Next Article in Journal
Application of Image Analysis to Identify Quartz Grains in Heavy Aggregates Susceptible to ASR in Radiation Shielding Concrete
Next Article in Special Issue
Binary Alkali-Metal Silicon Clathrates by Spark Plasma Sintering: Preparation and Characterization
Previous Article in Journal
The Influence of Crosslink Density on the Failure Behavior in Amorphous Polymers by Molecular Dynamics Simulations
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis and Structural Characterization of the New Clathrates K8Cd4Ge42, Rb8Cd4Ge42, and Cs8Cd4Ge42

Department of Chemistry and Biochemistry, University of Delaware, Newark, DE 19716, USA
*
Author to whom correspondence should be addressed.
Materials 2016, 9(4), 236; https://doi.org/10.3390/ma9040236
Submission received: 3 March 2016 / Revised: 17 March 2016 / Accepted: 21 March 2016 / Published: 25 March 2016
(This article belongs to the Special Issue Inorganic Clathrate Materials)

Abstract

:
This paper presents results from our exploratory work in the systems K-Cd-Ge, Rb-Cd-Ge, and Cs-Cd-Ge, which yielded the novel type-I clathrates with refined compositions K8Cd3.77(7)Ge42.23, Rb8Cd3.65(7)Ge42.35, and Cs7.80(1)Cd3.65(6)Ge42.35. The three compounds represent rare examples of clathrates of germanium with the alkali metals, where a d10 element substitutes a group 14 element. The three structures, established by single-crystal X-ray diffraction, indicate that the framework-building Ge atoms are randomly substituted by Cd atoms on only one of the three possible crystallographic sites. This and several other details of the crystal chemistry are elaborated.

Graphical Abstract

1. Introduction

Clathrates of silicon and germanium with the alkali metals have been known now for almost half a century [1]. The idea of phonon-glass electron-crystal (PGEC), coined by G. Slack [2], succinctly captures the two most important structural features of these clathrates: rigid open frameworks, made up of covalently bonded atoms, and guest atoms residing in the large cages. The stable frameworks contribute to the favorable carrier mobilities, while the filler atoms that vibrate (or “rattle”, as is frequently said) in the oversized cages are believed to be the reason for the low lattice thermal conductivity exhibited by many clathrates. Therefore, this class of compounds has gained interest for their prospects as thermoelectric materials [2,3,4,5].
Most studied clathrate compounds are based on the group 14 elements Si, Ge, and Sn (Tt). These atoms form extended networks adopting several different structure types. Fractions of the framework atoms can be substituted by group 13 and 12 elements, as well as late transition metals (M), which can be stabilized in tetrahedral coordination. There are large cages in the clathrate structures, which are partially or fully occupied by guest atoms (A). The typical guest atoms are alkali metals, alkaline earth metals, or Ce and Eu from the rare earth metals [6,7,8,9,10].
This paper deals with three new clathrate phases with compositions K8Cd3.77(7)Ge42.23, Rb8Cd3.65(7)Ge42.35, and Cs7.80(1)Cd3.65(6)Ge42.35, which adopt the type-I structure (Figure 1). The nominal formula for this structure is A8(Cd,Ge)46, and it boasts cages of 20- and 24-atoms. Here, we would like to mention that numerous clathrates of germanium with the alkali metals are known as of today, but this study is among very few to identify cadmium as a substituent of germanium-based clathrates—the quaternary phase K6Eu2Cd5Ge41 appears to be the only report of similar chemistry so far [11]. The corresponding systems K-M-Ge and Rb-M-Ge with M being the group 12 elements Zn and Hg have already been explored, and the structures of the type-I clathrates K8Zn4Ge42 [12], K8Hg3.19Ge42.81, and Rb8Hg3.03Ge42.97 [13] have been published.

2. Results

2.1. Crystallographic Analysis

The structure solutions and refinements proceeded in a straightforward manner (Table 1), and only a few details deserve special mention. First, the contrast between the X-ray atomic scattering factors of Cd and Ge is significant, allowing precise refinements of the site occupation factors should there be mixed-occupied sites. Indeed, in all cases, when the occupancies of the framework sites were first freely refined (individually, while the remaining ones were kept fixed), it was noted that the occupation factors for 16i and 24k sites did not deviate from 100%, while sites 6c in all three structures appeared to be “heavier”. This indicates that Cd (Z = 48) and Ge (Z = 32) co-occupy framework site 6c only (in a ratio ca. 60% Cd, 40% Ge). Such distribution of group 12 and group 14 elements is consistent with the published refinements for K8Hg3.19Ge42.81 and Rb8Hg3.03Ge42.97 [13], K8Zn3.46Si42.54 and Rb7.86Zn3.63Si42.37 [14], and K8Zn3.78Sn42.22, Rb8Zn3.52Sn42.48, and Cs8Zn3.44Sn42.56 [15]. If one considers the alkaline earth clathrates, such as Ba8Zn7Si39 [16], the 6c site is also mostly occupied by Zn (77% Zn, 23% Si), with the remainder of the Zn found at 24k (9% Zn, 91% Si).
Notice that, in all three structures, the Zintl-Klemm concept [17], which appears to be followed by many other clathrates [8], is not completely satisfied by the above-mentioned compounds. For instance, based on the rationalization [A+]8[M2−]4[Tt0]42, one should expect the structural formulae to be A8M4Tt42 (A = alkali metal, M = Zn, Cd, Hg; Tt = tetrel, or Si, Ge, Sn). The same holds true for Ba8Zn8Si38 (=[Ba2+]8[Zn2−]8[Si0]38). The reasons for the slightly lower refined content of Zn, Cd, or Hg are not yet understood. This would mean, however, that all these materials are metallic conductors, not semiconductors, as expected from the Zintl-Klemm concept. One might argue that the structures have both Cd/Ge positional disorder and defects on the 6c sites, i.e., in analogy with Ba8ZnxGe46–xyy and Ba8CdxGe46–xyy (☐ = vacancy) [18,19]. This certainly is a valid argument, which warrants further investigations. We will note here that, while for Ba8ZnxGe46–xyy and Ba8CdxGe46–xyy the hypothesis for vacancies in the framework had been supported by the low occupation factors and elongated displacement parameters of the atoms neighboring the defects, none of these indicators of additional structural disorder are observed for the herein discussed structures.
We also need to mention the fact that when checking the occupancies of the guest atoms in the reported structures 1 and 2, they did not deviate from full. However, when the occupancies of the Cs sites in 3 were checked, it became obvious that site 2a is underoccupied (occupation factor 89.8(4)%). This is the center of the smaller pentagonal dodecahedral cage in the type-I clathrate, which might be not large enough to accommodate the very large Cs atom. Therefore, 3 is the only structure without 100% filled cages, refined as Cs7.80(1)Cd3.65(6)Ge42.35. To help the reader of this article appreciate the subtleties of the refinements Cs7.80(1)Cd3.65(6)Ge42.35 vs. Cs8Cd3.65(6)Ge42.35, the .CIF for the latter is provided as supporting evidence (please see the supplementary electronic information associated with this article). Despite the respectable residuals, quick convergence and quite reasonable anisotropic displacement parameters, the relatively deep hole in the difference electron density map (the Fourier synthesis indicates a hole of 4 e3 just 0.2 Å away from Cs2) is a telling sign that the respective position is not fully occupied. Indeed, when the occupation factor of Cs2 is freed, the difference Fourier map flattens out completely (Table 1 and Table 2).
Lastly, while commenting on the size of the guest atoms and the clathrate cages, we should point the attention to the anisotropic displacement parameter of K1 in structure 1, site 6d (Table 3). This atom is at the center of the larger tetrakaidecahedral cage (Figure 2). The size/shape of the thermal ellipsoid is not dependent on the site occupation factor (deviates from unity less than 3σ). The equivalent isotropic displacement parameter for K1 is, by far, the largest of all. Its slightly oblate shape may hint at off-centering (Table 3), but such positional disorder is very small and could not be resolved from the available crystallographic data. For comparison, the disorder in the type-I clathrates of tin, where the tetrakaidecahedral cages are even larger, is easily modeled from data collected on an in-house diffractometer [20,21,22]. Sr8Ga16Ge30 and Ba8Ga16Ge30 are other well-known examples of filler atoms being off-centered from their equilibrium positions, and both structures have been worked out from synchrotron and neutron diffraction data [23,24,25].

2.2. Structural Metrics

As seen in Table 1, the unit cell parameters of the three cubic type-I clathrates (space group Pm 3 ¯ n (No. 223)) increase from a = 10.8710(4) Å for K8Cd3.77(7)Ge42.23, to a = 10.9099(5) Å for Rb8Cd3.65(7)Ge42.35, to a = 10.9643(7) Å for Cs7.80(1)Cd3.65(6)Ge42.35. This increase can be attributed to the increase in size of the alkali metal atoms (rK ≈ 2.03 Å, rRb ≈ 2.16 Å, rCs ≈ 2.35 Å, according to Pauling [26]). The small deviations in the refined Cd content must also have an effect on the unit cell volumes, but it is expected to be subtle (the difference in the refined Cd content is less than 2σ). Notice, however, that in the single-bonded Pauling radii for the Cd and Ge are quite different, rGe ≈ 1.24 Å, rCd ≈ 1.38 Å [26], and, as a result, the Cd substitutions to the Ge-based framework result in enlargement of the unit cell, clearly seen by comparing our data with the data for the known binary type-I clathrates K8Ge442 [27] and Cs8Ge442 [28], which have periodicity constants of a = 10.686(4) Å and a = 10.8238(2) Å, respectively. Of course, the presence of vacancies in the framework for K8Ge442 and Cs8Ge442 (☐ = vacancy) should not be overlooked, as it contributes to the contraction of the unit cell. Given that Cd and In are neighboring elements in the periodic chart with similar atomic radii (rIn ≈ 1.42 Å [26]), it is no surprise that the type-I clathrates from the systems K-In-Ge, Rb-In-Ge, and Cs-In-Ge show similar characteristics. The unit cell parameters of the latter increase are in the following order: a = 10.997(2) Å for K8In8.14Ge37.86; a = 11.033(2) Å for Rb8In7.81Ge38.19; a = 11.079(2) Å for Cs8In8.22Ge37.78 [29,30]. Another relevant comparison can be made between K8Cd3.77(7)Ge42.23 on the one hand, and K8Zn4Ge42 and K8Hg3.19Ge42.81 on the other [12,13]. The atomic size of Zn is slightly smaller than that of Cd (rZn ≈ 1.21 Å [26]), hence the smaller unit cell parameter for K8Zn4Ge42 (a = 10.7488(1) Å) [12]. Mercury and cadmium are very similar in size (rCd ≈ 1.38 Å; rHg ≈ 1.39 Å [26]), but the refined Hg content in K8Hg3.19Ge42.81 is lower that the Cd content in K8Cd3.77(7)Ge42.23, hence the smaller unit cell parameter for the former (a = 10.8489(13) Å) [13]. The same is true for Rb8Cd3.65(7)Ge42.35 (2) vs. Rb8Hg3.03Ge42.97 (a = 10.8750(13) Å [13]).
The net result of the substitution of the larger Cd for the smaller Ge is a small increase in the cage sizes, and therefore an expansion of the unit cells (vide supra). This can be also observed in the atomic distances (see Table 4), which fall in the intervals of dGe–Ge = 2.4931(4) to 2.52(1) Å for 1, dGe–Ge = 2.5029(4) to 2.539(1) Å for 2, and dGe–Ge = 2.5118(4) to 2.570(1) Å for 3, respectively. Notice that, since Cd substitutes only at the 6c site, Cd-Cd contacts are avoided. This site only neighbors Ge1 and the corresponding dCd/Ge3-Ge1 distances monotonically increase in the following order: 2.5858(6) Å for 1, 2.5912(5) Å for 2, and 2.6019(5) Å for 3, respectively. The distances from the guest atoms in the cages to the framework follow the same trend (Table 4).

3. Discussion

In 2014, we reported for the very first time the occurrence of the type-I and type-II clathrates Rb5.20Na2.80(4)Zn3.85Si42.15(2) and Rb8Na16Zn8.4Si127.6(1) [31]. Shortly after, another team reported the structure determination for K8Zn3.46Si42.54 and Rb7.86Zn3.63Si42.37 [14]. Subsequently, we set out to synthesize the Cd-analogs of these compounds, but these studies did not yield any clathrates.
As a result, we turned our attention to the germanium clathrates. We noticed that there were prior reports on K8Zn4Ge42 and the mixed-cation KxBa8–xZnyGe46–y [12]. K8Hg3.19Ge42.81 and Rb8Hg3.03Ge42.97 [13] have also been known for some time. The mixed-cation clathrates K6Eu2(Zn or Cd)5Ge41 also appear in the literature [11], but the corresponding crystallographic information is not available from the ICSD.
Given that mercury and cadmium are very similar in size, we thought it was surprising that the corresponding K-Cd-Ge, Rb-Cd-Ge, and Cs-Cd-Ge systems had not been carefully explored. This work fills this gap in the literature by detailing the structures of the type-I clathrates K8Cd3.77(7)Ge42.23, Rb8Cd3.65(7)Ge42.35, and Cs7.80(1)Cd3.65(6)Ge42.35. However, the latter clathrate phases are always co-crystallizing with small amounts of secondary phases, irrespective of the tried different synthesis routes. As mechanical separation was not achievable either, measurements of the transport properties could not be performed.
In further investigations, we will aim to resolve the synthetic problems leading to impurity phases and study the transport properties. One of our more distant goals will be to explore the systems Cs-Na-Cd-Ge and Rb-Na-Cd-Ge. The mixed cations (large and small) can prove promising for synthesizing the hitherto unknown Cs8Na16Cd12Ge124 and Rb8Na16Cd12Ge124 type-II clathrates. We will recall that the crystal chemistry and the chemical bonding in many type-I clathrate structures are satisfactorily understood because they are more easily accessible in ternary systems. For type-II clathrates, the difficulty of synthesizing selectively new compounds remains an open challenge, which has been attributed to the fact that the cavities of the type-II clathrates have a larger difference in size. Therefore, we have speculated (and have shown experimentally on the examples of (Cs or Rb)8Na16(Si or Ge)136 [32]) that the directed synthesis of type-II can be greatly facilitated by choosing spatially different guest atoms. This idea, combined with the proper choice of a framework-substituent, can lead to new clathrate type-II, as demonstrated by the subsequent studies on Cs8Na16Ag6.7Ge129.3 [33] and Cs8Na16Cu5Ge131 [34]. Very recently, the applicability of notion that two types of different guest atoms will be preferred for the complete and ordered filling of both cavities in the type-II compounds was confirmed for the tin-based Cs8Ba16Ga39.7Sn96.3 and Rb9.9Ba13.3Ga36.4Sn99.6 [35], suggesting that the Cs-Ba-Cd-Ge and Rb-Ba-Cd-Ge systems are worthy candidates for further investigations.

4. Materials and Methods

4.1. Synthesis

The syntheses were carried out by loading stoichiometric mixtures of the respective elements in suitably prepared Nb tubes, which were then sealed by arc-welding.
Due to the extremely high reactivity of the alkali metals to moisture and oxygen, all manipulations were done with great care in an argon-filled glove box. The atmosphere in the glovebox was maintained at O2/H2O level below 1 ppm. The elements were purchased from Alfa or Sigma-Aldrich with a stated purity higher than 99.9 wt % (metal basis). In order to carry out the reactions in a safe and reliable manner, the elements were weighed in a ratio of A:M:Ge = 8:4:42 (A = K, Rb, Cs). Total mass in each case was ca. 300 mg. After arc-welding, the Nb tubes with the reactants inside were enclosed in fused silica tubes. Under dynamic vacuum, the fused silica tubes were baked and then flame-sealed.
The samples were heated slowly in programmable muffle furnaces to 950 °C with a rate of 10 °C/h, annealed for 15 h, and then cooled down (rate −150 °C/h) to 650 °C, dwelled for 4 d, and cooled down (rate −5 °C/h) to room temperature. The obtained type-I clathrates were stable in air and moisture and were handled on the bench. Based on the powder X-ray diffraction patterns, the yields were high, estimated to be over 70–80 wt %, with some small impurity phases, yet unidentified, present in each specimen.

4.2. Powder X-ray Diffraction

X-ray powder diffraction patterns of selected crystals were carried out at room temperature on a Rigaku MiniFlex powder diffractometer using Cu-Kα radiation. The data collection scans were done in θ-θ mode (2θmax = 65°) with a step of 0.05° and 2 s/step counting time. The data were analyzed with the JADE 6.5 software package. The intensities and the positions of the experimentally observed peaks and those calculated based on the corresponding single-crystal structures matched very well with one another.

4.3. Single-Crystal X-ray Diffraction

Single-crystal X-ray diffraction data were collected on a Bruker CCD-based diffractometer using graphite-monochromated Mo-Kα radiation (λ = 0.71073 Å). Temperature was maintained at 200(2) K. Suitable single-crystals from each compound were selected and cut to smaller dimensions (less than 0.1 mm) under mineral oil. The SMART [36] and SAINTplus [37] programs were used for the data collection, integration, and the global unit cell refinement from all data. Semi-empirical absorption correction based on equivalent reflections was applied with SADABS [38]. The structures were refined to convergence by full-matrix least-square methods on F2, as implemented in SHELXTL [39]. All sites were refined with anisotropic displacement parameters.
Selected details of the data collections and structure refinement parameters are listed in Table 1. The atomic coordinates and equivalent isotropic displacement parameters are given in Table 2. The anisotropic displacement parameters are tabulated in Table 3, and selected interatomic distances are summarized in Table 4. Additional details of the crystal structure analyses may be requested from the Fachinformationszentrum Karlsruhe, D-76344 Eggenstein-Leopoldshafen (Karlsruhe, Germany) on quoting the depository numbers CSD-430998 for K8Cd3.77(7)Ge42.23, CSD-430999 for Rb8Cd3.65(7)Ge42.35, and CSD-431000 for Cs7.80(1)Cd3.65(6)Ge42.35, respectively.

4.4. Energy-Dispersive Analysis

Multiple crystals for each composition were analyzed by means of energy dispersive X-ray spectroscopy (EDX). Data were gathered using a JEOL 7400F electron microscope equipped with an INCA-OXFORD energy-dispersive spectrometer. Only the specified elements (i.e., no unrecognized impurities) could be detected in ratios consistent with the refined compositions.

5. Conclusions

With this paper, our team presented the synthesis and the structural characterization of the type-I clathrates K8Cd3.77(7)Ge42.23, Rb8Cd3.65(7)Ge42.35, and Cs7.80(1)Cd3.65(6)Ge42.35. In the future, we will be exploring the systems Cs-Na-Cd-Ge and Rb-Na-Cd-Ge. Based on the presented results and the overview of the current literature, we believe that using mixed cations (large and small) can yield the hitherto unknown Cs8Na16Cd12Ge124 and Rb8Na16Cd12Ge124 type-II clathrates.

Supplementary Materials

The following are available online at www.mdpi.com/1996-1944/9/4/236/s1. Structure refinement for Cs8Cd3.65(6)Ge42.35, in .CIF.

Acknowledgments

Svilen Bobev acknowledges financial support from the U.S. Department of Energy, Office of Science, Basic Energy Sciences, under Award DE-SC0008885.

Author Contributions

Marion C. Schäfer and Svilen Bobev conceived and designed the experiments; Marion C. Schäfer performed the experiments; Marion C. Schäfer and Svilen Bobev analyzed the data; Svilen Bobev wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest. The funding sponsors had no role in the design of the study, in the collection, analyses, or interpretation of data, in the writing of the manuscript, or in the decision to publish the results.

Abbreviations

The following abbreviations are used in this manuscript:
PGEC
Phonon-Glass Electron-Crystal
Tt
Tetrel, group 14 elements Si, Ge and Sn
A
group 1, 2 and 3 elements, which partially or fully occupy the cages within the clathrate framework
M
group 13 and 12 elements, as well as late transition metals, substituting framework atoms
vacancy

References

  1. Kasper, J.S.; Hagenmuller, P.; Pouchard, M.; Cros, C. Clathrate structure of silicon Na8Si46 and NaxSi136 (x < 11). Science 1965, 150, 1713–1714. [Google Scholar] [PubMed]
  2. Slack, G.A. New materials and performance limits for thermoelectric cooling. In CRC Handbook of Thermoelectrics; Rowe, D.M., Ed.; CRC Press: Boca Raton, FL, USA, 1995; pp. 407–440. [Google Scholar]
  3. Christensen, M.; Johnson, S.; Iversen, B.B. Thermoelectric clathrates of type-I. Dalton Trans. 2010, 39, 978–992. [Google Scholar] [CrossRef] [PubMed]
  4. Nolas, G.S.; Cohn, J.L.; Slack, G.A.; Schjuman, S.B. Semiconducting Ge clathrates: Promising candidates for thermoelectric applications. Appl. Phys. Lett. 1998, 73, 178–180. [Google Scholar] [CrossRef]
  5. Sales, B.C.; Chakoumakos, B.C.; Mandrus, D.; Sharp, J.W. Atomic displacement parameters and the lattice thermal conductivity of clathrate-like thermoelectric compounds. J. Solid State Chem. 1999, 146, 528–532. [Google Scholar] [CrossRef]
  6. Bobev, S.; Sevov, S.C. Clathrates of group 14 with alkali metals: An exploration. J. Solid State Chem. 2000, 153, 92–105. [Google Scholar] [CrossRef]
  7. Beekman, M.; Nolas, G.S. Inorganic clathrate-II materials of group 14: Synthetic routes and physical properties. J. Mater. Chem. 2008, 18, 842–851. [Google Scholar] [CrossRef]
  8. Shevelkov, A.V.; Kovnir, K. Zintl clathrates. In Structure and Bonding; Springer: Berlin, Germany, 2011; Volume 990, pp. 97–142. [Google Scholar]
  9. Paschen, S.; Carrillo Cabrera, W.; Bentien, A.; Tran, V.H.; Baenitz, M.; Grin, Y.; Steglich, F. Structural, transport, magnetic and thermal properties of Eu8Ga16Ge30. Phys. Rev. B 2001, 64. [Google Scholar] [CrossRef]
  10. Prokofiev, A.; Sidorenko, A.; Hradil, K.; Ikeda, M.; Svagera, R.; Waas, M.; Winkler, H.; Neumaier, K.; Paschen, S. Thermopower enhancement by encapsulating cerium in clathrate cages. Nat. Mater. 2013, 12, 1096–1101. [Google Scholar] [CrossRef] [PubMed]
  11. Paschen, S.; Budnyk, S.; Köhler, U.; Prots, Y.; Hiebl, K.; Steglich, F.; Grin, Y. New type-I clathrates with ordered Eu distribution. Physica. B 2006, 383, 89–92. [Google Scholar] [CrossRef]
  12. Kishimoto, K.; Sasaki, Y.; Koyanagi, T.; Ohoyama, K.; Akai, K. Crystal structure and thermoelectric properties of KxBa8–xZnyGe46–y clathrates. J. Appl. Phys. 2012, 111. [Google Scholar] [CrossRef]
  13. Kaltzoglou, A.; Ponou, S.; Faessler, T.F. A4Ge9 (A = K, Rb) as precursors for Hg-substituted clathrate-I synthesis: Crystal structure of A8Hg3Ge43. Eur. J. Inorg. Chem. 2008, 29, 4507–4510. [Google Scholar] [CrossRef]
  14. Baran, V.; Faessler, T.F. Si-based clathrates with partial substitution by Zn and Ga: K8Zn3.5Si42.5, Rb7.9Zn3.6Si42.4, and Cs8–xGa8–ySi38+y. Z. Anorg. Allg. Chem. 2015, 641, 1435–1443. [Google Scholar] [CrossRef]
  15. Schäfer, M.C.; Bobev, S. Copper and zinc substitutions in clathrates of tin: Synthesis, structural characterization, and physical properties of A8Cu2.67Sn43.33 and A8Zn4Sn42 (A = K, Rb, Cs) with the type-I structure. Chem. Mater. 2013, 25, 3737–3744. [Google Scholar] [CrossRef]
  16. Nasir, N.; Grytsiv, A.; Melnychenko-Koblyuk, N.; Rogl, P.; Bauer, E.; Lackner, R.; Royanian, E.; Giester, G.; Saccone, A. Clathrates Ba8{Zn,Cd}xSi46–x, x~7: Synthesis, crystal structure and thermoelectric properties. J. Phys. 2009, 21, 385404. [Google Scholar] [CrossRef] [PubMed]
  17. Kauzlarich, S.M. Chemistry, Structure, and Bonding of Zintl. Phases and Ions; VCH: New York, NY, USA, 1996. [Google Scholar]
  18. Melnychenko-Koblyuk, N.; Grytsiv, A.; Fornasari, L.; Kaldarar, H.; Michor, H.; Roehrbacher, F.; Koza, M.; Royanian, E.; Bauer, E.; Rogl, P.; et al. Ternary clathrates Ba–Zn–Ge: Phase equilibria, crystal chemistry and physical properties. J. Phys. Condens. Matter. 2007, 19, 216223. [Google Scholar] [CrossRef]
  19. Melnychenko-Koblyuk, N.; Grytsiv, A.; Berger, S.T.; Kaldarar, H.; Michor, H.; Roehrbacher, F.; Royanian, E.; Bauer, E.; Rogl, P.; Schmid, H.; et al. Ternary clathrates Ba-Cd-Ge: Phase equilibria, crystal chemistry and physical properties. J. Phys. Condens. Matter. 2007, 19, 046203. [Google Scholar] [CrossRef]
  20. Schäfer, M.C.; Bobev, S. K and Ba distribution in the structures of the clathrate compounds KxBa16−x(Ga,Sn)136 (x = 0.8, 4.4, and 12.9) and KxBa8−x(Ga,Sn)46 (x = 0.3). Acta. Cryst. 2013, C69, 319–323. [Google Scholar] [CrossRef] [PubMed]
  21. Schäfer, M.C.; Yamasaki, Y.; Fritsch, V.; Bobev, S. Ternary compounds in the Sn-rich section of the Ba-Ga-Sn system: Ba8Ga16–xSn30+x (1.1 ≤ x ≤ 2.8) clathrates of type-I and type-VIII, and BaGa2–xSn4+x (x ≈ 0.2) with a clathrate-like structure. Crystals 2011, 1, 145–162. [Google Scholar] [CrossRef]
  22. Von Schnering, H.-G.; Carillo-Cabrera, W.; Kröner, R.; Peters, E.-M.; Peters, K. Crystal structure of the clathrate β-Ba8Ga16Sn30. Z. Kristallogr. New Cryst. Struct. 1998, 213, 679. [Google Scholar]
  23. Chakoumakos, B.C.; Sales, B.C.; Mandrus, D.; Nolas, G.S. Structural disorder and thermal conductivity of the semiconducting clathrate Sr8Ga16Ge30. J. Alloys Compd. 2000, 296, 80–86. [Google Scholar] [CrossRef]
  24. Chakoumakos, B.C.; Sales, B.C.; Mandrus, D. Structural disorder and magnetism of the semiconducting clathrate Eu8Ga16Ge30. J. Alloys Compd. 2001, 322, 127–134. [Google Scholar] [CrossRef]
  25. Nolas, G.S.; Weakley, T.J.R.; Cohn, J.L.; Sharma, R. Structural properties and thermal conductivity of crystalline Ge clathrates. Phys. Rev. B 2000, 61, 3845–3850. [Google Scholar] [CrossRef]
  26. Pauling, L. The Nature of the Chemical Bonding, 3rd ed.; Cornell University Press: Ithaca, NY, USA, 1960; p. 403. [Google Scholar]
  27. Von Schnering, H.-G.; Llanos, J.; Peters, K.; Baitinger, M.; Grin, Y.; Nesper, R. Refinement of the crystal structure of K8Ge442, an intermetallic clathrate I. Z. Kristallogr. New Cryst. Struct. 2011, 226, 9–10. [Google Scholar]
  28. Veremchuk, I.; Wosylus, A.; Boehme, B.; Baitinger, M.; Borrmann, H.; Prots, Yu.; Burkhardt, U.; Schwarz, U.; Grin, Y. Preparation and crystal structure of the clathrate-I Cs8–xGe44+y2–y. Z. Anorg. Allg. Chem. 2011, 637, 1281–1286. [Google Scholar] [CrossRef]
  29. Von Schnering, H.-G.; Menke, H.; Kroener, R.; Peters, E.M.; Peters, K.; Nesper, R. Crystal structure of the clathrates Rb8In8Ge38 and K8In8Ge38. Z. Kristallogr. New Cryst. Struct. 1998, 213, 673–674. [Google Scholar]
  30. Menke, H.; Carrillo Cabrera, W.; Peters, K.; Peters, E.M.; von Schnering, H.-G. Crystal structure of the clathrate Cs8In8Ge38. Z. Kristallogr. New Cryst. Struct. 1999, 214, 14. [Google Scholar] [CrossRef]
  31. Schäfer, M.C.; Bobev, S. New type-I and type-II clathrates in the systems Cs–Na–Ga–Si, Rb–Na–Ga–Si, and Rb–Na–Zn–Si. Inorganics 2014, 2, 79–95. [Google Scholar] [CrossRef]
  32. Bobev, S.; Sevov, S.C. Synthesis and characterization of stable stoichiometric clathrates of silicon and germanium: Cs8Na16Si136 and Cs8Na16Ge136. J. Am. Chem. Soc. 1999, 121, 3795–3796. [Google Scholar] [CrossRef]
  33. Beekman, M.; Wong-Ng, W.; Kaduk, J.A.; Shapiro, A.; Nolas, G.S. Synthesis and single-crystal X-ray diffraction studies of new framework substituted type II clathrates, Cs8Na16AgxGe136−x (x < 7). J. Solid State Chem. 2007, 180, 1076–1082. [Google Scholar]
  34. Beekman, M.; Kaduk, J.A.; Gryko, J.; Wong-Ng, W.; Shapiro, A.; Nolas, G.S. Synthesis and characterization of framework-substituted Cs8Na16Cu5Ge131. J. Alloys Compd. 2009, 470, 365–368. [Google Scholar] [CrossRef]
  35. Schäfer, M.C.; Bobev, S. Novel tin clathrates with the type-II structure. J. Am. Chem. Soc. 1999, 121, 3795–3796. [Google Scholar]
  36. SMART NT, version 5.63. Bruker Analytical X-ray Systems Inc.: Madison, WI, USA, 2003.
  37. SAINT NT, version 6.45. Bruker Analytical X-ray Systems Inc.: Madison, WI, USA, 2003.
  38. SADABS NT, version 2.10. Bruker Analytical X-ray Systems Inc.: Madison, WI, USA, 2001.
  39. SHELXTL, version 6.12. Bruker Analytical X-ray Systems Inc.: Madison, WI, USA, 2001.
Figure 1. Schematic view of the clathrate with type-I structure. For the drawing, the structural information for Cs7.80(1)Cd3.65(6)Ge42.35 was used and the atoms are labeled accordingly.
Figure 1. Schematic view of the clathrate with type-I structure. For the drawing, the structural information for Cs7.80(1)Cd3.65(6)Ge42.35 was used and the atoms are labeled accordingly.
Materials 09 00236 g001
Figure 2. Representative fragment of the K8Cd3.77(7)Ge42.23 structure, drawn with thermal ellipsoids at the 98% probability level. Ueq (as one third of the trace of the orthogonalized Uij tensor) for K1 is more than twice that of K2, hinting at small vibrations about the equilibrium position.
Figure 2. Representative fragment of the K8Cd3.77(7)Ge42.23 structure, drawn with thermal ellipsoids at the 98% probability level. Ueq (as one third of the trace of the orthogonalized Uij tensor) for K1 is more than twice that of K2, hinting at small vibrations about the equilibrium position.
Materials 09 00236 g002
Table 1. Selected crystal data and structure refinement parameters for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
Table 1. Selected crystal data and structure refinement parameters for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
Compound123
Fw/g·mol−13803.24170.24519.1
Crystal systemCubic
Space groupPm 3 ¯ n (No. 223), Z = 1
a10.8710(4)10.9099(5)10.9643(7)
V31284.72(8)1298.56(10)1318.08(15)
T/K200(2)
RadiationMo Kα, λ = 0.71073 Å
ρ/g·cm−34.925.335.69
μ/cm−1264.3329.7304.7
data/restraints/parameters291/0/17318/0/17327/0/18
R1 (I >2σ(I)) a0.01820.01780.0138
wR2 (I >2σ(I)) a0.03590.03650.0298
R1 (all data) a0.02410.02320.0180
wR2 (all data) a0.03780.03860.0314
GOF1.1561.0641.116
largest peak & hole/e·Å−30.54 & −0.570.62 & −0.850.63 & −0.56
a R1 = ∑||Fo| – |Fc||/∑|Fo|; wR2 = [∑[w(Fo2 – Fc2)2]/∑[w(Fo2)2]]1/2, where w = 1/[σ2Fo2 + (A·P)2 + (B·P)], and P = (Fo2 + 2Fc2)/3, A and B weight coefficients.
Table 2. Atomic coordinates and equivalent isotropic displacement parameters (Ueq2) for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
Table 2. Atomic coordinates and equivalent isotropic displacement parameters (Ueq2) for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
AtomSitex/ay/bz/cOccupancyUeq a
K8Cd3.77(7)Ge42.23
K16d01/41/2100%0.0358(7)
K22a000100%0.0175(9)
Ge124k00.30355(5)0.11589(5)100%0.0129(2)
Ge216i0.18327(4)xx100%0.0119(2)
Ge/Cd36c1/401/237(1)/63(1)%0.0137(3)
Rb8Cd3.65(7)Ge42.35
Rb16d01/41/2100%0.0254(3)
Rb22a000100%0.0124(3)
Ge124k00.30365(5)0.11637(5)100%0.0123(2)
Ge216i0.18356(3)xx100%0.0114(2)
Ge/Cd36c1/401/239(1)/61(1)%0.0127(3)
Cs7.80(1)Cd3.65(6)Ge42.35
Cs16d01/41/2100%0.0204(2)
Cs22a00089.8(4)%0.0117(3)
Ge124k00.30334(4)0.11719(4)100%0.0123(1)
Ge216i0.18370 (3)xx100%0.0116(2)
Ge/Cd36c1/401/239(1)/61(1)%0.0136(3)
a Ueq is defined as one third of the trace of the orthogonalized Uij tensor.
Table 3. Anisotropic displacement parameters (Uij2) for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
Table 3. Anisotropic displacement parameters (Uij2) for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
AtomU11U22U33U23U13U12
K8Cd3.77(7)Ge42.23
K10.038(1)0.032(2)=U11000
K20.0175(9)=U11=U11000
Ge10.0121(3)0.0137(3)0.0130(3)0.0000(2)00
Ge20.0119(2)=U11=U11−0.0006(1)=U23=U23
Ge/Cd30.0157(5)0.0127(4)=U22000
Rb8Cd3.65(7)Ge42.35
Rb10.0278(4)0.0205(6)=U11000
Rb20.0124(3)=U11=U11000
Ge10.0119(3)0.0127(3)0.0124(3)0.0003(2)00
Ge20.0114(2)=U11=U11−0.0005(1)=U23=U23
Ge/Cd30.0144(5)0.0119 (3)=U22000
Cs7.80(1)Cd3.65(6)Ge42.35
Cs10.0226(2)0.0159(3)=U11000
Cs20.0117(3)=U11=U11000
Ge10.0115(2)0.0122(3)0.0132(3)0.0003(2)00
Ge20.0116(2)=U11=U11−0.0002(1)=U23=U23
Ge/Cd30.0158(4)0.0125(3)=U22000
Table 4. Selected interatomic distances for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
Table 4. Selected interatomic distances for K8Cd3.77(7)Ge42.23 (1), Rb8Cd3.65(7)Ge42.35 (2), and Cs7.80(1)Cd3.65(6)Ge42.35 (3).
Compound 1dCompound 2dCompound 3d
Ge1-Ge2 (2×)2.4931(4)Ge1-Ge2 (2×)2.5029(4)Ge1-Ge2 (2×)2.5118(4)
Ge1-Ge12.520(1)Ge1-Ge12.539(1)Ge1-Ge12.570(1)
Ge1-Ge/Cd32.5858(6)Ge1-Ge/Cd32.5912(5)Ge1-Ge/Cd32.6019(5)
Ge2-Ge22.513(1)Ge2-Ge22.511(1)Ge2-Ge22.518(1)
Ge2-Ge1 (3×)2.4931(4)Ge2-Ge1 (3×)2.5029(4)Ge2-Ge1 (3×)2.5118(4)
Ge/Cd3-Ge1 (4×)2.5858(6)Ge/Cd3-Ge1 (4×)2.5912(5)Ge/Cd3-Ge1 (4×)2.6019(5)
K1-Ge1 (8×)3.6789(4)Rb1-Ge1 (8×)3.6932(4)Cs1-Ge1 (8×)3.7167(4)
K1-Ge2 (8×)4.0438(3)Rb1-Ge2 (8×)4.0564(3)Cs1-Ge2 (8×)4.0758(3)
K1-Ge/Cd3 (4×)3.8435(2)Rb1-Ge/Cd3 (4×)3.8572(2)Cs1-Ge/Cd3 (4×)3.8765(2)
K1-Ge1 (4×)4.2157(6)Rb1-Ge1 (4×)4.2262(5)Cs1-Ge1 (4×)4.2378(5)
K2-Ge2 (8×)3.4507(7)Rb2-Ge2 (8×)3.4686(6)Cs2-Ge2 (8×)3.4885(6)
K2-Ge1 (12×)3.5322(6)Rb2-Ge1 (12×)3.5477(5)Cs2-Ge1 (12×)3.5654(5)

Share and Cite

MDPI and ACS Style

Schäfer, M.C.; Bobev, S. Synthesis and Structural Characterization of the New Clathrates K8Cd4Ge42, Rb8Cd4Ge42, and Cs8Cd4Ge42. Materials 2016, 9, 236. https://doi.org/10.3390/ma9040236

AMA Style

Schäfer MC, Bobev S. Synthesis and Structural Characterization of the New Clathrates K8Cd4Ge42, Rb8Cd4Ge42, and Cs8Cd4Ge42. Materials. 2016; 9(4):236. https://doi.org/10.3390/ma9040236

Chicago/Turabian Style

Schäfer, Marion C., and Svilen Bobev. 2016. "Synthesis and Structural Characterization of the New Clathrates K8Cd4Ge42, Rb8Cd4Ge42, and Cs8Cd4Ge42" Materials 9, no. 4: 236. https://doi.org/10.3390/ma9040236

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop