Semiconducting Polymer Photodetectors with Electron and Hole Blocking Layers: High Detectivity in the Near-Infrared

Sensing from the ultraviolet-visible to the infrared is critical for a variety of industrial and scientific applications. Photodetectors with broad spectral response, from 300 nm to 1,100 nm, were fabricated using a narrow-band gap semiconducting polymer blended with a fullerene derivative. By using both an electron-blocking layer and a hole-blocking layer, the polymer photodetectors, operating at room temperature, exhibited calculated detectivities greater than 1013 cm Hz1/2/W over entire spectral range with linear dynamic range approximately 130 dB. The performance is comparable to or even better than Si photodetectors.


Introduction
Sensing from the ultraviolet (UV)-visible to the infrared is critical for a variety of industrial and scientific applications, including image sensing, communications, environmental monitoring, remote control, day-and night-time surveillance and chemical/biological sensing [1][2][3]. Today, separate OPEN ACCESS sensors are fabricated from inorganic materials for different sub-bands within the UV to near-infrared (NIR) wavelength (λ) range [4]. Colloidal inorganic semiconductor quantum dots (PbS) were used to fabricate NIR-photodetectors onto gold interdigitated electrodes [5,6]. These NIR-photodetectors showed photoconductive gain and photoresponse out to 1,450 nm [6]. However, the quantum dot NIR-photodetectors were fabricated using the "in-plane" structure with electrode spacing >5 µm. As a result the required driving voltage is too high (>40 V) to be used with any commercially available thin film transistor (TFTs) arrays for read-out. These limitations significantly restrict the application of inorganic photodetectors in day-and night-time surveillance and chemical/biological sensing where high-speed and low power photodetectors are desired.
Polymer photodetectors (PPDs) have been the subject of extensive research in the past decade. PPDs offer a number of advantages: large-area detection, wide selection of materials, thin and light weight, low-cost fabrication on flexible substrates and operation at room temperature. PPDs with fast temporal-response have been reported [7][8][9][10]. In previous work [10], we reported PPDs with spectral response from 300 nm to 1,450 nm with detectivities larger than 10 13 cm Hz 1/2 /W. Although very small dark currents are required for high performance, there is no previous report that addresses how to minimize thermally generated dark currents from narrow-band gap semiconducting polymers. We report here PPDs comprising bulk heterojunction materials. By using electron and hole blocking layers, we have reduced the dark current by 3 orders of magnitude. As a result the detectivity is enhanced by a factor of 20.

Current-Voltage Measurement:
The light source was calibrated solar simulator. For J-V measurement of PPDs, a band-pass filter was used to obtain the light at 800 nm. Data were collected using a Keithley 236 SMU.

External Quantum Efficiency (EQE) Measurement:
EQEs under short circuit was determined by illuminating the device with periodic (i.e., "chopped") monochromatic light. The AC photocurrent from the device is converted to an AC voltage and measured with a lock-in amplifier. Incident light from a xenon lamp (100 W) passing through a monochromator was chopped at 170 Hz and focused on the active area of device. A calibrated crystalline silicon diode (818UV, Newport) was used as a reference before each measurement.
The current-density voltage (J-V) characteristics measured in the dark and under illumination (λ = 800 nm) with light intensity of 0.22 mW/cm 2 are shown in Figure 2. All PPDs (A, B and C) show good rectification ratios in the dark, 10 4 at ±1 V, indicating the formation of good diodes. The dark currents observed from PPD B are more than 2 orders of magnitude smaller than that from PPD A; the dark currents observed from PPD C are more than 10 times smaller than that from PPD B. These results indicate that the thin C 60 and PS-TPD-PFCB buffer layers are important for minimizing the dark currents generated withinfrom the PCPDTBT:PCBM PC 70 BM BHJ structure.  For PPDs A, B and C, the current density (J)-voltage (V) relationship can be described by the standard diode equation [15]: and A* = 4πqm*K B 2 /h 3 , J 0 is the saturation current density, q is the electron charge V is the voltage, n is the ideality factor, K B is the Boltzman constant, T is the absolute temperature R S is the series resistance, R SH is the shunt resistance, m* is the effective electron mass, h is Planck's constant, A* is Richardson's constant and E PF is the energy difference between the HOMO of PCPDTBT and the LUMO of PC 70 BM (~0.6 eV).
As described above, a high dark current is expected from PPD A because E PF (~0.6 eV) is relatively small. In PPD B, because the HOMO of C 60 is lower than the HOMO of PCPDTBT, a thin layer of C 60 can block holes from moving into the Al cathode, resulting in a lower dark current. In PPD C, because the LUMO of PS-TPD-PFCB is higher than the LUMO of PC 70 BM, even higher than the LUMO of PCPDTBT, a thin layer of PS-TPD-PFCB blocks electrons from moving into the ITO/PEDOT:PSS bi-layer anode. The thin layer of C 60 also blocks holes from moving into the Al cathode. Therefore, a significantly lower dark current was observed in PPD C because of the insertion of the C 60 hole-blocking layer and the PS-TPD-PFCB electron-blocking layer.
Moreover, due to a thin layer of C 60 inserted between PCPDTBT:PC70BM and the Al electrode, R S in PPD B should be larger than in PPD A because R S is the sum of the contact resistance and the bulk resistance of the materials [16,17]. For PPD A, R S = R ITO +R PEDOT:PSS +R PCPDTBT:C70BM For PPD B, R S = R ITO + R PEDOT:PSS + R (PCPDTB:PC70BM) + R C60 + R Al . For PDD C, For PPD B, R S = R ITO + R PEDOT:PSS + R PS-TPD-PFCB R (PCPDTB : PC70BM) + R C60 + R Al . The R s values were obtained by fitting the J-V curves shown in Figure 2 to Equation 1. R s = 2.6 × 10 3 Ω/cm 2 , 4.6 × 10 3 Ω/cm 2 and 2.5 × 10 4 Ω/cm 2 for PPD A, PPD B and PPD C, respectively. The R sh values are the following: R sh = 5.6 × 10 5 Ω/cm 2 , 6.3 × 10 6 Ω/cm 2 and 4.6 × 10 8 Ω/cm 2 for PPD A, PPD B and PPD C, respectively. Therefore, the dark current densities in these PPDs is controlled by the blocking layers: J D (PPD A) > J D (PPD B) > J D (PPD C), as described by Equation (1).
In order to get photoresponsivity (PR), the ratio of photocurrent to incident-light power, we measured the photocurrent under the light at λ = 800 nm with a light intensity of 0.22 mW/cm 2 as shown in Figure 2. PR is calculated accordingly from the observed photocurrents and the light intensity used for measurement of photo response. With a bias at 0 V, the PR = 217 mA/W, 96 mA/W and 54 mA/W for PPDs A, B and C, respectively. With a bias at −0.5 V, the PR = 387 mA/W, 129 mA/W and 72 mA/W for PPDs A, B and C, respectively. These high PR values demonstrate very good photoresponsivity.
We also measured the external quantum efficiency (EQE) under short-circuit and reversed bias chopping the light and using a lock-in amolifier. The data are presented in Figure 1. For comparison, the absorption spectra of pristine PCPDTBT and the composite of PCPDTBT:PC 70 BM thin films are also presented in Figure 1. The similar spectral profiles of absorption and EQE of PCPDTBT:PC 70 BM indicate that photons absorbed in IR range by both PCPDTBT and PC 70 BM contribute to the photocurrent. At λ= 800 nm, the EQE is 33% at 0 V and increases by a factor of 2 to 60% at −0.5 V. We note that recently several novel narrow-band gap semiconducting polymers are reported to have efficient photovoltaic activity in IR spectral region [18][19][20][21]. For example, Yao et al. showed spectral response extended to 1,000 nm with EQE of 19% at 850 nm [21]. Mühlbacher et al. showed 38% EQE around 700 nm and 13% EQE at 850 nm [20]. The high EQE observed from PCPDTBT: PC 70 BM BHJ structure imply that PPDs fabricated by PCPDTBT: PC 70 BM will exhibit high detectivity.
Assuming that the shot noise from the dark current is the dominant contribution [4,10,22], the detectivity can be expressed as where PR is the photoresponsivity; q is the absolute value of electron charge (1.6 × 10 −19 Coulombs), J d is the dark current, J ph is the photo current, and L light is the light intensity. Detectivities were calculated based on the measured photocurrent, dark current and incident light intensity ( Figure 2). Under illumination at λ = 800 nm with light intensity of 0.22 mW/cm 2 , the calculated detectivities are D* = 2.7 × 10 12 cm Hz 1/2 /W (Jones), 4.4 × 10 12 Jones, and 4.0 × 10 13 Jones for PPDs A, B and C, respectively (at zero bias); D* = 5.4 × 10 11 Jones, 1.6 × 10 12 Jones, and 7.2 × 10 12 Jones for PPDs A, B and C, respectively (at −0.5 V).
By combining the calculated detectivities at 800 nm with the photoresponsivity data, the PPDs detectivity values were obtained over the entire spectral range; the results are shown in Figure 3. The calculated detectivities at λ = 800 nm are also shown in Figure 3, represented by points A, B and C for PPDs A, B and C, respectively. Operating at room temperature, all PPDs exhibited spectral response from 300 nm to 1,100 nm. PPD C calculated showed detectivity greater than 10 13 Jones from 300 nm to 900 nm and greater than 10 12 Jones from 900 nm to 1,100 nm (10 times larger than observed from PPD B, and approximately 20 times larger than observed from PPD A). These results demonstrate that the electron-blocking layer, PS-TPD-PFCB, and the hole-blocking layer, C 60 , are important for achieving high detectivity NIR polymer photodetectors.   Figure 4 shows the photocurrent versus light intensity for PPD C (at λ = 800 nm). For PPD C, the photosensitivity is linear in light intensity over a range exceeding 130 dB, better than that of Si photodetectors (120 dB) [4]. 1mW/cm 2 In conclusion, the results presented here indicate that electron-blocking and hole-blocking layers are important for achieving high performance NIR polymer photodetectors. The results demonstrate that the performance parameters of near infrared polymer photodetectors based on PCPDTBT are comparable to or even better than Si photodetectors. The high detectivity and high photoresponsivity open opportunities for the creation of detectors with unusually wide spectral range and for the fabrication of high-resolution detector arrays for optical communications, chemical/biological sensing and day-and night-time surveillance.