventional methods are that membrane technology requires less setting up space and is less energy intensive [5].
Generally, membranes act as a barrier for the gas separation whereby its characteristics and properties play an important role in the separation performance [6]. Nevertheless, the gas separation performance is always limited by the selectivity and permeability trade-off as shown in the Robeson upper bound [7,8]. Permeability describes the ability of membrane to allow gas molecules to diffuse through the matrix and is governed by the Fick’s diffusion law [9]. Selectivity meanwhile describes the ratio of the permeance of species A with respect to species B. To date, most of the works carried out are focused on the development of advanced polymeric-based membranes that demonstrate superior permeability and selectivity in lab-scale applications [10].
One of the easiest and simplest ways to improve the existing performance of polymeric-based membranes is via surface coating. Polydimethylsiloxane (PDMS) and poly(ether block amide) (PEBAX) are widely used as coating materials for membrane to minimize not only its surface defects but also improve its separation performance. Studies showed that PDMS coating is able to repair membrane surface defects by eliminating the non-selective membrane pores and to enhance gas pair selectivity [11,12]. Wahab et al. [13] and Moaddeb and Koros [14] reported the potential use of PDMS-coated membranes to improve the gas separation process, especially in CO2 separation for combustion. Unlike PDMS, PEBAX contains multiblock copolymers which consist of rigid polyamide chains separated by flexible polyether fragments. Previous work showed that the good species separation performance of PEBAX-coated membrane is attributed to its soft block of polyether fragments that allows gas molecules to permeate easily [15,16]. The hard polyamide block meanwhile provides good mechanical strength for the membrane [16]. Because of this, PEBAX was applied as a coating material on the membrane to evaluate its performance in gas separation. Kim et al. [15] reported that PEBAX-coated polyacrylonitrile (PAN) membrane was able to improve the sour gases (SO2 and CO2) separation performance from nitrogen. Liu et al. [16] on the other hand found that polysulfone (PSF) flat sheet membranes coated with PEBAX via dip coating method were able to improve the permselectivity of CO2/N2.
In this study, two different coating materials i.e., PDMS and PEBAX were used to improve the separation properties of PSF hollow fiber membranes particularly for oxygen/nitrogen separation. The outer surfaces of membranes were coated with polymers at different concentrations followed by instrumental characterization before proceeding to gas separation performance evaluation.

2. Materials and Methods

2.1. Materials

The main material used for hollow fiber membrane fabrication was commercial PSF with the trade name UDEL-3500 (Amocco Chemicals, GA, USA). The solvent (N,N-dimethylacetamide, DMAc) and co-solvent (ethanol, EtOH) used to dissolve PSF pellets were obtained from Merck (Darmstadt, Germany), Tetrahydrofuran (THF) with purity >99% purchased from QReC (Selangor, Malaysia) was also used as co-solvent during dope solution preparation. The PDMS and PEBAX coating materials were purchased from Sigma-Aldrich, St. Louis, MO, USA and Arkema, PA, USA, respectively. They were used to form a selective layer on the outer surface of hollow fiber membrane. N-hexane obtained from Merck (Darmstadt, Germany) was used to prepare PDMS coating solution.

2.2. Fabrication of Hollow Fiber Membrane

The dope solution employed for the hollow fiber membrane fabrication was composed of 30 wt % PSF, 30 wt % DMAc, 30 wt % EtOH, and 10 wt % THF. Before dissolving in the solvent, the PSF pellets were dried in vacuum oven for one day at 70 °C to completely remove the moisture. The PSF pellets were then slowly added into the solution containing DMAc, EtOH, and THF under mechanical stirring. After the PSF pellets were completely dissolved, the mixture was continuously stirred for another 24 h in order to obtain a homogenous solution. The dope solution was then degassed in ultrasonic bath for 4 h to remove the air bubbles trapped in the solution.
Dry-jet wet phase inversion method was employed in this study to fabricate the PSF hollow fiber membrane and detailed description of the method can be found elsewhere [17,18]. The spinning machine is schematically shown in Figure 1 and the detailed spinning parameters are shown in Table 1. The dope solution was first transferred to a stainless-steel dope reservoir prior to the fabrication process. A gear pump was used to deliver the dope solution from the reservoir to the spinneret, passing through the annular spinneret. Bore fluid composed of distilled water would flow through the center of the spinneret to instigate the solvent/non-solvent exchange between the dope solution and bore fluid, forming lumen as shown in the insertion in Figure 1.
Nascent hollow fiber membrane was formed when it was contacted with large amount of water in the coagulation bath. The hollow fiber was then guided manually to the washing bath before being collected by wind-up drum. The hollow fibers collected from the drum were subjected to two-day immersion in water bath in order to completely remove the solvent residual. Lastly, the hollow fiber membranes were dried in the vacuum oven at 70 °C for one day in order to remove the moisture/residual solvent content. As the solvents from the dope solution are considered hazardous and will eventually be discharged into the drain, post-treatment using solvent absorbents is recommended. However, as our work only dealt with lab-scale membrane fabrication, there is no such treatment process implemented for the time being [19]. For large scale membrane fabrication process by phase inversion method, wastewater treatment process is required in order to treat the effluent containing solvents before being discharged to environment [20].

2.3. Coating of Membrane Surface

In this study, the coating solutions containing either PDMS or PEBAX were prepared at three different concentrations, i.e., 1, 3, and 5 wt % and were used to form a thin coating layer on the outer surface of hollow fiber membrane. To prepare the PDMS coating solution, the PDMS base was first mixed with the predetermined volume of n-hexane solution to obtain the desired weight percentage. The solution was continuously stirred for 2 h followed by 4 h sonication to remove microbubbles trapped in the solution. The dried PSF membranes were then dipped in the PDMS coating solution for 2 min before subjecting to heat treatment (curing step) in an oven at 70 °C for 4 h. The procedures were repeated five times in order to obtain good PDMS coating layer.
To prepare the PEBAX coating solution, PEBAX with specific quantity was first dissolved in a solution composed of distilled water and ethanol at volume ratio of 30:70. The mixture was then stirred at room temperature for 2 h prior before proceeding to the sonication process for 4 h. Similar to PDMS coating technique, the hollow fiber membranes were dipped into the PEBAX solution for 2 min followed by drying at 70 °C for 4 h. Similar to the PDMS coating protocol, the procedures were repeated five times in order to obtain good PEBAX coating layer. It must be noted that during the curing process, the PEBAX-coated fibers had to be kept separately to avoid them from sticking. Table 2 shows the types of the hollow fiber membranes coated with different materials at different concentrations.

2.4. Membrane Characterization

The cross sectional and morphology of the hollow fiber membrane were carefully examined by scanning electron microscope (Hitachi, Tokyo, Japan, S3400N). Prior to analysis, the hollow fiber membranes were cryogenically cracked using liquid nitrogen in order to obtain a clear morphology of the membrane without defect. The samples were then coated with a layer of gold using sputter coating machine (Emitech, East Sussex, UK, SC7620) to improve the surface conductivity [21]. Energy dispersive X-ray (EDX) spectrometer was used to analyze the elements present on the membrane outer surface. The element that can be used to confirm the existence of the coating layer were silicon (Si) for PDMS coating and nitrogen (N) for PEBAX coating. For each membrane sample, the membrane characterization was repeated five times to yield the average results with standard deviation.

2.5. Gas Permeation Study

The gas permeation setup is schematically illustrated in Figure 2. In this study, the gases used for experiment were pure oxygen and nitrogen gas supplied by MegaMount Industrial Gas, Johor, Malaysia with purity >99.99%. Five units of hollow fiber membranes with the length of 23 cm were bundled and placed within the stainless steel membrane housing. The hollow fiber membranes were sealed with dead end manner using epoxy resin (Loctite, Düsseldorf, Germany). The flow arrangement in this study was shell-side feed where the feed gas from the cylinder would diffuse through the outer surface of the hollow fiber membranes and the permeated gas will pass through the lumen of fibers. The permeated gas is connected to a soap bubble flow meter in which the gas permeance could be determined as
P A l = 273.15 × 10 6 Q A Δ P T
where PA/l is the gas permeance (GPU) (Note: 1 GPU = 10−6 cm3 (STP)/cm2 cm Hg), Q is the volumetric flowrate of gas diffuse across the membrane (cm3/s, STP), A is the effective membrane area (cm2), ΔP is the transmembrane pressure (cm Hg), and T is the temperature. The experiments were carried out at room temperature (28 °C) with constant feed pressure of 5 bar. For each membrane sample, the experiments were repeated five times to yield the average results with standard deviation. The membrane selectivity, αA/B describing the ratio of gas pair permeability can be calculated by the pressure normalized flux ratio of oxygen over nitrogen gas.
α A / B = P O 2 P N 2

3. Results and Discussion

3.1. Membrane Morphology

The SEM images for the uncoated PSF membranes fabricated via dry-jet wet phase inversion method are shown in Figure 3. As can be seen, a thin and dense structure can be found at both inner and outer layer of the membrane. Teardrop-like structure is found to dominate the cross-section morphology of the membrane. In addition, spongy-like structure is seen at the section close to the inner part of the membrane. The formation of thin dense structure at the inner and outer layer of the membrane is likely due to the use of high concentration of polymer dope solution (30 wt % PSF) that slows down the solvent/non-solvent exchange due to increased dope viscosity. The formation of the teardrop-like structure meanwhile can be attributed to the use of strong non-solvent (water) in the bore fluid and coagulation bath that promotes aggressive exchange between the solvents in the dope solution and the water [22,23,24].
Figure 4 compares the top surface of PSF hollow fiber membranes coated with PDMS and PEBAX with the uncoated membrane. One can observe that additional layer is formed on the top surface of PDMS- and PEBAX-coated membranes upon coating. With increasing the coating solution concentration from 1 to 5 wt %, the coating layer thickness of PDMS- and PEBAX-coated membranes increases from 0.7 to 1.7 μm and from 0.3 to 1.2 μm, respectively, as shown in Table 3. Meanwhile, Figures S1 and S2 shows the SEM images of membrane top surface coated with concentrations of PDMS and PEBAX solution. Our findings are in good agreement with the previous studies in which increasing the concentration of coating solution increased the coating layer thickness of membranes [25,26].

3.2. Effects of PDMS and PEBAX Coating on Membrane Surface Chemistry

Table 4 shows the EDX results on the surface of PSF hollow fiber membranes coated with different conditions. The area selected for each sample’s surface survey is shown in Figure S3. The detection of carbon, oxygen, and sulphur on the membrane surface can be attributed to the characteristics of the PSF itself that contains subunit of aryl-SO2-aryl. Upon coating with different polymeric materials at various concentrations, the detection of new element corresponding to the coating material can be found. For the PDMS coating, the detection of silicon on the membrane surface is the best indication on the presence of PDMS layer on the membrane surface and the increase in the PDMS coating solution results in higher amount of silicon detected. Similarly, nitrogen corresponding to the PEBAX can only be found in the membranes coated with the PEBAX. As the coating layer becomes thicker with the use of higher concentration of PEBAX solution, higher amounts of nitrogen are found. The increase in the amount of element detected (silicon for the PDMS-coated membrane and nitrogen for the PEBAX-coated membrane) is in good agreement with the increase in the respective coating layer thickness. Nevertheless, it is interesting to note that the thickness for the PEBAX coating is relatively lower than that of PDMS coating at the same concentration. According to Wang et al. [25] and Espositio et al. [26], PEBAX solution is less viscous and has ability to penetrate to the membrane surface pore more easily and form rapid gelation during curing process.

3.3. Effects of Coating on Membrane Performance

The effect of surface coating on the hollow fiber membrane performance with respect to gas permeation and selectivity were evaluated and the results are shown in Figure 5 and Table 5, respectively. The gas permeances of the membranes are in the range of 38–73 GPU for oxygen gas and 10–17 GPU for nitrogen gas. The uncoated membrane shows 62.35 and 15.11 GPU for the oxygen and nitrogen gas, respectively. As a comparison, the PDMS-coated membranes generally show higher gas permeance performance for both oxygen and nitrogen gas. The membrane coated with 1 and 3 wt % PDMS solution demonstrates 70.64 and 73.25 GPU, respectively for oxygen gas and 16.82 and 16.05 GPU, respectively for nitrogen gas.
The membrane coated with optimum concentration of PDMS solution (i.e., PSF-3PDMS) in particular exhibits 17.5% and 11.3% enhancement for oxygen and nitrogen gas permeance, respectively, in comparison to the results shown by the uncoated membrane (i.e., PSF). Results show that the excessive use of PDMS solution could negatively affect the membrane gas permeance. It is because the PSF-5PDMS membrane shows lower oxygen gas permeance than the PSF-1PDMS and PSF-3PDMS membranes. When the membranes are coated with low concentration of PDMS solution, the high affinity of PDMS towards oxygen molecules tends to improve the oxygen gas permeance of membrane without affecting the permeance of nitrogen gas. Coating the membrane surface with highest PDMS concentration however reduces the gas permeance because of increased diffusivity of resistance caused by the thicker PDMS layers formed. Other works have also reported the reduction in gas permeance following the use of high concentration of PDMS coating solution [27,28].
Meanwhile, it is found that the PEBAX-coated membranes in general show lower gas permeance for oxygen and nitrogen than that of uncoated membrane. Our findings are opposite compared to the works carried out by Wahab and Sunarti [29] and Wang et al. [25] in which the membrane gas permeance increased upon PEBAX coating on the flat sheet polymeric membranes. One of the main reasons contributing to the inconsistent findings is the use of membrane in hollow fiber configuration. The PEBAX coating procedure that is normally adopted for flat sheet membrane surface modification seems not effective to form good integrity coating layers on the hollow fiber surface. As PEBAX coating solution (on membrane surface) could experience rapid gelation during the drying process, it makes the fibers sticking together and/or being stuck with drying platform. This, as a result, affects the integrity of coating layer and the membrane performance. In order to tackle the issue, optimization on the PEBAX coating conditions particularly for hollow fiber membrane (circular shape) is required and will be reported in our coming research work.

3.4. Comparison of Oxygen and Nitrogen Gas Separation with Previous Studies

The extensive literature search reveals that many membrane gas separation studies focused on the carbon dioxide related gas separation such as CO2/N2, CO2/O2, and CO2/CH4 [30,31]. To the best of our knowledge, there are very few studies reporting the performance of hollow fiber membranes for oxygen/nitrogen separation. Table 6 summarizes the relevant works that have been previously carried out on the oxygen/nitrogen gas separation using either mixed matrix PSF membranes or membranes coated with PDMS or PEBAX. As can be seen, besides demonstrating higher permeance for oxygen and nitrogen gas, the surface-coated PSF membranes used in this study could still maintain reasonably high gas pair selectivity compared to most of the studies. The enhanced performance can be attributed to the unique structure of the hollow fiber membrane that possesses teardrop-like structure in the membrane cross-section, leading to lower mass transfer resistance for gas molecules. Although the work done by Prajapati et al. [32] showed that the gas pair selectivity of the hollow fiber membrane could be further increased with increasing PDMS concentration from 5 to 20 wt %, significant reduction in permeance was reported. Thus, they suggested that the coating solution concentration should be controlled at less than 5 wt %. Prajapati et al. [32] also suggested to reduce the concentration of toxic solvent (DMAc) during dope solution preparation. It is because by there was little effect on the membrane gas separation performance by reducing the DMAc concentration from 39 to 30 wt %. In order to further improve the coating layer properties of the hollow fiber membrane for gas separation, optimizing the coating solution and its conditions (both fabrication and post-treatment) are required.

4. Conclusions

In this study, the surface properties of the PSF hollow fiber membranes were modified by subjecting the membranes to dip-coating process using either PDMS or PEBAX at different concentrations. Results showed that the membranes coated with PDMS exhibited better permeance and selectivity in oxygen/nitrogen separation process in comparison to the membranes coated with PEBAX. Upon coating with 3 wt % PDMS, the membrane exhibited the best performance, showing permeance of 18.31 and 4.01 GPU for oxygen and nitrogen gas, respectively and recording oxygen/nitrogen selectivity of 4.56. Meanwhile, the best performing PEBAX-coated membrane (1 wt % PEBAX) only showed 12.23 and 3.11 GPU for oxygen and nitrogen gas, respectively and selectivity of 3.94. Although previous research works have shown that the PEBAX coating layer is more selective compared to the PDMS coating layer, contradictory results were obtained in this work. This is likely because the previous works only investigated the effects of PEBAX coating on the flat sheet membranes and when the same conditions were applied to the circular surface of hollow fiber membrane, it led to different results. As a conclusion, PDMS coating is more promising to improve the performance of PSF hollow fiber membrane for oxygen enrichment process compared to the PEBAX coating.

Supplementary Materials

The following are available online at https://www.mdpi.com/2073-4360/10/2/126/s1. Figure S1: Cross sectional SEM image of PSF membrane coated with PDMS concentration of (a) 1 wt % (b) 3 wt % and (c) 5 wt %; Figure S2: Cross sectional SEM image of PSF membrane coated with PEBAX at concentration of (a) 1 wt % (b) 3 wt % and (c) 5 wt %; Figure S3: EDX surface marking for PSF membrane coated with PDMS and PEBAX.

Acknowledgments

The authors would like to thank Mayair Manufacturing (M) Sdn. Bhd. for providing financial support in this work under the Studentship Research Grant (Grant No.: 4464/000) and Universiti Teknologi Malaysia for the research funding provided under Research University Grant (Grant No.: Q.J130000.2546.15H41).

Author Contributions

Kok Chung Chong, Soon Onn Lai and Hui San Thiam conceived and designed the experiments; Kok Chung Chong performed the experiments; Kok Chung Chong, Soon Onn Lai and Woei Jye Lau analyzed the data, Kok Chung Chong, Soon Onn Lai, Woei Jye Lau, Hui San Thiam, Ahmad Fauzi Ismail and Rosyiela Azwa Roslan contributed reagents/materials/analysis tools; Kok Chung Chong wrote most of the paper; Soon Onn Lai and Woei Jye Lau supervised the project and proofread the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Gordon, S.; Mortimer, K.; Grigg, J.; Balmes, J. In control of ambient and household air pollution—How low should we go. Lancet Respir. Med. 2017, 17, 1–2. [Google Scholar] [CrossRef]
  2. Chong, K.C.; Lai, S.O.; Lau, W.J.; Thiam, H.S.; Ismail, A.F.; Zulhairun, A.K. Fabrication and characterization of polysulfone membranes coated with polydimethysiloxane for oxygen enrichment. Aerosol Air Qual. Res. 2016, 1–8. [Google Scholar] [CrossRef]
  3. Hamad Karar, W.S.M.; Hamdi, A.A. Analysis of the factors that affect medical oxygen demand An empirical study at government Hospitals in Khartoum State. IOSR J. Math. 2016, 12, 22–26. [Google Scholar] [CrossRef]
  4. Baskar, P.; Senhilkumar, A. Effects of oxygen enriched combustion on pollution and performance characteristics of a diesel engine. Eng. Sci. Technol. Int. J. 2016, 19, 438–443. [Google Scholar] [CrossRef]
  5. Belaissaoui, B.; Moullec, Y.L.; Hagi, H.; Favre, E. Energy efficiency of oxygen enriched air production technologies: Cryogenic vs. membranes. Sep. Purif. Technol. 2014, 125, 142–150. [Google Scholar] [CrossRef]
  6. Pinnau, I.; Freeman, B.D. Formation and modification of polymeric membrane: Overview. ACS Symp. Ser. 1999, 744, 1–22. [Google Scholar] [CrossRef]
  7. Sanders, D.F.; Smith, Z.P.; Guo, R.; Robeson, L.M.; McGrath, J.E.; Paul, D.R.; Freeman, B.D. Energy-efficient polymeric gas separation membranes for a sustainable future: A review. Polymer 2013, 54, 4729–4761. [Google Scholar] [CrossRef]
  8. Robeson, L.M. The upper bound revisited. J. Membr. Sci. 2008, 320, 390–400. [Google Scholar] [CrossRef]
  9. Kamaruddin, H.D.; Koros, W.J. Some observations about the application of Fick’s first law for membrane separation of multi-component mixture. J. Membr. Sci. 1997, 135, 147–159. [Google Scholar] [CrossRef]
  10. Chong, K.C.; Lai, S.O.; Thiam, H.S.; Teoh, H.C.; Heng, S.L. Recent progress of oxygen/nitrogen separation using membrane technology. J. Eng. Sci. Technol. 2016, 11, 1016–1030. [Google Scholar]
  11. Kiadehi, A.D.; Rahimpour, A.; Jahanshahi, M.; Ghoreyshi, A.A. Novel carbon nano-fibers (CNF)/polysulfone (PSf) mixed matrix membranes for gas separation. J. Ind. Eng. Chem. 2015, 22, 199–207. [Google Scholar] [CrossRef]
  12. Magueijo, A.M.; Anderson, L.G.; Fletcher, A.J.; Shilton, S.J. Polysulfone mixed matrix gas separation hollow fibre membranes filled with polymer and carbon xerogels. Chem. Eng. Sci. 2013, 91, 13–20. [Google Scholar] [CrossRef]
  13. Wahab, M.F.A.; Ismail, A.F.; Shilton, S.J. Studies on gas permeation performance of asymmetric polysulfone hollow fiber mixed matrix membranes using nanosized fumed silica as fillers. Sep. Purif. Technol. 2012, 15, 41–48. [Google Scholar] [CrossRef]
  14. Moaddeb, M.; Koros, W.J. Occlusion of pores of polymeric membranes with colloidal. J. Membr. Sci. 1997, 136, 273–277. [Google Scholar] [CrossRef]
  15. Kim, K.; Ingole, P.G.; Kim, J.; Lee, H. Separation of PEBAX/PEI hollow fiber composite membrane for SO2/CO2/N2 mixed gas. Chem. Eng. J. 2013, 233, 242–250. [Google Scholar] [CrossRef]
  16. Liu, L.; Chakma, A.; Feng, X. CO2/N2 separation by poly(ether block amide) thin film hollow fiber composite membranes. Ind. Eng. Chem. Res. 2005, 44, 6874–6882. [Google Scholar] [CrossRef]
  17. Chong, K.C.; Lai, S.O.; Lee, K.M.; Lau, W.J.; Ismail, A.F.; Ooi, B.S. Characteristic and performance of polyvinylidene fluoride membranes blended with different additives in direct contact membrane distillation. Desalin. Water Treat. 2014, 1, 1–9. [Google Scholar] [CrossRef]
  18. Zulhairun, A.K.; Fachrurrazi, Z.G.; Izwanne, M.; Ismail, A.F. Asymmetric hollow fiber membrane coated with polydimethylsiloxane–metal organic framework hybrid layer for gas separation. Sep. Purif. Technol. 2015, 146, 85–93. [Google Scholar] [CrossRef]
  19. Razali, M.; Didaskalou, C.; Kim, J.F.; Babaei, M.; Drioli, E.; Lee, Y.M.; Szekely, G. Exploring and exploiting the effect of solvent treatment in membrane separations. ACS Appl. Mater. Interfaces 2017, 9, 11279–11289. [Google Scholar] [CrossRef] [PubMed]
  20. Razali, M.; Kim, J.F.; Attfield, M.; Budd, P.M.; Drioli, E.; Lee, Y.M.; Szekely, G. Sustainable wastewater treatment and recycling in membrane manufacturing. Green Chem. 2015, 17, 5196–5205. [Google Scholar] [CrossRef]
  21. Liu, H.B.; Shi, W.Y.; Zhang, Y.F.; Liu, D.Q.; Liu, X.F. Effects of additives on the morphology and performance of PPTA/PVDF in situ blend UF membrane. Polymers 2014, 6, 1846–1861. [Google Scholar] [CrossRef]
  22. Khayet, M.; Garcia-Payo, M.C.; Qusay, F.A.; Zubaidy, M.A. Structural and performance studies of poly(vinyl chloride) hollow fiber membranes prepared at different air gap lengths. J. Membr. Sci. 2009, 330, 30–39. [Google Scholar] [CrossRef]
  23. Farah, E.A.; Lalia, B.S.; Hashaikeh, R. A review on electrospinning for membrane fabrication: Challenges and applications. Desalination 2015, 356, 15–30. [Google Scholar]
  24. Wang, D.; Li, K.; Teo, W.K. Porous PVDF asymmetric hollow fiber membranes prepared with the use of small molecular additives. J. Membr. Sci. 2000, 178, 13–23. [Google Scholar] [CrossRef]
  25. Wang, L.J.; Li, Y.; Li, S.H.; Ji, P.F.; Jiang, C.Z. Preparation of composite poly(ether block amide) membrane for CO2 capture. J. Energy Chem. 2014, 23, 717–725. [Google Scholar] [CrossRef]
  26. Esposito, E.; Clarizia, G.; Bernardo, P.; Jansen, J.C.; Sedláková, Z.; Izák, P.; Curcio, S.; de Cindio, B.; Tasselli, F. Pebax®/PAN hollow fiber membranes for CO2/CH4 separation. Chem. Eng. Process. 2015, 94, 53–61. [Google Scholar] [CrossRef]
  27. Rowe, B.W.; Freeman, B.D.; Paul, D.R. Physical aging of ultrathin glassy polymer films tracked by gas permeability. Polymer 2009, 50, 5565–5575. [Google Scholar] [CrossRef]
  28. Rao, H.X.; Liu, F.N.; Zhang, Z.Y. Oxygen-enriching properties of silicone rubber crosslinked membrane containing cobalt. J. Membr. Sci. 2007, 296, 15–20. [Google Scholar] [CrossRef]
  29. Wahab, M.S.; Sunarti, A.R. Development of PEBAX based membrane for gas separation: A review. Int. J. Membr. Sci. Technol. 2015, 2, 78–84. [Google Scholar]
  30. Khalilinejad, I.; Sanaeepur, H.; Kargari, A. Preparation of poly(ether-6-block amide)/PVC thin film composite membrane for CO2 separation: Effect of top layer thickness and operating parameters. J. Membr. Sci. Res. 2015, 1, 124–129. [Google Scholar]
  31. Ahmadpour, E.; Shamsabadi, A.A.; Behbahani, R.M.; Aghajani, M.; Kargari, A. Study of CO2 separation with PVC/Pebax composite membrane. J. Nat. Gas Sci. Eng. 2004, 21, 518–523. [Google Scholar] [CrossRef]
  32. Prajapati, P.K.; Kansara, A.M.; Singh, P.S. Preparation and characterization of an oxygen permselective polydimethylsiloxane hollow fibre membrane. RSC Adv. 2016, 6, 88943–88953. [Google Scholar] [CrossRef]
  33. Bernado, P.; Jansen, J.C.; Bazzarelli, F.; Tasselli, F.; Fuoco, A.; Izák, P.; Jarmarová, V.; Kačírková, M.; Clarizia, G. Gas transport properties of Pebax®/room temperature ionic liquid gel membranes. Sep. Purif. Technol. 2012, 97, 73–82. [Google Scholar] [CrossRef]
  34. Rahman, M.M.; Filiz, V.; Shishatskiy, S.; Newmann, S.; Khan, M.M.; Abetz, V. PEG functionalized POSS incorporated PEBAX nanocomposite membrane. Procedia Eng. 2012, 44, 1523–1526. [Google Scholar] [CrossRef]
  35. Moradi, M.R.; Chenar, M.P.; Noie, S.H.; Hesampour, M.; Mänttäri, M. PDMS coating of used TFC-RO membranes for O2/N2 and CO2/N2 gas separation applications. Polym. Test. 2017, 63, 101–109. [Google Scholar] [CrossRef]
Figure 1. Schematic diagram of the dry-jet wet phase inversion apparatus setup for PSF hollow fiber membrane fabrication [2].
Figure 1. Schematic diagram of the dry-jet wet phase inversion apparatus setup for PSF hollow fiber membrane fabrication [2].
Polymers 10 00126 g001
Figure 2. Schematic diagram of gas permeation study [2].
Figure 2. Schematic diagram of gas permeation study [2].
Polymers 10 00126 g002
Figure 3. SEM image of uncoated PSF membrane: (a) overall cross section; (b) partial cross section; and (c) top skin layer.
Figure 3. SEM image of uncoated PSF membrane: (a) overall cross section; (b) partial cross section; and (c) top skin layer.
Polymers 10 00126 g003
Figure 4. SEM image of top surface of PSF membrane: (a) uncoated membrane; (b) 1 wt % PDMS coating; and (c) 1 wt % PEBAX coating.
Figure 4. SEM image of top surface of PSF membrane: (a) uncoated membrane; (b) 1 wt % PDMS coating; and (c) 1 wt % PEBAX coating.
Polymers 10 00126 g004
Figure 5. Effect of PDMS and PEBAX coating on the PSF membrane with respect to gas permeance.
Figure 5. Effect of PDMS and PEBAX coating on the PSF membrane with respect to gas permeance.
Polymers 10 00126 g005
Table 1. Spinning parameter of PSF hollow fiber membrane.
Table 1. Spinning parameter of PSF hollow fiber membrane.
Spinning ParameterValue
Spinneret OD/ID (mm/mm)0.6/0.3
Bore liquidDistilled water
Bore liquid temperature (°C)25
Bore liquid flow rate (mL/min)0.3
External coagulantTap water
External coagulant temperature (°C)25
Air gap (cm)30
Room relative humidity (%)55 ± 5
Table 2. Coating conditions for PSF-based hollow fiber membranes.
Table 2. Coating conditions for PSF-based hollow fiber membranes.
Membrane aPDMS Coating (wt %)PEBAX Coating (wt %)
PSF
PSF-1PDMS1
PSF-3PDMS3
PSF-5PDMS5
PSF-1PEBAX1
PSF-3PEBAX3
PSF-5PEBAX5
a The hollow fiber PSF membrane used in this study was composed of 30 wt % PSF, 30 wt % DMAc, 30 wt % EtOH, and 10 wt % THF.
Table 3. Coating thickness for the as spun hollow fiber membranes
Table 3. Coating thickness for the as spun hollow fiber membranes
MembraneThickness (μm)
PSF-1PDMS0.7 ± 0.07
PSF-3PDMS1.1 ± 0.05
PSF-5PDMS1.7 ± 0.06
PSF-1PEBAX0.3 ± 0.10
PSF-3PEBAX0.8 ± 0.09
PSF-5PEBAX1.2 ± 0.14
Table 4. EDX surface mapping result for the as spun hollow fiber membranes.
Table 4. EDX surface mapping result for the as spun hollow fiber membranes.
MembraneTrace Element (at %)
Carbon (C)Oxygen (O)Sulphur (S)Silicon (Si)Nitrogen (N)
PSF79.8417.882.28Not detectedNot detected
PSF-1PDMS79.6715.413.321.60Not detected
PSF-3PDMS78.6015.712.972.72Not detected
PSF-5PDMS70.5723.141.554.74Not detected
PSF-1PEBAX79.6615.343.44Not detected1.56
PSF-3PEBAX78.8315.602.98Not detected2.59
PSF-5PEBAX71.9521.271.80Not detected4.98
Table 5. Effect of PDMS and PEBAX coating on the PSF membrane with respect to gas selectivity.
Table 5. Effect of PDMS and PEBAX coating on the PSF membrane with respect to gas selectivity.
MembraneSelectivity (α)
PSF4.13 ± 0.14
PSF-1PDMS4.20 ± 0.23
PSF-3PDMS4.56 ± 0.15
PSF-5PDMS4.17 ± 0.12
PSF-1PEBAX3.94 ± 0.09
PSF-3PEBAX3.62 ± 0.10
PSF-5PEBAX3.60 ± 0.12
Table 6. Comparison of the surface-coated hollow fiber membrane for oxygen/nitrogen separation.
Table 6. Comparison of the surface-coated hollow fiber membrane for oxygen/nitrogen separation.
MembranePermeance (GPU)Permeability (Barrer)αO2/N2Reference
O2N2O2N2
Pristine PEBAX 15673.301.302.54Bernado et al. [33]
PEG-POSS with 10 wt % PEBAX 15674.291.433.00Rahman et al. [34]
PEG-POSS with 20 wt % PEBAX 15674.571.862.46Rahman et al. [34]
PEG-POSS with 30 wt % PEBAX 15677.142.852.51Rahman et al. [34]
TFC-RO membrane with PDMS21.6546.764.542.102.16Moradi et al. [35]
a PSF with 5 wt % PDMS coating11.0021.011.91Prajapati et al. [32]
a PSF with 10 wt % PDMS coating3.405.951.75Prajapati et al. [32]
a PSF with 15 wt % PDMS coating2.7510.753.91Prajapati et al. [32]
a PSF with 20 wt % PDMS coating2.168.273.83Prajapati et al. [32]
b PSF + 5 wt % CXb c17.895.4113.402.505.36Magueijo et al. [12]
b PSF + 10 wt % CX16.578.7112.402.604.77Magueijo et al. [12]
b PSF + 5 wt % μCX d15.311011.501.607.19Magueijo et al. [12]
PSF-3PDMS (3 wt % PDMS)73.2516.0518.314.014.56In this work
PSF-1PEBAX (1 wt % PEBAX)48.9112.4212.233.113.94In this work
a Hollow fiber membrane made of 22 wt % PSF, 39 wt % DMAc, and 39 wt % THF; b Hollow fiber membrane made of 22 wt % PSF, 32 wt % DMAc, 32 wt % THF, and 14% EtOH; c Cx is the abbreviation for aerogel; d μCx is the abbreviation for microaerogel.

Share and Cite

MDPI and ACS Style

Chong, K.C.; Lai, S.O.; Lau, W.J.; Thiam, H.S.; Ismail, A.F.; Roslan, R.A. Preparation, Characterization, and Performance Evaluation of Polysulfone Hollow Fiber Membrane with PEBAX or PDMS Coating for Oxygen Enhancement Process. Polymers 2018, 10, 126. https://doi.org/10.3390/polym10020126

AMA Style

Chong KC, Lai SO, Lau WJ, Thiam HS, Ismail AF, Roslan RA. Preparation, Characterization, and Performance Evaluation of Polysulfone Hollow Fiber Membrane with PEBAX or PDMS Coating for Oxygen Enhancement Process. Polymers. 2018; 10(2):126. https://doi.org/10.3390/polym10020126

Chicago/Turabian Style

Chong, Kok Chung, Soon Onn Lai, Woei Jye Lau, Hui San Thiam, Ahmad Fauzi Ismail, and Rosyiela Azwa Roslan. 2018. "Preparation, Characterization, and Performance Evaluation of Polysulfone Hollow Fiber Membrane with PEBAX or PDMS Coating for Oxygen Enhancement Process" Polymers 10, no. 2: 126. https://doi.org/10.3390/polym10020126

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop