Next Article in Journal
Neuronal Aneuploidy in Health and Disease:A Cytomic Approach to Understand the Molecular Individuality of Neurons
Next Article in Special Issue
Density Functional Study of Structures and Electron Affinities of BrO4F/BrO4F-
Previous Article in Journal
Composition-Dependent Dielectric Properties of DMF-Water Mixtures by Molecular Dynamics Simulations
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Probing the Structure, Stability and Hydrogen Adsorption of Lithium Functionalized Isoreticular MOF-5 (Fe, Cu, Co, Ni and Zn) by Density Functional Theory

Institute for Materials Research(IMR), 2-1-1, Katahira, Aoba-Ku, Sendai, 980 8577, Japan
*
Author to whom correspondence should be addressed.
Int. J. Mol. Sci. 2009, 10(4), 1601-1608; https://doi.org/10.3390/ijms10041601
Submission received: 21 February 2009 / Revised: 5 March 2009 / Accepted: 9 April 2009 / Published: 14 April 2009
(This article belongs to the Special Issue Applications of Density Functional Theory)

Abstract

:
Li adsorption on isoreticular MOFs with metal Fe, Cu, Co, Ni and Zn was studied using density function theory. Li functionalization shows a considerable structural change associated with a volume change in isoreticular MOF-5 except for the Zn metal center. Hydrogen binding energies on Li functionalized MOFs are seen to be in the range of 0.2 eV, which is the desired value for an ideal reversible storage system. This study has clearly shown that Li doping is possible only in Zn-based MOF-5, which would be better candidate to reversibly store hydrogen.

1. Introduction

Nowadays, worldwide interest is focused on using a clean burning substitute such as hydrogen in place of fossil fuels, due to both economic and environmental reasons [1,2]. However, hydrogen storage is one of the most important challenges impeding its practical application. Physisorption on large surface area materials is one significant approach for storing hydrogen. Some metal-organic frameworks (MOFs) show promising results for hydrogen adsorption, but the storage pressure and temperature conditions make their use economically unfavorable [35].
In order to improve the storage conditions, it is important to design new MOF materials having not only tailored pore dimensions and large void volumes, but also incorporating strong adsorption sites, like for instance, adsorbing alkali metals on the surface [610]. In addition, researchers have proposed that metal centers present in the MOFs play an important role in the gas adsorption property [1113]. Recently, Li doping was performed to enhance the storage capacity of MOFs both by experimental and theoretical means and to provide the desired binding enthalpies in the range of 0.2 – 0.3 eV for hydrogen [1418].
In the report, by means of first-principles calculations, we have studied the binding energies for hydrogen molecules on the Li functionalized Zn-MOF-5. Furthermore, we have made a study on Li-functionalized isoreticular M-MOF-5’s characterized by the presence of different metal centers (Scheme 1) to find the stability and structure of MOF’s after doping the M-MOF-5 unit (M = Fe, Co, Ni Cu and Zn) with Li atoms. The paper is organized as follows. In the first part, the effect of Li doping on the MOF-5 unit is explored by doping Li atom. In the second part we have studied the binding of hydrogen molecules on the Li functionalized Zn-MOFs. In the third part we have studied the structure and stability of lithium functionalized isoreticular MOF-5 and our conclusions are given in Section 4.

2. Results and Discussion

The structure of the primitive cell representing the unit cell was fully optimized without any geometrical constraints. In Table 1 we compare the present computational result of the MOF-5 structure with experimental data, which are in good agreement. This provides confidence in our computational method.

2.1. Stability of the Li doping on MOF’s

To examine the effect of Li doping, we first investigated the adsorption energy of doping Li atom on the benzene unit of Zn-MOF-5. A summary of Li adsorption energy on Zn-MOF-5 can be seen in Table 1. The energy gain in attaching Li to a MOF-5 unit is called the adsorption energy (ΔAE) and is defined as follows:
Δ A E = E ( Li MOF ) E ( Li ) E ( MOF )
where E(Li-MOF), E(Li) and E(MOF) are the total energies of the unit cell containing the adsorbed Li atoms and the energy of the MOF-5 unit respectively. A positive value of ΔAE would indicate an energy gain in attaching the Li to the MOF-5 surface, and the negative value is energy lost during the process. From our calculations it is evident that doping Li atom was found to be exothermic in nature. In addition a significant change in the bond length of benzene unit was observed, which was attributed to the charge transfer from the Li cation to the MOF-5 unit. Furthermore, up on Li functionalization only a slight change in structure and bond parameters is found to occur near OZn4 tetrahedra site. The calculated Li atom - benzene adsorption energy was lower than the reported values of 1.6 eV by Dixon and co-workers [19]. Such a decrease in expected as there exists effective conjugation between OZn4 tetrahedra unit and linker Benzene dicarboxylic (BDC) unit. Bader charge analysis on the system revealed, that Li atom carries a +0.9e charge over it. It is important to specify here that Rao and Jena had shown that a positive charge atom can bind a large amount of hydrogen that by a neutral atom by charge polarization mechanism [20].

2.2. Hydrogen adsorption on Li-functionalized MOF’s

To understand the effect of hydrogen adsorption on the Li-functionalized MOF’s we have optimized the Li-functionalized Zn-MOF-5 with hydrogen molecules near to the Li atom. Upon structural relaxation only slight change in structure and bond parameters was found to occur on the organic linker and near OZn4 tetrahedra. The hydrogen interaction or the binding energy per hydrogen molecule (ΔEb) can be defined as:
Δ E b = [ E T ( Li MOF ) + E T ( H 2 ) E T ( Li MOF + H 2 ) ] / nH 2
where ET(Li-MOF+H2) and ET(Li-MOF) refer to the total energy of the Li- functionalized Zn-MOF with and without hydrogen molecule respectively, while the ET(H2) refers to the total energy of the free hydrogen molecule and “n” is the number of hydrogen molecules. In the current work we have added one to four hydrogen molecules near the Li center. The calculated structural parameters and the binding energies are provided in Table 2, while the optimized structures are provided in Figure 1.
For the first H2, the interaction energy is 0.213 eV, with an intermolecular distance of 2.153 Ǻ. This binding energy per atom was close to the value reported for systems that can be used for an ideal reversible hydrogen storage system [22].The orientation of hydrogen is in T-shape, with a H-H bond distance of 0.760 Å, which corresponds to a very small change compared to the 0.750 Å bond length in a free hydrogen molecule. This indicates that the Li cation holds the H2 molecules by a charge – quadruple and charge – induced dipole interaction [23]. When the second hydrogen is introduced, the Li – H2 distance increases to 2.124 Å, while the binding energy per H2 molecule gets reduced to 0.209 eV. To know the number of hydrogen molecules a Li cation can hold, we doped the third and fourth H2 near the Li cation. With the introduction of third H2 the Li – H2 distance increases along with a decreases in the interaction energy value. A noticeable feature is the H – H distance which decreases with the increase in the number of H2. When the fourth hydrogen is introduced near the Li cation, three H2 are place near the Li atom and the other H2 molecule is moved away to a nonbonding distance of 4.036 Å. Thus each Li cation can hold up to 3 hydrogen molecules in a quasi molecular form. Furthermore, each BDC unit can adsorb one Li atom on each face and can maximize its storage to 6 hydrogen molecules per BDC unit. Further the existence of several metal sites will increase the storage capacity of the Li-functionalized MOF’s.

2.3. Effect of metal center on Li-functionalized MOF’s

To know the possibility of extending the Li doping to other IRMOF-5, we studied the adsorption of Li cation on IRMOF-5. We have selected metals (M= Fe, Co, Ni, Cu and Zn) from the same column of the periodic table by replacing Zn centers. Structural relaxation without Li atom shows only a slight change in volume to occur up on the change in metal sites. However, up on doping with Li atom a considerable change in shape and structure was observed for other materials except Zn. Table 3 contains structural information for the linker and the benzene-Li mean distance. One can observe that the linker unit benzene remains practically unchanged in all the studied compounds.
In Table 4. we have collected the M-O1, C1-O1, C1-C2 bond lengths, O1-M-O2 bond angles and the adsorption energy of Li for the optimized structure of M-MOF-5 system. From the table it is evident that a significant structural change is observed around the OM4 tetrahedra unit and linker BDC unit. The metal-metal distance deviation is shorter in the case of Zn, and very high reduction in distance is observed for iron system. Further, calculated adsorption energy for these compounds don’t show any regular trend with the metals. These results suggest that adsorption energy of Li not only depend on the metal centers but are greatly influenced by the structural change and the volume of the system that changes upon Li doping.

3. Computational Methods

The calculations were performed using density functional theory (DFT) in the generalized gradient approximation (GGA) with the exchange-correlation function proposed by Perdew–Wang (PW91) [24] as implemented in the VASP plane wave. To represent the atomic cores, we use the projector augmented wave pseudopotentials. Ionic positions and cell parameters were relaxed with respect to minimum forces and stress by using conjugated-gradient algorithms. All atoms were fully relaxed with the energy converged to less than 10−5 eV. Electronic wave functions are represented by plane waves up to 400 eV. Calculations were preformed on a 106-atom, primitive cell of dimension 26 Å X 13 Å X 13 Å which imposes periodic boundary conditions. As we are dealing with a large system, the Γ-point was used for sampling the Brillouin zone.

4. Conclusions

In summary, we have performed a DFT study to determine the stability of Li atom binding on Zn-MOF. The adsorption energy calculated shows that Li atom adsorption is exothermic in MOF system. Hydrogen adsorption on Li functionalized Zn-MOF-5 occurs with only a small structural change. Doping Li enhances the binding energy of hydrogen molecules to the desired value. Each Li was found to hold up to three hydrogen molecules in a near molecular form. Introduction of Li on isoreticular MOFs with metals Fe, Co, Ni, Cu shows a considerable structural change, to occurs near the OM4 tetrahedral site, leading to the reduction in the volume of the materials. The adsorption energy and stability of Li doping on these materials not only depend on the metal centers by are greatly influenced by the structural change and the volume of the system that changes after Li doping.

Acknowledgments

This work has been supported by New Energy and Industrial Technology Development Organization (NEDO) under “Advanced Fundamental Research Project on Hydrogen Storage Materials”. The authors thank the crew of the Center for Computational Materials Science at Institute for Materials Research, Tohoku University, for their continuous support of the HITACHI SR11000 supercomputing facility.

References and Notes

  1. Orimo, SI; Nakamori, Y; Eliseo, JR; Züttel, A; Jensen, CM. Complex Hydrides for Hydrogen Storage. Chem. Rev 2007, 107, 4111–4132. [Google Scholar]
  2. vanden Berg, AWC; Areán, CO. Materials for hydrogen storage: current research trends and perspectives. Chem Commun 2008, 668–681. [Google Scholar]
  3. Rosi, NL; Eckert, J; Eddaoudi, M; Vodak, DT; Kim, J; O’Keeffe, M; Yaghi, OM. Hydrogen Storage in Microporous Metal-Organic Frameworks. Science 2003, 300, 1127–1129. [Google Scholar]
  4. Rowsell, JLC; Spencer, EC; Eckert, J; Howard, JAK; Yaghi, OM. Gas Adsorption Sites in a Large-Pore Metal-Organic Framework. Science 2005, 309, 1350–1354. [Google Scholar]
  5. Farha, OK; Spokoyny, AM; Mulfort, JK; Hawthrone, MF; Mirkin, CA; Hupp, JT. Syntheis and Hydrogen Sorption Properties of Carborane Based Metal-Organic Framework Materials. J. Am. Chem. Soc 2007, 129, 12680–12681. [Google Scholar]
  6. Mulfort, KL; Hupp, JT. Alkali Metal Cation Effects on Hydrogen Uptake and Binding in Metal-Organic Frameworks. Inorg. Chem 2008, 47, 7936–7938. [Google Scholar]
  7. Yang, S; Lin, X; Blake, AJ; Thomas, KM; Hubberstey, P; Champness, NR; Schroder, M. Enhancement of H2 Adsorption in Li+-exchanged Co-ordination Framework Materials. Chem Commun 2008, 6108–6110. [Google Scholar]
  8. Chen, B; Ockwig, NW; Millward, AR; Contreras, DS; Yaghi, OM. High H2 Adsorption in a Microporous Metal-Organic Framework with Open metal Sites. Angew. Chem. Int. Ed 2005, 44, 4745–4749. [Google Scholar]
  9. Dinca, M; Long, JR. Strong H2 Binding and Selective Gas Adsorption within the Microporous Coordination Solid Mg3(O2C-C10H6-CO2)3. J. Am. Chem. Soc 2005, 127, 9376–9377. [Google Scholar]
  10. Li, Y; Xie, L; Liu, Y; Yang, R; Li, X. Favorable Hydrogen Storage Properties of M(HBTC)(4,4′-bipy).3DMF (M = Ni and Co). Inorg. Chem 2008, 47, 10372–10377. [Google Scholar]
  11. Ramsahye, NA; Maurin, G; Bourrelly, S; Llewellyn, PL; Serre, C; Loiseau, T; Devic, T; Férey, G. Probing the Adsorption Sites for CO2 in Metal Organic Frameworks Materials MIL-53 (Al, Cr) and MIL-47 (V) by Density Functional Theory. J. Phys. Chem. C 2008, 112, 514–520. [Google Scholar]
  12. Vitillo, JG; Regli, L; Chavan, S; Ricchiardi, G; Spoto, G; Dietzel, PDC; Bordiga, S; Zecchina, A. Role of Exposed Metal Sites in Hydrogen Storage in MOFs. J. Am. Chem. Soc 2008, 130, 8386–8396. [Google Scholar]
  13. Mueller, T; Ceder, G. A Density Functional Theory Study on Hydrogen Adsorption in MOF-5. J. Phys. Chem. B 2005, 109, 17974–17983. [Google Scholar]
  14. Han, SS; Goddard, WA. Lithium-Doped Metal-Organic Frameworks for Reversible H2 Storage at Ambient Temperature. J. Am. Chem. Soc 2007, 129, 8422–8423. [Google Scholar]
  15. Mulfort, KL; Hupp, JT. Chemical Reduction of Metal-Organic Framework materials as a Method to Enchance Gas Uptake and Binding. J. Am. Chem. Soc 2007, 129, 9604–9605. [Google Scholar]
  16. Zhao, D; Yuan, D; Zhou, H-C. The Current Status of Hydrogen Storage in Metal-Organic Frameworks. Energy Environ. Sci 2008, 1, 222–235. [Google Scholar]
  17. Klontazas, E; Mavrandonakis, A; Tylianakis, E; Froudakis, GE. Improving Hydroen Storage Capacity of MOF by Functionalization of the Organic Linker with Lithium Atoms. Nano Lett 2008, 8, 1572–1576. [Google Scholar]
  18. Blomqvist, A; Araújo, CM; Srepusharawoot, P; Ahuja, R. Li-decorated Metal-Organic Framework-5: A Route to Achieving a Suitable Hydrogen Storage Medium. Proc. Natl. Acad. Sci. USA 2007, 104, 20173–20176. [Google Scholar]
  19. Amicangelo, JC; Armentrout, PB. Absolute Binding Energies of Alkali-Metal Cation Complexes with Benzene Determined by Threshold Collision-Induced Dissociation Experiments and ab Initio Theory. J. Phys. Chem. A 2000, 104, 11420–11432. [Google Scholar]
  20. Niu, J; Rao, BK; Jena, P. Binding of hydrogen molecules by transition-metal ion. Phys. Rev. Lett 1992, 68, 2277–2280. [Google Scholar]
  21. Li, H; Eddaoudi, M; O’Keeffe, MO; Yaghi, OM. Design and Synthesis of an Exceptionally Stable and Highly Porous Metal-Organic Framework. Nature (London) 1999, 402, 276–279. [Google Scholar]
  22. Ströbel, R; Garche, J; Moseley, PT; Jörissen, L; Wold, G. Hydrogen Storage by Carbon Materials. J. Power Sources 2006, 159, 781–801. [Google Scholar]
  23. Lochan, RC; Head-Gordon, M. Computational Studies of Molecular Hydrogen Binding Affinities: The Role of Dispersion Forces, Electrostatics and Orbital Interactions. Phys. Chem. Chem. Phys 2006, 8, 1357–1370. [Google Scholar]
  24. Perdew, JP; Wang, Y. Accurate and Simple Analytic Representation of the Electron-Gas Correlation Energy. Phys Rev B 1992, 45, 13244–13249. [Google Scholar]
Figure 1. Optimized geometries of adsorbed hydrogen molecules on Li functionalized Zn-MOF-5 with one (a), two (b), three (c) and four (d) hydrogen molecules. Colors grey (C atoms), white (H atoms, red (O atoms) green (Li atoms) pale gray (Zn atoms).
Figure 1. Optimized geometries of adsorbed hydrogen molecules on Li functionalized Zn-MOF-5 with one (a), two (b), three (c) and four (d) hydrogen molecules. Colors grey (C atoms), white (H atoms, red (O atoms) green (Li atoms) pale gray (Zn atoms).
Ijms 10 01601f1
Scheme 1. Primitive unit cell of isoreticular MOF-5 (M = Fe, Co, Ni, Cu, Zn). Colors: blue (Metal center), gray (C atoms), white (H atoms), green (Li atom), red (oxygen). The structure is formed by OM4 tetrahedra at the corners linked by benzene dicarboxylic (BDC) groups.
Scheme 1. Primitive unit cell of isoreticular MOF-5 (M = Fe, Co, Ni, Cu, Zn). Colors: blue (Metal center), gray (C atoms), white (H atoms), green (Li atom), red (oxygen). The structure is formed by OM4 tetrahedra at the corners linked by benzene dicarboxylic (BDC) groups.
Ijms 10 01601f2
Table 1. Adsorption energy (AE, eV) and selected bond parameters (Å) for Li atom on Zn-MOF-5 unit.
Table 1. Adsorption energy (AE, eV) and selected bond parameters (Å) for Li atom on Zn-MOF-5 unit.
SystemΔAE eVC2–C3aC3–C4aC4–C5aC5–C6aC6–C7aC7–C2aCM–Lib
Li–Zn-MOF−1.561.4281.3801.4281.4281.3801.4282.229
Zn-MOFc1.399 (1.388)1.384 (1.375)1.399 (1.392)1.399 (1.397)1.384 (1.379)1.399 (1.392)
aFor numbering see Scheme 1.
bMean Li–C distance
cValues in parenthesis are experimental values from ref. [21].
Table 2. Selected bond parameters (Å) and binding energy per hydrogen molecule (eV) for the adsorption of hydrogen on Li functionalized Zn-MOF.
Table 2. Selected bond parameters (Å) and binding energy per hydrogen molecule (eV) for the adsorption of hydrogen on Li functionalized Zn-MOF.
No. of H2Avg. Benzene – Li (Å)Li – H2 (Å)Avg. H – H (Å)ΔEb (eV)
02.206-0.750-
12.2232.0960.7600.213
22.2412.1240.7590.209
32.2572.3150.7550.196
42.2522.379 (4.036)0.755 (0.751)0.163
Table 3. Calculated structural parameters (Å) in the organic linker of Li cation doped M-MOF-5 (M = Fe, Co, Ni, Cu, Zn).
Table 3. Calculated structural parameters (Å) in the organic linker of Li cation doped M-MOF-5 (M = Fe, Co, Ni, Cu, Zn).
SystemC2–C3C3–C4C4–C5C5–C6C6–C7C7–C2CM–Lia
Fe-MOF-51.4251.3691.4251.4251.3961.4252.274
Co-MOF-51.4171.4071.4171.4171.4071.4172.292
Ni-MOF-51.4101.3911.4101.4101.3911.4102.280
Cu-MOF-51.4071.3961.4081.4071.3941.4042.285
Zn-MOF-51.4361.3771.4371.4371.3771.4362.209
aMean benzene – Li distance
Table 4. Selected bond lengths (Å) bond angles (deg) and adsorption energy of Li on M-MOF-5 (M = Fe, Co, Ni, Cu, Zn).
Table 4. Selected bond lengths (Å) bond angles (deg) and adsorption energy of Li on M-MOF-5 (M = Fe, Co, Ni, Cu, Zn).
SystemM–O1C1–O1C1–C2O1–C–O2M1–M2ΔAE eV
Fe-MOF-51.9151.2891.479123.62.8810.621
Co-MOF-52.0101.2761.527125.42.3990.548
Ni-MOF-51.9491.2701.481127.12.8640.776
Cu-MOF-52.0091.2651.501128.22.9393.14
Zn-MOF-51.9561.2641.491129.53.1281.15
Zn-MOF-5a1.937 (1.911)1.274 (1.300)1.479129.3 (125.0)3.128 (3.160)-
aCalculated and experimental values (in parenthesis) for Zn-MOF-5 without Li doping. Experimental values are from ref. [20].

Share and Cite

MDPI and ACS Style

Venkataramanan, N.S.; Sahara, R.; Mizuseki, H.; Kawazoe, Y. Probing the Structure, Stability and Hydrogen Adsorption of Lithium Functionalized Isoreticular MOF-5 (Fe, Cu, Co, Ni and Zn) by Density Functional Theory. Int. J. Mol. Sci. 2009, 10, 1601-1608. https://doi.org/10.3390/ijms10041601

AMA Style

Venkataramanan NS, Sahara R, Mizuseki H, Kawazoe Y. Probing the Structure, Stability and Hydrogen Adsorption of Lithium Functionalized Isoreticular MOF-5 (Fe, Cu, Co, Ni and Zn) by Density Functional Theory. International Journal of Molecular Sciences. 2009; 10(4):1601-1608. https://doi.org/10.3390/ijms10041601

Chicago/Turabian Style

Venkataramanan, Natarajan Sathiyamoorthy, Ryoji Sahara, Hiroshi Mizuseki, and Yoshiyuki Kawazoe. 2009. "Probing the Structure, Stability and Hydrogen Adsorption of Lithium Functionalized Isoreticular MOF-5 (Fe, Cu, Co, Ni and Zn) by Density Functional Theory" International Journal of Molecular Sciences 10, no. 4: 1601-1608. https://doi.org/10.3390/ijms10041601

Article Metrics

Back to TopTop